DE2611516C3 - Process for making reflective elastic films - Google Patents

Process for making reflective elastic films

Info

Publication number
DE2611516C3
DE2611516C3 DE2611516A DE2611516A DE2611516C3 DE 2611516 C3 DE2611516 C3 DE 2611516C3 DE 2611516 A DE2611516 A DE 2611516A DE 2611516 A DE2611516 A DE 2611516A DE 2611516 C3 DE2611516 C3 DE 2611516C3
Authority
DE
Germany
Prior art keywords
amount
temperature
weight
film
approx
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE2611516A
Other languages
German (de)
Other versions
DE2611516A1 (en
DE2611516B2 (en
Inventor
Fermin Sabadell Barcelona Ginesta Palau (Spanien)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of DE2611516A1 publication Critical patent/DE2611516A1/en
Publication of DE2611516B2 publication Critical patent/DE2611516B2/en
Application granted granted Critical
Publication of DE2611516C3 publication Critical patent/DE2611516C3/en
Expired legal-status Critical Current

Description

Die Erfindung betrifft ein Verfahren zur Herstellung reflektierender elastischer Folien, in dem einer als Auflage dienenden Folie reflektierende Eigenschaften verliehen werden, wodurch in der Dunkelheit eine Rückstrahlung des einfallenden Lichtes erfolgt.The invention relates to a method for producing reflective elastic films, in which one As an overlay, reflective properties can be imparted to the film, which helps in the dark the incident light is reflected back.

Die als Auflage dienende Folie kann verschiedener Art sein wie z. B. Gewebe, Folien aus ungewebten Fasern, Papier, Kunststoff etc., jedoch stets unter der Voraussetzung, daß es sich um ein elatisches Materia! handelt.Serving as a support film can be of various types such. B. fabrics, films made of non-woven Fibers, paper, plastic, etc., but always on the condition that it is an elastic material! acts.

Die reflektierenden Eigenschaften werden durch eine einseitig auf die Folie angebrachte Beschichtung mit reflektierenden Mikrokugeln hervorgerufen, die in bevorzugter Ausführung einen RefraktionsindexThe reflective properties are achieved by a coating applied to one side of the film caused by reflective microspheres, which in a preferred embodiment have a refractive index

von 1,8 und einen Durchmesser von 0,09 mm. Diese Mikrokugeln werden auf der Folienoberfläche mit Hilfe einer Zwischenschicht befestigt, die die Biegsamkeit des Folienmaterials nicht beeinträchtigt und gleichzeitig die Undurchlässigkeit garantieren.
Das Verfahren umfaßt die folgenden Schritte:
Herstellung einer Folie, die für den Fall, daß sie aus einem Gewebe aus Kunststoff asern besteht, vorher thermofixiert werden muß.of 1.8 and a diameter of 0.09 mm. These microspheres are attached to the film surface with the help of an intermediate layer that does not impair the flexibility of the film material and at the same time guarantees impermeability.
The procedure consists of the following steps:
Production of a film which, in the event that it consists of a plastic fabric, must be heat-set beforehand.

Auftragung einer vorher gemischten Masse aus:Application of a previously mixed mass of:

a) Polychloroprena) polychloroprene

b) Phenolharz, das verträglich sein muß unö unter Wärmeeinfluß reagiertb) Phenolic resin, which must be compatible and react under the influence of heat

c) Weichmacherc) plasticizers

d) Methyl-Isobutyl-Ketond) methyl isobutyl ketone

e) Wassere) water

Die hergestellte Masse wird auf kritische Gehalte eingestellt, die auf das Oberflächengewicht der beschichteten Folie bezogen sind, und zwar in folgenden Mengen:The mass produced is adjusted to critical contents that depend on the surface weight of the coated Foil, in the following quantities:

16 Gewichtsanteile Polychloropren16 parts by weight of polychloroprene

10,5 Gewichtsanteile Phenolharz
5 Gewichtsanteile Weichmacher10.5 parts by weight phenolic resin
5 parts by weight of plasticizer

Diese Verbindungen werden mit in Wasser verdünntem Methyl-Isobutyl-Keton mit 32% Feststoffen vermischt, wodurch sich eine Viskosität von 15 000 cP ergibt.These compounds are made using methyl isobutyl ketone diluted in water at 32% solids mixed, resulting in a viscosity of 15,000 cP.

Die beschichtete Oberfläche wird durch Walzung homogenisiert, wobei eine Temperatur von 120° C und ein Vorschub von 8 mm eingehalten werden, ohne daß eine Änderung der Viskosität von 15000 cP erfolgt. The coated surface is homogenized by rolling, at a temperature of 120.degree and a feed of 8 mm can be maintained without a change in viscosity of 15,000 cP.

Auf die gewalzte Oberfläche wird eine homogene Schicht Metallpigmente in einer Menge von ca. 0,05 g/cm2 aufgebracht, wobei Temperatur und Viskosität konstant gehalten werden. Auf die mit Pigmenten versehene Oberfläche werden reflektierende Mikrokugeln in einer Menge von 0,3 g/cm2 aufgetragen. A homogeneous layer of metal pigments in an amount of approx. 0.05 g / cm 2 is applied to the rolled surface, the temperature and viscosity being kept constant. Reflective microspheres are applied to the pigmented surface in an amount of 0.3 g / cm 2.

Die Trocknung erfolgt durch Härtung bei 100° C während eines Zeitraumes von ca. 2 Stunden.Drying takes place by curing at 100 ° C during a period of approx. 2 hours.

Auf die reflektierende Oberfläche wird eine Silikonschicht aufgebracht und bei 95° C getrocknet.A silicone layer is applied to the reflective surface and dried at 95 ° C.

Die Beschichtungsmasse wird in einem üblichen Mischgerät hergestellt, und wenn auch als bevorzugte Bestandteile eine Verbindung aus Polychloropren, einem verträglichen und unter Wärmeeinfluß reagierendem Phenolharz und einem Weichmacher verwendet wird, kann dieses durchThe coating composition is prepared in a conventional mixer, albeit preferred Components a compound of polychloroprene, a compatible and reactive under the influence of heat Phenolic resin and a plasticizer are used, this can be done by

Butadien-AcrylnitrilButadiene acrylonitrile

Butadien-StyrolButadiene styrene

PolyurethanPolyurethane

PolyvinylchloridPolyvinyl chloride

natürlicher Kautschuk und allgemein allenatural rubber and all in general

Arten von künstlichem Kautschuk
ersetzt werden.Types of artificial rubber
be replaced.

In allen Fällen müssen die Polymeren und verträglichen Zusätze mit angebrachten Arbeitstemperaturen und der notwendigen Viskosität angewendet werden.In all cases, the polymers and compatible additives must be used with appropriate working temperatures and the necessary viscosity can be used.

Die Auftragung der Beschichtungsmasse auf die Folie erfolgt mittels einer Beschichtungs- und Transfermaschine, die mit Abstreifvorrichtung, Kalandern und Trockenofen ausgerüstet ist.The coating compound is applied to the film using a coating and transfer machine, which is equipped with a stripping device, calenders and a drying oven.

Die Metallpigmente und Mikrokugeln werden mittels einer Vibrationsdosiervorrichtung aufgeschleudert. The metal pigments and microspheres are centrifuged by means of a vibratory dosing device.

Die Beschichtungsmaschine arbeitet kontinuierlich und ist spes'.iell auf die Durchführung des erfindungs-The coating machine works continuously and is special to the implementation of the invention

26 Ii 51626 ii 516

gemäßen Verfahrens ausgerichtet. Sie umfaßt Mittel, mit denen der Auswurf eines Pigmenttyps unterbrochen und durch einen anderen ersetzt werden kann, so daß Zonen mit verschiedener Färbung entstehen, wodurch Muster auf die Folie aufgebracht werden können. Die Kalander erfüllen die Aufgabe, die aufgetragene Schicht zu glätten und die Haftung zwischen dieser Schicht und der Auflagefolie zu gewährleisten. Die Endfärbung der Folie hängt von dem verwendeten Metallpigment ab, d. h. ein Metallpigment aus Aluminium ergibt eine graue oder weiße Farbe, während das Pigment aus Kupfer einen rötlichen oder organgefarbenen Ton ergeben.aligned according to the procedure. It includes means by which the ejection of one type of pigment is interrupted and can be replaced by another, so that zones with different colors arise, whereby patterns can be applied to the film. The calenders fulfill the task of the applied To smooth the layer and to ensure the adhesion between this layer and the supporting film. The final color of the film depends on the metal pigment used, i.e. H. a metal pigment made from aluminum gives a gray or white color, while the pigment of copper gives a reddish or orange color Tone surrender.

Vorzugsweise enthält das Grundprodukt für die Beschichtung einen Farbstoff, der die Endfärbung vorteilhaft beeinflußt, ohne daß der Refraktionsindex beeinflußt wird.The base product for the coating preferably contains a dye which gives the final color influenced advantageously without the refractive index is influenced.

Wie bereits ausgeführt, weisen die reflektierenden Mikrokugeln einen Durchmesser von 0,09 mm und einen Refraktionsindex von 1,8 auf. Diese Mikrokugeln werden mit 50% ihres Durchmessers in der Beschichtungsmasse verankert und können aus Glas oder aus Polymethylmethacrylat bestehen.As already stated, the reflective microspheres have a diameter of 0.09 mm and has a refractive index of 1.8. These microspheres are 50% of their diameter in the coating composition anchored and can consist of glass or polymethyl methacrylate.

Falls erforderlich, könnten zwar Mikrokugeln aus Glas mit einem größeren Durchmesser verwendet werden, jedoch würde in diesem Fall der Refraktionsindex sinken und gleichzeitig der Widerstand gegen- If necessary, glass microspheres of larger diameter could be used but in this case the refractive index would decrease and at the same time the resistance to

über Abrieb, wobei außerdem eine Versteifung der Folie in Kauf genommen werden müßte.via abrasion, and stiffening of the film would also have to be accepted.

Die abschließende Behandlung, in der die beschichtete und polymerisierte Folie mit Silikon behandelt wild, ist äußerst wichtig für die Reflexionsleistung, denn dieser Überzug schützt die Oberfläche vor Wasser, Staub u. ä. und gewährleistet die Rückstrahlung des Lichtes auch bei ungünstigen Witterungsbedingungen. In diesem Zusammenhang konnte festgestellt werden, daß die Beschichtung selbst bei Temperaturen bis zu — 25 c C nicht härter wurde und auch keine Risse aufwies.The final treatment, in which the coated and polymerized film is treated with silicone, is extremely important for the reflection performance, because this coating protects the surface from water, dust and the like and ensures that the light is reflected even in unfavorable weather conditions. In this connection it was found that the coating did not harden even at temperatures of up to −25 ° C. and also did not show any cracks.

Weiterhin wurde festgestellt, daß ein mit dieser nach dem erfindungsgemäßen Verfahren hergestellten Folie angefertigtes Kleidungsstück in einer Entfernung bis 180 m sichtbar ist, wenn es von einem Lichtstrahl getroffen wird, und diese Entfernung kann als ausreichend angesehen werden, um einem Fahrzeug selbst bei hoher Geschwindigkeit die notwendige Zeit zum Anhalten zu geben.It was also found that a manufactured with this by the method according to the invention A garment made of film is visible from a distance of up to 180 m if it is seen by someone Light beam is hit and this distance can be considered sufficient to a vehicle giving the necessary time to stop even at high speed.

Auf Grund der vorteilhaften Eigenschaften der erfindungsgemäßen Folie kann diese als Ausgangsmaterial z. B. für Sicherheitskleidung, Hinweistafeln und Schlauchbooten verwendet werden und überhaupt für jeglichen Gegenstand, bei dem es darauf ankommt, daß dieser beim Auftreffen eines Lichtstrahls weithin sichtbar ist.Due to the advantageous properties of the film according to the invention, it can be used as a starting material z. B. for safety clothing, notice boards and inflatable boats and in general for any object that depends on being able to travel a long way when a beam of light hits it is visible.

Claims (4)

Patentanspruch:Claim: 1. Verfahren zur Herstellung reflektierender elastischer Folien, dadurch gekennzeichnet, daß dieses die Kombination folgender Verfahrensschritte umfaßt:1. A method for producing reflective elastic films, characterized in that that this comprises the combination of the following process steps: 1. auf eine als Auflage dienende elastische Folie wird eine Mischung aus1. on an elastic film serving as a support is a mixture of a) einem Elsatomeren aus der Gruppe Polychloropren, Butadien-Acrylnitril, Butadien-Styrol, Polyurethan, Polyvinylchlorid und natürlicher oder künstlicher Kautchuk,a) an Elsatomeren from the group polychloroprene, butadiene-acrylonitrile, butadiene-styrene, Polyurethane, polyvinyl chloride and natural or artificial rubber, b) einem verträglichen und unter Wärmeeinfluß reagierendem Phenolharz,b) a compatible phenolic resin that reacts under the influence of heat, c) einem Weichmacher,c) a plasticizer, d) Methyl-Isobutyl-Keton undd) methyl isobutyl ketone and e) Wassere) water kontinuierlich bei 120° C und mit einem Vorschub von 8 m/Min, aufgetragen, wobei das Elastomer in einer Menge von 16 Gew.-Teilen in bezug auf das Gewicht der Folie, das Phenolharz in einer Menge von 10,5 Gew.-Teilen und der Weichmacher in einer Menge von 5 Gew.-Teilen vorhanden sind, und wobei 32 % Feststoffe in dem mit Wasser verdünnten Methyl-Isobutyl-Keton vorliegen; applied continuously at 120 ° C and with a feed rate of 8 m / min, wherein the elastomer in an amount of 16 parts by weight based on the weight of the film, the phenolic resin is present in an amount of 10.5 parts by weight and the plasticizer is present in an amount of 5 parts by weight, and wherein 32% solids are present in the water-diluted methyl isobutyl ketone; 2. die beschichtete Oberfläche wird der Wirkung von Druckwalzen ausgesetzt und erhält unter Beibehaltung der Temperatur der Masse eine Oberflächenschicht aus Metallpigmenten in einer Menge von ca. 0,05 g/ cm2;2. the coated surface is exposed to the action of pressure rollers and, while maintaining the temperature of the mass, receives a surface layer of metal pigments in an amount of approx. 0.05 g / cm 2 ; 3. unter Beibehaltung von Temperatur und Vorschub werden reflektierende Mikrokugeln mit einem Durchmesser von 0,09 mm und einem Refraktionsindex von 1.8 in einer Menge von 0,3 g/cm2 aufgetragen; bei einer Temperatur von ca. 100° C und während einer Dauer von ca. 2 Stunden wird die erhaltene Folie gehärtet; und3. while maintaining the temperature and advance, reflective microspheres with a diameter of 0.09 mm and a refractive index of 1.8 are applied in an amount of 0.3 g / cm 2 ; the film obtained is cured at a temperature of approx. 100 ° C. and for a period of approx. 2 hours; and 4. auf die mit den Mikrokugeln versehene Oberfläche wird eine Silikonschicht mit einer Vorschubgeschwindigkeit von 11 m/Sek. und einer Temperatur von 95° C aufgebracht. 4. A silicone layer with a Feed speed of 11 m / sec. and a temperature of 95 ° C applied.
DE2611516A 1975-03-18 1976-03-18 Process for making reflective elastic films Expired DE2611516C3 (en)