DE1453867A1 - Filling for shaped charge projectiles - Google Patents

Filling for shaped charge projectiles

Info

Publication number
DE1453867A1
DE1453867A1 DE19651453867 DE1453867A DE1453867A1 DE 1453867 A1 DE1453867 A1 DE 1453867A1 DE 19651453867 DE19651453867 DE 19651453867 DE 1453867 A DE1453867 A DE 1453867A DE 1453867 A1 DE1453867 A1 DE 1453867A1
Authority
DE
Germany
Prior art keywords
alloy
shaped charge
copper
charge projectiles
zinc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19651453867
Other languages
German (de)
Inventor
Michel Precoul
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Technique de Recherches Industrielles et Mecaniques
Original Assignee
Technique de Recherches Industrielles et Mecaniques
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Technique de Recherches Industrielles et Mecaniques filed Critical Technique de Recherches Industrielles et Mecaniques
Publication of DE1453867A1 publication Critical patent/DE1453867A1/en
Pending legal-status Critical Current

Description

Akten-Nr. J^ 16 670 B/HO in der Antwort bitte angebenFile no. J ^ 16 670 B / HO please indicate in the answer

SOCIETE TECHNIQUE DE RECIIERCHEb INDUbTRIELLES ETSOCIETE TECHNIQUE DE RECIIERCHEb INDUbTRIELLES ET

MECANIQUES
S.T.R.I.M., 2, rue de Teheran, Paris, FrankreichMECANIQUES
STRIM, 2, rue de Tehran, Paris, France

"Ausfütterung für Hohlladungsgeschosse""Lining for shaped charge projectiles"

Me Erfindung "betrifft Ausfütterungen "bzw. Auskleidungen für Hohlladungsgeschosse. Sie geht von einem Stande der Technik (französische Patentschrift 1 057 294·) aus, gemäß welchem zur Ausfütterung von Hohlladungsgeschossen Zweistofflegierungen verwendet werden, welche gewisse Zusatzelemente enthalten, die es ermöglichen, Dehnungen von mehr als 4-5 Ms 50 fo und sogar bis über'60 "fi zu erzielen· Me invention "relates to linings" or Linings for shaped charge projectiles. It is based on a state of the art (French patent specification 1 057 294 ·), according to which two-material alloys are used for lining hollow charge projectiles, which contain certain additional elements that allow elongations of more than 4-5 Ms 50 fo and even up to Achieve '60 "fi ·

Es handelt sich dabei insbesondere unr Kupfer-Arsen-, Kupfer-Nickel-, Kupfer-Titan- oder Flußstahl-Titanlegierungen. Die damit erzielbaren Dehnungen liegen kaum über 60 #.These are in particular copper-arsenic, copper-nickel, copper-titanium or mild steel-titanium alloys. The elongations that can be achieved with this are barely more than 60 #.

Die Entwicklung der neuzeitlichen Panzer und die sichThe development of modern tanks and the

^9 09835/0023 "2"^ 9 09835/0023 " 2 "

H53867H53867

aus dieser Entwicklung ergebenden Voraussetzungen für ihre Bekämpfung zwingen zu einer Verbesserung der hierfür verwendeten Hohlladungsgeschosse mit dem Ziele, auf eine beträchtliche Entfernung noch eine hinreichende Durchschlagskraft für Verbundziele, - Doppel -, Dreifach- und Mehrfachpanzerungen - zu erzielen, insbesondere wenn das Durchschlagen der aufeinanderfolgenden Panzerungen sowohl mit großem Einfallswinkel wie bei erheblichen Zwischenräumen der Panzerungen voneinander (die einen Meter oder sogar mehr betragen können) erfolgen soll.from this development resulting prerequisites for fighting them force an improvement of the hollow charge projectiles used for this purpose with the aim of a considerable distance still sufficient penetration for composite targets - double, triple and multiple armor - to achieve, especially when penetrating the successive Armoring with a large angle of incidence as well as with considerable spaces between the armor (the can be one meter or even more).

Ferner wird die Forderung an Hohlladungsgeschosse gestellt, daß sie "auf Abstand" (mit großem "stand off") und nicht lediglich durch Kontakt der GeschoiäspiTize mit der Panzerung wirken.Furthermore, the requirement is made on shaped charge projectiles, that they are "at a distance" (with a large "stand off") and not merely through contact with the GeschoiäspiTize of the armor.

Diese verschiedenen Vorbedingungen erfordern einerseits ein Ausziehen oder ein Ausbreiten des Strahles und andererseits die Erzielung eines ununterbrochenen Strahles. These various preconditions require, on the one hand, an extension or spreading of the beam and, on the other hand, the achievement of an uninterrupted beam.

Durch die Erfindung wird es ermöglicht, diesen Vorbedingungen in denkbar vollkommener Weise Rechnung zu tragen, indem als Ausfütterung für die Hohlladung eine Metallegierung auf Grundlage von Kupfer, vorzugsweise eine Dreist offkupferlegierung, verwendet wird, welche einer in besonderer weise durchgeführten Wärmebehandlung (Weich-The invention makes it possible to take these preconditions into account in the most perfect way possible, by using a metal alloy based on copper, preferably a Dreist, as a lining for the shaped charge off-copper alloy, which one in particular wisely carried out heat treatment (soft

9 09835/0023 ~3~9 09835/0023 ~ 3 ~

glühen) unterworfen wurde. Die Verwendung einer solchen Legierung ermöglicht es, weit größere Dehnungen als iie nach dem Stande der Technik erreichbar sind, nämlich solche von vorzugsweise 70 bis 80 ^ , und jedenfalls immer über 60 % , zu erzielen.glow) was subjected. The use of such an alloy enables elongations far greater than iie are achievable according to the state of the art, namely those of preferably 70 to 80 ^, and in any case always over 60% to achieve.

Die Auskleidungen mit Dehnungen über 60 % und von vorzugsweise 70 bis 80 i* erhält man nach der Erfindung, indem man die vorzugsweise aus einem Dreistoffsystem bestehende Zusammensetzung oder Mischung der legierung mit einer Mischung der Legierung mit einer Wärmebehandlung bei erhöhter (Weichglüh-) Temperatur kombiniert.The linings with elongations above 60% and preferably from 70 to 80 i * are obtained according to the invention by combining the composition or mixture of the alloy, which preferably consists of a three-component system, with a mixture of the alloy with a heat treatment at elevated (soft annealing) temperature .

Dieser Wärmebehandlung erfolgt gemäß der Erfindung vorzugsweise bei einer Temperatur oberhalb von 6000C, (vorzugsweise etwa bei 7000C) für eine zweckentsprechend gewählte Zeitdauer, die 60 Minuten erreichen und sogar übersohreiten kann. Die Wärmebehandlung kann aber a.uch ohne den Rahmen der Erfindung zu verlassen, durch eine damit äquivalent wirkende Wärmebehandlung ersetzt werden.This heat treatment of the invention is carried out according to preferably at a temperature above 600 0 C, (preferably about 700 0 C) for an appropriately selected period of time, which can even reach 60 minutes and übersohreiten. The heat treatment can, however, also without departing from the scope of the invention, be replaced by a heat treatment which has an equivalent effect.

Die Einzelheiten und weitere Merkmale und Vorteile der Erfindung ergeben sich aus der folgenden Beschreibung von Ausführungsbeispielen derselben, auf die die Erfindung aber keineswegs beschränkt ist. Vielmehr können, ohne Rahmen der Erfindung zu verlassen, die in den BeispielenThe details and further features and advantages of the invention will become apparent from the following description of FIG Embodiments of the same, but to which the invention is in no way limited. Rather, without To leave the scope of the invention in the examples

909835/0023 ~4~909835/0023 ~ 4 ~

U53867U53867

genannten Legierungen durch, alle Arten anderer einschlägiger Lege/Lrungen und die v/ärmebehandlung durch jede, zu dem gleichen Ziele führende v/ärmebehandlung ersetzt werden.named alloys by, all kinds of other relevant Lay / Lrungen and the v / heat treatment by each, to the same goal leading v / heat treatment to be replaced.

Gemäß diner ersten Ausführungsform der Erfindung "besteht die Dreistofflegierung aus Plupfer mit einem Zusatz vonAccording to the first embodiment of the invention "consists the ternary alloy from Plupfer with the addition of

titi

10 Ms 15 'i'o Wickel und 20 bis 25 /° Zink. Sie wird etwa. 60 Minuten lang bei einer Temperatur von 700 C geglüht. Die so behandelte Legierung besitzt eine Dehnung von über bo ■;··>. 10 Ms 15 'i'o wraps and 20 to 25 / ° zinc. She will be about. Annealed for 60 minutes at a temperature of 700 C. The alloy treated in this way has an elongation of over bo ■; ··>.

Grumä'3 einer anderen Ausfünrungsform der Erfindung besteht die Dreistofflegjerung aus Kupfer mit einem Zusatz von 5 bis 10 /■' Zinn und 4 /« Zink. kSie v/ird 15 bis 30 Minuten lang bei einer Temperatur von bOO bis TOO0C geglüht, wodurch sich eine D/ehnung von 70 bis 75 L/o ergibt.In another embodiment of the invention, the ternary alloy consists of copper with an addition of 5 to 10% tin and 4% zinc. It is annealed for 15 to 30 minutes at a temperature of 100 to TOO 0 C, resulting in a thinning of 70 to 75 L / o .

Eine Messinglegierung mit 30 bis 40 fo Zink, die 15 bis 30 Minuten lang bei einer Temperatur von etwa. 700°c geglüht wurde, ergibt eine haltende Ausfütterung mit einer Dehnung von 80 >a . Dieser außerordentlich hohe Wert entspricht in besonders vollkommener Weise den Eigenschaften, die zur Erzielung des angestrebten Erfolges, insbesondere der Beeinflussung des Strahles bei der Bekämpfung von neuzeitlichen Panzerungen der eingangs beschriebenen Art, erforderlich sind.A brass alloy with 30 to 40 fo zinc that lasts 15 to 30 minutes at a temperature of about. 700 ° C was annealed, results in a holding lining with an elongation of 80> a. This extraordinarily high value corresponds in a particularly perfect way to the properties which are required to achieve the desired success, in particular to influence the jet in the fight against modern armor of the type described at the beginning.

909835/0023 Patentansprüche: 909835/0023 claims:

BADBATH

Claims (5)

H53867 PatentansprücheH53867 claims 1.) Ausiütterung für Hohl la.dungs geschosse, dadurch gekennzeichnet , da us sie a.us einer bei iioher, größenordnungsgeinäß 70O0C betragender Tempera.-tur für eine Zeitdauer von bis zu 6ü Minuten geglühten Legierung auf der Grundlage von Kupier und mit einer Dehnung von 70 bis 80 fo, wenigstens aber über'uO >ό, besteht.1.) Feeding for hollow charge projectiles, characterized in that they are annealed from an alloy based on Kupier and with a temperature of the order of 70O 0 C for a period of up to 60 minutes an elongation of 70 to 80 fo, but at least over'uO> ό, exists. 2.) Ausfütterung nach Anspruch 1, dadurch gekennzeichnet , daw die Legierung eine JJreistofflegierung ist. .2.) Lining according to claim 1, characterized in that the alloy is one Is a pure alloy. . j.) Ausfütterung nach Anspruch 1 und 2, dadurch gekennzei-chnet , da^ reiner 10 bis I^ ,-> Nickel und 20 bis 23 cß> Zink enthaltenden Kupferdreistoff legierung besteht. j.) Lining according to claim 1 and 2, characterized in that there is a pure copper tri-alloy containing 10 to 1 ^, -> nickel and 20 to 23 c ß> zinc. 4.) Ausfüttemng nach Anspruch 1 und 2, dadurch gekennzeichnet , daß sie a.us einer Kupferdreistoff legierung, die ο bis 10 $ Zinn und etwa 4 0Io Zink enthält, besteht.4.) Ausfüttemng according to claim 1 and 2, characterized in that it consists a.us of a copper tri-alloy which contains ο to 10 $ tin and about 4 0 Io zinc. 5.) Ausfütterung nach Anspruch 1, dadurch gekennzeichnet , daß sie a.us einer Kupfer-5.) lining according to claim 1, characterized that they a.from a copper Zweiatofflegierung, die 30 bis 40 >> Zink enthält, besteht, 909835/0023Two-atom alloy, the 30 to 40 >> Zinc contains, consists, 909835/0023
DE19651453867 1964-10-13 1965-10-05 Filling for shaped charge projectiles Pending DE1453867A1 (en)