DE102005045477A1 - Gold alloy for manufacture of jewelry contains 75 to 91 per cent weight of the elements gold, silver, zinc and copper - Google Patents

Gold alloy for manufacture of jewelry contains 75 to 91 per cent weight of the elements gold, silver, zinc and copper Download PDF

Info

Publication number
DE102005045477A1
DE102005045477A1 DE200510045477 DE102005045477A DE102005045477A1 DE 102005045477 A1 DE102005045477 A1 DE 102005045477A1 DE 200510045477 DE200510045477 DE 200510045477 DE 102005045477 A DE102005045477 A DE 102005045477A DE 102005045477 A1 DE102005045477 A1 DE 102005045477A1
Authority
DE
Germany
Prior art keywords
weight
gold
alloy
zinc
copper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE200510045477
Other languages
German (de)
Inventor
Ruth Humpfle
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QVC Handel GmbH
Original Assignee
QVC Handel GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QVC Handel GmbH filed Critical QVC Handel GmbH
Priority to DE200510045477 priority Critical patent/DE102005045477A1/en
Publication of DE102005045477A1 publication Critical patent/DE102005045477A1/en
Withdrawn legal-status Critical Current

Abstract

A gold alloy contains 75 to 91% Wt. Of the elements gold, silver, zinc and copper. The alloy contains e.g. 75-91 % Wt. Ag, Zn and Cu, plus 0-14% Ni, 0-0.2% Si, and the remainder 100% Au.

Description

Die vorliegende Erfindung betrifft eine Gold enthaltende Legierung.The The present invention relates to a gold-containing alloy.

Goldlegierungen, die für die Schmuckherstellung verwendet werde, enthalten mindestens 33,3 Gew.-% Gold. Legierungen mit geringerem Goldanteil sind für diesen Zweck nicht bekannt. Es ist bislang nicht gelungen, eine Goldlegierung mit einem geringeren Goldanteil zu schaffen, die in wesentlichen Faktoren die für die Schmuckherstellung erforderlichen Eigenschaften wie Bearbeitbarkeit, Korrosionsbeständigkeit, Hautverträglichkeit und nicht zuletzt Aussehen aufweisen.Gold alloys, the for jewelery production contains at least 33.3% by weight Gold. Alloys with lower gold content are for this Purpose unknown. It has not succeeded so far, a gold alloy with a lower gold content to create that in essence Factors for the jewelry manufacturing required properties such as machinability, Corrosion resistance, skin compatibility and not least have appearance.

Es ist deshalb Aufgabe der vorliegenden Erfindung, Goldlegierungen zu schaffen, die bei geringerem Goldgehalt für die Schmuckherstellung geeignet sind.It is therefore an object of the present invention, gold alloys to create, which is suitable for jewelery production with lower gold content are.

Diese Aufgabe wird von einer Legierung mit den Merkmalen des Anspruchs 1 gelöst.These Task is an alloy with the features of the claim 1 solved.

Weil die Schmucklegierung außer Gold in der Summe 75 Gew.-% bis 91 Gew.-% der Elemente Silber, Zink und Kupfer enthält, ergibt sich eine preiswerte Legierung mit dennoch guten Eigenschaften in der Schmuckherstellung und bei der späteren Verwendung als Schmuckgegenstand.Because the jewelry alloy except Gold in the sum of 75 wt .-% to 91 wt .-% of the elements silver, zinc and copper, results in a low-cost alloy with good properties in jewelry making and later use as a jewelry item.

Insbesondere ist es vorteilhaft, eine Legierung mit in der Summe 75– 91 Gew.-% wenigstens eines Elements ausgewählt aus der Gruppe, die Ag, Zn und Cu umfasst, 0–14% Ni, 0–0,2% Si, und den Rest zu 100% an Au zu wählen.Especially it is advantageous to use an alloy with a total of 75-91% by weight selected at least one element from the group comprising Ag, Zn and Cu, 0-14% Ni, 0-0.2% Si, and the remainder 100% Au to choose.

Vorzugsweise liegt der Goldgehalt zwischen 10,0 und 12,0 Gew.-%.Preferably the gold content is between 10.0 and 12.0 wt .-%.

Insbesondere kann der der Goldgehalt 11,1 Gew.-% betragen.Especially the gold content may be 11.1% by weight.

Die in den weiteren abhängigen Ansprüchen aufgeführten Merkmale betreffen besondere Ausführungsformen für bestimmte Farbvarianten (Rot-, Gelb- und Weissgold) und verschiedene Verarbeitungsmöglichkeiten (Gusslegierung und Walz- oder Knetlegierung).The in the other dependent claims listed Features pertain to particular embodiments for particular ones Color variants (red, yellow and white gold) and various processing options (Cast alloy and rolled or wrought alloy).

Nachfolgend werden sechs Ausführungsformen anhand ihrer Zusammensetzung näher beschrieben.following become six embodiments closer by their composition described.

Beispiel 1:Example 1:

Eine Blech-Gelbgoldlegierung ergibt sich bei folgender Zusammensetzung: Ag 15,11 Gew.-% Si 0,04 Gew.-% Ni 1,32 Gew.-% Zn 15,74 Gew.-% Cu 56,68 Gew.-% Au zu 100%. A sheet-metal yellow gold alloy results in the following composition: Ag 15.11% by weight Si 0.04% by weight Ni 1.32% by weight Zn 15.74% by weight Cu 56.68% by weight Au to 100%.

Diese Legierung weist das Erscheinungsbild von Gelbgold mit höheren Goldgehalten auf und zeichnet sich durch gute Bearbeitungseigenschaften aus.These Alloy has the appearance of yellow gold with higher gold contents and is characterized by good processing properties.

Beispiel 2:Example 2:

Eine Blech-Weissgoldlegierung ergibt sich bei folgender Zusammensetzung: Ag 0,89 Gew.-% Ni 11,30 Gew.-% Zn 12,91 Gew.-% Cu 63,80 Gew.-% Au zu 100%. A tin-white gold alloy results from the following composition: Ag 0.89% by weight Ni 11.30% by weight Zn 12.91% by weight Cu 63.80% by weight Au to 100%.

Diese Legierung weist das Erscheinungsbild von Weissgold mit höheren Goldgehalten auf und zeichnet sich durch gute Bearbeitungseigenschaften aus.These Alloy has the appearance of white gold with higher gold contents and is characterized by good processing properties.

Beispiel 3:Example 3:

Eine Blech-Rotgoldlegierung ergibt sich bei folgender Zusammensetzung: Ag 9,98 Gew.-% Zn 2,04 Gew.-% Cu 76,87 Gew.-% Au zu 100%. A sheet-metal red gold alloy results from the following composition: Ag 9.98% by weight Zn 2.04% by weight Cu 76.87% by weight Au to 100%.

Diese Legierung weist das Erscheinungsbild von Rotgold mit höheren Goldgehalten auf und zeichnet sich durch gute Bearbeitungseigenschaften aus.These Alloy has the appearance of rose gold with higher gold contents and is characterized by good processing properties.

Beispiel 4:Example 4:

Eine Guss-Gelbgoldlegierung ergibt sich bei folgender Zusammensetzung: Cu 55,24 Gew.-% Zn 17,06 Gew.-% Si 0,13 Gew.-% Ag 16,46 Gew.-% Au zu 100%. A cast yellow gold alloy results in the following composition: Cu 55.24% by weight Zn 17.06% by weight Si 0.13% by weight Ag 16.46% by weight Au to 100%.

Diese Legierung weist das Erscheinungsbild von Gelbgold mit höheren Goldgehalten auf und zeichnet sich durch gute Bearbeitungseigenschaften aus.These Alloy has the appearance of yellow gold with higher gold contents and is characterized by good processing properties.

Beispiel 5:Example 5:

Eine Guss-Weissgoldlegierung ergibt sich bei folgender Zusammensetzung: Cu 8,80 Gew.-% Si 0,09 Gew.-% Zn 6,21 Gew.-% Ag 73,80 Gew.-% Au zu 100%. A cast white gold alloy results in the following composition: Cu 8.80% by weight Si 0.09% by weight Zn 6.21% by weight Ag 73.80% by weight Au to 100%.

Diese Legierung weist das Erscheinungsbild von Weissgold mit höheren Goldgehalten auf und zeichnet sich durch gute Bearbeitungseigenschaften aus.These Alloy has the appearance of white gold with higher gold contents and is characterized by good processing properties.

Beispiel 6:Example 6:

Eine Guss-Rotgoldlegierung ergibt sich bei folgender Zusammensetzung: Cu 72,09 Gew.-% Zn 8,53 Gew.-% Si 0,07 Gew.-% Ag 8,21 Gew.-% Au zu 100%. A cast red gold alloy results from the following composition: Cu 72.09% by weight Zn 8.53% by weight Si 0.07% by weight Ag 8.21% by weight Au to 100%.

Diese Legierung weist das Erscheinungsbild von Rotgold mit höheren Goldgehalten auf und zeichnet sich durch gute Bearbeitungseigenschaften aus.These Alloy has the appearance of rose gold with higher gold contents and is characterized by good processing properties.

Die Eigenschaften beim Walzen, Kneten und Gießen lassen sich durch Anpassung der Silizium- und Nickelgehalte beeinflussen, ohne dass der Grundgedanke der oben beschriebenen Lösung verlassen wird. Ausführungsbeispiele der vorliegenden Erfindung:

Figure 00050001

  • (alle Angaben in Gewichtsprozenten)
The properties of rolling, kneading and casting can be adjusted by adjusting the silicon and Influence nickel contents without departing from the basic idea of the solution described above. Embodiments of the present invention:
Figure 00050001
  • (all figures in weight percentages)

Claims (11)

Legierung mit folgenden Bestandteilen: 75–91 Gew.-% wenigstens eines weiteren Elements ausgewählt aus der Gruppe Ag, Zn, Cu, 0–14 Ni, 0–0,2% Si, Rest zu 100% an Au.Alloy having the following constituents: 75-91% by weight of at least one further element selected from the group Ag, Zn, Cu, 0-14 Ni, 0-0.2% Si, balance 100% Au. Legierung nach Anspruch 1, dadurch gekennzeichnet, dass der Goldgehalt zwischen 10,0 und 12,0 Gew.-% liegt.Alloy according to claim 1, characterized in that that the gold content is between 10.0 and 12.0 wt .-%. Legierung nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass der Goldgehalt 11,1 Gew.-% beträgt.Alloy according to one of the preceding claims, characterized characterized in that the gold content is 11.1 wt .-%. Legierung nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass folgende Zusammensetzung vorgesehen ist: Ag 15,11 Gew.-% Si 0,04 Gew.-% Ni 1,32 Gew.-% Zn 15,74 Gew.-% Cu 56,68 Gew.-% Au zu 100%.
Alloy according to one of the preceding claims, characterized in that the following composition is provided: Ag 15.11% by weight Si 0.04% by weight Ni 1.32% by weight Zn 15.74% by weight Cu 56.68% by weight Au to 100%.
Legierung nach einem der vorhergehenden Ansprüche 1 bis 3, dadurch gekennzeichnet, dass folgende Zusammensetzung vorgesehen ist: Ag 0,89 Gew.-% Ni 11,30 Gew.-% Zn 12,91 Gew.-% Cu 63,80 Gew.-% Au zu 100%.
Alloy according to one of the preceding claims 1 to 3, characterized in that the following composition is provided: Ag 0.89% by weight Ni 11.30% by weight Zn 12.91% by weight Cu 63.80% by weight Au to 100%.
Legierung nach einem der vorhergehenden Ansprüche 1 bis 3, dadurch gekennzeichnet, dass folgende Zusammensetzung vorgesehen ist: Ag 9,98 Gew.-% Zn 2,04 Gew.-% Cu 76,87 Gew.-% Au zu 100%.
Alloy according to one of the preceding claims 1 to 3, characterized in that the following composition is provided: Ag 9.98% by weight Zn 2.04% by weight Cu 76.87% by weight Au to 100%.
Legierung nach einem der vorhergehenden Ansprüche 1 bis 3, dadurch gekennzeichnet, dass folgende Zusammensetzung vorgesehen ist: Cu 55,24 Gew.-% Zn 17,06 Gew.-% Si 0,13 Gew.-% Ag 16,46 Gew.-% Au zu 100%.
Alloy according to one of the preceding claims 1 to 3, characterized in that the following composition is provided: Cu 55.24% by weight Zn 17.06% by weight Si 0.13% by weight Ag 16.46% by weight Au to 100%.
Legierung nach einem der vorhergehenden Ansprüche 1 bis 3, dadurch gekennzeichnet, dass folgende Zusammensetzung vorgesehen ist: Cu 8,80 Gew.-% Si 0,09 Gew.-% Zn 6,21 Gew.-% Ag 73,80 Gew.-% Au zu 100%.
Alloy according to one of the preceding claims 1 to 3, characterized in that the following composition is provided: Cu 8.80% by weight Si 0.09% by weight Zn 6.21% by weight Ag 73.80% by weight Au to 100%.
Legierung nach einem der vorhergehenden Ansprüche 1 bis 3, dadurch gekennzeichnet, dass folgende Zusammensetzung vorgesehen ist: Cu 72,09 Gew.-% Zn 8,53 Gew.-% Si 0,07 Gew.-% Ag 8,21 Gew.-% Au zu 100%.
Alloy according to one of the preceding claims 1 to 3, characterized in that the following composition is provided: Cu 72.09% by weight Zn 8.53% by weight Si 0.07% by weight Ag 8.21% by weight Au to 100%.
Verwendung einer Legierung nach einem der vorhergehenden Ansprüche zur Herstellung von Schmuckwaren.Use of an alloy according to one of the preceding claims for the production of jewelery. Schmuckgegenstand mit einem metallischen Anteil, der einer Legierung nach den Ansprüchen 1 bis 9 entspricht.Jewelery item with a metallic part, which corresponds to an alloy according to claims 1 to 9.
DE200510045477 2005-09-22 2005-09-22 Gold alloy for manufacture of jewelry contains 75 to 91 per cent weight of the elements gold, silver, zinc and copper Withdrawn DE102005045477A1 (en)