DE2131256A1 - Joining objects with two-components adhesives - by placing the components separately onto the two objects - Google Patents

Joining objects with two-components adhesives - by placing the components separately onto the two objects

Info

Publication number
DE2131256A1
DE2131256A1 DE19712131256 DE2131256A DE2131256A1 DE 2131256 A1 DE2131256 A1 DE 2131256A1 DE 19712131256 DE19712131256 DE 19712131256 DE 2131256 A DE2131256 A DE 2131256A DE 2131256 A1 DE2131256 A1 DE 2131256A1
Authority
DE
Germany
Prior art keywords
components
objects
adhesive
workpieces
component
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19712131256
Other languages
German (de)
Inventor
Erich Dolderer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WEVO CHEMIE HEINZ WENZEL
Original Assignee
WEVO CHEMIE HEINZ WENZEL
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WEVO CHEMIE HEINZ WENZEL filed Critical WEVO CHEMIE HEINZ WENZEL
Priority to DE19712131256 priority Critical patent/DE2131256A1/en
Publication of DE2131256A1 publication Critical patent/DE2131256A1/en
Pending legal-status Critical Current

Abstract

Objects are joined with two component (binder and hardener) commercial adhesives by placing a definite volume of the first component on one object and a definite volume of the second component on the other objects. The surfaces are mutually contacted pref. moved and pressed relative to each other and left to cure. It is disadvantageous to heat the objects before contact to 50-90 degrees C and subject them to u.v. light after contact. Pref. adhesive components are not highly viscous and esp. suitable are those having epoxy resin binder and polyamide resin hardener with mixing ratio 1:1 by vol. The technique eliminates limited pot-life condition.

Description

Verfahren zum Verbinden zweier Werkstücke Die Erfindung betrifft ein Verfahren zum Verbinden zweier Werkstücke mittels eines aushärtbaren Zweikomponentenklebers. Method for joining two workpieces The invention relates to a method for joining two workpieces by means of a hardenable two-component adhesive.

Bei der bekannten Zweikomponentenverklebung werden die beiden Komponenten des Klebers ("Binder und Härter") miteinander vermischt, auf eine oder beide der zu verbindenen Werkstücke aufgetragen und die Werkstücke zusammengebracht, worauf die Verbindung nach Aushärtuna des Klebers zustandekommt. Nachteilig ist bei dieser bekannten Verklebung, daß die beiden Komponenten vor dem Auftrag auf die lnterkstficke in bestimmten Mengenverhältnis vermischt werden messen, was zu Mischfehlern und Fehlverkiebungen ffihren kann. in weiterer angel besteht darin, daß die vermischten Komponenten nur eine begrenzte "Topfzeit" haben, innerhalb welcher sie verarbeitet werden müssen. Eine nicht verarbeitete Restmenge härtet aus und ist unbrauchbar.With the known two-component bonding, the two components are of the adhesive ("binder and hardener") mixed together on one or both of the Applied to connected workpieces and brought the workpieces together, whereupon the connection is made after the adhesive has hardened. This is a disadvantage known bonding that the two components are applied to the linterkstficke before application to be mixed in certain proportions measure, which leads to mixing errors and Can lead to misalignments. Another angel is that the mingled Components only limited Have "pot life" within which they need to be processed. Any remaining amount that has not been processed will harden and is useless.

Aufgabe der Erfindung ist es, eine Zueikomponentenverklebung ohne vorherige Vermischung der Komponenten durchzuführen.The object of the invention is to provide a glue component bond without carry out prior mixing of the components.

Die Aufgabe wird erfindungsgemäß dadurch gelöst, daß eine bestimmte Menge der einen Kleberkomponente auf das eine Werkstück und eine bestimmte Menge der anderen Kleberkomponente auf das andere Werkstück aufgebracht- wird, und daß die Vermischung der beiden Kleberkomponenten durch die gegenseitige Kontaktierung der mit den Komponenten beschichteten Werkstücke vorgenommen wird.The object is achieved in that a certain Amount of one adhesive component on one workpiece and a certain amount the other adhesive component is applied to the other workpiece, and that the mixing of the two adhesive components due to the mutual contact of the workpieces coated with the components.

Bei einer bevorzugten Ausführungsform des erfindungsgemäßen Verfahrens wird die Klebeschicht zwischen den Werkstücken nach deren Kontaktierung mit Ultraschall bestrahlt. Hierdurch kann bereits nach einer Bestrahlung von einigen Sekunden eine ausreichende Abbindung der Klebestelle erreicht werden.In a preferred embodiment of the method according to the invention becomes the adhesive layer between the workpieces after their contact with ultrasound irradiated. This means that after just a few seconds of irradiation, a sufficient setting of the glue point can be achieved.

Von weiterem Vorteil ist es, die miteinander zu verbindenen Werkstücke zu erwärmen. Die Ijrwärmung macht die Kleberkomponenten dünnflüssiger und begünstigt damit die gegenseitige Vermischung. Außerdem beschleunigt die Erwärmung auch die Aushärtung des Klebers.Another advantage is that the workpieces to be joined together to warm up. The Ijrwärmung makes the adhesive components thinner and favors thus the mutual mixing. In addition, the heating also accelerates the Hardening of the glue.

Die nachstehende Beschreibung bevorzugter Ausführungsformen der Erfindung dient im Zusammenhang mit einigen Beispielen der weiteren Erläuterung Es wurde gefunden, daß eine Zweikomponentenverklebung auch ohne vorherige Vermischung der beiden Kleberkomponenten durchführbar ist. So genügt es in bestimmten Fällen beispielsweise, die Klebefläche des einen Werkstückes mit der einen Kleberkomponente und die Klebefläche des anderen Werkstückes mit der anderen Kleberkomponente zu beschichten, wobei die beiden Komponenten möglichst dünnflüssig sein sollen. Durch Inberührungbringen der beiden beschichteten Klebe flächen erfolgt bereits aufgrund von Diffusionsvorgangen, z. B. im Verlauf einiger Stunden, eine derartige Durchdringung der beiden Komponenten, daß eine befriedigende Aushärtung eintritt. Die Durchdringung der beiden Komponenten kann durch leichtes Zusammenpressen und/oder Bewegen der Werkstücke an ihrer Klebefläche relativ zueinander verbessert werden. Insbesondere kommt eine relative~Dreh- oder Taumelbewegung der Werkstücke in Frage. Die Abbindung erfolgt innerhalb weniger Minuten.The following description of preferred embodiments of the invention serves for further explanation in connection with some examples It it has been found that a two-component bond can also be used without prior mixing of the two adhesive components is feasible. So it is sufficient in certain cases for example, the adhesive surface of one workpiece with one adhesive component and the adhesive surface of the other workpiece with the other adhesive component to coat, whereby the two components should be as thin as possible. By Bringing the two coated adhesive surfaces into contact is already due to of diffusion processes, e.g. B. in the course of a few hours, such a penetration of the two components that a satisfactory curing occurs. The penetration the two components can be easily pressed together and / or moved Workpieces can be improved relative to one another on their adhesive surface. In particular a relative ~ rotating or tumbling movement of the workpieces comes into question. The binding takes place within a few minutes.

Die Qualität der Klebung und die Abbindezeit wird weiterhin günstig beeinflußt, wenn die zu verbindenen Werkstücke vor dem Aufbringen der Kleberkomponenten oder nach dem Zusammenfügen erwärmt werden, wobei die Temperaturen von der Beschaffenheit der Werkstücke und des verwendeten Klebers abhängen. In Frage kommen beispielsweise Temperaturen zwischen etwa 50 und 900 C.The quality of the bond and the setting time will continue to be favorable affects when the workpieces to be joined before the application of the adhesive components or heated after joining, the temperatures depending on the nature depend on the workpieces and the adhesive used. For example Temperatures between about 50 and 900 C.

Uberraschend gute Erfolge erreicht man erfindungsgemäß, wenn die Klebeschicht zwischen den miteinander in Kontakt gebrachten Werkstücken mit Ultraschall bestrahlt wird, wobei Je nach Größe der Klebefläche einige bis mehrere Sekunden Bestrahlzeit ausreichen. Offenbar wird durch die Einwirkung des Ultraschalls die molekulare Durchdringung der beiden Komponenten besonders gefördert.Surprisingly good results are achieved according to the invention when the adhesive layer irradiated with ultrasound between the workpieces brought into contact with one another depending on the size of the adhesive surface, irradiation time from a few to several seconds sufficient. The molecular penetration becomes apparent through the action of the ultrasound of the two components are particularly encouraged.

Das Mengenverhältnis der auf die Werkstücke aufzubringenden Kleberkomponenten kann je nach Art des benutzen Klebers variieren. Vorteilhaft ist ein Mengenverhältnis nach Volumenteilen von 1:1, weil hierdurch die Auftragung der Kleberkomponenten auf die Werkstückflächen besonders einfach wird.The quantity ratio of the adhesive components to be applied to the workpieces may vary depending on the type of glue used. A quantitative ratio is advantageous according to parts by volume of 1: 1, because this means that the adhesive components are applied is particularly easy on the workpiece surfaces.

Das Auftragen der Komponenten kann z. B. durch Aufwalzen oder mittels eines Stempels erfolgen.The application of the components can, for. B. by rolling or by means of a stamp.

Für die Durchführung des erfindungsgemaßen Verfahrens eignen sich praktisch alle handelsüblichen, aus Binder und Härter bestehenden Zweikomponentenkleber. Insbesondere sind diejenigen Kleber geeignet, welche als Binder ein Expoxiharz und als Härter ein Polyamidharz enthalten. In der Regel sind diese Kleber zähflüssige Massen.Suitable for carrying out the method according to the invention practically all commercially available two-component adhesives consisting of binder and hardener. In particular, those adhesives are suitable which use an epoxy resin as a binder and contain a polyamide resin as hardener. Usually these adhesives are viscous Crowds.

Die nachstehend angegebenen Beispiele beziehen sich auf die Verklebung eines Ferritmagneten mit einem Spulengehäuse aus duroplastischem Werkstoff. Die Klebefläche betragt an beiden 2 Werkstücken etwa 1 cm . Die Klebeflächen sind unvorbehandelt.The examples given below relate to bonding a ferrite magnet with a coil housing made of thermoset material. the The adhesive area is about 1 cm on both 2 workpieces. The adhesive surfaces are untreated.

Die nachstehend angegebenen Festigkeitswerte lassen sich durch Vorbehandeln der Klebeflächen, z. B. Sandbestrahlen, noch verbessern. Die Kleberkomponenten werden jeweils mit einer Schichtdicke von etwa 0,05 mm aufgebracht. Der verwendete Kleber umfaßt als Binder ein Kondensationsprodukt aus Bisphenol-A mit Epichlorhydrin und als Härter ein .Kondensationsprodukt aus monomeren Fettsäuren mit Aminogruppen-haltigen, organischen Verbindungen.The strength values given below can be pre-treated the adhesive surfaces, e.g. B. sandblasting, still improve. The adhesive components are each applied with a layer thickness of about 0.05 mm. The glue used comprises as a binder a condensation product of bisphenol-A with epichlorohydrin and as a hardener, a condensation product of monomeric fatty acids with amino groups, organic compounds.

Beispiel I: Der Binder des Klebers wird auf die Klebefläche des Ferritmagneten und der Härter auf die Klebefläche am Spulengehäuse aufgebracht. Beide Komponenten sind verhältnimäßig dünnflüßig, was z. B. durch Erwärmen der Komponenten vor dem Auftragen noch gesteigert werden kann. Die beiden Werkstücke werden ohne besondere DruckausUbung aufeinandergesetzt.Example I: The binder of the adhesive is on the adhesive surface of the ferrite magnet and the hardener is applied to the adhesive surface on the bobbin case. Both components are relatively thin, what z. B. by heating the components before Application can be increased. The two workpieces are made without special Pressure exertion on top of each other.

Nach einer Aushärtung von sechs Stunden ergibt sich eine Zugfestigkeit der miteinander verklebten Werkstücke von etwa 50 kg/cm².A tensile strength results after curing for six hours of the workpieces glued together of about 50 kg / cm².

Beispiel II: Man verfährt wie in Beispiel I, erwärmt jedoch den Ferritmagneten und das Spulengehäuse vor demKlebstoffauftrag auf ca. Zimmertemperatur.Example II: The procedure is as in Example I, but the ferrite magnet is heated and the bobbin case to about room temperature before the adhesive is applied.

Nach einer Aushärtung von ca. einer halben Stunde wird eine Zugfestigüng von etwa 100 kg/cm² gemessen.After hardening for about half an hour, tensile strength is achieved measured at about 100 kg / cm².

Beispiel III: Man verfährt wie in Beispiel II, dreht jedoch den Ferritmagnetkern auf dem Spulengehäuse, ohne die Lage der Klebstelle zu verändern, mehrmals hin und her. Nach einer Aushärtzeit von etwa einer halben Stunde wird eine Zugfestigkeit von 180 kg/cm² gemessen.Example III: The procedure is as in Example II, but the ferrite magnetic core is rotated back and forth several times on the bobbin case without changing the position of the splice here. After a curing time of about half an hour, a tensile strength is achieved measured at 180 kg / cm².

Beispiel IV: Man verfährt wie in Beispiel II. Nach dem Aufsetzen des erwärmten und mit dem Binder beschichteten Ferritmagnetkerns auf das ebenfalls erwärmte, mit dem Härter beschichtete Spulengehäuse, wird die Klebeschicht fünf Sekunden lang mit Ultraschall bestrahlt. Nach einer Aushärtzeit von etwa einer Minute wird eine Zugfestigkeit von ca. 260 kg/cm² gemessen.Example IV: The procedure is as in Example II. After the warmed up and with the binder coated ferrite magnetic core on the also heated, with the hardener coated bobbin case, the adhesive layer will last five seconds irradiated with ultrasound. After a curing time of about one minute, a Tensile strength of approx. 260 kg / cm² measured.

Durch Verwendung anderer Zweikomponentenkleber, höherer Erwärmungstemperaturen und/0 der größerer Ultraschallintensitäten ist es möglich, die Abbindzeiten bis auf wenige Sekunden zu verringern.By using other two-component adhesives, higher heating temperatures and / 0 of the greater ultrasound intensities it is possible to reduce the setting times up to to be reduced to a few seconds.

Claims (5)

PatentansprücheClaims 1. Verfahren zum Verbinden zweier Werkstücke mittels eines aushärtbaren Zweikomponentenklebers, dadurch gekennzeichnet, daß eine bestimmte Menge der einen Kleberkomponente auf das eine Werkstück und eine bestimmte Menge der anderen Kleberkomponente auf das andere Werkstück aufgebracht wird, und daß die Vermischung der beiden Kleberkomponenten durch die gegenseitige Kontaktierung der mit den Komponenten beschichteten Werkstücke vorgenommen wird.1. Method for joining two workpieces by means of a hardenable Two-component adhesive, characterized in that a certain amount of one Adhesive component on one workpiece and a certain amount of the other adhesive component is applied to the other workpiece, and that the mixing of the two adhesive components through the mutual contact between the workpieces coated with the components is made. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß die zu verbindenen Werkstücke erwärmt werden.2. The method according to claim 1, characterized in that the to be connected Workpieces are heated. 3. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Werkstücke nach ihrer Kontaktierung an der Klebefläche relativ zueinander bewegt werden.3. The method according to claim 1 or 2, characterized in that the Workpieces moved relative to one another after their contact on the adhesive surface will. 4. Verfahren nach Anspruch 1, 2 oder 3, dadurch gekennzeichnet, daß die Klebeschicht zwischen den Werkstücken nach deren Kontaktierung mit Ultraschall bestrahlt wird.4. The method according to claim 1, 2 or 3, characterized in that the adhesive layer between the workpieces after contacting them with ultrasound is irradiated. 5. Verfahren nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß das Mengenverhältnis der beiden Komponenten# nach Volumenteilen etwa 1:1 beträgt.5. The method according to any one of claims 1 to 4, characterized in that that the quantitative ratio of the two components # by volume is about 1: 1.
DE19712131256 1971-06-24 1971-06-24 Joining objects with two-components adhesives - by placing the components separately onto the two objects Pending DE2131256A1 (en)