DE102010044741A1 - Coin blank for manufacturing coin, comprises core made of ferrous material, which has cover layer made of nickel provided close to surface of finely dispersed copper doping

Info

Publication number: DE102010044741A1
Application number: DE102010044741A
Authority: DE
Inventors: Thomas Bilas; Stephan Siegel
Original assignee: Saxonia Eurocoin GmbH
Current assignee: Saxonia Eurocoin GmbH
Priority date: 2010-09-08
Filing date: 2010-09-08
Publication date: 2012-03-08

Abstract

The coin blank comprises core made of ferrous material (1), which has cover layer (2) made of nickel provided close to surface of finely dispersed copper doping (3). The penetration depth of copper doping is 0.5 to 10 microns. The cover layer is doped with copper and/or silver.

Description

Die Erfindung betrifft einen Rohling für eine Münze (coin blank) mit einem Kernmaterial aus einem Eisenwerkstoff, der mit einer Nickelschicht bedeckt ist.The invention relates to a blank for a coin (coin blank) with a core material of a ferrous material, which is covered with a nickel layer.

Rohlinge für Münzen aus einem mit Nickel plattiertem oder insbesondere galvanisch mit Nickel beschichtetem Eisenwerkstoff sind international allgemein üblich. Daraus geprägte Münzen gefallen den Verbrauchern als Zahlungsmittel wegen ihres dauerhaft hellen Metallglanzes. Nickel erfüllt dabei auch hervorragend den Zweck des Korrosionsschutzes und der Abriebfestigkeit für einen langen Gebrauch der Umlaufmünzen.Blanks for coins made of a nickel-plated or in particular electroplated with nickel-coated iron material are common practice internationally. Coined coins appeal to consumers as a means of payment because of their permanently bright metallic luster. Nickel also excellently fulfills the purpose of corrosion protection and abrasion resistance for a long use of the circulation coins.

Wegen der allergenen Eigenschaft des Nickels wird Nickel als Deckschicht aber teilweise gemieden oder durch eine zweite Schicht aus Kupfer überdeckt. DE 41 20 291 beschreibt einen Münzrohling mit einem Kern aus einem Eisenwerkstoff, der mit einer ersten Schicht aus Nickel und einer zweiten Schicht aus Kupfer und vorzugsweise nochmals mit Nickel beschichtet ist. Eine Zweifachbeschichtung Nickel-Kupfer zeigt ebenfalls den bekannten optischen Nachteil, dass eine Kupferdeckschicht im Langzeit-Gebrauch matt wird. Andererseits ist die Dreifachbeschichtung Nickel-Kupfer-Nickel aufwendig und bringt aber nicht den Vorteil einer antibakteriellen Wirkung, wie sie eine Deckschicht aus Kupfer besitzt. Diese antibakterielle Wirkung von Kupfer und insbesondere von Silber ist allgemein bekannt.Because of the allergenic nature of the nickel, however, nickel is partially avoided as a capping layer or covered by a second layer of copper. DE 41 20 291 describes a coin blank having a core of a ferrous material which is coated with a first layer of nickel and a second layer of copper and preferably again with nickel. A double coating of nickel-copper also shows the known optical disadvantage that a copper capping becomes dull in long-term use. On the other hand, the triple coating nickel-copper-nickel consuming and does not bring the advantage of antibacterial effect, as it has a cover layer of copper. This antibacterial effect of copper and especially silver is well known.

Umlaufmünzen haben generell einen vielfachen Personenkontakt und sind deshalb auch potentielle Überträger von Bakterien und anderen Krankheitskeimen. In früheren Zeiten wurden auch deshalb Münzen massiv aus den Metallen Silber und Kupfer und aus deren Legierungen geprägt, wobei auch die stark antibakterielle Wirkung von Silber und Kupfer erkennbar wurde. Silber wurde früher als Münzmetall mit Geldwert und auch wegen seines schönen Glanzes umfangreich verwendet. Der Einsatz bleibt aber wegen des hohen Silberpreises aktuell weitgehend nur noch auf Sondermünzen beschränkt.Circulating coins generally have multiple personal contact and are therefore also potential carriers of bacteria and other germs. In former times coins were also massively shaped from the metals silver and copper and from their alloys, whereby also the strongly antibacterial effect of silver and copper became recognizable. Silver used to be widely used as coin metal with monetary value and also because of its beautiful luster. However, due to the high price of silver, the stake is currently largely limited to special coins only.

Münzen aus Kupfer oder verkupferte Münzen mit einem Stahlkern bilden im Umlauf nach relativ kurzer Zeit oxidische, matte Deckschichten, wodurch solche Münzen für den Nutzer schnell optisch unattraktiv werden, wie das bei den Euromünzen der Nominale 1, 2 und 5 Cent aktuell der Fall ist. International übliche Münzen aus einer Nickellegierung oder mit einer Nickelschicht versehene Münzen mit Stahlkern besitzen zwar dauerhaft einen schönen hellen Glanz, verfügen aber über keine antibakteriellen Eigenschaften. Dem Verbraucher gefallen aber erwiesenermaßen bevorzugt Umlaufmünzen mit einem hellen Glanz, so dass allgemein Münzen mit Nickelglanz vor Münzen mit einer matten Oberfläche bevorzugt werden.Coins made of copper or copper-plated coins with a steel core form after circulation in a relatively short time oxidic, matte outer layers, making such coins for the user quickly visually unattractive, as is currently the case with the euro coins of the nominal 1, 2 and 5 cents. Although internationally common coins made of a nickel alloy or nickel-coated coins with a steel core have permanently a beautiful bright luster, but have no antibacterial properties. The consumer, however, has proven to enjoy preferably circulation coins with a bright luster, so that coins with nickel gloss in front of coins with a matt surface are generally preferred.

Aufgabe ist es, einen Münzrohling (coin blank) mit einem Kern aus einem Eisenwerkstoff bereitzustellen, der eine dauerhafte glänzende Nickelschicht aufweist und der zu einer Münze prägbar ist, die antibakterielle Eigenschaften besitzt.The object is to provide a coin blank having a core of a ferrous material which has a durable shiny nickel layer and which is embossable into a coin having antibacterial properties.

Erfindungsgemäß wird ein Münzrohling bereitgestellt, der aus einem Kern aus einem Eisenwerkstoff und aus einer Nickelschicht besteht, die vorzugsweise galvanisch aufgebracht wurde, in die feinstdispers/mikrodispers Kupfer und/oder Silber oberflächlich und oberflächennah dotiert ist. Die Kupferdotierung besitzt eine Eindringtiefe in die Nickelschicht von 0,5 bis 10 μm und weist an der Oberfläche der Nickelschicht einen Anteil von 18 bis 65 Massen-% Kupfer auf, bezogen auf Nickel.According to the invention, a coin blank is provided, which consists of a core made of a ferrous material and a nickel layer, which was preferably applied by electroplating, in which finely dispersed / microdispersed copper and / or silver is doped superficially and near the surface. The copper doping has a penetration depth in the nickel layer of 0.5 to 10 microns and has on the surface of the nickel layer, a proportion of 18 to 65% by mass of copper, based on nickel.

Weniger effektiv bezüglich der antibakteriellen Wirksamkeit, aber erfindungsgemäß nicht auszuschließen ist eine Dotierung der Nickelschicht mit einem anderen Metall aus der Reihe der antibakteriell wirksamen Metalle, wie andere Edelmetalle, Zink, Zinn.Less effective in terms of antibacterial activity, but according to the invention can not be ruled out doping of the nickel layer with another metal from the series of antibacterial metals, such as other precious metals, zinc, tin.

Die Vorteile solcher Münzen, die aus einem erfindungsgemäßen Münzrohling (coin blank) geprägt sind, bestehen darin, dass erstens der ästhetische Glanz der Nickelschicht auch im Langzeitumlauf der Münzen dauerhaft erhalten bleibt, dass eine Verfärbung durch Oxidation von Kupfer oder durch Anlaufen von Silber nicht eintritt. Es wird quasi eine Nickelschicht mit der antibakteriellen Eigenschaft von Kupfer und/oder Silber als eine geringe Dotierung, ausreichend im Oberflächenbereich, bereitgestellt. Es hat sich überraschenderweise gezeigt, dass eine erfindungsgemäß geringe Dotierung der oberflächennahen Zone der Nickelschicht eine hohe Effizienz besitzt bezüglich der antibakteriellen Wirkung der Münzrohlinge und der letztendlich daraus geprägten Umlaufmünzen.The advantages of such coins, which are embossed from a coin blank according to the invention, consist in the fact that, firstly, the aesthetic gloss of the nickel layer is permanently retained even in the long-term circulation of the coins, that discoloration due to oxidation of copper or by tarnishing of silver does not occur , There is provided, as it were, a nickel layer having the antibacterial property of copper and / or silver as a small dopant, sufficiently in the surface area. It has surprisingly been found that a low doping according to the invention of the near-surface zone of the nickel layer has a high efficiency with regard to the antibacterial effect of the coin blanks and the circulating coins ultimately embossed therefrom.

Der erfindungsgemäße Münzrohling ermöglicht das Prägen von Umlaufmünzen einer neuen Qualität, nämlich von Münzen mit einem hellem Glanz durch Nickel, die gleichzeitig die antibakteriellen Eigenschaften von Kupfer und/oder Silber besitzen.The coin blank according to the invention enables the embossing of circulation coins of a new quality, namely coins with a bright shine through nickel, which at the same time have the antibacterial properties of copper and / or silver.

Die erfinderische Lösung schließt Rohlinge für Gedenkprägungen, Medaillen und ähnliche Anwendungsfälle nicht aus. Ebenso sind Gegenstände, die eine Oberfläche aus Nickel oder aus einer kupferfreien Nickellegierung besitzen, erfindungsgemäß mit Kupfer und/oder Silber dotierbar, wie z. B. Griffe, Türklinken, Beschläge.The inventive solution does not exclude blanks for memorial embossing, medals and similar applications. Likewise, articles which have a surface of nickel or of a copper-free nickel alloy, according to the invention dopable with copper and / or silver, such as. As handles, door handles, fittings.

Die Erfindung wird nachstehend an einem Ausführungsbeispiel näher erläutert: The invention is explained in more detail below using an exemplary embodiment:

1 zeigt den Querschnitt durch einen erfindungsgemäßen Münzrohling (coin blank). 1 shows the cross section through a coin blank according to the invention (coin blank).

BezugszeichenlisteLIST OF REFERENCE NUMBERS

11: Stahlkernsteel core
22: galvanische Nickelschichtgalvanic nickel layer
33: Kupferdotierung in der NickelschichtCopper doping in the nickel layer

Der Münzrohling besteht aus einem Kern 1 aus einem für Münzprägungen üblichen, niedriglegierten Stahl, der mit einer galvanisch aufgebrachten Nickelschicht 2 von 30 μm Stärke beschichtet ist, in die eine Kupferdotierung 3 mit atomarer Verteilung oberflächlich und oberflächenah eingebracht ist. Die Kupferdotierung 3 besitzt eine Eindringtiefe von 6 μm in die Nickelschicht 2 und weist ein degressives Konzentrationsgefälle innerhalb der Nickelschicht 2 auf.The coin blank consists of a core 1 from a customary for coinage, low-alloy steel, with an electroplated nickel layer 2 coated by 30 microns thickness, in which a copper doping 3 with atomic distribution superficial and surface-mounted. The copper doping 3 has a penetration depth of 6 μm into the nickel layer 2 and has a degressive concentration gradient within the nickel layer 2 on.

2a zeigt einen Querschnitt durch einen üblichen, mit Nickel beschichteten Münzrohling als Stand der Technik 2a shows a cross section through a conventional, nickel-coated coin blank prior art

2b zeigt den Querschnitt durch einen erfindungsgemäßen Münzrohling mit dem Konzentrationsverlauf der Kupferdotierung 3 in der Nickelschicht 2. 2 B shows the cross section through a coin blank according to the invention with the concentration curve of copper doping 3 in the nickel layer 2 ,

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

DE 4120291 [0003]

Claims

Coin blank comprising a core of a ferrous material provided with a nickel layer, characterized in that the nickel layer ( 2 ) superficially and near the surface a finely divided copper doping ( 3 ) having.

Coin blank according to claim 1, characterized in that the copper doping ( 3 ) in the nickel layer ( 2 ) has a penetration depth of 0.5 to 10 microns.

Coin blank according to claim 1, characterized in that the copper doping ( 3 ) on the surface of the nickel layer ( 2 ) has a concentration of 0.18 to 0.65% by mass of copper and in the nickel layer ( 2 ) declining.

Coin blank according to claim 1, characterized in that the nickel layer ( 2 ) instead of copper doping ( 3 ) has a doping with copper and / or silver.