DE3336743A1 - Plastic composition for plastic facing sheets and adhesives - Google Patents

Plastic composition for plastic facing sheets and adhesives

Info

Publication number
DE3336743A1
DE3336743A1 DE3336743A DE3336743A DE3336743A1 DE 3336743 A1 DE3336743 A1 DE 3336743A1 DE 3336743 A DE3336743 A DE 3336743A DE 3336743 A DE3336743 A DE 3336743A DE 3336743 A1 DE3336743 A1 DE 3336743A1
Authority
DE
Germany
Prior art keywords
plastic
fibers
plastic compound
flat facing
phosphoric acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE3336743A
Other languages
German (de)
Other versions
DE3336743C2 (en
Inventor
Des Erfinders Auf Nennung Verzicht
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Elastolith Farben und Putze 4799 Borchen De GmbH
Original Assignee
GFP GESELLSCHAFT fur PUTZE BAUMATERIALIEN U WAERMEDAEMMSYSTEME MBH 4799 BORCHEN DE
GFP GES fur PUTZE BAUMATERIAL
Gfp Gesellschaft Fuer Putze Baumaterialien U Waermedaemmsysteme Mbh 4799 Borchen
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GFP GESELLSCHAFT fur PUTZE BAUMATERIALIEN U WAERMEDAEMMSYSTEME MBH 4799 BORCHEN DE, GFP GES fur PUTZE BAUMATERIAL, Gfp Gesellschaft Fuer Putze Baumaterialien U Waermedaemmsysteme Mbh 4799 Borchen filed Critical GFP GESELLSCHAFT fur PUTZE BAUMATERIALIEN U WAERMEDAEMMSYSTEME MBH 4799 BORCHEN DE
Priority to DE3336743A priority Critical patent/DE3336743A1/en
Publication of DE3336743A1 publication Critical patent/DE3336743A1/en
Application granted granted Critical
Publication of DE3336743C2 publication Critical patent/DE3336743C2/de
Granted legal-status Critical Current

Abstract

Plastic compositions for the production of plastic facing sheets should be sufficiently elastic and reliably bondable, and in addition fire prevention demands are made. It has been found that plastic compositions which allow both the production of a plastic facing sheet and the preparation of an adhesive for these facings can be produced on a vinyl basis with addition of plasticisers, the necessary elasticity and flame resistance being achieved by employing as plasticisers, chlorinated alkyl compounds and/or organic phosphoric acid esters. The structure of the facings is achieved by structure-forming additives, added fibres preventing the facings cracking when bent around tight corners.

Description

Kunststoff-FlachverblenderPlastic flat facing brick

Die Erfindung betrifft eine Kunststoffmasse auf der Basis von Polyvinylacetat, insbesondere als Copolymerisat mit Vinylalkohol-Fettsäureestern und/oder Vinylchlorid, zur Herstellung von Kunststoff-Flachverblendern, sowie eines für deren Verarbeitung geeigneten Klebers .The invention relates to a plastic compound based on polyvinyl acetate, in particular as a copolymer with vinyl alcohol fatty acid esters and / or vinyl chloride, for the production of plastic flat facing bricks, as well as an adhesive suitable for their processing .

Aus der DE-GM 78 29 6o1 ist bekannt, Kunststoff-Flachverblender auf der Basis von ausgehärteten Acrylharzen, denen mineralische Zuschläge beigemischt sind, herzustellen. Die DE-OS 3o 45 747 lehrt darüber hinaus als Basis für die Kunststoff-Flachverblender Vinylacetat als Polymerisat oder als Copolymerisat zusammen mit anderen Vinylalkoholestern einfacher Fettsäuren einzusetzen und durch die Auswahl von aufeinander abgestimmten KörnungenFrom DE-GM 78 29 6o1 it is known, flat plastic facing bricks based on cured acrylic resins, to which mineral aggregates are added. DE-OS 3o 45 747 also teaches as a basis for the plastic flat facing brick, vinyl acetate as a polymer or to use as a copolymer together with other vinyl alcohol esters of simple fatty acids and through the selection of coordinated grain sizes

mineralischen Zuschläge besondere Strukturen zu erhalten. Dabei wird - um ein leichtes Verarbeiten und eine gute Dauerstandsfähigkeit zu erreichen - der Kunststoffmasse ein Weichmacher zugesetzt, wobei der Weichmacher insbesonere ein Gemisch aus einem relativ niedrig siedenden und einem hochsiedenden Bestandteil ist und wobei der niedrig siedende Bestandteil im wesentlichen die Verarbeitbarkeit und der hochsiedende das Dauerstandsverhältnis beeinflußt. Diese Weichmacher dampfen im Laufe der Zeit ab, wodurch die "Weichheit" des Kunststoffes nachteilig abnimmt.mineral aggregates to obtain special structures. Thereby - an easy processing and a good one To achieve durability - the plastic mass a plasticizer added, the plasticizer in particular a mixture of a relatively low-boiling point and a high boiling point ingredient, and wherein the low boiling point ingredient is essentially processability and the high boiling point is the duration ratio influenced. These plasticizers evaporate over time, which makes the "softness" of the plastic disadvantageous decreases.

Darüber hinaus ist es, wie die Erfahrung zeigt, immer wieder problematisch, die so hergestellte Kunststoff-Flachverb lender in Dünnbett-Klebetechnik auf senkrechten Wänden zu befestigen. Unterschiedliche Temperaturdehnungen und unzureichende Abstimmung zwischen dem Kunststoff-Kleber und dem Kunststoff-Flachverblender können bei starkes Temperaturwechsel zum Abfallen der Kunststoff-Flachverblender führen.In addition, as experience shows, it is always problematic to use the plastic flat connector produced in this way lender to be attached to vertical walls using thin-bed adhesive technology. Different temperature expansions and insufficient coordination between the plastic adhesive and the plastic flat facing brick can result in strong Temperature change for the plastic flat facing brick to fall off to lead.

Hier setzt die Erfindung ein, der die Aufgabe zugrunde liegt, eine gattungsgemäße Kunststoffmasse zur Herstellung derartiger Kunststoff-Flachverblender sowie des für deren Verarbeitung geeigneten Klebers anzugeben, wobei das Dauerstandsverhalten der Kunststoff-Flachverblender wesentlich verbessert und die Abstimmung des Kunststoff-Klebers auf die Kunststoff-Flachverblender von vornherein gegeben ist.This is where the invention, on which the object is based, comes in, a generic plastic compound for production specify such plastic flat facing bricks as well as the adhesive suitable for their processing, with the long-term behavior the plastic flat facing significantly improved and the coordination of the plastic adhesive on the plastic flat facing is given from the start.

Nach der Erfindung wird diese Aufgabe dadurch gelöst, daß der Kunststoffmasse als Weichmacher chlorierte Alkyle und/ oder organische Phosphorsäureester mit mindestens zwei Phenol- bzw. Kresylgruppen oder mit mindestens zweiAccording to the invention, this object is achieved in that the plastic compound is chlorinated alkyls and / or organic phosphoric acid esters with at least two phenol or cresyl groups or with at least two

chlorierten Alkylgruppen in Mengen von mindestens zwei
und höchstens acht Gewichtsprozent, bezogen auf die fertige Kunststoffmasse, zugesetzt sind. Durch diese Wahl
der Weichmacher wird ein erheblich verbessertes Dauerstandsverhalten erreicht. Darüber hinaus haben diese
Weichmacher noch einen überraschenden Vorteil: Ihr Einsatz verbessert das Brandverhalten der Kunststoff-Flachverblender bzw. des Klebers mit dem diese Kunststoff-Flachverblender befestigt werden, in dem die gegebene Brennbarkeit der Kunststoffmasse erheblich herabgesetzt wird.chlorinated alkyl groups in amounts of at least two
and a maximum of eight percent by weight, based on the finished plastic compound, are added. By that choice
the plasticizer, a significantly improved durability behavior is achieved. They also have this
Plasticizers have another surprising advantage: their use improves the fire behavior of the plastic flat facing bricks or the adhesive with which these plastic flat facing bricks are attached, in which the given flammability of the plastic mass is considerably reduced.

Darüber hinaus wird vorgeschlagen, daß als chlorierte Alkyle Chlorparaffine mit einer Kettenlänge von mindestens
zehn C und/oder einem Molukulargewicht von mindestens 3oo
zugesetzt sind. Chlorparaffin als Weichmacher hat bei dieser Kettenlänge und/oder dem Molukulargewicht einen so kleinen Dampfdruck, daß eine wesentliche Verringerung des Gehaltes an diesem Weichmacher auch büer lange Zeiten hinweg nicht
eintritt. Die praktische Unbrennbarkeit dieses Weichmachers beeinflußt das Brandverhalten des Endprodukts, nämlich des Kunststoff-Flachverblenders bzw. des Klebers.It is also proposed that the chlorinated alkyls chlorinated paraffins with a chain length of at least
ten C and / or a molecular weight of at least 300
are added. At this chain length and / or molecular weight, chlorinated paraffin as a plasticizer has such a low vapor pressure that a substantial reduction in the content of this plasticizer does not occur, even over long periods of time
entry. The practical incombustibility of this plasticizer influences the fire behavior of the end product, namely the plastic flat facing or the adhesive.

Ein anderer Vorschlag geht dahin, daß der organische Phosphorsäureester mindestens eine weitere Phenol-, Kresyl-
oder Octylgruppe enthält. Auch die organischen Phosphorsäureester, besonders A-^ry!phosphorsäureester besitzen vernachlässigbare Dampfdrücke und gewährleisten so ein
dauerplastisches Verhalten, der aus der Kunststoffmasse hergestellten Kunststoff-Flachverblender bzw. des Klebers.
Typische Weichmacher dieser Gruppe sind Diphenyloctylphosphat, Diphenylkresylphosphat, Trioctylphosphat, Trikresylphosphat. Another proposal is that the organic phosphoric acid ester at least one more phenol, cresyl
or contains octyl group. The organic phosphoric acid esters, especially Ary! Phosphoric acid esters, have negligible vapor pressures and thus ensure a
Permanently plastic behavior of the plastic flat facing brick made from the plastic compound or the adhesive.
Typical plasticizers of this group are diphenyl octyl phosphate, diphenyl cresyl phosphate, trioctyl phosphate and tricresyl phosphate.

Ein anderer Vorschlag geht dahin, daß die organischen Phosphorsäureester mindestens eine mehrfach halegonisierte Al-Another suggestion is that the organic phosphoric acid ester at least one Halegonized Al-

kylgruppe enthalten. Diese Phosphorsäureester sind ebenfalls als Weichmacher mit vernachlässigbarem Dampfdruck geeignet und sie vereinigen hinsichtlich ihres Einflusses auf die Feuerbeständigkeit die Eigenschaften der Phosphorsäureester und der chlorierten Alkyle. Ein vorzugsweise anzuwendender Weichmacher dieser Gruppe ist Trichloräthylphosphat. contain kyl group. These phosphoric acid esters are also useful as plasticizers with negligible vapor pressure suitable and they combine the properties of the phosphoric acid ester with regard to their influence on the fire resistance and the chlorinated alkyls. A plasticizer of this group that is preferably to be used is trichloroethyl phosphate.

In bezug auf einen Kunststoff-Flachverblender, hergestellt aus einer Kunststoffmasse wird vorgeschlagen, daß mindestens 15% dieser Kunststoffmasse mit höchstens 7o% Sand und strukturgebenden Körnungen gemischt sind, wobei als Rest feinkörniger Füller, vorzugsweise Kalkstein oder Quarzmehl mit einer Körnung von ο bis o,1 mm beigegeben ist. Darüber hinaus wird vorgeschlagen, daß der Kunststoffmasse Fasern mit einer Faserlänge von o,1 mm - 1o mm mit einem Anteil von etwa 2% bezogen auf die fertige Kunststoffmasse zugesetzt werden, wobei als Fasern -Cellulusefasern, textile Synthesefasern oder Glasseidenfasern oder ein Gemisch dieser Fasern benutzt wird.With respect to a plastic flat facing brick from a plastic mass it is proposed that at least 15% of this plastic mass with a maximum of 70% sand and texturing grains are mixed, with as The remainder of fine-grain filler, preferably limestone or quartz powder with a grain size of ο to 0.1 mm is added. In addition, it is proposed that the plastic mass fibers with a fiber length of 0.1 mm - 1o mm with a Share of about 2% based on the finished plastic mass can be added, the fibers being cellular fibers, textile Synthetic fibers or glass silk fibers or a mixture this fiber is used.

In bezug auf einen Kleber hergestellt aus der Kunststoffmasse wird vorgeschlagen, daß mindestens 12% dieser Kunststoffmasse mit höchstens 7o% eines feinkörnigen Füllers, vorzugsweise Kalkstein- oder Quarzmehl· mit einer Körnung von ο - o,1 mm gemischt sind, wobei als Rest Sand zugegeben ist.With regard to an adhesive made from the plastic compound, it is proposed that at least 12% of this plastic compound with a maximum of 70% of a fine-grain filler, preferably limestone or quartz powder with one grain of ο - 0.1 mm are mixed, the remainder being sand.

Die so hergestellten Kunststoff-Flachverblender zeichnen sich durch gute Plastizität auch über lange Standzeiten aus. Der dazu gehörige Kleber ist auf diese Kunststoff-Flachverblender sowohl im Hinblick auf das Material, als auch im Hinblick auf das Verhalten, beispielsweise im Hinblick auf Temperaturdehnung, abgestimmt. Dadurch werdenThe plastic flat facing bricks produced in this way are characterized by good plasticity, even over a long service life the end. The associated adhesive is on this plastic flat facing brick both in terms of the material and in terms of behavior, for example in With regard to temperature expansion. This will be

Haftungsfehler oder - bei starken Temperaturschwankungen etwa im Laufe eines Tages - auftretende Spannungen, die zum Reißen führen, vermieden. Darüber hinaus ist die Herstellung sowohl der Kunststoff-Flachverblender als auch des dazu gehörenden Klebers wirtschaftlich, weil die Grundmasse, die Kunststoffmasse als Ausgangsbasis für beide im wesentlichen gleich ist.Liability errors or - in the event of strong temperature fluctuations, for example in the course of a day - occurring tensions that lead to tearing, avoided. In addition, the manufacture of both the plastic flat facing brick as well the associated adhesive is economical because the base material, the plastic material, is the starting point for both in the is essentially the same.

ein typisches Rezept für die Kunststoffmasse ist (alle Angaben in Gewichtsprozent bezogen auf die fertige Kunststoffmasse) :a typical recipe for the plastic mass is (all Information in percent by weight based on the finished plastic compound) :

Wasserwater

Verdicker (Zelloluse o.a.)Thickener (cellulose or similar)

ρ -Puffer
ηρ buffer
η

Pigmentverteiler (anorganisch) Pigmentverteiler (organisch) Glykol (u.a. höhere Alkohole) Thixotropie-Zusätze Weichmacher
Kunststoffdispersion (5o%ig)Pigment distributor (inorganic) Pigment distributor (organic) Glycol (including higher alcohols) Thixotropic additives Plasticizers
Plastic dispersion (5o%)

Zur Herstellung von Kunststoff-Flachverblendern werden eingesetzt: The following are used to manufacture plastic flat facing bricks:

Kunststoffmasse etwa 26% Sande und strukturgebendePlastic compound about 26% sand and structuring

Putze etwa 66%Plaster about 66%

Füllstoffe (Gesteinsmehl) etwa 6,6%Fillers (rock flour) about 6.6%

-Cellulusefasern-Cellular fibers

o,2 - 2 mm etwa 1,4%o, 2 - 2 mm about 1.4%

25,oo%25, oo% 4o,oo%4o, oo% o,25%o, 25% o,7o%o.7o% o,12%o, 12% o,35%o, 35% o,25%o, 25% o,7o%o.7o% o,25%o, 25% o,7o%o.7o% o,35%o, 35% 1,oo%1, oo% 1 ,25%1.25% 2,oo%2, oo% 2,oo%2, oo% 8,oo%8, oo% 52,oo%52, oo% 66,oo%66, oo%

Zur Herstellung des Klebers wird vorteilhaft eingesetztIt is advantageous to use for the production of the adhesive

Kunststoffmasse etwa 2o%Plastic mass about 2o%

Füllstoffe (Gesteinsmehl) etwa 66% Sande etwa 13%Fillers (rock flour) approx. 66% sands approx. 13%

Dabei werden unter Füllstoffen vorzugsweise Gesteinsmehle mit einer Körnung von ο - o,1 m verstanden, wobei vorzugsweise Kalkstein-Mehl oder Quarzmehl eingesetzt wird. Die Körnungslinien der Sande liegt im Bereich von ο - 5 mm; die strukturgebenden Körnungen sind im wesentlichen geblähte Mineralien, beispielsweise Perlite, die neben der Strukturrierung auch die Wasserdampfdurchlässigkeit günstig beeinflussen.In this context, fillers are preferably understood to mean rock flour with a grain size of ο - 0.1 m, with preferably Limestone flour or quartz flour is used. The grading lines of the sands are in the range of ο - 5 mm; the Structure-giving grains are essentially expanded minerals, for example perlite, which in addition to the structuring also have a beneficial effect on water vapor permeability.

Claims (7)

PatentansprücheClaims 1. Kunststoffmasse auf der Basis von Polyvinylacetat, insbesondere als Copolymerisat mit Vinylalkohol-Fettsäureestern und/oder Vinylchlorid zur Herstellung von Kunststoff-Flachverblendern sowie eines für deren Verarbeitung geei .gneten Klebers, dadurch gekennzeichnet, daß der Kunststoffmasse als Weichmacher chlorierte Alkyle und/oder organische Phosphorsäureestern mit mindestens zwei Phenol- bzw. Kresylgruppen oder mit mindestens zwei chlorierten Alkylgruppen in Mengen von mindestens zwei und höchstens acht Gewichtsprozent, bezogen auf die fertige Kunststoffmasse, zugesetzt sind.1. Plastic compound based on polyvinyl acetate, in particular as a copolymer with vinyl alcohol fatty acid esters and / or vinyl chloride for the production of plastic flat facing bricks and one suitable for their processing Adhesive, characterized in that the plastic compound contains chlorinated alkyls and / or organic phosphoric acid esters as plasticizers with at least two phenol or cresyl groups or with at least two chlorinated alkyl groups added in amounts of at least two and no more than eight percent by weight, based on the finished plastic compound are. 2. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, daß als chlorierte Alkyle Chlorparaffine mit einer Kettenlänge von mindestens 1o C und/oder einem Molukulargewicht von mindestens 3oo zugesetzt sind.2. Plastic compound according to claim 1, characterized in that that chlorinated paraffins as chlorinated alkyls with a chain length of at least 1o C and / or a molecular weight of at least 300 are added. 3. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, daß der organische Phosphorsäureestern mindestens eine weitere Phenol-, Kresyl-, oder Octylgruppe enthält.3. Plastic compound according to claim 1, characterized in that that the organic phosphoric acid ester contains at least one further phenol, cresyl or octyl group. 4. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, daß die organischenPhoshorsäureestern mindestens eine mehrfach halegonisierte Alky!gruppe enthalten.4. Plastic compound according to claim 1, characterized in that that the organic phosphoric acid esters contain at least one multiply halogenated alkyl group. 5. Kunststoff-Flachverblender hergestellt aus einer Kunststoffmasse nach einem der Ansprüche 1-4, dadurch gekennzeichnet, daß mindestens 15% dieser Kunststoffmasse mit höchstens 7o% Sand und strukturgebender Körnungen gemischt sind, wobei als Rest feinkörniger Füller, vorzugsweise Kalkstein- oder Quarzmehl mit einer Körnung von ο - o,1 mm beigegeben ist.5. Plastic flat facing made from a plastic mass according to any one of claims 1-4, characterized in that at least 15% of this Plastic compound with a maximum of 7o% sand and structuring agent Grains are mixed, the remainder being fine-grained filler, preferably limestone or Quartz flour with a grain size of ο - 0.1 mm is added. 6.. Kunststoff-Flachverblender nach Anspruch 5, dadurch gekennzeichnet, daß der Kunststoffmasse zusätzlich Fasern mit einer Faserlänge von o,1 mm - 1o mm mit einem Anteil von etwa 2% bezogen auf die fertige Kunststoffmasse zugesetzt werden, wobei als Fasern -Cellulusefasern, textile Synthesefasern oder Glasseidenfasern oder Gemische dieser Fasern benutzt werden.6 .. plastic flat facing brick according to claim 5, characterized characterized in that the plastic compound additionally contains fibers with a fiber length of 0.1 mm - 10 mm in a proportion of about 2% based on the finished plastic mass, the fibers being cellular fibers, Textile synthetic fibers or glass silk fibers or mixtures of these fibers are used. 7. Kleber zum Verarbeiten der Kunststoff-Flachverblender gemäß Anspruch 5 oder 6, dadurch gekennzeichnet, daß mindestens 12% dieser Kunststoffmasse mit höchstens 7o% eines feinkörnigen Füllers, vorzugsweise Kalkstein- oder Quarzmehl mit einer Körnung von o-o,1 mm sind, wobei als Rest Sand zugegeben ist.7. Adhesive for processing the plastic flat facing according to claim 5 or 6, characterized in that at least 12% of this plastic mass with a maximum of 7o% of a fine-grain filler, preferably limestone or quartz powder with a grain size of 0.1 mm, the remainder being sand.
DE3336743A 1983-10-08 1983-10-08 Plastic composition for plastic facing sheets and adhesives Granted DE3336743A1 (en)