DE2935580A1 - Foamed hot melt adhesives - decreases use of adhesive but gives good bond esp. used for book binding, packaging and coating - Google Patents

Foamed hot melt adhesives - decreases use of adhesive but gives good bond esp. used for book binding, packaging and coating

Info

Publication number
DE2935580A1
DE2935580A1 DE19792935580 DE2935580A DE2935580A1 DE 2935580 A1 DE2935580 A1 DE 2935580A1 DE 19792935580 DE19792935580 DE 19792935580 DE 2935580 A DE2935580 A DE 2935580A DE 2935580 A1 DE2935580 A1 DE 2935580A1
Authority
DE
Germany
Prior art keywords
melt adhesive
hot melt
adhesive
hot
foaming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19792935580
Other languages
German (de)
Other versions
DE2935580C2 (en
Inventor
Dipl.-Chem. Erhard 7085 Bopfingen Bister
Dipl.-Chem. Rudolf Schieber
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henkel Dorus GmbH and Co KG
Original Assignee
Dr Rudolf Schieber GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dr Rudolf Schieber GmbH and Co KG filed Critical Dr Rudolf Schieber GmbH and Co KG
Priority to DE2935580A priority Critical patent/DE2935580C2/en
Publication of DE2935580A1 publication Critical patent/DE2935580A1/en
Application granted granted Critical
Publication of DE2935580C2 publication Critical patent/DE2935580C2/en
Expired legal-status Critical Current

Abstract

The use of foamed hot melt adhesives (I) to bond materials is new. (I)contains a blowing agent, (II) which is inactive when mixed with (I) but forms a foam when (I) is used. (II) is pref. e.g. azodicarbonamide, or dinitroso-pentamethylene tetramine, etc. pref. with an average particle size of 10-30 micron. The compsn. pref. also contains a crosslinker. (II) and the crosslinker are chosen so that foaming and crosslinking takes place simultaneously. (I) is EVA and/or thermoplastic elastomer opt contg.a resin such as a coumarone-indene or (cyclo)aliphatic hydrocarbon resin or (co)polyamide or polyester. Despite using less (I), high adhesion can be achieved. (I) can be used for wood, metal, fibres, paper, cardboard etc. e.g. carpet laying bands, book binding, packaging.

Description

Verwendung von geschäumten Schmelzklebstoffen Use of foamed hot melt adhesives

sowie Verfahren zu deren Herstellung Die Erfindung betrifft die Verwendung von geschäumten Schmelzklebstoffen zur Verbindung von Gegenständen und Verfahren zur Herstellung geschäumter bzw. schäumbarer Schmelzklebstoffe. and processes for their production. The invention relates to the use of foamed hot melt adhesives for joining objects and processes for the production of foamed or foamable hot melt adhesives.

Schmelzklebstoffe sind Klebstoffe, die keine sich verflüchtigenden organischen Lösungsmittel oder Wasser, das beim Trocknen bzw. Abbinden entfernt bzw. verbraucht wird, enthalten. Allein durch Druck und Temperatur findet beim Verkleben von Gegenständen mittels Schmelzklebstoff die Verbindung der zu vereinenden Oberflächen statt.Hot melt adhesives are adhesives that do not volatilize organic solvent or water, which is removed during drying or setting or is consumed. Gluing takes place solely through pressure and temperature of objects using hot melt adhesive the connection of to unifying surfaces instead.

Schmelzklebstoff hat gegenüber lösungsmittelhaltigen Klebstoffen den Vorteil, daß bei der Herstellung keine Lösungsmittel benötigt und infolgedessen bei der Anwendung frei werden.Hot melt adhesive has the opposite to solvent-based adhesives Advantage that no solvents are required in the production and as a result become free in the application.

In der Praxis werden Schmelzklebstoffeflächig auf die zu verbindenden Flächen aufgebtacht, die dann unter Druck und bei einer Temperatur, die ausreicht, um den Kleber aufzuschmelzen,veCpreßtmserden. Beim Erkalten erhält man dann eine dauerhafte feste Binduny. Zur Verringerung der erforderlichen Klebstoffmenge, aber auch zur Erreichung anderer Zwecke ist Schmelzkleber bereits punkt-, strich-bzw. rasterförmig aufgetragen worden, wodurch eine Klebebindung zwischen den zu verklebenden Flächen in diskont 1-nuierlicher Weise erreicht wird.In practice, hot melt adhesives are applied over the area to be joined Surfaces that are then applied under pressure and at a temperature that is sufficient in order to melt the adhesive, press earth. When it cools down, you get a permanent firm binding. To reduce the amount of glue required, however To achieve other purposes, hot melt adhesive is already point-, line- or. has been applied in a grid pattern, creating an adhesive bond between the Areas is achieved in a discounted 1-way manner.

Im Rahmen der Erfindung wurde nun gefunden, daß eine erhebliche Einsparung an Schmelzkleber und trotzdem eine überraschend hohe Haftung erzielbar ist, wenn man geschäumten Schmelzklebstoff zum Verbinden von Gegenständen einsetzt Das Schäumen von Kunststoffen für zahlreiche Anwenaungszwecke ist grundsätzlich bekannt. Die Palette der aus geschäumtem Kunststoff gefertigten Produkte ist unübersehbar und reicht beispielsweise von aus Polyurethanharz (kal.t) geschäumten Autositzen bis zu Schuhsohlenmaterialien für Badeschuhe aus Äthgen-Vinylacetat, meistens in Kombination mit Füllstoffen. In diesen Fällen wird der Kunststoff als Werkstoff eingesetzt und das Schäumen erfolgt weniger zur Materialeinsparung als zur Erzielung bestimmter technischer Effekte, die für den Anwendungszweck von Bedeutung sind. Es sind auch bereits Leime, z.B. Dispersionsleime oder Harnstoffharzleime verschäumt worden. Schmelzklebstoff ist jedoch im geschäumten Zustand in der Praxis nicht zum Einsatz gekommen.In the context of the invention it has now been found that a considerable saving to hot-melt adhesive and nevertheless a surprisingly high level of adhesion can be achieved if foamed hot melt adhesive is used to join objects. Foaming of plastics for numerous uses is known in principle. the The range of products made of foamed plastic is unmistakable and ranges, for example, from car seats foamed from polyurethane resin (kal.t) to to shoe sole materials for bathing shoes made from ethgen vinyl acetate, mostly in combination with fillers. In these cases, the plastic is used as the material and foaming occurs less to save material than to achieve it certain technical effects that are important for the application. There are also glues, e.g. dispersion glues or urea resin glues, foamed been. In practice, however, hot melt adhesive is not used in the foamed state Use come.

Der Schmelzklebstoff setzt sich im allgemeinen aus einem Kunstharz oder einem Kunstharz gemisch, oftmals in Verbindung mit natürlich vorkommenden Harzen, zusammen. Ein bekanntes Schmelzklebersystem, dessen Anwendung erfindungsgemäß bevorzugt ist, stellen Copolymerisate aus Äthylen und Vinylacetat, (nachstehend auch zu EVA abgekürzt), häufig in Kombination mit Kolophoniumharzen, dar. Im Rahmen der Erfindung werden jedoch auch Schmelzklebstoffe (Elastomere) auf Basis von Polyamid, Copolyamiden, thermoplastischem Kautschuk oder Polyester in Betracht gezogen. Beispiele für thermoplastischen Kautschuk sind z. B. sogenannte SIS-Thermoplasten (Styrol-Isopren-Styrol-Massen) bzw.The hot melt adhesive is generally composed of a synthetic resin or a synthetic resin mixture, often in combination with naturally occurring resins, together. A known hot melt adhesive system, the use of which is preferred according to the invention are copolymers of ethylene and vinyl acetate, (hereinafter also referred to as EVA abbreviated), often in combination with rosins. Within the scope of the invention However, hot melt adhesives (elastomers) based on polyamide, copolyamides, thermoplastic rubber or polyester are considered. Examples of thermoplastic Rubber are z. B. So-called SIS thermoplastics (styrene-isoprene-styrene compounds) respectively.

SBS-Thermoplasten (Styrol-Butadien-Styrol-Massen).SBS thermoplastics (styrene-butadiene-styrene compounds).

Als dem Schmelzklebstoffbasisharz häufig mit Vorteil zumischbares Polymerisationsharz haben sich neben Rolophoniumharz als Beispiel für Naturharz auch andere Harze wie Cumaron-Indenharze, veresterte Baumharze oder auch Polymerisationsharze auf halb- bzw. vollsynthetischer Basis bewährt. Solche sind beispielsweise aliphatische cylische Kohlenwasserstoffharze. Dem Schmelzklebstoff können übliche Zusätze, wie Streckmittel, Füllstoffe, zugefügt sein.As can often be advantageously mixed with the hot melt adhesive base resin Polymerization resin have proven themselves alongside rolophonium resin as an example of natural resin also other resins such as coumarone-indene resins, esterified tree resins or polymerization resins proven on a semi or fully synthetic basis. Such are, for example, aliphatic cyclic hydrocarbon resins. Usual additives such as Extenders, fillers, may be added.

Die erfindungsgemäß als Klebstoff zu verwendenden geschäumten Schmelzklebstoff können in folgender Weise hergestellt werden: Man gibt bei der Herstellung des Schmelzklebstoffs aus z.B.The foamed hot melt adhesive to be used as an adhesive according to the invention can be produced in the following way: One gives in the production of the hot melt adhesive from e.g.

EVA, Naturharz, wie Kolophonium und gegebenenfalls Streckmittel, ein Schäumungsmittel hinzu, das bei der Herstellungstemperatur des Schmelzklebers noch keine Schaumbildung bewirkt. Erfolgt die Herstellung des Schmelzklebstoffes durch Vermischen der Komponenten unter Aufschmelzen der Harze bei 1300C, so darf das zur Verwendung kommende Schäumungsmittel bei dieser Temperatur noch keine Verschäumung bewirken, es muß also im wesentlichen noch stabil sein. Wird ein so mit einem Schäumungsmittel versehener Schmelzkleber dann später bei seiner Anwendung einer höheren Temperatur, z.B. von 180 bis 200 C, ausgesetzt, so tritt die Wirkung des Schäumungsmittels ein und die geewnschte Verschäumung des Schmelzklebers findet statt.EVA, natural resin such as rosin and optionally an extender Foaming agent added, which is still at the production temperature of the hot melt adhesive does not cause foaming. The production of the hot melt adhesive takes place by Mixing the components with melting of the resins at 1300C, this is allowed for Use upcoming foaming agents at this temperature no foaming effect, so it must still be essentially stable. Will one with a foaming agent provided hot-melt adhesive then later when it is applied at a higher temperature, e.g. from 180 to 200 C, the action of the foaming agent occurs and the desired foaming of the hot melt adhesive takes place.

Es ist aber nicht erforderlich, das Verschäumungssystem bereits bei der Herstellung des Schmelzkleberpolymeren einzuarbeiten, da diese häufig bei recht hohen Temperaturen erfolgt. Daher wird im Einzelfall das Verschäumungsmittel in einer nachfolgenden Stufe, z.B. bei der Konditionierung des Schmelzklebstoffes, zur Einarbeitung kommen.But it is not necessary to have the foaming system already at to incorporate the production of the hot melt adhesive polymer, as these are often quite high temperatures. Therefore, the foaming agent is used in individual cases a subsequent stage, e.g. in the conditioning of the hot melt adhesive, come for training.

Das Schäumungsmittel kann auch erst bei der Verarbeitung des Schmelzklebstoffes kurz vor dessen Auftrag auf die zu verklebenden Flächen zugegeben werden In diesem Fall ist es in gleicher Weise möglich, das Verschäumungsmittel, z.B.The foaming agent can also only be used during processing of the hot melt adhesive shortly before it is applied to the surfaces to be bonded In the same way it is possible to use the foaming agent, e.g.

in einem geeigneten Träger oder vehikel in den Schmelzklebstoff einzutragen. Im letzteren Falle kann man z.B.to be added to the hot melt adhesive in a suitable carrier or vehicle. In the latter case one can e.g.

das Schäumungsmittel bei z.B. etwa 1500C dem Schmelzklebstoff in einem geschlossenen, unter Druck befindlichen System zuführen. Am Auslaßende des Systems, z.B. eines Schneckenextruders, findet dann das Auf schäumen statt und der yeschäumte Schmelzklebstoff kann direkt auf die zu verbindende Oberfläche aufgebracht werden. Bei dieser Auftragstechnik können mit Vorteil solche Extruder Einsatz finden, bei denen durch geeignete Maßnahmen, z.B. die Ausbildung der Förderschnecke, für eine besonders homogene Einmischung des Verschäumungsmittels Rechnung getragen wird.the foaming agent at e.g. about 1500C the hot melt adhesive in one Supply closed, pressurized system. At the outlet end of the system, e.g. of a screw extruder, the foaming then takes place and the foamed Hot melt adhesive can be applied directly to the surface to be bonded. With this application technique, such extruders can be used with advantage which through suitable measures, e.g. the formation of the screw conveyor, for a particularly homogeneous mixing of the foaming agent is taken into account.

Der erfindungsgemäß zu verwendende verschäumbare Schmelzklebstoff kann bei einer alternativen Auftragsmethodik in Auftragswalzen eingefüllt und durch diese auf das zu beschichtende Substrat aufgebracht werden. Beispielsweise können Walzen, die mit einem Raster von Kavitäten versehen sind, Anwendung finden, wobei der in die Kavitäten eingefüllte Schmelzklebstoff auf das zu verklebende Substrat aufgewalzt wird. Hierbei ist es grundsätzlich möglich, daß der Schmelzkleber in die Auftragswalzen bei niedrigen Temperaturen, z.B. bei Raumtemperatur, eingebracht und auf das Substrat aufgetragen wird. Die Verschäumung kann dann durch Erhitzung des Substrates auf diesem erfolgen. Es ist aber auch möglich, den Schmelzkleber bei höherer Temperatur, bei der er aber noch nicht sehr klebend wirkt, in die Kavitäten der Auftragswalze bzw. auf deren Flächen aufzubringen.The foamable hot melt adhesive to be used according to the invention can be filled into and through application rollers with an alternative application method these are applied to the substrate to be coated. For example, can Rolls that are provided with a grid of cavities are used, wherein the hot melt adhesive filled into the cavities on the substrate to be bonded is rolled on. It is basically possible that the hot melt adhesive in the application rollers are introduced at low temperatures, e.g. at room temperature and applied to the substrate. The foaming can then be done by heating of the substrate take place on this. But it is also possible to use the hot melt adhesive into the cavities at a higher temperature, at which it is not yet very adhesive to be applied to the application roller or to its surfaces.

So kann beispielsweise der Schmelzklebstoff, in den das Verschäumungsmittel eingemischt ist, über einen Extruder auf die Auftragswalzen gebracht werden.For example, the hot melt adhesive in which the foaming agent is mixed in, are brought to the application rollers via an extruder.

Als zu beschichtende Substrate kommen prinzipiell all solche Flächen in Betracht, die der Verklebung bedürfen. Diese Flächen können Holz, Metall, textile Substrate aus tierischer bzw. synthetischer Faser, Papier, Karton etc. bzw.In principle, all such surfaces are used as substrates to be coated into consideration that require gluing. These surfaces can be wood, metal, textile Substrates made of animal or synthetic fibers, paper, cardboard etc. or

Kombinationen hiervon darstellen.Represent combinations of these.

Das in der Erfindung einzusetzende Verschäumungsmittel kann ein übliches Verschäumungsmittel wie Azodicarbonamid, Dinitroso-pentamethylentetramin, p,p-Oxy-bis-benzol-sulfonylhydrazid, Toluolsulfonylhydrazid usw. sein Ein im Rahmen der Erfindung besonders bevorzugtes Verschäumungsmittel ist Azodicarbonamid. Die optimale mittlere Teilchengröße des Verschäumungsmittels, das gemäß der Erfindung verwendet wird, kann im Bereich von 10 bis 30 )um liegen, der aber nicht als einschränkend anzusehen ist. Bei diesen geringen Teilchengrößen des Verschäumungsmittels kann eine besonders homogene Schaumstruktur, was allerdings wiederum von der Schmelzkleberbasis abhangag sein kanne im allgemeinen erreicht werden. Die einsetzbaren Schäumungsmittel sind jedoch nicht auf die vorstehend genannten Systeme beschränkt , da alle solche im Regelfall einsetzbar sindo die beim Vermischen der Bestandteile des Schmelzklebstoffes noch stabil sind, sich bei der späteren Anwendungstemperatur des Schmelzklebers aber unter Gasentwicklung zersetzen Bei einigen Anwendungszwecken der Erfindung kann es noch nicht ausreichend sein lediglich den Schmelzkleber zu verschäumen Deshalb ist eine bevorzugte Ausführungsforin der Erfindung auf den zusätzlichen Einsatz eines Vernetzungsmittels gerichtet Beispiele für geeignete Vernetzungsmittel sind z.B. 2,5-Dimethyl-2,5-di-(tert.-butyl)-peroxyhexan, Dicumyl-peroxid, 1,10-Decan-bis-sulfonazide, p-Chinondioxim ete. Andere Vernetzungsmittel sind bekannt Durch die zusätzliche Einbringung von Vernetzungsmittel in das Schmelzklebstoffsystem, die nach den vorstehend für die Einbringung des Verschäumungsmittels angegebenen Methodiken in gleicher Weise erfolgen kann, wird es möglich, noch bessere Haftungen und Verbundungsfestigkeiten der verklebten Systeme zu erreichen. Durch die zusätzliche Einbringung von Vernetzungsmittel kann im Einzelfall auch eine Stabilisierung der Schaumstruktur wie auch eine besondere Gleichmäßigkeit der Poren erreicht werden Besondere Vorn teile können im Rahmen der Erfindung dann erreicht werden wenn das Verschäumungsmittel und der Vernetzer derart gewählt werden, daß die Verschäumung und die Vernetzung im wesentlichen gleichzeitig bewirkt werden. Dies kann im Regelfall dann erreicht werden, wenn ein Verschäumungsmittel eingesetzt wird, dessen Zersetzungstemperatur gleich oder höher ist als diejenige des Vernetzungsmittels. Anders ausgedrückt soll sich eine gewisse Überlappung der Zersetzungskurven von Vernetzungsmittel und Verschäumungsmittel ergeben, damit die erreichte Verschäumungsstruktur durch die im wesentlichen gleichzeitige Vernetzung stabilisiert werden kann.The foaming agent to be used in the invention may be a usual one Foaming agents such as azodicarbonamide, dinitroso-pentamethylenetetramine, p, p-oxy-bis-benzene-sulfonylhydrazide, Toluenesulfonyl hydrazide, etc. are particularly preferred in the present invention The foaming agent is azodicarbonamide. The optimal mean particle size of the Foaming agent used according to the invention can range from 10 to 30) around, but this is not to be regarded as restrictive. With these small particle sizes of the foaming agent can be a special one homogeneous foam structure, which in turn depends on the hotmelt adhesive base can be achieved in general. The foaming agents that can be used are but not limited to the above systems, since all such im As a rule, they can be used when mixing the components of the hot melt adhesive are still stable at the later application temperature of the hot melt adhesive but decompose with evolution of gas In some applications of the invention It may not be enough to just foam the hot melt adhesive a preferred embodiment of the invention is based on the additional insert a crosslinking agent are examples of suitable crosslinking agents e.g. 2,5-dimethyl-2,5-di- (tert-butyl) -peroxyhexane, dicumyl-peroxide, 1,10-decane-bis-sulfonazide, p-quinone dioxime. Other crosslinking agents are known by the additional Introduction of crosslinking agents into the hot melt adhesive system according to the above for the introduction of the foaming agent in the same way This way, it becomes possible to have even better adhesions and bond strengths of the bonded systems. Through the additional introduction of crosslinking agents can also be a stabilization of the foam structure as well as a special one in individual cases Uniformity of the pores can be achieved. Special advantages can be achieved in the frame of the invention can then be achieved when the foaming agent and the crosslinker are chosen such that the foaming and the crosslinking are effected essentially simultaneously. As a rule, this can then be achieved if a foaming agent is used, its decomposition temperature is equal to or higher than that of the crosslinking agent. In other words, it should there is a certain overlap of the decomposition curves of crosslinking agent and foaming agent result, so that the foam structure achieved by the substantially simultaneous Networking can be stabilized.

Die Verschämmung und gegebenenfalls die Vernetzung, sofern zusätzlich ein Vernetzer eingesetzt wird, kann durch Wärmebehandlung, wie beispielsweise Heißluft, Wasserdampf, Bestrahlung, z.B. mit Infrarot, Hochfrequenzheizung etc.The grouting and, if necessary, the networking, if additional a crosslinker is used, can be achieved by heat treatment, such as hot air, Water vapor, radiation, e.g. with infrared, high-frequency heating, etc.

erreicht werden.can be achieved.

Eine bevorzugte Kombination von Verschäumer und Vernetzer im erfindungsgemäßen Verfahren, ist Azodicarbonamid (Zersetzungstemperatur etwa 2050C) und Dicumyl-Peroxid. Die Verwendung dieses Systems erlaubt die Einmischung z.B.A preferred combination of foaming agent and crosslinker in the invention Process, is azodicarbonamide (decomposition temperature about 2050C) and dicumyl peroxide. The use of this system allows interference e.g.

in einem Bereich von 100 bis 1500C in den Schmelzklebstoff, ohne daß die Verschäumung und Vernetzung bereits eintritt.in a range from 100 to 1500C in the hot melt adhesive without foaming and networking is already taking place.

Mischeinrichtungen hierfür, wie sie allgemein verwendet werden, sind Mischwalzen, Kneter,Banbury-Mischer, Extruder etc. Die Verschäumung und Vernetzung kann bei dem angesprochenen System dann in einem Bereich zwischen 180 und 3000C, vorzugsweise zwischen 180und 2300C, erreicht werden.Mixing devices for this, as they are generally used, are Mixing rollers, kneaders, Banbury mixers, extruders, etc. Foaming and crosslinking can then in the addressed system in a range between 180 and 3000C, preferably between 180 and 2300C.

Die Verwendung von geschäumtem Schmelzklebstoff ist in mehrfacher Hinsicht vorteilhaft. Es ergeben sich nicht nur erhebliche Materialeinsparungen, sondern auch berraschend gute Verklebungswerte. Durch den Einsatz des gegeschäumten Schmelzklebers kann je nach Anwendungszweck und der Menge des eingesetzten Klebers eine verbesserte Wärmeisolation verbesserter Griff bzw Polsterungseigenschaften, verbesserte Wetterbeständigkeit, niedrigere Versprödungstemperatur und insbesondere vorzügliche mechanische Rigenschaften des erzielten Verbundes erreicht werden Auch ist ein flächiges Auftragen in einer verhältnismäßig hohen Stärke aufgrund des Schaumzustandes des Schmelzklebers, der mit Vorteil durch die Vernetzung stabilisiert werden kann, möglich. Dies ist insbesondere dann vortelhaft, wenn rauhe Flächen zur Verklebung gelangen Zum Beispiel sind mit Schmelzkleber versehene Teppichverlegebänder eine Anwendungsmöglichkeit ur die erfindungsgemäßen geschäumten Schmelzkleber, wo dies von Bedeutung ist Im Hinblick auf die zum Einsatz gelangenden Schmelzklebstoffe erstreckt sich der Rahmen der Erfindung insbesondere auf Holzkanteverleimungsklebstoffe, Beschichtungsklebstoffe und Ummantelungsklebstoffe. Diese haben typischerweise die Zusammensetzung Schmelzklebelastomer, Polymerisationsharz, z.B. Kolophoniumharz, Streckmittel, Verschäumungsmittel und gegebenenfalls Vernet zungsmittel Durch den Einsatz des geschäumten Schmelzklebstoffes werden auch im Bereich der Verpackungsverklebung Vorteile erzielt Daher wird erfindungsgemäß auch die Verwendung von Verpackungsschmelzklebstoff in Betracht gezogen. Dieser besteht typischerweise aus Schmelzklebstoffelastomer, gegebenenfalls unter Zusatz von Polymerisationsharz, paraffinen und/ode Wachsen und Schäummittel. Diesem schäumbaren Verpackungsschmelzklebstoff kann mit Vorteil ein Vernetzungssystem, beispielsweise der vorstehend angesprochenen Art, zugefügt sein Ein anderes Anwendungsgebiet der erfindungsgemäßen Verwendung liegt auf dem Sektor der Buchbindeklebstoffe.The use of foamed hot melt adhesive is multiple Aspects advantageous. There are not only significant material savings, but also surprising good adhesion values. Because of the engagement of the foamed hot melt adhesive can depending on the application and the amount of the adhesive used, improved thermal insulation, improved grip and padding properties, improved weather resistance, lower embrittlement temperature and in particular Excellent mechanical properties of the bond achieved are also achieved is a flat application in a relatively high strength due to the foam condition of the hot melt adhesive, which can advantageously be stabilized by the crosslinking, possible. This is particularly advantageous when rough surfaces are to be glued For example, carpet laying tapes with hot melt adhesive are one Possible application ur the foamed hot melt adhesive according to the invention, where this is important with regard to the hot melt adhesives used the scope of the invention extends in particular to wood edge gluing adhesives, Coating adhesives and jacketing adhesives. These typically have the Composition hot melt adhesive polymer, polymerisation resin, e.g. rosin resin, Extenders, foaming agents and optionally cross-linking agents The foamed hotmelt adhesive is also used in the field of packaging bonding Advantages achieved Therefore, according to the invention, the use of hot-melt packaging adhesive is also achieved taken into consideration. This typically consists of a hot melt adhesive elastomer, optionally with the addition of polymerization resin, paraffins and / or waxes and foaming agents. This foamable hot melt packaging adhesive can be used with advantage a networking system, for example of the type discussed above, added be Another field of application of the use according to the invention is in the sector of bookbinding adhesives.

Schmelzklebstoffe für diesen Anwendungszweck sind bekannt, in den gemäß der erfindungsgemäßen Verfahren ein Verschäumer und gegebenenfalls zusätzlich ein Vernetzer eingebracht sind.Hot melt adhesives for this application are known in the according to the method according to the invention, a foamer and optionally additionally a crosslinker are introduced.

Die Erfindung betrifft schließlich auch Schmelzhaftkleber, z.B. auf Basis vonÄthylenrVinylacetat und/oder thermoplastischem Kautschuk, gegebenenfalls in Verbindung mit Polymerisationsharz.Finally, the invention also relates to hot-melt pressure-sensitive adhesives, e.g. Based on ethylene / vinyl acetate and / or thermoplastic rubber, if necessary in connection with polymerisation resin.

Die Erfindung wird nachstehend in einem Ausführungsbeispiel erläutert, das nicht beschränkend ist.The invention is explained below in an exemplary embodiment, that is not limiting.

BEISPIEL Einem Ansatz zur Herstellung eines Schmelzklebstoffes aus Äthylen-Vinylacetat und Kolophonium in gleichen Teilen, dem etwa 20 bis 30 % Gips, bezogen auf das Gewicht der Gesamtmischung zugefügt sind, gibt man Azodicarbonamid in einer Menge von 2 bis 8 Gew.-% sowie Dicumyl-Peroxid in einer Menge von 1 bis 2 Gew.-% zu. Die Mischung wird bei 130 bis 150°C in einem Kneter (der Firma AMK, Aachen) etwa 30 Minuten vermischt und dann in üblicher Weise granuliert und abgepackt.EXAMPLE One approach to making a hot melt adhesive from Ethylene vinyl acetate and rosin in equal parts, to which about 20 to 30% gypsum, based on the weight of the total mixture are added, azodicarbonamide is added in an amount of 2 to 8 wt .-% and dicumyl peroxide in an amount of 1 to 2% by weight. The mixture is at 130 to 150 ° C in a kneader (from AMK, Aachen) mixed for about 30 minutes and then granulated and packaged in the usual way.

Der Verbraucher schmilzt das erhaltene Granulat in einem Extruder bei 180 bis 2000C auf. An der Austragsdüse tritt der Schmelzklebstoff unter Verschäumung aus und wird auf die zu verklebenden Oberflächen, z.B. Kanten von Holzmöbeln, aufgetragen.The consumer melts the granulate obtained in an extruder at 180 to 2000C. At the discharge nozzle, the hot melt adhesive is foamed and is applied to the surfaces to be glued, e.g. the edges of wooden furniture.

Claims (14)

Verwendung von yeschaumten Schmelzklebstoffen sowie Verfahren zu deren Herstellung P a t e n t a n s p r ü c h e 1. Verwendung von geschäumtem Schmelzklebstoff zum Verbinden von Gegenständen. Use of foamed hot melt adhesives and processes too their production P a t e n t a n s p r ü c h e 1. Use of foamed hot melt adhesive for connecting objects. 2. Verfahren zur Herstellung eines geschäumten Schmelzklebstoffes für die Verwendung gemäß Anspruch 1, d a -d u r c h g e k e n n z e i c h n e t , daß man einem Schmelzklebstoff ein Schäumungsmittel zusetzt, das beim Vermischen mit dem Schmelzklebstoff noch im wesentlichen inaktiv ist, bei der späteren Anwendung des Schmelzklebstoffes aber die Schäumung bewirkt 2. Process for the production of a foamed hot melt adhesive for the use according to claim 1, d a -d u r c h g e k e n n n z e i c h n e t that one adds a foaming agent to a hot melt adhesive, which when mixed with the hot melt adhesive is still essentially inactive during later use of the hot melt adhesive causes foaming 3. Verfahren nach Anspruch 2, d a d u r c h g e -k e n n z e i c h n e t , daß als Schäumungsmittel Azodicarbonamid, Dinitroso-Pentamethylentetramin, p,p-Q#bis -benzol-sulfonylhydraz id, Toluolsulfonylhydraz id verwendet wird.3. Procedure according to Claim 2, that as a foaming agent Azodicarbonamide, dinitroso-pentamethylenetetramine, p, p-Q # bis -benzene-sulfonylhydraz id, toluenesulfonylhydrazide is used. 4. Verfahren nach einem oder mehreren der vorher genannten Ansprüche, d a d u r c h g e k e n n z e i c h -n e t , daß das Verschäumungsmittel eine mittlere Teilchengröße von 10 bis 30 um im Durchmesser besitzt.4. The method according to one or more of the preceding claims, d a d u r c h e k e n n n z e i c h -n e t that the foaming agent has a medium Particle size of 10 to 30 µm in diameter. 5. Verfahren nach einem oder mehreren der vorigen Ansprüche, d a d u r c h g e k e n n z e i c h n e t daß man zusätzlich einen Vernetzer verwendet.5. The method according to one or more of the preceding claims, d a d u r c h g e k e n n n n z e i c h n e t that an additional crosslinker is used. 6. Verfahren nach Anspruch 5, d a d u r c h g e -k e n n z e i c h n e t , daß der Vernetzer Dicumylperoxid, 2,5-Dimethyl-2,5-di-(tert.-butyl)-Peroxyhexan, 1 , 1 O-Decan-bis-ulfonazid, p-Chinondioxim etc. ist.6. The method according to claim 5, d a d u r c h g e -k e n n z e i c h n e t that the crosslinker dicumyl peroxide, 2,5-dimethyl-2,5-di- (tert-butyl) -peroxyhexane, 1, 1 O-decane-bis-ulfonazide, p-quinone dioxime etc. is. 7. Verfahren nach Anspruch 5 oder 6, d a d u r c h g e k e n n z e i c h n e t , daß das Verschäumungsmittel und der Vernetzer derart gewählt werden, daß die Verschäumung und die Vernetzung im wesentlichen gleichzeitig bewirkt werden.7. The method according to claim 5 or 6, d a d u r c h g e k e n n z e i c h n e t that the foaming agent and the crosslinking agent are chosen in such a way that that the foaming and the crosslinking are effected essentially simultaneously. 8. Verfahren nach einem oder mehreren der Ansprüche 2 bis 6, d a d u r c h g e k e n n z e i c h n e t , daß als Schmelzklebstoff ein Copolymerisat aus Äthylen und Vinylacetat, gegebenenfalls zusammen mit Polymerisationsharz, verwendet wird.8. The method according to one or more of claims 2 to 6, d a d u r c h e k e n n n n z e i n e t that a copolymer is used as a hot melt adhesive of ethylene and vinyl acetate, optionally together with polymerization resin, is used will. 9. Verfahren nach einem oder mehreren der Ansprüche 2 bis 7, d a d u r c h g e k e n n z e i c h n e t daß als Schmelzklebstoffelastomer Polyamid, Copolyamid, thermoplastischer Kautschuk oder Polyester verwendet wird 9. The method according to one or more of claims 2 to 7, d a d u r c h g e k e n n n z e i c h n e t that as a hot melt adhesive elastomer polyamide, Copolyamide, thermoplastic rubber or polyester is used will 10. Verfahren nach Anspruch 3 oder 9, d a d u r c h g e k e n n. z e i c h n e t , daß zusätzlich ein Polymerisationsharz, wie Cumaron-Inden-Zarz oder cyclisches oder aliphatisches I'ohlenwasserstoffharz- zu dem Schmelzklebstoff zugefügt wird.10. The method according to claim 3 or 9, d a d u r c h g e k e n n. Z e i c h n e t that in addition a polymerization resin, such as coumarone-indene-zarz or cyclic or aliphatic hydrocarbon resin is added to the hot melt adhesive. 11. Verfahren nach einem oder mehreren der Ansprüche 2 bis 10, d a a u r c h g e k e n n z e i c h n e t , daß als Schmelzklebstoff ein Holzkantenverleimungsklebstoff, Beschichtungsklebstoff oder Ummantelungsklebstoff in der Zusammensetzung Schmelzklebstoff, gegebenenfalls Polymerisationsharz, Streckmittel, Schäummittel und gegebenenfalls Vernetzer verwendet wird.11. The method according to one or more of claims 2 to 10, d a notices that the hot-melt adhesive used is a glue for glueing wood edges, Coating adhesive or sheathing adhesive in the composition hot melt adhesive, optionally polymerization resin, extender, foaming agent and optionally Crosslinker is used. 12. Verfahren nach einem oder mehreren der Ansprüche 2 bis 10, d a d u r c h g e k e n n z e i c h n e t daß der Schmelzklebstoff ein Verpackungsschmelzklebstoff aus Schmelzkleberelastomer, gegebenenfalls Polymerisationsharz, Paraffin, Wachs und Schäum- und Vernetzungsmittel ist.12. The method according to one or more of claims 2 to 10, d a It is noted that the hot-melt adhesive is a packaging hot-melt adhesive Made of hot-melt adhesive elastomer, optionally polymerization resin, paraffin, wax and is foaming and crosslinking agent. 13. Verfahren nach einem oder mehreren der Ansprüche 2 bis 10, d a d u r c h g e k e n n z zu e i c h n e t daß der Schmelzklebstoff ein Buchbindeklebstoff ist.13. The method according to one or more of claims 2 to 10, d a It is noted that the hotmelt adhesive is a bookbinding adhesive is. 14. Verfahren nach einem oder mehreren der Ansprüche 2 bis 10, d a d u r c h g e k e n n z e i c h n e t daß der Schmelzklebstoff ein Schmelzhaftklebstoff auf Basis Äthylen-Vinylacetat und/oder thermoplastischem Sautschuk, gegebenfalls in Verbindung mit Polymerisationsharz, ist.14. The method according to one or more of claims 2 to 10, d a It is noted that the hot-melt adhesive is a hot-melt pressure-sensitive adhesive based on ethylene vinyl acetate and / or thermoplastic rubber, if necessary in connection with polymerisation resin.
DE2935580A 1979-09-03 1979-09-03 Foamable hot melt adhesive Expired DE2935580C2 (en)