DE2740564A1 - COMPOSITE FOR THERMAL DEFORMING - Google Patents

COMPOSITE FOR THERMAL DEFORMING

Info

Publication number
DE2740564A1
DE2740564A1 DE19772740564 DE2740564A DE2740564A1 DE 2740564 A1 DE2740564 A1 DE 2740564A1 DE 19772740564 DE19772740564 DE 19772740564 DE 2740564 A DE2740564 A DE 2740564A DE 2740564 A1 DE2740564 A1 DE 2740564A1
Authority
DE
Germany
Prior art keywords
film
carrier
composite
composite according
metal layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19772740564
Other languages
German (de)
Inventor
Francois Luginbuhl
Duc Paul Van
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cellophane SA France
Original Assignee
Cellophane SA France
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cellophane SA France filed Critical Cellophane SA France
Publication of DE2740564A1 publication Critical patent/DE2740564A1/en
Withdrawn legal-status Critical Current

Description

ΡΛΓΕΝ. ANWXLIEΡΛΓΕΝ. ANWXLIE

DR. E. WIEGAND DipLlNG. Vv. ΝΙΞΜΑΝΝ DR. M. KÖHLER DIPL-ING. C. GERNHARDTDR. E. WIEGAND Diploma. Vv. ΝΙΞΜΑΝΝ DR. M. KÖHLER DIPL-ING. C. GERNHARDT

MÖNCHEN O HAMBURGMONKS O HAMBURG TELEFON: 55547« 8000 M ü N C H E N 2,TELEPHONE: 55547 «8000 M ü N C H E N 2,

TELEGRAMME: KAR PATENT MATH I ID ENSTRASSE 12 T E I E X : 5 29048 KARPDTELEGRAMS: KAR PATENT MATH I ID ENSTRASSE 12 T E I E X: 5 29048 KARPD

W. 42 912/77 Zi/Ul .q. September 19 77W. 42 912/77 Zi / Ul .q. 19 September 77

LA CELLOPHANE Paris/ FrankreichLA CELLOPHANE Paris / France

Verbundstoff für die Wärmeverformung.Composite for thermal deformation.

Die Erfindung bezieht sich auf einen Verbundstoff zur Herstellung von Gegenständen durch Wärmeverformung mit einem Träger aus einem wärmeverformbaren Material, das mit einem Film aus einem nicht wärmeverformbaren Kunststoffmaterial überzogen ist, wobei der Träger und der Film mit Hilfe eines Klebstoffes miteinander verbunden sind.The invention relates to a composite for the manufacture of articles by thermoforming with a Carrier made from a thermally deformable material covered with a film made from a non-thermally deformable plastic material is coated, the carrier and the film being bonded to one another by means of an adhesive.

Verbundstoffe dieser Art sind bekannt und werden bei der Verpackung von Lebensmitteln verwendet. Der Vorteil dieser Verbundstoffe liegt insbesondere in einer guten Konservierung der verpackten Lebensmittel, da diese Verbundstoffe für bestimmte Gase undurchlässig sind. Man weiss beispielsweise, dass Polyäthylen eine geringe Durchlässigkeit für Wasserdampf und eine starke Durchlässigkeit für Gase, wie Sauerstoff, Stickstoff und Schwefligsäureanhydrid (anhydride sulfureux) hat.Composites of this type are known and used in food packaging. The advantage of these composite materials lies in particular in the good preservation of the packaged food, since these composite materials are impermeable to certain gases. It is known, for example, that polyethylene has a low permeability for water vapor and a high permeability for gases such as oxygen, nitrogen and sulphurous anhydride (anhydride sulfureux).

Polyäthylenterephthalat besitzt die entgegengesetzten Eigenschaften, so daß es vor-Polyethylene terephthalate possesses the opposite properties, so that it

809812/0729809812/0729

teilhaft ist, Verbundstoffe aus diesen Produkten herzustellen. it is beneficial to make composites from these products.

Die Verwendung dieser Verbundstoffe bei der Verpackung, insbesondere bei der Lebensraittelverpackung ist lange Zeit aufgrund der Tatsache gebremst gewesen, dass der Polyester im allgemeinen nicht wärmeverformbar ist und die Verbundstoffe auf der Grundlage eines derartigen Produktes es ebenfalls nicht sind.The use of these composites in packaging, particularly in food packaging, has been used for a long time has been stunted by the fact that the polyester is generally not heat deformable, and so are the composites on the basis of such a product are not either.

Eine Lösun g dieses Problems ist bereits in der franz. Patentschrift 2 259 696 vorgeschlagen worden. Diese Lösung besteht darin, dass ein Verbundstoff auf der Grundlage von nicht gerecktem Polyäthylen und nicht gerecktem Polyethylenterephthalat verwendet wird, das eine Kristallisationstemperatur von mindestens 15o°C hat. Es ist einleuchtend, dass ein derartiger Verbundstoff wärmeverformbar ist, zumal dasPolyethylen von Natur aus wärmeverformbar ist, während der Polyester mit einer Kristallisationstemperatur über I500 C ebenfalls wärmeverformbar ist, sofern die Wärmeverformung bei einer niedrigeren Temperatur erfolgt, was ganz und gar möglich ist. Diese Lösung weist zahlreiche Nachteile auf. Einer dieser Nachteile besteht darin, dass die Lösung des Problems sehr spezifisch ist und nur für eine einzige Polyesterart angewandt werden kann. Ein anderer Nachteil beruht auf der Tatsache, dass der Polyester im Handel in Form von Filmen erhältlich iac, die im allgemeinen biaxial gereckt und nicht wärmeverformbar sind, was deren Verwendung für die oben angegebenen Zwecke und die Herstellung eines Verbundstoffes mit einem wärmeverformbaren Träger unter zu Hilfenahme eines Klebstoffes verbietet.A solution to this problem is already in the French. U.S. Patent 2,259,696 has been proposed. This solution consists in using a composite based on unstretched polyethylene and unstretched polyethylene terephthalate which has a crystallization temperature of at least 150 ° C. It is obvious that such a composite is thermoformable, especially dasPolyethylen is thermoformable by nature, while the polyester having a crystallization temperature over I50 0 C is also thermoformable, heat distortion unless carried out at a lower temperature, which is entirely possible. This solution has numerous disadvantages. One of these disadvantages is that the solution to the problem is very specific and can only be applied to a single type of polyester. Another disadvantage arises from the fact that the polyester is commercially available in the form of films which are generally biaxially stretched and not thermally deformable, which makes their use for the purposes indicated above and the manufacture of a composite with a thermoformable carrier with the aid of of an adhesive.

Die Erfindung beseitigt diese Nachteile. The invention overcomes these disadvantages.

809812/0729809812/0729

Der Verbundstoff gemäss der Erfindung ist dadurch gekennzeichnet, dass eine dünne Metallschicht zwischen dem Film und dem Träger angeordnet ist.The composite according to the invention is characterized in that that a thin metal layer is arranged between the film and the carrier.

Es wurde überraschenderweise festgestellt, dass die Anwesenheit einer Metallschicht zwischen dem Film und dem Träger den Verbundstoff vollständig wärmeverformbar macht.It was surprisingly found that the presence of a metal layer between the film and the Carrier makes the composite fully thermoformable.

Die Metallschicht wird vorteilhafterweise durch Vakuumaufdampfung oder durch irgendeine andere bekannte Massnahme auf den Träger oder auf den Film aufgebracht. Der Verbund des Filmes und des Trägers wird dann nach einem in der US-PS 2 7o2 580 beschriebenen Verfahren hergestellt.The metal layer is advantageously applied by vacuum vapor deposition or by any other known means applied to the support or to the film. The composite of the film and the carrier is then according to one of the US Pat 2 7o2 580 method described.

Man kann im allgemeinen jede Art eines Trägers verwenden, sofern der Träger wärmeverformbar ist. Die gegenwärtig am meisten verwendeten Träger sind beispielsweise Polyvinylchlorid, Polystyrol, Polyäthylen, Acrylnitril-Styrolbutadien, Methylstyrol-Butadien-Polymethacrylat usw. Die oben aufgeführten Stoffe stellen lediglich Beispiele dar, ohne die Erfindung auf die genannten Stoffe zu beschränken. In general, any type of carrier can be used as long as the carrier is thermally deformable. The present Most commonly used carriers are, for example, polyvinyl chloride, polystyrene, polyethylene, acrylonitrile-styrene-butadiene, Methylstyrene-butadiene-polymethacrylate, etc. The substances listed above are only examples, without restricting the invention to the substances mentioned.

Hinsichtlich der Filme aus nicht wärmeverformbarem Kunststoff kann man jeden Film aus Polyester, Polypropylen, biaxial gerecktem Nylon und dergl. verwenden. Beispiele für den Polyester sind biaxial gerecktes Polyäthylenterephthalat, PoIyäthylennaphthalenat und dgl.Regarding the films made of non-deformable plastic any film made of polyester, polypropylene, biaxially oriented nylon, and the like can be used. Examples of the polyester are biaxially stretched polyethylene terephthalate, polyethylene naphthalenate and the like

Die verwendbaren Metalle sind alle Metalle, die sich in Form einer dünnen Schicht unter einigen Mikron auf einem Kunststoff oder Film niederschlagen lassen. Man kann beispielsweise verschiedene Metalle durch Metallisation unter Vakuum niederschlagen. Derartige Metalle sind beispielsweise Aluminium, Zink, Gold, Silber, Chrom und dergl. sowieThe metals that can be used are all metals that are in the form of a thin layer under a few microns on one Let the plastic or film precipitate. You can, for example, different metals by metallization under Defeat the vacuum. Such metals are, for example, aluminum, zinc, gold, silver, chromium and the like. As well

803812/0729803812/0729

-Jr--Jr-

bestimmte Legierungen hieraus. Ein Verfahren zum Metallisieren unter Vakuum ist beispielsweise in den US-PSen 2 665 bis 2 665 229 beschrieben.certain alloys from it. One method of metallizing under vacuum is shown, for example, in US Pat. No. 2,665 to 2,665,229.

Die Metalle können auch ganz allgemein mit Hilfe der Galvanoplastik auf den Kunststoff aufgebracht werden: die isolierende Oberfläche des Materials wird durch eine chemische Behandlung mit einem Palladiumsalz und einem Harz elektrisch leitend gemacht. Diese Technik wird insbesondere auf dem Gebiet der gedruckten Schaltungen angewandt. Die Metalle, wie Kupfer, Zink, Zinn, Nickel, Chrom, Silber, Gold und dergl. und deren Legierungen können in sehr dünnen Schichten auf irgendeinem isolierenden Träger niedergeschlagen werden.The metals can also be applied to the plastic in general with the help of electroplating: the insulating surface of the material is chemically treated with a palladium salt and a Resin made electrically conductive. This technique is used in particular in the field of printed circuits. The metals such as copper, zinc, tin, nickel, chromium, silver, gold and the like. And their alloys can be used in very thin layers are deposited on some insulating support.

Es ist auch möglich, ein Fällverfahren unter Verwendung eines Metallsalzes anzuwenden. Derartige Metallsalze können beispielsweise die Salze von Zink, Zinn, Nickel, Silber und dergl. sein. In jedem Fall soll die Dicke der Metallschicht nicht unter O,o1 Mikron liegen. Unterhalb dieser Dicke lässt sich keine ausreichend zusammenhängende Schicht und kein warmeverformbarer Verbundstoff erzielen.It is also possible to use a precipitation method using a metal salt. Such metal salts can for example the salts of zinc, tin, nickel, silver and the like. In any case, the thickness of the metal layer should be not less than 0.1 microns. Below this thickness, there is no sufficiently coherent layer and no achieve thermoformable composite.

Was die Klebstoffe anbetrifft, müssen diejenigen ausgewählt werden, die bei der Temperatur der Wärmeverformung des Verbundstoffes beständig sind und ein Trennen der beiden Schichten verhindern. Man wählt vorzugsweise Klebstoffe auf der Grundlage von Polyurethan (in einem seiner Lösungsmittel in Lösung) und das in der US-PS 2 7o2 580 beschriebene Verfahren.As for the adhesives, those must be selected which are stable at the temperature of the thermal deformation of the composite and a separation of the two Prevent shifts. It is preferable to choose adhesives based on polyurethane (in one of its solvents in solution) and the process described in US Pat. No. 2,7o2,580.

Die mit diesen Verbundstoffen erzielten Ergebnisse sind überaus zufriedenstellend. Wenn der Film aus nicht warmeverformbarem Material transparent ist, erzielt manThe results obtained with these composites are extremely satisfactory. If the movie isn't out heat-deformable material is transparent, one achieves

809812/0729809812/0729

durch Wärmeverformung dieses Verbundstoffes Gegenstände, die das Aussehen eines nicht oxidierenden Stahls und die Eigenschaften des Materials haben, welches die Gegenstände bildet.by heat deformation of this composite objects that have the appearance of a non-oxidizing steel and the Have properties of the material that makes up the objects.

Man hat festgestellt, dass ein der Wärmeverformung unterworfener Verbundstoff, dessen Oberfläche vom optischen Standpunkt aus verhältnismässig dürftig ist, nach der Wärmeverformung das Aussehen eines Spiegels hat.It has been found that a composite subjected to heat deformation, its surface from the optical point of view from is relatively poor, has the appearance of a mirror after heat deformation.

Die Wärmeverformung dieses Verbnndstoffes gestattet die Herstellung von Verpackungen, insbesondere von Lebensmittelverpackungen. Wenn die Lebensmittel mit dem Film in Berührung gelangen, wählt man vorzugsweise Polyester.The thermal deformation of this compound allows the Manufacture of packaging, in particular food packaging. When the food comes into contact with the film get, one preferably chooses polyester.

Die Wärmeverformung eines derartigen Verbundstoffes umfasst auch die Verwendung für Dekorationszwecke: man kann beispielsweise reliefartige Taschen für Schallplatten mit einem gewünschten metallischen Aussehen oder reliefartige Dekorationsgegenstände mit einem gewünschten metallischen Aussehen herstellen, die man aufhängen oder an einer Mauer befestigen kann.The thermal deformation of such a composite also includes its use for decorative purposes: one can for example relief-like pockets for records with a desired metallic appearance or relief-like Make decorative objects with a desired metallic appearance that you can hang up or on a wall can attach.

Vor dem Verbinden von Träger und Film kann die Metallschicht beispielsweise ganz oder teilweise mit einer Farbschicht überzogen werden, die durch Lichtdruck aufgebracht wird: man kann auf diese Weise einen durch Wärme verformten Gegenstand erzielen, welcher ein metallisches Aussehen mit der gewünschten Farbe hat.Before the carrier and film are connected, the metal layer can, for example, be completely or partially coated with a layer of paint that is applied by light pressure: in this way one can be deformed by heat Achieve object which has a metallic appearance with the desired color.

Einer der Vorteile der Gegenstände, die durch eine Wärmeverformung des Verbundstoffes gemäss der Erfindung erzielt werden, ist besonders wichtig: man hat festgestellt, dass die aus dem erfindungsgemässen Verbundstoff hergestell-One of the advantages of the articles obtained by thermoforming the composite according to the invention is particularly important: it has been found that the materials produced from the composite according to the invention

609812/0729609812/0729

274Q56A274Q56A

ten Behälter ein Temperaturverhalten haben, welches dem Temperaturverhalten der Behälter weit überlegen ist, die nur durch eine Wärmeverformung des Trägers erzielt werden. Dies ist insbesondere bei der Lebensmittelverpackung von Interesse: man kann die Lebensmittel, wie Konfitüre, Tomatenkonzentrat und dergl. bei erhöhter Temperatur direkt in den Behältern verpacken, die durch Wärmeverformung eines Verbundstoffes gemäss der Erfindung hergestellt worden sind.th containers have a temperature behavior which is far superior to the temperature behavior of the container that can only be achieved by heat deformation of the carrier. This is especially true in the case of food packaging Interest: you can put the food like jam, tomato concentrate and the like directly in the at elevated temperature Pack containers made by thermoforming a composite according to the invention.

Die Erfindung wird im nachstehenden anhand von Beispielen näher erläutert.The invention is explained in more detail below with the aid of examples.

Beispiel 1example 1

Auf einen Träger aus Polyvinylchlorid mit einer Dicke von 3oo Mikron wird durch Lichtdruck ein Klebstoff auf der Grundlage von Polyurethan in Lösung in einem Äthylacetat aufgebracht. Es kann beispielsweise ein Klebstoff verwendet werden, der von der Firma Henkel unter der Bezeichnung UK 364o verkauft wird,, wobei ein Härter UK 6000 mit verwendet wird.An adhesive is applied to the 300 micron thick polyvinyl chloride carrier by light pressure Based on polyurethane applied in solution in an ethyl acetate. For example, an adhesive can be used which is sold by the company Henkel under the name UK 364o, with a hardener UK 6000 being used.

Der Klebstoff wird dann getrocknet und anschliessend mit einenn metallisierten Polyesterfilm mit einer Dicke von 12 Mikron verbunden. Der Film wird unter dem Warenzeichen CLARYL verkauft. Die metallisierte Fläche des Polyesterfilms befindet sich auf der Seite des Klebstoffs. "Nähere Einzelheiten über das Verfahren zur Erzielung eines Verbundes gehen aus der US-PS 2 7o2 580 hervor.The adhesive is then dried and then coated with a metallized polyester film with a thickness of 12 microns connected. The film is sold under the CLARYL trademark. The metallized area of the polyester film is on the side of the adhesive. "More details on the process for achieving an association are disclosed in US Pat. No. 2,7o2,580.

Es wurde eine Maschine zur Wärmeverformung von der Firma_Illig, Bauart SB 53, verwendet, die mit einer positiven, rechteckigen Form mit 35 cm χ 25 cm und einer Tiefe von 2,5 cm ausgerüstet war. Die Maschine war mit einem Heizelement versehen, das eine Leistung von 5KW hatte. Mit HilfeThere was a machine for the thermal deformation of the Firma_Illig, type SB 53, used that with a positive, rectangular shape with 35 cm χ 25 cm and a depth 2.5 cm. The machine was provided with a heating element with an output of 5KW. With help

809812/0729809812/0729

-f--f-

dieser Maschine wurde der Verbundstoff durch Ansaugen wärmeverformt. In this machine, the composite was thermoformed by suction.

Im nachstehenden sind die Heizzeiten und die erhitzte Fläche, sowie die dabei erzielten Ergebnisse angegeben:The heating times and the heated area as well as the results achieved are given below:

Erhitzte FlächeHeated surface

PolyvinylchloridPolyvinyl chloride

Heizzeiten in SekundenHeating times in seconds

2o2o

erzieltes Ergebnisresult achieved

MetallisierterMetallized 1212th unzureichende Wärmeinsufficient heat HeizgrenzeHeating limit PolyesterfilmPolyester film verformungdeformation Bruch des FilmsBreak of the film 1717th gute Warmeverformunggood heat deformation 1818th titi 2o2o ηη 2222nd ηη 2525th ηη 2828 3o3o

Mangelhafte Wärmeverformung Insufficient heat deformation

Die erzielten Ergebnisse bei den Heizzeiten zwischen 17 und 28 Sekunden unter den oben genannten Versuchsbedingungen sind besonders gut. Man kann bei den gleichen Bedingungen und unter Verwendung von geeigneten Formen mit gegebenenfalls vorgesehenen Gegenpatrizen Verpackungen, wie Behälter zum Abpassen von Butter, Konfitüre und dergleichen mit einem besonders gepflegten Aussehen erzielen.The results obtained with the heating times between 17 and 28 seconds under the above-mentioned test conditions are particularly good. One can under the same conditions and using suitable molds with optionally provided counter-male packaging, such as containers for holding butter, jam and the like achieve with a particularly well-groomed appearance.

809812/0729809812/0729

λολο

Beispiel 2Example 2

Bei diesem Ausführungsbeispiel wurde ein VerbundstoffIn this embodiment, a composite was used

mit einem Träger aus Polystyrol mit einer. Dicke von 5oo Mironwith a support made of polystyrene with a. Thickness of 5oo Miron

mit Härter UK 6000 verwendet, der mit dem Klebstoff UK 3648\ der Firma Henkel überzogen und mit einem metallisierten Polyesterfilm mit einer Dicke von 12 Mikron verbunden war. Der metallisierte Polyesterfilm wird unter dem Warenzeichen CLARYL verkauft. Der vorstehend genannte Verbundstoff wurde nach dem gleichen Verfahren wie in Beispiel 1 und auf der gleichen Maschine mit der gleichen Form einer Warmeverformung unterworfen. Die Polyesterseite des Verbundstoffes wurde 12 Sekunden lang 3rhitzt. Man erzielte eine sehr gute Wärmeverformung.used with hardener UK 6000, the one with the adhesive UK 3648 \ from Henkel coated and bonded with a metallized polyester film 12 microns thick. The metallized Polyester film is sold under the trademark CLARYL. The above composite was made according to the same Procedure as in Example 1 and subjected to heat deformation on the same machine with the same shape. the Polyester side of the composite was heated for 12 seconds. Very good heat distortion was achieved.

Beispiel 3Example 3

Es wurde ein Verbundstoff nach dem im Beispiel 1 beschriebenen Verfahren mit einem Träger aus Polyäthylen mit einer Dicke von 8o Mikron hergestellt, der mit dem Klebstoff UK 364o/aer Firma Henkel überzogen und mit dem eine Dicke von 12 Mikron aufweisenden CTLARYL-FiIm beschichtet war.It was a composite according to the method described in Example 1 with a carrier made of polyethylene with a thickness of 80 microns, which is coated with the adhesive UK 3640 / aer company Henkel and with the one thickness was coated with 12 micron CTLARYL film.

Mit Hilfe einer Maschine Multivac M 72 mit einer einzigen Heizfläche einer Leistung über 6 KV/ und mit einem Arbeitstakt von 2o HUben / Minute (2o wärmeverformte Gegenstände pro Minute) wurden Verpackungen für Fleisch- und Wurstwaren mit einer maximalen Tiefe von 2o mm hergestellt.With the help of a Multivac M 72 machine with a single Heating surface with a power over 6 KV / and with a work cycle of 2o strokes / minute (2o heat-deformed objects per minute), packaging for meat and sausage products with a maximum depth of 20 mm was produced.

Beispiel 4Example 4

Es wurde der gleiche Verbundstoff wie in Beispiel 1 hergestellt.The same composite as in Example 1 was made.

809812/0729809812/0729

Mit Hilfe einer Maschine der Firma Illig mit einem Heizelement einer Leistung über 7 KW und einem Heizelement einer Leistung unter 4 KW wurden Gegenstände für Wanddekorationen mit einer Form von 5o cm χ 5o cm hergestellt. Der Polyester wurde gegenüber dem Heizelement mit der grösseren Heizleistung angeordnet. Man erzielte bei der Wärmeverformung eine Tiefe bis zu 8 cm. Die Heizzeit der beiden Elemente lag in der GrossenOrdnung von 2o Sekunden. Das Aneinandersetzen dieser wärmeverformten Gegenstände auf einer Zwischenwand ergibt aufgrund des metallischen Aussehens dieser Gegenstände eine sehr gefragte Dekorationswirkung, beispielsweise bei der Belebung von Geschäften und Läden. Objects for wall decorations with a shape of 50 cm × 50 cm were produced with the aid of a machine from Illig with a heating element with an output of over 7 KW and a heating element with an output of less than 4 KW. The polyester was arranged opposite the heating element with the greater heating power. A depth of up to 8 cm was achieved with the heat deformation. The heating time of the two elements was in the order of 20 seconds. Putting these thermally deformed objects together on a partition wall results in a decorative effect that is in great demand due to the metallic appearance of these objects, for example in the enlivening of shops and stores.

Beispiel 5Example 5

Es wurde ein Verbundstoff wie in Beispiel 1 aus einemIt was a composite as in Example 1 from a

Träger aus Polyvinylchlorid mit einer Dicke von 3oo MikronPolyvinyl chloride carrier 300 microns thick

mit Härter UlL 6QOQ. hergestellt, der mit dem Klebstoff UK 364öVder Firma Henkel überzogen und mit einem metallisierten Polyäthylennaphthalenat-Finm verbunden war, der von der Firma Teijin unter der Handelsbezeichnung Q-FiIm verkauft wird.with hardener UlL 6QOQ. made with the adhesive UK 364öV from Henkel coated with a metallized polyethylene naphthalenate finm which is sold by the Teijin company under the trade name Q-FiIm.

Die hier erzielten Ergebnisse entsprachen im wesentlichen den Ergebnissen in Beispiel 1.The results obtained here essentially corresponded to the results in Example 1.

Beispiel 6Example 6

Es wurde ein erster kreisförmiger Behälter mit einem Durchmesser von I5 cm und einer Tiefe von 3 cm aus Polyvinylchlorid und ein zweiter Behälter mit den gleichen Abmessungen aus einem in Beispiel 1 beschriebenen Verbundstoff hergestellt, dessen Polyesterseite den hohlen Teil des BehältersIt became a first circular container 15 cm in diameter and 3 cm deep made of polyvinyl chloride and a second container of the same dimensions made from a composite material described in Example 1, whose polyester side the hollow part of the container

809812/0729809812/0729

- Vf-AX - Vf-AX

bildete. Beide Behälter wurden einem Versuch zur Untersuchung des Temperaturverhaltens unterworfen: jeder Behälter wurde mit einem unter der Bezeichnung FLUITHERMA verkauften Öl mit einer bestimmten Temperatur für die Dauer von 5 Minuten gefüllt. Wenn die Temperatur des Öls 800C erreicht, verformt sich der erste Behälter und wird gelb. Man muss eine Öltemperatur von 1500C abwarten, um eine leichte Verformung des zweiten Behälters festzustellen. Die Haut des zweiten Behälters vergilbt jedoch nicht.formed. Both containers were subjected to a test to investigate the temperature behavior: each container was filled with an oil sold under the name FLUITHERMA at a certain temperature for a period of 5 minutes. When the temperature of the oil reaches 80 0 C, the first container deforms and turns yellow. You have to wait for an oil temperature of 150 ° C. to detect a slight deformation of the second container. However, the skin of the second container does not yellow.

Es wurde daraufhin ein dritter Behälter aus einem Verbundstoff nach Beispiel 1 hergestellt, dessen Polyvinylchlorid-Seite den hohlen Teil des Behälters bildete.A third container was then made from a composite material according to Example 1, its polyvinyl chloride side formed the hollow part of the container.

Der Behälter verformt sich nicht bis zu einer Temperaron 13o°C. Das Polyvii
bis zu dieser Temperatur.The container does not deform up to a temperature of 130 ° C. The Polyvii
up to this temperature.

tür von 13o°C. Das Polyvinylchlorid vergilbt ebenfalls nichtdoor of 13o ° C. The polyvinyl chloride does not yellow either

Die vorstehenden Beispiele stellen lediglich eine nicht begrenzende Erläuterung dar. Es ist selbstverständlich, dass der Fachmann alle den verwendeten Einrichtungen äquivalente Einrichtungen substituieren und alle möglichen Abwandlungsformen vornehmen kann, ohne vom allgemeinen Erfindungsgedanken abzuweichen.The above examples are merely not representative of one It is understood that those skilled in the art would have all equivalents to the means used Substitute facilities and make all possible forms of modification, without departing from the general inventive concept to deviate.

809812/0729809812/0729

Claims (8)

- jrf -- jrf - PATENTANSPRÜCHEPATENT CLAIMS Verbundstoff zur Herstellung von Gegenständen durch iTarmeverformung, dadurch gekennzeichnet, dass er einen Träger aus einem wärmeverformbaren Material und einen Film aus einem nicht wärmeverformbaren Material aufweist und dass der Träger oder der Film mit einer dünnen Metallschicht überzogen ist und der Träger und der Film mit Hilfe eines Klebstoffes auf der Grundlage von Polyurethan verbunden sind.Composite material for the manufacture of objects by deformation of the arms, characterized in that it has a carrier made of a heat-deformable material and a film made of a non-heat-deformable material and that the carrier or the film is covered with a thin metal layer and the carrier and the film are coated with the aid of an adhesive are connected on the basis of polyurethane. 2. Verbundstoff nach Anspruch 1, dadurch gekennzeichnet, dass die Metallschicht durch Vakuumverdampfung, Galvanoplastik oder Ausfällen vor dem Verbinden des Films mit dem Träger auf den Film aufgebracht wird.2. Composite according to claim 1, characterized in that the metal layer is formed by vacuum evaporation, electroplating or precipitation is applied to the film prior to bonding the film to the support. 3. Verbundstoff nach Anspruch 1, dadurch gekennzeichnet, dass die Metallschicht durch Vakuumverdampfung, Galvanoplastik oder Ausfällen vor dem Verbinden des Trägers mit dem Film auf den Träger aufgebracht wird.3. The composite according to claim 1, characterized in that the metal layer is formed by vacuum evaporation, electroplating or precipitation is applied to the carrier prior to bonding the carrier to the film. 4. Verbundstoff nach einem der Ansprüche 1-3, dadurch gekennzeichnet, dass der Träger aus Polyvinylchlorid, Polystyrol, Polyäthylen, Acrylnitril-Styrolbutadien oder Methylstyrolbutadien-Polymethacrylat besteht.4. Composite according to one of claims 1-3, characterized in that the carrier made of polyvinyl chloride, Polystyrene, polyethylene, acrylonitrile-styrene-butadiene or methylstyrene-butadiene-polymethacrylate. 5. Verbundstoff nach einem der Ansprüche 1-4, dadurch gekennzeichnet, dass der Film aus einem biaxial gereckten Polyester, Polypropylen oder Nylon besteht.5. The composite according to any one of claims 1-4, characterized in that the film consists of a biaxially stretched one Polyester, polypropylene or nylon. 6. Verbundstoff nach einem der Ansprüche 1-5, dadurch gekennzeichnet, dass die Metallschicht vor dem Zusammenbau von Film und Träger durch Lichtdruck gefärbt oder getönt ist.6. Composite material according to one of claims 1-5, characterized in that the metal layer is colored or tinted by light pressure before the assembly of the film and carrier. 809812/0729 original inspected809812/0729 original inspected 7. Verbundstoff nach einem der Ansprüche 1-6, dadurch gekennzeichnet, dass der Film aus biaxial gerecktem Polyathylenterephthalat besteht, mit einem unter Vakuum aufgebrachten Aluminium überzogen ist und mittels des Klebstoffes auf der Grundlage von Polyurethan mit dem Träger aus Polyvinylchlorid verbunden ist.7. Composite according to one of claims 1-6, characterized in that the film is made of biaxially stretched polyethylene terephthalate consists, is coated with an aluminum applied under vacuum and by means of the adhesive on the Polyurethane base is connected to the polyvinyl chloride carrier. 8. Verwendung eines Verbundstoffs nach einem der Ansprüche 1 bis 7 zur Herstellung von Verpackungen von Lebensmitteln durch Wärmeverformung.8. Use of a composite according to one of claims 1 to 7 for the production of food packaging by heat deformation. 809812/0729809812/0729
DE19772740564 1976-09-10 1977-09-08 COMPOSITE FOR THERMAL DEFORMING Withdrawn DE2740564A1 (en)