DE1021326B - Process for the simultaneous permanent flameproof and water-repellent finishing of fibrous material, especially textiles - Google Patents
Process for the simultaneous permanent flameproof and water-repellent finishing of fibrous material, especially textilesInfo
- Publication number
- DE1021326B DE1021326B DEQ350A DEQ0000350A DE1021326B DE 1021326 B DE1021326 B DE 1021326B DE Q350 A DEQ350 A DE Q350A DE Q0000350 A DEQ0000350 A DE Q0000350A DE 1021326 B DE1021326 B DE 1021326B
- Authority
- DE
- Germany
- Prior art keywords
- water
- treatment bath
- parts
- textiles
- fibrous material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
DEUTSCHESGERMAN
Die Verwendung von Metalloxyden, insbesondere Antimontrioxyd, zusammen mit fixierend wirkenden Substanzen zum Flammenfestmachen von Textilien ist bekannt. Als Fixierungsmittel sind insbesondere chlorhaltige organische Substanzen, wie z. B. chlorierte Paraffine oder Naphthaline, Chlorkautschuk, Polyvinylchlorid od. dgl., vorgeschlagen worden. Ferner sind auch Harnstoff-, Cumaron- und andere Harze bzw. deren Vorkondensationsprodukte für diesen Zweck zusätzlich angegeben worden. Die Fixierungsmittel werden, soweit sie löslich sind, meist in Lösungsmitteln gelöst und dann zugemischt. Es ist auch bekannt, sie unter Zuhilfenahme von Seifen, Netzmitteln und ähnlichen Substanzen zu dispergieren, wobei Stabilisatoren, wie Casein, Leim od. dgl., zugesetzt werden. Es wurde ferner der Zusatz von Säuren, wie beispielsweise Phosphorsäure, vorgeschlagen, wenn es sich darum handelte, die obengenannten Vorkondensate beim Trocknen der behandelten Textilien auszukondensieren. The use of metal oxides, especially antimony trioxide, together with fixing agents Substances for making textiles flame-proof are known. As a fixative are in particular organic substances containing chlorine, such as B. chlorinated paraffins or naphthalenes, chlorinated rubber, polyvinyl chloride or the like, has been proposed. Furthermore, urea, coumarone and other resins or their precondensation products have also been specified for this purpose. The fixatives are, as far as they are soluble, mostly dissolved in solvents and then mixed in. It is also known to disperse them with the help of soaps, wetting agents and similar substances, whereby Stabilizers, such as casein, glue or the like., Are added. There was also the addition of acids, such as for example phosphoric acid, suggested when it came to the above-mentioned precondensates condense out when the treated textiles dry.
Alle diese bekannten Verfahren bringen jedoch zahlreiche schwerwiegende Nachteile mit sich. Es ist zwar möglich, infolge der verhältnismäßig großen, beispielsweise bis zu 50% betragenden Mengen an Metalloxyden und Fixierungsmitteln, den damit behandelten Geweben neben der Flammenfestigkeit auch eine gewisse Wasserdichtigkeit zu erteilen, jedoch kann eine gute wasserabstoßende Wirkung nicht oder nur durch eine Nachbehandlung in einem zweiten Bad erzielt werden, wodurch wiederum der Flammenfesteffekt beeinträchtigt wird, da in diesem Fall die zum Wasserabstoßendmachen benutzten brennbaren Substanzen mehr auf als in dem Textilmaterial verteilt sind und so die Brennbarkeit gerade an seiner Oberfläche begünstigen. However, all of these known methods yield numerous serious disadvantages with it. Although it is possible due to the relatively large, for example Up to 50% amounts of metal oxides and fixatives, those treated with them To give fabrics a certain waterproofness in addition to the flame resistance, however, a good water-repellent effect is not achieved or only achieved by a subsequent treatment in a second bath which in turn deteriorates the flameproof effect, since in this case they make water repellent used flammable substances more than are distributed in the textile material and thus favoring the flammability precisely on its surface.
Bei der Beschreibung der bekannten Verfahren wurde vielfach der Standpunkt vertreten, daß man eine Mindestmenge an von den chlorierten Produkten abzugebender Salzsäure benötigt, um den gewünschten Flammenfesteffekt zu erzielen. Es wurden daher verhältnismäßig große Mengen der chlorierten Produkte, meistens 30 bis 50, mindestens aber 10%, bezogen auf das Behandlungsbad, vorgesehen. Dadurch wird jedoch nicht nur der Nachteil erhalten, daß die mit solchen Mitteln behandelten Textilien einen steifen und oft auch klebrigen Griff erhalten, sondern es bereitet auch Schwierigkeiten, die auch bei gewöhnlicher Temperatur während längerer Zeit stattfindende Salzsäureabspaltung, welche zu einer Verringerung der Reißfestigkeit der behandelten Textilien führt, zu kompensieren. Man benötigt dazu sehr große Mengen entsprechend befähigter Substanzen, deren Anwesenheit wiederum die Flammenfestigkeit und insbesondere den Griff der behandelten Textilien ungünstig beein-Verfahren zur gleichzeitigen beständigen flammenfesten und wasserabstoßendenIn the description of the known processes, the position has often been taken that one a minimum amount of hydrochloric acid to be given off by the chlorinated products is required to achieve the desired To achieve flame retardant effect. There were therefore relatively large quantities of the chlorinated products, usually 30 to 50, but at least 10%, based on the treatment bath, provided. This will however not only get the disadvantage that the textiles treated with such agents have a stiff and often also get a sticky grip, but it also causes difficulties, even at ordinary temperature Hydrochloric acid splitting off over a long period of time, which leads to a reduction in the tear strength of the treated textiles leads to compensate. You need very large quantities for this appropriately capable substances, their presence in turn the flame resistance and in particular the handle of the treated textiles adversely affect the simultaneous permanent flameproof and water-repellent
Ausrüstung von faserigem. Material,Finishing of fibrous. Material,
insbesondere Textilienespecially textiles
Anmelder:
Dr. Kurt Quehl, Speyer/Rhein, Burgstr. 6Applicant:
Dr. Kurt Quehl, Speyer / Rhine, Burgstr. 6th
Dr. Kurt Quehl, Speyer/Rhein,
ist als Erfinder genannt wordenDr. Kurt Quehl, Speyer / Rhine,
has been named as the inventor
flußt. Werden bei der Flammenfestausrüstung von Textilien gleichzeitig Kunstharzkondensate benutzt und die Bäder sauer eingestellt, so dient die saure Reaktion lediglich zur Förderung der Weiterkondensation des Kunstharzes auf den Textilien. Es treten hierbei erhebliche Nachteile auf, weil bei den bei der Trocknung anzuwendenden hohen Kondensationstemperaturen Faserschädigungen auftreten. Schließlich ist bei allen Verfahren, die eine beständige Flammenfestausrüstung von Textilien anstreben, nach der Einwirkung einer Flamme ein verhältnismäßig langdauerndes Nachglimmen festzustellen. flows. Are synthetic resin condensates used at the same time for the flame retardant finish of textiles and the baths are set to be acidic, the acidic reaction only serves to promote further condensation of the synthetic resin on the textiles. There are considerable disadvantages here because of the drying high condensation temperatures to be applied, fiber damage occurs. Finally is at all processes that aim to give textiles a permanent flame retardant finish after exposure detect a relatively long afterglow of a flame.
Es ist schließlich ein Verfahren zum beständigen Flammenfestmachen von Textilien unter Verwendung eines oder mehrerer als Flammenschutzmittel bekannter Metalloxyde, wie Antimontrioxyd, Zinnoxyd, Titandioxyd od. dgl., und von nachchloriertem Polyvinylchlorid vorgeschlagen worden, bei welchem ein auf einen pH-Wert von mindestens 7 eingestelltes Behandlungsbad, das geringe Mengen (in der Größenordnung von 5%) an nachchloriertem Polyvinylchlorid mit einem Chlorgehalt von mindestens 60% enthält, verwendet wird. Bei diesem Verfahren kann zum gleichzeitigen Wasserdichtmachen ein Behandlungsbad verwendet werden, das außer den vorgenannten Bestandteilen wasserabstoßend machende Stoffe, wie Fettsäuren, Seifen oder Wachs- bzw. Paraffinemulsionen, enthält, und gegebenenfalls kann noch eine Nachbehandlung der Ware in einer Ameisensäure oder essigsaure Tonerde enthaltenden Flotte vorgenommen werden.Finally, it is a method of resistant flame mooring textiles using one or more as a flame retardant known metal oxides, such as antimony trioxide, tin oxide, od titanium dioxide. The like., And has been proposed by post-chlorinated polyvinyl chloride, in which a to a pH value of at least 7 adjusted treatment bath containing small amounts (of the order of 5%) of post-chlorinated polyvinyl chloride with a chlorine content of at least 60% is used. In this process, a treatment bath can be used for simultaneous waterproofing, which, in addition to the aforementioned components, contains substances that make water repellant, such as fatty acids, soaps or wax or paraffin emulsions, and, if necessary, the goods can also be post-treated in a liquor containing formic acid or acetic acid clay be made.
Zweck der Erfindung ist die Schaffung eines verbesserten Verfahrens zur gleichzeitigen beständigen flammenfesten und wasserabstoßenden AusrüstungThe purpose of the invention is to provide an improved Process for the simultaneous permanent flame-retardant and water-repellent finish
709 846/455709 846/455
von faserigen Materialien, insbesondere Textilien, Papier, Leder od. dgl., in einem Bad. Ein weiterer Zweck der Erfindung besteht darin, ein Verfahren zu schaffen, bei welchem neben der gleichzeitigen beständigen flammenfesten und der wasserabstoßenden Ausrüstung von Textilmaterial der textile Charakter und die Reißfestigkeit der behandelten Ware erhalten bleiben. Schließlich soll das sonst nach dem Einwirken einer Flamme meist auftretende Nachglimmen auf ein Mindestmaß herabgesetzt werden.of fibrous materials, in particular textiles, paper, leather or the like, in a bathroom. Another The purpose of the invention is to create a method in which, in addition to the simultaneous permanent Flameproof and the water-repellent finish of textile material of the textile character and the tear strength of the treated goods are retained. After all, this should otherwise be done after it has taken effect Afterglow that usually occurs with a flame can be reduced to a minimum.
Unter einer »beständigen« Flammenfestausrüstung wird in diesem Zusammenhang verstanden, daß die Flammenfestigkeit auch nach Einwirkung von Wasser. Waschen und Witterungseinflüssen weitgehend erhalten bleibt.In this context, "permanent" flame retardant equipment is understood to mean that the Flame resistance even after exposure to water. Wash and weather conditions largely preserved remain.
Gemäß der Erfindung wird das faserige Material, insbesondere Textilmaterial, mit einem sauren Behandlungsbad, das durch Zusammenmischen einer Lösung oder Dispersion wasserabstoßend wirkenderAccording to the invention, the fibrous material, in particular textile material, is treated with an acidic treatment bath, the water-repellent effect by mixing a solution or dispersion together
Anwendung solcher geringen Mengen die oben geschilderten Nachteile der bekannten Verfahren weitgehend vermieden werden können. Auch vom wirtschaftlichen Standpunkt aus besitzt die Verwendung geringer Mengen an Fixierungsmittel erhebliche Vorteile. Use of such small amounts largely eliminates the disadvantages of the known processes outlined above can be avoided. Also from the economic point of view, the use has small amounts of fixative have considerable advantages.
Es ist ferner möglich, zusätzlich zu dem nachchlorierten Polyvinylchlorid noch andere Fixierungsmittel, insbesondere chlorhaltige Substanzen, wie Chlorparaffin oder Chlorkautschuk, zu benutzen. Auch in diesemFall ist es zweckmäßig, nur geringe Mengen, z. B. 2 bis 5%, auf das Behandlungsbad bezogen, von den genannten anderen Fixierungsmitteln zu verwenden. It is also possible, in addition to the post-chlorinated polyvinyl chloride, to use other fixing agents, in particular chlorine-containing substances, such as Chlorinated paraffin or chlorinated rubber. In this case, too, it is advisable to use only small amounts z. B. 2 to 5%, based on the treatment bath, of the other fixatives mentioned to be used.
X5 Es ist bekannt, daß man zu Mitteln zum Flammenfestmachen von Textilien auch Zinkborat, das als schwer wasserlösliches Pulver angewendet wird, zusetzen kann, um dadurch das Naehglimmen herab- X 5 It is known that zinc borate, which is used as a poorly water-soluble powder, can also be added to agents for making textiles flame-resistant, in order to reduce the smoldering.
Dispersionen in Mengen von 1 bis 3% der Gesamtmenge zugegeben werden kann, wodurch eine überraschende Glimmfestigkeit erzielt wird.Dispersions in amounts of 1 to 3% of the total amount can be added, creating a surprising Corona resistance is achieved.
Falls gefärbte Ware ausgerüstet werden soll, können dem Behandlungsbad auch Pigmentfarbstoffe zugesetzt werden, um den durch das flammensichermachendc Metalloxyd, wie Antimontrioxyd, bedingten Weißgehalt zu überdecken. Durch Erhöhung des Gehaltes If colored goods are to be finished, pigment dyes can also be added to the treatment bath to cover the whiteness caused by the flame-proofing metal oxide such as antimony trioxide. By increasing the salary
zusetzen. Obgleich Zinkborat in Säuren weitgehend Substanzen, wie Paraffine, Wachse, Fettsäuren, und 20 löslich ist, wurde überraschenderweise gefunden, daß
einer Lösung nachchlorierten Polyvinylchlorids in es auch den erfindungsgemäß anzuwendenden sauren
organischen Lösungsmitteln mit einer organische
Säure und Stabilisatoren, wie Gummiarabicum, Albumin, Leim, Methylcellulose, sowie Aluminium- oder
Zirkonsalze enthaltenden wässerigen Lösung und 25
darauffolgendes Einbringen eines oder mehrerer als
Flammenschutzmittel bekannter Metalloxyde, wie insbesondere Antimontrioxyd, hergestellt worden ist,
imprägniert und anschließend getrocknet. Als organische Säure für die Einstellung des Bades kommt 30 an Pigmentfarbstoffen ist es auch möglich, ungefärbte
insbesondere Ameisensäure oder Essigsäure in Frage. Waren mit den sauren Dispersionen gemäß der Erfindung auszurüsten und zu färben. Auch bakterienhemmende
Substanzen, wie Chlorphenol od. dgl., können ebenso wie griffgebende Appreturmittel zuWirkung erzielen kann, wenn man dafür sorgt, daß 35 gesetzt werden. Auf diese Weise können also je nach
die wirksamen Substanzen zu gleicher Zeit Gelegen- Wunsch nicht nur vorgefärbte Textilien behandeltto add. Although zinc borate is largely soluble in acids such as paraffins, waxes, fatty acids, and 20, it was surprisingly found that a solution of post-chlorinated polyvinyl chloride in the acidic organic solvents to be used according to the invention with an organic
Acid and stabilizers such as gum arabic, albumin, glue, methyl cellulose, as well as aluminum or
Aqueous solution containing zirconium salts and 25
subsequent introduction of one or more than
Flame retardants of known metal oxides, such as in particular antimony trioxide, have been produced,
impregnated and then dried. As an organic acid for the setting of the bath, pigment dyes can also be used, in particular uncolored formic acid or acetic acid. Goods to be equipped with the acidic dispersions according to the invention and to be colored. Bacteria-inhibiting substances such as chlorophenol or the like can also have an effect, as can handle-giving finishing agents, if one ensures that 35 are set. In this way, depending on the active substances, not only pre-dyed textiles can be treated at the same time on occasion
werden, sondern es können auch Rohwaren in einem einzigen Bade gefärbt, beständig flammenfest, wasserabstoßend bzw. wasserdicht und fäulnisfest bei gleichstellung, daß man sauer reagierende beständige 40 zeitiger Beeinflussung des Griffes ausgerüstet werden. Flammenschutzmittel zusammen mit wasserabstoßend Die Erfindung wird nachstehend an Hand einigerraw materials can also be dyed in a single bath, permanently flame-retardant, water-repellent or waterproof and rot-proof with the same equation that you are equipped with acidic reacting resistant 40 times influencing the handle. Flame retardant along with water repellent The invention will be explained below with reference to some
Die Erfindung ist auf die Erkenntnis gegründet, daß man einen ausgezeichneten beständigen Flammenf esteffekt und zugleich eine sehr gute wasserabstoßendeThe invention is based on the knowledge that one can have an excellent persistent flame f esteffekt and at the same time a very good water-repellent
heit haben, in die Faser bzw. das zu behandelnde Gewebe in möglichst feinzerteilter Form einzudringen. Die Erfindung stützt sich auf die überraschende Festwirkenden Substanzen, wie Paraffin u.dgl.. verwenden kann, ohne die textlien Eigenschaften oder die Flammfestigkeit des behandelten Gutes zu beeinträchtigen. Es war auch nicht vorauszusehen, daß es durch Anwendung von Stabilisatoren der angegebenen Art gelingt, die heterogene Dispersion, die neben anorganischen Stoffen, wie den genannten Metalloxyden und gegebenenfalls Pigmenten, wasserunlösliche Lösungs-have the ability to penetrate the fiber or the tissue to be treated in as finely divided form as possible. The invention is based on the surprising solid-acting substances such as paraffin and the like .. use can without impairing the textile properties or the flame resistance of the treated goods. It was also not foreseeable that the use of stabilizers of the type indicated would lead to the heterogeneous dispersion, which in addition to inorganic substances such as the metal oxides mentioned and possibly pigments, water-insoluble solutions
Beispiele näher erläutert, wobei die angegebenen Teile und Prozentsätze Gewichtsteile bzw. Gewichtsprozente bezeichnen.Examples explained in more detail, the specified parts and percentages being parts by weight and percentages by weight describe.
0,5 bis 1,5 Teile Gummiarabicum und 1.5 bis 3 Teile Blutalbumin wurden in der fünffachen Menge Wasser gelöst, und es wurden langsam 0,5 Teile Ameisenmittel, wasserunlösliche chlorierte organische Ver- 50 säure und danach 3 bis 5 Teile ameisensaure Tonerde, bindungen und Paraffin od. dgl. enthält, in praktisch 11° Be, und schließlich 15 bis 20 Teile Wasser zuverwendbare Form zu bringen. 0.5 to 1.5 parts of gum arabic and 1.5 to 3 parts of blood albumin were added to five times the amount of water dissolved, and slowly 0.5 parts of formic acid, water-insoluble chlorinated organic acid and then 3 to 5 parts of formic alumina, Bonds and paraffin or the like. Contains, in practically 11 ° Be, and finally 15 to 20 parts of water to bring usable form.
Es wurde nun überraschenderweise gefunden, daßIt has now surprisingly been found that
man stabile, d. h. schwer sedimentierende saure Disone stable, d. H. heavily sedimenting acidic dis
gegeben. Daneben wurde eine zweite Lösung aus 4 bis 6 Teilen nachchloriertem Polyvinylchlorid, 0,5 Teilen Pentachlorphenol und 2 bis 3 Teilen Paraffin persionen dadurch erhalten kann, daß man zuerst alle 55 in einem Lösungsmittelgemisch aus 8 bis 12 Teilen emulgierbaren Bestandteile, wie Paraffine. Wachse. Aceton und 22 bis 18 Teilen Trichloräthylen gelöst. Fettsäuren, nachchloriertes Polyvinylchlorid, in orga- Diese zweite Lösung wurde zu der erstgenannten Lönischen Lösungsmitteln, in einer organische Säure sung unter gutem Rühren zugefügt, und danach wur- und Stabilisatoren enthaltenden wässerigen Phase den 12 bis 15 Teile Antimontrioxyd, 1 bis 3 Teile emulgiert und dann in der erhaltenen stabilen Emiil- 60 Zinkcarbonat, das in einer doppelten Menge Wasser sion mit ihrem hohen Tragevermögen die gröber aufgeschlämmt war, und 8 bis 12 Teile eines olivdispersen Metalloxydteilchen dispergiert. grünen Pigmentfarbstoffes langsam zugesetzt.given. In addition, a second solution of 4 to 6 parts post-chlorinated polyvinyl chloride, 0.5 Parts of pentachlorophenol and 2 to 3 parts of paraffin persions can be obtained by first all 55 in a solvent mixture of 8 to 12 parts emulsifiable ingredients such as paraffins. Waxes. Acetone and 22 to 18 parts of trichlorethylene dissolved. Fatty acids, post-chlorinated polyvinyl chloride, in organic This second solution became the first-mentioned Lönische Solvents, added in an organic acid solution with thorough stirring, and then was and the aqueous phase containing stabilizers, the 12 to 15 parts of antimony trioxide, 1 to 3 parts emulsified and then in the obtained stable Emiil- 60 zinc carbonate, which in a double amount of water sion with its high carrying capacity which was more coarsely slurried, and 8 to 12 parts of an olive dispersion Metal oxide particles dispersed. green pigment added slowly.
Gemäß einer bevorzugten Ausführungsform de: Nachdem die Mischung zur weiteren Homogenisie-According to a preferred embodiment de: After the mixture for further homogenization
Erfindung wird das als Fixierungsmittel dienende rung durch eine Hurrelmaschine gegeben worden war. nachchlorierte Polyvinylchlorid in einer Menge von 3 65 wurde sie auf einem Foulard zur Ausrüstung eines bis 7, vorzugsweise 5% des Behandlungsbades ver- entsprechend vorgefärbten Netzes verwendet, wobei wendet. Es wurde nämlich gefunden, daß viel geringere der Abquetschdruck so eingestellt wurde, daß das Netz Mengen an Fixierungsmittel, als sie bei den bekannten ungefähr 100% seines Gewichts von dem Behandlungs-Verfahren angewendet werden, genügen, um die ge- bad aufnahm. Danach wurde das Netz auf dem Spannwünschte Wirkung zu erzielen, und daß durch die 7° rahmen getrocknet. Es wurde auf diese Weise nebenInvention is that serving as a fixative tion was given by a whirling machine. post-chlorinated polyvinyl chloride in an amount of 3 6 5 it was used on a padder to equip up to 7, preferably 5% of the treatment bath appropriately pre-dyed net, with turns. Indeed, it has been found that the nip pressure was set much lower so that the net sufficient amounts of fixative than are used in the known approximately 100% of its weight by the treatment process to absorb the damage. After that, the net on the stretching was to achieve the desired effect, and that through the 7 ° frame was dried. It was next this way
einer sehr guten wasserabstoßenden Wirkung eine wetterbeständige Flammenfestigkeit und sehr gute Fäulnisfestigkeit erzielt.a very good water-repellent effect, a weather-resistant flame resistance and very good Rot resistance achieved.
Es wurde eine erste Lösung gemäß Beispiel 1 hergestellt. Darauf wurden zur Herstellung der zweiten Lösung 4 bis 6 Teile nachchloriertes Polyvinylchlorid und 2 bis 3 Teile Chlorparaffin, 7O°/oig, sowie 0,5 Teile Pentachlorphenol und 2 bis 3 Teile Paraffin in einem Lösungsmittelgemisch von 8 bis 12 Teilen Aceton und 22 bis 18 Teilen Trichloräthylen gelöst. Im übrigen wurde das Verfahren gemäß Beispiel 1 befolgt. A first solution according to Example 1 was prepared. They were then used to make the second Solution 4 to 6 parts of post-chlorinated polyvinyl chloride and 2 to 3 parts of chlorinated paraffin, 70%, and 0.5 Parts of pentachlorophenol and 2 to 3 parts of paraffin in a solvent mixture of 8 to 12 parts of acetone and 22 to 18 parts of trichlorethylene dissolved. The procedure of Example 1 was otherwise followed.
Auch auf diese Weise wurde ein ausgezeichnet flammenfestes und wasserabstoßendes Erzeugnis erzielt, das sowohl wetterbeständig als auch fäulnisfestIn this way, too, an excellent flame-retardant and water-repellent product was obtained, that is both weatherproof and rot-proof
Eine Lösung von 0,5 bis 1 Teil Gummiarabicum und 1 bis 2,5 Teilen Blutalbumin in fünffacher Menge Wasser wurde mit 1 bis 1,5 Teilen Ameisensäure und anschließend mit 4 bis 7 Teilen einer Paraffin-Leim-Tonerde-Emulsion versetzt. In diesen Ansatz wurde eine Lösung von 5 bis 7 Teilen nachchloriertem Polyvinylchlorid und 0 bis 2 Teilen Chlorparaffin, 70 °/oig, in einem Lösungsmittelgemisch von 8 Teilen Aceton, 7 Teilen Chloräthylen und 15 Teilen Perchloräthylen vorsichtig eingerührt. Schließlich wurden 12 bis 15 Teile Antimontrioxyd und ungefähr 200 Teile Wasser und 2 Teile eines marineblauen Pigmentfarbstoffes hinzugefügt.A solution of 0.5 to 1 part gum arabic and 1 to 2.5 parts blood albumin in five times the amount Water was mixed with 1 to 1.5 parts of formic acid and then with 4 to 7 parts of a paraffin-glue-clay emulsion offset. A solution of 5 to 7 parts of post-chlorinated polyvinyl chloride was used in this batch and 0 to 2 parts of chlorinated paraffin, 70%, in a solvent mixture of 8 parts of acetone, 7 parts of chloroethylene and 15 parts of perchlorethylene are carefully stirred in. Eventually 12 were up 15 parts of antimony trioxide and approximately 200 parts of water and 2 parts of a navy blue pigment added.
Mit dieser Dispersion wurde auf einem Foulard ein blaugefärbter Berufsköper so behandelt, daß er ungefähr 100% seines Gewichts von dem Behandlungsbad aufnahm. Nach dem Trocknen auf dem Spannrahmen zeigte die Ware eine ausgezeichnete Flammenfestigkeit, wobei gleichzeitig nur ein sehr geringes Nachglimmen feststellbar war. Ebenso wies die Ware eine sehr gute wasserabstoßende Wirkung auf. Die Reißfestigkeit der Ware war um etwa 8°/o erhöht, während die Scheuerfestigkeit ebenfalls wesentlich verbessert war.With this dispersion, a blue-colored professional body was treated on a padder so that it approximately Received 100% of its weight from the treatment bath. After drying on the stenter the goods showed excellent flame resistance, although at the same time only a very low one Afterglow was detectable. The goods also had a very good water-repellent effect. the The tear resistance of the goods was increased by about 8%, while the abrasion resistance was also significantly was improved.
Claims (4)
F. Wein, Spezial- und Hochveredlungsverfahren der Textilien aus Zellulose, 1951, S. 166, 191, 192;Considered publications:
F. Wein, Spezial- und Hochveredlungsverfahren der textiles made of cellulose, 1951, p. 166, 191, 192;
USA.-Patentschrift Nr. 2 536 978.Fischer-Bobsien, Lexicon for the total. Textile finishing and border areas, p. 188;
U.S. Patent No. 2,536,978.