DE1494508A1 - Coating compound that can be sealed by the action of heat - Google Patents
Coating compound that can be sealed by the action of heatInfo
- Publication number
- DE1494508A1 DE1494508A1 DE19641494508 DE1494508A DE1494508A1 DE 1494508 A1 DE1494508 A1 DE 1494508A1 DE 19641494508 DE19641494508 DE 19641494508 DE 1494508 A DE1494508 A DE 1494508A DE 1494508 A1 DE1494508 A1 DE 1494508A1
- Authority
- DE
- Germany
- Prior art keywords
- component
- heat
- coating composition
- composition according
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
E S * A HOBINSOH (HOLDINGS) UNITED 1 1 Redcliffe Street, \ IT * A HOBINSOH (HOLDINGS) UNITED 1 1 Redcliffe Street, \
Bristol 1 / England 27.5.1964 Bristol 1 / England May 27, 1964
Dr. Expl.Dr. Expl.
Die Erfindung betrifft durch Hitzewirkung vereiegelbare Überzugsmasse für Trägerstoffe aus Papier, Pappe, für Filme, folien, lamellenartige und mit einer Auflage versehene Stoffe, die einen festen, durch Hitzewirkung versiegelten Verschluß von geringer Kohäsionskraft ermöglichen, der durch Ablösen leioht geöffnet werden kann· % Der Überzug kann auch auf Verpackungselemente von starrer ί oder halbstarrer Beschaffenheit, z.B. auf termisch-geformte Behälter aufgebracht werden·The invention relates to heat effect vereiegelbare coating composition for carrier materials of paper, cardboard, for films, sheets, lamellar and is provided with a support substances which make a firm, sealed by heat effect closure of low cohesive force, which can be opened leioht by peeling ·% The Coating can also be applied to packaging elements of a rigid ί or semi-rigid nature, e.g. on thermally formed containers.
Gemäß der Erfindung besteht der unter Hitzewirkung versiegelbare Überzug aus einer Mischung von mindestens zwei Komponenten, von denen die eine Komponente ein unter Hitzewirkung versiegelbarer synthetischer Harz ist, der an dem Trägermaterial anklebt, während die andere Komponente eine organische Substanz ist, welche die Kohäsions- oder Adhäsionskraft der erstgenannten Komponente herabsetzt und dadurch die Ablösbarkeit ermöglicht. Vorzugsweise , besteht die erste Komponente aus einem Polymer oder ; Copolymer. Die zweite Komponente kann ebenfalls unter Hitzewirkung versiegelbar .sein.According to the invention, the heat-sealable coating consists of a mixture of at least two components, one component of which is a heat sealable synthetic resin, the adheres to the carrier material, while the other component is an organic substance, which the cohesive or Reduces the adhesive force of the first-mentioned component and thereby enables it to be removed. Preferably, the first component consists of a polymer or; Copolymer. The second component can also be found under Heat-sealable.
Die erste Komponente kann ein Copolymer aus A'thylen- und Vinylacetat sein, während die zweite Komponente Polystyrol oder Acrylnitril-Butadien-Copolymer oder chloriertes Polyvinylchlorid ist. Die Erfindung schließt auch blatt- oder strangförmige Stoffe ein, die mit der Überzugsmasse beschichtet sind, sowie daraus hergestellte Beutel und Verpackungen.The first component can be a copolymer of ethylene and vinyl acetate, while the second component can be polystyrene or acrylonitrile-butadiene copolymer or is chlorinated polyvinyl chloride. The invention also includes sheet or string-shaped materials with the Coating mass are coated, as well as bags and packaging made therefrom.
909849/1456909849/1456
18 215 - 2 - 18 215 - 2 -
_2_ U94508_ 2 _ U94508
Die beiden genannten Komponenten lassen sich der nachstehend aufgeführten Liste entnehmen mit der Maßgabe, daß die zweite Komponente die Adhäsions- oder Kohäsionskraft der ersten Komponente verringert und somit einen Oberzug bildet, der ablösbar ist.The two components mentioned can be found in the list below with the proviso that that the second component is the force of adhesion or cohesion the first component is reduced and thus forms a cover that can be removed.
Äthylen-ZVinylacetat-Copolymer, beispielsweise Elvax 220 oderEthylene-vinyl acetate copolymer, for example Elvax 220 or
Elvax 260.Elvax 260.
Polystyrol, beispielsweise Lustre* G-PHS. Polyamid, beispielsweise Versamid 950· Polymethyl-Methacrylat, beispielsweise Diakon LG oderPolystyrene, for example Luster * G-PHS. Polyamide, for example Versamid 950 · Polymethyl methacrylate, for example Diakon LG or
Diakon MG.Deacon MG.
Polyteippene, beispielsweise Piccolyte 155, BX.85 oder BX.115.Polyteippene, for example Piccolyte 155, BX.85 or BX.115.
Polyester, beispielsweise Titel PE.200.Polyester, for example title PE.200.
Polyvinylacetat, beispielsweise Mowilith 30 oder Mowilith 40.Polyvinyl acetate, for example Mowilith 30 or Mowilith 40.
Copolymer aus Vinylchlorid und -acetat, beispielsweiseCopolymer of vinyl chloride and acetate, for example
Hostalit M. 131.Hostalit M. 131.
Polyvinylydenchlorid, beispielsweise Saran P.220.Polyvinylydene chloride, for example Saran P.220.
Polyvinylbutyral, beispielsweise Mowital B.3OH, Mowital B.3OTPolyvinyl butyral, for example Mowital B.3OH, Mowital B.3OT
oder Mowital B.6OT.or Mowital B.6OT.
Chloriertes Polyvinylchlorid, beispielsweise Rhenoflei 408 oderChlorinated polyvinyl chloride, for example Rhenoflei 408 or
Genclor S.Genclor S.
Chlorsulfoniertes Polyäthylen, beispielsweise Hypalon 40.Chlorosulfonated polyethylene, e.g. Hypalon 40.
Polychloropren, beispielsweise Neopren W.Polychloroprene, for example neoprene W.
Chloriertes Paraffin, beispielsweise Chloroparaffin 70.Chlorinated paraffin, for example chloroparaffin 70.
- 3 909849/U56 - 3 909849 / U56
Chlorkautschuk» beispielsweise Allpprene B. Polypropylen (amorph), beiepieleweiee Oletao 100· Butadien-Aorylnitril-Oopolymer,belepieleweiee Butakon A.4051· Butadien-etyrol-Copolymer, beiepieleweiee Butakon 8.8551.Chlorinated rubber »for example Allpprene B. Polypropylene (amorphous), for example Oletao 100 · Butadiene-Aorylnitril-Oopolymer, Belepieleweiee Butakon A.4051 · Butadiene-etyrene copolymer, e.g. Butakon 8.8551.
Acrylnitril-Butadien-Styrol-Copolymer, beiepieleweiee Cycolao AK, Oyoolao f oder Oyoolac 17.Acrylonitrile-butadiene-styrene copolymer, for example Cycolao AK, Oyoolao f or Oyoolac 17.
8tyrol-0opolymer» beiepieleweiee Pioootez 100 oder Picootez 12a8tyrene-0opolymer »for example Pioootez 100 or Picootez 12a
Piooopale 100·Piooopale 100
Polymer aue eynthetieohem Alkyd und aromatteehern Kohlenwaeeerstoff (Synthetic alkyd Aromatiο Hydrocarbon polymer), beiepieleweiee Inkorar 146.Polymer aue eynthetieohem alkyd and aromatic tehern carbon (Synthetic alkyd Aromatiο hydrocarbon polymer), for example Inkorar 146.
Äthylselluloee, beiapieleweise Ithyl Celluloee H.7. Zelluloeeaoetat-Butyraty beiepieleweiee 1/2-Sek. Butyrat. Oumaron-Inden-Har«, beiepleleweiee Bpok 0.469· Aoryleulfonamid/Formaldehydhars» beiepieleweiee Santolyte MHP. Nichto?cydierender Alkydharz» beiepieleweiee Cellolyn 102. Epoxyharz, beiepieleweiee Araldite AT.1.Ethyl cellulose, for example Ithyl cellulose H.7. Cellulose acetate butyrate for example 1/2 sec. Butyrate. Oumaron-Inden-Har ", beiepleleweiee Bpok 0.469 · Aoryleulfonamide / formaldehyde hares »beiepieleweiee Santolyte MHP. Non-oxidizing alkyd resin »for example Cellolyn 102. Epoxy resin such as Araldite AT.1.
Phenoxyharz, beispielsweise Phenoxy PKDA.8500 oder PBDA 8080. Pliolitharz, beispieleweise Pllolite HBP.1230.Phenoxy resin, for example phenoxy PKDA.8500 or PBDA 8080. Pliolite resin, for example Pllolite HBP.1230.
Das Gewicht dee aufgebrachten Oberzugs sollte als Trockengewicht nicht weniger ale 0»04 g/m betragen·The dry weight of the applied top layer should not be less than 0-04 g / m ·
9Ö9S49/US69Ö9S49 / US6
■ - 4 *- '■■'.■■ - 4 * - '■■'. ■
H94508H94508
Sie nachstehenden Beispiele sind das Ergebnis von Versuchen, die mit den in der obigen Liste aufgeführten Komponenten bei bestimmten Trägerstoffen und bestimmten Siegeltemperaturen durchgeführt wurden· Pur andere Trägerstoffe sind selbstverständlich andere !Temperaturen anzuwenden·The examples below are the result of attempts those with the components listed in the above list for certain carriers and certain sealing temperatures other carriers are of course different! Temperatures to be used
In allen fällen sind die beiden Komponenten in gleichen Anteilen verwendet worden· Selbstverständlich können die Anteile entsprechend den jeweiligen Bedingungen variert werden· Wenn ein Weichmacher zugegeben wird, ändern sich die Anteile der beiden Komponenten entsprechend·In all cases the two components are the same Shares have been used · Of course, the shares can be changed according to the respective conditions If a plasticizer is added, the proportions of the two components change accordingly
1) Anwendung bei einem mit einem Polypropylen-Überzug versehenen gebleichten Fackpapier, yersiegelungstemperatur etwa 176.6 C. 1) Use with a bleached flare paper with a polypropylene coating, sealing temperature approx. 176.6 C.
Elvax 220 + Diakon MG.Elvax 220 + Deacon MG.
" Ethyl Cellulose H.7. " 1/2-second Butyrate."Ethyl Cellulose H.7." 1/2-second Butyrate.
2) Anwendung bei einem Folyäthylen-JFilm,2) application to a polyethylene film,
150-250 Stärke (gauge),Versiegelungetemperatür etwa 115.5° C. 150-250 gauge, sealing temperature about 115.5 ° C.
Elvax 220 + Versamid 950· N Saran P.220.
M Piccodiene.
* Epok C.469·Elvax 220 + Versamid 950 N Saran P.220.
M Piccodiene.
* Epok C.469
3) Anwendung bei Pergamin, Versiegelungetemperatur etwa 93.3° C. 3) Use with glassine, sealing temperature about 93.3 ° C.
Elvax 220 + Alloprene B.
« Hostalit M131. " Mowital B.3OH.
" Phenoxy PKDA 8500· " Phenoxy PBDA 8080.Elvax 220 + Alloprene B.
«Hostalit M131. "Mowital B.3OH." Phenoxy PKDA 8500 • "Phenoxy PBDA 8080.
- 5 909849/U56 - 5 909849 / U56
4) Anwendung bei einem mit einem Polyäthylen-Oberzug versehenen gebleichten Packpapier, Yersiegelungstemperatur etwa 93.3 bis 115«5 4) Use with a bleached wrapping paper with a polyethylene cover, sealing temperature about 93.3 to 115-5
/ Elvax 220 + Diakon MG./ Elvax 220 + Deacon MG.
/ " Diakon LG./ "Deacon LG.
/ n Hypalon 40·/ n Hypalon 40
/ w Polyterpene BX.85·/ w polyterpenes BX.85
/ " i/2-eeoond Butyrate./ "i / 2-eeoond Butyrate.
/ » Vitel PB200./ »Vitel PB200.
Φ » Bhenoflex 408. Φ »Bhenoflex 408.
/ n / n ßenclor S.ßenclor S.
«« Butakon A4O51Butakon A4O51
/ w Hostalit M131./ w Hostalit M131.
/ n Howital B.3OT./ n Howital B.3OT.
/ « Chloroparaffin/ «Chloroparaffin
/ " Oletac 100./ "Oletac 100.
/ " Piccopale 100·/ "Piccopale 100 ·
" Santolyte MHP."Santolyte MHP.
Φ « Oycolac ABS AH. Φ «Oycolac ABS AH.
Φ n Oyoolac ABS 17· Φ n Oyoolac ABS 17
" Pliolite HEP 1230."Pliolite HEP 1230.
/ Versiegelungstemperatur etwa 93»3° C. Φ- Versiegelungstemperatur etwa 115,5° C. / Sealing temperature about 93 »3 ° C. Φ- Sealing temperature about 115.5 ° C.
5) Anwendung bei mit Polyäthylen überzogenem Packpapier, Polyäthylen-Film oder mit Polypropylenüberzug versehenem Packpapier bei den in den obigen Beispielen angegebenen Versiegelungstemperaturen. 5) Use with polyethylene-coated wrapping paper, polyethylene film or polypropylene-coated wrapping paper at the sealing temperatures given in the above examples.
llvax 220 + Polyterpene BI 115· " Piccolyte 135. " Mowilith 30. « Mowilith 40. ' " Piccotex 100. « Picootex 120·llvax 220 + polyterpenes BI 115 "Piccolyte 135. "Mowilith 30." Mowilith 40. ' "Piccotex 100.« Picootex 120 ·
909849/U56 - 6 -909849 / U56 - 6 -
H94508H94508
S Elvax 220 + Mowital B.30-H.S Elvax 220 + Mowital B.30-H.
" Mowital B.60.T."Mowital B.60.T.
" Heoprene W."Heoprene W.
M Araldite A.T.1 M Araldite AT1
" Cellolyn 102,"Cellolyn 102,
X " Phenoxy PKDA.8500.X "Phenoxy PKDA.8500.
X n Phenoxy PEDA.8080.X n Phenoxy PEDA.8080.
n Cycolac ABS.!D. n Cycolac ABS.! D.
11 Inkoyar 146· 11 Inkoyar 146
n Epok C.469. n Epok C. 469.
auch bei Pergamin, etwa 93,3° C Versiegelungstemperatur. also with glassine, about 93.3 ° C sealing temperature.
Gemäß einer Ausführungsfora der Erfindung besteht die Oberzugsmasse aus einem Gewichteanteil eines Copolymere, welches unter dem Warenzeichen "Blrax" bekannt ist, undAccording to one embodiment of the invention, the coating composition consists of a proportion by weight of a copolymer, which is known under the trademark "Blrax", and
j einem Gewichtsanteil Polystyrol; welches in !Toluol gelöst ist.j a part by weight of polystyrene; which dissolved in toluene is.
Anstelle einer Lösung kann der Überzug auch aus einer wässrigen Dispersion oder einer heißen Schmelze bestehen·Instead of a solution, the coating can also consist of an aqueous dispersion or a hot melt
Der Überzug wird auf Polyäthylen oder auf irgendein ' lamellenartiges oder nicht lamellenartiges Verpackungs-" material als Trägerstoff mit Hilfe τοη Vorrichtungen aufgebracht, die sich für den genannten Trägerstoff und das Überzugsmittel eignen, beispielsweise mit Hilfe einer tföevtragsrolle eines geätzten Zylinders oder durch Pressen (extrusion)· Der Überzug kann die gesamte Oberfläche des Trägerstoffs bedecken oder in Form eines gedruckten Musters aufgebracht werden·The cover is on polyethylene or on some 'laminate or non-laminate wrapper " material applied as a carrier with the help of τοη devices, which are for the said carrier and the Coating agents are suitable, for example with the aid of a roller transferring an etched cylinder or by pressing (extrusion) · The coating can cover the entire surface of the substrate or in the form of a printed pattern to be applied
- 7 -90984 9/1 456 BAD 0RIGINAL - 7 -90984 9/1 456 BAD 0RIGINAL
-7- U9A508-7- U9A508
Gemäß einer anderen Ausführungeform der Erfindung enthält die überzugsmasse 45 Gewichtsanteile Aorylnitril-Butadien-Copolymer und 45 Gewichtsanteile "Elvax" sowie 10 Gewichtsanteile eines Weichmachers, beispielsweise Cyelohexyl-Benzol-Sulfonamid oder Cyclohexyl-Toluol-Sulfonamid. Die Kohäsionskraft des ablösbaren Überzugs beträgt in diesem speziellen Beispiel etwa 2g/2,54 cm·According to another embodiment of the invention, contains the coating composition 45 parts by weight of aorylnitrile-butadiene copolymer and 45 parts by weight of "Elvax" and 10 parts by weight of a plasticizer, for example cyelohexyl-benzene-sulfonamide or cyclohexyl-toluene-sulfonamide. The cohesive force of the peelable coating is in this particular example about 2g / 2.54 cm
Eine abgeänderte Überzugsmasse gemäß der Erfindung enthält 6 Gewichtsanteile chloriertes Polyvinylchlorid und einen Gewichteanteil eines Copolymers aus Vinylacetat und Äthylen·A modified coating composition according to the invention contains 6 parts by weight of chlorinated polyvinyl chloride and one Percentage by weight of a copolymer of vinyl acetate and ethylene
Der Überzug wird auf unerweichtes Polyrinylohlorld oder auf irgendein anderes Verpackungsmaterial als Trägerstoff, welches lamellenartig ausgebildet ist oder eine andere Form besitzt, mit Hilfe von Vorrichtungen aufgebracht, die für diesen Trägerstoff und die überzugsmittel geeignet sind·The coating is applied to un-softened Polyrinylohlorld or on any other packaging material as a carrier material, which is lamellar or has another shape, applied with the help of devices, which are suitable for this carrier and the coating agent
Die überzugsmasse gemäß der Erfindung ist unter Hitzeeinwirkung schmelzbar· lach Abstreifen des Überzugs kann dieser durch Erhitzen wieder versiegelt werden· Eine Verpackung, die mit der Überzugsmasse gemäß der Erfindung unter Hitzeeinwirkung versiegelt ist, kann leicht wieder geöffnet werden, indem der Überzug von der Oberfläche, auf der er anhaftet, abgeschält wird.The coating composition according to the invention is meltable under the action of heat after the coating has been stripped off this can be resealed by heating · A packaging that is coated with the coating material according to the Invention is sealed under the action of heat, can easily be opened again by removing the cover from the surface, on which it adheres, is peeled off.
Wenn zwei Trägerstoffe von gleicher oder unterschiedlicher Art mit ihren Stirnflächen gegeneinander gelegt und durch die überzugsmasse gemäß der Erfindung unter Hitzeeinwirkung miteinander verbunden werden, so lassen sich diese wieder voneinander trennen, ohne daß die genannten Stirnflächen beschädigt werden· Sie wesentliche Eigenschaft des erfindungsgemäßen Überzugs besteht daher in seiner Ablösbarkelt·When two carrier materials of the same or different types are placed with their end faces against each other and through the coating composition according to the invention under the action of heat are connected to one another, they can be separated from one another again without the aforementioned end faces The essential property of the coating according to the invention is therefore that it can be removed
909849/1456909849/1456
Claims (9)
- 9 -909849 / U56
- 9 -