DE4224280C1 - Use of copper@-chromium@-titanium@ alloy - for rolled or drawn profiles for spectacle frame mfr. - Google Patents
Use of copper@-chromium@-titanium@ alloy - for rolled or drawn profiles for spectacle frame mfr.Info
- Publication number
- DE4224280C1 DE4224280C1 DE19924224280 DE4224280A DE4224280C1 DE 4224280 C1 DE4224280 C1 DE 4224280C1 DE 19924224280 DE19924224280 DE 19924224280 DE 4224280 A DE4224280 A DE 4224280A DE 4224280 C1 DE4224280 C1 DE 4224280C1
- Authority
- DE
- Germany
- Prior art keywords
- alloy
- copper
- rolled
- chromium
- titanium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Die Erfindung betrifft die Verwendung einer Kupfer
legierung zur Herstellung von gewalzten oder gezogenen
Profilen für die Herstellung von Brillengestellen.
Dem Stand der Technik auf dem Gebiet der Brillengestelle sind Kupferlegierungen bekannt,
die als wesentlichen Legierungsbestandteil Nickel um
fassen. Solche Legierungen werden üblicherweise als
"Monel" bezeichnet.
In Anbetracht der Tatsache, daß
zunehmend Nickelallergien auftreten und Nickel als Werk
stoff für Brillengestelle daher vermieden werden soll,
liegt der Erfindung die Aufgabe zugrunde, eine neue
Verwendung einer Kupferlegierung zu schaffen, die nickel
frei ist, aber eine ausreichende Festigkeit aufweist,
so daß die Herstellung von entsprechenden Brillenge
stellen aus Profilen möglich ist, wobei diese Materialien
lötbar und schweißbar sein müssen. Zudem soll die Her
stellung kostengünstig erfolgen können.
Zur Lösung dieser Aufgabe wird die Verwendung einer
Kupferlegierung zur Herstellung von gewalzten oder ge
zogenen Profilen für die Herstellung von Brillenge
stellen vorgeschlagen, wobei die Kupferlegierung folgen
de Legierungsbestandteile umfaßt:
0,1 bis 1,4 Gew.% Chrom,
1,5 bis 4 Gew.% Titan,
zulässige Beimengungen von bis zu 0,5 Gew.% Silizium
und/oder bis zu 0,5 Gew.% Eisen
Rest Kupfer.
0,1 bis 1,4 Gew.% Chrom,
1,5 bis 4 Gew.% Titan,
zulässige Beimengungen von bis zu 0,5 Gew.% Silizium
und/oder bis zu 0,5 Gew.% Eisen
Rest Kupfer.
Bei Zugabe von Titan in einer Größenordnung von mehr
als 4 Gew.% neigt der Werkstoff zur Rißbildung beim
Warmwalzen oder Ziehen der Profile, so daß derartige
Legierungen nicht brauchbar sind. Bei einem Zusatz von
weniger als 1,5 Gew.% Titan sind die aus der Legierung
hergestellten Profilen zu weich, so daß sie für die
Herstellung von Brillengestellen ungeeignet sind. Durch
die Zugabe von Chrom wird eine erhebliche Verbesserung
der Festigkeit des Werkstoffes und damit der daraus
gefertigten Profile erreicht. Zu diesem Zweck ist ein
Mindestanteil von 0,1 Gew.% Chrom als unterste Grenze
erforderlich. Eine Zugabe von mehr als 1,4 Gew.% Chrom
führt zu keiner Verbesserung, sondern zu einer Ver
schlechterung der Eigenschaften der Legierung.
Die angegebenen Beimengungen von Silizium und/oder Eisen
sind zwar zulässig, jedoch wird die Legierung hierdurch
nicht verbessert.
Eine besonders geeignete Kupferlegierung zur erfindungs
gemäßen Verwendung umfaßt folgende Legierungsbestand
teile:
0,5 Gew.% Cr,
2 Gew.% Ti
Rest Cu.
0,5 Gew.% Cr,
2 Gew.% Ti
Rest Cu.
Die erfindungsgemäße Legierung wird üblicherweise im
Hochvakuumschmelzverfahren hergestellt, wobei möglichst
reine Legierungsbestandteile verwendet werden.
Durch die erfindungsgemäße Verwendung wird erreicht,
daß der zur Herstellung von Brillengestellen ver
wendete Werkstoff frei von Nickel ist, wobei dennoch
nicht nur eine ausreichende, sondern eine hervorragen
de Festigkeit des Werkstoffes erreicht wird, der im
Ergebnis dazu führt, daß daraus hergestellte Brillen
gestelle elastisch verformbar sind und in ihre ur
sprüngliche Form zurückkehren. Desweiteren ist der Werk
stoff lötbar und schweißbar, was zur Herstellung von
Brillengestellen unbedingtes Erfordernis ist.
Ein besonderer Vorteil ergibt sich daraus, daß der er
findungsgemäß verwendete Werkstoff aushärtbar ist, so
daß insbesondere hierdurch erreicht wird, daß ein hieraus
hergestelltes Brillengestell weitgehend federnd ist.
ln der Zeichnungsfigur 1 ist ein übliches Profil zur
Herstellung von Brillengestellen gezeigt. Das Profil
1 ist insbesondere als Glaseinfassung geeignet, wozu
das Profil eine entsprechende Aufnahmekerbe 2 für das
Brillenglas aufweist. Andere Profilformen sind möglich
und erforderlich, um aus dem angegebenen Werkstoff ein
entsprechendes Brillengestell fertigen zu können.
Die Erfindung ist nicht auf die Ausführungsbeispiele
beschränkt, sondern im Rahmen der Offenbarung vielfach
variabel.
Alle neuen, in der Beschreibung und/oder Zeichnung
offenbarten Einzel- und Kombinationsmerkmale werden
als erfindungswesentlich angesehen.
Claims (2)
1. Verwendung einer Kupferlegierung zur Herstellung
von gewalzten oder gezogenen Profilen für die Her
stellung von Brillengestellen, wobei die Kupfer
legierung folgende Legierungsbestandteile umfaßt:
0,1 bis 1,4 Gew.% Chrom,
1,5 bis 4 Gew.% Titan,
zulässige Beimengungen von bis zu 0,5 Gew-% Silizium
und/oder bis zu 0,5 Gew.% Eisen
Rest Kupfer.
0,1 bis 1,4 Gew.% Chrom,
1,5 bis 4 Gew.% Titan,
zulässige Beimengungen von bis zu 0,5 Gew-% Silizium
und/oder bis zu 0,5 Gew.% Eisen
Rest Kupfer.
2. Verwendung nach Anspruch 1, wobei die Kupfer
legierung folgende Legierungsbestandteile um
faßt:
0,5 Gew% Cr,
2 Gew.% Ti
Rest Cu.
0,5 Gew% Cr,
2 Gew.% Ti
Rest Cu.