DE10254678B4 - Shaped body, in particular for a seat cushion - Google Patents

Shaped body, in particular for a seat cushion Download PDF

Info

Publication number
DE10254678B4
DE10254678B4 DE10254678A DE10254678A DE10254678B4 DE 10254678 B4 DE10254678 B4 DE 10254678B4 DE 10254678 A DE10254678 A DE 10254678A DE 10254678 A DE10254678 A DE 10254678A DE 10254678 B4 DE10254678 B4 DE 10254678B4
Authority
DE
Germany
Prior art keywords
gel
shaped body
polyurethane
foam layer
moldings according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE10254678A
Other languages
German (de)
Other versions
DE10254678A1 (en
Inventor
Adolf Stender
Peter Dr. Gansen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Technogel GmbH and Co KG
Original Assignee
Technogel GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Technogel GmbH and Co KG filed Critical Technogel GmbH and Co KG
Priority to DE10254678A priority Critical patent/DE10254678B4/en
Priority to EP03019425A priority patent/EP1421878B1/en
Priority to DE50302403T priority patent/DE50302403D1/en
Priority to AT03019425T priority patent/ATE317655T1/en
Priority to US10/715,397 priority patent/US20040098806A1/en
Publication of DE10254678A1 publication Critical patent/DE10254678A1/en
Application granted granted Critical
Publication of DE10254678B4 publication Critical patent/DE10254678B4/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

A molded article, preferably a seat cushion, comprises a lower bearing surface (1), a gel layer (2), comprising a polyurethane gel, having integral supports (3) separated from each other by extending channels (4), upon which a polyurethane foam layer (6) lies, whose upper face (5) is covered by an outer covering (7).

Description

Die Erfindung betrifft einen Formkörper, insbesondere für ein Sitzpolster, mit einer tragenden, unteren Auflagefläche und einer oberen Auflage.The Invention relates to a molding, especially for a seat cushion, with a supporting, lower support surface and an upper edition.

In der WO 82/00578 A1 wird eine Unterlage für Sitz- oder Liegeflächen beschrieben, die mit einer Hülle versehen ist, die als obere Auflage einen Fellüberzug aufweist. Innerhalb dieser Hülle befindet sich eine Schaumstoff-Ummantelung für eine in einer feuchtigkeitsundruchlässigen Umhüllung eingeschlossenen Einlage aus einem Material flüssiger bis pastöser Konsistenz, das unter der Einwirkung eines dem Gewicht des menschlichen oder tierischen Körpers entsprechenden Druckes (praktisch) nicht zusammendrückbar ist. Die Einlage lagert dabei auf einer unteren Auflagefläche, die aus dem unteren Teil der Schaumstoff-Ummantelung gebildet wird, auf.In WO 82/00578 A1 describes a pad for sitting or lying areas, those with a shell is provided, which has a fur cover as the upper edition. Within this shell There is a foam sheath for a trapped in a moisture-impermeable sheath Insert of a material liquid until pasty Consistency, which under the action of a human weight or animal body corresponding pressure (practically) is not compressible. The deposit is stored on a lower support surface, the is formed from the lower part of the foam sheath, on.

Nachteilig an der in der WO 82/00578 A1 beschriebenen Unterlage ist, dass Sie aufgrund Ihres Aufbaus eine große Bauhöhe aufweist.adversely to the document described in WO 82/00578 A1 is that you due to your construction a big one height having.

Von dieser Problemstellung ausgehend, liegt der Erfindung die Aufgabe zu Grunde, einen Formkörper mit geringer Bauhöhe so zu gestalten, dass er sich insbesondere für ein Sitzpolster verwenden lässt und hier zu einem hohen Sitzkomfort bei gegenüber her kömmlichen Sitzpolstern verringerter Bauhöhe führt und der sich generell für den Sitzmöbelbereich (Armauflagen, Rückenkissen, Nackenkissen) und insbesondere auch für den Fahrzeugbereich einsetzen lässt, bei denen eine Verringerung der Bauhöhe besonders vorteilhaft ist, da hierdurch unter dem Fahrzeugsitz ein höherer Einbauraum für technische Einbauten geschaffen werden kann.From Based on this problem, the invention is the task at the bottom, a molding with low height be designed so that he use in particular for a seat cushion lets and here to a high level of comfort in comparison with conventional seat cushions reduced Height leads and generally speaking for the seating area (armrests, Back cushions, Neck pillow) and in particular also for the vehicle sector leaves, where a reduction in height is particularly advantageous, as a result, under the vehicle seat, a higher installation space for technical installations can be created.

Diese Aufgabe wird gelöst durch einen gattungsgemäßen Formkörper, der sich dadurch auszeichnet, dass die Auflagefläche eine aus einem Polyurethan-Gel bestehende Gellage ist, die auf Ihrer Oberseite integrale, voneinander über Ausdehnungskanäle beabstandete Auflager aufweist, auf denen eine Polyurethan-Schaumstofflage aufliegt, deren Oberseite durch die obere Auflage abgedeckt ist.These Task is solved by a generic molding, the characterized in that the bearing surface of a polyurethane gel existing gel layer is integral on its top, spaced apart from one another via expansion channels Having supports bearing a polyurethane foam layer, the top of which is covered by the upper support.

Dabei ist es zweckmäßig, wenn die Auflage im Bereich der bei Belastung auftretenden Druckspitzen einen engeren Abstand voneinander aufweisen, wobei die Auflage vorzugsweise säulenförmig ausgebildet sein können.there it is useful if the support in the area of the pressure peaks occurring under load a closer distance from each other, wherein the support preferably formed columnar could be.

Aus Belüftungszwecken ist es vorteilhaft, wenn die obere Auflage ein Abstandsgewirk ist, das aus zwei durch Abstandsfäden miteinander verbundenen textilen Flächen besteht. Das an sich bekannte Abstandsgewirk setzt sich zusammen aus einer Warengrunde, einer Warenseite und aus diese miteinander verbindende Legebarren. Die Eigenschaften eines Abstandsgewirkes werden im Wesentlichen von den Bindungsstrukturen, also der Einbindung der Fäden in die Fläche, der Maschendichte sowie der Fadenstärke beeinflusst. Durch ihre 3D-Struktur bieten Abstandsgewirke viele technische Vorteile wie Luftdurchlässigkeit, geringes Gewicht, gutes Rückstellverhalten, Schockabsorption, Wärmezirkulation, Recyclingfähigkeit, Sortenreinheit und gute Verformbarkeit.Out ventilation purposes it is advantageous if the upper support is a spacer, that of two by spacer threads interconnected textile surfaces. The known Spacer knit consists of a goods reason, a Goods side and from these interconnecting guide bar. The Properties of a spacer knit are essentially determined by the binding structures, so the involvement of the threads in the Area, the mesh density and the thread strength influenced. Through her 3D structure, spacer fabrics offer many technical advantages such as air permeability, low weight, good resilience, Shock absorption, heat circulation, recyclability, Varietal purity and good ductility.

Hinsicht spezieller Ausführungsformen der Polyurethan-Schaumstofflage sowie ihrer Verbindung mit der Gellage wird auf die Gegenstände der Ansprüche 6 bis 10 verwiesen.respect special embodiments the polyurethane foam layer and its connection with the gel layer is on the objects the claims 6 to 10 referenced.

Erfindungsgemäß besteht die Gellage aus einem Polyurethan-Gel, dessen chemische Struktur aus langen Polymer-Fäden und nur wenigen Verkettungen ohne Verwendung zugesetzter Weichmacher bestehen kann.According to the invention the gel layer of a polyurethane gel, its chemical structure long polymer threads and consist of only a few links without the use of added plasticizers can.

Es ist aber möglich, dass für das Gel ein untervernetztes Polyurethan auf der Basis von Polyolen und Polyisocyanaten oder Polyethern und Polyisocyanaten eingesetzt wird.It but it is possible that for the gel is an undercrosslinked polyurethane based on polyols and Polyisocyanates or polyethers and polyisocyanates is used.

Erfindungsgemäß ist es zweckmäßig, wenn die Gelmassen mit Rohstoffen einer Isocyanat-Funktionalität der Polyolkomponente von mindestens 5,2 vorzugsweise von mindestens 6,5, insbesondere von mindestens 7,5 hergestellt werden.It is according to the invention expedient if the Gelled with raw materials of an isocyanate functionality of the polyol component of at least 5.2, preferably of at least 6.5, in particular of at least 7.5.

Dabei ist es vorteilhaft, wenn die Polyolkomponente zur Herstellung des Gels aus einem Gemisch aus

  • a) einem oder mehreren Polyolen mit Hydroxylzahlen unter 1 12 und
  • b) einem oder mehreren Polyolen mit Hydroxyzahlen im Bereich von 112 bis 600 besteht,
wobei das Gewichtsverhältnis der Komponente a) zu Komponente b) zwischen 90:10 und 10:90 liegt, die Isocyanat-Kennzahl des Reaktionsgemisches im Bereich von 15 und 60 liegt und das Produkt aus Isocyanat-Funktionalität und Funktionalität der Polyolkomponente mindestens 6 beträgt.It is advantageous if the polyol component for the preparation of the gel from a mixture of
  • a) one or more polyols having hydroxyl numbers below 1 12 and
  • b) one or more polyols having hydroxyl numbers ranging from 112 to 600,
wherein the weight ratio of component a) to component b) is between 90:10 and 10:90, the isocyanate index of the reaction mixture in the range of 15 and 60 and the product of isocyanate functionality and functionality of the polyol component is at least 6.

Als Alternativlösung kann vorgesehen sein, dass die Polyolkomponente zur Herstellung des Gels aus einem oder mehreren Polyolen mit einem Molekulargewicht zwischen 1000 und 12000 und einer OH-Zahl zwischen 20 und 1 12 besteht, wobei das Produkt der Funktionalitäten der polyurethanbildenden Komponenten mindestens 5 beträgt und die Isocyanat-Kennzahl zwischen 15 und 60 liegt.When alternative solution it can be provided that the polyol component for the preparation of the gel of one or more polyols having a molecular weight between 1000 and 12000 and an OH number between 20 and 1 12, the product of the functionalities of the polyurethane-forming Components is at least 5 and the isocyanate index is between 15 and 60.

Schließlich ist es vorteilhaft, wenn man als Isocyanate zur Gelherstellung solche der Formel Q (NCO) einsetzt, in der n für 2 bis 4 steht und Q einen aliphatischen Kohlenwasserstoffrest mit 8 bis 18 C-Atomen, einen cycloaliphatischen Kohlenwasserstoffrest mit 4 bis 15 C-Atomen, einen aromatischen Kohlenwasserstoffrest mit 6 bis 15 C-Atomen oder einen aralisphatischen Kohlenwasserstoffrest mit 8 bis 15 C-Atomen bedeutet, und wenn das Polyurethan mit Isocyanaten in reiner Form oder mit urethanisierten, allophanisierten, biurethisierten oder funktionell entsprechend modifizierten Isocyanaten hergestellt ist.Finally is it is advantageous if, as isocyanates for gel production such of the formula Q (NCO) in which n is 2 to 4 and Q is an aliphatic Hydrocarbon radical having 8 to 18 carbon atoms, a cycloaliphatic Hydrocarbon radical with 4 to 15 C atoms, an aromatic hydrocarbon radical with 6 to 15 carbon atoms or an aralisphatic hydrocarbon radical with 8 to 15 carbon atoms means, and when the polyurethane with isocyanates in pure form or with urethanised, allophanised, biuretted or is functionally prepared according to modified isocyanates.

Die EP 57 838 A1 beansprucht Gele zur Vermeidung von Dekubitus, welche durch eine niedrige Kennzahl, das heißt durch sogenannte Untervernetzung gekennzeichnet sind. Sie werden durch Umsetzung eines Polyisocyanates mit langkettigen Polyolen, die frei von kurzkettigen Anteilen sein sollen, hergestellt. Diese formstabilen Gele aus Polyurethan-Rohstoffen können als Matratzen, Matratzeneinlagen, Automobilsitze und als Polstermaterial zum Einsatz kommen. Die EP 51 1 570 A1 offenbart verbesserte Gele aus Polyolen und Isocyanaten mit niedrigen Kennzahlen, die aus Gemischen von langkettigen und kurkettigen Polyethern hergestellt werden. Die verarbeitungstechnisch günstiger herzustellen Polyol- und Polyiscyanatgemische finden bevorzugte Anwendung als Polstermaterial in der Schuhindustrie, als Auflagen zur Ver meidung von bzw. Verhinderung von Verletzungen, Gesichtsmasken, als Abpolsterungen von Pferdesätteln sowie in weiteren Anwendungen.The EP 57 838 A1 claims gels for the prevention of bedsores, which are characterized by a low characteristic, that is by so-called sub-crosslinking. They are prepared by reacting a polyisocyanate with long-chain polyols, which should be free of short-chain fractions. These dimensionally stable gels made of polyurethane raw materials can be used as mattresses, mattress inserts, automobile seats and as upholstery material. The EP 51 1 570 A1 discloses improved low-glock polyols and isocyanates prepared from blends of long-chain and short-chain polyethers. The processing technology to produce cheaper polyol and Polyiscyanatgemische find preferred use as cushioning material in the footwear industry, as conditions for the avoidance of Ver or prevention of injuries, face masks, as padding of horse saddles and in other applications.

Die bekannten Polyol- und Isocyanatgemische weisen für die oben beispielhaft genannten Anwendungen stets den Nachteil des hohen Eigengewichtes und die damit verbundene hohe Wärmekapazität auf. Aufgrund des hohen Eigengewichtes von etwa 1,0 g/cm3 ist der Einsatz auf Anwednungen beschränkt, bei denen das Gewicht in Relation zu den hervorragenden druckverteilenden Eigenschaften eine untergeordnete Rolle spielt. Darüber hinaus kann die hohe Wärmekapazität des Polyurethan-Gels im direkten Körperkontakt als unangenehm empfunden werden, da Körperwärme zum Aufwärmen der jeweiligen Gelmassen deutlich wahrnehmbar dem Körper entzogen wird.The known polyol and isocyanate mixtures always have the disadvantage of the high own weight and the associated high heat capacity for the applications exemplified above. Due to the high weight of about 1.0 g / cm 3 , the use is limited to applications in which the weight plays a minor role in relation to the excellent pressure-distributing properties. In addition, the high heat capacity of the polyurethane gel in direct body contact can be perceived as unpleasant, since body heat to warm up the respective gel masses is clearly removed from the body.

In der DE 43 08 445 A1 werden verschiedene Verfahren bzw. Patentschriften ( EP 0 057 839 A1 ; WO-88/01878 A1; EP 0 453 286 A2 zur Herstellung von Gelschäumen mit Luft, Stickstoff und Kohlendioxid genannt. Die Reduzierung des spezifischen Gewichts und damit verbundene Verringerung der Wärmekapazität sind im gewünschten Maße erreicht, die Gele weisen aber den Nachteil auf, dass die gebildeten Zellen bei Druckbeanspruchung an den Zellinnenwänden aufgrund des sehr hohen Selbstklebeverhaltens der stets untervernetzten Reaktionsprodukte auf Basis von Polyolen und Polyisocyanaten verkleben. Darüber hinaus stellen die Zellen eine Schwächung der Gelmatrix dar, die sich negativ auf die mechanischen Eigenschaften, wie Bruchdehnung und Zugfestigkeit auswirkt. Auch kehrt ein zelliges Gel nach Belastung langsamer in seine Ausgangsposition zurück. Des Weiteren können Schrumpfprobleme auftreten, wie sie aus der Verarbeitung von Polyurethanschaumstoffen bekannt sind.In the DE 43 08 445 A1 Are various methods or patents ( EP 0 057 839 A1 ; WO-88/01878 A1; EP 0 453 286 A2 for producing gel foams with air, nitrogen and carbon dioxide. The reduction of the specific weight and the associated reduction of the heat capacity are achieved to the desired extent, but the gels have the disadvantage that the cells formed under compressive stress on the cell inner walls due to the very high self-sticking behavior of always undercrosslinked reaction products based on polyols and polyisocyanates , In addition, the cells are a weakening of the gel matrix, which has a negative effect on the mechanical properties, such as elongation at break and tensile strength. Also, a cellular gel returns more slowly to its original position after loading. Furthermore, shrinkage problems can occur, as they are known from the processing of polyurethane foams.

Ein weiterer Nachteil der beschriebenen Polyurethan-Gele ist das Einsitzverhalten. Insbesondere beim ersten Kontakt wird ein Gel-Kissen häufig als hart empfunden, weil erst mit einer Zeitverzögerung das Gel in die gewünschte eine optimale Druckverteilung garantierende Position fließt bzw. geflossen ist.One Another disadvantage of the polyurethane gels described is the single seat behavior. Especially at the first contact, a gel pad is often considered hard felt, because only with a time delay, the gel in the desired one optimal position of the pressure guaranteeing or flowing flowed.

Eine Gelmasse, die eine deutliche Reduzierung des Gewichtes, der Wärmekapazität und des Einsitzkomforts unter Beibehaltung der typischen Geleigenschaften, wie z.B. der Aufnahme von Scherkräften möglich macht, bedeutet eine deutliche technische Verbesserung.A Gel mass, which significantly reduces the weight, the heat capacity and the Einsitzkomforts while retaining the typical gel properties, e.g. of the Absorption of shear forces possible makes a significant technical improvement.

Die für die erfindungsgemäß vorgesehene Gellage zu verwendenden Gelmassen sollten die vorstehend genannten Nachteile vermeiden und die typischen vorteilhaften Geleigenschaften mit einem niedrigen spezifischen Gewicht einer insgesamt niedrigeren Wärmeleitfähigkeit sowie guter Haltbarkeit und dauerhaft gleich bleibenden Gebrauchsmustereigenschaften verbinden. Es ist daher vorteilhaft, wenn die Gellage elastische Mikrohohlkugeln als Füllstoff enthält, wobei die Mikrohohlkugeln aus polymerem Material, vorzugsweise Polyolefin bestehen und mit einer Deckschicht aus einem anorganischen Material, vorzugsweise Calciumkarbonat, beschichtet sind.The for the Gellage provided according to the invention Gel masses to be used should have the disadvantages mentioned above avoid and the typical favorable gel properties with a low specific weight of an overall lower thermal conductivity as well as good durability and permanently consistent utility model properties connect. It is therefore advantageous if the gel layer is elastic Hollow microspheres as filler contains wherein the hollow microspheres of polymeric material, preferably polyolefin consist and with a cover layer of an inorganic material, preferably calcium carbonate coated.

Es ist vorteilhaft, wenn die Mikrohohlkugeln einen Durchmesser von 10 μm bis 150 μm besitzen, und wenn der Anteil der Mikrohohokugeln in dem Gelwerkstoff 0,1–10 Gew.-% beträgt.It is advantageous if the hollow microspheres have a diameter of 10 μm to Have 150 microns, and if the proportion of micro-spheres in the gel material is 0.1-10% by weight is.

Der Sitzkomfort lässt sich insgesamt noch dadurch verbessern, dass in der Gelmasse grobkörnige Feststoffteilchen verteilt sind, die aus Korkstückchen, Korkmehl, Holzstückchen, Holzspänen, Schaumstoffflocken, Styropor, Textilfasern oder Textilstücken bestehen, deren Durchmesser vorzugsweise zwischen 0,1 mm und 15 mm liegt.Of the Seating comfort leaves Overall, even better, that in the gel mass coarse-grained solid particles are distributed from cork pieces, Cork flour, pieces of wood, Wood shavings, foam flakes, Styrofoam, textile fibers or textile pieces consist whose diameter preferably between 0.1 mm and 15 mm.

Erfindungsgemäß wird der Einsitz-Komfort durch die obenliegende Polyurethan-Schaumstofflage wesentlich verbessert.According to the invention Single-seat comfort through the overhead polyurethane foam layer essential improved.

In der Zeichnung sind einige als Beispiele dienende Ausführungsformen der Erfindung dargestellt. Es zeigen:In The drawings are a few exemplary embodiments represented the invention. Show it:

1 – im Querschnitt einen Formkörper mit einer unteren Gellage und einer oberen Schaumstofflage; 1 - In cross-section, a shaped body with a lower gel layer and an upper foam layer;

2 – in einer Darstellung gemäß 1 eine mit unteren Ansätzen in Ausdehungskanäle der Gellager eintauchende Schaumstofflage; 2 - in a representation according to 1 a foam layer immersed with lower lugs in expansion channels of the gel bearings;

3 – in einer Darstellung gemäß 2 eine die Gellage seitlich einfassende Schaumstofflage, deren untere Ansätze sich bis auf den Boden der Ausdehnungskanäle erstrecken; und 3 - in a representation according to 2 a Gellage laterally enclosing foam layer, the lower lugs extend to the bottom of the expansion channels; and

4 – in einer Darstellung gemäß 2 eine untere Gellage mit unterschiedlich gestalteten Ausdehnungskanälen. 4 - in a representation according to 2 a lower gel layer with differently shaped expansion channels.

1 zeigt im Querschnitt einen insbesondere als Sitzpolster dienenden Formkörper, mit einer unteren, tragenden, eine untere Auflagefläche 1 bildenden, aus einem Polyurethan-Gel bestehenden Gellage 2, die auf ihrer Oberseite integrale, voneinander über Ausdehnungskanäle 4 beabstandete Auflager 3 aufweist, auf denen eine Polyurethan-Schaumstofflage 6 aufliegt, deren Oberseite 5 durch eine obere Auflage 7 abgedeckt ist. 1 shows in cross section serving in particular as a seat cushion molding, with a lower, supporting, a lower support surface 1 forming, consisting of a polyurethane gel gel layer 2 Integral on their top, from each other via expansion channels 4 spaced supports 3 comprising, on which a polyurethane foam layer 6 rests, whose top 5 through an upper edition 7 is covered.

Bei der in 2 dargestellten abgewandelten Ausführungsform weist die Polyurethan-Schaumstofflage 6 auf ihrer Unterseite integrale Ansätze 6a auf, die in die Ausdehnungskanäle 4 der Gellage 2 eintauchen.At the in 2 illustrated modified embodiment, the polyurethane foam layer 6 integral approaches on its underside 6a on that in the expansion channels 4 the Gellage 2 plunge.

Bei der Ausführungsform gemäß 3 erstrecken sich die integralen Ansätze 6a der Polyurethan-Schaumstofflage 6 bis auf den Boden 8 der Ausdehnungskanäle und können sich auf diesen abstützen. Ferner zeigt 3, dass die Polyurethan-Schaumstofflage 6 die Gellage 2 seitlich vollständig einfasst.In the embodiment according to 3 extend the integral approaches 6a the polyurethane foam layer 6 down to the ground 8th the expansion channels and can be supported on this. Further shows 3 that the polyurethane foam layer 6 the gellation 2 completely enclosed laterally.

4 zeigt eine weiterhin abgewandelte Ausführungsform, die quasi eine Kombination der Ausführungsformen gemäß den 1 und 3 darstellt. Denn hier sind einerseits Ausdehnungskanäle 4 vorgesehen, die frei von unteren Ansätzen der Polyurethan-Schaumstofflage 6 sind, die aber mit integralen Ansätzen 6a in Ausdehnungskanäle geringerer Tiefe und kleineren Querschnitts eintaucht, wobei sich diese Ansätze 6a auf dem Boden 8 dieser Ausdehnungskanäle abstützen können. 4 shows a further modified embodiment, which is a combination of the embodiments according to the quasi 1 and 3 represents. Because here are on the one hand expansion channels 4 provided, which are free from lower approaches of the polyurethane foam layer 6 are, but with integral approaches 6a immersed in expansion channels of lesser depth and smaller cross-section, with these approaches 6a on the ground 8th can support these expansion channels.

Die Gellage 2 kann nach Abziehen einer zusammen mit ihr hergestellten Folie mit der Polyurethan-Schaumstofflage 6 verklebt sein. Alternativ könnte die Polyurthan-Schaumstofflage auch über einen aufgetragenen Kleber mit den Auflagern der Gellage verklebt sein.The Gellage 2 can after removal of a film produced with her with the polyurethane foam layer 6 be glued. Alternatively, the Polyurthan foam layer could also be glued over an applied adhesive to the supports of the gel layer.

Bei allen Ausführungsformen ist die obere Auflage 7 ein Abstandsgewirk, das aus zwei durch Abstandsfäden miteinander verbundenen textilen Flächen besteht.In all embodiments, the upper edition 7 a spacer fabric consisting of two textile surfaces interconnected by spacer threads.

Die wesentlichen Vorteile des erfindungsgemäßen Formkörpers sind zu sehen in dem erhöhten Sitzkomfort bei verringerter Bauhöhe, den günstigen Belüftungseigenschaften, der guten Druckverteilung, einem weichen Einsitzverhalten und in dem reduzierten Gewicht im Vergleich mit einem reinen Gelsitz.The Significant advantages of the molding according to the invention can be seen in the increased seating comfort at reduced height, the favorable ventilation properties, the good pressure distribution, a soft seated and in the reduced weight compared to a pure gel seat.

Claims (24)

Formkörper, insbesondere für ein Sitzpolster, mit einer tragenden, unteren Auflagefläche (1) und einer oberen Auflage (7), dadurch gekennzeichnet, dass die Auflagefläche (1) eine aus einem Polyurethan-Gel bestehende Gellage (2) ist, die auf Ihrer Oberseite integrale, voneinander über Ausdehnungskanäle (4) beabstandete Auflager (3) aufweist, auf denen eine Polyurethan-Schaumstofflage (6) aufliegt, deren Oberseite (5) durch die obere Auflage (7) abgedeckt ist.Shaped body, in particular for a seat cushion, with a supporting, lower support surface ( 1 ) and an upper edition ( 7 ), characterized in that the bearing surface ( 1 ) a gellage consisting of a polyurethane gel ( 2 ), which are integral on their top, from each other via expansion channels ( 4 ) spaced supports ( 3 ), on which a polyurethane foam layer ( 6 ) rests whose top ( 5 ) through the upper support ( 7 ) is covered. Formkörper nach Anspruch 1, dadurch gekennzeichnet, dass die Auflager (3) im Bereich der bei Belastung auftretenden Druckspitzen einen engeren Abstand voneinander aufweisen.Shaped body according to claim 1, characterized in that the supports ( 3 ) have a closer distance from each other in the area of the pressure peaks occurring under load. Formkörper nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die Auflager (3) säulenförmig ausgebildet sind.Shaped body according to claim 1 or 2, characterized in that the supports ( 3 ) are columnar. Formkörper nach Anspruch 1, 2 oder 3, dadurch gekennzeichnet, dass die Polyurethan-Schaumstofflage (6) auf ihrer Unterseite integrale Ansätze (6a) aufweist, die in die Ausdehnungskanäle (4) der Gellage (2) eintauchen.Shaped body according to claim 1, 2 or 3, characterized in that the polyurethane foam layer ( 6 ) on its underside integral approaches ( 6a ), which in the expansion channels ( 4 ) of the Gellage ( 2 ) immerse. Formkörper nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die obere Auflage (7) ein Abstandsgewirk ist, das aus zwei durch Abstandsfäden miteinander verbundenen textilen Flächen besteht.Shaped body according to one of the preceding claims, characterized in that the upper support ( 7 ) is a Abstandsgewirk consisting of two interconnected by spacer threads textile surfaces. Formkörper nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Polyurethan-Schaumstofflage (6) die Gellage (2) ganz oder teilweise seitlich einfasst.Shaped body according to one of the preceding claims, characterized in that the polyurethane foam layer ( 6 ) the gellation ( 2 ) in whole or in part on the sides. Formkörper nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Gellage (2) nach Abziehen einer zusammen mit ihr hergestellten Folie mit der Polyurethan-Schaumstofflage (6) verklebt ist.Shaped body according to one of the preceding claims, characterized in that the gel layer ( 2 After removing a film produced with her with the polyurethane foam layer ( 6 ) is glued. Formkörper nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass die Polyurethan-Schaumstofflage (6) über einen aufgetragenen Kleber mit den Auflagern (3) der Gellage (2) verklebt ist.Shaped body according to one of claims 1 to 6, characterized in that the polyurethane foam layer ( 6 ) over an applied adhesive with the supports ( 3 ) of the Gellage ( 2 ) is glued. Formkörper nach einem der Ansprüche 4 bis 8, dadurch gekennzeichnet, dass sich die integralen Ansätze (6a) der Polyurethan-Schaumstofflage (6) bis auf den Boden (8) der Ausdehnungskanäle (4) erstrecken.Shaped body according to one of claims 4 to 8, characterized in that the integral approaches ( 6a ) of the polyurethane foam layer ( 6 ) down to the ground ( 8th ) of the expansion channels ( 4 ). Formkörper nach Anspruch 9, dadurch gekennzeichnet, dass sich die Ansätze (6a) der Polyurethan-Schaumstofflage (6) auf dem Boden (8) der Ausdehnungskanäle (4) abstützen.Shaped body according to claim 9, characterized in that the lugs ( 6a ) of the polyurethane foam layer ( 6 ) on the ground ( 8th ) of the expansion channels ( 4 ). Formkörper nach einem der vorgenannten Ansprüche, dadurch gekennzeichnet, dass die chemische Struktur des Polyurethan-Gels aus langen Polymer-Fäden und nur wenigen Verkettungen ohne Verwendung zugesetzter Weichmacher besteht.moldings according to one of the preceding claims, characterized that the chemical structure of the polyurethane gel consists of long polymer threads and only a few links without the use of added plasticizers consists. Formkörper nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass für das Gel ein untervernetztes Polyurethan auf der Basis von Polyolen und Polyisocyanaten oder Polyethern und Polyisocyanaten eingesetzt ist.moldings according to one of the claims 1 to 10, characterized in that the gel is an undercrosslinked Polyurethane based on polyols and polyisocyanates or Polyethers and polyisocyanates is used. Formkörper nach Anspruch 12, dadurch gekennzeichnet, dass die Gelmassen mit Rohstoffen einer Isocyanat-Funktionalität der Polyolkomponente von mindestens 5,2 vorzugsweise von mindestens 6,5, insbesondere von mindestens 7,5 hergestellt sind.moldings according to claim 12, characterized in that the gel masses with Raw materials of an isocyanate functionality of the polyol component of at least 5.2, preferably of at least 6.5, in particular of at least 7.5 are made. Formkörper nach Anspruch 12 oder 13, dadurch gekennzeichnet, dass die Polyolkomponente zur Herstellung des Gels aus einem Gemisch aus a) einem oder mehreren Polyolen mit Hydroxylzahlen unter 112 und b) einem oder mehreren Polyolen mit Hydroxyzahlen im Bereich von 112 bis 600 besteht, wobei das Gewichtsverhältnis der Komponente a) zu Komponente b) zwischen 90:10 und 10:90 liegt, die Isocyanat-Kennzahl des Reaktionsgemisches im Bereich von 15 und 60 liegt und das Produkt aus Isocyanat-Funktionalität und Funktionalität der Polyolkomponente mindestens 6 beträgt.moldings according to claim 12 or 13, characterized in that the polyol component for Preparation of the gel from a mixture of a) one or more Polyols with hydroxyl numbers below 112 and b) one or more Polyols having hydroxyl numbers in the range of 112 to 600, in which the weight ratio component a) to component b) is between 90:10 and 10:90, the isocyanate number of the reaction mixture in the range of 15 and 60 is and the product of isocyanate functionality and functionality of the polyol component is at least 6. Formkörper nach Anspruch 12 oder 13, dadurch gekennzeichnet, dass die Polyolkomponente zur Herstellung des Gels aus einem oder mehreren Polyolen mit einem Molekulargewicht zwischen 1000 und 12000 und einer OH-Zahl zwischen 20 und 1 12 besteht, wobei das Produkt der Funktionalitäten der polyurethanbildenden Komponenten mindestens 5 beträgt und die Isocyanat-Kennzahl zwischen 15 und 60 liegt.moldings according to claim 12 or 13, characterized in that the polyol component for Preparation of the gel from one or more polyols with a Molecular weight between 1000 and 12000 and an OH number between 20 and 1 12, wherein the product of the functionalities of the polyurethane-forming Components is at least 5 and the isocyanate index is between 15 and 60. Formkörper nach einem der Ansprüche 12 bis 15, dadurch gekennzeichnet, dass man als Isocyanate zur Gelherstellung solche der Formel Q (NCO) einsetzt, in der n für 2 bis 4 steht und Q einen aliphatischen Kohlenwasserstoffrest mit 8 bis 18 C-Atomen, einen cycloaliphatischen Kohlenwasserstoffrest mit 4 bis 15 C-Atomen, einen aromatischen Kohlenwasserstoffrest mit 6 bis 15 C-Atomen oder einen araliphatischen Kohlenwasserstoffrest mit 8 bis 15 C-Atomen bedeutet.moldings according to one of the claims 12 to 15, characterized in that as isocyanates for gel production those of the formula Q (NCO), in which n is 2 to 4 and Q is a aliphatic hydrocarbon radical having 8 to 18 carbon atoms, a cycloaliphatic hydrocarbon radical having 4 to 15 C atoms, an aromatic hydrocarbon radical having 6 to 15 carbon atoms or an araliphatic hydrocarbon radical with 8 to 15 carbon atoms means. Formkörper nach einem der Ansprüche 12 bis 16, dadurch gekennzeichnet, dass das Polyurethan mit Isocyanaten in reiner Form oder mit urethanisierten, allophanisierten, biurethisierten oder funktionell entsprechend modifizierten Isocyanaten hergestellt ist.moldings according to one of the claims 12 to 16, characterized in that the polyurethane with isocyanates in pure form or with urethanized, allophanised, biuretted or functionally prepared according to modified isocyanates is. Formkörper nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Gellage (2) elastische Mikrohohlkugeln als Füllstoff enthält.Shaped body according to one of the preceding claims, characterized in that the gel layer ( 2 ) contains elastic hollow microspheres as filler. Formkörper nach Anspruch 18, dadurch gekennzeichnet, dass die Mikrohohlkugeln aus polymeren Material, vorzugsweise Polyolefin bestehen.moldings according to claim 18, characterized in that the hollow microspheres made of polymeric material, preferably polyolefin. Formkörper nach Anspruch 18 oder 19, dadurch gekennzeichnet, dass die Mikrohohlkugeln mit einer Deckschicht aus einem anorganischen Material, vorzugsweise Calciumcarbonat, beschichtet sind.moldings according to claim 18 or 19, characterized in that the hollow microspheres with a cover layer of an inorganic material, preferably Calcium carbonate, coated. Formkörper nach Anspruch 18, 19 oder 20, dadurch gekennzeichnet, dass die Mikrohohlkugeln einen Durchmesser von 10 μm bis 150 μm aufweisen.moldings according to claim 18, 19 or 20, characterized in that the hollow microspheres a Diameter of 10 μm up to 150 μm exhibit. Formkörper nach einem der Ansprüche 18 bis 21, dadurch gekennzeichnet, dass der Anteil der Mikrohohlkugeln in dem Gelwerkstoff 0,1 bis 10 Gew.-% beträgt.moldings according to one of the claims 18 to 21, characterized in that the proportion of hollow microspheres in the gel material is 0.1 to 10 wt .-%. Formkörper nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass in der Gelmasse grobkörnige Feststoffteilchen verteilt sind, die aus Korkstückchen, Korkmehl, Holzstückchen, Holzspänen, Schaumstoffflocken, Styropor, Textilfasern oder Textilstücken bestehen.moldings according to one of the preceding claims, characterized that in the gel mass coarse-grained Particles of cork, cork flour, pieces of wood, wood shavings, foam flakes, Styrofoam, textile fibers or textile pieces exist. Formkörper nach Anspruch 23, dadurch gekennzeichnet, dass der Durchmesser der Feststoffteilchen zwischen 0,1 und 15 mm liegt.moldings according to claim 23, characterized in that the diameter of the Solid particles between 0.1 and 15 mm.
DE10254678A 2002-11-22 2002-11-22 Shaped body, in particular for a seat cushion Expired - Fee Related DE10254678B4 (en)