DE2440846A1 - Perforated sun shade webs - formed by plastics coated nets in which yarns at intersections are located in net plane - Google Patents
Perforated sun shade webs - formed by plastics coated nets in which yarns at intersections are located in net planeInfo
- Publication number
- DE2440846A1 DE2440846A1 DE2440846A DE2440846A DE2440846A1 DE 2440846 A1 DE2440846 A1 DE 2440846A1 DE 2440846 A DE2440846 A DE 2440846A DE 2440846 A DE2440846 A DE 2440846A DE 2440846 A1 DE2440846 A1 DE 2440846A1
- Authority
- DE
- Germany
- Prior art keywords
- web
- plastic
- nets
- network
- threads
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
"Durchbrochene Sicht- und/oder Sonnenschutzbahn" Die Erfindung betrifft eine durchb mchene und daher winddurchlässige Bahn mit einem tragenden Netz aus KunststoXff-umhUlltem zugfestem Material, die sich insbesondere als Sicht- und/ oder Sonnenschutzbahn eignet, aber auch für andere Zwecke verwendbar ist. "Openwork visual and / or sun protection sheet" The invention relates to a perforated and therefore wind-permeable membrane with a load-bearing net Plastic-encased, tensile material, which is particularly useful as a visual and / or sun protection membrane, but can also be used for other purposes.
Derartige Bahnen sind aus dem deutschen Gebrauchsmuster 1 980 443 der Anmelderin bekannt.Such webs are from the German utility model 1 980 443 known to the applicant.
Das bekannte Bahnmaterial besteht imwesentlichen aus einem Gittergewebe, welches allseitig mit einem aufgeschäumten Kunststoff ummantelt und somit in diesen eingebettet ist.The known sheet material consists essentially of one Mesh fabric, which is encased on all sides with a foamed plastic and thus in it is embedded.
Der geschäumte Kunststoff umgibt dabei die Fäden mehr oder weniger gleichmäßig.The foamed plastic more or less surrounds the threads evenly.
Dieses bekannte Bahnmaterial soll durch die Erfindung dahingehend verbessert werden, daß das Verhältnis der um die gesamte Fläche der Durchbrechungen verringerten Gesamtfläche der Bahn zu der Gesamtfläche der Durchbrechungen vergrößert wird. Der naheliegende Weg hierzu ist eine dichtere Einstellung des Gittergewebes. Das führt aber nicht nur einen Mehraufwand an Gewebematerial, sondern auch einen solchen an umhüllendem Kunststoffmaterial mit sich. Ferner wird das Eigengewicht pro Flächeneinheit vergrößert und damit die höchstzulässige Größe einer frei ausgespannten Bahn verkleinert. Die Erfindung will das dargelegte Ziel unter Vermeidung der Nachteile des naheliegenden Weges und in vielen Fällen sogar unter Einsparung von Material erreichen.This known sheet material is intended by the invention to that effect can be improved that the ratio of the total area of the perforations reduced total area of the path to the total area of the openings increased will. The obvious way to do this is to make the mesh more dense. However, this not only leads to additional expenditure in terms of fabric material, but also one those of enveloping plastic material with it. Furthermore, the dead weight increased per unit area and thus the maximum permissible size of a freely stretched one Orbit reduced. The invention aims to achieve the stated aim while avoiding the disadvantages the obvious way and in many cases even with savings of material reach.
Gemäß Erfindung wird diese Aufgabe dadurch gelöst, daß die Fäden des Netzes jeweils allseitig in an den Fadenkreuzungspunkten ineinander übergehende flexible Kunststoffbänder eingebettet sind, die in der Ebene des Netzes verlaufen, daß heißt also, deren Quererstreckung mit der Ebene des Netzes zusammenfällt. Der Ausdruck Ebene ist hier nicht im sathematischen Sinne gebraucht. Im vorliegenden Sinne kann die Ebene eines Netzes oder Bandes durchaus, je nach dem, wie man das Netz oder das Band biegt oder faltet, ebenfalls gebogen oder gefaltet werden. Die Bahn gemäß der Erfindung hat also im Vergleich zu den vorbekannten Sicht- oder Sonnenschutzbahnen im wesentlichen die Form einer Folie mit gleichmäßig verteilten Perforationen. Auf diese Weise kann bei gleichem Verbrauch an Netzmaterial und gleichem Verbrauch an unhüllendem Kunststoff die Schattenwirkung der Bahn vervielfacht werden, das heißt also, wenn eine Bahn der vorbekannten Art beispielsweise 20 % des zwischen ihren Umrißlinien liegenden Bodens beschattete, beschattet eine Bahn gemäß der Erfindung je nach Dimensionierung 30 bis 90 %. Bleibt man mit dem erreichten Schattiereffekt im unteren Bereich, so wird gegenüber dem vorbekannten Schattiergewebe sogar noch eine wesentliche Verringerung des Materialverbrauchs bewirkt.According to the invention this object is achieved in that the threads of the Mesh in each case merging into one another at the cross-hairs on all sides flexible plastic strips are embedded that run in the plane of the network, that is to say, the transverse extent of which coincides with the plane of the network. Of the Expression level is not in the mathematical here Senses used. In the present sense, the level of a network or band may well, depending on how to bend or fold the net or ribbon, also bent or folded will. The web according to the invention has in comparison to the previously known visual or sun protection sheets essentially in the form of a film with evenly distributed Perforations. In this way, with the same consumption of net material and the same Consumption of non-enveloping plastic multiplies the shadow effect of the web, that is, if a web of the previously known type, for example, 20% of the between shaded its outlines lying ground, shaded a web according to the invention 30 to 90% depending on the dimensions. One remains with the achieved shading effect in the lower area, it is even more compared to the previously known shading fabric causes a significant reduction in material consumption.
Auf diese Weise ermöglicht die Erfindung erstmalig den Einsatz von derartigen netzarmierten durchbrochenen Kunststoffbahnen in großem Umfang unter anderem auch für landwirtschaftliche Zwecke. Da die Bahn gemäß der Erfindung eine sehr hohe Festigkeit haben kann, können einzelne Bahnen mit ihren '§Re dern aneinandergenäht oder sonstwie verbunden werden, um auch große Flächen abzudecken. Die Bahnen sind dabei flexibel genug, um auch je nach Bedarf etwa jalousieartig zusammengefaltet und wieder auseinandergezogen zu werden.In this way, the invention enables the use of for the first time such mesh-reinforced, perforated plastic sheets to a large extent also for agricultural purposes. Since the web according to the invention a can have very high strength, individual panels can be sewn together with their backs or otherwise connected to cover large areas. The lanes are flexible enough to be folded up in the manner of a blind, for example and to be pulled apart again.
Das tragende Netz der Bahn kann beispielsweise ein Gittergewebe sein. Bevorzugt wird jedoch ein gittergewebeähnliches Gewirk, vorzugsweise ein Kettstuhlgewirk verwendet. Derartige Gewirke haben gegenüber dem Gewebe - auch gegenüber dem Drehergewebe, das immerhin schon wesentlich besser ist als ein einfaches Gittergewebe - den Vorteil einer hohen Söhiebefestigkeit der einzelnen Fäden gegeneinander. Außerdem bietet das Gewirk mehr Gestaltungsmöglichkeiten der Gitterstruktur und große Exaktheit des Flächenmusters. Das Netz kann beispielsweise aus zwei orthogonal zueinander verlaufenden Fadenscharen bestehen, die zwischen sich rechteckige oder quadratische Maschen frei lassen. Die Fäden des Netzes können aber beispielsweise auch so verlaufen, daß sie zwischen sich Dreiecke oder Sechsecke frei lassen. Die Art des gewählten Fadenlaufes hängt davon ab, wie das Netz festigkeitsmäßig beansprucht werden soll. Soll beispielsweise die Beanspruchung im wesentlichen nur in einer von zwei senkrecht aufeinanderstehenden Richtungen erfolgen, so wählt man zweckmäßig ein Netz mit in der Richtung der Beanspruchung verlaufenden parallel zueinander liegenden Fäden. Ist die Bahn dagegen auf allen Seiten eingespannt, so können auch sechseckige Durchbrechungen oder Maschen ergebende Fadenrichtungen gewählt werden.The supporting network of the web can, for example, be a mesh fabric. However, a mesh-like knitted fabric, preferably a warp knitted fabric, is preferred used. Such knitted fabrics have compared to the fabric - also compared to the leno fabric, which is much better than a simple mesh fabric - the advantage high strength of the individual threads against each other. Also offers the knitted fabric has more design options for the lattice structure and great precision of the surface pattern. The network can, for example, consist of two orthogonal to each other There are running sets of threads that are rectangular or square between them Leave stitches free. The threads of the net can, for example, also run like this, that they leave triangles or hexagons free between them. The type of chosen The course of the thread depends on how the network is to be stressed in terms of strength. For example, if the stress is to be essentially perpendicular only in one of two are carried out on one another, it is expedient to choose a network with in the direction of the stress running parallel threads. If, on the other hand, the web is clamped in on all sides, hexagonal openings can also be used or thread directions resulting in stitches can be selected.
Wenn gewünscht, können die Fäden auch selbst bandförmig sein, wobei die Fläche des Bandes mit der Fläche des Netzes zusammenfällt. Bandförmige Fäden sind vorteilhaft aus mehreren feineren Fäden zusammengeflochten, was beim Wirken des Netzes erfolgen kann.If desired, the threads themselves can also be ribbon-shaped, wherein the area of the band coincides with the area of the mesh. Ribbon-shaped threads are advantageously braided together from several finer threads, which is when knitting of the network can be done.
Das Netz ist vorteilhaft stoffschlüssig mit dem es- umgebenden Kunststoff verbunden. Wenn ein derartiger Stoffschluß nicht von vornherein aufgrund des gewählten Kunststffmaterials und des Netzmaterials entsteht, kann ein solcher durch Aufbringen von geeigneten Haftvermittlern, wie z.B. einem handelsüblichen Polyurethan-PVC-Haftvermittlersystem auf das Netz vor dem Aufbringen des Kunststoffes geschaffen werden. Ist dies nicht möglich, so kann das Netzmaterial wenigstens zusätzlich dadurch formschlüssig mit dem Kunststoff verbunden werden, daß man das Netz aus einen bestimmten Anteil an Stapelfasern enthaltenden Garnen herstellt.The network is advantageously cohesive with the plastic surrounding it tied together. If such a material bond is not a priori due to the selected Kunststffmaterials and the net material arises, such can be achieved by applying of suitable adhesion promoters, such as a commercially available polyurethane-PVC adhesion promoter system be created on the mesh before applying the plastic. Is not this possible, the net material can thereby at least additionally form a positive fit to be connected to the plastic that you can make the network from a certain proportion of Manufactures yarns containing staple fibers.
Das Netz selbst besteht vorzugsweise aus synthetischen endlosen Fäden oder endlosen Glas fäden. Selbst wenn das Material der Fäden nicht 100-%ig witterungsbeständig, insbesondere nicht gegen Sonneneinstrahlung beständig ist, wie dies z.B.The net itself is preferably made of synthetic endless threads or endless glass threads. Even if the material of the threads is not 100% weatherproof, in particular is not resistant to solar radiation, as e.g.
bei Polyamid, weniger bei Polyesterfasern der Fall ist, stört dies nicht, da die Kunststoffumhüllung das Netz gegen Lichteinstrahlung schützt. Zu diesem Zweck ist der Kunststoff vor teilhaft mit stark deckenden Farbstoffen oder Pigmenten hoher Lichtechtheit eingefärbt. Vorteilhaft sind die Farbstoffe stark lichtreflektierend, insbesondere auch infrarotreflektierend.This is a problem with polyamide and less so with polyester fibers not, as the plastic cover protects the net against light radiation. To this Purpose is the plastic in front partly with highly opaque dyes or colored with pigments of high lightfastness. The dyes are advantageously strong light-reflecting, in particular also infrared-reflecting.
Glasfäden haben den Vorteil besonders hoher Festigkeit. Da sie nicht beliebig gebogen werden können, ist man bei der Verwendung derselben in der Auswahl des Gewirkes beschränkt. Zur Zeit wird Polyester als Fadenmaterial bevorzugt, da es kein Wasser aufnimmt, praktisch 100 % witterungsbeständig ist, hohe Festigkeit besitzt und auch sehr maßstabil ist. Letzteres gilt auch bei erhöhten Temperaturen, die gerade bei der Verwendung als Sonnenschutzbahn leicht auftreten können.Glass threads have the advantage of particularly high strength. Because they don't can be bent at will, you can choose when using them of the knitted fabric limited. At the moment, polyester is preferred as the thread material it does not absorb water, is practically 100% weatherproof, high strength and is also very dimensionally stable. The latter also applies at elevated temperatures, which can easily occur, especially when used as a sun protection membrane.
Die Erfindung betrifft auch ein Verfahren zur Herstellung der Bahn. Bei diesem Verfahren werden die Fäden des Netzes allseitig mit einem vorzugsweise pastenförmigen aufschäumbaren Kunststoff, vorzugsweise einem Plastisol, wie z.B. einer PVC-Plastisolpaste, überzogen. Dann wird der Plastisolüberzug aufgeschäumt, so daß nun jeder Faden von einer relativ dicken Umhüllung aus Schaumkunststoff überzogen ist. Dann wird dieser Schaumkunststoffüberzug in warmem thermoplastischem Zustand flachgedrückt und durch Abkühlen verfestigt. Dadurch, daß man nicht einfach die Fäden des Netzes mit einem einfachen Plastisol überzieht, dieses ausgeliert und dann den Überzug breit drückt, sondern zunächst das Volumen des Sohaumüberzuges auf ein Mehrfaches erhöht, wird die beim Zusammendrücken des Kunststoffüberzuges erreichbare Breite des den einzelnen Netzfaden einhüllenen Kunststoffbandes auf ein Mehrfaches erhöht. Obwohl der fertige Kunststoffüberzug seine Schaumstoffstruktur fast ganz wieder verloren hat und damit auch den zusätzlichen Vorteil einer hohen Scheuerfestigkeit gewonnen hat, wird durch die Zwischenschaltung des Schaumstoffzustandes der Kunststoffumhüllung' eine wesentliche Verbreiterung der plattgedrückten Umhüllung erreicht.The invention also relates to a method of making the web. In this method, the threads of the network are preferably on all sides with one paste-like foamable plastic, preferably a plastisol, e.g. a PVC plastisol paste. Then the plastisol coating is foamed, so that now each thread is covered by a relatively thick covering made of foam plastic is. Then this foam plastic cover is in a warm thermoplastic state flattened and solidified by cooling. By not just doing the Threads of the network are covered with a simple plastisol, this gelled and then presses the cover wide, but first of all the volume of the sole cover to a multiple is increased when the plastic coating is compressed achievable width of the plastic tape enveloping the individual net thread increased several times. Although the finished plastic cover has its foam structure almost completely lost again and with it the additional advantage of a high Has gained abrasion resistance, is through the interposition of the foam state the plastic envelope 'a substantial widening of the flattened envelope achieved.
Dem Grunde nach kann das Plattdrücken beispielsweise edblgen, indem das schaumstoffumhüllte Netz wenigstens angenähert bis in den thermoplastischen Bereich erwärmt und dann-mittels entsprechend großer Stempel flachgedrückt wird. Bevorzugt erfolgt jedoch die Fertigung von Bahnmaterial gemäß der Erfindung kontinuierlich. Bei einer solchen Fertigung durchläuft eine fortlaufende Netzbahn zunächst eine Beschichtungsstation, in welcher das Netz in gewünschtem Umfang z.B. mit dem Plastisol überzogen wird. Danach durchläuft die Bahn zweckmäßig einen Gelierofen, in dem das Plastisol angeliert aber noch nicht aufgeschäumt wird. Das bewirkt eine Entgasung des Plastisols und aufgrund der Oberflächenspannungen im Plastisol auch eine Vergleichmäßigung des Plastisolüberzugs. Danach durchläuft die Bahn zweckmäßig einen heißeren Teil des Ofens, in welchem nun die Kunststoffumhüllung des Netzes aufschäumt. Hinter dem Ofen läßt man dann vorzugsweise die Bahn erkalten. Die erkaltete Bahn wird dann - vorzugsweise durch langwellige Infrarotstrahlung - wieder erwärmt bis die äußeren Bereiche wieder thermoplastisch sind, während die inneren Bereiche des Überzuges noch thermoelastisch sind. Dann wird die Bahn zwischen einem entsprechend eng eingestellten Walzenpaar hindurchgeführt, um so das Plattdrücken des Kunststoffes zu bewirken. Anschliessend wird die Bahn wieder abgekühlt, die dann aufgerollt, in Einzelbahnen zerschnitten oder sonstwie gegebenenfalls weiterverarbeitet werden kann. Ein Bedrucken der Bahn erfolgt vorzugsweise in kaltem Zustand, vor oder nach dem Plattdrücken.Basically, flat pressing can, for example, be done by the foam-covered network at least approximately to the thermoplastic The area is heated and then pressed flat by means of a correspondingly large punch. However, the manufacture of web material according to the invention is preferably carried out continuously. In such a production, a continuous network track first runs through one Coating station, in which the net to the desired extent, e.g. with the plastisol is covered. The web then expediently passes through a gelling oven in which the Plastisol gels but is not yet foamed. This causes degassing of the plastisol and, due to the surface tension in the plastisol, also an equalization of the plastisol coating. After that, the web expediently runs through a hotter part of the oven, in which the plastic covering of the net now foams. Behind the oven the web is then preferably allowed to cool. The cooled down The web is then reheated - preferably by long-wave infrared radiation until the outer areas are thermoplastic again, while the inner areas of the coating are still thermoelastic. Then the path between one is accordingly closely adjusted pair of rollers passed, so as to flatten the plastic to effect. The web is then cooled down again, which is then rolled up, cut into individual lanes or otherwise processed further if necessary can. The web is preferably printed in the cold state, before or after the flat pressing.
Nachfolgend ist die Erfindung in Form eines Beispiels anhand der Zeichnungen näher erläutert.Below is the invention in the form of an example with reference to the drawings explained in more detail.
Fig. 1 zeigt schematisch ein für die Erfindung vorteilhaft einzusetzendes Kettstuhlgewirk etwa in natürlicher Größe.Fig. 1 shows schematically one to be used advantageously for the invention Warp knitted fabric roughly natural size.
Fig. 2 zeigt eine andere Ausführungsform eines derartigen Gewirks.Fig. 2 shows another embodiment of such a knitted fabric.
Fig. 3 zeigt das Gewirk gemäß Fig. 1 nach dem Umhüllen mit einem Plastisol.FIG. 3 shows the knitted fabric according to FIG. 1 after being wrapped with a plastisol.
Fig. 4 zeigt das plastisolumhüllte Gewirk gemäß Fig. 3 nach dem Aufschäumen der Kunststoffumhüllung desselben.FIG. 4 shows the plastisol-coated knitted fabric according to FIG. 3 after foaming the plastic casing of the same.
Fig. 5 zeigt das Bahnmaterial gemäß Fig. 4 nach dem Plattdrücken des Kunststoffüberzugs desselben.Fig. 5 shows the web material according to FIG. 4 after the flattening of the Plastic coating of the same.
Fig. 6 zeigt schematisch in wesentlich vergrößertem Maßstab den Querschnitt durch ein "Band" des Bahnmaterials gemäß Fig. 5.Fig. 6 shows schematically on a significantly enlarged scale the cross section by a "band" of the web material according to FIG. 5.
Fig. 7 zeigt schematisch die kontinuierliche Herstellung einer fortlaufenden Bahn gemäß der Erfindung.Fig. 7 shows schematically the continuous production of a continuous Web according to the invention.
Die in Fig. 1 gezeigte für Bahnmaterial gemäß der Erfindung besonders geeignete Ware 1 ist ein Rascheltüll. Dieser besteht im Prinzip aus zwei orthogonal zueinander verlaufenden Fadenscharen, in welcher jeder Faden wiederum aus einer Mehrzahl miteinander verdrehter und/oder verflochtener feinerer Fäden oder Elementarfäden besteht. Der Rascheltüll 1 besteht im Ausführungsbeispiel aus Polyesterfäden.The one shown in Fig. 1 for web material according to the invention in particular suitable product 1 is a rustling tulle. This basically consists of two orthogonal mutually extending sets of threads, in which each thread in turn consists of one Multiple twisted and / or intertwined finer threads or filaments consists. In the exemplary embodiment, the rustling tulle 1 consists of polyester threads.
Als tragendes Netz können natürlich auch andere Web- oder Wirkstoffe verwendet werden, so z.B. das in Fig. 2 schematisch angedeutete Kettstuhlgewirk 2, welches im wesentlichen aus drei Fadenscharen besteht, von welchen eine quer zur Wirkrichtung verläuft, während die anderen beiden schräg zu dieser verlaufen.Of course, other woven or active fabrics can also be used as a supporting net can be used, for example the warp knitted fabric indicated schematically in FIG 2, which consists essentially of three sets of threads, one of which is transverse runs to the direction of action, while the other two run obliquely to this.
Bei der weiteren Beschreibung der Erfindung wird von dem in Fig. 1 gezeigten Rascheltüll ausgegangen, der dort auch in für das darzulegende Beispiel natürlicher Größe gezeigt ist, wenn auch die Darstellung im einzelnen, insbesondere der Verlauf der Elementarfäden, nur schematisch angedeutet ist.In the further description of the invention, the in Fig. 1 assumed the rustling tulle shown there also in for the example to be presented natural size is shown, albeit the representation in detail, in particular the course of the filaments is only indicated schematically.
Es sei angenommen, daß auf der Vorratsrolle 3 in Fig. 7 ein derartiger Rascheltüll aufgerollt ist. Dieser wird dann von der Vorratsrolle 7 abgezogen und der Auftragsstation 4 zugeführt. Dort läuft die Tüllbahn 1 über ein umlaufendes endloses Gummiband 5, an dessen oberem ebenem Trum sie wie aus der Zeichnung ersichtlich, satt anliegt. Anstelle des Gummibandes kann auch eine Walze verwendet werden. Jedes dieser Elemente hat seine besonderen Vorteile. Das Gummiband 5 läuft mit einer Geschwindigkeit um, die wesentlich von der Fördergeschwindigkeit der Bahn 1 abweicht. Vorzugsweise läuft das endlose Gummiband 5 so um, daß das an der Tüllbahn anliegende Trum in der gleichen Richtung wie die Tüllbahn aber mit größerer Geschwindigkeit umläuft. Dadurch wird die gute Umhüllung der Fäden des von der Tüllbahn gebildeten Netzes mit dem Plastisol 6 begünstigt. Das Plastisol 6 wird in an sich bekannter Weise mit Hilfe eines Rakels 7 aufgebracht, der oberhalb des Gummibandes 5 das Plastisol 6 aufstreicht. Die Umlaufrichtung des endlosen Gummibandes 5 und die Laufrichtung des zu über ziehenden Netzbandes 1 sind durch den Pfeil in Fig. 7 angedeutet. Über der in Ablaufrichtung liegenden Umlenkrolle des Gummibandes 5 liegt eine weitere Andruckrolle 8, die ebenfalls die einwandfreie Umhüllung des Gitterbandes 1 mit dem Plastisol 6 begünstigt.It is assumed that on the supply roll 3 in Fig. 7 such Raschel tulle is rolled up. This is then withdrawn from the supply roll 7 and the application station 4 supplied. There the tulle sheet 1 runs over a circumferential one endless rubber band 5, on the upper flat run of which, as can be seen in the drawing, is full. A roller can also be used instead of the rubber band. Each this element has its special advantages. The rubber band 5 runs at one speed around, which differs significantly from the conveying speed of the web 1. Preferably runs around the endless rubber band 5 so that the strand lying on the tulle sheet in in the same direction as the Tüllbahn but with greater speed. This ensures that the threads of the network formed by the tulle web are well wrapped favored with the plastisol 6. The plastisol 6 is made in a manner known per se applied with the help of a doctor blade 7, the above the rubber band 5, the plastisol 6 spreads. The direction of rotation of the endless rubber band 5 and the direction of travel of the net tape 1 to be pulled over are indicated by the arrow in FIG. Above the deflection roller of the rubber belt in the direction of flow 5 is another pressure roller 8, which also ensures the proper wrapping of the Grid tape 1 with the plastisol 6 favors.
Das hier verwendete Auftragsprinzip ist das gleiche wie das beispielsweise in der DT-OS 1 560 826 der Anmelderin beschriebene.The order principle used here is the same as that for example described in DT-OS 1 560 826 of the applicant.
Ein Stück der nun plastisolumhüllten Netzbahn 9 ist in Fig.A piece of the now plastisol-coated mesh web 9 is shown in Fig.
3 gezeigt. Man erkennt dort jeweils in der Mitte der einzelnen Plastisolstränge den entsprechenden Faden des Netzes 1.3 shown. You can see there in the middle of the individual plastisol strands the corresponding thread of the net 1.
Nun wird die plastisolumhüllte Netzbahn 9 einem zweiteiligen Ofen 10 zugeführt. Im ersten Abteil 11 dieses Ofens wird die Bahn 9 auf eine Temperatur von z.B. 1200C erwärmt, so daß das aufschäumbare Plastisol ausgeliert und sich die Dicke desselben unter dem Einfluß der Oberflächenspannung auf dem Netz vergleichmäßigt. Im zweiten Teil 12 des Ofens 10 herrscht eine Temperatur von beispielsweise 1800C, welche das Treibmittel im Überzug aktiviert, so daß nun der Überzug aufschäumt.Now the plastisol-coated mesh web 9 is a two-part oven 10 supplied. In the first compartment 11 of this oven, the web 9 is brought to a temperature of e.g. 1200C, so that the foamable plastisol gels and the Thickness of the same evened out under the influence of surface tension on the mesh. In the second part 12 of the furnace 10 there is a temperature of 1800C, for example, which activates the propellant in the coating so that the coating now foams.
Die beim Verlassen des zweiten Ofenteils 12 mit einem dicken Schaumstoffüberzug versehene Netzbahn 13 ist in Fig. 4 dargestellt. Man erkennt hier, daß das Volumen des Kunststoffüberzugs durch das Aufschäumen auf ein Mehrfaches gestiegen ist. Der Maßstab von Fig. 4 ist ebenso wie der von Fig. 3 etwa 1 : 1.When leaving the second furnace part 12 with a thick foam cover provided net web 13 is shown in FIG. You can see here that the volume of the plastic coating has increased several times over due to the foaming. Of the The scale of FIG. 4, like that of FIG. 3, is approximately 1: 1.
Nun läßt man die Bahn 13 bis auf eine Temperatur erkalten, die bei oder über der Raumtemperatur aber höchstens im thermoelastischen Bereich des Kunststoffes liegt. Dann wird die Bahn mittels langwelliger Infrarotstrahler 18 so hoch erwärmt, daß die äußeren Bereiche der Kunststoffumhüllung wieder thermoplastisch werden, die inneren Bereiche aber noch im thermoelastischen Temperaturbereich bleiben. In diesem Zustand wird die Bahn 13 zwischen zwei Quetschwalzen 14 und 15 geführt, deren Spaltabstand voneinander vorteilhaft etwa der 1,1-bis 1,2-fachen Dicke der Kunststoffbänder entspricht. Beim Durchlaufen des Spalts zwischen den Walzen 14 und 15 wird der thermoplastische Schaumstoffüberzug platt- und breitgedrückt, so daß nun eine Bahn 16 entsteht, wie sie in Fig. 5 gezeigt ist. Diese Bahn ist ganz flach, dafür sind jedoch die Durchbrechungen 17 der Bahn wesentlich kleiner geworden als es die Durchbrechungen 18 der Bahn 13 waren. Die Breite b der einzelnen die Bahn bildenden, jeweils durch einen Faden des Netzes verstärkten Bänder ist, wie aus der Zeichnung ersichtlich, weitaus größer als dies möglich wäre, wenn man beispielsweise lediglich die vorgelierte Bahn, die den ersten Ofenteil 11 verläßt, ohne Aufschäumen zwischen den Walzen 14 und 15 hindurchführte.Now the web 13 is allowed to cool down to a temperature at or above room temperature but at most in the thermoelastic range of the plastic lies. Then the web is heated to such an extent by means of long-wave infrared radiators 18 that that the outer areas of the plastic coating become thermoplastic again, the inner areas, however, still remain in the thermoelastic temperature range. In this state, the web 13 is guided between two nip rollers 14 and 15, whose Gap spacing from one another is advantageously approximately 1.1 to 1.2 times the thickness of the plastic strips is equivalent to. When passing through the gap between the rollers 14 and 15, the thermoplastic Foam cover pressed flat and wide, so that now a web 16 is formed, as it is shown in FIG. This path is very flat, but that's what the openings are for 17 of the web has become much smaller than the openings 18 of the web 13 was. The width b of the individual forming the web, each by a thread As can be seen from the drawing, the ribbons reinforced by the mesh are much larger than would be possible if, for example, only the pregelatinized web that leaves the first furnace part 11, passed between the rollers 14 and 15 without foaming.
Durch die Einstellung des Spaltes zwischen den Walzen 14 und 15 kann man das Maß, in welchem die zunächst angenähert zylindrischen Sohaumstoffumhüllungen der Gitternetzfäden flachgedrückt werden, einstellen. Je geringer der Abstand, umso breiter sind die die Bahn 16 bildenden sich kreuzenden Bänder; das heißt, umso kleiner sind die in der Bahn verbleibenden öffnungen.By adjusting the gap between the rollers 14 and 15 can one is the extent to which the initially approximately cylindrical Sohaumstoffumhüllungen the grid threads are flattened. The smaller the distance, the more are wider the intersecting belts forming web 16; that is, the smaller the openings remaining in the web.
Es versteht sich, daß man das Verhältnis von Bandbreite zu öffnungsgröße nicht nur hierdurch, sondern - und das in erster Linie - durch die Maschenweite des Netzes und die Menge des Plastisolauftrages regeln kann, da man meist bestrebt sein wird, aus Materialersparnisgründen die Matte so dünn wie möglich zu halten.It goes without saying that the ratio of the bandwidth to the opening size not only because of this, but - and primarily - because of the mesh size of the network and the amount of plastisol application, as you usually strive will be to keep the mat as thin as possible to save material.
Fig. 6 zeigt den Querschnitt durch ein Band der Bahn 16 in vergrößertem Maßstab, welche also eine der in Fig. 5 dem Beschauer zugekehrten Schnittflächen der Bahn 16 aus Fig. 6 zeigt. In Fig. 6 sind die zusammengepreßten durch das Aufschäumen ursprünglich erzeugten Poren durch eine waagerechte Strichelung angedeutet. Diese feinen Bläschen verschwinden beim Umformen der Bahn 13 gemäß Fig. 4 in die Bahn 16 gemäß Fig. 5 nicht vollständig, sondern bleiben zum Teil in Form von flachen Unterbrechungen des Zusammenhalts in der Kunststoffmasse erhalten.Fig. 6 shows the cross section through a band of the web 16 in enlarged Scale, which is one of the cut surfaces facing the viewer in FIG. 5 the web 16 of Fig. 6 shows. In Fig. 6 are the compressed by the foaming originally generated pores indicated by a horizontal dashed line. These fine bubbles disappear when the web 13 according to FIG. 4 is formed into the web 16 according to FIG. 5 are not completely, but remain partly in the form of flat ones Get interruptions of cohesion in the plastic mass.
In der Praxis verlaufen diejenigen Fäden des Netzes, die sich im wesentlichen quer zur Durchlaufrichtung der Bahn durch die Walzen erstrecken, nicht genau in der Mitte ihrer Bänder", sondern etwas seitlich versetzt, da beim Einlaufen in der Walzenspalt der thermoplastische schaumstoff etwas zurückbleibt. Dieser Effekt ist umso geringer, je größer der Walzendurchmesser ist.In practice, those threads of the network that are essentially run away extend transversely to the direction of travel of the web through the rollers, not exactly in the middle of their ligaments ", but slightly offset to the side, because when entering the Nip the thermoplastic foam remains somewhat. This effect is all the less the larger the roller diameter is.
Die fertige Bahn 16 läßt man nach dem Verlassen der Walzen 14, 15 noch ausreichend auskühlen und wickelt sie dann auf eine Vorratsrolle 17 auf. Das fertige Bahnmaterial kann dann in gewünschten Längen oder Stückaizerteilt werden.The finished web 16 is left after it has left the rollers 14, 15 cool down sufficiently and then wind it up on a supply roll 17. That finished web material can then be divided into desired lengths or pieces.
Patentansprüche:Patent claims:
Claims (11)