DE1926363C - Method of reducing NH low 4 NO low 3 losses when heating ammonium trate or fertilizer containing ammonium trate - Google Patents
Method of reducing NH low 4 NO low 3 losses when heating ammonium trate or fertilizer containing ammonium trateInfo
- Publication number
- DE1926363C DE1926363C DE1926363C DE 1926363 C DE1926363 C DE 1926363C DE 1926363 C DE1926363 C DE 1926363C
- Authority
- DE
- Germany
- Prior art keywords
- trate
- low
- ammonium nitrate
- ammonium
- losses
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
I 926,363I 926,363
>' pci der Herstellung von Ammoniumnitrat als Dünge- Ammoniumnitrat? in {Berührung kommt, Vorzugsweise >' pci the production of ammonium nitrate as fertilizer ammonium nitrate? comes in {contact, preferably
mute! treten, häufig wäßrige Anfsehlftmrnungen oder l werden Ammoniak und Inertgas sorgfältig durch cinemute! ammonia and inert gas occur frequently aqueous Anfsehlftmrnungen or l carefully cine
('-. feuchte feste Produkte auf, die entweder aus Ammo- in der Leitung liegende Mischvorrichtung gemischt,('-. moist solid products, mixed either from Ammo in the line mixing device,
f. niuinnitrat oder Ammoniumnitrat und weiteren Pt'inge- ehe das Gasgemisch das Ammoniumnitrat erreicht,f. nickel nitrate or ammonium nitrate and other Pt'inge- before the gas mixture reaches the ammonium nitrate,
mitteln bestehen, [ro Zuge der Herstellung werden s Falls erwünscht, kann das Ammoniak aus den Ab-consist of agents, [ro in the course of production s If desired, the ammonia can be extracted from the waste
solches Ammoniumnitrat oder entsprechende Dünge- gasen in konventioneller Weise, z, B, durch Auswaschensuch ammonium nitrate or corresponding fertilizer gases in a conventional manner, for example by washing out
millelgemische direkt getrocknet, Durch das Trocknen mit Säure, wiedergewonnen werden.Millel mixtures directly dried, by drying with acid, can be recovered.
t ■ werden die weitere Handhabung erleichtert und die Da durch das erfindungsgemäße VerfaUren dieThe further handling is facilitated and the process according to the invention facilitates the
[ Transportkosten herabgesetzt. Es zeigte sich, daß beim Sublimation von NH4NO3 unterdrückt wird, können[Reduced transport costs. It was found that when subliming NH 4 NO 3 is suppressed, can
£ Trocknen bei Temperaturen oberhalb etwa 93°C das \q höhere Trocknungstemperaturen, als bisher angewandt£ drying at temperatures above about 93 ° C, the \ q higher drying temperatures than previously used
(■ Ammoniumnitrat ,sublimiert und sichtbaren Rauch werden. Beispielsweise kann die Austrittstempcratur (■ Ammonium nitrate, sublimated and visible smoke. For example, the exit temperature can
[t, bildet. Die Sublimation' ist einerseits vom wirtschaft- '!des Gases.'die bei konventionellen direkten. Trocknern[t, educates. The sublimation ' is on the one hand from the economy'! Of the gas. 'That with conventional direct. Dryers
i_ liehen Standpunkt aus unerwünscht, andererseits ct-vas unterhalb 93°C liegt, auf 120 bis 150'* erhöhtI_ borrowed point of view undesirable, on the other hand ct-vas is below 93 ° C, increased to 120 to 150 '*
\. können dieDämpfczueinerLuftverschmutziingführeu. werden. Da die Trocknunijsgeschwindigkeit propor- \. The dampers can lead to air pollution. will. Since the drying speed is proportional
f Eine ähnliche Rauchentwicklung tritt auf, wenn gc- ts tional der Trocknungstemperatur zunimmt, kann auff A similar development of smoke occurs when the drying temperature increases, can
L schmolzenes Ammoniumnitrat abgekühlt wird. · diese Weise die benöiigte Verweilzeit bei den höheren L molten ammonium nitrate is cooled. · In this way the required dwell time for the higher ones
Die Gründung betrifft nun ein Verfahren zum Ver- Temperatureii stark herabgesetzt werden. So WurdeThe foundation now concerns a method to reduce the temperatureii considerably. So became
ringen) von M 1,M)3-Verlusten beim Erhitzen von beispielsweise festgestellt, daß beim Trocknen von Ammoniumnitrat oder NH1NO3 enthaltenden Dünge- Ammoniumnitrat mit 0.40 Gewichtsprozent Wasser mitteln in einem Inert gasstrom auf Temperaturen νοη 2o auf einen Wassergehalt von 0,15 Gewichtsprozent in 93 bis !70 C: lias Verfahren ist dadurch gekennzcich- einem Wirbelschichttrockner bei 135 C eine Vervveilnet. daß dem Inertgasstrom vor seinem F.insalz 0,04 zeit von etwa 7'I2 Minuten, bei 99 C hingegen einewrestling) of M 1, M) 3 losses when heating, for example, found that when drying ammonium nitrate or NH 1 NO 3 containing fertilizer ammonium nitrate with 0.40 percent by weight of water averages in an inert gas stream to temperatures νοη 2o to a water content of 0, 15 percent by weight in 93 to 70 ° C: The process is characterized by a fluidized bed dryer at 135 ° C. that the inert gas stream before its F.insalz 0.04 time of about 7'I 2 minutes, at 99 C, however, one
: bis 3 Volumprozent Ammoniak (.bezogen auf das Verweilzeit von 7Ö Minuten benotigt wurde. Die Er-: up to 3 percent by volume of ammonia (based on the dwell time of 70 minutes was required.
ΐ Inertgas)/ugeset/t werden. Bevorzugt wird als Inertgas findung erlaubt daher die Verwendung kleinerer ΐ inert gas) / ugeset / t. The preferred inert gas is therefore the use of smaller ones
Luft. Man kann jedoch auch mit anderen Gasen, z. B. 25 Trocknungsaniagen mit höherer Kapazität.Air. However, you can also use other gases, such. B. 25 drying plants with higher capacity.
• Stickstoff, arbeiten. Die /ur Verringerung der Rauch- In den folgenden Beispielen beziehen sich die Pro-• Nitrogen, work. The reduction in smoke In the following examples, the pro-
; bildung benötigte Ammoniakmenge steigt logarith- zentangaben, falls nichts andcies venrtcrkt. auf das; The amount of ammonia required to form increases in logarithms, unless andcies are specified. on the
■: misch innerhalb de· .vbigen Bereichs mit zunehmender Volumen,■: mixed within the same range with increasing volume,
Temperatur des Ammoniumnitrat·, an. . 11Temperature of the ammonium nitrate ·, at. . 11th
Die Geschwindigkeit des Gussdoms wird gewöhn- 30 BeispielThe speed of the cast dome becomes habitual
lieh /wischen 90 und 240 m/pMn, vezogen auf daslent / wipe 90 and 240 m / PMN, v OVERTIGHTEN the
Ammoniumm rat. betragen. Wird das (Jas zum Trock- Durch folgende Versucnsreihe wird die Wirkung vonAmmonium rat. be. If the (yes to dry) The following series of experiments will determine the effect of
nen verwendet, so liegt die Eintrittstemperatur (die Ammoniak beim Trocknen von Ammoniumnitrat Temperatur, bei der das Gas zunächst mit dem Ammo- illustriert: HciUc Luft, in welche eine bestimmte Menge niumiiitrat in Berührung kommt) gewöhnlich zwischen 35 Ammoniak injiziert worden war. wurde in der Leitung etwa 150 und 427'C. Die Austrittstemperatur des mittels eines Propellers gemischt. rl dem Boden eines Gases liegt gewöhnlich zwischen 88 und 150 C. Die kleinen Wirbelsthi>:httrockners zugeführt, der etwa Volumenmenge an Gas pro Gewichtseinheit Ammo- 1.15 kg feuchtes Ammoniumnitrat (0,3 Gewichtsproniiimnitrat hängt vom Feuchtigkeitsgehalt des Ammo- zent Wasser) enthielt Das Luft-Ammoniak-Gemisch niumnitrats. ocr Gastemperatur und der Verwcil/cit ab. 40 wurde mit einer Geschwindigkeit von 1,36 cbm pro Übliche Werte liegen bei 3.1 bis 15,5 cbm Inertgas pro Minute durch djs Ammoniumnitrat geführt und aus Minute pro Kilogramm festes Ammoniumnitrat. dem oberen Teil des Wirbelschichttrockners abge-used, so is the inlet temperature (the ammonia when drying ammonium nitrate Temperature at which the gas initially illustrated with the Ammo: HciUc air, in which a certain amount sodium nitrate) usually between 35% ammonia was injected. was on the line around 150 and 427'C. The outlet temperature of the mixed by means of a propeller. rl the bottom of one The gas is usually between 88 and 150 C. The small eddies: httrockners supplied to the approx Amount of volume of gas per unit weight of ammonium 1.15 kg of moist ammonium nitrate (0.3% by weight of ammonium nitrate depends on the moisture content of the ammo- cent water) contained the air-ammonia mixture nium nitrate. ocr gas temperature and the Verwcil / cit. 40 was at a speed of 1.36 cbm per Usual values are 3.1 to 15.5 cbm of inert gas per minute passed through the ammonium nitrate and out Minute per kilogram of solid ammonium nitrate. the upper part of the fluidized bed dryer
Dic genaue Temperatur, bei welcher das Ammonium- zogen 10 Minuten lang wurden 0,3 cbm pro Minute mtr.it /u sublimieren und zu rauchen beginnt, hängt des Abgasgcmischrs über eine gesonderte Hntnahmc-VOi) d^r (eweils zu trocknenden Zusammensetzung ab. 45 leitung abgezogen; dieses Gasgemisch μ langte nachhi allen Fallen hcgmnt das Produkt erst oberhalb 93 C einander durch drei Waschflaschen. ν >u denen jede /11 rauchen. Beispielsweise beginnen sowohl Ammoni- K)OmI Wasser enthielt, und dann durch ein MiIhumnitrat wie auch Ammoniumnitratsulfat und ein p..renfilter. In den WascliH.ischcn wurden Ammoniak Nitrophosphatdünger im Bereich /wischen 93 und und große Feststoffteilchen (NH1NO3). die vom Abgas 1O? C /u sublimieren. I crncr werden in allen diesen 50 mitgerissen wirden waren, entfernt. Rauchpartikeln Fällen die Dampfe sehr dicht sobald die Temperatur (mitgerissenes Ammoniumnitrat) wurden auf dem um 8 bis 11 C. von der Anfangs-Sublimationstempe- Filter gesammelt. Nach Beendigung des Versuchs wurratur aus. angestiegen ist. den ύ\<· Rauchpartikelr. mit 100 ml W.isser vom FilterThe exact temperature at which the ammonium pull for 10 minutes will sublime 0.3 cbm per minute mtr.it / u and begin to smoke, depends on the exhaust gas mixer via a separate take-off (sometimes to be dried composition) 45 line disconnected; after all cases this gas mixture μ reached the product only above 93 C each other through three washing bottles. Each of them smoke also ammonium nitrate sulfate and a prene filter. In the washing machine, ammonia nitrophosphate fertilizers were found in the range of 93 and and large solid particles (NH 1 NO 3 ). from the exhaust gas 1 O? C / u sublimate. I crncr got swept away in all of these 50 goods. Smoke particles drop the vapors very tightly as soon as the temperature (entrained ammonium nitrate) has been collected on the filter by 8 to 11 C. from the initial sublimation temperature. After the end of the experiment, it came out. has increased. the ύ \ <· smoke particler. with 100 ml of white water from the filter
Die I rlindiiM|2 kann auf übliche direkte Tmcknungs- gcwast 'ien. Die Ammnniakkon/entraiion (aus dem ¥ verfahren angewandt werden, die in lu'rkömnill· hen 55 R.hkIii in diesem Waschwasscr wurde col ■ etrischThe I rlindiiM | 2 can be gcwasted on the usual direct Tmcknungs-. The Ammnniakkon / entraiion (from the ¥ procedure applied, which in lu'rkömnill ·hen 55 R.hkIii in this washing watercr became col etrical
,| Anlagen zur Verarbeitung von Aiifschlämmiingen oder unter Verwendung von Ncsslers Reagens gt· -3cn. Die, | Plants for processing ash slurry or using Ncssler's reagent> 3 cn. the
feuchten Feststoffen durchgeführt werden, Sie kann K.onzentratiort an Ammoniumnitrat in der .Vaschlö-wet solids, it can be concentrated in ammonium nitrate in the.
II sowohl in kontinuierlich wie diskontinuierlich arbei· sung des Filters wurde aus der gemessenen Ammo-,! tendon Trocknern, ζ, U. in Hoidcntrockncrn, pneu- ttiakkonzentration berechnet, I I in both continuous and discontinuous operation of the filter was determined from the measured ammo ,! tendon dryers, ζ, U. in Hoidcntrockncrn, pneumatic concentration calculated,
\ matischen Trocknern. Trommeltrockncrn und mit 60 Das obige Verfahren wurde unter Verwendung ver- \ matic dryers. Drum dryer and with 60 The above procedure was carried out using
i; Wirbelschicht arbeitenden Trocknern durchgeführt scliiedener Trockentcmperaturcrt und sowohl mit wiei ; Fluidized bed dryers carried out different drying temperatures and both with how
'. werden, Sie kann ferner ungewandt werden in Ztisam* auch ohne Ammoniakinjektion in den heißen Lufi-'. It can also be used in Ztisam * without ammonia injection into the hot air.
mcnhang mit Verfahren zum Abkühlen von Ammo- strom durchgeführt. Die Ergebnisse dieser Versuchecarried out in conjunction with methods for cooling ammo-current. The results of these experiments
; itiiimnilrat. beispielsweise in einem Kühlturm, in sind in der Zeichnung wiedergegeben, in der Gramm; itiiimnilrat. for example in a cooling tower, in are shown in the drawing in grams
,; welchem ein Ciasstrom /um Abkühlen der herabfallen* 65 Rauchpartikeln pro cbm Auatrittsgas gegen die Tem·,; which a cias current / to cool down the falling * 65 smoke particles per cbm of gas against the temperature
! den Tropfen aus geschmolzenem Ammoniumnitrat vcr- peratuf des Ammoniumnitrats aufgezeichnet sind, ! the droplets of molten ammonium nitrate are recorded against the peratuf of the ammonium nitrate ,
|. wendet wird. Die gewünschte Ammoniakmenge wird Wie aus der Zeichnung ersichtlich, wurde die Rauch-|. is turned. The desired amount of ammonia is As can be seen from the drawing, the smoke
ife«i Inerijiasslrom zugegeben, ehe das Gas mit dem bildung bei einer Amtncniumnitrattcmrjeriilur vonife «i Inerijiasslrom added before the gas with the formation with an officialniumnitrattcmrjeriilur of
■ f twft 137"C durch Zugabe von 0,29n/0 Ammonisik zur Luft; um etwa 75 f'/q herabgesetzt,'■ f twft 137 "C by adding 0.29 n / 0 ammonia to the air; reduced by about 75 f '/ q,'
; Ein Arnrnoniumnitratsulfat-Düngemittel wurde in einer Versuchsaningc mit einer LuFteintrittstempcrfttur; An ammonium nitrate sulfate fertilizer was used in a trial run with an air inlet temperature
1 von 22?c C und einer Feststoffaustrittstemperfitur von 1040C sowie mit einer Luftgeschwindigkeitvon21.,5cbm pro Minute zu Kugelchen verarbeitet. Ohne Ammoniakzugabc zur Eintrittsluft bildete sich im austretenden Gas ein schwerer Rauch, Die Menge an Rauchbestandteilen wurde durch Zugabe von 0,076 Volumprozent Ammoniak zur Eintrittsluft um 80 bis 9O°/o herabgesetzt, 1 of 22? c C and a solids outlet temperature of 104 0 C as well as an air speed of 21.5 cbm per minute processed into spheres. Without ammonia being added to the inlet air, a heavy smoke formed in the exiting gas. The amount of smoke constituents was reduced by 80 to 90% by adding 0.076 percent by volume of ammonia to the inlet air,
In einem Wirbelschichttrockner wurde ein feuchter, handelsüblicher Nitrophosphatdünger getrocknet. Bei einer Austrittstemperatur des Dün£,;rs von 100° C zeigten sich Spuren von sichtbarem Rauch. Hingegen trat bei einer Austrittstemperatur des Düngers von 117°C eine mittlere Rauchbildung und bei einer Austritts-A moist, commercially available nitrophosphate fertilizer was dried in a fluidized bed dryer. at an outlet temperature of the thin layer of 100 ° C traces of visible smoke. On the other hand, there was an exit temperature of the fertilizer of 117 ° C medium smoke formation and with an exit
temperatur von 1340C eine starke RmirliWidnng tuif. J3ei d,cr letztgenannten Temperatur wurden 0,5 Volum» prozent Ammoniak der EirUrUtsHift zugegeben, und eins Rauchen hörte innerhalb 5 Sekunden auf, Rann -5 wurde die Ammoniakzufuhr wieder abgestellt, und die Rauchbildung trat nach 20 Sekunden wieder oin.temperature of 134 0 C a strong RmirliWidnng tuif. At the last-mentioned temperature, 0.5 percent by volume of ammonia was added to the EirUtsHift, and smoking stopped within 5 seconds, the ammonia supply was switched off again after 20 seconds, and the smoke began to form again after 20 seconds.
Claims (3)
Family
ID=