DE301784C - - Google Patents
Info
- Publication number
- DE301784C DE301784C DENDAT301784D DE301784DA DE301784C DE 301784 C DE301784 C DE 301784C DE NDAT301784 D DENDAT301784 D DE NDAT301784D DE 301784D A DE301784D A DE 301784DA DE 301784 C DE301784 C DE 301784C
- Authority
- DE
- Germany
- Prior art keywords
- alloy
- manganese
- zinc
- percent
- chromium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
Gegenstand der Erfindung ist eine in erster .Linie binäre Legierung zwischen Zink und Mangan. Es ist nämlich gefunden worden, daß eine Zinklegierung mit bis 4 Prozent Mangan besondere und .wertvolle Eigenschaften aufweist. Das Metall wird ,nicht nur erheblich härter, also widerstandsfähiger (nach der Brinellschen Methode gemessen, ist die Härte etwa doppelt so groß wie die des Zinks), auch die Schlagbiegefestigkeit ist um 50 Prozent höher. Im Gegensatz zu den bisher bekannt gewordenenThe invention is a first .Linie binary alloy between zinc and Manganese. Namely, it has been found that a zinc alloy containing up to 4 percent manganese has special and valuable properties. The metal is not only considerably harder, but also more resistant (according to Brinell's Measured method, the hardness is about twice that of zinc), including the Impact resistance is 50 percent higher. In contrast to those previously known
. Zinklegierungen ist aber diese Legierung auch nach schwacher Anwärmung schmiedbar und läßt sich auch pressen und walzen. Diese Legierung ka,nn also für viele technische Zwecke als Ersatz sowohl für Kupfer wie auch füt. Zinc alloys, however, this alloy is malleable and even after slight heating can also be pressed and rolled. This alloy can therefore be used for many technical purposes as a substitute for both copper and füt
' Messing und Bronze dienen. Als besonders brauchbar hat sich eine Legierung gezeigt, die etwa 2 Prozent Mangan enthält". Es kann handelsübliches (bleihaltiges) Zink für diese Legierung verwendet werden.'Brass and bronze serve. An alloy has been shown to be particularly useful which contains about 2 percent manganese ". It can use commercial (leaded) zinc for this Alloy can be used.
Dieser binären Legierung können auch noch geringere Mengen Aluminium, Silizium, Mangan, wie auch Chrom und Nickel zugefügt werden. Behufs Desoxydation können geringe Mengen von Phosphor oder Phosphiden in Anwendung kommen.This binary alloy can also contain smaller amounts of aluminum, silicon, manganese, as well as chromium and nickel are added. Small amounts can be used for deoxidation of phosphorus or phosphides are used.
Claims (2)