DE3712947C2 - Process for rapid polymerization using warm catalysis and under pressure of resin used as a binder in agglomerated marble or granite and device for carrying out the process - Google Patents
Process for rapid polymerization using warm catalysis and under pressure of resin used as a binder in agglomerated marble or granite and device for carrying out the processInfo
- Publication number
- DE3712947C2 DE3712947C2 DE3712947A DE3712947A DE3712947C2 DE 3712947 C2 DE3712947 C2 DE 3712947C2 DE 3712947 A DE3712947 A DE 3712947A DE 3712947 A DE3712947 A DE 3712947A DE 3712947 C2 DE3712947 C2 DE 3712947C2
- Authority
- DE
- Germany
- Prior art keywords
- plate
- compressed air
- resin
- treated
- granite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Die Erfindung bezieht sich auf ein Ver fahren zur schnellen Polymerisation mittels Warm-Katalyse und unter Überdruck von als Bindemittel in agglomiertem Marmor oder Granit verwendeten Harz und Vorrichtung zur Durch führung des Verfahrens.The invention relates to a ver drive to rapid polymerization using warm catalysis and under pressure as a binder in agglomerated marble or granite used resin and device for through conduct of the procedure.
Bekannt ist ein Verfahren zur Polymeri sation von als Bindemittel in agglomiertem Marmor, Granit und anderen Steinen verwendeten Harz. Die Polymerisation findet dabei unter Atmosphärendruck und bei einer solchen Temperatur statt, daß die Auslöser, also Initiatoren der Polymerisation aktiviert werden.A method for polymerizing is known sation as a binder in agglomerated marble, granite and other stones used resin. The polymerization takes place thereby under atmospheric pressure and at such a temperature instead of the triggers, i.e. initiators of the polymerization to be activated.
Das auf diese Weise hergestellte Erzeugnis hängt von derjenigen Temperatur ab, bei welcher der Prozeß durch geführt wird. Wenn eine vergleichsweise niedrige Temperatur gewählt wird, dann ist die Geschwindigkeit der Vernetzung des Harzes größer als die Geschwindigkeit der Verdampfung des Verdünnungs-Reaktionsmittels ebenso wie die Verdampfungsge schwindigkeit des Wassers, welches in der Platte, dem Stein u. dgl. enthalten ist.The product made in this way hangs from the temperature at which the process through to be led. If a comparatively low temperature is selected, then the speed of networking the Resin greater than the rate of evaporation of the resin Dilution reagent as well as the evaporation gene dizziness of the water which is in the plate, the stone u. Like. Is included.
Das nach der Polymerisation erhaltene Erzeugnis hat zwar ein gefälliges Aussehen, wobei allerdings die zur voll ständigen Vernetzung erforderliche Zeit ziemlich lang ist (einige zehn Minuten). Auch ist der Materialeinsatz ziemlich hoch.The product obtained after the polymerization has although a pleasing appearance, but the full constant networking time is quite long (a few tens of minutes). The use of materials is also pretty high.
Wenn man nämlich die Temperatur erhöht, so ver mindert sich die erforderliche Zeit sehr schnell, wobei allerdings demgegenüber die Verdampfungsgeschwindigkeit so wohl des Verdünnungs-Reaktionsmittels als auch des Wassers ganz erheblich größer wird, und zwar so groß, daß sie sogar die zur Vernetzung erforderliche Geschwindigkeit übersteigt. Die Folge davon ist ein Erzeugnis, welches an der Oberfläche Narben und im Inneren Lunker sowie Risse zeigt, welche auf die Verdampfung des Verdünnungs-Reaktionsmittels zurückzuführen sind. Das auf diese Weise erhaltene Erzeugnis hat somit kein gefälliges Aussehen.If you increase the temperature, then ver the time required decreases very quickly, whereby however, the evaporation rate is the same probably the diluent as well as the water becomes considerably larger, and so large that it even exceeds the speed required for networking. The result of this is a product that is on the surface Scars and voids inside as well as cracks, which shows on the Evaporation of the diluent reagent attributed are. The product obtained in this way therefore has no pleasing appearance.
Aufgabe der Erfindung ist es daher, diese bekannte Methode so zu verbessern, daß das hierdurch gewonnene Erzeugnis in seiner Struktur fehlerfrei ist und ein gefälliges Aussehen zeigt.The object of the invention is therefore to make this known To improve the method so that the product thus obtained is flawless in its structure and pleasing to the eye shows.
Diese Aufgabe wird nach dem Oberbegriff des Anspruches 1 dadurch gelöst, daß die mit Harz als Binde mittel behandelte Platte oder der agglomierierte Block auf eine erhöhte Temperatur von über 100°C in einer Überdruck- Atmosphäre gebracht wird derart, daß ein Erzeugnis frei von Mängeln, wie von Oberflächen-Narben oder Innenrissen er halten und der Verfahrensablauf beschleunigt wird.This task is carried out according to the generic term of Claim 1 solved in that with resin as a bandage medium treated plate or the agglomerated block an elevated temperature of over 100 ° C in an overpressure Atmosphere is brought in such a way that a product is free of Defects such as surface scars or internal cracks hold and the process is accelerated.
Die zu behandelnden Platten kommen in der Vor richtung zur Durchführung des Verfahrens zwischen zwei Plat ten zu liegen, von welchen die eine Platte auf eine ganz be stimmte Temperatur aufgeheizt wird. Diese Platten liegen in einer unter Überdruck stehenden Kammer, in welcher die Ver dampfung des Verdünnungs-Reaktionsmittels verhindert wird, welches in dem als Bindemittel verwendeten Harz enthalten ist. Dabei wird gleichzeitig die Verdampfung des in der Platte u. dgl. enthaltenen Wassers verhindert. Das normalerweise austretende Wasser stellt einen erheblichen Nachteil dar, dem nur durch Einsatz von Platten mit kontrolliertem Feuch tigkeitsgehalt begegnet werden kann.The plates to be treated come first direction for performing the procedure between two plat ten, of which the one plate on a whole right temperature is heated. These plates are in a pressurized chamber in which the ver vaporization of the diluent is prevented, which is contained in the resin used as a binder. At the same time, the evaporation of the in the plate u. Contained water prevented. Usually escaping water is a significant disadvantage only by using panels with controlled moisture activity content can be met.
Das durch die erfindungsgemäße Methode erhaltene Erzeugnis weist keinerlei äußere Narben oder Innenlunker bzw. Innenrisse auf.The one obtained by the method according to the invention Product shows no external scars or voids or Internal cracks on.
Durch die erfindungsgemäße Methode wird der Nachteil der kleinen Vernetzungsgeschwindigkeit gegenüber der Verdampfungsgeschwindigkeit des Verdünnungs-Reaktions mittels und des Wassers - welche in dem Stein, also der zu behandelnden Platte enthalten ist - verhindert. Dies hat zur Folge, daß der Polymerisationsprozeß des Harzes bei vergleichsweise hohen Temperaturen erfolgt, so daß ein Erzeug nis erhalten wird, welches in einem jeden Falle frei von Mängeln ist, die bei einer zu schnellen Polymerisation zu verzeichnen sind.The method of the invention Disadvantage compared to the low networking speed the rate of evaporation of the dilution reaction by means of and the water - which in the stone, that is to say treating plate is included - prevented. This has the consequence that the polymerization process of the resin comparatively high temperatures, so that a production nis is received, which is in any case free of defects is to be noted if the polymerization is too rapid are.
Das erfindungsgemäße Verfahren sowie die Vorrich tung zu dessen Durchführung sind nachstehend anhand der Zeich nung veranschaulicht. In dieser zeigen in rein schematischer Weise:The inventive method and the Vorrich tion for its implementation are below with reference to the drawing illustrated. In this show in a purely schematic Wise:
Fig. 1 eine Ansicht der nach dem erfindungsge mäßen Verfahren hergestellten Platte oder Tafel, Fig. 1 is a view of the plate produced according to the method erfindungsge MAESSEN or panel,
Fig. 2 die zur Durchführung des erfindungsgemäßen Verfahrens vorgeschlagene Vorrichtung in der Offenstellung vor dem Beschicken mit der Platte bzw. Tafel, Fig. 2 shows the proposed device for performing the method according to the invention in the open position prior to feeding to the plate or panel,
Fig. 3 die zur Durchführung des erfindungsgemä ßen Verfahrens vorgeschlagene Vorrichtung in der Schließstellung bei eingesetzter Platte oder Tafel. Fig. 3 shows the device proposed for carrying out the method according to the invention in the closed position with the plate or panel inserted.
Wie die Fig. 2 der Zeichnung zeigt, besteht die Vorrichtung aus zwei Gehäusen 1, 2, von welchen zumindest das eine Gehäuse in senkrechter Richtung bewegbar ist, so daß eine gegenseitige Annäherung der beiden Gehäuse 1, 2 möglich ist.As shown in FIG. 2 of the drawing, the device consists of two housings 1 , 2 , of which at least one housing can be moved in the vertical direction, so that the two housings 1 , 2 can approach each other.
Die zu behandelnde Platte 4 oder Tafel stützt sich unter Einwirkung von in der Zeichnung nicht weiter dargestellten Mitteln auf eine Platte 5, die auf eine ganz bestimmte Temperatur aufheizbar ist.The plate 4 or plate to be treated is supported, under the action of means not shown in the drawing, on a plate 5 which can be heated to a very specific temperature.
Mit dem oberen Gehäuse 2 ist über elastische Mittel 6 eine bewegliche Platte 7 verbunden, welche ebenfalls auf eine ganz bestimmte Temperatur aufheizbar ist. Diese Platte 7 stützt sich in der Schließstellung der Vorrichtung auf die zu behandelnde Platte 4 oder Tafel auf.With the upper housing 2 , a movable plate 7 is connected via elastic means 6 , which can also be heated to a very specific temperature. This plate 7 is supported in the closed position of the device on the plate 4 or plate to be treated.
Wie die Fig. 3 der Zeichnung zeigt, liegt die zu behandelnde Platte 4 oder Tafel zwischen der Platte 7 und der unteren Platte 5. In dieser Stellung berühren die Ränder der beiden Gehäuse 1, 2 einander derart, daß sie beispielsweise mit Hilfe von Verschlüssen 8 und 9 einen geschlossenen Raum bilden. Der von den beiden Gehäusen 1, 2 eingeschlossene Raum wird über die Leitung 10 mit Druckluft beaufschlagt.As shown in FIG. 3 of the drawing, the plate 4 to be treated lies between the plate 7 and the lower plate 5 . In this position, the edges of the two housings 1 , 2 touch one another in such a way that they form a closed space, for example with the aid of closures 8 and 9 . The space enclosed by the two housings 1 , 2 is supplied with compressed air via line 10 .
In dieser Stellung und unter Berücksichtigung, daß die beiden Platten 5 und 7 auf eine über 100°C liegende Tem peratur aufgeheizt werden, ist der Vorgang der Polymerisation in einer außerordentlich kurzen Zeit von einigen wenigen Minu ten möglich.In this position and taking into account that the two plates 5 and 7 are heated to a temperature above 100 ° C., the process of polymerization is possible in an extremely short time of a few minutes.
Hierdurch weisen das Verdünnungs-Reaktionsmittel sowie das in dem Stein, also der Platte 4 enthaltene Wasser - welche nur einen geringen Dampfdruck aufweisen - einen gegenüber dem Außendruck höheren Druck auf und verflüchtigen deshalb nicht, weil deren Verdampfungsgeschwindigkeit kleiner ist als die Geschwindigkeit des Polymerisations-Prozesses.As a result, the dilution reagent and the water contained in the stone, that is to say the plate 4 - which have only a low vapor pressure - have a higher pressure than the external pressure and therefore do not evaporate because their rate of evaporation is lower than the rate of the polymerization process .
Das auf diese Weise erhaltene Produkt ist frei von Mängeln, welche normalerweise dann zu verzeichnen sind, wenn mit einer Temperatur gearbeitet wird, welche kleiner ist als die Umgebungstemperatur.The product obtained in this way is free of Defects that are usually noted when working with a temperature which is less than the ambient temperature.
Nach einer praktischen Verwirklichungsform der Vorrichtung zur Durchführung des erfindungsgemäßen Verfahrens kann diese an eine gleiche Vorrichtung angeschlossen werden, und zwar sowohl in senkrechter als auch in waagerechter Rich tung, so daß auf diese Weise diejenige Menge Druckluft reduziert werden kann, die zur Beaufschlagung einer jeden einzelnen Vor richtung erforderlich ist. In der Tat kann die der einen Vor richtung entnommene Druckluft zur Beaufschlagung der anderen Vorrichtung verwendet werden, was für die Gesamtbetriebskosten aber auch für die Geschwindigkeit des Betriebes vorteilhaft ist.According to a practical implementation of the Device for performing the method according to the invention can be connected to the same device, in both vertical and horizontal directions tion, so that that amount of compressed air is reduced can be used to act upon each individual front direction is required. Indeed, the one before Compressed air taken in the direction to act on the others Device used, what the total cost of ownership but is also advantageous for the speed of operation.
Claims (4)