DE1597867B1 - ELECTROPHOTOGRAPHIC PLATE - Google Patents

ELECTROPHOTOGRAPHIC PLATE

Info

Publication number
DE1597867B1
DE1597867B1 DE19671597867 DE1597867A DE1597867B1 DE 1597867 B1 DE1597867 B1 DE 1597867B1 DE 19671597867 DE19671597867 DE 19671597867 DE 1597867 A DE1597867 A DE 1597867A DE 1597867 B1 DE1597867 B1 DE 1597867B1
Authority
DE
Germany
Prior art keywords
citric acid
photoconductive
plate
layer
zno
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19671597867
Other languages
German (de)
Inventor
Tatsuo Aizawa
Akira Takatsu
Yasuo Ueda
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kyocera Mita Industrial Co Ltd
Original Assignee
Mita Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mita Industrial Co Ltd filed Critical Mita Industrial Co Ltd
Publication of DE1597867B1 publication Critical patent/DE1597867B1/en
Pending legal-status Critical Current

Description

i 597 867i 597 867

3 43 4

Belichtung) in 3 bis 5 Minuten nach der Belichtung Beisüiel IIExposure) in 3 to 5 minutes after exposure Example II

erholen kann, läßt sich die elektrophotographischecan recover, can be the electrophotographic

Platte sofort zur Herstellung von Reproduktionen Mikrokristallines Zinkoxyd 10 gImmediate plate for making reproductions Microcrystalline zinc oxide 10 g

nach dem elektrostatischen Druckprozeß verwenden. Zitronensäure 2 guse after the electrostatic printing process. Citric acid 2 g

Die elektrophotographische Platte gemäß der Erfin- 5 Wasser 25 gThe electrophotographic plate according to the invention is 5 water 25 g

dung erholt sich von dem Gedächtniseffekt der Be- .dung recovers from the memory effect of loading.

strahlung mit Licht in 3 bis 5 Minuten, wenn man sie Β e ι s ρ ι e 1 111Radiation with light in 3 to 5 minutes if you Β e ι s ρ ι e 1 111

für diese Zeitspanne im Dunkeln hält. Danach kann Mikrokristallines Zinkoxyd 10 gkeeps in the dark for this period of time. After that, microcrystalline zinc oxide can add 10 g

die elektrophotographische Platte einem Lichtmuster Zitronensäure 2 gthe electrophotographic plate to a light pattern citric acid 2 g

ausgesetzt werden, wozu übliche photographische io Wasser 5 gare exposed, including conventional photographic io water 5 g

Mittel, einschließlich der Berührung mit einem Äthylalkohol 20 gMeans, including contact with an ethyl alcohol 20 g

Negativ oder der Projektion eines Bildes auf dieNegative or projecting an image onto the

elektrophotographische Platte dienen, und das Latent- Es ist offenbar, daß die Überzugsmischung jedesserve electrophotographic plate, and the latent It is evident that the coating mixture each

bild, welches so erzeugt worden ist, kann in der Beispiels in gleichmäßiger Überzugsdicke auf die üblichen Weise der Elektrophotographie entwickelt 15 Unterlage aufgebracht wird, wodurch elektrophotowerden. Die erfindungsgemäße elektrophotographische graphische Platten hergestellt werden, die Überzüge Platte ist besonders vorteilhaft für die ladungslose mit ausreichender Dicke, wie z. B. 5 μ, aufweisen, um elektrostatische Druckmethode, da das Bild ohne das ein befriedegendes Bild zu erzeugen.
Erfordernis der Ladung der elektrophotographischen Die entwickleten Bilder können entsprechend denImage, which has been produced in this way, can be applied in the example in a uniform coating thickness developed in the usual manner of electrophotography, whereby the substrate is electrophotographed. The electrophotographic graphic plates according to the invention are produced, the coatings plate is particularly advantageous for the non-charged with sufficient thickness, such as. B. 5 μ, have to electrostatic printing method, since the image without producing a satisfactory image.
Electrophotographic Charge Requirement The developed images can be processed according to the

Platte erzeugt werden kann. Das Farbmittel kann 20 elektrostatischen Druckverfahren unter Anwendung geladen werden, bevor es in Berührung mit dem Latent- einer Aufladungsbehandlung hergestellt werden, doch bild kommt, welches durch Belichtung auf der photo- die Aufladung kann auch völlig unterbleiben. Das graphischen Platte hergestellt ist, und dieses sollte entwickelte Bild entsprechend Beispiel II ist klarer innerhalb von 3 Minuten geschehen, bevor sich die als das Bild entsprechend Beispiel I5 und das Bild elektrophotographische Platte von dem Gedächtnis- 25 entsprechend Beispiel III ist klarer als das gemäß effekt erholen kann. Beispiel II hergestellte Bild.Plate can be generated. The colorant can be charged using electrostatic printing processes before it is made into contact with the latent charging treatment, but the image that comes through exposure on the photographic charging can also be omitted entirely. The graphic plate is made, and this developed image according to Example II should be done more clearly within 3 minutes, before the image according to Example I 5 and the image of the electrophotographic plate of the memory plate according to Example III is clearer than that according to effect can recover. Example II produced image.

Die elektrophotographische Platte gemäß der Erfin- Die Ergebnisse zeigen, daß das entwickelte BildThe electrophotographic plate according to the invention. The results show that the developed image

dung macht es möglich, sichtbare Bilder mit mehr klarer wird, wenn die Menge der Zitronensäure steigt Schärfe, Glanz und Fläche darauf herzustellen, als und daß das Bild durch Zugabe eines organischen bisher erzielbar war, wenn ein besonderes Harzbinde- 30 Lösungsmittels noch klarer wird. Es zeigt sich durch mittel verwendet wurde, und es läßt sich damit ein weitere Versuche, daß das entwickelte Bild schlechter klar sichtbares Bild nach dem ladungslosen elektro- ausfällt, wenn die Zitronensäure in einer Menge oberstatischen Druckverfahren herstellen. halb von 20 °/o der Menge des Zinkoxyds oder in einer Ein organisches Lösungsmittel (z. B. Äthylalkohol) Menge unterhalb von 10 % der Menge des Zinkoxyds in Mischung mit Wasser kann außer Zitronensäure 35 verwendet wird.dung makes it possible to view images with more clarity when the amount of citric acid increases Produce sharpness, gloss and surface on it than and that the picture by adding an organic was previously achievable when a special resin binder 30 is even clearer. It shows through medium was used, and it can be used to make further attempts that the developed image is worse Clearly visible image after the no-charge electro-fail when the citric acid in a lot of top-static printing processes produce. half of 20 per cent of the amount of zinc oxide or in one An organic solvent (e.g. ethyl alcohol) less than 10% of the amount of zinc oxide In addition to citric acid 35, it can be mixed with water.

und Wasser photoleitfähigem Zinkoxyd zugesetzt So sieht man, daß die auf einer Unterlage aufge-and water added to photoconductive zinc oxide.

werden, um die Zwecke der Erfindung zu erfüllen, brachte Überzugszusammensetzung und die damit wodurch die Mahlzeit, die erforderlich ist, um alle hergestellte elektrophotographische Platte ohne ein Bestandteile ausreichend zu mischen, reduziert wird, besonderes Harzbindemittel einfach ist und ein und die Mischung mit Alkohol kann leichter auf die 4° wirtschaftliches Produkt darstellt.
Unterlageplatte aufgebracht werden, unabhängig da- Das auf der elektrophotographischen Platte gemäßIn order to achieve the purposes of the invention, coating composition and the like, thereby reducing the meal required to mix any manufactured electrophotographic plate sufficiently without a component, particular resin binder is simple and one can and can mix with alcohol easier to represent the 4 ° economical product.
Backing plate can be applied regardless of that on the electrophotographic plate according to

von, ob die Unterlageplatte aus Kunstdruckpapier der Erfindung entwickelte Bild besitzt mehr KUarheit oder anderen geeigneten Materialien besteht. und Definiertheit, als mit bekannten elektrophoto-of whether the backing plate developed from art paper of the invention possesses more clarity or other suitable materials. and definition, as with known electrophoto-

Folgende Beispiele sollen zur näheren Erläuterung graphischen Platten erzeilbar war, und die elektroder Erfindung dienen: 45 photographische Platte gemäß der Erfindung läßt . -/τ sich ™ ladungslosen elektrostatischen Druckverfahren Beispiel 1 verwenden, wodurch dieses vereinfacht wird und dieThe following examples are intended to provide a more detailed explanation of graphic plates and the electroder Invention serve: 45 photographic plate according to the invention. - / τ sich ™ uncharged electrostatic printing process Use example 1, which simplifies this and the

Mikrokristallines Zinkoxyd 10 g Kosten der Bürokopiermaschinen reduziert werden,Microcrystalline zinc oxide 10 g cost of office copier machines can be reduced,

Zitronensäure Ig wo unerfahrenes Personal Kopien großer KlarheitCitric acid Ig where inexperienced staff copies of great clarity

Wasser 20 g 50 herstellen soll.Water should produce 20 g 50.

Claims (2)

1 2 graphische Platte offenbart werden, bei der kein Harz- p .. , bindemittel benötigt wird. Dabei soll die elektro- -Fatentansprucne: photographische Platte gemäß der Erfindung zum : " . ladungslosen elektrostatischen Drucken geeignet sein.1 2 graphic plate are disclosed in which no resin p .., binder is required. The electro-patent claims: photographic plate according to the invention should be suitable for: ". Charge-free electrostatic printing. 1. Elektrophotographische Platte aus einem 5 Gegenstand der Erfindung, womit diese Aufgabe Schichtträger und einer ZnO, ein Reaktionsprodukt gelöst wird, ist eine elektrophotographische Platte aus aus ZnO und Zitronensäure und Zitronensäure einem Schichtträger und einer ZnO, ein Reaktionsenthaltenden photoleitf ähigen Schicht, dadurch produkt aus ZnO und Zitronensäure und Zitronensäure gekennzeichnet, daß die photoleitfähige enthaltenden photoleitf ähigen Schicht mit dem Kenn-Schichi Zitronensäure als einziges Bindemittel io zeichen, daß die photoleitfähige Schicht Zitronensäure enthält. . ........ . als einziges Bindemittel enthält.1. Electrophotographic plate from a 5 object of the invention, this object A substrate and a ZnO, a reaction product, is made up of an electrophotographic plate of ZnO and citric acid and citric acid on a support and a ZnO, a reaction-containing one photoconductive layer, thus a product of ZnO and citric acid and citric acid characterized in that the photoconductive containing photoconductive layer with the identification layer Citric acid as the only binder io sign that the photoconductive layer is citric acid contains. . ......... contains as the only binding agent. 2. Platte nach Anspruch 1, dadurch gekenn- . Es wurde' nämlich gefunden, daß die photoleitende zeichnet, daß die Schicht'auf 10 GWichtsteile Schicht am Schichtträger infolge einer exothermen ZnO 1 bis 2 Gewichtsteile Zitronensäure enthält. Reaktion zwischen der als Ausgangsstoff verwendeten2. Plate according to claim 1, characterized. Namely, it has been found that the photoconductive shows that the layer on 10 parts by weight of the layer on the substrate as a result of an exothermic ZnO contains 1 to 2 parts by weight of citric acid. Reaction between the used as starting material 15 Zitronensäure und einem Teil des als Ausgangsstoff15 citric acid and part of the raw material verwendeten Zinkoxyds ohne Verwendung einesused zinc oxide without using a ______ besonderen Bindemittels, insbesondere ohne Ver-______ special binding agent, especially without ■ Wendung des bisher üblichen Harzbindemittels, festhaftet. Ein weiterer Vorteil der Erfindung besteht ao darin, daß das erfindungsgemäß zusammengesetzte■ Reversal of the previously customary resin binder, firmly adhered. Another advantage of the invention is that the composite according to the invention Die Erfindung betrifft das elektrostatische Drucken Material nach der Bestrahlung mit Licht erheblich und bezieht sich auf eine dazu erforderliche elektro- kürzere Oberflächenpotentialverringerungszeiten als photographische Platte aus einem Schichtträger und das bekannte Material mit Harzbindemittel aufweist einer ZnO, ein Reaktionsprodukt aus ZnO und und dem bekannten Material daher auch hinsichtlich Zitronensäure und Zitronensäure enthaltenden photo- 25 der Druckbildqualität überlegen ist. leitfähigen Schicht. Insbesondere bezieht sich die Vorzugsweise enthält die photoleitfähige SchichtThe invention relates significantly to electrostatic printing material after exposure to light and relates to a required electro- shorter surface potential reduction times than photographic plate comprising a support and the known material with resin binder a ZnO, a reaction product of ZnO and and the known material therefore also with regard to Photo- 25 containing citric acid and citric acid is superior in image quality. conductive layer. In particular, it relates to preferably contains the photoconductive layer Erfindung auf die Zusammensetzung der photoleit- auf 10 Gewichtsteile Zinkoxyd 1 bis 2 Gewichtsteile fähigen Schicht, deren Schichtträger aus Kunstdruck- Zitronensäure, um die optimalen Bildqualitäten bei papier ode- anderem passenden Unterlagematerial damit hergestellten Aufnahmen zu erzielen, besteht. 30 Eine solche elektrophotographische Platte läßt sichInvention on the composition of the photoconductive to 10 parts by weight of zinc oxide 1 to 2 parts by weight capable layer, the substrate of which is made of art print citric acid, to ensure the optimal image quality paper or other suitable supporting material to achieve recordings made with it, consists. 30 Such an electrophotographic plate can be Ein bekanntes Verfahren zur Herstellung von elek- derart herstellen, daß man photoleitfähiges ZnO und trophotographischen Platten besteht aus dem Mischen Zitronensäure in einem wäßrigen Medium in solchen eines photoleitfähigen Materials mit einem elektrisch Mengenanteilen mischt, daß ein Teil des ZnO unreaisolierenden plattenbildenden Trägermaterial und giert bleibt und sich eine viskose Trübe bildet, daß einem flüchtigen organischen Lösungsmittel, z. B. 35 man diese Trübe ohne Verwendung eines Bindemittelaus dem Mischen von Zinkoxyd und einem Silikonharz harzes auf eine Unterlage aufbringt und daß man den mit Toluol, wodurch eine Form von photoleitfähigem Überzug auf der Unterlage trocknet. Medium hergestellt wird, welches schon von RCA Dabei können die Zitronensäure und Wasser demA known method for the production of elek- produce such that photoconductive ZnO and The trophotographic plate consists of mixing citric acid in an aqueous medium in such of a photoconductive material mixed with an electrical proportions that a portion of the ZnO is nonreactive plate-forming carrier material and remains and a viscous cloud forms that a volatile organic solvent, e.g. B. 35 this pulp without using a binder the mixing of zinc oxide and a silicone resin resin is applied to a base and that the with toluene, which dries some form of photoconductive coating on the base. Medium is produced, which is already from RCA. Citric acid and water can dem Amerika entwickelt wurde. Das Silikonharzbindemittel photoleitfähigen Material aus mikrokristallinem Zinkwird verwendet, um eine photoleitfähige Überzugs- 4° oxyd zugesetzt werden, oder die Zitronensäure kann schicht festklebend mit einer Schichtträgerplatte zu zu dem mikrokristallinen, in Wasser dispergierten verbinden und um Elektronen, die durch Korona- Zinkoxyd zugesetzt werden, oder das Wasser kann entladung ausgestrahlt wurden, festzuhalten. einer Mischung aus mikrokristallinem Zinkoxyd undAmerica was developed. The silicone resin binder becomes microcrystalline zinc photoconductive material used to add a photoconductive coating 4 ° oxide, or the citric acid can be added layer firmly adhering to a layer support plate to the microcrystalline, dispersed in water connect and around electrons, which are added by corona zinc oxide, or the water can discharge were broadcast. a mixture of microcrystalline zinc oxide and Die Verwendung eines flüchtigen organischen Lö- Zitronensäure zugesetzt werden. Auch kann die sungsmittels für den Träger hat indessen einige Nach- 45 Zitronensäure im Wasser gelöst und dem mikroteile, insbesondere die, daß das Lösungsmittel teuer . kristallinen Zinkoxyd zugesetzt werden, und daher unwirtschaftlich ist und die meisten organi- Es wurde auch gefunden, daß die photoleitfähigeThe use of a volatile organic lo- citric acid can be added. Can also The solvent for the carrier has, however, dissolved some post-45 citric acid in the water and especially the one that the solvent is expensive. crystalline zinc oxide is added, and therefore uneconomical and most organic. It has also been found that the photoconductive sehen Lösungsmittel entflammbar und giftig sind, Überzugsschicht aus Zinkoxyd, Zitronensäure und wodurch Unfälle beim Betriebspersonal auftreten Wasser durch weiteren Zusatz eines mit Wasser mischkönnen. Selbst wenn Wasser als Trägermaterial ver- 50 baren organischen Lösungsmittels, insbesondere von wendet wird, ist noch das Harzbindemittel verhält- Äthylalkohol und Verwendung einer geringen Wassernismäßig teuer. menge in der Mischung noch stärker an der Unter-see solvents which are flammable and toxic, coating layer made of zinc oxide, citric acid and whereby accidents occur with the operating personnel. Water can be mixed with water by adding another one. Even if water is available as a carrier material, in particular from organic solvents is used, the resin binder is still behaving in terms of ethyl alcohol and using a low amount of water expensive. amount in the mixture is even more dependent on the Außerdem ist aus der britischen Patentschrift lageplatte haftet.In addition, from the British patent ply plate is liable. 1020 506 eine elektrophotographische .Platte aus Die exotherme Reaktion zwischen Zitronensäure1020 506 an electrophotographic plate from The Exothermic Reaction Between Citric Acid einem Schichtträger untl einer ZnO-Teilche'n und ein 55 und Zinkoxyd hat die Eigenart, zu bewirken, daß die Reaktionsprodukt aus ZnO und einer aliphatischen Überzugsschicht fest auf der Unterlageplatte haftet, Polykarbonsäureverbindung, z. B. Zitronensäure ent- ohne daß ein zusätzliches Bindemittel erforderlich ist. haltenden photoleitfähigen Schicht bekannt. Auch Durch Versuche zeigte sich, daß sich eine ent-a layer support and a ZnO particle and a 55 and zinc oxide has the peculiarity of causing the Reaction product of ZnO and an aliphatic coating layer firmly adheres to the base plate, Polycarboxylic acid compound, e.g. B. Citric acid without an additional binder is required. holding photoconductive layer known. Experiments have also shown that a de- hierbei wird ein Harzbindemittel verwendet, das einen sprechend der Erfindung hergestellte elektrophotoweiteren Bestandteil des Überzugs bildet, so daß auch 60 graphische Platte von dem Gedächtniseffekt in 3 bis in diesem Fall ein entsprechend hoher Kostenaufwand 5 Minuten nach der Belichtung erholen kann. Die vorliegt. photographische Platte gemäß der Erfindung solltehere, a resin binder is used which is an electrophotographic one made according to the invention Forms part of the coating, so that also 60 graphic plates of the memory effect in FIGS in this case a correspondingly high cost can recover 5 minutes after exposure. the is present. photographic plate according to the invention should Der Erfindung liegt die Aufgabe zugrunde, diese innerhalb von 3 Minuten entwickelt werden, um mit-Nachteile und Schwierigkeiten zu überwinden und tels des üblichen Farbstoffs, der in der elektrophotoeine verbesserte elektrophotographische Platte zu 65 graphischen Reproduktion verwendet wird, ein sichtschaffen, welche wirtschaftlich ist und mit einem bares Bild zu erzeugen. Da Versuche zeigten, daß sich Minimum an Aufwand gefertigt werden kann. Vor die elektrophotographische Platte vom Gedächtnisallem soll durch die Erfindung eine elektrophoto- effekt (dem Strahlungseffekt, hervorgerufen durchThe invention is based on the task of developing this within 3 minutes in order to deal with disadvantages and difficulties to be overcome and by means of the usual dye found in the electrophotoeine improved electrophotographic plate used for 65 graphic reproduction, a visual creation, which is economical and can be produced with a real image. Since experiments showed that Can be manufactured with a minimum of effort. Before the electrophotographic plate of memory everything is intended by the invention an electrophoto effect (the radiation effect, caused by
DE19671597867 1966-11-26 1967-11-24 ELECTROPHOTOGRAPHIC PLATE Pending DE1597867B1 (en)