DE1985474U - PRINT TEMPLATE. - Google Patents
PRINT TEMPLATE.Info
- Publication number
- DE1985474U DE1985474U DE1968R0036851 DER0036851U DE1985474U DE 1985474 U DE1985474 U DE 1985474U DE 1968R0036851 DE1968R0036851 DE 1968R0036851 DE R0036851 U DER0036851 U DE R0036851U DE 1985474 U DE1985474 U DE 1985474U
- Authority
- DE
- Germany
- Prior art keywords
- screen printing
- polyvinyl alcohol
- layer
- printing stencil
- stencil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
DruckschablonePrinting template
Die !Steuerung betrifft eine Sieb= oder Filmdruckschablone rait einem Gewebeträger und einer Chromat-Polyvinylalkohol-Schicht, die bildgemäß belichtet,, mit Wasser entwickelt und chemisch gehärtet ist. Im nachstehenden wird abkürzend nur von Siebdruck gesprochen, jedoch versteht sich, daß mit dieser Bezeichnung auch Filmdruck und verwandte Techniken umfaßt werden«The control concerns a screen or film printing stencil rait a fabric carrier and a chromate-polyvinyl alcohol layer, which is exposed according to the image, developed with water and chemically hardened. The following is abbreviated only spoken of screen printing, but it goes without saying that this term also includes film printing and related techniques to be included "
Mach einer Ausfuhrungsform des Siebdrucks versieht man die Gaze mit einer lichtempfindlichen Chromat-Kolloidschicht, kopiert die Vorlage ein, wodurch die belichteten Schicht·= teile schwer löslich werden, und entfernt die unbelichteten Stellen mit Wasser. Die so erhaltene Siebdruckschablone wird dann in üblicher Weise zum Drucken benutzt,,In one embodiment of screen printing, the Gauze with a light-sensitive chromate colloid layer, copies the original in, making the exposed layers difficult to dissolve, and removes the unexposed ones Places with water. The screen printing stencil obtained in this way is then used in the usual way for printing.
Als Kolloid hat sich seit langem Polyvinylalkohol eingeführt, der gegenüber Gummiarabikum, Gelatine, Fischleim u.dgl ο verschiedene Vorteile hatοPolyvinyl alcohol has long been introduced as a colloid, which has various advantages over gum arabic, gelatine, isinglass and the like ο
■ ■ ' - 2 -■ ■ '- 2 -
Ss hat sich jedoch gezeigt, daß die chromatgehartete Polyvinylalkohol-Schicht allein den mechanischen und chemischen Beanspruchtangen nicht standzuhalten vermag, denen sie bei der Durchführung des Siebdruckes unterliegtβ Um ihre Widerstandsfähigkeit zu erhöhen, verstärkt man sie gewöhnlich nach dem Auslösen durch Auftragen einer Lackschicht. Diese Verstärkung bedeutet jedoch nicht nur einen zusätzlichen Arbeitsgang, sondern führt auch oftmals zu Störungen, die auf eine schlechte Haftung des Verstärkerlacks auf der Polyvinylalkohol-Schicht zurückzuführen sind«Ss has shown, however, that the chromatgehartete polyvinyl alcohol layer alone can not withstand the mechanical and chemical Claimed Angen that they in the practice of screen printing β subject order to increase their resistance, it amplifies usually after triggering by applying a layer of varnish. This reinforcement does not only mean an additional work step, but also often leads to malfunctions that can be attributed to poor adhesion of the reinforcement varnish to the polyvinyl alcohol layer «
Nun ist es zwar bekannt, daß sich die Wasserfestigkeit von Polyvinylallcohol-Schichten, durch chemische Umsetzung mit Stoffen erhöhen lässt, die mit den HydroxyI-Gruppen des Polyvinylalkohole su reagieren vermögen» Die meisten dieser Umsetzungen bedingen jedoch erhöhte Reaktionstemperaturen. Gerade hier sind bei den üblichen Siebdruckgeweben (Seide, Polyamide, Polyester) Grenzen gesetzt<, Normalerweise darf man nicht über etwa 80 C gehen, um einerseits das Gewebe nicht zu beeinträchtigen und anderer= seits Passerschwierigkeiten zu vermeiden»Now it is known that the water resistance of polyvinyl alcohol layers is increased by chemical reaction with substances that can increase with the HydroxyI groups of the polyvinyl alcohols are able to react »Most of these reactions, however, require elevated reaction temperatures. Especially here there are limits to the usual screen printing fabrics (silk, polyamides, polyester) <, Usually you shouldn't go above around 80C on the one hand not to impair the fabric and on the other hand to avoid fitting difficulties »
Die Härtung der PoIyvinylalkohol-Schichten sollte also tunlichst bei entsprechend mäßiger Temperatur durchgeführt werden«, So könnte man daran, denken, die Reaktivität von Polyvinylalkohol gegenüber Aldehyden wie Formaldehyd in Gegenwart von sauren Katalysatoren auszunutzen, durch die die Wasserfestigkeit des Polyvinylalkohole bekanntlichThe hardening of the polyvinyl alcohol layers should therefore should be carried out at a correspondingly moderate temperature «, one might think of the reactivity of To exploit polyvinyl alcohol over aldehydes such as formaldehyde in the presence of acidic catalysts by which the water resistance of polyvinyl alcohols is known
verbessert werden, kann. Die nachträgliche Behandlung der entwickelten Siebdruckschablone mit solchen Agentien hat sich jedoch als mühsam, unangenehm und nicht immer erfolg= reich erwiesen* Für den Siebdruck ist die Reproduzierbarkeit der Ergebnisse jedoch notwendige VorausSetzung, und darüfoerhinaus ist - wie gesagt - eine möglichst einfache Arbeitstechnik anzustreben»can be improved. The subsequent treatment of the developed screen printing stencil with such agents However, it has proven to be laborious, uncomfortable and not always successful * For screen printing, however, the reproducibility of the results is a necessary prerequisite, and In addition, as I said, it is as simple as possible To strive for work technique »
Wie praktische Versuche gezeigt haben, ist es auch nicht möglich, Formaldehyd oder Verbindungen, die Formaldehyd in reaktiver Form enthalten, homogen in die Polyvinyl-= alkohol-Schicht oder die zum Beschichten benutzte Polyvinylalkohol·= Lösung einzuverleibenο So verbietet sich die Mischung von wässrigen Poly vinylalkohol·=· Lösungen mit wäss= rigen Lösungen von Harnstoff/Formaldehyd-Vorkondensaten wegen der Unverträglichkeit dieser beiden Bestandteile„As practical tests have shown, it is not either possible formaldehyde or compounds containing formaldehyde contained in reactive form, homogeneously in the polyvinyl = alcohol layer or the polyvinyl alcohol used for coating · = Incorporating a solution ο Mixing aqueous polyvinyl alcohol · = · solutions with water = solutions of urea / formaldehyde precondensates due to the incompatibility of these two components "
Die Neuerung bezweckt, diesen Wachteilen abzuhelfen, und löst die Aufgabe, eine Siebdruckschablone zu schaffen, die in direktem Prozess herstellbar ist und sich nach der Fertigstellung durch einen Film hoher Beständigkeit, Elastizität und Abriebfestigkeit auszeichnet, ohne daß es der Anwendung hoher Temperaturen oder des Aufbringens von Verstärkerlacken bedarfοThe aim of the innovation is to remedy these parts of the guard, and solves the task of creating a screen printing stencil that can be produced in a direct process and that is based on the Finishing characterized by a film of high durability, elasticity and abrasion resistance without it the use of high temperatures or the deposition of amplifier varnishes is required ο
Diese Aufgabe wird neuerungsgemäß dadurch gelöst, daß die Polyvinylalkohol-Schicht ein plastifiziertes Aminoplast-Harz fein dispergiert enthält und nach Fertigstellung derThis object is achieved according to the invention in that the Polyvinyl alcohol layer a plasticized aminoplast resin contains finely dispersed and after completion of the
Siebdruckschablone mit Hilfe eines sauren, Katalysators ausgehärtet ist„Screen printing stencil is cured with the help of an acidic catalyst "
Zweckmäßigerweise enthält die Schicht ein Pigment, insbe= sondere TiO»,, das eine verstärkende Wirkung hat»The layer expediently contains a pigment, in particular = special TiO »,, which has a reinforcing effect»
Mit Vorteil ist das Miinoplast-'Harz mit Alkydharz modifiziert,, um seiner Sprödigkeit entgegen zu wirken.The Miinoplast resin is advantageously modified with alkyd resin, to counteract its brittleness.
Besonders bewährt hat sich die Härtung durch Tränken der Schicht mit alkoholischer Salzsäureο Zweckmäßigerweise ist der Härter angefärbt, so daß an der Siebdruckschablone erkennbar ist," an welchen Stellen Härter aufgebracht,, doho die Vernetzung der Polyvinylalkohol-Schicht vollzogen ist»Proved particularly suitable curing has by impregnating the layer with alcoholic Salzsäureο Conveniently, the hardener is stained so that it can be seen on the screen printing stencil, ",, d o h o is complete the crosslinking of the polyvinyl alcohol layer at which points hardener applied"
Die Neuerung beruht auf der unerwarteten Feststellung,, daß es möglich ist, in Polyvinylalkohol eine vorzugsweise alkoholische Lösung eines säurehärtenden Äminoplast-Harzes exnzudispergxeren und dadurch eine sehr stabile Emulsion herzustellen. Für die Dispergierung genügt ein Schnell= rührer, da die Verteilung der Harnstoffharze leicht erfolgt und keine großen Scherkräfte erfordert.The innovation is based on the unexpected finding, that it is possible to use a preferably alcoholic solution of an acid-hardening aminoplast resin in polyvinyl alcohol Exnzudispergxeren and thereby to produce a very stable emulsion. A Schnell = is sufficient for dispersion stirrer, since the urea resins are easily distributed and do not require high shear forces.
Ohne die Neuerung auf eine bestimmte Theorie zu beschränken wird angenommen, daß die Härtung des Polyvinylalkohole durch Reaktion mit Formaldehyd und/oder Methylolgruppen des Ä&iinoplast-Harzes in Gegenwart des sauren Katalysators erfolgt, wodurch eine Vernetzung des Polyvinylalkohole-. bewirkt wird.Without restricting the innovation to a specific theory It is believed that the polyvinyl alcohols harden through reaction with formaldehyde and / or methylol groups of the A & iinoplast resin in the presence of the acidic catalyst takes place, whereby a crosslinking of the polyvinyl alcohol. is effected.
Ebenso wie die Chromathärtung von Polyvinylalcohol allein zur Erzielung der geforderten Beständigkeit", insbesondere Xf asser festigkeit, nicht genügt, behalten Schichten aus Polyvinylalkohol auch nach dem Hydrophobieren etwa mit Formaldehyd bzw* Formaldehyd^Verbindungen bekanntlich eine deutliche Wasserquellfoarkeit. Neuerungsgemäß wird jedoch eine synergistische Wirkung des Formaldehydes und des Chromates, verbunden mit dem Einfluß des aktinischen Lichtes, beobachtet,, so daß die erstrebte Beständigkeit der Poly= vinylalkohol-Schicht erreicht wird,,Just like the chromate hardening of polyvinyl alcohol alone to achieve the required resistance ", in particular Xf ater strength, not enough, keep layers out Polyvinyl alcohol is also known to be a water repellent, for example with formaldehyde or * formaldehyde ^ compounds clear water swelling. However, according to the innovation a synergistic effect of formaldehyde and chromate, combined with the influence of actinic light, observed, so that the desired resistance of the poly = vinyl alcohol layer is achieved,
Unter "Aminoplast-Harz" werden hier allgemein Kondensationsprodukte von Aldehyden, insbesondere Formaldehyd, mit Harnstoff oder/und Thioharnstoff verstanden, wie sie die Industrie mit einem stufenlosen Molverhältnis zwischen ca, 1 % 1 und 4 ι 1 liefert«,"Aminoplast resin" is here generally understood to mean condensation products of aldehydes, in particular formaldehyde, with urea and / or thiourea, as is supplied by industry with a continuously variable molar ratio between approx. 1% 1 and 4 ι 1 «,
Zur Herstellung der Siebdruckschablone verfährt man beispielsweise wie folgt?To produce the screen printing stencil, for example, do you proceed as follows?
In 58 Gewichtsteilen einer etwa 10%igen wässrigen Lösung eines handelsüblichen Polyvinylalkohole mit einem mittleren Molgewicht von ca, 85000, einer Verseifungszahl von 85 - 90% und einer Viskosität von 25 cP (bei 4%iger Lösung) werden 2 Gewichtsteile TiO» und 40 Gewichtsteile einer etwa 30%igen butanolischen Lösung eines hochelastischen mit Butanol verätherten, mit Alkydharz modifizierten Harnstoff/Form= aläehyd-Harzes eingerührte Zu diesem Zweck benutzt manIn 58 parts by weight of an approximately 10% aqueous solution a commercially available polyvinyl alcohol with an average molecular weight of approx. 85000, a saponification number of 85 - 90% and a viscosity of 25 cP (with 4% solution) 2 parts by weight of TiO »and 40 parts by weight of an approximately 30% strength butanolic solution of a highly elastic urea etherified with butanol and modified with alkyd resin / form = aläehyd resin stirred in. For this purpose one uses
einoiSchnellrührer und verteilt solange, bis eine feine Emulsion entstanden ist, was in wenigen Minuten eintritt=One oi high-speed beater and spread until a fine Emulsion has arisen, which occurs in a few minutes =
Diese Emulsion wird wie eine herkömmliche Photoschicht weiter verarbeitet» Die Sensibilisierung erfolgt mit 10 Gewichtsteilen einer 20%igen j^moniumdichromat-Lösungo Die Mischung wird in bekannter Weise auf ein Gewebe aufgetragen, das straff auf den Rahmen der Siebdruckschablone gespannt ist, bei sehr feinen SchabIonengeweben gegebenenfalls nach vorheriger Verdünnung mit Wasser„ Man erhält eine weißliche Schichte Nach dem Trocknen wird die Vorlage einkopiert«, Bei der Bemessung der Belichtungszeit können die um ca. 20 % erhöhten Srfahrungswerte für normale Kopier·= schichten auf Polyvinylalkohol-Basis zugrunde gelegt werden«This emulsion is further processed as a conventional photo layer »The sensitization is effected with 10 parts by weight of a 20% j ^ moniumdichromat solution o The mixture is applied in a known manner on a fabric tautly stretched to the frame of the screen printing stencil, fine at very Stencil fabrics, if necessary after prior dilution with water "A whitish layer is obtained after drying, the original is copied in."
Nach der Belichtung entwickelt man mit etwa handwarmen WasserοAfter exposure you develop with about lukewarm Waterο
Nach einer weiteren Zwischentrocknung wird eine ca, 2%ige alkoholische HCl-Lösung, die mit einem mineralsäurebeständigen Farbstoff, beispielsweise mit Tetraäthyl-ρ,ρ*- diamino-diphenodisulfonaphthofuchsonimonium (Natrium-Salz des inneren Sulfonats) oder einem anderen direktziehenden Substantiven Farbstoff angefärbt ist, beidseitig und gleichmäßig mit einem Pinsel oder Schwamm auf der Schablone verteilt, und zwar in einer Menge, daß auf jeder Seite pro After a further intermediate drying, an approx. 2% strength alcoholic HCl solution with a mineral acid-resistant dye, for example with tetraethyl-ρ, ρ * - diamino-diphenodisulfonaphthofuchsonimonium (sodium salt of the inner sulfonate) or another substantive noun dye, spread evenly on both sides with a brush or sponge on the stencil, in an amount that is per each side per
2
m ca. 100 aal Härter lösung aufgetragen werden o Die aus=
reichende und gleichmäßige Verteilung wird durch die2
m approx. 100 eel hardener solution are applied o Sufficient and even distribution is ensured by the
Anfärbung der Härterlösung erleichterte Die Schicht nimmt die benötigte Menge Härter auf, während der Überschuß verdunstet. Nachdem die Schablone im wesentlichen getrocknet ist,, wird die endgültige Aushärtung durch Wärmebehandlung bei 50 - 80°C bewirkte Danach ist die Schablone druckfertigο Der ausgehärtete Polyvinylalkohol~Film besitzt eine gute Elastizität,, höhe Abriebfestigkeit und hervorragende Be-= ständigkeit gegen Lösungsmittel, wie aliphatisch^ und aromatische Kohlenwasserstoffe,, niedere Alkohole und Ester sowie Chemikalien, insbesondere Säuren und Laugen in den im Filmdruck üblichen Konzentrationen»Staining of the hardener solution eased the layer takes the required amount of hardener while the excess evaporates. After the stencil has essentially dried is ,, becomes the final hardening by heat treatment at 50 - 80 ° C then the stencil is ready for printing The cured polyvinyl alcohol film has good properties Elasticity ,, high abrasion resistance and excellent loading = Resistance to solvents such as aliphatic and aromatic hydrocarbons, lower alcohols and esters as well as chemicals, especially acids and alkalis in the concentrations customary in film printing »
Ein Ausschnitt aus einer so hergestellten Siebdruckschablone ist als Modell beigefügt; die Bildwiedergabe ist nicht neuerungswesentlich»A section from a screen printing stencil made in this way is attached as a model; the image reproduction is not essential to the innovation »
Claims (2)