DE3328462A1 - Process for extreme-temperature-resistant adhesive bonding tape narrow planar UP to edges of wood-based material of extreme-temperature-resistant - Google Patents
Process for extreme-temperature-resistant adhesive bonding tape narrow planar UP to edges of wood-based material of extreme-temperature-resistantInfo
- Publication number
- DE3328462A1 DE3328462A1 DE3328462A DE3328462A DE3328462A1 DE 3328462 A1 DE3328462 A1 DE 3328462A1 DE 3328462 A DE3328462 A DE 3328462A DE 3328462 A DE3328462 A DE 3328462A DE 3328462 A1 DE3328462 A1 DE 3328462A1
- Authority
- DE
- Germany
- Prior art keywords
- temperature
- extreme
- resistant
- wood
- narrow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
- JL- - JL-
Titel der ErfindungTitle of the invention
Verfahren zum temperaturbeständigen Verkleben von üP-Schraalfläohenband auf HolzwerkstoffkantenProcess for temperature-resistant gluing of UP-Schraalfläohenband on wooden material edges
Anwendungsgebiet der ErfindungField of application of the invention
Die Erfindung betrifft ein Verfahren stan Verkleben von Schmalflächenband auf die Kanten von Holsi^rkstoffplatten mittels Schmelzklebstoffen nach dem sogenannten Heiß-Kalt-Verfahren im Zuge der Möbelfertigung· Bei den verwendeten Schmalflächenbändern handelt es sich um Schichtstoffa3 die durch Kalthärtung von mit ungesättigten Polyesterharzen (UP) getränkten Papieren hergestellt wurden·The invention relates to a method of gluing narrow-surface tape on the edges of Holsi ^ rkstoffplatten by means of hot-melt adhesives in the course of the so-called hot-cold process in the course of furniture production.The narrow- surface tapes used are laminates 3 which are produced by cold curing with unsaturated polyester resins (UP ) impregnated papers were produced
Charakteristik der bekannten technischen LösungenCharacteristics of the known technical solutions
Es sind bandförmige Schichtstoffe aur Kantenbeschichtung von
Möbelbauteilen auf Basis von mit ungesättigten Polyesterharzen getränkten Papieren bekannt· Derartige Materialien können 2.B,
nach der DD-PS 113 046 hergestellt werden (Salthärtungsverfahren)
·
Das KLeben der Schmalflächenbänder auf die HolzwerkstoffkantenStrip-shaped laminates are known for the edge coating of furniture components based on papers impregnated with unsaturated polyester resins. Such materials can be produced according to DD-PS 113 046 (salt hardening process)
The glueing of the narrow-surface tapes onto the wood-based material edges
ist sowohl mit Dispersions- und Kondensationsklebstoffen im sogenannten Kalt-Heiß-Verfahren als auch mit thermoplastischen Schmelzklebstoffen im Heiß-Kalt-Verfahren möglich. (Vgl· Böhme, Industrielle Oberflächenbehandlung von plattenförmigen Werkstoffen aus Holz, VEB Fachbuchverlag Leipzig 1980, S, 153 ff·).is both with dispersion and condensation adhesives in the so-called cold-hot process as well as with thermoplastic Hot-cold process possible with hot-melt adhesives. (See Böhme, industrial surface treatment of plate-shaped materials made of wood, VEB Fachbuchverlag Leipzig 1980, S, 153 ff ·).
Mt den erst genannt en Klebstoffen kaon eins temperatures tändigi Varlclebung erzielt 'werden, die auch den Anforderungen gerecht Tiird, die insbesondere an Möbel gestellt werden müssen, die ausgesprochenem Trockenklima ausgesetzt sind» Ungeachtet dessen ist festsusteilenj daß viele Möbelhersteller dem Heiß-Kalt-Verfahren mit Schmelzklebstoffen den Vorzug geben? und zwar aus Gründen, die sieh aus der einfacheren Iechnologie, der geringeren benötigten Baulänge der Maschinen und der hohen Produktivität dieses Verfahrens ergeben. Bestimmte Vorteile bestehen außerdem hinsichtlich der Qualität der Bekoroberflache: Während das DTachschrurapfen eines hits©härt1bar@n Klebstoffes eine zusätzliche Oberflächenunruhe erzeugt, tTirkt der Schmelzkleber im Gegenteil als Hbispensationaschicht, mit der Unebenheiten der Schmalfläche bis zu ©inem gewissen Grade ausgeglichen werden können· Der Hachteil der Heiß-Halt-Verklebung mit thermoplastischen Schiselsklebstoffen 10t nun aber darin su sehen, daß sie nicht temperaturbeständig ist· Unter standardisierten öürockanklimabedingangen τοη 55 0C und 20 % relativer Luftfeuchtigkeit lösen sich die Schmalflächenbänder bereits nach 1 bi3 2 h iTieder von der Kante ab·With the first-mentioned adhesives, one temperature constant variation can be achieved, which also meets the requirements that must be placed in particular on furniture that is exposed to a decidedly dry climate Give preference to hot melt adhesives? for reasons that result from the simpler technology, the shorter overall length required for the machines and the high productivity of this process. There are also certain advantages with regard to the quality of the surface: While the scratching of a hits © hardenable @ n adhesive creates additional surface irregularities, the hot melt adhesive, on the contrary, acts as a bispensation layer, with which unevenness of the narrow surface can be compensated to a certain extent However, the hot-hold bonding with thermoplastic Schiselsklebstoffen 10t now see that it is not temperature-resistant Under standardized Öürockanklimabendenangen τοη 55 0 C and 20 % relative humidity, the narrow-surface tapes detach from the edge after 1 to 3 2 hours.
la ist zwar bekannt 3 Schmalfläclienbänder zur Erzielung einer besseren Verklebung nach dem Haiß-Kalt-Verfahren auf ihrer Rückseite mit einem Haftvermittler für Dispersions- und Kondensationsklebstoffe zu versehen· Hierfür kommt auch Polyvinylacetat in !rage, das meistens vor dem Aufkleben des Schmalflächenbandea auf die mit Dispersionsklebstoff beschichtete Werk stoffkante mittels Heißluft reaktiviert wird·It is known to provide 3 narrow-surface tapes on their back with an adhesion promoter for dispersion and condensation adhesives to achieve better adhesion using the Haiß-Kalt method Material edge coated with dispersion adhesive is reactivated by means of hot air
Ziel der ErfindungObject of the invention
Ziel der Erfindung ist es, mittels üblicher Schmelzklebstoffe eine temperaturbeständige Verbindung stri.sehen dem UP-Sehmalflächenband und der Hol zt7erks toff leant e zu erzielen» Die Beständigkeit soll insbesondere unter Srockenklimabedingungen gegeben sein, darüber hinaus aber auch vor allem unter Wechselklimabeanspruchung· Die Beständigkeit gegenüber ständigen großen Schwankungen der !Temperatur und der Luftfeuchtigkeit, wie sie beispielsweise für tropische KLimate oder auch für KuchenmöbelThe aim of the invention is to use conventional hot melt adhesives a temperature-resistant connection stri. see the UP visual surface tape and the wood material leant e to achieve »The durability should be given in particular under dry climatic conditions, but also especially under changing climatic conditions The resistance to constant large fluctuations in temperature and humidity, like them for example for tropical climates or for cake furniture
typisch sind, ist nach wie vor problematisch und dringend verbesserungsbedürftig. Gleichzeitig soll die Haftung des Schmalflachenbandes auch gegenüber weiteren äußeren Einflüssen verbessert werden, die bisher ebenfalls häufig au AbIöseerscheinungen führen, wie leuchteeinwirkungen oder Beanspruchung bei maschineller Bearbeitung der Werkstoffkanten·are typical is still problematic and in urgent need of improvement. At the same time, the adhesion of the narrow flat belt should can also be improved in relation to other external influences, which up to now also frequently appear to be detachable such as the effects of light or stress when machining the material edges
Darlegung des Wesens der ErfindungExplain the essence of the invention
Der Erfindung liegt die Aufgabe zugrunde, das UP-Schmalflächenband durch eine geeignete Vorbehandlung so auszurüsten, daß beim Verkleben eine stabile mechanische Verankerung mit dem verwendeten Schmelzklebstoff eintritt·The invention is based on the object of the UP narrow-surface tape to equip by a suitable pretreatment so that a stable mechanical anchoring with the used Hot melt adhesive enters
Erfindungsgemäß wird auf die Rückseite eines in üblicher Weise
nach dem Kaithärtungsverfahren hergestellten UP-Schmalflachenbandes
vor der Verarbeitung eine wäßrige Polyvinylacetat-Dispersion
aufgetragen, der, bezogen auf ihre Gesamtmasse, 10 bis 40 % eines anorganischen Pullstoffes zugesetzt wurden· Als Füllstoffe
kommen von den Anstrichstoffen her bekannte und übliche natürliche
und künstliche anorganische Mineralien in Betracht, insbesondere also oxLdische und silikalisch® Verbindungen sowie
Sulfate und Karbonate der Srd- und Erdalkalimetalle· Bekannte Vertreter dieser Stoffgruppe sind beispielsweise Bariumsulfat
(Schwerspat), wasserhaltiges Calciumsulfat (Leiehtspat, Mneralweiß),
Calciumkarbonat (Kalzit, Kreide), Kaolin, Glimmer, Siliciumdioxid (Quarzmehl, Kieselgur), Titandioxid· Der Füllstoff
wird der Polyvinylacetat (PVAC)-Dispersion in möglichst feiner Verteilung zugesetzt» Dia für die Anstrichstofftechnik
handelsüblichen Füllstoffe stehen in genügend feinem Vermahlungsgrad zur Verfügung· Füllstoffe, deren OJeilchengröße sich in der
wäßrigen Dispersion wesentlich ändert, sollen/ für den vorliegenden
Zweck nicht verwendet werden· Hierzu gehören beispielsweise quellfähige Kaolin-Sorten, wie das als Extender verwendete
Betonit· Farner mit Wasser abbindende Mineralien, wie gebrannter
Gips.
Die PVAC-Dispersion ist so eingastallt, daß sie vor Zusatz des According to the invention, an aqueous polyvinyl acetate dispersion, to which, based on its total mass, 10 to 40% of an inorganic pull material has been added as fillers come from the paints, is applied to the back of a UP narrow-flat tape produced in the customary manner by the clay curing process before processing known and customary natural and artificial inorganic minerals into consideration, in particular oxide and silical® compounds as well as sulfates and carbonates of the alkaline earth and alkaline earth metals.Famous representatives of this group of substances are, for example, barium sulfate (heavy spar), water-containing calcium sulfate (leichtspat, mineral white), calcium carbonate (calcite , Chalk), kaolin, mica, silicon dioxide (quartz powder, kieselguhr), titanium dioxide · The filler is added to the polyvinyl acetate (PVAC) dispersion in the finest possible distribution Available fillers whose particle size changes significantly in the aqueous dispersion should / should not be used for the present purpose These include, for example, swellable types of kaolin, such as betonite used as an extender
The PVAC dispersion is so einastallt that before the addition of the
Füllstoffes eine dynamische Viskosität von etwa 200 Ms 500 mPa< besitzt· Me Auftragsmenge beträgt, bezogen auf das in der Dispersion enthaltene FVAG9 10 Ms 30 g/m2 β Nach erfolgtem Auftrag wird das "beschichtete Sehmalfläohenband getrocknet. ffach dem Trocknen der aufgetragenen PVAC/Püllstoff-Schicht erfolgt das Sieben nach dem HaiB-SaIt-Verfahren in üblicher Weise ? wobei alle bekannten Schmelzklebstoffe verwendet werden können« Dabei srfxd der erwärmte Schraelsklebstoff auf dia zu beschichtende Werk stoffkante aufgetragen und das beschichtete Sehmalflächenband aufgei^alzt« Ss ist ;je&och auch möglich, so zu verfahren, daß das mit PVAG und Füllstoff beschichtete Schmalflächenband nach der Troclmung ausätalich mit dem Schmelaklebstoff beschichtet wird, der dann beim KLebeprozeS in bekannter Weise mittels Heißluft reaktiviert wird·Filler has a dynamic viscosity of about 200 ms 500 mPa <possesses · Me application amount is, based on contained in the dispersion FVAG 9 10 ms 30 g / m 2 β After the application, the "coated Sehmalfläohenband is dried. Ffach drying the coated PVAC / Püllstoff -schicht is sieving according to the HaiB-SaIt method in the usual way - all known hotmelt adhesives can be used. The heated Schraels adhesive is applied to the edge of the material to be coated and the coated visual surface tape is applied It is also possible to proceed in such a way that the narrow surface tape coated with PVAG and filler is coated with the melt adhesive after drying, which is then reactivated in the known manner by means of hot air during the gluing process.
Die erfindungsgemäße Ausrüstung des Schmalflächenbandes verleiht diesem ein hohes rückseitiges Adhäsionsvermögen zum Schmelsklebstoff, indem bei der HeiS-Salt-TTerklebung eine stabile Verschweißung der beiden unterschiedlichen klebenden Komponenten eintritt. Sie erzielte Temperaturbeständigkeit entspricht derjenigen bei der Verklebung nach dem Kalt-Heiß-Verfahren, so daß die nach der Schmelzkleber-Sechnologie beschichteten Möbelbauteile voll den Anforderungen an alle KLimabedingungen entsprechen. The finishing of the narrow-surface belt according to the invention imparts This has a high rear-side adhesion to the hot-melt adhesive, in that the HeiS-Salt-T adhesive has a stable Welding of the two different adhesive components occurs. It corresponds to the temperature resistance achieved those in the case of gluing according to the cold-hot process, so that the furniture components coated according to the hot-melt adhesive technology fully meet the requirements of all climatic conditions.
Me erfindungsgemäße Ausrüstung des Schmalflächenbandes verleiht der Klebfuge eine höh©. Widerstandsfähigkeit gegenüber Wechaelklimabeanspruchungj' also gegenüber rasch und häufig abwechselnden hohen und tiefen !Oemperaturen, hoher und niedriger luftfeuchtigkeit·Me gives the finishing of the narrow-surface belt according to the invention the glue line a little higher. Resistance to alternating climatic stress, i.e. to rapidly and frequently alternating high and low temperatures, high and low humidity·
Bas Sohmalflächenband weist außerdem ein© erhöhte Haftung gegenüber Feuchtigkeitseimrirkungan auf 9 ebenso ?/ie gßgeniibex Seherbeanspruchung, m.© sie besonders bei der Maschinenbearbeitung der Holzwerkstoffe im Tferkzeugaustrittbereich auftritt.Basal surface tape also has increased adhesion to moisture penetration, 9 as well as visual stress, which occurs particularly when machining wood-based materials in the area of the tool exit area.
AusführungsbeispielEmbodiment
Auf ein UP-Schmalfläcfeenband des lyps 2 U (Hersteller: VEB Sprela-Werke Spremberg) werden mit Hilfe eines AbstreifmessersOn a UP narrow-surface tape of the lyps 2 U (manufacturer: VEB Sprela-Werke Spremberg) are made with the help of a scraper
ORIGINAL INSPECTEDORIGINAL INSPECTED
BAD ORIGINAL COPY BAD ORIGINAL COPY
20 g/m PVAO in wäßriger Dispersion aufgetragen, der vorher 10 % Mineralweiß zugesetzt und in ihr gleichmäßig verteilt wurden. Die Menge zugesetzten PUllstoffes ist auf die Gesamtmasse der Dispersion berechnet. Nach dem Trocknen des Auftrags wird das so behandelte Sehmalflächenband auf die Kanten von Holzwerk-20 g / m PVAO applied in an aqueous dispersion to which 10 % mineral white was previously added and evenly distributed in it. The amount of PUllstoffes added is calculated on the total mass of the dispersion. After the application has dried, the visual surface tape treated in this way is applied to the edges of woodwork
stoffplatten aufgewalzt, auf die unmittelbar vorher 200 g/m eines auf 200 0G erwärmten SchmelzKLebstoffes aufgetragen wurden· fabric sheets rolled onto which 200 g / m 2 of a hot melt adhesive heated to 200 0 G were applied immediately beforehand.
Claims (2)