DE2065687A1 - Glass containers for drinks - with chemicals resisting outer surface on in weather conditions dissolving glass material - Google Patents

Glass containers for drinks - with chemicals resisting outer surface on in weather conditions dissolving glass material

Info

Publication number
DE2065687A1
DE2065687A1 DE19702065687 DE2065687A DE2065687A1 DE 2065687 A1 DE2065687 A1 DE 2065687A1 DE 19702065687 DE19702065687 DE 19702065687 DE 2065687 A DE2065687 A DE 2065687A DE 2065687 A1 DE2065687 A1 DE 2065687A1
Authority
DE
Germany
Prior art keywords
glass
layer
packaging
glass material
drinks
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19702065687
Other languages
German (de)
Inventor
Bo Torsten Krister Bodelind
Bo Ragnar Joensson
Gunnar Georg Toll
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Platmanufaktur AB
Original Assignee
Platmanufaktur AB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from SE07834/69A external-priority patent/SE368190B/xx
Application filed by Platmanufaktur AB filed Critical Platmanufaktur AB
Priority to DE19702065687 priority Critical patent/DE2065687A1/en
Publication of DE2065687A1 publication Critical patent/DE2065687A1/en
Pending legal-status Critical Current

Abstract

Glass containers especially bottles for beer and other drinks are made from glass dissolving when exposed to weathering conditions and including treated outer surface to protect them against action of chemicals. The glass from which the containers are made of contains a larger proportion of additives such as alkali to increase its flowing properties and a smaller proportion of stabilising additives such as calium oxide. The outer protective surface of the containers is formed by a layer of a crystalised ceramic material which is applied when the surface of the glass material is de-alkalised.

Description

PATENTANWALT DIPL-PHYS. HEINRICH SEIDS 62 Wiesbaden-Bierstadt · Bierstadter Höhe IS · Postfach 12068 · Telefon (06121) 5653 82 Postsdiedc Frankfurt/Main 181008 - Bank Deutsche Bank 3956372 · Nass. Sparkasse 108003065PATENT ADVOCATE DIPL-PHYS. HEINRICH SEIDS 62 Wiesbaden-Bierstadt · Bierstadter Höhe IS · PO Box 12068 · Telephone (06121) 5653 82 Postsdiedc Frankfurt / Main 181008 - Bank Deutsche Bank 3956372 · Nass. Sparkasse 108003065

P 20 65 687.5 Wiesbaden, den 25. Oktober 1974 P 208 gr/rdP 20 65 687.5 Wiesbaden, October 25, 1974 P 208 gr / rd

AB Platmanufactur 2065687AB Platmanufactur 2065687

Malmö (Schweden)Malmo (Sweden)

Ausscheidung aus P 20 26 909.2-24Eliminated from P 20 26 909.2-24

Verpackung mit einem Hohlkörper aus Glas und Verfahren zu deren HerstellungPackaging with a hollow body made of glass and process for the manufacture thereof

Die Erfindung bezieht sich auf eine Verpackung mit einem Glaskörper, der mit einer äusseren Schutzschicht versehen ist.The invention relates to a packaging with a glass body, which is provided with an outer protective layer.

Verpackungen aus Glas, insbesondere Flaschen für Bier und erfrischende Getränke, haben infolge ihres geringen Preises und ihrer allgemeinen technischen Eignung eine starke Erhöhung in der Benutzung erfahren, und zwar sowohl in Form von Wiederauffüllglas, als auch in Form von Einweg-Verpackungen. Glass packaging, especially bottles for beer and refreshing beverages, has a low price due to its low price and their general technical suitability have seen a large increase in use, both in form of refill jars, as well as in the form of one-way packaging.

/2 509814/0403 / 2 509814/0403

DipL-Phys. Heinrich Seids · Patentanwalt · 62 Wiesbaden-Bierstadt · Bierst. Höhe 15 · Postf. 120 68 · & (0 6121) 56 53Diploma Phys. Heinrich Seids · Patent Attorney · 62 Wiesbaden-Bierstadt · Bierst. Height 15 Postf. 120 68 & (0 6121) 56 53

Es hat sich aber auch gezeigt, dass der geringe Preis und die technische Eignung der Glasemballage nachteilig ist. So ist festzustellen, dass hin und wieder sich Benutzer sich der Glasemballage an anderen Stellen als Mülltonnen als auch an anderen Abfallsammelstellen entledigen, wodurch das Glas nicht der normalen Müllaufbereitung unterworfen wird, und nur der normalen Verwitterung unterliegt. Durch seine guten technischen Eigenschaften wird aber Glas durch die normale Verwitterung nicht in nennenswertem Mass angegriffen. Es kommt hinzu, dass beim Zerschlagen von Glasemballage scharfe Scherben entstehen, die wegen der sehr geringen Verwitterungseinflüsse ihre Gefährlichkeit auf lange Zeiträume behalten. Auch wenn die Anzahl der nicht , in den Müll- bzw. sonstigen Abfall, gelangende Glasemballage im Verhältnis zu der Umsatzmenge ausserordentlich gering ist, besteht trotzdem das Bedürfnis, Mittel und Wege zu finden, die Gefährlichkeit der nicht in den Müll, oder sonstigen Abfall gelangenden Glasemballage wesentlich herabzusetzen. However, it has also been shown that the low price and the technical suitability of the glass packaging are disadvantageous. It can be seen that every now and then users find the glass packaging in other places than garbage cans as well as at other waste collection points, which means that the glass is not subjected to normal waste processing, and is only subject to normal weathering. Due to its good technical properties, however, the normal weathering not affected to any significant extent. There is also the fact that the glass packaging is broken sharp shards arise, which because of the very low weathering effects on their dangerousness keep for long periods of time. Even if the number of glass packaging that does not end up in the garbage or other waste extremely low in relation to the sales volume is, there is still the need to find ways and means to reduce the danger of not being in the garbage, or otherwise Reduce the amount of waste that comes with glass packaging.

Aufgabe der Erfindung ist es, eine Verpackung bzw. ein Glas zu entwickeln, welches sich unter Verwitterungseinflussen leicht auflöst und zugleich die Auflage eines vertretbaren Preises für Massenproduktion dieser Art erfüllt»The object of the invention is to develop a packaging or a glass which is exposed to the effects of weathering easily dissolves and at the same time fulfills the requirement of a reasonable price for mass production of this kind »

509814/0403 /3 509814/0403 / 3

Dipl.-Phys. Heinridi Seids · Patentanwalt · 62 Wiesbaden-Bierstadt · Bierst. Höhe IS · Postf. 12068 · & (06121) 565382Dipl.-Phys. Heinridi Seids · Patent Attorney · 62 Wiesbaden-Bierstadt · Bierst. Height IS Postf. 12068 & (06121) 565382

Dem steht aber die bisherige technische Entwicklung entgegen, die darauf ausgerichtet gewesen ist, im Interesse des Verpackungsinhaltes ein technisch besseres Glas zu entwickeln.However, this is countered by the previous technical development, which has been geared towards the interests of the packaging content to develop a technically better glass.

Die gestellte Aufgabe wird daher gemäss der Erfindung dadurch gelöst, dass der Glaskörper aus verwitterungsfähigem Glas gebildet ist und an der Oberfläche eine Schutzschicht gegen Zersetzen bzw. chemischen Angriff trägt.The object set is therefore achieved according to the invention solved that the glass body is made of weatherable glass and on the surface a protective layer against Decomposition or chemical attack.

Ein leicht lösliches Glas kann durch eine einfache Veränderung der Zusammensetzung der Glasmasse erreicht werden, und braucht beispielsweise nur eine Erhöhung des Flussmittelgehaltes (z.B. Alkali) beinhalten, oder eine Verminderung der Stabilisatoren (z.B. Kalzium-Oxyd). Ein derartiges Glas hat eine so niedrige chemische Resistenz, dass es beispielsweise . schnell scharfe Kanten an Scherben durch Witterung verliert und allmählich unter Einwirkung von Feuchtigkeit ganz aufgelöst wird. Ein Verpackungskörper aus solchem, leicht M löslichem Glas könnte dann unmittelbar benutzt werden, wenn der Verpackungsinhalt trocken ist, und somit den Glaskörper nicht angreift.An der Aussenseite des Glaskörpers könnte der Schutz gegen Feuchtigkeit durch die aufgebrachte Kunststoffschicht gewährleistet werden. FUr feuchten oder flüssigenEasily soluble glass can be achieved by simply changing the composition of the glass mass and, for example, only needs to increase the flux content (e.g. alkali) or reduce the stabilizers (e.g. calcium oxide). Such a glass has such a low chemical resistance that it is, for example. quickly loses sharp edges on broken glass due to the weather and gradually dissolves completely under the action of moisture. A packaging body made of such easily M soluble glass could then be used immediately when the contents of the packaging are dry and thus not attack the glass body. On the outside of the glass body, protection against moisture could be ensured by the applied plastic layer. For wet or liquid

/4 5098U/OA03/ 4 5098U / OA03

Dipl.-Phys, Heinridi Seids · Patentanwalt · 62 Wiesbaden-Bierstadt · Bierst. Höhe IS · Postf. 120 68 · ® (0 6121) 56 5382Dipl.-Phys, Heinridi Seids · Patent Attorney · 62 Wiesbaden-Bierstadt · Bierst. Height IS Postf. 120 68 ® (0 6121) 56 5382

Verpackungsinhalt, beispielsweise Getränke, müsste das leichtlösliche Glas zumindest an der Innenseite des Glaskörpers einer Oberflächenbehandlung unterworfen werden, die mit Glaskörper die erforderliche chemische Resistenz verleiht.The contents of the packaging, for example drinks, should be easily soluble Glass is subjected to a surface treatment, at least on the inside of the glass body, with the glass body gives the necessary chemical resistance.

Zur Verbesserung der Festigkeit und zur Erhöhung der chemischen Resistenz kann beispielsweise die Oberfläche des Glaskörpers £ entalkalisiert oder evtl. mit einer Schmelzglasur oder einem Glas beschichtet werden, die bzw. das mit der GlasobeiELäche umgebrannt wird und einen niedrigeren Ausdehnungsquotienten sowie gute chemische Resistenz hat. Hierdurch erhält man die gewünschte Resistenz gegenüber dem Inhalt, aber auch eine sehr beträchtliche Erhöhung der Festigkeit, da die bei Abkühlung in der Oberfläche der Glasverpackung entstehende Kompression das Entstehen der Oberflächenschäden verhindert. Im Rahmen der Erfindung kann die Glasoberfläche auch eine Schicht aus Metalloxyd, beispielsweise Zinnoxyd aufweisen, die in Form einer gasförmigen Metallverbindung, z.B. Zinnchlorid, zugeführt wird, wodurch die erforderliche Verstärkung der chemischen Resistenz und eine Erhöhung der Festigkeit erreicht werden.To improve strength and increase chemical Resistance can, for example, the surface of the glass body £ dealkalized or possibly with a melting glaze or a Glass that is burned over with the glass surface and has a lower expansion ratio and good chemical resistance. This gives you the one you want Resistance to the contents, but also a very considerable increase in strength, as the in The compression created on the surface of the glass packaging prevents surface damage from occurring. Within the scope of the invention The glass surface can also have a layer of metal oxide, for example tin oxide, which is in the form of a gaseous metal compound, e.g. tin chloride, is supplied, whereby the necessary reinforcement of the chemical Resistance and an increase in strength can be achieved.

/5/ 5

509 8. U/0403509 8th U / 0403

Dipl.-Phys. Heinrich Seids · Patentanwalt · 62 Wiesbaden-Bierstadt · Bierst. Höhe 15 · Postf. 120 68 · $? (06121) 565382Dipl.-Phys. Heinrich Seids · Patent Attorney · 62 Wiesbaden-Bierstadt · Bierst. Height 15 · Postf. 120 68 · $? (06121) 565382

Die Erfindung hat sich auch zur Aufgabe gestellt, Verfahren zur Herstellung von Verpackungen der oben beschriebenen Art zu schaffen, Nach einem vorzugsweise zu benutzenden Verfahren wird der warme, von der Glasmaschine kommende Glaskörper mit einer Schicht aus Zinnoxyd oder Titandioxyd beschichtet, das in einer Gasphase, beispielsweise in Form von Zinnchlorid oder Isopropylerthotitanat zugeführt wird.The invention has also set itself the task of providing a method for producing packaging of the type described above to create, According to a preferred method to be used the warm glass body coming from the glass machine is coated with a layer of tin oxide or titanium dioxide is supplied in a gas phase, for example in the form of tin chloride or isopropyl thotitanate.

Im Rahmen der Erfindung lässt sich eine Oberflächenverstärkung des Glaskörpers dadurch erreichen, in dem auf die Oberfläche eine Schmelzglasur oder eine Schicht aus verwitterungsfestem Glas aufgebracht wird.In the context of the invention, a surface reinforcement of the glass body can be achieved in that on the surface a melt glaze or a layer of weatherproof glass is applied.

Einige Ausführungsbeispiele der Verpackungen gemäss der Erfindung werden im folgenden anhand der Zeichnung näher erläutert. Es zeigen:Some embodiments of the packaging according to the invention are explained in more detail below with reference to the drawing. Show it:

Fig. 1 einen halben axialen Schnitt durch eine Flasche M gemäss der Erfindungj1 shows a half axial section through a bottle M according to the invention

Fig. 2Fig. 2

und 3 vergrösserte Darstellungen des Ausschnittes II der Figur 1 in verschiedenen Ausführungsformen.and 3 enlarged representations of section II of Figure 1 in various embodiments.

/6/ 6

5098U/04035098U / 0403

Dipl.-Phys. Heinridi Seids · Patentanwalt ■ 62 Wissbaden-Bierstadt · Bierst. Höhe 15 · Postf. 120 68 · & (0 6121) 56 53Dipl.-Phys. Heinridi Seids · Patent Attorney ■ 62 Wissbaden-Bierstadt · Bierst. Height 15 Postf. 120 68 & (0 6121) 56 53

Im Beispiel der Figur 1 ist der Flaschenkörper 1 praktisch vollständig, d.h.. vom Mundungswulst 2 des. Flaschenhalses bis über den gesamten Flaschenboden 3 mit einer Kunststoffschicht 4 gemäss der Erfindung überzogen. In the example of FIG. 1, the bottle body 1 is practically complete, i.e. from the mouth bead 2 of the bottle neck Coated over the entire bottle base 3 with a plastic layer 4 according to the invention.

Im Beispiel der Figur 2 besteht der Flaschenkörper 1 aus leicht löslichem Glas und ist an der Innenseite mit einerIn the example of Figure 2, the bottle body 1 consists of easily soluble glass and is on the inside with a

™ Schicht 5, beispielsweise keramischer Art oder von Glasurart belegtf um den Flaschenkörper 1 für die Aufnahme von Flüssigkeiten geeignet zu machen. Auf-der Aussenseite ist eine" Kunststoffschicht 4 aus Polyäthylen, Polyvinylchlorid, Methylmetakrylat oder einer Polymerschicht aus Polyvinylchlorid und Polyvinylacetat fest aufgebracht.Has ™ layer 5, for example of ceramic type or of Glasurart f around the bottle body 1 for the containment of liquids to make it suitable. A plastic layer 4 made of polyethylene, polyvinyl chloride, methyl methacrylate or a polymer layer made of polyvinyl chloride and polyvinyl acetate is firmly applied to the outside.

Im Beispiel der Figur 3 besteht der Flaschenkörper 1 wiederum aus leicht löslichem Glas und ist an der Innenseite mit einer £ chemisch resistenten Schicht 5 versehen. Auf der Aussenseite des Flaechenkörpers 1 ist ebenfalls eine chemisch resistente und verstärkend® Schicht 6 ausgebildet. Auf diese Schicht des Flaschenkörpers 1 ist eine zusätzliche Schicht 7 aus Polyäthylensuspension gelegt, auf die aussen wiederum eine Polyäthylenschicht 4, beispielsweise im Wirbelschichtverfahren, aufgebracht ist.In the example of Figure 3, the bottle body 1 again consists of easily soluble glass and is on the inside with a £ chemically resistant layer 5 provided. On the outside of the surface body 1 there is also a chemically resistant one and reinforcing® layer 6 formed. An additional layer 7 is made of this layer of the bottle body 1 Placed polyethylene suspension, on the outside in turn a polyethylene layer 4, for example in the fluidized bed process, is upset.

-Patentansprüche--Patent claims-

. ' , ~' ·. - . 509814/0403 /7. ', ~' ·. -. 509814/0403 / 7

Claims (6)

Dipl.-Phys. Heinrkh Seids ■ Patentanwalt · 62 Wiesbaden-Bieretadt · Bierst. Höhe 15 · Postf. 12068 · <g" (06121) 565362 PatentansprücheDipl.-Phys. Heinrkh Seids ■ Patent Attorney · 62 Wiesbaden-Bieretadt · Bierst. Height 15 · Postf. 12068 · <g "(06121) 565362 claims 1)!Verpackung mit einem Glaskörper, beispielsweise einer Flasche, die mit einer äusseren Schutzschicht versehen ist, dadurch gekennzeichnet, dass der Glaskörper (1) aus verwitterungsfähigem Glas gebildet ist und an der Oberfläche eine Schutzschicht gegen Zersetzen bzw. chemischen Angriff trägt. : 1)! Packaging with a glass body, for example a bottle, which is provided with an outer protective layer, characterized in that the glass body (1) is made of weatherable glass and has a protective layer on the surface against decomposition or chemical attack. : 2) Verpackung nach Anspruch 1, dadurch gekennzeichnet, dass das Glasmaterial erhöhten Flüssmittelgehalt, beispielsweise Alkali und verringerten Gehalt an Stabilisatoren, beispielsweise Calciumoxyd, aufweist.2) Packaging according to claim 1, characterized in that the glass material increased liquid content, for example alkali and reduced content of stabilizers, for example Calcium oxide. 3) Verpackung nach einem der Ansprüche 1 und 2, dadurch gekennzeichnet, dass die Oberfläche des Glasmaterials (1) entalkalisiert ist.3) Packaging according to one of claims 1 and 2, characterized in that that the surface of the glass material (1) is dealalized. 4) Verpackung nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Oberfläche des Glasmaterials (1) aus einer kristallisierten, keramikartigen Schicht (7) gebildet ist.4) Packaging according to one of the preceding claims, characterized in that the surface of the glass material (1) is formed from a crystallized, ceramic-like layer (7). /8 5098U/0A03/ 8 5098U / 0A03 Dipl.-Phys. Heinrich Seids · Patentanwalt · 62 Wiesbaden-Bierstadt · Bierst. Höhe 15 · Postf. 120 68 · & (0 6121) 56 53Dipl.-Phys. Heinrich Seids · Patent Attorney · 62 Wiesbaden-Bierstadt · Bierst. Height 15 Postf. 120 68 & (0 6121) 56 53 5) Verfahren zur Herstellung einer Verpackung nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Glasoberfläche (T) durch eine Schicht aus Metalloxid,
beispielsweise Zinnoxid, gebildet ist.5) Method for producing a package according to one of the preceding claims, characterized in that the glass surface (T) is covered by a layer of metal oxide,
for example tin oxide is formed. 6) Verfahren nach Anspruch 5, dadurch gekennzeichnet, dass die Oberfläche des Glaskörpers durch eine Schmelzglasur oder eine Schicht aus verwitterungsfestem Glas gebildet6) Method according to claim 5, characterized in that the surface of the glass body is covered by a melt glaze or formed a layer of weatherproof glass W ist. W is. 50 98 1 4/040350 98 1 4/0403
DE19702065687 1969-06-03 1970-06-02 Glass containers for drinks - with chemicals resisting outer surface on in weather conditions dissolving glass material Pending DE2065687A1 (en)