DE2410197C3 - Means for preventing welding beads from sticking to workpiece surfaces - Google Patents
Means for preventing welding beads from sticking to workpiece surfacesInfo
- Publication number
- DE2410197C3 DE2410197C3 DE19742410197 DE2410197A DE2410197C3 DE 2410197 C3 DE2410197 C3 DE 2410197C3 DE 19742410197 DE19742410197 DE 19742410197 DE 2410197 A DE2410197 A DE 2410197A DE 2410197 C3 DE2410197 C3 DE 2410197C3
- Authority
- DE
- Germany
- Prior art keywords
- water
- thickener
- electrically conductive
- welding beads
- workpiece surfaces
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Beim Lichtbogenschweißen verspritzen vom Elektrodenmaterial kugelförmige Teilchen, die in der Umgebung der Schweißstellen an der Werkstücksoberfläche festkleben und nur unter erheblichem Aufwand beseitigt werden können.During arc welding, spherical particles from the electrode material spatter into the surrounding area of the welds stick to the workpiece surface and can only be removed with considerable effort can be.
Um die Beseitigung der besagten Teilchen zu erleichtern, ist es bekannt, die gefährdeten Oberflächen vor dem Schweißen mit flüssigen Mitteln in Lack- oder Sprayform zu benetzen, um auf diese Weise das Festkleben der Schweißperlen zu verhindern. Diese Mittel enthalten organische Bindemittel (Alkydharze, öle) sowie brennbare Lösungsmittel, so daß sie in Schweißereien nicht gefahrlos und nur unter erheblichen Sicherheitsvorkehrungen verarbeitet werden können. Sie haben auch den Nachteil, im Gebrauch durch Dampf- und Geruchsbildung das Arbeiten zu erschweren und/oder durch Rückstandsbildung das weitere Behardeln der geschweißten Werkstücke mit Farbe ohne aufwendige Nachreinigung nicht zuzulassen, da die Rückstände den Farbauftrag zersetzen wurden. Außer- > dem besteht bei den bekannten Mitteln durch Gasentwicklung die Gefahr einer Lunkerbildung beim Schweißen.In order to facilitate the removal of said particles, it is known that the endangered surfaces Before welding, moisten with liquid agents in paint or spray form in order to achieve the Prevent the welding beads from sticking. These agents contain organic binders (alkyd resins, oils) as well as flammable solvents, so that they are not safe in welding shops and only under considerable Security precautions can be processed. They also have the disadvantage of being due in use The formation of steam and odors make work more difficult and / or the further formation of residues Do not allow the welded workpieces to be coated with paint without costly post-cleaning, as the Residues decompose the paint application. Except-> with the known agents there is a risk of cavities forming due to the evolution of gas Welding.
Der Erfindung liegt die Aufgabe zugrunde, ein solches Mittel zu schaffen, das folgende Forderungen erfüllt:
ίο a) Herabsetzung der Haftkräfte für die Schweißperlen an der Werkstücksoberfläche,The invention is based on the object of creating such a means that meets the following requirements:
ίο a) Reduction of the adhesive forces for the welding beads on the workpiece surface,
b) Unbrennbarkeit des Mittels zwecks gefahrloser Verarbeitung,b) non-flammability of the agent for safe processing,
c) Vermeidung von Rauchentwicklung und Zersetzungsprodukten beim Schweißen,c) Avoidance of smoke development and decomposition products when welding,
d) leichte und gründliche Entfernung der Rückstände des Mittels nach dem Schweißvorgang von der Werkstücksoberfläche,d) easy and thorough removal of residues of the agent after the welding process from the Workpiece surface,
e) keine Reaktion eventueller Rückstandsreste mit aufgebrachten Grund- und Deckanstrichen,e) no reaction of possible residue residues with applied primer and top coats,
f) Vermeidung von lunkerbildenden Gaseinschlüssen in den Schweißnähten.f) Avoidance of void-forming gas inclusions in the weld seams.
Die Lösung der gestellten Aufgabe gelingt nach der Erfindung auf einfache und sichere Weise dadurch, daß das Trennmittel aus einem in Wasser gelösten Polymer als Bindemittel, einem in dieser Lösung feinverteilten, chemisch inaktiven Verdickungsmittel und einem feinverteilten, chemisch inaktiven elektrisch leitfähigen Zusatz zusammengesetzt ist.The object is achieved according to the invention in a simple and safe manner in that the release agent made of a polymer dissolved in water as a binder, one finely divided in this solution, chemically inactive thickener and a finely divided, chemically inactive electrically conductive Addition is composed.
Ein bevorzugtes Beispiel des erfindungsgemäßen Mittels enthält als Bindemittel 1 bis 10% Polymer in Form von Polyvinylalkohol und/oder Polyvinyläther, 2 bis 10% Verdickungsmittel in Form von hochdispersem Siliciumdioxid und/oder Bentonit sowie 5 bis 10%A preferred example of the agent according to the invention contains 1 to 10% polymer in as a binder Form of polyvinyl alcohol and / or polyvinyl ether, 2 to 10% thickener in the form of highly dispersed Silicon dioxide and / or bentonite and 5 to 10%
.15 Graphit zur Bildung einer elektrisch leitfähigen Trennschicht an der Werkstücksobei fläche..15 Graphite to form an electrically conductive separating layer on the workpiece surface.
Das Mittel kann leicht hergestellt werden, indem in dem auf 60 bis 70°C erhitzten Wasser die entsprechende Menge des Polymers gelöst und der Lösung die entsprechenden Mengen des Verdickungsmitlels sowie des leitfähigen Zusatzes zugerührt werden.The agent can be easily prepared by dissolving in the 60 to 70 ° C heated water the appropriate amount of the polymer and the solution, the respective amounts of the Verdickungsmitlels and the conductive e are supplied stirred n additive.
Es wird auf diese Weise ein Wasserlack als Antischweißperlenlack erhalten, der bei einer Schichtdicke von 8 bis 10pm eine Trocknungszeit von etwa einer Stunde aufweist und im verarbeitungsbereiten Zustand als Paste mit thixolropen Eigenschaften vorliegt.In this way, a water-based varnish is obtained as an anti-perspiration pearl varnish, which with one layer thickness from 8 to 10pm a drying time of about one hour and in the ready-to-use state as a paste with thixolropic properties is present.
Claims (5)