DE1198040B - Process for the surface coating of wood with thermoplastics - Google Patents

Process for the surface coating of wood with thermoplastics

Info

Publication number
DE1198040B
DE1198040B DEJ22376A DEJ0022376A DE1198040B DE 1198040 B DE1198040 B DE 1198040B DE J22376 A DEJ22376 A DE J22376A DE J0022376 A DEJ0022376 A DE J0022376A DE 1198040 B DE1198040 B DE 1198040B
Authority
DE
Germany
Prior art keywords
parts
weight
wood
coating
application
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DEJ22376A
Other languages
German (de)
Inventor
Dr Gerd-Zeno Jonas
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GERD ZENO JONAS DR
Original Assignee
GERD ZENO JONAS DR
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to DEI17022A priority Critical patent/DE1139263B/en
Priority claimed from FR905764A external-priority patent/FR1336380A/en
Application filed by GERD ZENO JONAS DR filed Critical GERD ZENO JONAS DR
Priority to DEJ22376A priority patent/DE1198040B/en
Publication of DE1198040B publication Critical patent/DE1198040B/en
Pending legal-status Critical Current

Description

Verfahren zur Oberflächenbeschichtung von Holz mit thermoplastischen Kunststoffen Die vorliegende Erfindung bezieht sich auf ein Verfahren zur Oberflächenbeschichtung von Holz mit thermoplastischen Kunststoffen und betrifft die Anwendung des in der Patentanmeldung J 17022 Ic/38 c, deutsche Auslegeschrift (1139 263) für Holzverleimung beschriebenen Verfahrens zu solchen Zwecken.Process for surface coating of wood with thermoplastic Plastics The present invention relates to a method for surface coating of wood with thermoplastics and concerns the application of the in the Patent application J 17022 Ic / 38 c, German Auslegeschrift (1139 263) for wood gluing described procedure for such purposes.

In der Hauptpatentanmeldung wird ein Verfahren zur Holzverleimung unter Verwendung von thermoplastischen Kunststoffen beansprucht, das dadurch gekennzeichnet ist, daß der thermoplastische Kunststoff über seinen Erweichungspunkt erhitzt und dann auf die zu verbindenden Flächen aufgetragen wird, wonach er gegebenenfalls unter Druck abkühlen und erstarren gelassen wird.In the main patent application, a method for gluing wood claimed using thermoplastics, which is characterized is that the thermoplastic is heated above its softening point and is then applied to the surfaces to be joined, after which it is optionally is allowed to cool and solidify under pressure.

Es zeigte sich nun, daß ein solches Verfahren sich auch vorteilhaft für die Oberflächenbeschichtung von Holz eignet, wodurch gegenüber den bekannten Oberflächenbeschichtungsverfahren von Holz wesentliche Vorteile erzielt werden.It has now been found that such a process is also advantageous suitable for the surface coating of wood, which means compared to the known Surface coating process of wood provides significant advantages.

Die für das erfindungsgemäße Verfahren notwendige Verflüssigung der überzugsmassen erfolgt durch Erwärmung, die Abbindung bzw. Aushärtung wird durch Abkühlung vorgenommen. Dadurch tritt eine sehr schnelle Erstarrung des Überzuges ein, das Werkstück kann unmittelbar nach Aufbringen des Überzuges weiterverarbeitet werden. Irgendwelche Lager- oder Trockenzeiten (Aushärtungszeiten) entfallen.The liquefaction of the necessary for the process according to the invention Coating masses take place through heating, the setting or hardening is through Cooling made. This causes the coating to solidify very quickly one, the workpiece can be processed further immediately after the coating has been applied will. There is no need for any storage or drying times (curing times).

Es ist für die Oberflächenbeschichtung von Holz bekannt, thermoplastischen Kunststoff kalt auf den Holzträger aufzutragen und dann durch Druck und Hitze zum Fließen zu bringen, worauf sich durch Abkühlen die Oberflächenschicht bildet.It is known for the surface coating of wood, thermoplastic Apply plastic cold to the wooden support and then by means of pressure and heat to To bring flow, whereupon the surface layer is formed by cooling.

Bei diesen Verfahren wurde der thermoplastische Kunststoff entweder in gelöster Form, als Dispersion bzw. Emulsion, angewendet oder in Folien oder Filmform aufgebracht.In this process, the thermoplastic was either in dissolved form, as a dispersion or emulsion, applied or in foil or film form upset.

Das erfindungsgemäße Verfahren unterscheidet sich von diesen bisher gebräuchlichen Methoden vorteilhaft dadurch, daß für das Auftragen der Überzüge Lösungs-, Dispersions- oder Emulsionsmittel nicht mehr erforderlich sind bzw. daß die Verwendung von in getrennten Arbeitsgängen herzustellenden Filmen oder Folien in Fortfall kommt.The method according to the invention differs from these up to now Usual methods advantageous in that for the application of the coatings Solvents, dispersants or emulsifiers are no longer required or that the use of films or foils to be produced in separate operations in failure comes.

Da das mit dem Überzug zu versehende Werkstück erfindungsgemäß nicht erwärmt werden muß, findet eine schonende Behandlung statt. Es wird eine Befeuchtung des Werkstückes durch Diffusion der Lösungsmittel oder Dispersions- und Emulsionsträger vermieden, die sonst unter Umständen eine Wiedertrocknung oder Konditionierung des Holzes erfordern. Ein weiterer Nachteil, nämlich der des Festhaltens von Lösungsmitteln durch viele Kunstharze über lange Zeiträume, wodurch der Überzug eine Qualitätsminderung erfahren kann, kommt in Fortfall.Since the workpiece to be provided with the coating is not according to the invention must be heated, a gentle treatment takes place. It becomes a humidification of the workpiece by diffusion of the solvents or dispersion and emulsion carriers avoided, which could otherwise result in re-drying or conditioning of the Require wood. Another disadvantage, namely that of the retention of solvents due to many synthetic resins over long periods of time, which results in a deterioration in the quality of the coating can experience, comes in discontinuation.

In der Regel sind angesetzte Farben, Lacke, Harze usw. nicht unbegrenzt haltbar, sondern müssen innerhalb einer mehr oder weniger langen Zeit verarbeitet werden. Die erfindungsgemäß zur Anwendung kommenden thermoplastischen Kunstharze sind hingegen praktisch unbegrenzt haltbar. Sie können nach dem Erwärmen über ihren Schmelzpunkt und dem folgenden Abkühlen und Erstarren erneut durch wiederholtes Erwärmen geschmolzen werden, ohne dadurch irgendwelche Qualitätseinbußen zu erleiden.As a rule, mixed colors, varnishes, resins, etc. are not unlimited durable, but must be processed within a longer or shorter period of time will. The thermoplastic synthetic resins used according to the invention however, have a practically unlimited shelf life. You can put them over theirs after heating Melting point and the subsequent cooling and solidification again by repeated Heating can be melted without suffering any loss of quality.

Für den erfindungsgemäßen Auftrag der Überzüge ist nur ein verhältnismäßig geringer Maschinenaufwand nötig. Erforderlich ist ein heizbarer und in der Temperatur regelbarer Vorratsbehälter oder eine entsprechende Einrichtung, in der die Erwärmung und damit das Schmelzen der als Überzug verwendeten Stoffe erfolgt. Die für die Folien- und Filmverklebung benötigten heizbaren Preßvorrichtungen entfallen also. Außerdem muß natürlich für einen geeigneten Auftrag gesorgt werden. Die zweckmäßigste Auftragsvorrichtung richtet sich nach der Art der verwendeten Kunststoffe und des zu beschichtenden Werkstückes.For the application of the coatings according to the invention, only one is proportionate low machine effort required. What is required is a heatable and in temperature adjustable storage container or a corresponding device in which the heating and thus the melting of the substances used as a coating takes place. The for the Foil and film bonding required heatable pressing devices are therefore not required. In addition, a suitable order must of course be arranged. The most expedient Application device depends on the type of plastics used and the workpiece to be coated.

Beispielsweise kann das verflüssigte Material aufgegossen werden. Der Schmelzbehälter kann dabei unter Überdruck stehen, so daß beim anschließenden Beschichten unter Normaldruck als Folge der stattgefundenen Überhitzung bei sonst verhältnismäßig zähflüssigen Stoffen ein Viskositätsabfall eintritt und ein dünner Film aufgetragen werden kann. Dabei kann man mit Preßluft oder zur Schonung des Materials mit einem inerten Gas (z. B. Stickstoff) arbeiten, um etwaige Oxydationserscheinungen auszuschließen.For example, the liquefied material can be poured on. The melting container can be under excess pressure, so that during the subsequent Coating under normal pressure as a result of overheating, otherwise relatively viscous substances a drop in viscosity occurs and a thin film can be applied. You can use compressed air or to To protect the material, work with an inert gas (e.g. nitrogen) to avoid any To exclude signs of oxidation.

Ebenso ist es zur schonenden Behandlung des Gutes möglich, das ganze Beschichtungssystem unter Vakuum zu setzen, wodurch eine erhebliche Erniedrigung der Verarbeitungstemperatur erreicht wird.It is also possible to treat the goods gently, the whole Putting the coating system under vacuum, resulting in a significant degradation the processing temperature is reached.

Für den Auftrag des Beschichtungsgutes eignen sich z. B. Verfahren wie Aufgießen, Aufdüsen, Aufspritzen, Luftbürsten, Aufwalzen oder Kombinationen dieser Methoden.For the application of the material to be coated, for. B. Procedure such as pouring on, jetting, spraying on, air brushing, roller application or combinations these methods.

Geeignete Einrichtungen zum Aufbringen derartiger Überzüge können auch als transportable Geräte ausgeführt werden. Diese können unter anderem vorzugsweise für das Beschichten (Versiegeln) von Fußböden aus Holz, wie Parkett, ebenso für Holzwände und Holzdecken Anwendung finden.Suitable devices for applying such coatings can can also be designed as portable devices. These can, among other things, preferably for coating (sealing) floors made of wood, such as parquet, as well as for Wooden walls and wooden ceilings are used.

In ähnlicher Weise wie das Aufbringen üblicher Überzüge ist auch das Auftragen von Schaumschichten auf Werkstücke möglich. Zweckmäßig wird das verwendete Auftragsgut zuvor mit Treibmitteln vermischt; durch die Erwärmung im Auftragsbehälter bildet sich der Schaum. Es ist aber auch möglich, die Schaumbildung, die gegebenenfalls bereits im Auftragsbehälter beginnt, auf dem Werkstück fortzusetzen. Das Aufbringen von Schaumschichten kann vor allem für Isolierzwecke vorteilhaft sein.This, too, is similar to the application of conventional coatings Foam layers can be applied to workpieces. This is expediently used Order material mixed with propellants beforehand; due to the heating in the order container the foam is formed. But it is also possible to prevent the foam formation, if necessary already in the order container begins to continue on the workpiece. The application Foam layers can be particularly beneficial for insulation purposes.

In jedem Fall ist der Maschinenaufwand bei dem erfindungsgemäßen Verfahren geringer als bei üblichen maschinellen Methoden, weil vor allem die Trocknung bzw. Aushärtung in entsprechenden Apparaturen wegfällt und große und kostspielige Preßanlagen sich erübrigen. Ebenso sind Spritzkabinen, Entlüftungsanlagen usw. nicht erforderlich. Die Brandgefahr wird gleichzeitig wesentlich vermindert. -Es entfallen erfindungsgemäß alle Warte-, Trocken-und Aushärtungszeiten. Der Auftrag des Überzuges geht schnell im Durchlaufverfahren vor sich, die Abbindung erfolgt innerhalb weniger Sekunden. Dadurch ist der Arbeitsablauf im Vergleich zu allen bisherigen Methoden wesentlich schneller.In any case, the machine outlay is in the method according to the invention lower than with conventional machine methods, because above all the drying or There is no need for curing in the appropriate equipment and there is no need for large and expensive pressing systems be unnecessary. Spray booths, ventilation systems, etc. are also not required. At the same time, the risk of fire is significantly reduced. -It is omitted according to the invention all waiting, drying and curing times. The application of the coating is quick in a continuous process in front of you, the setting takes place within a few seconds. This makes the workflow essential compared to all previous methods more quickly.

Die meisten bisher verwendeten Überzugsmassen neigen in mehr oder minder starkem Umfang zum Schrumpfen während der Abbindung. Erfindungsgemäß ist eine Schrumpfung des Überzuges nicht oder in nur sehr geringem - praktisch nicht meßbarem - Umfang vorhanden.Most of the coating compositions used to date tend to be more or less inferior circumference to shrink during setting. Is according to the invention a shrinkage of the coating not or only to a very small extent - practically not measurable - scope available.

Die meisten Lacküberzüge werden nicht in einem Arbeitsgang, sondern in mehreren aufeinanderfolgenden aufgebracht. Dabei geht man so vor, daß der erste Auftrag zunächst durchhärten muß, d. h., die vorhandenen Lösungsmittel müssen aus der Lackschicht verdampfen oder abwandern, ehe der nächste Auftrag erfolgen kann. Zwischen dem ersten und zweiten Auftrag erfolgt meist noch ein kurzer Schliff, um unter anderem Staubreste, die sich während des Trocknens festgesetzt haben, zu entfernen.Most paint coatings are not done in one go, but applied in several consecutive. One proceeds in such a way that the first The order must first cure, d. that is, the solvents present must be taken out the paint layer evaporate or migrate before the next application can be made. Between the first and second application, there is usually a short sanding in order Among other things, to remove dust residues that have settled during the drying process.

Erfindungsgemäß sind alle diese Arbeitsgänge nicht erforderlich, weil keinerlei Lösungsmittel verwendet werden. Der Überzug kann vielmehr in einem Arbeitsgang in jeder beliebigen Schichtdicke aufgebracht werden. Ob ein nachfolgender Schliff notwendig oder zweckmäßig ist, richtet sich nach dem gewählten Arbeitsverfahren und den gestellten Qualitätsanforderungen. Für das erfindungsgemäße Aufbringen von Überzügen (Beschichtungen) kommen sowohl großflächige als auch kleine Werkstücke in Betracht.According to the invention, all of these operations are not necessary because no solvents are used. Rather, the coating can be carried out in one operation can be applied in any layer thickness. Whether a subsequent touch is necessary or appropriate, depends on the chosen working method and the quality requirements. For the inventive application of Coverings (coatings) come both large-area and small workpieces into consideration.

Es kann auch z. B. ein Kantenschutz von z. B. Holzspanplatten zum Zwecke der Reduzierung der Wasseraufnahme von Interesse sein. Ebenso können die Hirnflächen von Hölzern beschichtet werden, um Rißbildungen bei der natürlichen oder künstlichen Trocknung zu vermeiden.It can also e.g. B. an edge protection of z. B. chipboard for Purposes of reducing water intake may be of interest. Likewise, the End faces of woods are coated to prevent cracking when natural or avoid artificial drying.

Erfindungsgemäß eignen sich für Beschichtungen alle thermoplastischen Kunststoffe, die sich innerhalb eines bestimmten für das Holz im Zeitbereich der Einwirkungsdauer nicht schädlichen Temperaturbereiches unter geeigneten Druckverhältnissen erweichen und verflüssigen lassen. Die Zugabe sogenannter Verflüssigungsmittel, die also den Schmelzpunkt erniedrigen, kann gegebenenfalls ratsam erscheinen.According to the invention, all thermoplastic coatings are suitable Plastics that are within a certain range for the wood in the time range Duration of exposure to non-harmful temperature range under suitable pressure conditions soften and liquefy. The addition of so-called liquefying agents, those that lower the melting point may appear advisable.

Brauchbar sind beispielsweise Polyvinylverbindungen, Polystyrole, Polyindene, Cumaronharze, Polyamide, Polyäthylene, Polycarbonate, Mischpolymerisate, aber unter bestimment Voraussetzungen auch Phenolharze in Form der Novolake.For example, polyvinyl compounds, polystyrenes, Polyindenes, coumarone resins, polyamides, polyethylene, polycarbonates, copolymers, but under certain conditions also phenolic resins in the form of novolaks.

Die genannten Stoffe können für sich allein oder im Gemisch mit anderen eingesetzt werden.The substances mentioned can be used on their own or in a mixture with others can be used.

Die Mischung von Thermoplasten mit unterschiedlichen Erweichungspunkten ist für das erfindungsgemäße Verfahren vorteilhaft. Dabei spielt es keine Rolle, ob die Kunststoffe gleichartiger oder ungleichartiger chemischer Konstitution sind. Durch die unterschiedlichen Erweichungspunkte, die auch auf Unterschiede im Polymerisationsgrad hinweisen, werden die Eigenschaften hinsichtlich der Haftung am Untergrund verbessert.The mixture of thermoplastics with different softening points is advantageous for the method according to the invention. It doesn't matter whether the plastics are of similar or dissimilar chemical constitution. Due to the different softening points, which also reflect differences in the degree of polymerization point out, the properties with regard to adhesion to the substrate are improved.

Um einen ausreichenden Zeitraum für das Haften und Abbinden des Überzuges zu erhalten - um also zu vermeiden, daß die Abbindung schon während des Auftragens einsetzt -, wird der verwendete Stoff zweckmäßig nicht nur bis zu seinem Erweichungspunkt, sondern darüber hinaus erhitzt. Je nach dem verwendeten Material wird die Überhitzung in der Regel 5 bis 35° C betragen, wobei man im Mittel mit Überhitzungstemperaturen von etwa 20 bis 30° C rechnen kann.To allow sufficient time for the coating to adhere and set to get - so to avoid that the setting already during the application starts - the substance used is expediently not only up to its softening point, but also heated. Depending on the material used, the overheating will be usually 5 to 35 ° C, with an average of overheating temperatures from about 20 to 30 ° C.

Den erfindungsgemäß anzuwendenden thermoplastischen Kunststoffen können Zusatzstoffe wie modifizierte Naturharze, Farbstoffe, Streckmittel, Füllstoffe, Haftverbesserer und/oder Weichmacher zugesetzt werden.The thermoplastics to be used according to the invention can Additives such as modified natural resins, dyes, extenders, fillers, Adhesion improvers and / or plasticizers are added.

Durch die Zugabe von Stearaten kann die Geschmeidigkeit von Überzügen in gewisser Weise erhöht und die wasserabstoßende Wirkung verbessert werden. Ebenso ist eine gewisse Mattierung erzielbar.The suppleness of coatings can be reduced by adding stearates can be increased to some extent and the water-repellent effect can be improved. as well a certain matting can be achieved.

Alle in der Hauptpatentanmeldung beschriebenen Verfahrensmaßnahmen eignen sich auch für das erfindungsgemäße Verfahren.All procedural measures described in the main patent application are also suitable for the process according to the invention.

Beispiele für erfindungsgemäß aufzubringende überzugsmassen sind folgende: Erweichungs- punkt, ° C 1. 80 Gewichtsteile Polyvinylacetat ... 115 bis 118 20 Gewichtsteile Polyvinylacetat ... 85 2. 80 Gewichtsteile Polyvinylacetat ... 115 bis 119 10 Gewichtsteile Polyvinylacetat ... 1.00 10 Gewichtsteile Dicyclohexyl- phthalat (Weichmacher) Erweichungs- punkt, ° C 3. 80 Gewichtsteile nach Beispiel 1 oder 2 15 Gewichtsteile Erd-, Mineral- oder andere Farbstoffe 5 Gewichtsteile Maleinsäure- anhydrid (als Haftverbesserer) 4. 80 Gewichtsteile Polyamid . . . . . . . . 105 bis 115 5 Gewichtsteile Polyamid . . . . . . . . 180 bis 190 5 Gewichtsteile Polyamid . . . . . . . . 45 bis 55 10 Gewichtsteile Dibutylphthalat (Weichmacher) 5. 60 Gewichtsteile Cumaronharz .... 155 10 Gewichtsteile Cumaronharz .... 85 30 Gewichtsteile Füll- und/oder Streckmittel, Farbstoffe. Nach Beispiel 5 können auch Polyindene allein oder im Gemisch mit Cumaronharzen u. a. ver- arbeitet werden. 6. 40 Gewichtsteile Polymerisatharz styrolhaltiger Kohlenwasserstoffe 110 20 Gewichtsteile Polymerisatharz styrolhaltiger Kohlenwasserstoffe 80 10 Gewichtsteile Phenol-(Kresol-) Novolak ..................... 80 bis 100 5 Gewichtsteile Maleinsäureanhydrid 25 Gewichtsteile nach Beispiel 5 Füll-, Streckmittel u. Farbstoffe 7. 60 Gewichtsteile Polyindenharz ... 80 10 Gewichtsteile Vinylpolymerisat 95 10 Gewichtsteile Dibutylphthalat 2 Gewichtsteile Maleinsäureanhydrid 18 Gewichtsteile Pigment und Füllmittel Erweichungs- punkt, ° C B. 70 Gewichtsteile Phenol-(Kresol-) Novolak . . . . . . . . . . . . . . . . . . . . . 80 bis 100 20 Gewichtsteile Polyindenharz ... 80 10 Gewichtsteile Cumaronharz (phenolmodifiziert) ............ 75 Nach Beispiel 8 kann zur weiteren Härtung Hexa- methylentatramin z. B. im Voranstrichverfahren ein- gesetzt werden. 9. 80 Gewichtsteile Polyvinylacetat ... 115 bis 118 9 Gewichtsteile Polyvinylacetat ... 96 4 Gewichtsteile Aluminiumstearat 2 Gewichtsteile Maleinsäureanhydrid 5 Gewichtsteile Weichmacher 10. 70 Gewichtsteile Cyclokautschuk .. 135 30 Gewichtsteile rizinenöl- modifiziertes Alkydharz 11. 50 Gewichtsteile Phenolharz- Novolak ..................... 75 bis 85 20 Gewichtsteile Phenolharz- Novolak ..................... 108 bis 118 10 Gewichtsteile Trikresylphosphat 15 Gewichtsteile Polyvinylacetat ... 96 5 Gewichtsteile Maleinsäureanhydrid gegebenenfalls Farbstoffe, Füll- und/oder Streckmittel. Examples of coating compositions to be applied according to the invention are as follows: Softening point, ° C 1. 80 parts by weight of polyvinyl acetate ... 115 to 118 20 parts by weight of polyvinyl acetate ... 85 2. 80 parts by weight of polyvinyl acetate ... 115 to 119 10 parts by weight of polyvinyl acetate ... 1.00 10 parts by weight of dicyclohexyl phthalate (plasticizer) Softening point, ° C 3. 80 parts by weight according to Example 1 or 2 15 parts by weight of earth, mineral or other dyes 5 parts by weight of maleic acid anhydride (as an adhesion improver) 4. 80 parts by weight of polyamide. . . . . . . . 105 to 115 5 parts by weight of polyamide. . . . . . . . 180 to 190 5 parts by weight of polyamide. . . . . . . . 45 to 55 10 parts by weight of dibutyl phthalate (Plasticizer) 5. 60 parts by weight of coumarone resin .... 155 10 parts by weight of coumarone resin .... 85 30 parts by weight of filling and / or Extenders, dyes. According to Example 5, polyindenes alone can also be used or mixed with coumarone resins, etc. will be working. 6. 40 parts by weight of polymer resin styrene-containing hydrocarbons 110 20 parts by weight of polymer resin styrene-containing hydrocarbons 80 10 parts by weight phenol (cresol) Novolak ..................... 80 to 100 5 parts by weight maleic anhydride 25 parts by weight according to Example 5 filling, Extenders and dyes 7. 60 parts by weight of polyindene resin ... 80 10 parts by weight of vinyl polymer 95 10 parts by weight of dibutyl phthalate 2 parts by weight maleic anhydride 18 parts by weight of pigment and Filler Softening point, ° C B. 70 parts by weight of phenol (cresol) Novolak. . . . . . . . . . . . . . . . . . . . . 80 to 100 20 parts by weight of polyindene resin ... 80 10 parts by weight of coumarone resin (phenol modified) ............ 75 According to Example 8, hexa- methylentatramine e.g. B. in the priming process be set. 9. 80 parts by weight of polyvinyl acetate ... 115 to 118 9 parts by weight of polyvinyl acetate ... 96 4 parts by weight of aluminum stearate 2 parts by weight maleic anhydride 5 parts by weight of plasticizer 10. 70 parts by weight of cyclo-rubber. 135 30 parts by weight of castor oil modified alkyd resin 11. 50 parts by weight of phenolic resin Novolak ..................... 75 to 85 20 parts by weight of phenolic resin Novolak ..................... 108 to 118 10 parts by weight of tricresyl phosphate 15 parts by weight of polyvinyl acetate ... 96 5 parts by weight maleic anhydride optionally dyes, fillers and / or extenders.

Claims (1)

Patentanspruch: Anwendung des Verfahrens zur Holzverleimung, in dem thermoplastischer Kunststoff über seinen Erweichungspunkt erhitzt und dann auf die zu verbindenden Flächen aufgetragen wird, wonach er gegebenenfalls unter Druck abkühlen und erstarren gelassen wird, nach Patentanmeldung J 17022Ic/38 c zur Oberflächenbeschichtung von Holz mit thermoplastischen Kunststoffen.Claim: Application of the process for gluing wood in which thermoplastic plastic heated above its softening point and then on the to be connected surfaces is applied, after which it may cool under pressure and is allowed to solidify, according to patent application J 17022Ic / 38 c for surface coating of wood with thermoplastics.
DEJ22376A 1959-09-25 1962-09-12 Process for the surface coating of wood with thermoplastics Pending DE1198040B (en)