DE3347061C1 - Self-supporting composite panel for double floors, ceilings or the like - Google Patents
Self-supporting composite panel for double floors, ceilings or the likeInfo
- Publication number
- DE3347061C1 DE3347061C1 DE3347061A DE3347061A DE3347061C1 DE 3347061 C1 DE3347061 C1 DE 3347061C1 DE 3347061 A DE3347061 A DE 3347061A DE 3347061 A DE3347061 A DE 3347061A DE 3347061 C1 DE3347061 C1 DE 3347061C1
- Authority
- DE
- Germany
- Prior art keywords
- filler
- composite panel
- openings
- reinforcement
- skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
Description
Die Erfindung bezieht sich auf eine freitragende Verbundplatte für Doppelböden, Decken oder dergleichen mit einer wannenförmigen äußeren Bewehrung aus Blech, vorzugsweise Stahlblech und einem im fließfähigen Zustand in diese Bewehrung einzubringenden, aushärtbaren, mineralischen Füllstoff, z. B. Anhydrit, wobei die Verbundwirkung zwischen dem ausgehärteten Füllstoff und der wannenförmigen Bewehrung durch in deren Boden- und Seitenwänden vorgesehenen Durchbrüche (Punzen) mit nach innen hervorstehenden, ausgefransten Rändern erzeugt wird, und wobei ferner die wannenförmige Bewehrung an ihrer Außenseite mit einer das Auslaufen des Füllstoffes durch die Durchbrüche verhindernden Schicht überzogen ist.The invention relates to a self-supporting composite panel for raised floors, ceilings or the like with a tub-shaped outer reinforcement made of sheet metal, preferably sheet steel and one in the flowable Condition to be introduced into this reinforcement, hardenable, mineral filler, z. B. anhydrite, where the composite effect between the cured filler and the trough-shaped reinforcement through in their Bottom and side walls provided openings (counters) with inwardly protruding, frayed Edges is generated, and the trough-shaped reinforcement on its outside with a the leakage-preventing layer is coated with the filler material.
Bei der Herstellung einer durch die DE-PS 20 04 101 bekanntgewordenen Verbundplatte der obigen Bauart wird das Auslaufen des im flüssigen Zustand in die wannenförmige Bewehrung eingebrachten mineralischen Füllstoffes, z. B. Anhydrit, durch die trichterähnlichen Durchbrüche in der Blechwanne zur Zeit dadurch verhindert, daß man vor dem Einfüllvorgang die Außenseite des Wannenbodens und der Wannenseitenwände mit Aluminiumfolie beklebt, welche die Wannendurchbrüche nach außen abschließt. Diese Art der Abdichtung der Durchbrüche in der wannenförmigen Bewehrung ist jedoch arbeitsintensiv und daher unwirtschaftlich. Andererseits werden diese trichterähnlichen Durchbrüche in der wannenförmigen Bewehrung zur Schaffung der erforderlichen Verbundwirkung zwischen Bewehrung und ausgehärtetem Füllstoff benötigt. Man hat nämlich herausgefunden, daß die Tragkraft der Verbundplatte im wesentlichen durch den Verbund zwischen dem ausgehärteten mineralischen Füllstoff und den als Schubanker wirkenden trichterähnlichen Durchbrüchen in der wannenförmigen Bewehrung bestimmt wird.In the manufacture of a composite panel of the above type made known by DE-PS 20 04 101 the leakage of the mineral introduced into the tub-shaped reinforcement in the liquid state Filler, e.g. B. anhydrite, currently prevented by the funnel-like openings in the sheet metal tub, that before the filling process, the outside of the tub bottom and the tub side walls with Laminated aluminum foil, which closes the tub openings from the outside. This type of waterproofing however, the openings in the trough-shaped reinforcement are labor-intensive and therefore uneconomical. on the other hand these funnel-like openings in the tub-shaped reinforcement are used to create the required bond between reinforcement and hardened filler. Because you have found that the load-bearing capacity of the composite panel is essentially due to the bond between the cured mineral filler and the funnel-like openings in the tub-shaped reinforcement is determined.
Die Erfindung dient der Aufgabe, die Abdichtung der als Schubanker wirkenden Durchbrüche in der wannenförmigen Bewehrung gegenüber dem flüssigen mineralischen Füllstoff zu vereinfachen und zugleich die Festigkeit und Biegesteifigkeit der fertigen Verbundplatte und damit deren Tragfähigkeit wesentlich zu erhöhen.The object of the invention is to seal the breakthroughs acting as a shear anchor in the trough-shaped To simplify reinforcement compared to the liquid mineral filler and at the same time increase strength and to significantly increase the flexural strength of the finished composite panel and thus its load-bearing capacity.
Gemäß der Erfindung wird die gestellte Aufgabe dadurch gelöst, daß die das Auslaufen des mineralischen Füllstoffes, z. B. Anhydrit, verhindernde Schicht aus einem flüssig oder plastisch aufgetragenen und danach ausgehärteten Oberflächenschutz- und/oder -veredelungsmittel besteht, welches als geschlossene Haut die mit entsprechend kleinem lichten Durchmesser in einer einem Reibeisen ähnlichen Vielzahl hergestellten Durchbrüche (Punzen) in der wannenförmigen Bewehrung verschließt. Diese Methode zur Abdichtung der Durchbrüche (Punzen) setzt ein Oberflächenschutz- oder -Veredelungsmittel mit entsprechender Viskosität sowie einen lichten Durchmesser der Durchbrüche (Punzen) von nur einigen wenigen Millimetern voraus. Da bei Verwendung von zum Beispiel einfachem Stahlblech zur Herstellung der wannenförmigen Bewehrung ohnehin ein Oberflächenschutz gegen Korrosion vorzusehen ist, kann erfindungsgemäß das hierfür erforderliche Mittel nunmehr zugleich für den Verschluß der erwähnten Durchbrüche in der wannenförmigen Bewehrung benutzt werden. Versuche haben gezeigt, daß selbst bei beträchtlicher Reduzierung der lichten Durchmeser der Durchbrüche im Vergleich zum Stand der Technik keine verringerte Tragkraft der Verbundplatte in Kauf genommen werden muß, sondern daß durch Vervielfachung der Zahl der Durchbrüche im Vergleich zum Stand der Technik sogar eine merkliche Erhöhung der Festigkeit, Biegesteifigkeit und damit Tragkraft der Verbundplatte erreicht werden kann.According to the invention, the object is achieved in that the leakage of the mineral Filler, e.g. B. anhydrite, preventive layer from a liquid or plastic applied and then cured surface protection and / or finishing agent, which as a closed skin the produced with a correspondingly small inside diameter in a variety similar to a grater Breakthroughs (counters) in the tub-shaped reinforcement are closed. This method of sealing the Breakthroughs (hallmarks) are made by a surface protection or finishing agent with a corresponding viscosity as well as a clear diameter of the openings (counters) of only a few millimeters ahead. As when using, for example, simple sheet steel to produce the trough-shaped reinforcement A surface protection against corrosion is to be provided anyway, according to the invention the necessary for this can be provided Means now at the same time for the closure of the mentioned openings in the tub-shaped reinforcement to be used. Tests have shown that even with a considerable reduction in the clear Compared to the prior art, the diameter of the openings does not reduce the load-bearing capacity of the composite panel must be accepted, but that by multiplying the number of breakthroughs in the Compared to the prior art, there is even a noticeable increase in strength, flexural rigidity and thus Load-bearing capacity of the composite panel can be achieved.
Mit anderen Worten, Grundlage der Erfindung sind zwei neue Erkenntnisse, durch deren Kombination eine überraschende Rationalisierung in der Fertigung und zugleich eine äußerst bedeutsame Erhöhung der Tragfähigkeit erzielt wird. Die erste neue Erkenntnis besteht darin, daß die Größe der Schubkraft, die durch die »Punzen« vom Wannenboden auf den eingefüllten druckfesten Füllstoff übertragen wird, abhängig ist von der Summe aller Oberflächen, die aus dem Wannenboden heraus in den druckfesten Füllstoff hineinragen, je größer also die Summe dieser Rand-Seitenflächen der Punzen ist, desto größer wird auch die übertragende Schubkraft, bevor das Füllmaterial vom Wannenboden abreißt. Man kann also durch eine sehr große Anzahl kleiner Punzen eine wesentlich höhere Schubkraft übertragen als durch eine geringe Anzahl großer Punzen, während andererseits die Schwächung des Bodens und damit die Minderung der Zugkraft im Boden nicht im gleichen Maße steigt.In other words, the basis of the invention are two new discoveries, by combining them one surprising rationalization in production and at the same time an extremely significant increase in load-bearing capacity is achieved. The first new finding is that the magnitude of the thrust exerted by the "Punzen" is transferred from the bottom of the tub to the filled pressure-resistant filler, depends on the sum of all surfaces that protrude from the tank bottom into the pressure-resistant filler, depending So the greater the sum of these edge-side surfaces of the counters, the greater the transferring Thrust before the filling material tears off the bottom of the tub. So you can go through a very large number small punches transmit a significantly higher thrust than through a small number of large punches, while on the other hand the weakening of the soil and thus the reduction of the tensile force in the soil is not in the increases equally.
Die zweite Erkenntnis besteht darin, daß man kleine Durchbrüche (Punzen) rationell durch eine Schutzschicht verschließen kann, die dem Korrosionsschulz bzw. der Oberflächenveredelung des Wanncnmaterials dient. Die Erfindung besteht daher in der Kombination der beiden neuen Erkenntnisse. So wird der Wannenboden nicht wie beim Stand der Technik mit einer relativ kleinen Zahl großer Durchbrüche (Punzen), sondern mitThe second finding is that you can efficiently use a protective layer to make small perforations (hallmarks) can close that the corrosion risk or the surface refinement of the tub material serves. The invention therefore consists in the combination of the two new findings. This is how the bottom of the tub will be not with a relatively small number of large perforations (hallmarks) as in the prior art, but with
3 43 4
einer mehrfach so großen Anzahl von Durchbrüchen kung zwischen dem ausgehärteten Füllstoff 12 und dera multiple of the number of breakthroughs between the cured filler 12 and the
mit kleinem lichten Durchmesser versehen, und dann wannenförmigen Bewehrung 11 dienen ebenfallsProvided with a small inside diameter, and then trough-shaped reinforcement 11 also serve
wird eine Haut flüssig oder plastisch aufgetragen, und Durchbrüche 13 (Punzen) mit nach innen hervorstehen-a skin is applied in liquid or plastic form, and openings 13 (hallmarks) with protruding inwards
man läßt diese Haut aushärten bevor der mineralische den, ausgefransten Rändern 14. Das Auslaufen des flüs-this skin is allowed to harden before the mineral reaches the frayed edges 14. The leakage of the fluid
Füllstoff, z. B. Anhydrit, eingebracht wird. Dadurch wird 5 sigen mineralischen Füllstoffes 12 durch diese Durch-Filler, e.g. B. anhydrite is introduced. As a result, 5 mineral filler 12 is through this through-
der flüssig eingefüllte aushärtbare minerale Füllstoff be- bräche 13 hindurch wird hier jedoch durch ein auf diehowever, the curable mineral filler filled in as a liquid breaks through 13 here through an on the
hindert, durch die Durchbrüche (Punzen) auszulaufen. Außenseite der wannenförmigen Bewehrung 11 vorprevents leakage through the perforations (hallmarks). Outside of the trough-shaped reinforcement 11 before
Eine Ausgestaltung der Erfindung sieht vor, daß die dem Einfüllvorgang flüssig aufgetragenes, aushärtendes die Durchbrüche verschließende Haut durch einen Oberflächenschutz- oder -Veredelungsmittel verhindert, schnell trocknenden Lack gebildet ist, der einen Füll- io das nach dem Aushärten auf der gesamten Außenseite stoff aus z. B. Faserstückchen enthält. Der Füllstoff setzt der wannenförmigen Bewehrung (Boden und Seitensich beim Auftragen bzw. Aufspritzen des Kunstharz- wände) eine Haut 19 bildet, welche die Durchbrüche 13 lackes auf die Außenseite der wannenförmigen Beweh- nach außen verschließt. Als Oberflächenschutz- oder rung vorteilhaft in den trichterförmigen Durchbrüchen -Veredelungsmittel kann z. B. ein schnell trocknender fest und begünstigt dadurch an der Haut die Ausbildung 15 entsprechend viskoser Kunstharzlack verwendet wervon »Verschlußstopfen« in den Durchbrüchen. den, der auf die Außenseite der wannenförmigen Be-One embodiment of the invention provides that the liquid applied to the filling process, hardening Prevents skin that closes the breakthroughs with a surface protection or finishing agent, quick-drying varnish is formed, which has a filling io that after curing on the entire outside fabric from z. B. contains bits of fiber. The filler sets the trough-shaped reinforcement (bottom and side when the synthetic resin walls are applied or sprayed on, a skin 19 forms which the openings 13 lacquer on the outside of the tub-shaped mold closes to the outside. As surface protection or tion advantageous in the funnel-shaped breakthroughs finishing agent can, for. B. a quick drying one firmly and thereby favors the formation of 15 correspondingly viscous synthetic resin varnish on the skin "Sealing plugs" in the breakthroughs. the one on the outside of the tub-shaped loading
Nach einer anderen Ausgestaltung der Erfindung wehrung 11 aufgespritzt wird. Dieser KunstharzlackAccording to another embodiment of the invention, defense 11 is sprayed on. This synthetic resin paint
kann die die Durchbrüche verschließende Haut eine kann Faserstückchen, z. B. Glasfaserstückchen, als Füll-the skin closing the openings can be a piece of fiber, e.g. B. pieces of glass fiber, as filling
Zinkhaut sein. Diese Zinkhaut kann z. B. durch Aufsprit- stoff enthalten, um die Durchbrüche 13 sicher zu ver-Be zinc skin. This zinc skin can, for. B. contained by spray-on in order to secure the openings 13
zen einer Zinkstaubfarbe oder im Zuge einer Feuerver- 20 schließen und nach außen abzudichten, wie in F i g. 4zen a zinc dust paint or in the course of a fire seal 20 and seal to the outside, as in FIG. 4th
zinkung der wannenförmigen Bewehrung aus Stahl- gezeigt ist. Es versteht sich, daß erst nach dem Aushär-zincing of the trough-shaped steel reinforcement is shown. It goes without saying that only after curing
blech ausgebildet werden. ten des Oberflächenschutz- und/oder -veredelungsmit-sheet are formed. the surface protection and / or finishing agent
Die Erfindung wird anschließend anhand der Zeich- tels bzw. Ausbildung der Schutz- und AbdichtungshautThe invention will then be explained on the basis of the drawing or the design of the protective and sealing skin
nung eines Ausführungsbeispiels erläutert. Es zeigt 19 der flüssige mineralische Füllstoff 12 in die wannen-.Explained tion of an embodiment. It shows 19 the liquid mineral filler 12 in the tub.
Fig. 1 eine Teil-Schnittansicht einer Verbundplatte, 25 förmige Bewehrung 11 eingebracht wird. Die Abbinde-Fig. 1 is a partial sectional view of a composite panel, 25-shaped reinforcement 11 is introduced. The binding
die dem Stand der Technik entspricht, zeit des aus einer schnell trocknenden Qualität beste-which corresponds to the state of the art, at the best of a quick-drying quality
Fig.2 eine Teil-Schnittansicht einer Verbundplatte henden Lackes kann durch Wärmezufuhr noch begemäß der Erfindung, schleunigt werden.Fig. 2 is a partial sectional view of a composite panel existing paint can still be according to heat supply of the invention.
F i g. 3 eine Teil-Draufsicht der wannenförmigen Be- Damit sich über den Durchbrüchen 13 zuverlässigF i g. 3 shows a partial top view of the trough-shaped loading so that it can be reliably positioned over the openings 13
wehrung der Verbundplatte nach F i g. 2 ohne Füllstoff 30 eine geschlossene Haut 19 (F i g. 2) ausbilden kann, be-Reinforcement of the composite panel according to FIG. 2 can form a closed skin 19 (FIG. 2) without filler 30, but
und trägt deren kleinster lichter Durchmesser £2 nur einenand its smallest clear diameter £ 2 has only one
F i g. 4 die in F i g. 2 angedeutete Einzelheit X in stark Bruchteil, z. B. 3 mm, des kleinsten lichten Durchmes-F i g. 4 the in F i g. 2 indicated detail X in a strong fraction, e.g. B. 3 mm, the smallest clear diameter
vergrößertemMaßstab. sers b\ der Ausführung nach Fig. 1. Im Vergleich zurenlarged scale. sers b \ the embodiment according to Fig. 1. Compared to
Die in F i g. 1 gezeigte Verbundplatte 10 bekannter Konstruktion nach F i g. 1 ist ferner die Zahl der DurchBauart weist eine wannenförmige äußere Bewehrung 11 35 brüche 13 mehrfach oder vielfach erhöht, z. B. etwa um aus z. B. Stahlblech sowie einen aushärtbaren minerali- das Sechsfache im Bodenbereich und um etwa das Dreischen Füllstoff 12, z. B. Anhydrit, auf, der im flüssigen fache im Seitenwandbereich der wannenförmigen Be-Zustand in die wannenförmige Bewehrung 11 einge- wehrung 11. Dadurch wird die Tragfähigkeit der erfinbracht wird. Die erforderliche Verbundwirkung zwi- dungsgemäßen Verbundplatte 10Λ gegenüber der besehen dem ausgehärteten Füllstoff 12 und der wannen- 40 kannten Ausführung sogar erheblich größer, weil die förmigen Bewehrung 11 wird mittels zahlreicher Durch- Höhe des nach innen ragenden Randes 14 der Durchbrüche 13 (Punzen) erreicht, welche nach innen hervor- brüche 13 bei der Verbundplatte der F i g. 2 nur geringstehende, ausgefranste Ränder 14 aufweisen. Diese fügig kleiner als jene bei der bekannten Verbundplatte Durchbrüche 13 werden mittels in das Stahlblech von nach F i g. 1 ist, während andererseits die Summe aller außen einzutreibender spitzer Dorne erzeugt. Die Höhe 45 Seitenflächen der Durchbrüche (Punzen) die Schubkraft dieser Ränder 14 beträgt etwa 5 mm und der kleinste zwischen Wannenboden und Füllstoff übertragen, welichte Durchmesser b\ der Durchbrüche 13 ca. 8 mm. sentlich vergrößert ist.The in F i g. 1 shown composite panel 10 of known construction according to FIG. 1 is also the number of DurchBauart has a trough-shaped outer reinforcement 11 35 breaks 13 increased several times or many times, z. B. about from z. B. sheet steel and a hardenable mineral six times as much in the bottom area and around the three-dimensional filler 12, z. B. anhydrite, which in the liquid fold in the side wall area of the trough-shaped loading state in the trough-shaped reinforcement 11 is reinforced 11. This increases the load-bearing capacity of the invention. The required composite effect between the composite panel 10Λ compared to the cured filler 12 and the well-known version is even considerably greater, because the shaped reinforcement 11 is achieved by means of numerous through-heights of the inwardly protruding edge 14 of the openings 13 (counters) which protrudes inwards 13 in the composite panel of FIG. 2 have only slightly protruding, frayed edges 14. These are slightly smaller than those in the known composite panel openings 13 by means of in the steel sheet according to FIG. 1, while on the other hand the sum of all pointed mandrels to be driven in from the outside is generated. The height 45 side surfaces of the openings (counters), the shear force of these edges 14 is about 5 mm and the smallest transferred between the tub bottom and filler, which diameter b \ of the openings 13 is about 8 mm. is significantly enlarged.
Die Durchbrüche 13 mit den nach innen ragenden Rän- The openings 13 with the inwardly protruding edges
dem 14 kann man auch als Schubanker bezeichnen. Um Hierzu 1 Blatt Zeichnungen
beim Einfüllen des flüssigen mineralischen Füllstoffes 12 50
in die wannenförmige Bewehrung 11 ein Auslaufen desselben durch diese Durchbrüche 13 hindurch zu vermeiden,
werden bisher auf die Außenseite des Bodens 15
und der Seitenwände 16 der wannenförmigen Bewehrung 11 Aluminiumfolien 17 bzw. 18 aufgeklebt, welche 55
die Durchbrüche 13 nach außen verschließen. Die fertige Verbundplatte 10 hat einen quadratischen Grundriß
und wird mit ihren Ecken auf Fußstützen aufgelagert,
die ihrerseits auf dem jeweiligen Gehäuseboden aufgestellt sind (nicht gezeigt). 60dem 14 can also be referred to as a shear anchor. To do this, 1 sheet of drawings
when filling the liquid mineral filler 12 50
To prevent the same from running out of the trough-shaped reinforcement 11 through these openings 13, up to now on the outside of the base 15
and the side walls 16 of the trough-shaped reinforcement 11, aluminum foils 17 and 18, respectively, are glued on, which 55
the openings 13 close to the outside. The finished composite panel 10 has a square plan
and is supported with its corners on footrests,
which in turn are set up on the respective housing base (not shown). 60
Die in Fig.2 gezeigte erfindungsgemäße Verbundplatte
10/4 weist die zwei gleichen Hauptbestandteile
wie die Verbundplatte 10 der F i g. 1 auf, nämlich die
wannenförmige äußere Bewehrung 11 aus z. B. Stahlblech
sowie den mineralischen Füllstoff 12, z. B. Anhy- 65
drit. Der Füllstoff 12 wird gleichfalls flüssig in die wannenförmige Bewehrung 11 eingefüllt, und man läßt ihn
dann darin aushärten. Zur Erzielung der Verbundwir-The composite panel 10/4 according to the invention shown in FIG. 2 has the same two main components
like the composite panel 10 of FIG. 1, namely the
tub-shaped outer reinforcement 11 made of z. B. sheet steel and the mineral filler 12, z. B. Anhy- 65
third. The filler 12 is also poured into the trough-shaped reinforcement 11 in liquid form, and it is left in place
then harden in it. In order to achieve the composite
- Leerseite -- blank page -
Claims (3)