DE102012206490A1 - Multilayer coating comprises lower curtain coating layer comprising pigment, subsequent upper curtain coating layer and top coating layer, where pigment of upper and top coating layer is different from pigment of lower curtain coating layer - Google Patents

Multilayer coating comprises lower curtain coating layer comprising pigment, subsequent upper curtain coating layer and top coating layer, where pigment of upper and top coating layer is different from pigment of lower curtain coating layer Download PDF

Info

Publication number
DE102012206490A1
DE102012206490A1 DE201210206490 DE102012206490A DE102012206490A1 DE 102012206490 A1 DE102012206490 A1 DE 102012206490A1 DE 201210206490 DE201210206490 DE 201210206490 DE 102012206490 A DE102012206490 A DE 102012206490A DE 102012206490 A1 DE102012206490 A1 DE 102012206490A1
Authority
DE
Germany
Prior art keywords
coating
coating layer
pigment
curtain
multilayer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE201210206490
Other languages
German (de)
Inventor
Henri Vaittinen
Simo Rahkonen
Jouni Haavisto
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Valmet Technologies Oy
Original Assignee
Metso Paper Oy
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Metso Paper Oy filed Critical Metso Paper Oy
Priority to DE201210206490 priority Critical patent/DE102012206490A1/en
Publication of DE102012206490A1 publication Critical patent/DE102012206490A1/en
Withdrawn legal-status Critical Current

Abstract

Multilayer coating comprises a lower curtain coating layer (8) comprising at least one pigment, at least subsequent upper curtain coating layer and at least one top coating layer on the next upper curtain coating layer, where the subsequent upper curtain coating layer and the top coating layer contain a pigment, which is different from the pigment of lower curtain-coating layer. An independent claim is also included for multilayer coating of a cardboard or paper sheet, comprising forming a lower coating layer comprising at least one pigment by a curtain coating station, forming at least one subsequent upper coating layer by a curtain coating station and forming at least one top coating layer on the subsequent upper coating layer which is formed by curtain-coating station, by at least one blade- or rod coating station, where at least two curtain coating layers are coated by a multilayer curtain coating station, or by at least two single curtain coating stations.

Description

Technisches Gebiet der ErfindungTechnical field of the invention

Die vorliegende Erfindung betrifft eine Mehrlagenbeschichtung, ein mehrlagenbeschichtetes Blatt und ein Verfahren zum Mehrlagenbeschichten eines Pappe- oder Papierblatts.The present invention relates to a multilayer coating, a multilayer coated sheet, and a method of multilayer coating a paperboard or paper sheet.

Stand der TechnikState of the art

In der Papier- und Pappeindustrie werden Beschichtungen häufig benutzt. Die ISO-Helligkeit eines Basisblatts ist nicht immer für die gewünschte Anwendung geeignet, sodass Mehrlagenbeschichtungen für Basisblätter entwickelt wurden, um die ISO-Helligkeit von mehrlagenbeschichteten Blättern zu verbessern. Wie in 1 gezeigt, enthalten typischerweise Mehrlagenbeschichtungen, die zum Beschichten von Pappen oder Papier verwendet werden, zumindest zwei, manchmal drei separate Beschichtungen (2, 3, 4) auf einer Seite eines Basisblatts (1) mit keiner Rückseitenbeschichtung und für einige Anwendungen wie Kunstkarton auf beiden Seiten des Gewebes. Wie in 2 gezeigt, kann zum Beispiel Faltschachtelkarton der skandinavischen Art (FBB), der typischerweise drei oder vier Lagen umfasst, doppelt beschichtet sein (5) auf der oberen Seite oder doppelt beschichtet sein (5) auf der oberen Seite und einfach beschichtet (6) auf der unteren Seite. Die ISO-Helligkeit des Basisblatts (1), das typischerweise für solche Mehrlagenbeschichtungen verwendet wird, variiert von 45 bis 65%. Während die finale ISO-Helligkeit solcher mehrlagenbeschichteter Blätter, die durch konventionelle Mehrlagenbeschichtungen erhältilich sind, von 78–90% variiert. Um solch eine finale ISO-Helligkeit von 78–90% zu erreichen, müssen deckende Pigmente verwendet werden. Meistens wird TiO2 wegen seines hohen Brechungsindex verwendet. Bedauerlicherweise unterscheidet sich der Farbton von TiO2 von anderen Pigmenten. Deshalb benutzen einige Papierhersteller Farbstoffe, um den unterschiedlichen Farbton von TiO2-Pigmenten in mehrlagenbeschichteten Blättern zu verbergen. Selbst wenn jedoch solche Farbstoffe verwendet werden, wird in einigen Fällen eine gefleckte Oberfläche, die keine einheitliche ISO-Helligkeit wegen des unterschiedlichen Farbtons von TiO2 aufzeigt, beobachtet. Außerdem wird solch eine gefleckte Oberfläche häufig beobachtet, wenn abschließendes Kalendrieren durchgeführt wird.Coatings are commonly used in the paper and board industry. The ISO brightness of a base sheet is not always suitable for the desired application, so multi-layer coatings for base sheets have been developed to improve the ISO brightness of multilayer coated sheets. As in 1 typically, multilayer coatings used to coat paperboard or paper contain at least two, sometimes three separate coatings ( 2 . 3 . 4 ) on one side of a base sheet ( 1 ) with no back coating and for some applications like art cardboard on both sides of the fabric. As in 2 For example, Scandinavian type folding boxboard (FBB), which typically comprises three or four layers, can be double-coated ( 5 ) on the upper side or double coated ( 5 ) on the upper side and simply coated ( 6 ) on the lower side. The ISO brightness of the base sheet ( 1 ), which is typically used for such multilayer coatings, varies from 45 to 65%. While the final ISO brightness of such multilayer coated sheets obtained by conventional multilayer coatings varies from 78-90%. To achieve such a final ISO brightness of 78-90% opaque pigments must be used. Mostly TiO 2 is used because of its high refractive index. Unfortunately, the color of TiO 2 differs from other pigments. Therefore, some paper manufacturers use dyes to hide the different hue of TiO 2 pigments in multilayer coated sheets. However, even if such dyes are used, in some cases, a speckled surface that does not exhibit uniform ISO brightness due to the different hue of TiO 2 is observed. In addition, such spotted surface is often observed when final calendering is performed.

Erweiterte Beschreibung der ErfindungExtended description of the invention

Die Aufgabe der vorliegenden Erfindung ist eine Mehrlagenbeschichtung, ein mehrlagenbeschichtetes Blatt und ein Verfahren zum Mehrlagenbeschichten eines Pappe- oder Papierblatts bereitzustellen, das ermöglicht hohe einheitliche ISO-Helligkeit einer Mehrlagenbeschichtung oder eines mehrlagenbeschichteten Blatts zu erhalten, sogar auf Substraten, die niedrige ISO-Helligkeit aufweisen.The object of the present invention is to provide a multilayer coating, a multilayer coated sheet, and a method of multilayer coating a paperboard or paper sheet which enables high uniform ISO brightness of a multilayer coating or a multilayer coated sheet to be obtained, even on substrates having low ISO brightness ,

Die Erfindung liefert die folgenden Lösungen für Verbesserungen betreffend die Gegenstände, welche sie betrifft:

  • 1. Mehrlagenbeschichtung, die eine untere Curtain-Coating-Schicht, die zumindest ein Pigment umfasst, eine oder mehrere darauffolgende obere Curtain-Coating-Schicht(en) und eine oder mehrere obere Coating-Schicht(en) auf der (den) darauffolgenden oberen Curtain-Coating-Schicht(en) umfasst, wobei die darauffolgende(n) obere(n) Curtain-Coating-Schicht(en) und die obere(n) Coating-Schicht(en) ein Pigment(e), das (die) sich von einem Pigment(en) von der unteren Curtain-Coating-Schicht unterscheidet(en), umfasst(en). Solch eine Mehrlagenbeschichtung weist eine hohe völlig einheitliche ISO-Helligkeit unabhängig von der Art des Substrats, das die Mehrlagenbeschichtung trägt, auf. Ferner, durch Verwenden verschiedener Pigment(e) in Kombination mit den verschiedenen Schichten von der Mehrlagenbeschichtung kann der Fachmann die hohe einheitliche ISO-Helligkeit der Mehrlagenbeschichtung einfach einstellen.
  • 2. Mehrlagenbeschichtung nach Gegenstand 1, wobei die untere Curtain-Coating-Schicht TiO2 als ein Pigment umfasst. Solch eine untere Curtain-Coating-Schicht weist hohe Deckkraft auf und ist eine Voraussetzung um sehr hohe ISO-Helligkeit der Mehrlagenbeschichtung in Kombination mit den folgenden Schichten aufzuweisen.
  • 3. Mehrlagenbeschichtung nach Gegenstand 1 oder 2, ferner umfassend eine untere Blade- oder Rod-Coating-Schicht unterhalb der unteren Curtain-Coating-Schicht. Solch eine untere Blade- oder Rod-Coating-Schicht verbessert die Oberflächenglätte der folgenden Schichten unabhängig von der Art des Substrats, das die Mehrlagenschicht trägt.
  • 4. Mehrlagenbeschichtung nach einem der Gegenstände 1 bis 3, wobei die eine oder mehreren obere(n) Coating-Schicht(en) eine Blade- oder Rod-Coating-Schicht(en) ist (sind). Solch eine obere Blade- oder Rod-Coating-Schicht(en) ermöglicht eine insgesamt verbesserte Oberflächenglätte und Glanz von der Mehrlagenbeschichtung.
  • 5. Mehrlagenbeschichtung nach einem der Gegenstände 1 bis 4, wobei sich ein Pigment(e), das (die) in der (den) darauffolgenden oberen Curtain-Coating-Schicht(en) verwendet ist (sind), von einem Pigment(en), das (die) in der unteren Curtain-Coating-Schicht verwendet ist (sind), im Brechungsindex um mindestens 0,5 Einheiten unterscheidet(en). Solch ein Pigment (solche Pigmente) liefert (liefern) eine gute deckende Abdeckung der Beschichtungsschicht.
  • 6. Mehrlagenbeschichtung nach einem der Gegenstände 1 bis 5, wobei sich ein Pigment(e), das (die) in der (den) darauffolgenden oberen Curtain-Coating-Schicht(en) verwendet ist (sind), von einem Pigment(en), das (die) in der unteren Curtain-Coating-Schicht verwendet ist (sind), in der ISO-Helligkeit um mindestens 5% Einheiten unterscheidet(en). Solch ein Pigment (solche Pigmente) liefert (liefern) eine hohe Helligkeit des Endprodukts.
  • 7. Mehrlagenbeschichtung nach Gegenstand 6, wobei die darauffolgende(n) obere(n) Curtain-Coating-Schicht(en) und die obere(n) Coating-Schicht(en) das gleiche Pigment (die gleichen Pigmente) enthält (enthalten). Solch darauffolgende obere Curtain-Coating-Schicht(en) und obere Coating-Schicht(en) liefern eine bessere einheitliche ISO-Helligkeit.
  • 8. Mehrlagenbeschichtung nach einem der Gegenstände 1 bis 7, wobei die Mehrlagenbeschichtung durch Umfassen eines abschließenden Kalendrier-Schritts erhältlich ist. Eine solche Mehrlagenbeschichtung liefert eine zufriedenstellende ISO-Helligkeit und ist nicht gefleckt, auch wenn ein abschließender Kalendrier-Schritt auf die Mehrlagenbeschichtung angewendet wird.
  • 9. Mehrlagenbeschichtung nach Gegenstand 8, wobei der abschließende Kalendrier-Schritt ein Hart-Nip(s)-Kalendrier-Schritt oder ein Weich-Nip(s)-Kalendrier-Schritt ist. Ein solcher Kalendrier-Schritt liefert die benötigte Glätte des Endprodukts.
  • 10. Mehrlagenbeschichtung nach Gegenständen 8 oder 9, wobei der abschließende Kalendrier-Schritt eine Last von mehr als 40 kN/m anwendet. Ein solcher abschließende Kalendrier-Schritt liefert eine einheitliche Glätte der Mehrlagenbeschichtung.
  • 11. Mehrlagenbeschichtung nach Gegenstand 10, wobei der abschließende Kalendrier-Schritt eine Last von mehr als 100 kN/m anwendet. Ein solcher abschließende Kalendrier-Schritt liefert sogar eine bessere einheitliche Glätte der Mehrlagenbeschichtung.
  • 12. Mehrlagenbeschichtetes Blatt, das ein Basisblatt umfasst, auf welchem eine Mehrlagenbeschichtung nach einem der Gegenstände 1 bis 11 beschichtet ist. Ein solches mehrlagenbeschichtetes Blatt liefert eine besonders einheitliche hohe ISO-Helligkeit.
  • 13. Mehrlagenbeschichtetes Blatt nach Gegenstand 12, wobei die ISO-Helligkeit des Basisblatts weniger als 45% ist. Ein solches Basisblatt ermöglicht das Erhalten zufriedenstellender ISO-Helligkeit in einem Bereich von 78–90%, sogar von Basisblättern von niedriger ISO-Helligkeit.
  • 14. Mehrlagenbeschichtetes Blatt nach Gegenstand 13, wobei die ISO-Helligkeit des Basisblatts in einem Bereich von 5–30% ist. Solch ein Basisblatt ermöglicht das Erhalten sogar noch zufriedenstellender ISO-Helligkeit in einem Bereich von 78–90%, sogar von Basisblättern von sehr niedriger ISO-Helligkeit.
  • 15. Mehrlagenbeschichtetes Blatt nach einem der Gegenstände 12 bis 14, wobei das mehrlagenbeschichtete Blatt eine ISO-Helligkeit in dem Bereich von 78–90% aufweist. Solch eine ISO-Helligkeit liefert ein einheitliches Endprodukt sogar mit einem niedrigen hellen Basisblatt.
  • 16. Mehrlagenbeschichtetes Blatt nach einem der Gegenstände 12 bis 15, wobei das Blatt eine Pappe oder ein Papier ist. Ein solches Blatt liefert ein mehrlagenbeschichtetes Blatt, das eine besonders einheitliche ISO-Helligkeit aufweist.
  • 17. Verfahren zum Mehrlagenbeschichten eines Pappe- oder Papierblatts, das das Bilden einer unteren Coating-Schicht, die zumindest ein Pigment umfasst, durch eine Curtain-Coating-Station, das Bilden einer oder mehrerer darauffolgenden(r) oberen(r) Coating-Schicht(en) durch eine Curtain-Coating-Station(en) und das Bilden einer oder mehrerer oberer Coating-schicht(en) auf der(n) darauffolgenden oberen Coating-Schicht(en), die durch eine Curtain-Coating-Station(en) gebildet wird (werden), durch zumindest eine Blade- oder Rod-Coating-Station umfasst, wobei die darauffolgende(n) obere(n) Coating-Schicht(en), die durch eine Curtain-Coating-Station(en) gebildet wird (werden), und die obere(n) Coating-Schicht(en) ein Pigment(e) umfasst(en), das (sie) sich von einem Pigment(en) der unteren Coating-Schicht, die durch eine Curtain-Coating-Station gebildet wird, unterscheidet(en), wobei zumindest zwei folgende Curtain-Coating-Schichten durch eine Mehrlagen-Curtain-Coating-Station, die zumindest zwei Schichten gleichzeitig beschichtet, oder durch zumindest zwei Einzel-Curtain-Coating-Stationen beschichtet wird. Ein solches Verfahren liefert eine Mehrlagenbeschichtung mit einer hohen völlig einheitlichen ISO-Helligkeit unabhängig von der Art des Substrats, das die Mehrlagenbeschichtung trägt. Ferner durch Verwenden von verschiedenen Pigment(en) in Kombination mit den verschiedenen Schichten der Mehrlagenbeschichtung kann der Fachmann einfach die hohe einheitliche ISO-Helligkeit der Mehrlagenbeschichtung einstellen.
  • 18. Verfahren nach Gegenstand 17, wobei die untere Coating-Schicht TiO2 als ein Pigment umfasst. Eine solche untere Coating-Schicht weist eine hohe Deckkraft auf und ist eine Vorbedingung zum Aufweisen sehr hoher ISO-Helligkeit der Mehrlagenbeschichtung in Kombination mit den folgenden Schichten.
  • 19. Verfahren nach Gegenständen 17 oder 18 ferner umfassend Bilden einer unteren Coating-Schicht durch eine Blade- oder Rod-Coating-Station unterhalb der unteren Coating-Schicht, die durch eine Curtain-Coating-Station gebildet ist. Eine solche untere Coating-Schicht verbessert die Oberflächenglätte der folgenden Schichten unabhängig von der Art des Blatts, das die Mehrlagenbeschichtung trägt.
  • 20. Verfahren nach einem der Gegenstände 17 bis 19, wobei die erste oder mehrere obere(n) Coating-Schicht(en) auf den darauffolgenden oberen Coating-Schichten, die durch eine Curtain-Coating-Station(en) gebildet ist (sind), eine obere Coating-Schicht(en) ist (sind), die durch eine Blade- oder Rod-Coating-Station gebildet ist (sind). Eine solche obere Blade- oder Rod-Coating-Schicht liefert eine über alles verbesserte Oberflächenglätte und Glanz der Mehrlagenbeschichtung.
  • 21. Verfahren nach einem der Gegenstände 17 bis 20, wobei sich ein Pigment(e), das (die) in der (den) darauffolgenden oberen Curtain-Coating-Schicht(en) verwendet wird (werden), von einem Pigment(en), das (die) in der unteren Curtain-Coating-Schicht verwendet wird (werden), im Brechungsindex um mindestens 0,5 Einheiten unterscheidet(en). Solch ein Pigment (solche Pigmente) liefert (liefern) eine gute deckende Abdeckung der Beschichtungsschicht.
  • 22. Verfahren nach einem der Gegenstände 17 bis 21, wobei sich ein Pigment(e), das (die) in der (den) darauffolgenden oberen Curtain-Coating-Schicht(en) verwendet wird (werden), von einem Pigment(en), das (die) in der unteren Curtain-Coating-Schicht verwendet wird (werden), in der ISO-Helligkeit um mindestens 5% Einheiten unterscheidet(en). Solch ein Pigment (solche Pigmente) liefert (liefern) eine hohe Helligkeit des Endprodukts.
  • 23. Verfahren nach Gegenstand 22, wobei die darauffolgende(n) obere(n) Curtain-Coating-Schicht(en) und die obere(n) Coating-Schicht(en) das gleiche Pigment (die gleichen Pigmente) enthält (enthalten). Solch darauffolgende obere Curtain-Coating-Schicht(en) und obere Coating-Schicht(en) liefern eine bessere einheitliche ISO-Helligkeit.
  • 24. Verfahren nach einem der Gegenstände 17 bis 23, wobei die Mehrlagenbeschichtung auf einem Basisblatt gebildet wird. Ein solches mehrlagenbeschichtetes Blatt liefert eine besonders einheitliche hohe ISO-Helligkeit.
  • 25. Verfahren nach Gegenstand 24, wobei die ISO-Helligkeit des Basisblatts weniger als 45% ist. Ein solches Basisblatt ermöglicht das Erhalten zufriedenstellender ISO-Helligkeit in einem Bereich von 78–90%, sogar von Basisblättern von niedriger ISO-Helligkeit.
  • 26. Verfahren nach Gegenstand 25, wobei die ISO-Helligkeit des Basisblatts in einem Bereich von 5–30% ist. Solch ein Basisblatt ermöglicht das Erhalten sogar noch zufriedenstellender ISO-Helligkeit in einem Bereich von 78–90%, sogar von Basisblättern von sehr niedriger ISO-Helligkeit.
  • 27. Verfahren nach einem der Gegenstände 25 oder 26, wobei das mehrlagenbeschichtete Blatt eine ISO-Helligkeit in dem Bereich von 78–90% aufweist. Solch eine ISO-Helligkeit liefert ein einheitliches Endprodukt sogar mit einem niedrigen hellen Basisblatt.
  • 28. Verfahren nach einem der Gegenstände 18 bis 27, wobei das Verfahren einen abschließenden Kalendrier-Schritt umfasst. Ein solches Verfahren liefert eine Mehrlagenbeschichtung mit befriedigender ISO-Helligkeit und ist nicht gefleckt sogar wenn ein abschließender Kalendrier-Schritt auf die Mehrlagenbeschichtung angewendet wird.
  • 29. Verfahren nach Gegenstand 28, wobei der abschließende Kalendrier-Schritt ein Hart-Nip(s)-Kalendrier-Schritt oder ein Weich-Nip(s)-Kalendrier-Schritt ist. Ein solcher Kalendrier-Schritt liefert die benötigte Glätte des Endprodukts.
  • 30. Verfahren nach Gegenständen 28 oder 29, wobei der abschließende Kalendrier-Schritt eine Last von mehr als 40 kN/m anwendet. Ein solcher abschließende Kalendrier-Schritt liefert einheitliche Glätte der Mehrlagenbeschichtung.
  • 31. Verfahren nach Gegenstand 30, wobei der abschließende Kalendrier-Schritt eine Last von mehr als 100 kN/m anwendet. Ein solcher abschließende Kalendrier-Schritt liefert sogar höhere einheitliche Glätte der Mehrlagenbeschichtung.
The invention provides the following solutions for improvements concerning the objects to which it relates:
  • A multilayer coating comprising a lower curtain coating layer comprising at least one pigment, one or more subsequent upper curtain coating layers and one or more upper coating layers on the subsequent upper layer (s) Curtain coating layer (s), wherein the subsequent upper curtain coating layer (s) and the upper (s) coating layer (s) comprise a pigment (s) that (s) differs from a pigment (s) from the lower curtain coating layer (s). Such a multilayer coating has a high, completely uniform ISO brightness regardless of the type of substrate carrying the multilayer coating. Further, by using different pigment (s) in combination with the various layers of the multilayer coating, one skilled in the art can easily adjust the high uniform ISO brightness of the multilayer coating.
  • 2. A multilayer coating according to item 1, wherein the lower curtain coating layer comprises TiO 2 as a pigment. Such a lower curtain coating layer has high hiding power and is a prerequisite for having very high ISO brightness of the multilayer coating in combination with the following layers.
  • 3. multilayer coating according to item 1 or 2, further comprising a lower blade or rod coating layer below the lower curtain coating layer. Such a lower blade or rod coating layer improves the surface smoothness of the following layers regardless of the type of substrate supporting the multilayer.
  • 4. The multilayer coating according to any one of items 1 to 3, wherein the one or more upper coating layer (s) is (are) a blade or rod coating layer (s). Such an upper blade or rod coating layer (s) allows for overall improved surface smoothness and gloss from the multilayer coating.
  • A multilayer coating according to any one of items 1 to 4, wherein a pigment (s) used in the subsequent upper curtain coating layer (s) is derived from a pigment (s). which is (are) used in the lower curtain coating layer, differs in refractive index by at least 0.5 units. Such a pigment (s) will provide good coverage of the coating layer.
  • 6. A multilayer coating according to any one of items 1 to 5, wherein a pigment (s) used in the subsequent upper curtain coating layer (s) is derived from a pigment (s). , which is (are) used in the lower curtain coating layer, in which ISO brightness differs by at least 5% units. Such a pigment (such pigments) provides high brightness of the final product.
  • 7. The multilayer coating according to item 6, wherein the subsequent upper curtain coating layer (s) and the upper coating layer (s) contain the same pigment (s). Such subsequent upper curtain coating layer (s) and upper coating layer (s) provide better uniform ISO brightness.
  • A multilayer coating according to any one of items 1 to 7, wherein the multilayer coating is obtainable by including a final calendering step. Such a multilayer coating provides satisfactory ISO brightness and is not spotted, even though a final calendering step is applied to the multilayer coating.
  • 9. The multilayer coating of item 8, wherein the final calendering step is a hard nip (s) calendering step or a soft nip (s) calendering step. Such a calendering step provides the required smoothness of the final product.
  • 10. Multilayer coating according to item 8 or 9, wherein the final calendering step applies a load of more than 40 kN / m. Such a final calendering step provides uniform smoothness of the multilayer coating.
  • 11. A multilayer coating according to item 10, wherein the final calendering step applies a load of more than 100 kN / m. Such a final calendering step even provides better uniform smoothness of the multilayer coating.
  • A multi-layer coated sheet comprising a base sheet on which a multi-layer coating according to any one of items 1 to 11 is coated. Such a multilayer coated sheet provides a particularly uniform high ISO brightness.
  • 13. The multilayer coated sheet of item 12, wherein the ISO brightness of the base sheet is less than 45%. Such a base sheet makes it possible to obtain satisfactory ISO brightness in a range of 78-90%, even base sheets of low ISO brightness.
  • 14. A multilayer coated sheet according to item 13, wherein the ISO brightness of the base sheet is in a range of 5-30%. Such a base sheet makes it possible to obtain even satisfactory ISO brightness in a range of 78-90%, even base sheets of very low ISO brightness.
  • A multilayer coated sheet according to any one of items 12 to 14, wherein the multilayer coated sheet has an ISO brightness in the range of 78-90%. Such an ISO brightness provides a uniform end product even with a low bright base sheet.
  • 16. A multi-layer coated sheet according to any one of items 12 to 15, wherein the sheet is a cardboard or a paper. Such a sheet provides a multilayer coated sheet having a particularly uniform ISO brightness.
  • A method of multilayer coating a paperboard or paper sheet comprising forming a lower coating layer comprising at least one pigment through a curtain coating station, forming one or more subsequent upper coating layers (EN) by a curtain coating station (s) and forming one or more upper coating layer (s) on the subsequent upper coating layer (s) covered by a curtain coating station (s ) is formed by at least one blade or rod coating station, the subsequent top coating layer (s) being formed by a curtain coating station (s) and the top coat layer (s) comprises a pigment (s) derived from a pigment (s) of the lower coating layer that is curtain-coated. Station is formed, (s), wherein at least two following curtain coating layers by a multi-layer curtain coating station, at least zw coated simultaneously, or coated by at least two single-curtain coating stations. Such a process provides a multilayer coating with a high, completely uniform ISO brightness regardless of the type of substrate carrying the multilayer coating. Further, by using different pigment (s) in combination with the various layers of the multilayer coating, one skilled in the art can easily adjust the high uniform ISO brightness of the multilayer coating.
  • 18. The method of item 17, wherein the lower coating layer comprises TiO 2 as a pigment. Such a lower coating layer has high opacity and is a prerequisite for having very high ISO brightness of the multilayer coating in combination with the following layers.
  • 19. The method of item 17 or 18 further comprising forming a lower coating layer by a blade or rod coating station below the lower coating layer formed by a curtain coating station. Such a lower coating layer improves the Surface smoothness of the following layers regardless of the type of sheet bearing the multilayer coating.
  • 20. The method of any one of items 17 to 19, wherein the first or more topcoat layers are formed on the subsequent topcoat layers formed by a curtain coating station (s). , is an upper coating layer (s) formed by a blade or rod coating station. Such an upper blade or rod coating layer provides an overall improved surface smoothness and gloss of the multilayer coating.
  • 21. A method according to any one of items 17 to 20, wherein a pigment (s) used in the subsequent upper curtain coating layer (s) is replaced by a pigment (s). , which is (are) used in the lower curtain coating layer, differs in refractive index by at least 0.5 units. Such a pigment (s) will provide good coverage of the coating layer.
  • 22. A method according to any one of items 17 to 21, wherein a pigment (s) used in the subsequent upper curtain coating layer (s) is replaced by a pigment (s). which is used in the lower curtain coating layer, in which ISO brightness differs by at least 5% units. Such a pigment (such pigments) provides high brightness of the final product.
  • 23. The method of item 22, wherein the subsequent upper curtain coating layer (s) and upper coating layer (s) contain the same pigment (s). Such subsequent upper curtain coating layer (s) and upper coating layer (s) provide better uniform ISO brightness.
  • 24. The method according to any one of items 17 to 23, wherein the multilayer coating is formed on a base sheet. Such a multilayer coated sheet provides a particularly uniform high ISO brightness.
  • 25. The method of item 24, wherein the ISO brightness of the base sheet is less than 45%. Such a base sheet makes it possible to obtain satisfactory ISO brightness in a range of 78-90%, even base sheets of low ISO brightness.
  • 26. The method of item 25, wherein the ISO brightness of the base sheet is in a range of 5-30%. Such a base sheet makes it possible to obtain even satisfactory ISO brightness in a range of 78-90%, even base sheets of very low ISO brightness.
  • 27. The method of any of items 25 or 26, wherein the multilayer coated sheet has an ISO brightness in the range of 78-90%. Such an ISO brightness provides a uniform end product even with a low bright base sheet.
  • 28. The method of any one of items 18 to 27, wherein the method comprises a final calendering step. Such a process provides a multilayer coating with satisfactory ISO brightness and is not spotted even when a final calendering step is applied to the multilayer coating.
  • 29. The method of item 28, wherein the final calendering step is a hard nip (s) calendering step or a soft nip (s) calendering step. Such a calendering step provides the required smoothness of the final product.
  • 30. Method according to item 28 or 29, wherein the final calendering step applies a load of more than 40 kN / m. Such a final calendering step provides uniform smoothness of the multilayer coating.
  • 31. The method of item 30, wherein the final calendering step applies a load of greater than 100 kN / m. Such a final calendering step will even provide higher uniform smoothness of the multilayer coating.

Kurze Beschreibung der ZeichnungenBrief description of the drawings

1 zeigt eine konventionelle Mehrlagenbeschichtung mit einem Basisblatt (1) und drei Beschichtungsschichten (2, 3, 4). 1 shows a conventional multilayer coating with a base sheet ( 1 ) and three coating layers ( 2 . 3 . 4 ).

2 zeigt FFB vom skandinavischen Typ mit drei Lagen einer doppelten oberseitigen Coating-Schicht (5) und einer einfachen unterseitigen Coating-Schicht (6). 2 shows Scandinavian type FFB with three layers of a double topcoating layer ( 5 ) and a simple underside coating layer ( 6 ).

3 zeigt eine bevorzugte Ausführungsform der Erfindung. Die Mehrlagenbeschichtung weist ein Basisblatt (1), eine untere Blade-Coating-Schicht (7), eine untere Curtain-Coating-Schicht (8), die TiO2 umfasst, eine obere Curtain-Coating-Schicht (9) und eine obere Blade-Coating-Schicht (10) auf. 3 shows a preferred embodiment of the invention. The multilayer coating has a base sheet ( 1 ), a lower blade coating layer ( 7 ), a lower curtain coating layer ( 8th ) comprising TiO 2 , an upper curtain coating layer ( 9 ) and an upper blade coating layer ( 10 ) on.

Detaillierte Beschreibung der bevorzugten AusführungsformenDetailed Description of the Preferred Embodiments

Ausführungsform 1 der vorliegenden Erfindung wird jetzt mit Bezugnahme auf 3 beschrieben.Embodiment 1 of the present invention will now be described with reference to FIG 3 described.

Die Mehrlagenbeschichtung ist durch erstens Aufbringen einer unteren Blade-Coating-Schicht (7) auf einer Seite eines braunen Basisblatts (1), das niedrige ISO-Helligkeit in einem Bereich von 5–30% aufweist, durch eine Blade-Coating-Station einer Papierprozessierungsmaschine gebildet. Auf die Blade-Coating-Station folgt eine Mehrlagen-Curtain-Coating-Station einer Papierprozessierungsmaschine, die zwei darauffolgende Curtain-Coating-Schichten simultan bildet. Von diesen zwei darauffolgend gebildeten Curtain-Coating-Schichten ist die untere Curtain-Coating-Schicht (8) direkt auf der unteren Blade-Coating-Schicht (7) gebildet und diese Schicht (8) umfasst TiO2 als deckendes Pigment in einem Bereich von 1 bis 4 Gramm pro Quadratmeter (gsm) als Trockengehalt. Der Rest der Pigmente der unteren Curtain-Coating-Schicht (8) ist CaCO3. Die zweite Curtain-Coating-Schicht, die durch die Mehrlagen-Curtain-Coating-Station einer Papierprozessierungsmaschine gebildet ist, ist die obere Curtain-Coating-Schicht (9), die eine Mischung aus Ton und CaCO3 als Pigmente enthält. Schließlich folgt auf die Mehrlagen-Curtain-Coating-Station eine obere Blade-Coating-Station, die eine Blade-Coating-Schicht (10), die eine Mischung aus Ton und CaCO3 als Pigmente enthält, auf die obere Curtain-Coating-Schicht bildet. Eine einzelne Coating-Schicht weist ein gesamtes Beschichtungsgewicht von 8 bis 13 gsm auf, das beinhaltet Pigmente, Bindemittel und alle anderen Chemikalien. Zuletzt durchlief das mehrlagenbeschichtete Blatt eine Hart-Nip-Kalendrier-Station, die eine Last von mehr als 100 kN/m anwendet.The multilayer coating is achieved by firstly applying a lower blade coating layer ( 7 ) on one side of a brown base sheet ( 1 ) having low ISO brightness in a range of 5-30% is formed by a blade coating station of a paper processing machine. On the Blade coating station is followed by a multi-layer curtain coating station of a paper processing machine, which forms two subsequent curtain coating layers simultaneously. Of these two subsequently formed curtain coating layers, the lower curtain coating layer ( 8th ) directly on the lower blade coating layer ( 7 ) and this layer ( 8th ) comprises TiO 2 as opacifying pigment in a range of 1 to 4 grams per square meter (gsm) as dry content. The rest of the pigments of the lower curtain coating layer ( 8th ) is CaCO 3 . The second curtain coating layer, which is formed by the multilayer curtain coating station of a paper processing machine, is the upper curtain coating layer (FIG. 9 ) containing a mixture of clay and CaCO 3 as pigments. Finally, the multilayer curtain coating station is followed by an upper blade coating station which has a blade coating layer ( 10 ), which contains a mixture of clay and CaCO 3 as pigments, forms on the upper curtain coating layer. A single coating layer has a total coating weight of 8 to 13 gsm, which includes pigments, binders and all other chemicals. Most recently, the multilayer coated sheet passed through a hard-nip calendering station applying a load of greater than 100 kN / m.

Die Mischung aus Ton in Ausführungsform 1 wies einen Brechungsindex auf, der unter Verwendung von gewöhnlich verwendeter Vorrichtungen in chemischen Laboratorien zum Messen des Brechungsindex gemessen wurde, der sich von TiO2 zumindest um 0,5 Einheiten unterscheidet, und wies eine ISO-Helligkeit auf, die sich von TiO2 zumindest um 5% Einheiten unterscheidet. Die ISO-Helligkeit der Pigmente, die in den unterschiedlichen Coating-Schichten verwendet wurden, wurde gemäß ISO 2470 unter Verwendung gewöhnlich anzutreffender Instrumente, die zum Messen der ISO-Helligkeit in Übereinstimmung mit ISO 2470 geeignet sind, gemessen. Des Weiteren weist die erhaltene Mehrlagenbeschichtungsschicht der Ausführungsform 1 eine hohe einheitliche befriedigende ISO-Helligkeit innerhalb von 78–90% auf und zeigte keine gefleckte Oberfläche.The clay mixture in Embodiment 1 had a refractive index measured by using commonly used devices in refractive index measuring chemical laboratories different from TiO 2 by at least 0.5 unit, and had ISO brightness, which differs from TiO 2 by at least 5% units. The ISO brightness of the pigments used in the different coating layers was determined according to ISO 2470 using commonly encountered instruments suitable for measuring ISO brightness in accordance with ISO 2470. Further, the obtained multilayer coating layer of Embodiment 1 has a high uniform satisfactory ISO brightness within 78-90% and showed no speckled surface.

Ausführungsform 2 der vorliegenden Erfindung wird jetzt beschrieben.Embodiment 2 of the present invention will now be described.

Die Mehrlagenbeschichtung ist durch erstens Aufbringen einer unteren Rod-Coating-Schicht auf einer Seite eines braunen Basisblatts, das niedrige ISO-Helligkeit in einem Bereich von 5–30% aufweist, durch eine Rod-Coating-Station einer Papierprozessierungsmaschine gebildet. Auf die Rod-Coating-Station folgen zwei Einzel-Curtain-Coating-Stationen einer Papierprozessierungsmaschine, die jede eine einzelne Curtain-Coating-Schicht bilden. Von diesen zwei darauffolgenden gebildeten Curtain-Coating-Schichten ist die untere Curtain-Coating-Schicht direkt auf der unteren Rod-Coating-Schicht durch eine einzelne Curtain-Coating-Stationen gebildet und diese Schicht umfasst TiO2 als deckendes Pigment in einem Bereich von 1 bis 4 Gramm pro Quadratmeter (gsm) als Trockengehalt. Der Rest der Pigmente der unteren Curtain-Coating-Schicht ist CaCO3. Die zweite Curtain-Coating-Schicht, die durch die zweite Curtain-Coating-Station einer Papierprozessierungsmaschine gebildet ist, ist die obere Curtain-Coating-Schicht, die eine Mischung aus Ton und CaCO3 als Pigmente enthält. Schließlich folgt auf die zwei Einzel-Curtain-Coating-Stationen eine obere Rod-Coating-Station, die eine Rod-Coating-Schicht, die eine Mischung aus Ton und CaCO3 als Pigmente enthält, auf die obere Curtain-Coating-Schicht bildet. Eine einzelne Coating-Schicht weist ein gesamtes Beschichtungsgewicht von 8 bis 13 gsm auf, das beinhaltet Pigmente, Bindemittel und alle anderen Chemikalien. Zuletzt durchlief das mehrlagenbeschichtete Blatt eine Weich-Nip-Kalendrier-Station, die eine Last von mehr als 100 kN/m anwendet. Die Pigmente, die in den unterschiedlichen Schichten verwendet wurden, sind dieselben wie in der Ausführungsform 1. Deshalb, zeigten die Pigmente dieselben Eigenschaften bezüglich der ISO-Helligkeit und des Brechungsindex wie in der Ausführungsform 1 genannt. Das erhaltene mehrlagenbeschichtete Blatt aus der Ausführungsform 2 zeigte keine gefleckte Oberflache und wies eine hohe einheitliche befriedigende ISO-Helligkeit innerhalb 78–90% auf.The multilayer coating is formed by first applying a bottom rod coating layer on one side of a brown base sheet having low ISO brightness in a range of 5-30% by a rod coating station of a paper processing machine. The rod coating station is followed by two single curtain coating stations of a paper processing machine, each forming a single curtain coating layer. Of these two subsequent formed curtain coating layers, the lower curtain coating layer is formed directly on the lower Rod coating layer by a single curtain coating station, and this layer comprises TiO 2 as opacifying pigment in a range of 1 to 4 grams per square meter (gsm) as dry content. The rest of the pigments of the lower curtain coating layer is CaCO 3 . The second curtain coating layer formed by the second curtain coating station of a paper processing machine is the upper curtain coating layer containing a mixture of clay and CaCO 3 as pigments. Finally, the two single curtain coating stations are followed by an upper rod coating station which forms a rod coating layer containing a mixture of clay and CaCO 3 as pigments on top of the curtain coating layer. A single coating layer has a total coating weight of 8 to 13 gsm, which includes pigments, binders and all other chemicals. Most recently, the multilayer coated sheet passed through a soft-nip calendering station applying a load of greater than 100 kN / m. The pigments used in the different layers are the same as in Embodiment 1. Therefore, the pigments showed the same properties in terms of ISO brightness and refractive index as mentioned in Embodiment 1. The resulting multilayer coated sheet of Embodiment 2 showed no spotted surface and had a high uniform satisfactory ISO brightness within 78-90%.

Ausführungsform 3 der vorliegenden Erfindung wird jetzt beschrieben.Embodiment 3 of the present invention will now be described.

Die Mehrlagenbeschichtung der Ausführungsform 3 wurde in der gleichen Weise wie in der Ausführungsform 1 erhalten außer, dass das mehrlagenbeschichtete Blatt abschließend durch eine Weich-Nip-Kalendrier-Station gelaufen ist, die eine Last von mehr als 40 kN/m anwendet. Das mehrlagenbeschichtete Blatt der Ausführungsform 3 wies auch eine hohe einheitliche befriedigende ISO-Helligkeit innerhalb 78–90% auf und zeigte auch keine gefleckte Oberfläche.The multilayer coating of Embodiment 3 was obtained in the same manner as in Embodiment 1 except that the multilayer coated sheet was finally passed through a soft-nip calendering station applying a load of more than 40 kN / m. The multilayer coated sheet of Embodiment 3 also had a high uniform satisfactory ISO brightness within 78-90% and also showed no spotted surface.

Ausführungsform 4 der vorliegenden Erfindung wird jetzt beschrieben.Embodiment 4 of the present invention will now be described.

Die Mehrlagenbeschichtung der Ausführungsform 4 wurde in der gleichen Weise wie in der Ausführungsform 1 außer Verwenden eines Basisblatts mit einer niedrigen ISO-Helligkeit von weniger als 45% erhalten. Das mehrlagenbeschitete Blatt der Ausführungsform 4 wies auch eine hohe einheitliche befriedigende ISO-Helligkeit innerhalb 78–90% auf und zeigte keine gefleckte Oberfläche.The multilayer coating of Embodiment 4 was obtained in the same manner as in Embodiment 1 except for using a base sheet having a low ISO brightness of less than 45%. The multilayer-coated sheet of Embodiment 4 also had a high uniform satisfactory ISO brightness within 78-90% and showed no spotted surface.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte Nicht-PatentliteraturCited non-patent literature

  • ISO 2470 [0010] ISO 2470 [0010]

Claims (12)

Mehrlagenbeschichtung, die eine untere Curtain-Coating-Schicht, die zumindest ein Pigment umfasst, eine oder mehrere darauffolgende obere Curtain-Coating-Schicht(en) und eine oder mehrere obere Coating-Schicht(en) auf der (den) darauffolgenden oberen Curtain-Coating-Schicht(en) umfasst, wobei die darauffolgende(n) obere(n) Curtain-Coating-Schicht(en) und die obere(n) Coating-Schicht(en) ein Pigment(e), das (die) sich von einem Pigment(en) von der unteren Curtain-Coating-Schicht unterscheidet(en), umfasst(en).A multilayer coating comprising a lower curtain coating layer comprising at least one pigment, one or more subsequent upper curtain coating layers and one or more upper coating layers on the subsequent upper curtain. Coating layer (s), wherein the subsequent upper curtain coating layer (s) and the upper (s) coating layer (s) a pigment (s), the ( A pigment (s) from the lower curtain coating layer (s) comprises (s). Mehrlagenbeschichtung nach Anspruch 1, wobei die untere Curtain-Coating-Schicht TiO2 als ein Pigment umfasst.The multilayer coating according to claim 1, wherein the lower curtain coating layer comprises TiO 2 as a pigment. Mehrlagenbeschichtung nach Anspruch 1 oder 2, ferner umfassend eine untere Blade- oder Rod-Coating-Schicht unterhalb der unteren Curtain-Coating-Schicht.The multilayer coating according to claim 1 or 2, further comprising a lower blade or rod coating layer below the lower curtain coating layer. Mehrlagenbeschichtung nach einem der Ansprüche 1 bis 3, wobei die eine oder mehreren obere(n) Coating-Schicht(en) eine Blade- oder Rod-Coating-Schicht(en) ist (sind).A multilayer coating according to any one of claims 1 to 3, wherein the one or more top coating layers is or are a blade or rod coating layer (s). Mehrlagenbeschichtung nach einem der Ansprüche 1 bis 4, wobei sich ein Pigment(e), das (die) in der (den) darauffolgenden oberen Curtain-Coating-Schicht(en) verwendet ist (sind), von einem Pigment(en), das (die) in der unteren Curtain-Coating-Schicht verwendet ist (sind), im Brechungsindex um mindestens 0,5 Einheiten unterscheidet(en).A multilayer coating according to any one of claims 1 to 4, wherein a pigment (s) used in the subsequent upper curtain coating layer (s) of a pigment (s), is (which) is used in the lower curtain coating layer (s), differs in refractive index by at least 0.5 units. Mehrlagenbeschichtung nach einem der Ansprüche 1 bis 5, wobei sich ein Pigment(e), das (die) in der (den) darauffolgenden oberen Curtain-Coating-Schicht(en) verwendet ist (sind), von einem Pigment(en), das (die) in der unteren Curtain-Coating-Schicht verwendet ist (sind), in der ISO-Helligkeit um mindestens 5% Einheiten unterscheidet(en).A multilayer coating according to any one of claims 1 to 5, wherein a pigment (s) used in the subsequent upper curtain coating layer (s) of a pigment (s), is (that) is used in the lower curtain coating layer, in which ISO brightness differs by at least 5% units. Mehrlagenbeschichtung nach einem der Ansprüche 1 bis 6, wobei die Mehrlagenbeschichtung durch Umfassen eines abschließenden Kalendrier-Schritts erhältlich ist.A multilayer coating according to any one of claims 1 to 6, wherein the multilayer coating is obtainable by including a final calendering step. Mehrlagenbeschichtetes Blatt, das ein Basisblatt umfasst, auf welchem eine Mehrlagenbeschichtung nach einem der Ansprüche 1 bis 7 beschichtet ist.A multi-layer coated sheet comprising a base sheet on which a multi-layer coating according to any one of claims 1 to 7 is coated. Mehrlagenbeschichtetes Blatt nach Anspruch 8, wobei die ISO-Helligkeit des Basisblatts weniger als 45% ist.The multilayer coated sheet according to claim 8, wherein the ISO brightness of the base sheet is less than 45%. Mehrlagenbeschichtetes Blatt nach Anspruch 9, wobei die ISO-Helligkeit des Basisblatts in einem Bereich von 5–30% ist.The multilayer coated sheet according to claim 9, wherein the ISO brightness of the base sheet is in a range of 5-30%. Verfahren zum Mehrlagenbeschichten eines Pappe- oder Papierblatts, das das Bilden einer unteren Coating-Schicht, die zumindest ein Pigment umfasst, durch eine Curtain-Coating-Station, das Bilden einer oder mehrerer darauffolgenden(r) oberen(r) Coating-Schicht(en) durch eine Curtain-Coating-Station(en) und das Bilden einer oder mehrerer oberer Coating-schicht(en) auf der(n) darauffolgenden oberen Coating-Schicht(en), die durch eine Curtain-Coating-Station(en) gebildet wird (werden), durch zumindest eine Blade- oder Rod-Coating-Station umfasst, wobei die darauffolgende(n) obere(n) Coating-Schicht(en), die durch eine Curtain-Coating-Station(en) gebildet wird (werden), und die obere(n) Coating-Schicht(en) ein Pigment(e) umfasst(en), das (die) sich von einem Pigment(en) der unteren Coating-Schicht, die durch eine Curtain-Coating-Station gebildet wird, unterscheidet(en), wobei zumindest zwei folgende Curtain-Coating-Schichten durch eine Mehrlagen-Curtain-Coating-Station, die zumindest zwei Schichten gleichzeitig beschichtet, oder durch zumindest zwei Einzel-Curtain-Coating-Stationen beschichtet wird.A method of multilayer coating a paperboard or paper sheet, comprising forming a lower coating layer comprising at least one pigment through a curtain coating station, forming one or more subsequent upper (r) coating layers (e through a curtain coating station (s) and forming one or more upper coating layers on the subsequent upper coating layer (s) formed by a curtain coating station (s) is (are) by at least one blade or rod coating station, wherein the subsequent upper (n) coating layer (s), which is formed by a curtain coating station (s) (be ), and the upper (n) coating layer (s) comprises a pigment (s) formed by a pigment (s) of the lower coating layer formed by a curtain coating station is distinguished (s), wherein at least two following curtain coating layers by a multi-layer curtain coating station, the at least two S coated simultaneously, or coated by at least two single-curtain coating stations. Verfahren nach Anspruch 11, wobei das Verfahren einen abschließenden Kalendrier-Schritt umfasst.The method of claim 11, wherein the method comprises a final calendering step.
DE201210206490 2012-04-19 2012-04-19 Multilayer coating comprises lower curtain coating layer comprising pigment, subsequent upper curtain coating layer and top coating layer, where pigment of upper and top coating layer is different from pigment of lower curtain coating layer Withdrawn DE102012206490A1 (en)