DE3036206A1 - Verschleissfester, vor oxidation und korrosion schuetzender ueberzug, korrosions- und verschleissfeste ueberzugslegierung, mit einem solchen ueberzug versehener gegenstand und verfahren zum herstellen eines solchen ueberzugs - Google Patents
Verschleissfester, vor oxidation und korrosion schuetzender ueberzug, korrosions- und verschleissfeste ueberzugslegierung, mit einem solchen ueberzug versehener gegenstand und verfahren zum herstellen eines solchen ueberzugsInfo
- Publication number
- DE3036206A1 DE3036206A1 DE19803036206 DE3036206A DE3036206A1 DE 3036206 A1 DE3036206 A1 DE 3036206A1 DE 19803036206 DE19803036206 DE 19803036206 DE 3036206 A DE3036206 A DE 3036206A DE 3036206 A1 DE3036206 A1 DE 3036206A1
- Authority
- DE
- Germany
- Prior art keywords
- coating
- carbides
- weight
- mcraly
- matrix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
- C23C4/06—Metallic material
- C23C4/073—Metallic material containing MCrAl or MCrAlY alloys, where M is nickel, cobalt or iron, with or without non-metal elements
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
- Y02T50/00—Aeronautics or air transport
- Y02T50/60—Efficient propulsion technologies, e.g. for aircraft
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Physics & Mathematics (AREA)
- Plasma & Fusion (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Coating By Spraying Or Casting (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US06/085,132 US4275090A (en) | 1978-10-10 | 1979-10-15 | Process for carbon bearing MCrAlY coating |
US06/085,131 US4275124A (en) | 1978-10-10 | 1979-10-15 | Carbon bearing MCrAlY coating |
Publications (1)
Publication Number | Publication Date |
---|---|
DE3036206A1 true DE3036206A1 (de) | 1981-04-23 |
Family
ID=26772337
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
DE19803036206 Withdrawn DE3036206A1 (de) | 1979-10-15 | 1980-09-25 | Verschleissfester, vor oxidation und korrosion schuetzender ueberzug, korrosions- und verschleissfeste ueberzugslegierung, mit einem solchen ueberzug versehener gegenstand und verfahren zum herstellen eines solchen ueberzugs |
Country Status (8)
Country | Link |
---|---|
AU (1) | AU535069B2 (fr) |
BR (1) | BR8005977A (fr) |
CA (1) | CA1168477A (fr) |
DE (1) | DE3036206A1 (fr) |
FR (1) | FR2467243A1 (fr) |
GB (1) | GB2063305B (fr) |
IL (1) | IL61022A (fr) |
SE (1) | SE8006409L (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3304320C1 (de) * | 1983-02-09 | 1988-07-07 | M.A.N. Maschinenfabrik Augsburg-Nürnberg AG, 8900 Augsburg | Leichtmetallkolben für - insbesondere schwerölbetriebene - Brennkraftmaschinen |
DE3590031C2 (de) * | 1984-01-31 | 1995-06-22 | Castolin Sa | Verfahren zum Herstellen eines Metallpulvers |
DE102014202457A1 (de) * | 2014-02-11 | 2015-08-13 | Siemens Aktiengesellschaft | Verbesserte Verschleißbeständigkeit eines Hochtemperaturbauteils durch Kobaltbeschichtung |
Families Citing this family (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4677034A (en) * | 1982-06-11 | 1987-06-30 | General Electric Company | Coated superalloy gas turbine components |
DE3422138A1 (de) * | 1984-06-14 | 1985-12-19 | M.A.N. Maschinenfabrik Augsburg-Nürnberg AG, 8000 München | Verfahren und beschichtungsmaterial zum herstellen von keramik/metall-verbundbeschichtungen |
US4666733A (en) * | 1985-09-17 | 1987-05-19 | Electric Power Research Institute | Method of heat treating of wear resistant coatings and compositions useful therefor |
GB2214523B (en) * | 1985-09-17 | 1990-04-04 | Electric Power Res Inst | Chromium carbide compositions |
IL84067A (en) * | 1986-10-30 | 1992-03-29 | United Technologies Corp | Thermal barrier coating system |
US5137422A (en) * | 1990-10-18 | 1992-08-11 | Union Carbide Coatings Service Technology Corporation | Process for producing chromium carbide-nickel base age hardenable alloy coatings and coated articles so produced |
ES2075546T3 (es) * | 1991-07-12 | 1995-10-01 | Praxair Technology Inc | Miembro de cierre rotatorio recubierto con carburo de cromo y una aleacion de base de niquel endurecible por envejecimiento. |
JPH11343564A (ja) | 1998-05-28 | 1999-12-14 | Mitsubishi Heavy Ind Ltd | 高温機器 |
US20070116884A1 (en) * | 2005-11-21 | 2007-05-24 | Pareek Vinod K | Process for coating articles and articles made therefrom |
US7601431B2 (en) | 2005-11-21 | 2009-10-13 | General Electric Company | Process for coating articles and articles made therefrom |
US8262812B2 (en) | 2007-04-04 | 2012-09-11 | General Electric Company | Process for forming a chromium diffusion portion and articles made therefrom |
US20090022259A1 (en) * | 2007-07-20 | 2009-01-22 | General Electric Company | Fuel rod with wear-inhibiting coating |
-
1980
- 1980-09-09 GB GB8029118A patent/GB2063305B/en not_active Expired
- 1980-09-10 IL IL61022A patent/IL61022A/xx unknown
- 1980-09-12 SE SE8006409A patent/SE8006409L/xx not_active Application Discontinuation
- 1980-09-18 BR BR8005977A patent/BR8005977A/pt unknown
- 1980-09-23 AU AU62645/80A patent/AU535069B2/en not_active Ceased
- 1980-09-25 DE DE19803036206 patent/DE3036206A1/de not_active Withdrawn
- 1980-09-30 FR FR8020950A patent/FR2467243A1/fr not_active Withdrawn
- 1980-10-10 CA CA000362144A patent/CA1168477A/fr not_active Expired
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3304320C1 (de) * | 1983-02-09 | 1988-07-07 | M.A.N. Maschinenfabrik Augsburg-Nürnberg AG, 8900 Augsburg | Leichtmetallkolben für - insbesondere schwerölbetriebene - Brennkraftmaschinen |
DE3590031C2 (de) * | 1984-01-31 | 1995-06-22 | Castolin Sa | Verfahren zum Herstellen eines Metallpulvers |
DE102014202457A1 (de) * | 2014-02-11 | 2015-08-13 | Siemens Aktiengesellschaft | Verbesserte Verschleißbeständigkeit eines Hochtemperaturbauteils durch Kobaltbeschichtung |
US10100651B2 (en) | 2014-02-11 | 2018-10-16 | Siemens Aktiengesellschaft | Wear resistance of a high-temperature component imparted by a cobalt coating |
Also Published As
Publication number | Publication date |
---|---|
GB2063305B (en) | 1984-02-01 |
SE8006409L (sv) | 1981-04-16 |
FR2467243A1 (fr) | 1981-04-17 |
GB2063305A (en) | 1981-06-03 |
AU535069B2 (en) | 1984-03-01 |
AU6264580A (en) | 1981-06-25 |
IL61022A0 (en) | 1980-11-30 |
IL61022A (en) | 1984-02-29 |
BR8005977A (pt) | 1981-05-19 |
CA1168477A (fr) | 1984-06-05 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE2801016C2 (de) | Gegenstand aus einem Superlegierungskörper mit einem durch Flammspritzen aufgebrachten Überzug aus einem Pulver sowie Verfahren zu dessen Herstellung | |
DE68911363T2 (de) | Mit Keramik beschichteter hitzebeständiger Legierungsbestandteil. | |
DE2657288C2 (de) | Überzogener Superlegierungsgegenstand und seine Verwendung | |
DE69401260T2 (de) | Beschichtungszusammensetzung mit gutem Korrosions- und Oxydationsschutz | |
DE68921194T2 (de) | Verfahren zum Beschichten von Superlegierungen mit yttriumangereicherten Aluminiden. | |
DE2356617C3 (de) | Verfahren zum Aufbringen eines gegenüber hohen Temperaturen und Abrieb beständigen Überzugs auf Metallgegenständen | |
DE3010608A1 (de) | Ueberzugszusammensetzung fuer nickel, kobalt und eisen enthaltende superlegierung und superlegierungskomponente | |
DE2829369C3 (de) | Verfahren zum Ausbilden von harten, verschleißfestenMetallkarbide enthaltenden Überzügen | |
US4275124A (en) | Carbon bearing MCrAlY coating | |
DE3030961A1 (de) | Bauteile aus superlegierungen mit einem oxidations- und/oder sulfidationsbestaendigigen ueberzug sowie zusammensetzung eines solchen ueberzuges. | |
DE60038715T2 (de) | Wärmedämmendes Beschichtungssystem für ein Turbinenmotorbauteil | |
DE3785424T2 (de) | Verschleisskörper und Pulver sowie Verfahren zur Herstellung. | |
DE3426201C2 (fr) | ||
DE69116303T2 (de) | Herstellung von Chromiumkarbid-Nickel-Beschichtungen | |
DE3211583A1 (de) | Superlegierungs-ueberzugszusammensetzung mit hoch-temperatur-oxidationsbestaendigkeit | |
DE2758618A1 (de) | Hochtemperaturbestaendige, abriebfeste ueberzugszusammensetzung | |
US4275090A (en) | Process for carbon bearing MCrAlY coating | |
DE2419145A1 (de) | Mit ueberzug versehener gegenstand, herstellungsverfahren und material fuer den ueberzug | |
CH653375A5 (de) | Beschichtungsmaterial. | |
DE3036206A1 (de) | Verschleissfester, vor oxidation und korrosion schuetzender ueberzug, korrosions- und verschleissfeste ueberzugslegierung, mit einem solchen ueberzug versehener gegenstand und verfahren zum herstellen eines solchen ueberzugs | |
DE2842848A1 (de) | Ueberzogener gegenstand, insbesondere superlegierungsgasturbinenschaufel | |
DE2734529A1 (de) | Gegen oxydation und korrosion bestaendige, hochwarmfeste legierungen und ueberzuege | |
DE69916167T2 (de) | Hochtemperaturschutzschicht | |
DE3103129A1 (de) | Thermisch belastbares maschinenteil und verfahren zu dessen herstellung | |
DE2817321A1 (de) | Korrosionsbestaendige superlegierung auf nickelbasis, daraus hergestellte verbundschaufel und verfahren zum schutz von gasturbinenschaufelspitzen mit einer solchen legierung |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
8139 | Disposal/non-payment of the annual fee |