DE4340252A1 - Method of tooth restoration with aid of at least one screen layer - Google Patents
Method of tooth restoration with aid of at least one screen layerInfo
- Publication number
- DE4340252A1 DE4340252A1 DE19934340252 DE4340252A DE4340252A1 DE 4340252 A1 DE4340252 A1 DE 4340252A1 DE 19934340252 DE19934340252 DE 19934340252 DE 4340252 A DE4340252 A DE 4340252A DE 4340252 A1 DE4340252 A1 DE 4340252A1
- Authority
- DE
- Germany
- Prior art keywords
- partially
- layer
- veneer layer
- veneered
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
In den letzten Jahren sind die ästhetischen Anforderungen an medizinische Prothesen und Zahnersatz stark angestiegen. Die MehrzahI der z. B. direkt einsehbaren Zahnersatzoberflächen werden daher möglichst individuell zahnfarben gestaltet oder zahnfarben verblendet. Als Ver blendwerkstoffe haben sich aufgrund ihrer Beständigkeit im Mundmileu, ihrer Verschleiß stabilität und brillanten optischen Eigenschaften keramische Werkstoffe bewährt. Die üblicher weise verwendeten, silikatkeramischen Dentalporzellane bestehen zum größten Teil aus einer überwiegend amorphen Matrixphase aus Siliziumdioxid und einem geringen Anteil an zumeist oxidischen Füllstoffen, wie z. B. Aluminiumoxid, Magnesiumoxid oder Leuzit sowie anorgani schen Farbstoffen, wie z. B. Metalloxide. Sie liegen dem Zahntechniker in Form verschieden eingefärbter Pulversysteme vor.In recent years, the aesthetic requirements for medical prostheses and Dentures rose sharply. The MehrzahI of z. B. directly visible denture surfaces are therefore designed as individually as possible tooth colors or veneered tooth colors. As ver blend materials have become due to their resistance in the oral environment, their wear stability and brilliant optical properties of ceramic materials. The more common Silicate-ceramic dental porcelains used for the most part consist of one predominantly amorphous matrix phase made of silicon dioxide and a small proportion of mostly oxidic fillers, such as. As aluminum oxide, magnesium oxide or leucite and inorganic Dyes such as. B. metal oxides. The dental technician has different forms colored powder systems.
Zur individuellen Farbgebung der Zahnrestaurationen oder Prothesen erfolgt üblicherweise ein Farbabgleich am Patienten mit Hilfe von Farbmustern, wie sie z. B. in der DE 39 29 737 beschrieben sind. In den meisten Fällen geben die Farbmuster vom Hersteller festgelegte, kon fektionierte Farbabstufungen verschiedener Farbtöne vor und bestehen aus fertigungstechni schen Gründen häufig nicht aus denselben Werkstoffen, wie sie später zur Herstellung der Rekonstruktionen verwendet werden. Dies erschwert eine reproduzierbare, individuelle Farb rekonstruktion und führt nicht selten zu ästhetischen Mißerfolgen.For the individual coloring of the tooth restorations or prostheses, there is usually a Color matching on the patient with the help of color samples such as z. B. in DE 39 29 737 are described. In most cases, the color samples specified by the manufacturer, con prefabricated shades of different shades and consist of manufacturing technology reasons often not from the same materials as they were later used to manufacture the Reconstructions are used. This complicates a reproducible, individual color reconstruction and often leads to aesthetic failures.
Die technische Herstellung individueller keramischer Prothesenteile oder Zahnrestaurationen, wie z. B. Einlagefüllungen, Verblendschalen, Kronen, Brücken, Prothesen, künstlicher Zähne oder Epithesen erfolgt üblicherweise auf formtreuen, thermisch stabilen Einbettmassemodellen der zu rekonstruierenden Elemente, z. B. präparierter Zähne und/oder auf gerüstartig ausgebilde ten, metallischen oder keramischen Subkonstruktionen. Zur Verbesserung der Oberflächen haftung der Verblendporzellane an z. B. metallischen Gerüstkonstruktionen sowie zur Abdeckung der metallischen Grundfarben sind systemspezifische, flüssige oder pastöse Haftvermittler und/ oder Opakermassen bekannt.The technical production of individual ceramic prosthesis parts or tooth restorations, such as B. fillings, veneers, crowns, bridges, prostheses, artificial teeth or epitheses usually take place on true-to-shape, thermally stable investment models the elements to be reconstructed, e.g. B. prepared teeth and / or trained on a scaffold metallic, ceramic substructures. To improve the surfaces Adhesion of the porcelain to z. B. metallic scaffolding structures as well as covering the metallic basic colors are system-specific, liquid or pasty adhesion promoters and / or opaque masses known.
Nach manuellem Anmischen der mit Hilfe der Farbmuster vorausgewählten, verschieden einge färbten Kramikpulvern mit materialspezifischen Anmischflüssigkeiten, z. B. auf einer Glasplat te, werden die so erhaltenen Schlickermassen, z. B. mit Hilfe eines Pinsels, in den individuellen Farb- und Transparenzabstufungen schichtweise auf das Einbettmassemodell bzw. die Gerüst subkonstruktion aufgetragen und gebrannt. In einem ersten Schicht- bzw. Brandzyklus (Sinter temperatur) wird üblicherweise Porzellanmasse des ausgewählten Grundfarbtones aufgetragen, um einen ersten Substanzauftrag zu erreichen. In wenigstens einem darauffolgenden Schicht- bzw. Brandzyklus wird die Grobform unter weitgehender Berücksichtigung der individuellen Farbschattierungen und Transparenzabstufungen rekonstruiert, wobei größere Volumenab schnitte zur Steuerung der Volumenschwindung jeweils eingeschnitten und bis zur davor gebrannten Schicht separiert werden. Ein letzter Schicht- bzw. Sinterzyklus dient der Versiege lung der letzten Einschnitte, der funktionellen Gestaltung sowie der endgültigen Farb- und Transparenzanpassung.After manually mixing the preselected with the help of the color samples, put in different colored ceramic powders with material-specific mixing liquids, e.g. B. on a glass plate te, the slip materials thus obtained, e.g. B. with the help of a brush, in the individual Color and transparency gradations in layers on the investment model or the framework Substructure applied and fired. In a first layer or fire cycle (sinter temperature), porcelain paste of the selected basic color is usually applied, to achieve a first substance application. In at least one subsequent shift or fire cycle is the rough form taking into account the individual Color shades and gradations of transparency reconstructed, with larger volumes cuts to control the shrinkage in volume and cut up to the previous one fired layer can be separated. A final layer or sinter cycle is used for drying the last incisions, the functional design and the final color and Transparency adjustment.
Nach manueller Ausarbeitung und ggf. Formkorrektur auf dem Modellstumpf bzw. am Patienten wird die Restauration poliert und/oder unter Verwendung materialspezifischer, ggf. eingefärbter Glasurflüssigkeiten in einem Bemal- bzw. Glasurbrandzyklus bei Temperaturen geringfügig unterhalb der vorherigen Sintertemperaturen glasiert.After manual elaboration and, if necessary, shape correction on the model stump or on the patient the restoration is polished and / or using material-specific, possibly colored Slightly glaze liquids in a painting or glaze firing cycle at temperatures glazed below the previous sintering temperatures.
Die für die gebräuchlichen Sinterporzellane typische Verknüpfung der Formrekonstruktion mit der individuellen Farb- und Transparenzgestaltung, z. B. von Zahnrestaurationen, erfordert ein manuelles, schichtweises Auftragen verschieden eingefärbter Schlickermassen in mehreren Brandzyklen sowie Mindestschichtstärken von wenigstens 1 mm und resultiert, z. B. durch Phasenbildungen, Blaseneinschlüsse, Verunreinigungen und Initialrisse, in einer Vielzahl von fertigungsinduzierten Volumenfehlern, die zu einer wesentlichen Verringerung der Festigkeits kennwerte und der Zuverlässigkeit der Rekonstruktion führen.The linking of the form reconstruction typical for the common sintered porcelain with the individual color and transparency design, e.g. B. of tooth restorations, requires a manual, layer-by-layer application of differently colored slip masses in several Firing cycles as well as minimum layer thicknesses of at least 1 mm and results, e.g. B. by Phase formation, bubble inclusions, impurities and initial cracks, in a variety of Manufacturing-induced volume errors that lead to a substantial reduction in strength characteristics and the reliability of the reconstruction.
Die erforderlichen Mindestschichtstärken bedingen eine exzessive Präparation beispielsweise von Zahnstümpfen unter häufig restaurationsbedingt-iatrogener Entfernung gesunder Zahnhart substanz, was insbesondere im Unterkieferfrontzahngebiet oder bei jugendlichen Zähnen zu einer irreversiblen Traumatisierung der Zahnpulpa und möglicherweise sekundär erforderlichen Wurzelkanalbehandlungen führen kann.The required minimum layer thicknesses require excessive preparation, for example of tooth stumps with healthy tooth hardness, often due to restoration-related iatrogenic removal substance, which in particular in the mandibular anterior region or in adolescent teeth irreversible traumatization of the tooth pulp and possibly secondary Root canal treatments can lead.
Der analog vorausgewählter Farbschichtungen erfolgende, schichtweise Substanzauftrag ist durch die farbfremde Einfärbung der Porzellanschlickermassen sowie die erst nach dem Sinter vorgang hervortretenden Farberscheinungen der Keramikfarben, außerordentlich schwierig, zeitintensiv und erfordert hohe Erfahrungswerte des Technikers. Die endgültige Farbgestaltung ist zudem erst nach vollständiger Fertigstellung der Rekonstruktion; bei Verwendung eingefärb ter Glasurmassen erst nach Abschluß der Oberflächenglasur erkennbar.The layer-by-layer application of substance that occurs analogously to pre-selected color layers due to the color-neutral coloring of the porcelain slip masses and only after sintering color phenomena of the ceramic colors, extremely difficult, time-consuming and requires high experience of the technician. The final color scheme is also only after the completion of the reconstruction; colored when used The glaze can only be recognized after the surface glaze has been completed.
Farbkorrekturen ohne Veränderung der Zahnform sind nicht möglich und resultieren häufig in einer notwendigen Neuanfertigung keramischer Verblendungen oder vollkeramischer Restaura tionen.Color corrections without changing the tooth shape are not possible and often result in a necessary new production of ceramic veneers or all-ceramic restorations ions.
Zahntechnisch gebräuchliche, ggf. eingefärbte Glasurmassen oder Intensivfarben, wie sie z. B. als Flüssigkeiten oder Pasten zur individuellen Farbgestaltung von keramischen, insbesondere glaskeramischen Prothesenteilen oder Zahnersatz verwendet werden, bestehen aus einer flußmit telreichen, amorphen, weitgehend ungefüllten Feldspatmatrixstruktur mit anorganischen Farb stoffen. Aufgrund ihrer daraus resultierenden ausgeprägten Hydrolyseempfindlichkeit und hohen Säurelöslichkeit sowie ihrer lackartig dünnen, verfahrensspezifisch ungleichmäßigen Schicht starken sind herkömmliche Glasurschichten sowie dadurch erreichte Farbschattierungen im Mundmilieu wenig zeitstabil und nicht verschleißbeständig. Dental technically used, possibly colored glaze materials or intensive colors, such as z. B. as Liquids or pastes for the individual color design of ceramic, in particular Glass-ceramic prosthesis parts or dentures are used, consist of a flux rich, amorphous, largely unfilled feldspar matrix structure with inorganic color fabrics. Because of their resulting pronounced sensitivity to hydrolysis and high Acid solubility and its thin, varnish-like, process-specific uneven layer conventional glaze layers and the color shades achieved in this way are thicker Oral environment not very stable in time and not resistant to wear.
Die Erfindung löst die genannten Probleme durch den Gegenstand des Patentanspruches 1.The invention solves the problems mentioned by the subject matter of claim 1.
Die erfindungsgemäße fertigungstechnische Trennung zwischen der Formgestaltung der Rekon struktionen und deren endgültiger Farb- und/oder Transparenz- und/oder Oberflächengestaltung ermöglicht erstmals eine einfache, individuelle, reproduzierbare und korrigierbare ästhetische Gestaltung oder Oberflächenvergütung metallischer oder keramischer medizinischer Formkör per, insbesondere Zahnrestaurationen, z. B. aus Glaskeramiken, Oxidkeramiken, Nichtoxidkera miken, Verbundkeramiken mit oder ohne organischem Matrixanteil bzw. aus mundbeständigen Metallegierungen.The inventive separation between the shape of the Rekon structures and their final color and / or transparency and / or surface design enables a simple, individual, reproducible and correctable aesthetic for the first time Design or surface treatment of metallic or ceramic medical molded articles by, in particular tooth restorations, e.g. B. from glass ceramics, oxide ceramics, non-oxide ceramics miken, composite ceramics with or without organic matrix or from mouth-resistant Metal alloys.
Darüber hinaus können Sinterporzellanrestaurationen in einer vereinfachten Schichttechnik, z. B. in vorausgewählten, insbesondere monochromatischen Grundfarbtönen aufgebaut und erst nach der endgültigen Formgestaltung mit Hilfe der erfindungsgemäßen Verblendschichten farblich individuell gestaltet werden, was die Fertigungstechnik wesentlich vereinfacht sowie in einer Reduktion der festigkeitslimitierenden Volumenfehler und einer dadurch verbesserten Zuverläs sigkeit der Rekonstruktionen resultiert. Das beschriebene Verfahren bzw. die Vorrichtung ermöglicht ferner eine wesentliche Reduktion der Mindestschichtstärken, z. B. zahnfarbener Verblendungen, gegenüber herkömmlichen Porzellanschichttechniken und erlaubt daher ein substanzschonenderes Vorgehen, z. B. bei der Präparation von Zahnstümpfen.In addition, sintered porcelain restorations can be made using a simplified layering technique, e.g. B. built up in preselected, especially monochromatic basic colors and only after the final shape with the help of the veneer layers according to the invention in color be individually designed, which significantly simplifies the manufacturing technology and in one Reduction of the volume errors that limit the strength and thus an improved reliability reconstruction results. The described method and the device also enables a significant reduction in the minimum layer thicknesses, e.g. B. tooth-colored Facing, compared to conventional porcelain layering techniques and therefore allows one more substance-conserving procedure, e.g. B. in the preparation of tooth stumps.
Erfindungsgemäß können sämtliche Formteiloberflächen farblich individuell gestaltet und/oder vergütet werden, insbesondere bei Zahnrestaurationen die äußeren funktionellen Oberflächen und/oder die inneren defektzugewandten bzw. stumpfseitigen Oberflächen oder nur einzelne Segmente bzw. Abschnitte dieser Oberflächen, wie z. B. die direkt einsehbaren Oberflächen des Front- und vorderen Seitenzahngebietes oder einer Augenprothese. Außerdem können bei schichtweiser Verarbeitung von Sinterporzellanen im Rahmen ihrer Herstellung auch beliebige Zwischenschichten der zu fertigenden Rekonstruktion, wenigstens partiell, mit den erfindungs gemäßen Verblendschichten versehen werden.According to the invention, all molded part surfaces can be individually designed and / or colored the outer functional surfaces, especially in tooth restorations and / or the inner surfaces facing the defect or the die side or only individual surfaces Segments or sections of these surfaces, such as. B. the directly visible surfaces of the Anterior and posterior posterior region or an eye prosthesis. In addition, at layer-by-layer processing of sintered porcelain in the course of their manufacture also any Intermediate layers of the reconstruction to be manufactured, at least partially, with the invention appropriate veneer layers.
Selbstverständlich kann die erfindungsgemäße Individualisierung auch mehrfach nacheinander erfolgen und/oder mit anderen konventionellen Methoden der individuellen Porzellan schichttechnik und/oder der Verwendung von Intensivfarben und/oder ggf. eingefärbten Glasur massen kombiniert werden und/oder zur Farbkorrektur von z. B. herkömmlich gefertigten Rekonstruktionen eingesetzt werden.Of course, the individualization according to the invention can also be carried out several times in succession done and / or with other conventional methods of individual porcelain layering technology and / or the use of intensive colors and / or colored glaze if necessary masses are combined and / or for color correction of z. B. conventionally manufactured Reconstructions are used.
Darüber hinaus ermöglicht die Erfindung eine neue, vorteilhafte Ausgestaltung und Herstellungs technik von Farbmustern zur Farb- und/oder Transparenzauswahl, insbesondere für zahnfarbene Keramik- oder Kunststoffrestaurationen, die auf die erfindungsgemäße Vorrichtung bzw. Verfahren, auf konventionelle Porzallanschicht- oder Glasursysteme oder auf dentale Polymer komposits abgestimmt sind.In addition, the invention enables a new, advantageous embodiment and manufacture technology of color samples for color and / or transparency selection, especially for tooth-colored Ceramic or plastic restorations based on the device or Processes, on conventional Porzallanschicht- or glaze systems or on dental polymer composites are matched.
Die erfindungsgemäße Farb- und/oder Transparenzgestaltung bzw. Oberflächenvergütung er folgt durch wenigstens partielles Auftragen wenigstens einer Verblendschicht auf die umzuge staltenden Oberflächen bzw. Oberflächenabschnitte eines Formteiles, wie z. B. einer Zahnrestau ration oder Prothese oder deren Fertigungsvorstufen. Die Verblendschicht kann entweder im Rahmen der Herstellung der Formteile auf bzw. in die Rekonstruktion auf- bzw. eingebracht werden und zusammen mit den Keramikmassen und/oder Intensivfarbmassen und/oder Glasur massen gebrannt oder nach dem Auftragen auf eine bereits verfestigte, z. B. gebrannte Keramik oberfläche oder Metalloberfläche gebrannt und/oder zuvor, z. B. durch Polymerisation einzelner Bestandteile wenigstens teilweise erhärtet werden. Selbstverständlich können auch mehrere Verblendschichten gleichzeitig auf die zu verblendenden Oberflächen aufgebracht, ggf. teilweise erhärtet und/oder gebrannt werden.The color and / or transparency design or surface treatment according to the invention follows by at least partially applying at least one veneer layer to the move shaping surfaces or surface sections of a molded part, such as. B. a tooth rest ration or prosthesis or their pre-production stages. The veneer layer can either be in Frame of the manufacture of the molded parts on or in the reconstruction and together with the ceramic materials and / or intensive color materials and / or glaze mass burned or after application to an already solidified, e.g. B. fired ceramics burned surface or metal surface and / or previously, e.g. B. by polymerization of individual Components are at least partially hardened. Of course, several can Facing layers applied simultaneously to the surfaces to be veneered, if necessary partially hardened and / or burned.
Besonders eignet sich die erfindungsgemäße Verblendschicht zur individuellen Farb- und/oder Transparenzgestaltung und/oder Oberflächenvergütung von vollkeramischen oder keramisch zu verblendenden bzw. verblendeten medizinischen Formkörpern, insbesondere Zahnrestauratio nen. Die Gestaltung wenigstens partieller Farb- und/oder Transparenz- und/oder Opazitätseffekte und/oder reproduzierbarer, z. B. mechanischer, tribologischer, chemischer, elektrostatischer (z. B. Zeta-Potential) Oberflächeneigenschaften ist möglich. Dadurch kann z. B. die Belagbildung auf intraoralen Oberflächen und/oder der Verschleiß antagonistischer Zahnoberflächen und/oder die Festigkeit vollkeramischer Restaurationen, z. B. durch Ausbildung oberflächlicher Druckspan nungen und/oder durch Reaktion mit Ormoceren, günstig beeinflußt werden.The veneer layer according to the invention is particularly suitable for individual color and / or Transparency design and / or surface treatment of all-ceramic or ceramic too veneering or veneered medical moldings, in particular tooth restoration nen. The design of at least partial color and / or transparency and / or opacity effects and / or reproducible, e.g. B. mechanical, tribological, chemical, electrostatic (e.g. Zeta potential) surface properties is possible. This can, for. B. the formation of deposits intraoral surfaces and / or the wear of antagonistic tooth surfaces and / or the Solid all-ceramic restorations, e.g. B. by training superficial chip tions and / or by reaction with Ormoceren, can be influenced favorably.
In einer weiteren Anwendungsvariante ist die erfindungsgemäße Verblendschicht als Haftver mittlerschicht und/oder Opakerschicht und/oder zahnfarbene Verblendschicht unter möglicher Zugabe von metallischen Zusätzen, insbesondere legierungsspezifischen Metallpartikeln, ausge bildet und dient zur Verblendung metallischer Formkörper, obgleich dadurch auch keramische Formkörper wenigstens partiell mit metallischen Oberflächen versehen werden können. Als Haft vermittlersysteme ausgebildete Verblendschichten enthalten materialspezifische Zusätze, die als materialähnliche Substrate wenigstens teilweise in den zu verblendenden Oberflächen und den aufzubringenden Schichten enthalten sind. Geeignete Haftvermittlerverblendschichten zur Kera mik- oder Polymerkomposit-Verblendung metallischer Formteile, insbesondere wenig oxidbil denden Edelmetalle (z. B. Feingold), enthalten vorzugsweise metallische und keramische, z. B. silikatische Partikel.In a further application variant, the veneer layer according to the invention is used as an adhesive middle layer and / or opaque layer and / or tooth-colored veneer layer under possible Addition of metallic additives, especially alloy-specific metal particles forms and serves for veneering metallic moldings, albeit ceramic ones Moldings can be provided at least partially with metallic surfaces. As a detention mediator systems trained veneer layers contain material-specific additives, which as material-like substrates at least partially in the surfaces to be veneered and layers to be applied are included. Suitable adhesion promoter veneers for Kera Mic or polymer composite veneering of metallic moldings, especially little oxide precious metals (e.g. fine gold), preferably contain metallic and ceramic, e.g. B. silicate particles.
Weitere Ausführungsvarianten dieser Anwendung sind "Opakerschichten" zur farblichen Abdeckung von Metalloberflächen, beispielsweise mit erfindungsgemäßen, zahnfarbenen Ver blendschichten bzw. durch konventionelle Verblendmethoden mit individuell eingefärbten Polymerkomposits oder Porzellanmasse. Selbstverständlich sind Kombinationen dieser Schich ten zu mehrphasigen Verblendschichten möglich, wie z. B. eine vorteilhafte Kombination z. B. legierungsspezifischer Opakerschichten mit zahnfarbenen Verblendschichten und/oder Haftver mittlerschichten.Other variants of this application are "opaque layers" for color Covering of metal surfaces, for example with tooth-colored ver according to the invention blend layers or by conventional veneering methods with individually colored Polymer composites or porcelain paste. Combinations of this layer are of course possible for multi-phase veneer layers, such as. B. an advantageous combination z. B. alloy-specific opaque layers with tooth-colored veneer layers and / or adhesive middle classes.
Darüber hinaus ist eine wenigstens teilweise metallische Verblendung metallischer Formelemen te, wie z. B. Nichtedelmetallrestaurationen, z. B. mit Edelmetallpartikeln und/oder keramischen Partikeln enthaltenden Verblendschichten möglich, wodurch insbesondere in Kontaktbereichen zu anderen Metallrestaurationen, wie z. B. Edelmetallrestaurationen, die Ausbildung elektro chemischer Lokalelemente im Mundmilieu reduziert bzw. verhindert werden kann.In addition, an at least partially metallic veneer of metallic formula elements te, such as B. base metal restorations, e.g. B. with precious metal particles and / or ceramic Particle-containing veneer layers possible, which means in particular in contact areas to other metal restorations, e.g. B. precious metal restorations, training electro chemical local elements in the oral environment can be reduced or prevented.
Im Gegensatz zu herkömmlichen, flüssigen oder pastenartigen, ggf. eingefärbten Glasurmassen oder Intensivfarben, die erst nach dem Auftragen und Einbrennen auf den zu verblendenden Ober flächen, insbesondere Keramikoberflachen, als meist ungleichmäßige, dünne Schicht vorliegen, ist die erfindungsgemäße Verblendschicht bereits vor dem Auftragen oder Einbrennen wenig stens teilweise vorhanden und/oder formstabil und/oder verformbar und/oder bezüglich ihrer geometrischen Form und/oder Schichtstärke und/oder Farb- und/oder Transparenzabstufung definiert.In contrast to conventional, liquid or paste-like, possibly colored glaze materials or intensive colors, which are only applied and burned onto the surface to be veneered surfaces, in particular ceramic surfaces, as a mostly non-uniform, thin layer, the veneer layer according to the invention is little even before application or baking at least partially present and / or dimensionally stable and / or deformable and / or with respect to them geometric shape and / or layer thickness and / or color and / or transparency gradation Are defined.
Die Verblendschicht(en) kann (können) in beliebigen, anwendungsspezifischen geometrischen Formen oder Schichtstärken, mit auf die zu verblendenen Materialien abgestimmten, werkstoff spezifischen Zusammensetzungen und Eigenschaften, insbesondere als Konfektionselement(e) vorliegen. Zur Verblendung von Zahnrestaurationen eignen sich insbesonders zahnformähnliche geometrische Ausbildungsformen der Verblendschicht(en) in der Größenordnung eines natürli chen Zahnes und/oder zahnsegmentähnliche, wie z. B. zahnhalsähnliche, zahnkörperähnliche oder zahnschneideähnliche Verblendschicht(en) in ähnlicher Größe und/oder kreisrunde Verblendschicht(en) mit einem Durchmesser in der Größenordnung einer mittleren Zahnbreite.The veneer layer (s) can be in any application-specific geometric Forms or layer thicknesses, with material matched to the materials to be veneered specific compositions and properties, especially as a ready-made element (s) available. Tooth restorations are particularly suitable for veneering dental restorations Geometric forms of formation of the veneer layer (s) in the order of a natural Chen tooth and / or tooth segment-like, such as. B. tooth neck-like, tooth body-like or veneer-like veneer layer (s) of similar size and / or circular Facing layer (s) with a diameter in the order of a medium tooth width.
Erfindungsgemäß besteht die Verblendschicht wenigstens teilweise aus wenigstens einem Trägerelement mit wenigstens teilweise anhaftenden und/oder eingebrachten Substraten, wie z. B. Farbstoffen oder keramischen Flußmitteln oder Glasurbestandteilen, die für die farbliche Individualisierung und/oder Oberflächenvergütung von keramischen oder metallischen, insbe sondere silikatkeramischen oder oxidkeramikenthaltenden Oberflächen geeignet sind.According to the invention, the veneer layer consists at least partially of at least one Carrier element with at least partially adhering and / or introduced substrates, such as e.g. B. dyes or ceramic fluxes or glaze constituents for the colored Individualization and / or surface treatment of ceramic or metallic, esp special silicate ceramic or oxide ceramic surfaces are suitable.
In einer bevorzugten Ausführungsvariante ist das Trägerelement als Folie oder Gewebe oder als Kombination derselben ausgebildet. Erfindungsgemäße Trägerelemente und/oder Verblend schichten können entweder definierte gleichmäßige und/oder abgestufte Schichtstärken aufwei sen, die vorteilhaft unter 1 mm liegen, besonders vorteilhaft unter 500 µm und ganz besonders bevorzugt zwischen 10 µm und 300 µm.In a preferred embodiment variant, the carrier element is in the form of a film or fabric or Combination of the same trained. Carrier elements and / or veneer according to the invention Layers can either have defined uniform and / or graded layer thicknesses sen, which are advantageously less than 1 mm, particularly advantageously less than 500 µm and very particularly preferably between 10 µm and 300 µm.
Geeignete Trägerelemente bestehen aus einem zur manuellen Handhabung sowie zur Infiltration der Substrate, insbesondere der Farbstoffe geeigneten Material. Besonders vorteilhaft sind wenig stens teilweise elastische oder verformbare Gewebe, die eine faltenfreie Adaptation der Verblend schichten auch auf z. B. unregelmäßig geformten Oberflächen, wie z. B. Zahnoberflächen, insbe sondere im Kauflächenbereich ermöglichen. Nach ihrer Applikation auf die zu verblendenen Oberflächenbereiche bleibt(en) die Trägerelement(e) in situ stabil und/oder können wenigstens teilweise, insbesondere durch interne Vernetzungsreaktionen (z. B. Polymerisation) oder durch Reaktion mit der zu verblendenden Oberfläche und/oder unter wenigstens partieller Verwendung wenigstens eines weiteren Substrates ausgehärtet werden. Nach thermischer Behandlung im Rahmen des Einbrennens der auf die Formkörperoberfläche aufgebrachten Verblendschicht(en), bevorzugt bei Temperaturen zwischen 200°C und 1400°C, insbesondere zwischen 400°C und 1100°C und ganz besonders bevorzugt zwischen 400°C und 950°C, verbrennt (verbrennen) das(die) Trägerelement(e) entweder rückstandsfrei und/oder wenigstens einzelne Bestandteile der(s) Trägerelemente(s) und/oder thermische Spaltprodukte und/oder Reaktionsprodukte kön nen mit den zu verblendenen Oberflächen reagieren und/oder teilweise an die neuentstandenen Oberflächenschichten angelagert und/oder in diese eingebaut werden.Suitable carrier elements consist of one for manual handling and for infiltration the substrate, in particular the material suitable for dyes. Little is particularly advantageous Mostly elastic or deformable fabrics that allow for a wrinkle-free adaptation of the veneer layers on z. B. irregularly shaped surfaces such. B. tooth surfaces, esp enable especially in the occlusal area. After their application to be veneered Surface areas, the support element (s) remains stable in situ and / or at least can partly, in particular by internal crosslinking reactions (e.g. polymerization) or by Reaction with the surface to be veneered and / or with at least partial use at least one further substrate are cured. After thermal treatment in Frame of baking the veneer layer (s) applied to the molded body surface, preferably at temperatures between 200 ° C and 1400 ° C, in particular between 400 ° C and 1100 ° C and very particularly preferably between 400 ° C and 950 ° C, burns (burn) the carrier element (s) either residue-free and / or at least individual components the carrier element (s) and / or thermal fission products and / or reaction products react with the surfaces to be veneered and / or partially to the newly created ones Surface layers are attached and / or built into them.
Besonders eigenen sich wachsartige oder kunststoffartige Trägerelemente. Ganz besonders bewährt haben sich wenigstens teilweise aus Polyestergeweben oder thermisch- oder photopoly merisierbaren Acrylatkunststoffen bestehende Trägerelemente, die beim Einbrennen bzw. Sintern der Schicht weitgehend rückstandsfrei verbrennen. Andere Substrate und oder Bestand teile alternativer Trägerelemente sind z. B. wenigstens teilweise Si-haltige Kunststoffe, wie z. B. Polysiloxane, die wenigstens teilweise, z. B. unter reaktiven Atmosphären, reaktionsgesintert oder pyrolysiert oder wenigstens teilweise in die Oberfläche mit eingebaut werden, wodurch sekundäre Oberflächenmatrixbestandteile eingebracht werden können, was beispielsweise in einer Optimierung des Verschleißverhaltens, der Hydrolysestabilität und durch Ausbildung oberflächennaher Druckspannungszonen innerhalb des verblendeten Formkörpers in einer Festigkeitserhöhung der Rekonstruktion resultieren kann.Wax-like or plastic-like carrier elements are particularly suitable. Most notably have proven themselves at least partially from polyester fabrics or thermal or photopoly merisable acrylic plastics existing carrier elements, which when baked or Burn the sintering of the layer largely without residue. Other substrates and or stock parts of alternative support elements are e.g. B. at least partially Si-containing plastics, such as. B. Polysiloxanes, at least partially, e.g. B. under reactive atmospheres, reaction sintered or pyrolyzed or at least partially incorporated into the surface, whereby secondary surface matrix components can be introduced, for example in optimization of wear behavior, hydrolysis stability and through training near-surface compressive stress zones within the veneered molded body in one Strengthening of the reconstruction can result.
Das (die) Trägerelement(e) werden wenigstens teilweise mit anorganischen, insbesondere kera mischen Farbstoffen oder Farbpartikeln, wie z. B. Metalloxiden und/oder Trübungsmitteln benetzt oder infiltriert. Insbesondere eigenen sich definierte Gemenge unterschiedlicher anorga nischer Farbstoffe bzw. Farbpartikel oder Trübungsmittel, die in anwendungsspezifisch definier ten Konzentrationen sowie unter anwendungsspezifisch reproduzierbarer Verteilung auf und/ oder in das Trägerelement eingebracht werden und nach Applikation derartiger Verblendschich ten auf keramische oder metallische Elemente mit definierten Form-, Material- und optischen Eigenschaften, bei definierten Brandführungen unter wenigstens teilweiser Verbrennung bzw. Umsetzung des Trägerelementes, reproduzierbare Farbeffekte ergeben. Zur individuellen Ver blendung von z. B. Zahnrestaurationen hat sich ein Set von unterschiedlichen, insbesondere reproduzierbar zahnfarben eingefärbten Verblendschichten bewährt.The (the) support element (s) are at least partially with inorganic, in particular kera mix dyes or color particles, such as. B. metal oxides and / or opacifiers wetted or infiltrated. Defined mixtures of different anorga are particularly suitable African dyes or color particles or opacifiers, which are defined in application-specific concentrations and under application-specific reproducible distribution on and / or can be introduced into the carrier element and after application of such veneer layer on ceramic or metallic elements with defined shape, material and optical Properties, with defined fire management under at least partial combustion or Implementation of the carrier element, reproducible color effects result. For individual ver glare from z. B. Tooth restorations has become a set of different ones, in particular reproducible tooth-colored veneers proven.
Es hat sich weiterhin bewährt das Trägerelement zusätzlich mit organischen Farbstoffen und/ oder Trübungsmitteln zu benetzten bzw. zu infiltrieren, die bzgl. ihrer Verteilung und/oder ihrers optischen Erscheinungsbildes vor dem Einbrennen der Verblendschicht auf die Farb- bzw. Transparenzeffekte der anorganischen Farb- bzw. Trübungsmittel nach dem Einbrennen der Verblendschicht abgestimmt sind und dadurch das optische Erscheinungsbild der Verblend schicht bereits vor deren thermischer Behandlung simmulieren. Dadurch kann die Farbanpassung eines zu verblendeten Elementes, in einem noch "reversiblen" Zustand, nach dem Auftragen und vor dem Einbrennen der Verblendschicht kontrolliert und ggf. durch wenigstens teilweises Auf bringen einer anderen und/oder zusätzlichen Verblendschicht optimiert werden. Die organischen Farbstoffe verbrennen, z. B. beim endgültigen Einbrennen bzw. Sintern der Verblendschicht, rückstandsfrei.The carrier element has also proven useful with organic dyes and / or to infiltrate or infiltrate opacifiers with regard to their distribution and / or theirs optical appearance before baking the veneer on the color or Transparency effects of the inorganic color or opacifying agents after baking Veneer layer are matched and thus the visual appearance of the veneer simulate the layer before its thermal treatment. This allows the color adjustment of an element to be veneered, in a "reversible" state, after application and checked before the veneering layer is baked and, if necessary, by at least partially opening bring another and / or additional veneer layer can be optimized. The organic Burn dyes, e.g. B. in the final baking or sintering of the veneer layer, residue-free.
Weitere anwendungsspezifische und verarbeitungserleichternde Zusätze der Verblendschichten, mit denen das Trägerelement wenigstens teilweise beschickt werden kann und die nach der thermischen Behandlung wenigstens teilweise an den erfindungsgemäß verblendeten Ober flächen anhaften und/oder in diese bzw. in Oberflächenrandzonen eingebaut werden, sind keramische Flußmittel, insbesondere Boride oder Feldspäte, z. B. zur Einstellung der Einbrenn temperaturbereiche, zur Oberflächenverglasung sowie zur Optimierung der Verbindung zu den verblendeten Substratoberflächen.Other application-specific and processing-facilitating additives for the veneer layers, with which the carrier element can be at least partially loaded and which after thermal treatment at least partially on the upper veneered according to the invention stick to surfaces and / or are built into these or in surface edge zones ceramic fluxes, especially borides or feldspars, e.g. B. to adjust the burn-in temperature ranges, for surface glazing and to optimize the connection to the veneered substrate surfaces.
Darüber hinaus können insbesondere die Oberflächeneigenschaften der erfindungsgemäß verblendeten Rekonstruktionen, z. B. durch Zugabe von silikatischen Matrixbestandteilen, Partikeln, Fasern, Ariosilen, oder anderen geeigneten Füllstoffen, insbesondere oxid- und/oder silikatkeramischen Füllstoffen oder Glasurbestandteilen auf bzw. in das Trägerelement, die ebenfalls nach thermischer Behandlung der verblendeten Oberflächen wenigstens teilweise an diese angelagert und/oder eingebaut werden, anwendungsspezifisch optimiert werden. In addition, in particular the surface properties of the invention veneered reconstructions, e.g. B. by adding silicate matrix components, Particles, fibers, ariosils, or other suitable fillers, in particular oxide and / or silicate ceramic fillers or glaze components on or in the carrier element, the also at least partially after thermal treatment of the veneered surfaces these are attached and / or installed, optimized for specific applications.
Zur besseren Handhabung kann das Trägerelement vor oder nach seiner Benetzung bzw. Infiltration, z. B. mit den o.g. Farbstoffen und/oder Zusätzen, mit einem anwendungsspezifisch, beliebig ausgestalteten Halteelement verbunden werden. Besonders geeignet sind folienartige oder papierartige Halteelemente, auf die oder die auf das Trägerelement bevorzugt vor seiner Imprägnierung aufgebracht werden.For better handling, the carrier element can be before or after wetting or Infiltration e.g. B. with the above Dyes and / or additives, with an application-specific, arbitrarily designed holding element can be connected. Foil-like ones are particularly suitable or paper-like holding elements, on which or on the carrier element preferably in front of it Impregnation can be applied.
Die Benetzung und/oder Imprägnierung erfolgt, z. B. in herkömmlichen drucktechnischen Ver fahren, wobei die Zusatzstoffe, insbesondere die Farbstoffe, wenigstens aber die organischen Farbstoffe bevorzugt auf das Halteelement durchgedruckt werden, was die Handhabung im Rahmen der Farbauswahl durch einen Betrachter wesentlich vereinfacht.The wetting and / or impregnation takes place, for. B. in conventional printing Ver drive, the additives, especially the dyes, but at least the organic Dyes are preferably printed on the holding element, which is the handling in Frame of the color selection by a viewer is considerably simplified.
Geeignete, anwendungsspezifische Halteelemente bestehen wenigstens zum Teil aus Zellstoff, Papier oder Kunststoff oder aus keramischen oder metallischen Elementen bzw. Folien. Zur Ver blendung von Zahnrestaurationen haben sich insbesondere etwa papierartige oder aus Kunststoff bestehende Halteelemente und die Ausbildung der Verblendschicht(en) als Schiebe- bzw. Abziehbild(er) bewährt. Andere Ausführungsvarianten sind z. B. in ein etwa ringartiges Gebilde, z. B. einen Kunststoffring, der wenigstens geringfügig größer als die zu verblendenen Oberflächen ausgebildet ist, eingebrachte Verblendschichten - mit oder ohne zusätzliche(s) Halteelement(e), wie z. B. Schutzfolie(n) - die z. B. im Tiefziehverfahren auf die zu verblendende(n) Oberfläche(n) aufgebracht wird (werden) Ferner sind wenigstens teilweise metallisch eingefärbte oder metal lische Halteelemente zur Aufnahme von Verblendschichten für zu verblendende metallische Oberflächen gut geeignet, da diese den optischen Effekt der zu verblendenden Metalloberfläche bereits bei der Betrachtung der Verblendschicht simmulieren.Suitable, application-specific holding elements consist at least in part of cellulose, Paper or plastic or from ceramic or metallic elements or foils. Ver Glare from tooth restorations have become especially paper-like or plastic existing holding elements and the formation of the veneer layer (s) as sliding or Decal (s) proven. Other design variants are e.g. B. in an approximately ring-like structure, e.g. B. a plastic ring that is at least slightly larger than the surfaces to be veneered veneered layers - with or without additional holding element (s), such as B. protective film (s) - the z. B. in the deep-drawing process on the surface (s) to be veneered is (are) also at least partially metallic or colored lische holding elements for receiving veneer layers for metallic to be veneered Surfaces well suited, as these have the optical effect of the metal surface to be veneered simulate when looking at the veneer layer.
Je nach Zusammensetzung und Oberflächenausgestaltung der zu verblendenden Oberfläche(n) ist es ggf. erforderlich diese vor dem Aufbringen der Verblendschicht mechanisch und/oder chemisch zu konditionieren. Geeignete Methoden zur Oberflächenkonditionierung metallischer oder keramischer Oberflächen sind Diamantbearbeitung, Sandstrahlen, z. B. mit Aluminiumoxid korn einer Korngröße unterhalb 250 µm sowie mit Drücken unterhalb 6 bar, Silikat- bzw. Si-Anreicherung im Bereich der Oberflächenrandzone, z. B. während des Sandstrahlens mit speziellen Korngemengen oder im Sol-Gel-Verfahren, oder chemische Konditioniermethoden, insbesondere Ätzen mit sauren oder alkalischen Lösungen, z. B. Flußsäurelösungen oder Ammoniumbifluoridlösungen.Depending on the composition and surface design of the surface (s) to be veneered it may be necessary to mechanically and / or before applying the veneer layer to chemically condition. Suitable methods for surface conditioning of metallic or ceramic surfaces are diamond processing, sandblasting, e.g. B. with alumina grain of a grain size below 250 µm and with pressures below 6 bar, silicate or Si enrichment in the area of the surface edge zone, e.g. B. during sandblasting special grain batches or in the sol-gel process, or chemical conditioning methods, especially etching with acidic or alkaline solutions, e.g. B. hydrofluoric acid solutions or Ammonium bifluoride solutions.
Darüber hinaus kann es vorteilhaft sein die Verblendschichten, unter wenigstens partieller Verwendung wenigstens eines zusätzlichen Substrates, auf die zu verblendenden Oberflächen aufzubringen, und/oder zu adaptieren und/oder zu verfestigen. Insbesondere eigenen sich Flüssigkeiten, Gele oder Pasten, wie z. B. Wasser, Alkohole, polare oder nichtpolare Lösungsmittel, Kunststoffe oder Klebesubstanzen, etc. Diese können bei der thermischen Behandlung der mit der erfindungsgemäßen Verblendschicht überschichteten Formkörper - entweder rückstandsfrei verdampfen, verbrennen oder mit Bestandteilen der Formkörper- und/ oder Verblendschichtoberflächen und/oder mit Spalt- und/oder Reaktionsprodukten wenigstens teilweise reagien und/oder in die Oberflächenschicht wenigstens teilweise eingebaut werden.In addition, it can be advantageous to veneer the layers, at least partially Use of at least one additional substrate on the surfaces to be veneered to apply, and / or to adapt and / or to solidify. Particularly suitable Liquids, gels or pastes, e.g. B. water, alcohols, polar or non-polar Solvents, plastics or adhesive substances, etc. These can be used for thermal Treatment of the molded articles covered with the veneer layer according to the invention either evaporate without residue, burn or with components of the molded and / or veneer surface and / or with cleavage and / or reaction products at least partially react and / or be at least partially incorporated into the surface layer.
Die Anwendung des beschriebenen Verfahrens bzw. der Vorrichtungen resultiert in einer wesentlich vereinfachten Farb- und/oder Transparenzgestaltung oder Farb- bzw. Transparenz korrektur von keramischen oder metallischen Formelementen, wie z. B. Zahnrestaurationen, Prothesen, Epithesen, medizinischen Implantaten oder Prothesen unter gleichzeitiger Optimierung der Werkstoffeigenschaften und der Zuverlässigkeit insbesondere von keramischer Rekonstruktionen, Minimierung der präparationsbedingten Entfernung ggf. gesunder Hart gewebe sowie erstmals in der reproduzierbaren Gestaltung definierter Oberflächeneigenschaften.The application of the described method or devices results in a significantly simplified color and / or transparency design or color or transparency correction of ceramic or metallic form elements, such as B. tooth restorations, Prostheses, epitheses, medical implants or prostheses under simultaneous Optimization of material properties and reliability, especially of ceramic ones Reconstructions, minimization of the preparation-related removal of healthy hard if necessary fabric and for the first time in the reproducible design of defined surface properties.
Die Herstellung der Zahnrestauration(en) oder Prothesenformteil(e) erfolgt, unter Verwendung bekannter Werkstoffe und Fertigungsverfahren, weitgehend endkonturnah, insbesondere in der definitiven Form der Rekonstruktion(en). Ggf. werden die zu verblendenen Oberflächen, wie oben beschrieben, vor dem Aufbringen der Verblendschicht(en) konditioniert.The tooth restoration (s) or prosthetic molded part (s) is produced using Known materials and manufacturing processes, largely close to the final shape, especially in the definitive form of the reconstruction (s). Possibly. the surfaces to be veneered, such as described above, conditioned prior to application of the veneer layer (s).
Die Farbauswahl kann mit herkömmlichen Farbauswahlsystemen, wie z. B. dem in der Zahntech nik verbreiteten Vita Lumin Vaccum Farbring erfolgen. The color selection can be done with conventional color selection systems such as e.g. B. that in the Zahntech nik widespread Vita Lumin Vaccum color ring.
Selbstverständlich können mit Hilfe des beschriebenen Verfahrens bzw. der Vorrichtung(en) auch wenigstens ein Farbmusterelement, insbesondere ein Set an Farbmusterelementen, z. B. zum Auswählen von Zahnfarben, hergestellt werden. Besonders vorteilhaft für Farbmusterelement(e) ist die Verwendung analoger Verblendschicht(en) oder Kombinationen von Verblendschichten, wie diese zur späteren Verblendung der Rekonstruktion(en) eingesetzt werden. Darüber hinaus hat es sich bewährt die Verblendschicht(en) definitiv, z. B. eingebrannt bzw. gesintert oder wiederablösbar, insbesondere abziehbar bzw. abschiebbar auf bzgl. der Materialzusammen setzung oder Einfärbung oder Schichtstärke oder Oberflächenstruktur äquivalent der zu verblen denden Rekonstruktionen ausgebildeten Farbmusterelementen aufzubringen, und dadurch den Einfluß der unverblendeten Rekonstruktion bzw. Subkonstruktion auf das spätere optische Erscheinungsbild der erfindungsgemäß verblendeten Rekonstruktion zu simmulieren.Of course, with the help of the described method or the device (s) also at least one color pattern element, in particular a set of color pattern elements, e.g. B. to Choosing tooth shades to be made. Particularly advantageous for color sample element (s) is the use of analog veneer layer (s) or combinations of veneer layers, how these are used for later veneering of the reconstruction (s). Furthermore Has the veneer layer (s) definitely proven itself, e.g. B. baked or sintered or removable, in particular removable or pushable with respect to the material together settlement or coloring or layer thickness or surface structure equivalent to the fade Apply the reconstructions trained color pattern elements, and thereby the Influence of the unrefined reconstruction or subconstruction on the later optical To simulate the appearance of the reconstruction blinded according to the invention.
Die Form derartiger Farbmusterelemente wird nur durch die vorgesehene Handhabung, z. B. im Munde eines Patienten, bestimmt; insbesondere eigenen sich zahnformähnliche Ausbildungs varianten oder solche, wie sie aus der DE 39 29 737 bekannt sind, jeweils mit einem geeigneten Griffelement zur einfachen Anwendung.The shape of such color pattern elements is only determined by the intended handling, e.g. B. in Mouth of a patient, determined; training similar to tooth form is particularly suitable Variants or such as are known from DE 39 29 737, each with a suitable one Handle element for easy use.
Erfindungsgemäß kann selbstverständlich auch ein papierartiges und z. B. farbneutrales Farb musterelement oder restaurationswerkstoffspezifisches Farbmusterelement in der optischen Erscheinungsform der unverblendeten Rekonstruktion ausgebildet sein. Auch dadurch wird das Erscheinungsbild der darüber aufgebrachten Verblendschicht bereits bei der Auswahl geeigneter Verblendschicht(en) entsprechend der später verblendeten Rekonstruktion simmuliert, was die Verwendung z. B. eines erfindungsgemäß geeigneten Abzieh- oder Schiebebildes als direktes Farbmuster erlaubt.According to the invention can of course also a paper-like and z. B. color neutral color sample element or restoration material-specific color sample element in the optical Appearance of the unrefined reconstruction. This also makes it Appearance of the veneer layer applied above already when selecting suitable ones Facing layer (s) simulates what the Use e.g. B. a suitable according to the invention decal or sliding picture as a direct Color samples allowed.
Zur Farbgestaltung der ggf. vorkonditionierten Rekonstruktion bzw. Rekonstruktionsoberflä chen wird (werden) die vorausgewählte(n) Verblendschicht(en) auf die zu verblenden Oberflä chen übertragen, aufgeschoben, aufgeklebt etc. und/oder in Position gebracht und/oder ggf. fixiert. Es können auch Verblendschichten ohne Farbeffekte, als "Glasurfolien", oder solche mit definierten Farbverläufen und Abstufungen, z. B. zwischen Zahnhals-, Zahnbein- und Schneide farben oder monochromatisch eingefärbte Verblendschichten verwendet werden. Die Adaptation erfolgt entweder durch Aufschieben, Aufkleben, Auflegen mit oder ohne zusätzliche Substrate, wie z. B. Lösungsmitteln oder Klebesubstanzen und/oder im Tiefziehverfahren und kann über die gesamte Oberfläche oder an beliebigen Oberflächenbereichen jeweils ein und/oder mehrschich tig erfolgen.For the color design of the possibly preconditioned reconstruction or reconstruction surface the preselected veneer layer (s) will be on the surface to be veneered transferred, pushed on, glued etc. and / or brought into position and / or if necessary fixed. It can also veneer layers without color effects, as "glaze foils", or those with defined color gradients and gradations, e.g. B. between the tooth neck, dentin and cutting edge colored or monochromatically colored veneer layers can be used. The adaptation takes place either by pushing on, gluing on, laying on with or without additional substrates, such as B. solvents or adhesive substances and / or in the deep-drawing process and can over the one or more layers on the entire surface or on any surface areas done.
Bevorzugt nach endgültiger Übereinstimmung des farblichen Erscheinungsbildes der verblende ten Restauration bzw. Restaurationsabschnitte entweder mit einem Farbmuster und/oder direkt nach Einprobe am Patienten wird (werden) die Verblendschicht(en) thermisch, bei material spezifischen Temperaturen oder Brandführungen, wenigstens teilweise gebrannt und/oder einge brannt bzw. gesintert. Durch die dünne Schichtstärke der Verblendschicht(en) und die gleichzei tige Oberflächenverglasung (Glasur) ist eine Ausarbeitung nach der thermischen Behandlung nicht erforderlich bzw. kann auf ein Minimum reduziert werden.Preferably after the color appearance of the veneer has been completely matched restoration or restoration sections either with a color sample and / or directly After trying in on the patient, the veneer layer (s) become (thermally), with material specific temperatures or firing, at least partially burned and / or turned on burns or sintered. Due to the thin layer thickness of the veneer layer (s) and the simultaneous surface glazing is a finishing after the thermal treatment not required or can be reduced to a minimum.
Selbstverständlich ist eine gleichzeitige und/oder nachträgliche Anwendung herkömmlicher Glasur- oder Porzellanverblendmassen möglich. Zur Abdeckung von z. B. transparenten Restau rationssegmenten oder Verfärbungen des Zahnstumpfes können auch opake Verblendschichten, die wenigstens teilweise Trübungsmittel, mit oder ohne Farbstoffzusätze enthalten, verwendet werden.Of course, simultaneous and / or subsequent use is more conventional Glaze or porcelain veneering materials possible. To cover z. B. transparent residual Ration segments or discoloration of the tooth stump can also be opaque veneers, which contain at least some opacifiers, with or without dye additives become.
Selbstverständlich können alle beschriebenen Verblendschichten auch auf die dem Patienten bzw. Zahnstumpf zugewandten "Innenseiten" einer Rekonstruktion aufgebracht und eingebrannt werden. Durch Reposition von Rekonstruktionen, insbesondere Zahnrestaurationen mit innen seitig aufgebrachten, verformbaren, erfindungsgemäßen Verblendschichten auf ein dimensions treues Modell der zu rekonstruierenden Oberflächen oder auf z. B. den Zahnstumpf und deren Stabilisierung und/oder thermischen Umsetzung, insbesondere durch Einbrennen, in der dadurch entstandenen Form, können z. B. fertigungsbedingte Forminkongruenzen zwischen der Restau ration und z. B. einem Zahnstumpf, wenigstens im Randbereich, minimiert und deren Passung dadurch optimiert werden. Insbesondere eignen sich dafür erfindungsgemäße Verblendschich ten, die bzgl. ihrer Schichtstärke auf den fertigungsspezifisch mittleren Fügespalt der unverblen deten Rekonstruktionen abgestimmt sind.Of course, all of the veneer layers described can also be applied to the patient or "stumps" facing tooth stump of a reconstruction applied and baked become. By repositioning reconstructions, especially dental restorations with the inside applied, deformable, veneer layers according to the invention to one dimension faithful model of the surfaces to be reconstructed or on z. B. the tooth stump and their Stabilization and / or thermal implementation, especially by baking, in the thereby resulting shape, z. B. Manufacturing-related form mismatches between the residual ration and z. B. a tooth stump, at least in the edge area, minimized and their fit thereby be optimized. Veneering layers according to the invention are particularly suitable for this ten, with regard to their layer thickness on the production-specific middle joint gap of the unblinded reconstructions are coordinated.
Claims (22)