DE102008038010A1 - Profile strip i.e. edge strip, for decorating e.g. kitchen countertop, has decorative layer containing crushed cork material, manufactured by extrusion process and viewable from visible side of strip - Google Patents

Profile strip i.e. edge strip, for decorating e.g. kitchen countertop, has decorative layer containing crushed cork material, manufactured by extrusion process and viewable from visible side of strip Download PDF

Info

Publication number
DE102008038010A1
DE102008038010A1 DE102008038010A DE102008038010A DE102008038010A1 DE 102008038010 A1 DE102008038010 A1 DE 102008038010A1 DE 102008038010 A DE102008038010 A DE 102008038010A DE 102008038010 A DE102008038010 A DE 102008038010A DE 102008038010 A1 DE102008038010 A1 DE 102008038010A1
Authority
DE
Germany
Prior art keywords
profile strip
strip
decorative layer
layer
profile
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102008038010A
Other languages
German (de)
Inventor
Thorsten Engelbrecht
Andreas Rückert
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rehau Automotive SE and Co KG
Original Assignee
Rehau AG and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rehau AG and Co filed Critical Rehau AG and Co
Priority to DE102008038010A priority Critical patent/DE102008038010A1/en
Publication of DE102008038010A1 publication Critical patent/DE102008038010A1/en
Withdrawn legal-status Critical Current

Abstract

The strip (1) has a decorative layer (2) containing a crushed cork material (4) and manufactured by an extrusion process. The strip is manufactured by co-extrusion process. The decorative layer is viewable from a visible side (3) of the strip. A carrier layer (5) includes a chemical composite, which is different relative to the decorative layer. A ratio of a thickness of the decorative layer to a thickness of the carrier layer ranges between 1 and 5. The carrier layer is colored in shade corresponding to basic color of the decorative layer.

Description

Die Erfindung betrifft eine Profilleiste. Derartige Profilleisten werden eingesetzt, um Gegenstände wie Möbelstücke oder dergleichen zu dekorieren.The The invention relates to a profile strip. Such moldings are used to get objects like pieces of furniture or to decorate the like.

Auf dem Markt besteht ein Bedarf nach hochwertigen Produkten bei erheblicher Produktvielfalt. Man kennt Profilleisten aus den Echtmaterialien Metall, Glas und dergleichen. Profilleisten aus Kork werden in der Industrie bisher nicht eingesetzt.On There is a need for high quality products at the market Product variety. You know profile strips from the real materials Metal, glass and the like. Moldings made of cork are in the Industry not yet used.

Die Verwendung von echtem Kork ist technisch sehr aufwändig und entsprechend teuer.The Use of real cork is technically very complicated and accordingly expensive.

Der Erfindung liegt die Aufgabe zugrunde, eine Profilleiste bereitzustellen, welche die Eigenschaften einer Profilleiste aus Kork in Bezug auf Haptik und Optik aufweist, aber gegenüber dieser Profilleiste wesentlich einfacher und kostengünstiger verarbeitbar ist.Of the Invention is based on the object of providing a profile strip, related to the characteristics of a cork profile strip Has feel and appearance, but compared to this profile strip essential easier and cheaper is processable.

Um die der Erfindung zugrunde liegende Aufgabe zu lösen, stellt die Erfindung die Profilleiste nach Anspruch 1 bereit, wobei die Profilleiste einen mehrschichtigen Aufbau aufweist, zumindest eine Schicht der Profilleiste ein zerkleinertes Korkmaterial enthält und zumindest eine Schicht der Profilleiste im Extrusionsverfahren gefertigt ist. Die mehrschichtige Struktur der erfindungsgemäßen Profilleiste ermöglicht eine funktionale Auslegung der Profilleiste. Die das zerkleinerte Korkmaterial enthaltende Schicht vermittelt der Profilleiste die charakteristischen Eigenschaften von Kork im Hinblick auf Geruch, Haptik und Optik. In zerkleinerter Form kann das Korkmaterial in eine Matrix, z. B. Kunststoff, eingebettet werden und beliebig geformt werden.Around to solve the problem underlying the invention, the invention provides the Profile strip according to claim 1 ready, wherein the profile strip a multilayer Structure, at least one layer of the profile strip a crushed Contains cork material and at least one layer of the profile strip in the extrusion process is made. The multilayer structure of the profile strip according to the invention allows a functional design of the profile strip. The crushed Cork material containing layer gives the profile bar the characteristic properties of cork with regard to odor, Haptics and optics. In shredded form, the cork material in a matrix, e.g. As plastic, are embedded and shaped arbitrarily become.

Das zerkleinerte Korkmaterial wird vorzugsweise aus Korkresten bzw. -abfällen gewonnen und liegt in einer Vielzahl von Korkteilchen bzw. -fasern vor. Die zumindest eine weitere Schicht ermöglicht eine leichte Verarbeitung und Montage der erfindungsgemäßen Profilleiste, indem sie der Profilleiste gegenüber dem einschichtigen Aufbau eine wesentlich steifere und stabilere Struktur verleiht.The shredded cork material is preferably made of cork residues or including wastes won and is present in a variety of cork particles or fibers. The at least one further layer allows easy processing and mounting the profile strip according to the invention, by facing the profile strip the single-layered structure a much stiffer and more stable Gives structure.

Es erweist sich als günstig, wenn zumindest eine Schicht der Profilleiste, vorzugsweise zwei, mehrere oder alle Schichten der Profilleiste, im Extrusionsverfahren gefertigt ist/sind. Die im Extrusionsverfahren gefertigte Schicht kann die das zerkleinerte Korkmaterial enthaltende Schicht und/oder die zumindest eine weitere Schicht sein. Die Fertigungstechnik der Extrusion erweist sich als besonders wirtschaftlich und praktisch, weil dadurch ein stabiles und zugfestes Stranggut geschaffen wird, das den in der Praxis auftretenden Belastungen bei den bevorzugten Anwendungen der Profilleiste standhält. Somit ist die erfindungsgemäße Profilleiste gegenüber dem echten Kork wesentlich leichter verarbeitbar, insbesondere leichter zerteilbar und leichter montierbar. In Abhängigkeit von dem bevorzugten Anwendungsfall kann es von Vorteil sein, wenn das Korkmaterial auf eine Größe von etwa 0,1 bis 50 mm zerkleinert wird. Das Korkmaterial liegt vorzugsweise als Vielzahl von Teilchen mit einer Teilchengröße von etwa 0,01 bis 10 mm bzw. bzw. als Fasern mit einer Faserlänge von etwa 0,1 bis 50 mm vor. Ein Anteil des zerkleinerten Korkmaterials in der Dekorschicht von wenigstens 5 Gew.-% reicht i. d. R. aus, um der Dekorschicht den charakteristischen Geruch von Kork zu vermitteln, wenn man davon ausgeht, dass die restlichen 95 Gew.-% der Material aus im wesentlichen geruchsneutralem Material bestehen. Ein Anteil des zerkleinerten Korkmaterials in der Dekorschicht von wenigstens 30 Gew.-% reicht i. d. R. aus, um der Dekorschicht die charakteristische Kork-Haptik zu vermitteln. Die erfindungsgemäße Profilleiste weist die Eigenschaften einer Kork-Profilleiste in Bezug auf Haptik und Optik auf, und ist gegenüber der Leiste aus echtem Kork wesentlich leichter herstellbar und verarbeitbar.It turns out to be cheap if at least one layer of the profile strip, preferably two, more or all layers of the profile strip, manufactured by extrusion is / are. The extruded layer can be the the crushed cork material containing layer and / or at least be another layer. The manufacturing technology of extrusion proves to be particularly economical and practical because of this stable and tensile Stranggut is created, which in the Practice occurring loads in the preferred applications the profile bar withstands. Thus, the profile strip according to the invention compared to the real cork much easier to process, especially lighter dividable and easier to assemble. Depending on the preferred Use case, it may be advantageous if the cork material on a size of about 0.1 to 50 mm is crushed. The cork material is preferably as a plurality of particles having a particle size of about 0.01 to 10 mm or as fibers with a fiber length of about 0.1 to 50 mm in front. A portion of the shredded cork material in the decorative layer of at least 5% by weight is sufficient i. d. R. to the decorative layer the to convey characteristic smell of cork, if one of it assumes that the remaining 95 wt .-% of the material from substantially odorless material. A portion of the minced Cork material in the decorative layer of at least 30 wt .-% ranges i. d. R. to the decorative layer the characteristic cork feel to convey. The profile strip according to the invention has the properties of a cork profile strip in terms of feel and feel Optics up, and is opposite the strip of real cork much easier to produce and process.

Es erweist sich als günstig, wenn die Profilleiste im Koextrusionsverfahren gefertigt ist. Diese Fertigungstechnik erweist sich als besonders wirtschaftlich und praktisch, da durch das Koextrusionsverfahren die Schichten der erfindungsgemäßen Profilleiste zuverlässig und dauerhaft verbunden werden können.It turns out to be cheap when the profile strip is manufactured by coextrusion. This production technology proves to be particularly economical and practical, as by the coextrusion process the layers of the profile strip according to the invention reliable and be permanently connected.

Es kann sich als vorteilhaft erweisen, wenn die Profilleiste eine Dekorschicht aufweist, die das zerkleinerte Korkmaterial enthält und die an einer Sichtseite der Profilleiste sichtbar ist. Das in der Dekorschicht enthaltene, zerkleinerte Korkmaterial verleiht der Dekorschicht in Bezug auf Optik und Haptik besonders realistisch die charakteristischen Eigenschaften einer Kork-Profilleiste.It may prove to be advantageous if the profile strip a decorative layer comprising the crushed cork material and that on a visible side the profile bar is visible. The included in the decorative layer, crushed cork material gives the decor layer in relation to Optics and feel particularly realistic the characteristic features a cork profile strip.

Es liegt insbesondere im Rahmen der vorliegenden Erfindung, dass die Profilleiste als Kantenband, Wandanschlussprofil, Fensterprofil oder Rollladenprofil ausgebildet ist. Das Kantenband hat die Funktion, ein Möbelstück, z. B. eine Küchenarbeitsplatte oder dergleichen, zu schützen, insbesondere ungeschützte Stellen wie Schnittstellen oder dergleichen zu kaschieren und zu versiegeln. Die Verarbeitung und Montage der erfindungsgemäßen Profilleiste gestaltet sich bei den genannten bevorzugten Anwendungsfällen besonders einfach.It is in particular in the context of the present invention that the Profile strip as edge band, wall connection profile, window profile or roller shutter profile is formed. The edge band has the function a piece of furniture, z. B. a kitchen counter or the like, to protect especially unprotected Sites such as interfaces or the like to hide and to to seal. The processing and assembly of the profile strip according to the invention designed especially in the aforementioned preferred applications easy.

Es kann sich als vorteilhaft erweisen, wenn die Dekorschicht Korkfasern enthält. Korkfasern können aus Korkabfällen leicht gewonnen werden und eignen sich hervorragend für die Anwendung im Rahmen der erfindungsgemäßen Profilleiste. Die Dekorschicht umfasst vorzugsweise Korkfasern und weitere Additive, welche in einem bevorzugten Mischverhältnis vermischt werden, um die charakteristischen Korkeigenschaften im Hinblick auf Geruch, Haptik und Optik aufzuweisen.It may prove advantageous if the decorative layer contains cork fibers. Cork fibers can be easily recovered from cork waste and are ideal for use in the context of the profile strip according to the invention. The decorative layer preferably comprises cork fibers and other additives, which in a preferred Mischver be mixed to show the characteristic Korkeigenschaften in terms of smell, feel and appearance.

Es kann auch von Vorteil sein, wenn ein Anteil des zerkleinerten Korkmaterials in der das zerkleinerte Korkmaterial enthaltenden Schicht, vorzugsweise der Dekorschicht, zwischen 10 und 90 Gew.-%, vorzugsweise zwischen 30 und 70 Gew.-%, bevorzugt zwischen 40 und 60 Gew.-%, und besonders bevorzugt 50 Gew.-% beträgt. Derartige Mischverhältnisse haben sich in Versuchen bewährt. Je größer der Anteil des zerkleinerten Korkmaterials ist, umso stärker sind die typischen Korkeigenschaften in der Profilleiste ausgeprägt.It may also be advantageous if a proportion of the shredded cork material in the layer containing the comminuted cork material, preferably the decorative layer, between 10 and 90 wt .-%, preferably between 30 and 70 wt .-%, preferably between 40 and 60 wt .-%, and especially preferably 50 wt .-% is. Such mixing ratios have proven themselves in tests. The bigger the Proportion of shredded cork material is the stronger the typical cork characteristics are pronounced in the profile strip.

Es kann von großem Nutzen sein, wenn die Dekorschicht einen Kunststoff mit einer Schmelztemperatur von weniger als +220°C, vorzugsweise weniger als +200°C, bevorzugt weniger als +150°C aufweist. Diese Schmelztemperatur liegt unterhalb eines Temperaturwerts, bei welchem viele gängige zerkleinerte Korkmaterialen, insbesondere Korkfasern, denaturieren. Bei einer derartigen Schmelztemperatur kann der als Bindemittel einzusetzende Kunststoff optimal aufgeschmolzen werden, um sich mit dem Korkmaterial zu vermischen, ohne dass das zerkleinerte Korkmaterial geschädigt wird.It can be great Be useful if the decorative layer is a plastic with a melting temperature less than + 220 ° C, preferably less than + 200 ° C, preferably less than + 150 ° C having. This melting temperature is below a temperature value, in which many common shredded cork materials, in particular cork fibers, denature. At such a melting temperature can as a binder be used optimally melted plastic to yourself to mix with the cork material without the shredded cork material damaged becomes.

Es kann sich als praktisch erweisen, wenn die Profilleiste eine Trägerschicht aufweist, die eine gegenüber der Dekorschicht unterschiedliche chemische Zusammensetzung aufweist. Als Trägerschicht kann beispielsweise ein Schicht eingesetzt werden, die der erfindungsgemäßen Profilleiste eine besonders stabile und besonders steife Struktur verleiht, so dass die Profilleiste leichter verarbeitet und montiert werden kann.It may prove to be useful if the profile strip a carrier layer which has one opposite the decorative layer has different chemical composition. As a carrier layer can For example, a layer can be used, the profile strip according to the invention gives a particularly stable and particularly stiff structure, so that The profile strip can be processed and assembled more easily.

Es kann sich als günstig erweisen, wenn die Trägerschicht und/oder die Dekorschicht ausgewählt ist aus der Gruppe der Polyolefine, der Acrylnitril-Butadien-Styrole, der Polymethylmethacrylate, der Polyethylenterephthalate, der Polyvinylchloride, der Polycarbonate, der thermoplastischen Copolyester, der Styrol-Blockcopolymere, der thermoplastische Copolyamide, der thermoplastischen Elastomere bspw. auf Basis von Styrol und/oder von Polyurethan und/oder von Polyolefine und dergleichen oder aus Mischungen dieser.It can be cheap prove when the backing layer and / or the decorative layer is selected from the group of polyolefins, acrylonitrile butadiene styrenes, polymethyl methacrylates, polyethylene terephthalates, polyvinyl chlorides, the polycarbonates, the thermoplastic copolyester, the styrene block copolymers, the thermoplastic copolyamides, the thermoplastic elastomers For example, based on styrene and / or polyurethane and / or of Polyolefins and the like, or mixtures of these.

Derartige Materialien eignen sich hervorragend als Bindemittel bzw. Matrixmaterial für den Einsatz in der erfindungsgemäßen Profilleiste, da sie das zerkleinerte Korkmaterial leicht aufnehmen können, um damit ein thermoplastisch verarbeitbares Gemisch zu bilden.such Materials are ideal as a binder or matrix material for the Insert in the profiled strip according to the invention, since they can easily pick up the shredded cork material to form a thermoplastic processable mixture.

Der thermoplastische Kunststoff ist selbst leicht verarbeitbar und weist Materialeigenschaften auf, die im Rahmen der vorliegenden Erfindung besonders vorteilhaft zur Geltung gebracht werden können.Of the Thermoplastic is itself easily processable and has Material properties in the context of the present invention can be brought to particular advantage.

Es liegt insbesondere im Rahmen der vorliegenden Erfindung, dass als Bindemittel in der Dekorschicht und als Hauptkomponente in der Trägerschicht identische Materialien, vorzugsweise identische thermoplastische Kunststoffe eingesetzt werden, und dass die Dekorschicht und die Trägerschicht stoffschlüssig verbunden und/oder einstückig hergestellt sind.It is in particular in the context of the present invention that as Binder in the decorative layer and as a main component in the carrier layer identical materials, preferably identical thermoplastic Plastics are used, and that the decorative layer and the backing cohesively connected and / or made in one piece are.

Es kann aber auch vorteilhaft sein, wenn ein Anteil des Kunststoffs in der Trägerschicht und/oder der Dekorschicht zwischen 90 und 10 Gew.-%, vorzugsweise zwischen 70 und 30 Gew.-%, bevorzugt zwischen 60 und 40 Gew.-%, und besonders bevorzugt 50 Gew.-% beträgt. Durch gezieltes Abmischen des als Bindemittel einzusetzenden Kunststoffs im Verhältnis zu dem zerkleinerten Korkmaterial, können die Eigenschaften der erfindungsgemäßen Profilleiste optimal auf den bevorzugten Anwendungsfall abgestimmt werden. Es kann nützlich sein, wenn die Dekorschicht und/oder die Trägerschicht Füll- und/oder Verstärkungsstoffe aufweist, vorzugsweise mineralische Füllstoffe wie Kreide, Talkum und dergleichen bzw. organische/anorganische Verstärkungsstoffe wie Glasfasern, Kohlefasern und dergleichen. Bei manchen Anwendungen kann eine höhere Traglastfähigkeit bzw. Steifigkeit der Profilleiste wünschenswert sein, die durch die Füll- und/oder Verstärkungsstoffe erreichbar ist.It but can also be beneficial if a share of the plastic in the carrier layer and / or the decorative layer between 90 and 10 wt .-%, preferably between 70 and 30% by weight, preferably between 60 and 40% by weight, and more preferably 50% by weight. By deliberately mixing the as a binder to be used plastic in relation to the crushed cork material, the properties of the inventive profile strip be optimally adapted to the preferred application. It can be useful be when the decorative layer and / or the carrier layer filling and / or reinforcing materials has, preferably mineral fillers such as chalk, talc and the like or organic / inorganic reinforcing agents such as glass fibers, carbon fibers and the like. In some applications can have a higher load capacity or stiffness of the profile strip may be desirable through the filling and / or reinforcing materials is reachable.

Dazu kann sich als vorteilhaft erweisen, wenn ein Anteil der Füll- und/oder Verstärkungsstoffe in der Dekorschicht und/oder der Trägerschicht zwischen 5 und 30 Gew.-%, vorzugsweise zwischen 5 und 25 Gew.-%, bevorzugt zwischen 7 und 20 Gew.-% beträgt. Eine Trägerschicht ohne Füll- und/oder Verstärkungsstoffe wird z. B. dort eingesetzt, wo eine hohe Schlagzähigkeit erwünscht ist.To may prove to be advantageous if a proportion of filling and / or Reinforcing materials in the decorative layer and / or the carrier layer between 5 and 30% by weight, preferably between 5 and 25% by weight, preferably between 7 and 20 wt .-% is. A carrier layer without filling and / or reinforcing materials is z. B. used where a high impact strength is desired.

Es kann sich als hilfreich erweisen, wenn die Trägerschicht der Dekorschicht unmittelbar benachbart angeordnet ist. So kann ohne zwischenliegende Haftvermittlerschicht ein besonders kompakter, stabiler und leicht verarbeitbarer Materialverbund geschaffen werden.It may prove helpful if the backing layer of the decorative layer is arranged immediately adjacent. So can without intermediate adhesive layer a particularly compact, stable and easily processed composite material be created.

Es kann von Vorteil sein, wenn die Profilleiste eine Breite zwischen 10 und 150 mm, vorzugsweise zwischen 20 und 100 mm, bevorzugt 43 mm aufweist. Diese Abmessungen sind für die meisten gängigen Anwendungsfälle vorteilhaft, z. B. für den Anwendungsfall als Kantenband zur Verkleidung von Möbelkanten. Dazu wird die Profilleiste vorzugsweise mit ca. 5 bis 30% Übermaß gegenüber der Breite einer zu dekorierenden Kante gefertigt, wobei der sich bei der Montage ergebende Überstand i. d. R. im Wege einer spanabhebenden Nachbearbeitung nachträglich entfernt wird (z. B. 19 mm Spanplatte, 23 mm Kante).It may be advantageous if the profile strip has a width between 10 and 150 mm, preferably between 20 and 100 mm, preferably 43 mm. These dimensions are advantageous for most common applications, eg. B. for the application as edge band for covering furniture edges. For this purpose, the profile strip is preferably made with about 5 to 30% excess over the width of an edge to be decorated, wherein the resulting during assembly supernatant usually in Removal of subsequent machining (eg 19 mm chipboard, 23 mm edge).

Es kann sich als nützlich erweisen, wenn die Profilleiste eine Dicke zwischen 0,1 und 10,0 mm, vorzugsweise zwischen 0,5 und 5,0 mm, bevorzugt 1,5 mm aufweist. Bei einer derartigen Dicke ist die Profilleiste beispielsweise sehr leicht von einem gestreckten Zustand in einen aufgerollten Zustand überführbar, und umgekehrt, ohne Schaden zu erleiden. So ist die Profilleiste transportfähig und lagerfähig.It can come in handy prove if the profile strip has a thickness between 0.1 and 10.0 mm, preferably between 0.5 and 5.0 mm, preferably 1.5 mm. With such a thickness, the profile strip, for example, is very easily convertible from a stretched state to a rolled state, and conversely, without suffering damage. So the profile strip is transportable and storable.

Es kann aber auch vorteilhaft sein, wenn ein Verhältnis einer Dicke der Dekorschicht zu einer Dicke der Trägerschicht zwischen 0,1 und 10, vorzugsweise zwischen 1 und 5, bevorzugt 4 beträgt. Je nach dem bevorzugten Anwendungsfall und dem gewünschten Eigenschaftsprofil kann das Verhältnis der Dicke der Dekorschicht zu der Dicke der Trägerschicht innerhalb der vorgegebenen Grenzen eingestellt werden. Es hat sich in Versuchen als besonders vorteilhaft herausgestellt, wenn das Verhältnis der Dicke der Dekorschicht zu der Dicke der Trägerschicht etwa 4 beträgt, wobei die Dekorschicht ca. 1,2 mm dick ist.It but may also be advantageous if a ratio of a thickness of the decorative layer to a thickness of the carrier layer between 0.1 and 10, preferably between 1 and 5, preferably 4 is. Depending on the preferred application and the desired Property profile can change the ratio of Thickness of the decorative layer to the thickness of the carrier layer within the specified Limits are set. It has proven to be particularly advantageous in experiments exposed when the ratio the thickness of the decorative layer to the thickness of the carrier layer is about 4, wherein the decorative layer is about 1.2 mm thick.

Es kann vorteilhaft sein, wenn die Dekorschicht und/oder die Trägerschicht wenigstens einen Farbstoff enthält, beispielsweise ein Pigment. Dadurch kann auf einfachem Wege eine bevorzugte Einfärbung der Profilleiste erreicht werden, wobei der Anteil an Pigmenten etwa 0,01 bis 10% betragen kann.It may be advantageous if the decorative layer and / or the carrier layer contains at least one dye, for example, a pigment. This can be a simple way preferred coloring the profile strip can be achieved, the proportion of pigments may be about 0.01 to 10%.

Es kann auch praktisch sein, wenn die Trägerschicht in einem Farbton eingefärbt ist, welcher im Wesentlichen einem Grundfarbton der Dekorschicht entspricht. Dadurch kann der Naturfarbton des zerkleinerten Korkmaterials zusätzlich verstärkt und hervorgehoben werden, was den optischen und ästhetischen Gesamteindruck der erfindungsgemäßen Profilleiste weiter aufwertet.It can also be handy if the backing layer in a hue colored is, which essentially corresponds to a basic color of the decorative layer. As a result, the natural color of the crushed cork material additionally reinforced and be emphasized, what the visual and aesthetic overall impression the profile strip according to the invention further enhances.

Es kann sich als nützlich erweisen, wenn die Profilleiste, vorzugsweise an einer Sichtseite, eine Prägung aufweist. Die Prägung beeinflusst die haptische Wahrnehmung beim Berühren der Profilleiste. Dazu kann es sich als vorteilhaft herausstellen, wenn die Prägung eine Korkoberflächenstruktur nachbildet. Durch die Prägung kann echter Kork im Hinblick auf Optik und Haptik noch besser nachgebildet werden.It can come in handy prove when the profile strip, preferably on a visible side, an imprint having. The imprint influences the haptic perception when touching the profile strip. To It may prove advantageous if the embossing a Korkoberflächenstruktur replicates. By imprinting real cork can be simulated even better in terms of look and feel become.

Es kann sich als praktisch erweisen, wenn die Profilleiste eine Imprägnierung und/oder Beschichtung mit Wachs und/oder Lack aufweist. Durch diese Maßnahme wird die Profilleiste gegenüber schädlichen Umwelteinflüssen geschützt und die Alterung wird verlangsamt. Dadurch kann die Lebensdauer der Profilleiste erheblich verlängert werden. Eine Prägung der Profilleiste kann vor und/oder nach der Imprägnierung und/oder Beschichtung erfolgen. Zudem kann es nützlich sein, wenn die Profilleiste an einer der Sichtseite abgewandten Unterseite einen Haftvermittler aufweist. Dadurch kann die Profilleiste schnell und ohne weitere Hilfsmittel an einem Gegenstand montiert werden.It can prove to be useful if the molding is impregnated and / or coating with wax and / or lacquer. Through this measure will be harmful to the profile strip environmental influences protected and aging is slowing down. This can extend the life the profile strip considerably extended become. An imprint the profile strip can before and / or after the impregnation and / or coating respectively. It can also be useful be when the profile strip facing away from the visible side Bottom has a bonding agent. This allows the profile bar fast and be mounted on an object without further aids.

Eine weitere Ausführung der Erfindung betrifft einen Gegenstand, insbesondere ein Möbelstück, eine Möbelbauplatte, ein Holzwerkstoffelement oder dergleichen, mit einer Profilleiste nach einer der vorangegangenen Ausführungen. Durch die Profilleiste können offenliegende Kanten des Gegenstands optisch kaschiert und versiegelt werden, um ein Eindringen von Feuchtigkeit und/oder Schmutz zu verhindern. So wird der Gegenstand durch die Profilleiste geschützt und in optischer sowie ästhetischer Hinsicht aufgewertet. Im Rahmen der Erfindung wird der Begriff Möbelbauplatte bzw. Holzwerkstoffelement so verstanden, dass das Element aus natürlichem Holz bzw. aus Einzelelementen aus natürlichem Holz oder aus einem aus Holz hergestellten Material besteht. Elemente, die aus Holz bestehenden Einzelelementen hergestellt sind, können beispielsweise Tischlerplatten sein. Materialien, die aus Holz hergestellt werden, können mitteldichte Faserplatten (MDF), hochdichte Faserplatten (HDF), Hartfaserplatten, Spanplatten sein.A further execution The invention relates to an article, in particular a piece of furniture, a furniture board, a wood material element or the like, with a profile strip according to one of the preceding embodiments. Through the profile strip can exposed edges of the object optically laminated and sealed to prevent ingress of moisture and / or dirt. Thus, the object is protected by the profile strip and in optical as well as aesthetic Upgraded. In the context of the invention, the term furniture board or wood-based material element understood that the element of natural Wood or single elements made of natural wood or from one made of wood material. Elements made of wood existing individual elements are made, for example, carpenter plates be. Materials made of wood can be medium density Fiberboard (MDF), high-density fibreboard (HDF), hardboard, Be chipboard.

Es kann sich als nützlich erweisen, wenn die Profilleiste mit einer der Sichtseite abgewandten Unterseite an einer Kante des Gegenstands angebracht ist. Die das zerkleinerte Korkmaterial enthaltende Schicht definiert vorzugsweise die Sichtseite der Profilleiste und vermittelt so den Eindruck, den Kork im Hinblick auf Haptik, Optik und Geruch vermitteln würde. Durch den erfindungsgemäßen Schichtaufbau ist die erfindungsgemäße Profilleiste allerdings wesentlich leichter handhabbar und verarbeitbar als eine vollständig aus Kork bestehende Profilleiste.It can come in handy prove when the profile strip facing away from the visible side Bottom is attached to an edge of the article. The the Crushed cork material containing layer preferably defines the visible side of the profile strip and gives the impression the cork in terms of feel, appearance and smell would convey. By the layer structure according to the invention is the profile strip according to the invention however, much easier to handle and process than a complete one Cork existing profile strip.

Eine weitere Ausführung der Erfindung betrifft ein Verfahren zur Herstellung einer Profilleiste, wobei das Verfahren die folgenden Schritte umfasst:

  • a) Überführen eines Werkstoffgemischs mit einem Anteil an zerkleinertem Korkmaterial in einen Zustand, in welchem das Werkstoffgemisch im Extrusionsverfahren thermoplastisch verarbeitbar ist,
  • b) Überführen eines thermoplastischen Werkstoffs in einen Zustand, in welchem der thermoplastische Werkstoff im Extrusionsverfahren verarbeitbar ist,
  • c) Verarbeiten des Werkstoffgemischs und des thermoplastischen Werkstoffs
im Wege der Koextrusion zu einer Profilleiste nach einer der vorangegangenen Ausführungen. Das bevorzugte Ausführungsbeispiel der vorliegenden Erfindung wird nachstehend mit Bezug auf die beiliegende Zeichnung beschrieben.A further embodiment of the invention relates to a method for producing a profiled strip, the method comprising the following steps:
  • a) transfer of a material mixture with a proportion of comminuted cork material into a state in which the material mixture is thermoplastically processable in the extrusion process,
  • b) transferring a thermoplastic material into a state in which the thermoplastic material can be processed by the extrusion process,
  • c) processing the material mixture and the thermoplastic material
in the way of coextrusion to a profile strip after egg ner of the previous versions. The preferred embodiment of the present invention will be described below with reference to the accompanying drawings.

Kurze Beschreibung der ZeichnungShort description of the drawing

1 zeigt einen Gegenstand mit der erfindungsgemäßen Profilleiste, wobei der Gegenstand als Möbelplatte und die Profilleiste als Kantenband ausgebildet ist 1 shows an article with the profile strip according to the invention, wherein the article is designed as a furniture panel and the profile strip as edge band

Detaillierte Beschreibung des bevorzugten AusführungsbeispielsDetailed description of the preferred embodiment

Die Erfindung betrifft eine Profilleiste 1 für die Möbelindustrie, wobei die Profilleiste 1 einen mehrschichtigen Aufbau aufweist, wobei zumindest eine Schicht 2 der Profilleiste 1 ein zerkleinertes Korkmaterial 4 enthält und zumindest eine Schicht 2 der Profilleiste 1 im Extrusionsverfahren gefertigt ist.The invention relates to a profile strip 1 for the furniture industry, with the profile strip 1 has a multilayer structure, wherein at least one layer 2 the profile strip 1 a crushed cork material 4 contains and at least one layer 2 the profile strip 1 is manufactured by extrusion.

Der Schichtaufbau der erfindungsgemäßen Profilleiste 1 wird im Folgenden erläutert:
Eine an einer Sichtseite 3 der Profilleiste 1 sichtbare Dekorschicht 2 enthält Korkteilchen als zerkleinertes Korkmaterial 4, einen thermoplastischen Kunststoff als Bindemittel/Matrix und weitere Additive/Zuschlagstoffe, um ein bevorzugtes Eigenschaftsprofil der Dekorschicht 2 einzustellen.The layer structure of the profile strip according to the invention 1 is explained below:
One on a visible side 3 the profile strip 1 visible decorative layer 2 contains cork particles as shredded cork material 4 , a thermoplastic as a binder / matrix and other additives / additives to a preferred property profile of the decorative layer 2 adjust.

Das zerkleinerte Korkmaterial 4 ist in feiner, vorzugsweise gleichmäßiger Verteilung, in der Matrix eingebettet. Ein Anteil des zerkleinerten Korkmaterials 4 in der Dekorschicht 2 beträgt zwischen 10 und 90 Gew.-%, vorzugsweise zwischen 30 und 70 Gew.-%, bevorzugt zwischen 40 und 60 Gew.-%, und besonders bevorzugt 50 Gew.-%. Ein Anteil des thermoplastischen Kunststoffs in der Dekorschicht 2 beträgt vorzugsweise zwischen 90 und 10 Gew.-%, vorzugsweise zwischen 70 und 30 Gew.-%, bevorzugt zwischen 60 und 40 Gew.-%, und besonders bevorzugt ca. 50 Gew.-%. Der als Bindemittel in der Dekorschicht 2 enthaltene thermoplastische Kunststoff ist bevorzugt ein thermoplastisches Elastomer, insbesondere ein thermoplastisches Elastomer auf Styrolbasis bspw. ein SEES (Styrol-Ethylen-Butylen-Styrol). Der Kunststoff weist eine Schmelztemperatur von weniger +250°C auf. Die Schmelztemperatur ist so gewählt, um die Korkteilchen beim Aufschmelzen des Kunststoffs nicht zu schädigen.The crushed cork material 4 is embedded in the matrix in a fine, preferably even distribution. A portion of the shredded cork material 4 in the decorative layer 2 is between 10 and 90 wt .-%, preferably between 30 and 70 wt .-%, preferably between 40 and 60 wt .-%, and particularly preferably 50 wt .-%. A proportion of the thermoplastic in the decorative layer 2 is preferably between 90 and 10 wt .-%, preferably between 70 and 30 wt .-%, preferably between 60 and 40 wt .-%, and particularly preferably about 50 wt .-%. The as a binder in the decorative layer 2 contained thermoplastic material is preferably a thermoplastic elastomer, in particular a thermoplastic elastomer based on styrene, for example, a SEES (styrene-ethylene-butylene-styrene). The plastic has a melting temperature of less + 250 ° C. The melting temperature is chosen so as not to damage the cork particles when the plastic melts.

Eine Trägerschicht 5 weist eine gegenüber der Dekorschicht 2 unterschiedliche chemische Zusammensetzung auf, enthält aber vorzugsweise identische Materialbestanteile wie die Dekorschicht 2. Die Trägerschicht 5 besteht vorzugsweise aus dem gleichen thermoplastischen Kunststoff, der in der Dekorschicht 2 als Bindemittel eingesetzt wird, wobei die Dekorschicht 2 und die Trägerschicht 5 vorzugsweise im Koextrusionsverfahren einstückig hergestellt und stoffschlüssig verbunden sind. Bei Bedarf ist die Trägerschicht 5 verstärkt, beispielsweise durch Beimischung von mineralischen Füllstoffen wie Talkum, Kreide und dergleichen oder Verstärkungsstoffen wie Fasern, vorzugsweise Glasfasern. Der Anteil des Verstärkungsmaterials in der Trägerschicht 5 beträgt vorzugsweise zwischen 3 und 25 Gew.-%. Die Dekorschicht 2 kann ebenfalls durch Beimischung von Füll- und/oder Verstärkungsstoffen wie Talkum oder Fasern, vorzugsweise Glasfasern, verstärkt sein, wobei der Anteil des Verstärkungsmaterials in der Dekorschicht 2 vorzugsweise ebenfalls zwischen 3 und 25 Gew.-% beträgt.A carrier layer 5 has one opposite the decorative layer 2 different chemical composition, but preferably contains identical material components as the decorative layer 2 , The carrier layer 5 preferably consists of the same thermoplastic material, in the decorative layer 2 is used as a binder, wherein the decorative layer 2 and the carrier layer 5 preferably produced in one piece in the coextrusion process and bonded cohesively. If necessary, the carrier layer 5 reinforced, for example by admixing mineral fillers such as talc, chalk and the like or reinforcing materials such as fibers, preferably glass fibers. The proportion of the reinforcing material in the carrier layer 5 is preferably between 3 and 25 wt .-%. The decorative layer 2 can also be reinforced by admixture of fillers and / or reinforcing materials such as talc or fibers, preferably glass fibers, wherein the proportion of the reinforcing material in the decorative layer 2 preferably also between 3 and 25 wt .-% is.

Die Profilleiste 1 kann bei Bedarf eine Imprägnierung und/oder Schutzbeschichtung mit Wachs und/oder Lack aufweisen. Die Imprägnierung und/oder Schutzbeschichtung wird vorzugsweise auf die Sichtseite 3 der Profilleiste 1 aufgetragen.The profile bar 1 If necessary, it may have an impregnation and / or protective coating with wax and / or lacquer. The impregnation and / or protective coating is preferably on the visible side 3 the profile strip 1 applied.

Ebenfalls bei Bedarf kann die Profilleiste 1 eine Prägung aufweisen. Die Prägung der Profilleiste 1 kann unabhängig von einer Imprägnierung und/oder Schutzbeschichtung der Profilleiste 1 erfolgen. Die Prägung kann aber auch zusätzlich zu einer Imprägnierung und/oder Schutzbeschichtung vorgesehen werden und erfolgt dann wahlweise vor und/oder nach der Imprägnierung und/oder Schutzbeschichtung.Also if necessary, the profile strip 1 have an imprint. The embossing of the profile strip 1 can be independent of impregnation and / or protective coating of the profile strip 1 respectively. However, the embossing can also be provided in addition to an impregnation and / or protective coating and is then optionally before and / or after the impregnation and / or protective coating.

Weiterhin bei Bedarf kann zumindest eine Schicht der Profilleiste 1 einen Farbstoff enthalten, um möglichst eine originalgetreue Einfärbung der Profilleiste 1 in einem gängigen Korkfarbton zu erhalten.Furthermore, if necessary, at least one layer of the profile strip 1 contain a dye, if possible to a true to the original coloring of the profile strip 1 to get in a common cork color.

Auf der Unterseite der Profilleiste 1 kann eine Haftvermittlerschicht vorgesehen sein.On the bottom of the profile strip 1 a primer layer may be provided.

1 zeigt einen erfindungsgemäßen Gegenstand 7 mit einer Oberseite 8, einer Stirnseite 9 und einer Unterseite 10, ebenso wie die an der Stirnseite 9 des Gegenstands 7 angebrachte, erfindungsgemäße Profilleiste 1. Der Gegenstand 7 ist im vorliegenden Ausführungsbeispiel eine im Wesentlichen aus Holz gefertigte Möbelplatte, z. B. Küchenarbeitsplatte oder Tischplatte. 1 shows an article according to the invention 7 with a top 8th , a front page 9 and a bottom 10 , as well as the one at the front 9 of the object 7 attached, inventive profile strip 1 , The object 7 is in the present embodiment, a substantially made of wood furniture plate, z. B. kitchen worktop or table top.

Die Profilleiste 1 ist mit der Unterseite 6 an der Stirnseite 9 des Gegenstands 7 angebracht, vorzugsweise angeklebt oder angeschweißt, und ist derart nachbearbeitet, dass die Seitenränder der Profilleiste 1 mit der Oberseite 8 und der Unterseite 10 des Gegenstands 7 bündig abschließen. Die längsrandseitigen Sichtkanten der Profilleiste 1 sind durch spanabhebende Bearbeitung abgerundet.The profile bar 1 is with the bottom 6 at the front 9 of the object 7 attached, preferably glued or welded, and is reworked such that the side edges of the profile strip 1 with the top 8th and the bottom 10 of the object 7 finish flush. The longitudinal edge visible edges of the profile strip 1 are rounded off by machining.

In diesem Ausführungsbeispiel umfasst die erfindungsgemäße Profilleiste 1 eine Dekorschicht 2 mit einem Korkanteil von 60 Gew.-% und einem Anteil eines thermoplastischen Kunststoffs SEES (Styrol-Ethylen-Butylen-Styrol) von 40 Gew.-% sowie geringe Bestandteile eines Phasenvermittlers. Die Trägerschicht 2 besteht zu 100% aus dem thermoplastisch verarbeitbarem Werkstoff Polypropylen.In this embodiment, the profile strip according to the invention comprises 1 a decorative layer 2 with a cork content of 60 wt .-% and a proportion of a thermoplastic SEES (styrene-ethylene-butylene-styrene) of 40 wt .-% and small components of a phase mediator. The carrier layer 2 consists of 100% thermoplastic material polypropylene.

Die Profilleiste 1 ist im Koextrusionsverfahren gefertigt, und die Trägerschicht 5 und die Dekorschicht 2 sind unmittelbar benachbart angeordnet. Die Profilleiste 1 weist im nicht nachgearbeiteten Zustand eine Breite von ca. 43 mm auf.The profile bar 1 is manufactured in the coextrusion process, and the carrier layer 5 and the decorative layer 2 are arranged immediately adjacent. The profile bar 1 has a width of approx. 43 mm when not reworked.

Durch spanabhebende Nachbearbeitung wird die Breite der Profilleiste 1 auf die Breite der stirnseitigen Kante 9 des als Möbelplatte ausgebildeten Gegenstandes 7 abgestimmt, und beträgt im nachgearbeiteten Zustand ca. 40 mm. Die Gesamtdicke der Profilleiste 1, die sich senkrecht zur Sichtseite 3 bzw. Unterseite 6 der Profilleiste 1 bemisst, beträgt ca. 1,5 mm. Ein Verhältnis einer Dicke der Dekorschicht 2 zu einer Dicke der Trägerschicht 5 beträgt ca. vier, wobei die Dekorschicht 2 eine Dicke von ca. 1,2 mm aufweist und die Trägerschicht 5 eine Dicke von ca. 0,3 mm aufweist. Die Trägerschicht 5 ist in einem Farbton eingefärbt, welcher im Wesentlichen dem Grundfarbton der Korkteilchen 4 und dem Grundfarbton der Dekorschicht 2 entspricht. Der Gesamtfarbton der Profilleiste 1 ist auf einen Gesamtfarbton der Oberfläche 8 des Gegenstands 7 abgestimmt.By machining, the width of the profile strip becomes 1 on the width of the front edge 9 of the formed as a furniture plate object 7 matched, and is in the reworked state about 40 mm. The total thickness of the profile strip 1 , which are perpendicular to the visible side 3 or bottom 6 the profile strip 1 measures approx. 1.5 mm. A ratio of a thickness of the decorative layer 2 to a thickness of the carrier layer 5 is about four, with the decorative layer 2 has a thickness of about 1.2 mm and the carrier layer 5 has a thickness of about 0.3 mm. The carrier layer 5 is colored in a hue which is essentially the basic hue of the cork particles 4 and the basic color of the decorative layer 2 equivalent. The overall color of the profile strip 1 is on a total shade of the surface 8th of the object 7 Voted.

Ein Verfahren zur Herstellung der erfindungsgemäßen Profilleiste 1 umfasst die folgenden Schritte im Wege der Koextrusion:

  • a) Überführen eines Werkstoffgemischs mit einem Anteil an zerkleinertem Korkmaterial 4 in einen Zustand, in welchem das Werkstoffgemisch im Extrusionsverfahren verarbeitbar ist,
  • b) Überführen eines thermoplastischen Werkstoffs in einen Zustand, in welchem der thermoplastische Werkstoff im Extrusionsverfahren verarbeitbar ist, und
  • c) Verarbeiten des Werkstoffgemischs und des thermoplastischen Werkstoffs
A method for producing the profile strip according to the invention 1 includes the following steps by way of coextrusion:
  • a) transfer of a mixture of materials with a proportion of crushed cork material 4 in a state in which the material mixture is processable by extrusion,
  • b) transferring a thermoplastic material to a state in which the thermoplastic material is processed by extrusion, and
  • c) processing the material mixture and the thermoplastic material

Das zerkleinerte Korkmaterial 4 kann als Vielzahl von Korkteilchen bzw. -fasern, Granulat, Mehl oder dergleichen vorliegen und wird vorzugsweise aus Korkabfällen gewonnen.The crushed cork material 4 may be present as a plurality of cork particles or granules, flour or the like and is preferably obtained from cork waste.

In Schritt a) wird ein als Granulat vorliegendes Kork-/Kunststoffgemisch für die Dekorschicht 2 erhitzt, so dass der als Bindemittel eingesetzte, thermoplastische Kunststoff in den flüssigen oder zumindest zählplastischen Zustand versetzt wird. Die Massetemperatur des Werkstoffgemischs sollte eine Temperatur von +220°C nicht überschreiten, um eine Beeinträchtigung des zerkleinerten Korkmaterials 4 zu verhindern.In step a) is present as granules cork / plastic mixture for the decorative layer 2 heated so that the binder used as a thermoplastic material is placed in the liquid or at least count plastic state. The melt temperature of the material mixture should not exceed a temperature of + 220 ° C in order to impair the shredded cork material 4 to prevent.

In Schritt b) wird der thermoplastische Werkstoff für die Trägerschicht 5 aufgeschmolzen bzw. in den flüssigen oder zumindest zählplastischen Zustand versetzt.In step b), the thermoplastic material for the carrier layer 5 melted or placed in the liquid or at least counted plastic state.

In Schritt c) werden das Werkstoffgemisch für die Dekorschicht 2 und der thermoplastische Kunststoff für die Trägerschicht 2 im Koextrusionsverfahren zusammengeführt, so dass die Dekorschicht 2 und die Trägerschicht 2 stoffschlüssig verbunden und einstückig ausgebildet sind.In step c), the material mixture for the decorative layer 2 and the thermoplastic for the carrier layer 2 merged in the coextrusion process, so that the decorative layer 2 and the carrier layer 2 cohesively connected and integrally formed.

In einem Schritt d) kann die Profilleiste 1 mit einer Imprägnierung beaufschlagt und/oder an der Sichtseite 3 mit einem transparenten Wachs und/oder Lack beschichtet werden.In a step d), the profile strip 1 treated with an impregnation and / or on the visible side 3 coated with a transparent wax and / or varnish.

In einem Schritt e) kann die Profilleiste 1 an der Sichtseite 3 mit einer Prägung versehen werden, die einer Korkoberfläche nachempfunden ist und eine Korkoberflächenstruktur nachbildet. Dabei wird die Profilleiste 1, insbesondere die Dekorschicht 2 verdichtet.In a step e), the profile strip 1 on the visible side 3 be imprinted, which is modeled after a cork surface and a cork surface pattern simulates. This is the profile bar 1 , in particular the decorative layer 2 compacted.

Schritt e) kann vor und/oder nach Schritt d) ausgeführt werden.step e) can be carried out before and / or after step d).

Schritt d) und/oder Schritt e) kann auch weggelassen werden.step d) and / or step e) can also be omitted.

Claims (16)

Profilleiste (1), vorzugsweise Kantenband, mit einem mehrschichtigen Aufbau, wobei zumindest eine Schicht (2) der Profilleiste (1) ein zerkleinertes Korkmaterial (4) enthält und zumindest eine Schicht (2) der Profilleiste (1) im Extrusionsverfahren gefertigt ist.Profile strip ( 1 ), preferably edge band, having a multilayer structure, wherein at least one layer ( 2 ) of the profile strip ( 1 ) a shredded cork material ( 4 ) and at least one layer ( 2 ) of the profile strip ( 1 ) is manufactured by extrusion. Profilleiste (1) nach Anspruch 1, dadurch gekennzeichnet, dass die Profilleiste (1) im Koextrusionsverfahren gefertigt ist.Profile strip ( 1 ) according to claim 1, characterized in that the profiled strip ( 1 ) is manufactured in the coextrusion process. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Profilleiste (1) eine Dekorschicht (2) aufweist, die das zerkleinerte Korkmaterial (4) enthält und die an einer Sichtseite (3) der Profilleiste (1) sichtbar ist.Profile strip ( 1 ) according to one of the preceding claims, characterized in that the profiled strip ( 1 ) a decorative layer ( 2 ) comprising the comminuted cork material ( 4 ) and on a visible side ( 3 ) of the profile strip ( 1 ) is visible. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass ein Anteil des zerkleinerten Korkmaterials (4) in der Dekorschicht (2) zwischen 10 und 90 Gew.-%, vorzugsweise zwischen 30 und 70 Gew.-%, bevorzugt zwischen 40 und 60 Gew.-%, und besonders bevorzugt 50 Gew.-% beträgt.Profile strip ( 1 ) according to one of the preceding claims, characterized in that a portion of the comminuted cork material ( 4 ) in the decorative layer ( 2 ) between 10 and 90 wt .-%, preferably between 30 and 70 wt .-%, preferably between 40 and 60 wt .-%, and particularly preferably 50 wt .-% is. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Profilleiste (1) eine Trägerschicht (5) aufweist, die eine gegenüber der Dekorschicht (2) unterschiedliche chemische Zusammensetzung aufweist.Profile strip ( 1 ) according to one of the preceding claims, characterized in that the profiled strip ( 1 ) a carrier layer ( 5 ), which one opposite the decorative layer ( 2 ) has different chemical composition. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Trägerschicht (5) und/oder die Dekorschicht (2) ausgewählt ist aus der Gruppe der Polyolefine, der Acrylnitril-Butadien-Styrole, der Polymethylmethacrylate, der Polyethylenterephthalate, der Polyvinylchloride, der Polycarbonate, der thermoplastischen Copolyester, der Styrol-Blockcopolymere, der thermoplastische Copolyamide, der thermoplastischen Elastomere und dergleichen oder aus Mischungen dieser.Profile strip ( 1 ) according to one of the preceding claims, characterized in that the carrier layer ( 5 ) and / or the decorative layer ( 2 ) is selected from the group of polyolefins, acrylonitrile-butadiene-styrenes, polymethyl methacrylates, polyethylene terephthalates, polyvinyl chlorides, polycarbonates, thermoplastic copolyesters, styrene block copolymers, thermoplastic copolyamides, thermoplastic elastomers and the like, or mixtures thereof , Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass ein Anteil des Kunststoffs in der der Trägerschicht (5) und/oder in der Dekorschicht (2) zwischen 90 und 10 Gew.-%, vorzugsweise zwischen 70 und 30 Gew.-%, bevorzugt zwischen 60 und 40 Gew.-%, und besonders bevorzugt 50 Gew.-% beträgt.Profile strip ( 1 ) according to one of the preceding claims, characterized in that a portion of the plastic in the carrier layer ( 5 ) and / or in the decorative layer ( 2 ) between 90 and 10 wt .-%, preferably between 70 and 30 wt .-%, preferably between 60 and 40 wt .-%, and particularly preferably 50 wt .-% is. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Dekorschicht (2) und/oder die Trägerschicht (5) Füll- und/oder Verstärkungsstoffe aufweist.Profile strip ( 1 ) according to one of the preceding claims, characterized in that the decorative layer ( 2 ) and / or the carrier layer ( 5 ) Has fillers and / or reinforcing materials. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass ein Anteil der Füll- und/oder Verstärkungsstoffe in der Dekorschicht (2) und/oder der Trägerschicht (5) zwischen 3 und 30 Gew.-%, vorzugsweise zwischen 5 und 25 Gew.-%, bevorzugt zwischen 7 und 20 Gew.-% beträgt.Profile strip ( 1 ) according to one of the preceding claims, characterized in that a proportion of the fillers and / or reinforcing materials in the decorative layer ( 2 ) and / or the carrier layer ( 5 ) is between 3 and 30% by weight, preferably between 5 and 25% by weight, preferably between 7 and 20% by weight. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Trägerschicht (5) der Dekorschicht (2) unmittelbar benachbart angeordnet ist.Profile strip ( 1 ) according to one of the preceding claims, characterized in that the carrier layer ( 5 ) of the decorative layer ( 2 ) is arranged immediately adjacent. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass ein Verhältnis einer Dicke der Dekorschicht (2) zu der der Trägerschicht (5) zwischen 0,1 und 10, vorzugsweise zwischen 1 und 5 beträgt.Profile strip ( 1 ) according to one of the preceding claims, characterized in that a ratio of a thickness of the decorative layer ( 2 ) to the support layer ( 5 ) is between 0.1 and 10, preferably between 1 and 5. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Dekorschicht (2) und/oder die Trägerschicht (5) wenigstens einen Farbstoff enthält.Profile strip ( 1 ) according to one of the preceding claims, characterized in that the decorative layer ( 2 ) and / or the carrier layer ( 5 ) contains at least one dye. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Trägerschicht (5) in einem Farbton eingefärbt ist, welcher im Wesentlichen einem Grundfarbton der Dekorschicht (2) entspricht.Profile strip ( 1 ) according to one of the preceding claims, characterized in that the carrier layer ( 5 ) is colored in a hue which is essentially a basic hue of the decorative layer ( 2 ) corresponds. Profilleiste (1) nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Profilleiste (1), vorzugsweise an einer Sichtseite (3), eine Prägung aufweist.Profile strip ( 1 ) according to one of the preceding claims, characterized in that the profiled strip ( 1 ), preferably on a visible side ( 3 ), has an imprint. Gegenstand (7), insbesondere Möbelstück oder dergleichen, mit einer Profilleiste (1) nach einem der vorangegangenen Ansprüche.Object ( 7 ), in particular furniture or the like, with a profile strip ( 1 ) according to any one of the preceding claims. Gegenstand (7) nach Anspruch 15, wobei die Profilleiste (1) mit einer der Sichtseite (3) abgewandten Unterseite (6) an dem Gegenstand (7) angebracht ist.Object ( 7 ) according to claim 15, wherein the profiled strip ( 1 ) with one of the visible side ( 3 ) facing away from the bottom ( 6 ) on the object ( 7 ) is attached.
DE102008038010A 2008-08-16 2008-08-16 Profile strip i.e. edge strip, for decorating e.g. kitchen countertop, has decorative layer containing crushed cork material, manufactured by extrusion process and viewable from visible side of strip Withdrawn DE102008038010A1 (en)