DE3523000A1 - Metal foil which moulds on automatically for dental crown retainers - Google Patents
Metal foil which moulds on automatically for dental crown retainersInfo
- Publication number
- DE3523000A1 DE3523000A1 DE19853523000 DE3523000A DE3523000A1 DE 3523000 A1 DE3523000 A1 DE 3523000A1 DE 19853523000 DE19853523000 DE 19853523000 DE 3523000 A DE3523000 A DE 3523000A DE 3523000 A1 DE3523000 A1 DE 3523000A1
- Authority
- DE
- Germany
- Prior art keywords
- metal foils
- foils according
- metal
- foil
- folding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die dentale Metallkeramik erlaubt es, Zahnkronen herzustellen, die in Form und Farbe den natürlichen Zähnen täuschend echt nachgebildet werden können. Diese Art der Ersatzkronenherstellung beruht auf dem Prinzip der Anfertigung eines paßgenauen, thermisch und mechanisch festen Kronengerüstes, auf welches keramische Massen aufgebrannt werden.Dental metal ceramics make it possible to manufacture tooth crowns the shape and color of natural teeth can be reproduced deceptively real. That kind of Replacement crown production is based on the principle of manufacture a precise, thermally and mechanically stable Crown framework on which ceramic masses are fired will.
Das Kronengerüst wurde bisher überwiegend in Wachs modelliert und in Aufbrennlegierung gegossen. Ein neues Verfahren nach Dr. SHOHER beruht darin, Metallfolien als sternförmiges Schirmchen vorzufertigen und später mit Hilfe einer speziellen Faltpinzette, einem Rotierinstrument und einem Druck-Schlag-Formgerät in Kappenform dem Zahnstumpf manuell anzupassen.The crown framework has so far mainly been modeled in wax and cast in baked alloy. A new procedure after Dr. SHOHER is based on metal foils as star-shaped Prefabricate umbrellas and later with the help of a special folding tweezers, a rotary instrument and one Manual push-blow molding device in cap form adapt.
Die manuelle Umformung mittels einer Faltpinzette aber ist zeitraubend, erheblichen Schwankungen durch die individuelle Handhabung des Zahntechnikers unterworfen, verursacht ungleichförmige Faltenbildung, die zu einem hohen Verlust an mechanischer Festigkeit führt. Infolge zufälliger und kantiger Faltenbildung kommt es zu Spannungen in der Keramikmasse. Allgemein ist die Herstellungstoleranz durch verschiedene Zahntechniker sehr groß: werkstoffkundliche Untersuchungen zeigten, daß die umständliche Faltung von Hand aus den sternförmigen Schirm heraus zu ungleichförmigen Innenflächen führt, die keine planen Diffusionsflächen mehr bilden. Die anschließende Diffusionsverschmelzung der Reingoldschicht zu einer kompakten, geschlossenen Kappe gelingt häufig unvollständig. Randverformung, Paßungenauigkeit und Keramikabplatzen sind die Folgen.Manual forming using folding tweezers is time consuming, significant fluctuations due to the individual Subject to handling by the dental technician irregular wrinkling leading to a high loss mechanical strength leads. As a result of random and edgy wrinkling there is tension in the Ceramic mass. In general, the manufacturing tolerance is through various dental technicians very large: material science Investigations showed that the cumbersome folding by hand out of the star-shaped screen to non-uniform Leads to inner surfaces that no longer have flat diffusion surfaces form. The subsequent diffusion fusion of the pure gold layer to a compact, closed cap often incomplete. Edge deformation, inaccuracy and Ceramic chipping is the result.
Die vorliegende Erfindung verwendet vorgefertigte Metallfolien,
die sich von selbst dem Zahnstumpf anlegen, sobald
eine Kraft K außen auf sie einwirkt. Fig. 1.
Durch die automatische Anformung werden folgende Vorteile
erreicht:
1. reproduzierbare, vom Zahntechniker unabhängige Optimalform
der Folienkappe.
2. Konstante und gleichmäßige Verteilung der Falten und
damit gleichmäßige Anordnung der Vertikalstreben.
3. Ausschaltung jeglicher Kanten- und Spaltenbildung, d. h.
spannungsfreie Basis für die Keramik.
4. Reproduzierbare Bildung planer Kapillarfugen mit stets
fehlerfreier Diffusionsverschmelzung durch Reingold.
5. Zeitersparnis durch Wegfall des bisher erforderlichen
manuellen Faltens, Einschneidens und Anrotierens.The present invention uses prefabricated metal foils which automatically attach themselves to the tooth stump as soon as a force K acts on them on the outside. Fig. 1. The following advantages are achieved by the automatic shaping:
1. Reproducible, optimal form of the foil cap independent of the dental technician.
2. Constant and even distribution of the folds and thus even arrangement of the vertical struts.
3. Elimination of any edge and column formation, ie tension-free basis for the ceramic.
4. Reproducible formation of flat capillary joints with always flawless diffusion fusion by pure gold.
5. Time saving by eliminating the manual folding, cutting and spinning that was previously required.
Besonders bevorzugte Ausführung der erfindungsgemäßen Metallfolie zur selbstätigen Anformung an Zahnstümpfen und Zahnstumpfmodellen werden im folgenden beispielhaft beschrieben.Particularly preferred embodiment of the invention Metal foil for automatic molding on tooth stumps and Tooth stump models are exemplified below described.
Ihre Wirkungsweise beruht darauf, die vertikale Umformung einer vormals planen Scheibe bzw. Folie derart schleifenförmig zu gestalten (Fig. 2), daß die Basis einer inneren schleifenartigen Faltenreihe (1) auf dem Zahnstumpf aufliegt, während die Basis der analogen äußeren Reihe einem Anpreßdruck ausgesetzt wird (2).Their mode of operation is based on the fact that the vertical shaping of a previously flat disk or film is designed in the form of a loop ( FIG. 2) in such a way that the base of an inner loop-like fold row ( 1 ) rests on the tooth stump, while the base of the analog outer row is exposed to a contact pressure will ( 2 ).
Jede Art einer von außen einwirkenden Kraft K schiebt die derart vorgeformte Metallfolie automatisch und gleichförmig in sich zusammen. Sie legt sich dadurch von selbst der Zahnstumpfoberfläche (3) an, wobei präzise, stets lineare Faltfugen in exakt gleichen Abständen entstehen (Fig. 3). Die Anzahl der schleifenförmigen Falten mit äußerer und innerer Basisfläche richtet sich nach Größe und Umfang eines Zahnstumpfes (Fig. 4), wobei die Öffnungen zwischen den Basisflächen so bemessen sind, daß ein präzises Faltmuster entsteht. Any type of external force K automatically and uniformly pushes the metal foil preformed in this way together. As a result, it attaches itself to the tooth stump surface ( 3 ), with precise, always linear folding joints being formed at exactly the same intervals ( FIG. 3). The number of loop-shaped folds with an outer and inner base surface depends on the size and circumference of a tooth stump ( FIG. 4), the openings between the base surfaces being dimensioned in such a way that a precise folding pattern is produced.
In einer beispielhaft dargestellten anderen Ausführung (Fig. 5) sind die Zwischenräume so bemessen, daß ein doppeltes Faltband (5) oder eine einfache, bandartige Vertikalstrebe entsteht (6). In einer zusätzlich beispielhaft aufgeführten Anwendung (Fig. 6) sind die Schleifenfalten zwei- oder mehrschichtig angeordnet (7). Bei großem Umfang wird dadurch eine hohe Flexibilität und Verwandlungsfähigkeit erreicht.In another exemplary embodiment ( FIG. 5), the gaps are dimensioned in such a way that a double folding band ( 5 ) or a simple, band-like vertical strut is produced ( 6 ). In an additionally exemplary application ( FIG. 6), the loop folds are arranged in two or more layers ( 7 ). To a large extent, a high degree of flexibility and versatility is achieved.
Eine beispielhafte Art der erfindungsgemäßen Metallfolie besteht darin, daß die Innenflächen der Folie zusätzlich mit einem fließfähigen Metall-Reingold, Lot oder ein anderes Metall, welches bei geringerer Temperatur fließt als die Trägerfolie selbst - belegt, bestrichen, beschichtet, bedampft oder aufgalvanisiert ist. Dadurch entfällt der bisherige Arbeitsgang des Einschneidens einer manuell gefalteten Metallfolie.An exemplary type of the metal foil according to the invention consists in the fact that the inner surfaces of the film also with a flowable metal pure gold, solder or another Metal that flows at a lower temperature than that Carrier film itself - occupied, coated, coated, is vaporized or electroplated. This eliminates the previous operation of cutting a manually folded Metal foil.
Eine besonders bevorzugte Anwendungsform der selbstanformenden Metallfolie ist dadurch gekennzeichnet, daß in der ebenen Scheibe der Trägerfolie Fenster (8) eingestanzt sind. Diese kommen nach Prägung der Schleifenfalten in die inneren bzw. mittleren Verbindungslamellen zu liegen (Fig. 7). Diese Fenster dienen der Gewichts- und Materialersparnis, dem Durchfließen des Lotes, sie machen die Folie anschmiegsamer und reduzieren in ihrem Bereich die Gesamtschichtstärke (8).A particularly preferred form of application of the self-forming metal foil is characterized in that windows ( 8 ) are stamped into the flat pane of the carrier foil. After embossing the loop folds, these come to rest in the inner or middle connecting lamellae ( FIG. 7). These windows are used to save weight and material, to flow through the solder, they make the film more supple and reduce the total layer thickness in their area ( 8 ).
Bei einer weiteren Form der erfindungsgemäßen Metallfolien sind die Außenkanten der Faltschlaufen leicht abstehend angeordnet, daß sie bei Einsparung einer inneren Diffusionsschicht vor der automatischen Anformung eingeschnitten werden können, um ein Durchfließen des Lotes zu ermöglichen. Eine andere bevorzugte Ausführung der automatisch anformbaren Metallfolie ist dadurch gekennzeichnet, daß die vertikalen Schleifenfalten nur einen Teil des Kronenumfanges bedecken. Dadurch wird erreicht, daß auf der sichtbaren Hälfte das Kronengerüst maximal dünn ist, auf der nichtsichtbaren Seite (10) aber eine erhöhte Festigkeit entsteht (Fig. 8).In a further form of the metal foils according to the invention, the outer edges of the folding loops are arranged so that they protrude slightly so that they can be cut in before the automatic molding, so that the solder can flow through, while saving an inner diffusion layer. Another preferred embodiment of the automatically formable metal foil is characterized in that the vertical loop folds cover only a part of the crown circumference. It is thereby achieved that the crown framework is maximally thin on the visible half, but increased strength arises on the invisible side ( 10 ) ( FIG. 8).
Ein anderer beispielhafter Verwendungstyp der erfindungsgemäßen Metallfolie ist durch parallelogrammartige (11) Querschnittsform der Vertikalfalten gekennzeichnet (Fig. 9). Another exemplary type of use of the metal foil according to the invention is characterized by a parallelogram-like ( 11 ) cross-sectional shape of the vertical folds ( FIG. 9).
Bei einer anderen beispielhaften und besonders bevorzugten Ausführung werden zwei getrennte Metallfolien formidentisch ineinander geschoben (Fig. 10). Die eine Folie wirkt als mechanisch und thermisch festes Trägergerüst (12), die bevorzugt in einer Palladium-Platin-Iridiunm-Legierung ausgeführt wird. Die andere Folie besteht aus niederschmelzendem Metall - oder Metallegierung und bewirkt bei Wärmezufuhr, daß die selbstätig geschlossenen Faltfugen zu einem homogenen Gerüst verschmelzen (13).In another exemplary and particularly preferred embodiment, two separate metal foils are pushed into one another in an identical shape ( FIG. 10). One film acts as a mechanically and thermally stable support frame ( 12 ), which is preferably carried out in a palladium-platinum-iridium alloy. The other foil consists of a low melting metal or metal alloy and, when heated, causes the automatically closed folding joints to fuse into a homogeneous framework ( 13 ).
In einer weiteren Ausführungsform besteht die mechanisch und thermisch stabile Trägerfolie ausschließlich aus den Edelmetallen Gold und den Metallen der Palladiumreihe. Ein anderes Anwendungsbeispiel bevorzugt die Legierungszusammensetzung der Trägerfolie entsprechend der Patentanmeldung 34 47 413-7.In a further embodiment, the mechanical and thermally stable carrier film made exclusively of precious metals Gold and the metals of the palladium series. Another application example prefers the alloy composition the carrier film according to the patent application 34 47 413-7.
Eine stark bevorzugte Ausführungsform der erfindungsgemäßen Metallfolien zur selbstätigen Anformung an Zahnstümpfe ist dadurch gekennzeichnet, daß die Trägerfolie im Innern einer Verblendfolie oder bei Verwendung getrennter Träger- und Verschmelzfolie 0-100% Platin enthält und 0-20% Iridium und 0-70% Palladium.A highly preferred embodiment of the invention Metal foils for automatic molding on tooth stumps characterized in that the carrier film inside a Veneer film or when using separate carrier and Fusion foil contains 0-100% platinum and 0-20% iridium and 0-70% palladium.
Ein anderes bevorzugtes Anwendungsbeispiel ist dadurch bestimmt, daß die Trägerfolie neben den Edelmetallanteilen nichtedle Bestandteile in solchen Mengen enthält, daß ein Oxidhaftmechanismus mit der späteren Keramikschicht entsteht, z. B. Kupfer, Eisen, Iridium und Zinn.This is another preferred application example determines that the carrier film in addition to the precious metal contains non-noble components in such amounts that a Oxide adhesion mechanism with the later ceramic layer arises, e.g. B. copper, iron, iridium and tin.
Eine weitere bevorzugte Anwendungsform der selbstätig anformbaren Metallfolie enthält auf der Außenfläche Retentionsstrukturen z. B. Perlen, Splitter u. Netzstrukturen zur Verbindung mit dentalen Verblendwerkstoffen.Another preferred application form of the self-moldable Metal foil contains retention structures on the outer surface e.g. B. pearls, fragments and. Network structures for connection with dental veneering materials.
Eine andere Ausführungsform ist dadurch gekennzeichnet, daß die äußere Folie bzw. Folienschicht die Verbindung dentaler Kunststoffe mit Hilfe des Silanisierungsverfahrens ermöglicht.Another embodiment is characterized in that the outer film or film layer connects dental Allows plastics with the help of the silanization process.
Besonders bevorzugt wird die selbstätig anformbare Metallfolie in Verbindung mit einem vor oder nach erfolgter Anpressung einbringbaren Lot oder Mittel zur Verschmelzung aus Reingold oder einem Goldlot mit Gold 0-90%, Silber 0-75%, C u0-35% und Palladium 0-60%. The automatically formable metal foil is particularly preferred in conjunction with a before or after Pressable solder or means for fusion made of pure gold or a gold solder with gold 0-90%, silver 0-75%, C u0-35% and palladium 0-60%.
In einer anderen besonders bevorzugten Ausführungsform
besteht die mechanisch und thermisch stabile Trägerfolie aus
NEM-Legierung (Nichtedelmetall), in der Zusammensetzung
a. Nickelfrei
Co 30-80%, Cr 10-14%, Mo 1-10%, Ti 0-50%.
b. Nickel-Chrom-Legierung
Cr 5-30%, Ni 20-90%, Sonst. 0-20%.In another particularly preferred embodiment, the mechanically and thermally stable carrier film consists of non-precious alloy (base metal), in the composition
a. Nickel free
Co 30-80%, Cr 10-14%, Mo 1-10%, Ti 0-50%.
b. Nickel-chrome alloy
Cr 5-30%, Ni 20-90%, otherwise. 0-20%.
Eine weitere bevorzugte Anwendungsart ist speziell für ungleichförmige Zahnstümpfe und für sehr geringe Konizität. Sie besitzen in der horizontalen Kreisfläche ein Faltreservoir aus konzentrisch vorgeformten Ringfalten.Another preferred application is specifically for irregular tooth stumps and for very low taper. They have a folding reservoir in the horizontal circular area from concentrically preformed ring folds.
Eine andere beispielhafte Ausführungsform ist nicht rotationssysmmetrisch, vielmehr wurde ihre Querschnittsform dem Wurzelquerschnitt beschliffener Zähne angenähert. Hiermit wird eine noch einfachere und fehlerfreie automatische Anformung erreicht ohne die Gefahr unkontrollierbarer Faltenfügung.Another exemplary embodiment is not rotationally symmetrical, rather their cross-sectional shape became approximates the root cross-section of ground teeth. This will make it even easier and error-free automatic molding achieved without the risk of uncontrollable Folding.
Um einerseits eine vollständige Diffusionsverschmelzung zu erreichen, andererseits die Herstellung weiter zu vereinfachen, wird in einer weiteren bevorzugten Ausführungsform die ganze Trägerfolie mit einem einheitlichen, netzstrukturartigen Perforationsmuster durchsetzt, während die getrennte zweite Folie aus einer dünnen Schicht Feingold besteht. Die Feingoldfolie kann wahlweise als Innenfolie eingelegt oder außen aufgesetzt werden, je nachdem, ob eine biologische Neutralisierung der Trägerfolie zum Zahngewebe hin durch das Feingold erfolgen soll oder ob eine goldene Farbtonwärme auf der Außenfläche unter der Keramikmasse wirken soll.On the one hand to complete diffusion fusion achieve, on the other hand, to further simplify production, is in a further preferred embodiment the entire carrier film with a uniform, network structure-like Perforation pattern interspersed while the separated second foil consists of a thin layer of fine gold. The Fine gold foil can either be inserted as an inner foil or outside, depending on whether a biological Neutralization of the carrier film to the tooth tissue through the Fine gold should take place or whether a golden color warmth the outer surface should work under the ceramic mass.
Für besonders große Beanspruchung z. B. beim Brückenpfeiler wird in einer anderen sehr bevorzugten Anwendung das automatisch anformende Metallgerüst aus drei getrennten Folienschichten gebildet: eine äußere verschmelzbare Schicht mit goldenem Farbhintergrund für die Keramik, einer mittleren Schicht mechanischer und thermischer Standfestigkeit sowie einer inneren Schicht aus Feingold oder Lotlegierung.For particularly large loads e.g. B. at the bridge pier it becomes automatic in another very preferred application molded metal frame made of three separate layers of film formed: with an outer fusible layer golden color background for ceramics, a medium one Layer of mechanical and thermal stability as well an inner layer of fine gold or solder alloy.
Schließlich besteht eine weitere bevorzugte Anwendungsform der automatisch anformenden Metallfolien darin, daß das schleifenförmige Faltmuster erst im zahntechnischen Labor unter Verwendung einer Hilfsvorrichtung in eine ebene oder sonstwie vorgeformte Folie eingeprägt wird.Finally, there is another preferred application of the automatically forming metal foils in that the loop-shaped folding patterns only in the dental laboratory using an auxiliary device in a flat or otherwise, preformed foil is embossed.
Claims (20)