DE102005001101A1 - Self-leveling floor filler with improved surface smoothness - Google Patents
Self-leveling floor filler with improved surface smoothness Download PDFInfo
- Publication number
- DE102005001101A1 DE102005001101A1 DE200510001101 DE102005001101A DE102005001101A1 DE 102005001101 A1 DE102005001101 A1 DE 102005001101A1 DE 200510001101 DE200510001101 DE 200510001101 DE 102005001101 A DE102005001101 A DE 102005001101A DE 102005001101 A1 DE102005001101 A1 DE 102005001101A1
- Authority
- DE
- Germany
- Prior art keywords
- dry mixture
- screed
- dry
- mixture according
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Gegenstand der Erfindung ist eine Trockenmischung, welche Portlandkalksteinzement, Aluminatzement (Tonerdezement) und Calciumsulfat in Kombination mit Eisensulfat und/oder Aluminiumsulfat enthält und sich insbesondere für Spachtel-, Estrich- oder Bodenausgleichsmassen eignet. Die auf diese Weise erhältlichen Spachtel-, Estrich- oder Bodenausgleichsmassen zeichnen sich nach ihrem Auftrag und Abbinden bzw. Aushärten durch eine besonders glatte Oberfläche mit einer gegenüber herkömmlichen Spachtel-, Estrich- oder Bodenausgleichsmassen deutlich reduzierten Rauhigkeit aus, so daß ein Vorschleifen der gespachtelten bzw. aufgetragenen Fläche nicht mehr erforderlich ist und das Verkleben mit einem Oberbelag deutlich erleichtert ist.The invention relates to a dry mixture containing Portlandkalksteinzement, Aluminatzement (alumina cement) and calcium sulfate in combination with iron sulfate and / or aluminum sulfate and is particularly suitable for putty, screed or ground leveling compounds. The putty, screed or floor leveling compounds obtainable in this manner are distinguished by their very high surface area and surface area after their application and curing or hardening by a significantly reduced roughness compared to conventional fillers, screed or floor leveling compounds, so that a pre-grinding of the filled or Placed surface is no longer required and the bonding with a top surface is much easier.
Description
Die vorliegende Erfindung betrifft eine Trockenmischung, insbesondere für ein hydraulisches Bindemittel, vorzugsweise für eine Spachtel-, Estrich- oder Bodenausgleichsmasse. Die Erfindung betrifft sowohl die Trockenmischung als solche als auch die mit Wasser angemachte Mischung sowie schließlich die ausgehärtete Masse, insbesondere die auf einem Untergrund aufgebrachte und abgebundene bzw. ausgehärtete Spachtel-, Estrich- oder Bodenausgleichsmasse.The The present invention relates to a dry blend, in particular for a hydraulic binder, preferably for a filler, screed or ground leveling compound. The invention relates both to the dry mix as such, as well as the mixture mixed with water and finally the cured Mass, in particular the applied and set on a substrate or hardened spatula, Screed or floor leveling compound.
Weiterhin betrifft die vorliegende Erfindung die Verwendung der erfindungsgemäßen Trockenmischung in oder als hydraulisches Bindemittel, vorzugsweise in oder als Spachtel-, Estrich- oder Bodenausgleichsmasse.Farther The present invention relates to the use of the dry mix according to the invention in or as a hydraulic binder, preferably in or as Putty, screed or ground leveling compound.
Böden, die mit einem Oberboden oder mit einem Oberbelag (z. B. einem PVC-Oberbelag) belegt werden, müssen für die Verlegung des Oberbodens bzw. Oberbelags vorbereitet werden. Hierzu werden sogenannte Spachtel-, Estrich- oder Bodenausgleichsmassen auf den mit dem Oberboden oder dem Oberbelag zu versehenden Untergrund aufgetragen, um etwaige Unebenheiten auszugleichen und den Boden für eine Verklebung des Oberbelags vorzubereiten.Floors that with a topsoil or with a topping (eg a PVC topping) be occupied for the Laying the topsoil or topping be prepared. For this become so-called filler, screed or ground leveling compounds on the surface to be provided with the topsoil or topsoil applied to compensate for any bumps and the ground for one Prepare gluing of the top coat.
Die Spachtel-, Estrich- oder Bodenausgleichsmassen des Standes der Technik liefern nach ihrer Applikation und Aushärtung im allgemeinen nur relativ rauhe und stumpfe Oberflächen. Dies hat den Nachteil, daß der Auftragswiderstand von Klebstoffen für die Oberbeläge hierdurch signifikant erhöht wird, was einen stärkeren Werkzeugverschleiß einerseits und eine schnellere Ermüdung des Verarbeiters andererseits zur Folge hat. Bedingt durch die Rauhigkeit der ausgehärteten Masse, ist der Klebstoffverbrauch zudem erhöht. Für bestimmte Oberbeläge (z. B. PVC-Oberbeläge) ist zudem ein Vorschleifen der gespachtelten Fläche unerläßlich.The Putty, screed or ground leveling compounds of the prior art provide relatively little after their application and curing in general rough and dull surfaces. This has the disadvantage that the Coating resistance of adhesives for the top linings thereby significantly increased becomes, what a stronger Tool wear on the one hand and a faster fatigue the processor on the other hand result. Due to the roughness the cured one Mass, the adhesive consumption is also increased. For certain surface coverings (eg PVC floor coverings) In addition, a pre-grinding of the filled area is essential.
Die Aufgabe der vorliegenden Erfindung besteht nun darin, eine Spachtel-, Estrich- oder Bodenausgleichsmasse bereitzustellen, welche die zuvor ge schilderten Nachteile und Probleme des Standes der Technik weitgehend vermeidet oder zumindest verringert.The The object of the present invention is therefore to provide a spatula, Screed or ground leveling compound to provide the previously ge described disadvantages and problems of the prior art largely avoids or at least reduces.
Die Anmelderin hat nun herausgefunden, daß eine Trockenmischung, welche Portlandkalksteinzement, Aluminatzement und Calciumsulfat in Kombination mit Eisensulfat und/oder Aluminiumsulfat enthält, sich ausgezeichnet als oder zur Verwendung in einer Spachtel-, Estrich- oder Bodenausgleichsmasse eignet.The Applicant has now found that a dry mix, which Portland limestone cement, aluminate cement and calcium sulfate in combination containing iron sulfate and / or aluminum sulfate, is excellent as or for use in a leveling, screed or leveling compound suitable.
Gegenstand der vorliegenden Erfindung – gemäß einem ersten Aspekt der vorliegenden Erfindung – ist somit eine Trockenmischung, insbesondere für eine Spachtel-, Estrich- oder Bodenausgleichsmasse, welche Portlandkalksteinzement, Aluminatzement (Tonerdezement) und Calciumsulfat in Kombination mit Eisensulfat und/oder Aluminiumsulfat enthält.object of the present invention - according to a first aspect of the present invention - is thus a dry mix, especially for a putty, screed or ground leveling compound containing Portland limestone cement, Aluminate cement (alumina cement) and calcium sulfate in combination containing iron sulfate and / or aluminum sulfate.
Der Begriff "Trockenmischung" wurde erfindungsgemäß gewählt, um die Mischung als solche gegenüber der eigentlichen Spachtel-, Estrich- oder Bodenausgleichsmasse, welche erst durch Zusetzen von Wasser zu der Trockenmischung resultiert, abzugrenzen. Der Begriff "Trockenmischung" bezeichnet also die Basis- oder Ausgangsmischung, aus der sich durch Anmachen mit Wasser dann die eigentliche Spachtel-, Estrich- oder Bodenausgleichsmasse herstellen läßt.Of the The term "dry mixture" was chosen according to the invention in order to the mixture as such the actual leveling, screed or ground leveling compound, which results only by adding water to the dry mixture, delineate. The term "dry mix" thus refers to the basic or starting mixture, from which by mixing with Water then the actual filler, screed or ground leveling compound can be produced.
Die erfindungsgemäße Rezeptur bzw. Zusammensetzung mit Portlandkalksteinzement, Aluminatzement (Tonerdezement) und Calciumsulfat in Kombination mit Eisensulfat und/oder Aluminiumsulfat und gegebenenfalls weiteren Inhaltsstoffen, insbesondere Additiven, wie z. B. Verflüssigern, Verzögerern, Stabilisierern, Erhärtungsbeschleunigern etc., ermöglicht überraschenderweise die Ausbildung einer insgesamt sehr glatten Oberfläche mit einer deutlich reduzierten Rauhigkeit im Vergleich zum Stand der Technik, wenn die vorgenannte Trockenmischung mit Wasser angemacht und als Spachtel-, Estrich- oder Bodenausgleichsmasse auf einen Untergrund aufgetragen wird und abbindet bzw. abtrocknet, um dann nachfolgend hierauf einen Oberboden oder einen Oberbelag aufzubringen zu können. Aufgrund der Ausbildung einer insgesamt sehr glatten Oberfläche mit einer deutlich reduzierten Rauhigkeit ist dann das Auftragen von Oberbelagsklebstoffen signifikant erleichtert. Ein Vorschleifen der gespachtelten bzw. aufgetragenen Fläche ist im allgemeinen nicht mehr erforderlich. Der Klebstoffverbrauch für die Verklebung des Oberbelags ist signifikant reduziert, verglichen mit dem Stand der Technik um etwa 20 Prozent und mehr. Zudem weist die auf diese Weise erhältliche Oberfläche ein ausgezeichnetes optisches Erscheinungsbild, insbesondere ein gleichmäßige Färbung über die gesamte Fläche, vorzugsweise ohne Fehlstellen, auf.The novel formulation or composition with Portlandkalksteinzement, Aluminatzement (alumina cement) and calcium sulfate in combination with iron sulfate and / or aluminum sulfate and optionally other ingredients, especially additives such. As liquefiers, retarders, stabilizers, hardening accelerators, etc., surprisingly allows the formation of an overall very smooth surface with a significantly reduced roughness compared to the prior art, when the aforementioned dry mix with water and dressed as a leveling, screed or ground leveling compound a subsurface is applied and sets or dries, to then subsequently apply a topsoil or a topcoat can. Due to the formation of an overall very smooth surface with a significantly reduced roughness then the application of topping adhesives is significantly easier. A pre-grinding of the filled or applied surface is generally no longer necessary. The glue consumption for bonding the top layer is significantly reduced compared to the State of the art by about 20 percent and more. In addition, the surface obtainable in this way has an excellent visual appearance, in particular a uniform coloring over the entire surface, preferably without defects.
Die glattere Oberfläche mit der deutlich reduzierten Rauhigkeit ist insbesondere auf die im Vergleich zum Stand der Technik relativ kurzstengelige, gedrungene bis tonnenförmige Ausbildung der Ettringitkristalle zurückzuführen, welche in der abgebundenen bzw. ausgehärteten Spachtel-, Estrich- bzw. Bodenausgleichsmasse, insbesondere an deren Oberfläche, vorhanden sind. Die gezielte, insbesondere kurzstengelige Ettringitbildung wird erfindungsgemäß durch den Einsatz von Portlandkalksteinzement, Aluminatzement (Tonerdezement) und Calciumsulfat in Kombination mit Eisensulfat und/oder Aluminiumsulfat erreicht. In rasterelektronenmikroskopischen (REM) Studien konnte die Anmelderin an der Oberfläche der aufgetragenen und ausgehärteten Spachtel-, Estrich- oder Bodenausgleichsmasse die ungewöhnlich kurzstengeligen und gedrungenen Ettringitstrukturen nachweisen.The smoother surface with the significantly reduced roughness is particular to the Relatively short-stemmed, stocky compared to the prior art to barrel-shaped Formation of Ettringitkristalle attributed to the hardened or cured Putty, screed or ground leveling compound, in particular at the Surface, available. The targeted, especially kurzstengelige Ettringitbildung is inventively the use of Portland limestone cement, aluminate cement (alumina cement) and calcium sulfate in combination with iron sulfate and / or aluminum sulfate reached. In scanning electron microscopy (SEM) studies could the applicant on the surface the applied and cured Spachtel, screed or ground leveling compound the unusually short-stemmed and stubborn ettringite structures.
Unter Ettringit versteht man im allgemeinen ein hexagonales Mineral der chemischen Zusammensetzung Ca6Al2[(OH)4/SO4]3·24 H2O oder 26 H2O, welches glasglänzende bis seidenglänzende Kristalle oder Nadeln ausbildet. Bei der Abbindung von hydraulischen Bindemitteln entsteht Ettringit in tricalciumaluminathaltigem Portlandkalksteinzement durch Bindung von CaSO4 aus umgebendem Wasser. Für weitere diesbezügliche Einzelheiten kann verwiesen werden auf Römpp Chemielexikon, 10. Auflage, Band 2, 1997, Georg Thieme Verlag Stuttgart/New York, Seite 1245, Stichwort: "Ettringit".Ettringite is generally understood to mean a hexagonal mineral of the chemical composition Ca 6 Al 2 [(OH) 4 / SO 4 ] 3 .24H 2 O or 26H 2 O, which forms glazed or semi-glossy crystals or needles. When binding hydraulic binders, ettringite is formed in tricalcium aluminate-containing Portland limestone cement by binding CaSO 4 from surrounding water. For further details in this regard may be made to Römpp Chemielexikon, 10th edition, Volume 2, 1997, Georg Thieme Verlag Stuttgart / New York, page 1245, keyword: "ettringite".
Eine Besonderheit der erfindungsgemäßen Trockenmischung bzw. Rezeptur muß darin gesehen werden, daß anstelle von ansonsten in Spachtel-, Estrich- oder Bodenausgleichsmassen üblicherweise verwendetem Portlandzement Portlandkalksteinzement eingesetzt wird.A Particularity of the dry mix according to the invention or recipe must be in it be seen that instead otherwise in leveling, screed or ground leveling compounds usually used Portland cement Portland limestone cement is used.
Der Anteil an Portlandkalksteinzement kann in weiten Bereichen variieren. Im allgemeinen liegt er, bezogen auf die erfindungsgemäße Trockenmischung bzw. Zusammensetzung, im Bereich von 0,5 bis 20 Gew.-%, insbesondere 1,5 bis 12 Gew.-%, bevorzugt 2 bis 8 Gew.-%. Dennoch kann es einzelfallbedingt oder anwendungstechnisch erforderlich sein, von den vorgenannten Mengen abzuweichen.Of the Portland limestone cement content can vary widely. In general, it is based on the dry blend according to the invention or composition, in the range of 0.5 to 20 wt .-%, in particular 1.5 to 12 wt .-%, preferably 2 to 8 wt .-%. Nevertheless, it may be due to individual circumstances or application technology required, of the aforementioned Deviating quantities.
Besonders gute Ergebnisse werden erhalten, wenn Portlandkalksteinzement mit einer spezifischen Oberfläche nach Blaine von 3.000 bis 6.000 cm2/g, insbesondere 3.500 bis 5.500 cm2/g, bevorzugt 4.500 bis 5.000 cm2/g, verwendet wird.Particularly good results are obtained when Portland limestone cement having a Blaine surface area of from 3,000 to 6,000 cm 2 / g, in particular 3,500 to 5,500 cm 2 / g, preferably 4,500 to 5,000 cm 2 / g, is used.
Bevorzugterweise ist der eingesetzte Portlandkalksteinzement ein Portlandkalksteinzement auf Basis von Calciumsilikaten.preferably, Portland limestone cement used is a Portland limestone cement based on calcium silicates.
Ein erfindungsgemäß besonders bevorzugter Portlandkalksteinzement enthält, jeweils bezogen auf den Portlandkalksteinzement, 60 bis 70 Gew.-% CaO, 20 bis 30 Gew.-% SiO2, 2 bis 6 Gew.-% Al2O3 und 1 bis 5 Gew.-% Fe2O3, jeweils bestimmt nach DIN EN 196-2:1994.An inventively particularly preferred Portland limestone cement contains, based on the Portland limestone cement, 60 to 70 wt .-% CaO, 20 to 30 wt .-% SiO 2 , 2 to 6 wt .-% Al 2 O 3 and 1 to 5 wt. % Fe 2 O 3 , each determined according to DIN EN 196-2: 1994.
Was die Aluminatzementkomponente anbelangt, so kann die Menge an Aluminatzement – synonym auch als Tonerdezement bezeichnet – in der erfindungsgemäßen Trockenmischung bzw. Rezeptur gleichermaßen in weiten Bereichen variieren. Im allgemeinen liegt die Menge an Aluminatzement im Bereich von 5 bis 30 Gew.-%, insbesondere 5 bis 25 Gew.-%, bevorzugt 15 bis 20 Gew.-%, bezogen auf die erfindungsgemäße Trockenmischung bzw. Rezeptur. Dennoch kann es einzelfallbedingt oder anwendungstechnisch erforderlich sein, von den vorgenannten Mengen abzuweichen.What As far as the aluminate cement component is concerned, the amount of aluminate cement may be synonymous called alumina cement - in the dry mix according to the invention or recipe alike vary widely. In general, the amount is Aluminate cement in the range of 5 to 30 wt .-%, in particular 5 to 25 wt .-%, preferably 15 to 20 wt .-%, based on the dry blend according to the invention or recipe. Nevertheless, it may be due to case or application be necessary to deviate from the abovementioned quantities.
Besonders gute Ergebnisse werden erhalten, wenn ein Aluminatzement mit einer spezifischen Oberfläche nach Blaine von 2.000 bis 4.000 cm2/g, insbesondere 2.500 bis 3.750 cm2/g, bevorzugt 2.750 bis 3.500 cm2/g, eingesetzt wird.Particularly good results are obtained when an aluminate cement having a Blaine surface area of from 2,000 to 4,000 cm 2 / g, in particular 2,500 to 3,750 cm 2 / g, preferably 2,750 to 3,500 cm 2 / g, is used.
Der eingesetzte Aluminatzement ist ein hydraulisches Bindemittel auf der Grundlage von Calciumaluminaten – im Gegensatz zur Portlandzementen, die aus Calciumsilikaten bestehen. Die Calciumaluminate geben dem Aluminatzement Eigenschaften, die im Rahmen der erfindungsgemäßen Rezeptur besonders bei der Formulierung von bauchemischen Anwendungen erforderlich sind, insbesondere für selbstverlaufende bzw. selbstfließende Spachtel-, Estrich- oder Bodenausgleichsmassen. Im Gegensatz zu Portlandzementen setzt der Aluminatzement bei der Hydratation keinen Kalk frei; diese Eigenschaften sowie seine geringe Porosität gibt bauchemischen Formulierungen der zuvor genannten Art eine gute chemische Widerstandfähigkeit und vermeidet Ausblühungen. Insbesondere wirkt der erfindungsgemäß eingesetzte Aluminatzement im Rahmen der erfindungsgemäßen Trockenmischung bzw. Rezeptur unter anderem als ein Abbinde- und Erhärtungsbeschleuniger, so daß eine Trockenmischung resultiert, die sich nach Anmachen mit Wasser durch eine hohe Leistungsfähigkeit und eine hohe Schnelligkeit bei der Hydratation auszeichnet.The aluminate cement used is a hydraulic binder based on calcium aluminates - in contrast to Portland cements, which consist of calcium silicates. The calcium aluminates give the aluminate cement properties which, in the context of the formulation according to the invention, are required in particular in the formulation of construction-chemical applications, in particular for self-leveling or self-flowing filler, screed or leveling compounds. In contrast to Portland cements, the aluminate cement releases no lime during hydration; these properties and its low porosity gives chemical mixtures of the abovementioned type a good chemical resistance and avoids efflorescence. In particular, the aluminate cement used according to the invention acts within the framework the dry mixture or formulation according to the invention, inter alia, as a setting and hardening accelerator, so that a dry mix results, which is characterized by a high performance and high speed of hydration after mixing with water.
Ein erfindungsgemäß bevorzugt eingesetzter Aluminatzement weist, jeweils bezogen auf den Aluminatzement und jeweils bestimmt nach DIN EN 196-2:1994, 35 bis 41 Gew.-% CaO, 1 bis 6 Gew.-% SO2, 35 bis 45 Gew.-% Al2O3 und 12 bis 19 Gew.-% Fe2O3 auf.An inventive preferred aluminate cement, in each case based on the aluminate cement and in each case determined according to DIN EN 196-2: 1994, 35 to 41 wt .-% CaO, 1 to 6 wt .-% SO 2 , 35 to 45 wt .-% Al 2 O 3 and 12 to 19 wt .-% Fe 2 O 3 on.
Was die Calciumsulfat-Komponente der erfindungsgemäßen Trockenmischung anbelangt, so wird diese vorzugsweise in hydratisierter Form, insbesondere in Form des Hemihydrats, eingesetzt.What As regards the calcium sulfate component of the dry blend according to the invention, so this is preferably in hydrated form, in particular in the form of hemihydrate.
Auch die Menge an eingesetztem Calciumsulfat in der erfindungsgemäßen Trockenmischung kann in weiteren Bereichen variieren. Im allgemeinen liegt die Menge an Calciumsulfat im Bereich von 3 bis 20 Gew.-%, insbesondere 5 bis 15 Gew.-%, bevorzugt 5 bis 10 Gew.-%, bezogen auf die Trockenmischung.Also the amount of calcium sulfate used in the dry mix according to the invention can vary in other areas. In general, the amount is on calcium sulfate in the range of 3 to 20 wt .-%, in particular 5 to 15 wt .-%, preferably 5 to 10 wt .-%, based on the dry mixture.
Besonders gute Ergebnisse werden erhalten, wenn ein Calciumsulfat mit einer spezifischen Oberfläche nach Blaine von 2.500 bis 3.500 cm2/g, bevorzugt 2.750 bis 3.250 cm2/g, besonders bevorzugt von etwa 3.000 cm2/g, eingesetzt wird. Das eingesetzte Calciumsulfat sollte einen Calciumsulfatgehalt von mindestens 90 Gew.-% aufweisen, bezogen auf das Calciumsulfat.Particularly good results are obtained when a calcium sulfate having a Blaine surface area of from 2,500 to 3,500 cm 2 / g, preferably 2,750 to 3,250 cm 2 / g, more preferably from about 3,000 cm 2 / g, is used. The calcium sulfate used should have a calcium sulfate content of at least 90% by weight, based on the calcium sulfate.
Ein erfindungsgemäß bevorzugtes Calciumsulfat besitzt eine Reindichte von 2,5 bis 3,0 g/cm3, insbesondere 2,7 bis 2,9 g/cm3, und eine Schüttdichte von 800 bis 1.200 g/l, insbesondere 850 bis 1.150 g/l, vorzugsweise 900 bis 1.100 g/l.A preferred calcium sulfate according to the invention has a true density of 2.5 to 3.0 g / cm 3 , in particular 2.7 to 2.9 g / cm 3 , and a bulk density of 800 to 1200 g / l, in particular 850 to 1150 g / 1, preferably 900 to 1100 g / l.
Wie zuvor geschildert, läßt sich das erfindungsgemäß geforderte Ergebnis – die Herstellung einer selbstverlaufenden bzw. selbstausgleichenden Spachtel-, Estrich- oder Bodenausgleichsmasse mit exzellenten Oberflächeneigenschaften, insbesondere hoher Eben- bzw. Glattheit und gutem optischem Erscheinungsbild – dann erreichen, wenn man die zuvor genannten Komponenten – nämlich Portlandkalksteinzement, Aluminatzement und Calciumsulfat – mit Eisensulfat und/oder Aluminiumsulfat kombiniert. Besonders bevorzugt ist eine Kombination der vorgenannten Komponenten Portlandkalksteinzement, Aluminatzement und Calciumsulfat mit Eisensulfat und Aluminiumsulfat.As previously described, can be the invention required Result - the Production of a self-leveling or self-leveling spatula, Screed or floor leveling compound with excellent surface properties, especially high level smoothness and good visual appearance - then achieve if you include the aforementioned components - namely Portland limestone cement, Aluminate cement and calcium sulfate - with iron sulfate and / or Aluminum sulfate combined. Particularly preferred is a combination the aforementioned components Portland limestone cement, aluminate cement and calcium sulfate with iron sulfate and aluminum sulfate.
Denn die Anmelderin hat herausgefunden, daß gerade die vorgenannte Kombination von Komponenten zu exzellenten Oberflächen führt, wenn die erfindungsgemäße Trockenmischung bzw. Rezeptur zu Spachtel-, Estrich- oder Bodenausgleichsmassen durch Anmachen mit Wasser verarbeitet und auf einen Untergrund aufgetragen und dort nachfolgend ausgehärtet bzw. abgebunden wird. Die erzielten Oberflächen der Spachtel-, Estrich- oder Bodenausgleichsmasse zeichnen sich nicht nur durch eine exzellente Oberflächenglattheit aus, sondern auch durch ein exzellentes und einheitliches optisches Erscheinungsbild mit durchgehend kontinuierlicher, gleichmäßiger Färbung der Oberfläche.Because the Applicant has found that it is the aforementioned combination from components to excellent surfaces, when the dry mix according to the invention or recipe for leveling, screed or leveling compounds processed by mixing with water and applied to a substrate and subsequently cured there or is tied off. The achieved surfaces of the screed, screed or ground leveling compound are characterized not only by an excellent Surface smoothness, but also by an excellent and uniform visual appearance with continuous, uniform coloring of the surface.
Was das erfindungsgemäß eingesetzte Eisensulfat anbelangt, so wird dieses bevorzugt in Form von Eisen(II)sulfat eingesetzt, vorzugsweise in hydratisierter Form, besonders bevorzugt in Form des Hexa- bis Heptahydrats. Die Menge an erfindungsgemäß eingesetztem Eisensulfat kann in weiten Bereichen variieren; im allgemeinen liegt sie im Bereich von 0,001 bis 2 Gew.-%, insbesondere 0,01 bis 0,25 Gew.-%, bevorzugt 0,025 bis 0,2 Gew.-%, bezogen auf die Trockenmischung. Dennoch kann es einzelfallbedingt oder anwendungstechnisch gegebenenfalls erforderlich sein, von den vorgenannten Werten abzuweichen. Ein erfindungsgemäß bevorzugtes Eisensulfat weist ein Schüttgewicht von 0,6 bis 1,0 t/m3, insbesondere 0,7 bis 0,9 t/m3, vorzugsweise von etwa 0,8 t/m3 auf.As regards the iron sulfate used according to the invention, it is preferably used in the form of iron (II) sulfate, preferably in hydrated form, more preferably in the form of the hexa to heptahydrate. The amount of iron sulfate employed according to the invention can vary within wide ranges; In general, it is in the range of 0.001 to 2 wt .-%, in particular 0.01 to 0.25 wt .-%, preferably 0.025 to 0.2 wt .-%, based on the dry blend. Nevertheless, it may be necessary, depending on the individual case or application, to deviate from the abovementioned values. An inventively preferred iron sulfate has a bulk density of 0.6 to 1.0 t / m 3 , in particular 0.7 to 0.9 t / m 3 , preferably from about 0.8 t / m 3 .
Was das erfindungsgemäß eingesetzte Aluminiumsulfat anbelangt, so kann dieses gleichermaßen in weiten Mengenbereichen eingesetzt werden. Im allgemeinen werden Mengen von Aluminiumsulfat von 0,001 bis 2 Gew.-%, insbesondere 0,01 bis 0,25 Gew.-%, bevorzugt 0,025 bis 0,2 Gew.-%, bezogen auf die Trockenmischung eingesetzt. Dennoch kann es anwendungstechnisch oder einzelfallbedingt erforderlich sein, von den vorgenannten Mengen abzuweichen.What the invention used As far as aluminum sulphate is concerned, this can be equally wide Quantity ranges are used. In general, quantities of aluminum sulfate of 0.001 to 2 wt .-%, in particular 0.01 to 0.25 wt .-%, preferably 0.025 to 0.2 wt .-%, based on the dry mixture used. Nevertheless, it may be application-related or case-by-case be necessary to deviate from the abovementioned quantities.
Die Leistungsfähigkeit der erfindungsgemäßen Trockenmischung läßt sich noch dadurch steigern, daß ihr außerdem noch Calciumhydroxid, insbesondere in hydratisierter Form, vorzugsweise in Form von Weißkalkhydrat, zugesetzt wird. Die Menge an Calciumhydroxid kann gleichermaßen in weiten Bereichen variieren. Im allgemeinen wird das Calciumhydroxid in Mengen von 0,001 bis 3 Gew.-%, insbesondere 0,01 bis 0,25 Gew.-%, bezogen auf die Trockenmischung, eingesetzt; dennoch kann es gegebenenfalls erforderlich sein von den vorgenannten Werten abzuweichen.The performance of the dry blend according to the invention can be further increased by the addition of calcium hydroxide, in particular in hydrated form, preferably in the form of hydrated lime. The amount of calcium hydroxide can likewise vary widely. In general, the calcium hydroxide is used in amounts of from 0.001 to 3% by weight, in particular from 0.01 to 0.25% by weight, based on the dry mixture; however, it may be required by deviate from the aforementioned values.
Weiterhin kann die erfindungsgemäße Trockenmischung außerdem Kalksteinmehl enthalten, insbesondere in Mengen von 5 bis 40 Gew.-%, vorzugsweise 20 bis 35 Gew.-%, besonders bevorzugt 25 bis 35 Gew.-%, bezogen auf die Trockenmischung. Erfindungsgemäß bevorzugtes Kalksteinmehl enthält mindestens 90 Gew.-%, vorzugsweise mindestens 95 Gew.-%, Calciumcarbonat, bezogen auf das Kalksteinmehl. Besonders gute Ergebnisse werden mit einem Kalksteinmehl mit einer Schüttdichte von 800 bis 1.000 g/l, insbesondere 900 bis 950 g/l, erhalten. Im Rahmen der vorliegenden Erfindung bevorzugtes Kalksteinmehl besitzt eine spezifische Oberfläche nach Blaine von 3.500 bis 4.500 cm2/g, vorzugsweise 3.750 bis 4.250 cm2/g, besonders bevorzugt von etwa 4.000 cm2/g.Furthermore, the dry mixture according to the invention may also contain limestone powder, in particular in amounts of 5 to 40 wt .-%, preferably 20 to 35 wt .-%, particularly preferably 25 to 35 wt .-%, based on the dry mixture. Limestone flour preferred according to the invention contains at least 90% by weight, preferably at least 95% by weight, of calcium carbonate, based on the limestone flour. Particularly good results are obtained with a limestone powder having a bulk density of 800 to 1,000 g / l, in particular 900 to 950 g / l. Limestone flour preferred in the context of the present invention has a Blaine specific surface area of 3,500 to 4,500 cm 2 / g, preferably 3,750 to 4,250 cm 2 / g, particularly preferably about 4,000 cm 2 / g.
Weiterhin kann es vorteilhaft sein, wenn die erfindungsgemäße Trockenmischung bzw. Rezeptur außerdem Quarzsand enthält, insbesondere in Mengen von 15 bis 80 Gew.-%, vorzugsweise 25 bis 50 Gew.-%, besonders bevorzugt 30 bis 35 Gew.-%, bezogen auf die Trockenmischung.Farther It may be advantageous if the dry mixture or formulation according to the invention Furthermore Contains quartz sand, especially in amounts of 15 to 80 wt .-%, preferably 25 to 50 wt .-%, particularly preferably 30 to 35 wt .-%, based on the Dry mixture.
Gemäß einer besonderen Ausführungsform der vorliegenden Erfindung wird ein Gemisch von Quarzsanden unterschiedlicher Korngrößen und/oder unterschiedlicher spezifischer Oberflächen nach Blaine eingesetzt. Insbesondere wird ein etwas feinkörnigerer Quarzsand mit einem etwas grobkörnigerem Quarzsand kombiniert. Erfindungsgemäß bevorzugter Quarzsand weist einen SiO2-Gehalt von mehr als 95 Gew.-%, vorzugsweise von mehr als 98 Gew.-%, bezogen auf den Quarzsand auf. Erfindungsgemäß bevorzugter Quarzsand weist eine theoretische spezifische Oberfläche (Blaine) von mindestens 65 cm2/g, vorzugsweise mindestens 75 cm2/g, besonders bevorzugt mindestens 85 cm2/g, auf.According to a particular embodiment of the present invention, a mixture of quartz sands of different grain sizes and / or Blaine specific surface areas is used. In particular, a somewhat finer-grained quartz sand is combined with a somewhat coarser-grained quartz sand. Quartz sand preferred according to the invention has an SiO 2 content of more than 95% by weight, preferably more than 98% by weight, based on the quartz sand. Quartz sand preferred according to the invention has a theoretical specific surface area (Blaine) of at least 65 cm 2 / g, preferably at least 75 cm 2 / g, particularly preferably at least 85 cm 2 / g.
Weiterhin kann es vorgesehen sein, daß die erfindungsgemäße Trockenmischung außerdem weitere Inhaltsstoffe und/oder Additive enthält, um die Anwendungseigenschaften erfindungsgemäßen Trockenmischung zu optimieren. Solche Inhaltsstoffe bzw. Additive können beispielsweise ausgewählt aus der Gruppe von Verflüssigern, Verzögerern, Stabilisierungsmitteln, Entschäumern, Beschleunigern, Füllstoffen und dergleichen.Farther can it be provided that the Dry mixture according to the invention Furthermore contains other ingredients and / or additives to the application properties Dry mixture according to the invention to optimize. Such ingredients or additives may, for example selected from the group of condensers, retarders, Stabilizers, defoamers, Accelerators, fillers and the same.
Beispielsweise kann die erfindungsgemäße Trockenmischung mindestens einen Verflüssiger enthalten, insbesondere in Mengen von 0,01 bis 5 Gew.-%, vorzugsweise 0,05 bis 2 Gew.-%, besonders bevorzugt 0,1 bis 0,5 Gew.-%, bezogen auf die Trockenmischung. Beispiele für erfindungsgemäß bevorzugte Verflüssiger sind Verflüssiger auf der Basis modifizierter Polycarboxylatether. Insbesondere werden die Verflüssiger derart ausgewählt, daß sie den Wasserbedarf beim Anmachen reduzieren und zudem vorteilhafterweise auch zu einer besonders guten Frühfestigkeitsentwicklung führen bzw. diese fördern.For example can the dry mix according to the invention at least one condenser contain, in particular in amounts of 0.01 to 5 wt .-%, preferably 0.05 to 2 wt .-%, particularly preferably 0.1 to 0.5 wt .-%, based on the dry mix. Examples of preferred according to the invention Condenser are condenser based on modified polycarboxylate ethers. In particular, be the liquefiers so selected that she to reduce the need for water when Anmachen and also advantageously also to a particularly good early strength development to lead or promote them.
Weiterhin kann die erfindungsgemäße Trockenmischung zur Optimierung der Anwendungseigenschaften ein die rheologischen und/oder physikalischen Eigenschaften verbesserndes bzw. beeinflussenden Additiv enthalten. Dieses kann beispielsweise auf Basis eines in Wasser redispergierbaren Polymerbindemittels, vorzugsweise auf Basis von Vinylacetat und Ethylen ausgebildet sein (Ethylen/Vinylacetat-Copolymer). Ein derartiges Additiv kann insbesondere in Mengen von 1 bis 15 Gew.-%, vorzugsweise 2 bis 10 Gew.-%, bezogen auf die Trockenmischung, eingesetzt werden.Farther can the dry mix according to the invention to optimize the application properties a the rheological and / or physical properties improving or influencing additive contain. This can for example be based on a in water redispersible polymer binder, preferably based on Be formed vinyl acetate and ethylene (ethylene / vinyl acetate copolymer). One Such additive may in particular be used in amounts of from 1 to 15% by weight, preferably 2 to 10 wt .-%, based on the dry mixture used become.
Weiterhin kann es für die Optimierung der Anwendungseigenschaften förderlich sein, wenn die erfindungsgemäße Trockenmischung außerdem mindestens einen Beschleuniger, insbesondere einen Erhärtungsbeschleuniger, enthält, beispielsweise auf Basis von Alkali- oder Erdalkalicarbonaten, besonders bevorzugt Lithiumcarbonat. Der Beschleuniger kann in Mengen von 0,001 bis 1 Gew.-%, insbesondere 0,05 bis 0,25 Gew.-%, bezogen auf die Trockenmischung, eingesetzt werden.Farther can it for the optimization of the application properties to be beneficial if the dry mix according to the invention Furthermore at least one accelerator, in particular a hardening accelerator, contains for example, based on alkali or alkaline earth carbonates, especially preferably lithium carbonate. The accelerator can be used in quantities of 0.001 to 1 wt .-%, in particular 0.05 to 0.25 wt .-%, based on the dry mix, are used.
Weiterhin kann die erfindungsgemäße Trockenmischung auch mindestens einen Entschäumer enthalten, beispielsweise eine feste Kombination von flüssigen Kohlenwasserstoffen, Polyglykolen und amorpher Kieselsäure. Ein solcher Entschäumer kann insbesondere in Mengen von 0,001 bis 1 Gew.-%, vorzugsweise 0,05 bis 3 Gew.-%, bezogen auf die Trockenmischung, eingesetzt werden.Farther can the dry mix according to the invention also at least one defoamer contain, for example, a solid combination of liquid hydrocarbons, Polyglycols and amorphous silica. Such a defoamer can in particular in amounts of 0.001 to 1 wt .-%, preferably 0.05 to 3 wt .-%, based on the dry mixture used.
Des weiteren kann die erfindungsgemäße Trockenmischung außerdem mindestens ein Stabilisierungsmittel enthalten. Solche Stabilisierungsmittel können beispielsweise ausgewählt sein aus Gummen (z. B. Diutan Gum) oder aber auf Basis von Cellulose oder Cellulosederivaten (z. B. Hydroxyethylcellulose ausgebildet sein). Gleichermaßen können verschiedene Stabilisierungsmittel miteinander kombiniert werden, z. B. Gummen einerseits und Cellulose oder Cellulosederivate andererseits. Wenn als Stabilisierungsmittel Gummen eingesetzt werden, können diese in Mengen von 0,001 bis 0,2 Gew.-%, vorzugsweise 0,03 bis 0,08 Gew.-%, bezogen auf die Trockenmischung eingesetzt werden. Wenn als Stabilisierungsmittel Cellulose bzw. Cellulosederivate (z. B. Hydroxyethylcellulose) eingesetzt werden, können diese in Mengen von 0,001 bis 0,5 Gew.-%, vorzugsweise 0,05 bis 0,15 Gew.-%, bezogen auf die Trockenmischung, eingesetzt werden.Furthermore, the dry mix according to the invention may additionally contain at least one stabilizing agent. Such stabilizing agents may be selected, for example, from gums (for example diutan gum) or else based on cellulose or cellulose derivatives (for example hydroxyethyl cellulose). Similarly, various stabilizers may be combined with each other, e.g. B. gums on the one hand and cellulose or cellulose derivatives on the other. When gums are used as the stabilizing agent, they may be used in amounts of from 0.001 to 0.2% by weight, preferably from 0.03 to 0.08 % By weight, based on the dry mixture. If cellulose or cellulose derivatives (for example hydroxyethyl cellulose) are used as stabilizing agents, they may be used in amounts of 0.001 to 0.5% by weight, preferably 0.05 to 0.15% by weight, based on the dry mixture, be used.
Für alle vorgenannten Mengenangaben gilt, daß es einzelfallbedingt oder anwendungstechnisch gegebenenfalls erforderlich sein kann, von diesen Mengenangaben abzuweichen. Dies zu entscheiden, liegt im Ermessen des Fachmanns.For all the above Quantity information applies that it depending on the individual case or application technology possibly required may be different from these quantities. To decide this is at the discretion of the skilled person.
Außerdem kann die erfindungsgemäße Trockenmischung mindestens einen Zusatz zur Einstellung des Wasserrückhaltevermögens enthalten.In addition, can the dry mix according to the invention contain at least one additive for adjusting the water retention capacity.
Im allgemeinen wird die erfindungsgemäße Trockenmischung derart formuliert, daß mehr als 99 % der Teilchen der Trockenmischung Teilchengrößen bzw. Teilchendurchmesser unterhalb von 400 μm, vorzugsweise unterhalb von 355 μm, gemäß Siebanalyse (DIN 66 165, April 1987, insbesondere Teil 2, Trockensiebung) und/oder mehr als 35 % der Teilchen Teilchengrößen bzw. Durchmesser im Bereich von 0 bis 63 μm gemäß Siebanalyse aufweisen.in the In general, the dry mix according to the invention is formulated in such a way that that more 99% of the particles of the dry mixture have particle sizes or Particle diameter below 400 microns, preferably below 355 μm, according to sieve analysis (DIN 66 165, April 1987, especially Part 2, dry screening) and / or more than 35% of the particles have particle sizes or diameters in the range from 0 to 63 μm according to sieve analysis exhibit.
Insbesondere
ist die Trockenmischung nach der vorliegenden Erfindung durch die
folgenden Teilchengrößenverteilung
gemäß Siebanalyse
gekennzeichnet: 
Die erfindungsgemäße Trockenmischung bzw. Rezeptur eignet sich insbesondere zur Verwendung in hydraulischen Bindemitteln, vorzugsweise in Spachtel-, Estrich- oder Bodenausgleichsmassen, bzw. zur Herstellung von den vorgenannten hydraulischen Bindemitteln. Gegenstand der vorliegenden Erfindung – gemäß einem weiteren Aspekt der vorliegenden Erfindung – ist somit die Verwendung der Trockenmischung bzw. Zusammensetzung nach der vorliegenden Erfindung in Spachtel-, Estrich- oder Bodenausgleichsmassen bzw. zur Herstellung von Spachtel-, Estrich- oder Bodenausgleichsmassen.The Dry mixture according to the invention or formulation is particularly suitable for use in hydraulic Binders, preferably in leveling, screed or leveling compounds, or for the production of the aforementioned hydraulic binders. Object of the present invention - according to another aspect of the present invention thus the use of the dry mixture or composition according to of the present invention in putty, screed or ground leveling compounds or for the production of fillers, floor screed or floor leveling compounds.
Weiterer Gegenstand der vorliegenden Erfindung – gemäß einem dritten Aspekt der vorliegenden Erfindung – sind Spachtel-, Estrich- oder Bodenausgleichsmassen, die unter Verwendung der erfindungsgemäßen Trockenmischung durch Anmachen mit Wasser bzw. durch Zusetzen von Wasser hergestellt werden können. Im allgemeinen werden die erfindungsgemäßen Troc kenmischungen unter Zugabe von 10 bis 30 Gew.-%, vorzugsweise 20 bis 30 Gew.-%, Wasser angemacht.Another Object of the present invention - according to a third aspect of present invention Putty, screed or ground leveling compounds using the dry mix according to the invention made by mixing with water or by adding water can be. In general, the invention Troc kenmischungen under Addition of 10 to 30 wt .-%, preferably 20 to 30 wt .-%, water turned on.
Die unter Verwendung der erfindungsgemäßen Trockenmischung durch Anmachen mit Wasser erhältlichen und nachfolgend auf einen Untergrund aufgetragenen und schließlich abgebundenen bzw. abgetrockneten Spachtel-, Estrich- oder Bodenausgleichsmassen, welche Ettringitkristalle enthalten, sind dadurch gekennzeichnet, daß die hierin enthaltenen, beim Abbinden entstandenen Ettringitkristalle – im Vergleich zu Spachtel-, Estrich- oder Bodenausgleichsmassen des Standes der Technik – besonders kurzstengelig bzw. gedrungen, sozusagen tonnenförmig ausgebildet ist.The using the dry blend of the invention by mixing available with water and subsequently applied to a substrate and finally set or dried putty, screed or ground leveling compounds, which contain ettringite crystals are characterized that the Compounded ettringite crystals contained in it during setting - in comparison to leveling, screed or ground leveling compounds of the prior Technology - especially kurzstengelig or stocky, so to speak barrel-shaped.
Das Länge/Durchmesser- bzw. Länge/Breite-Verhältnis der Ettringitkristalle in den erfindungsgemäßen Spachtel-, Estrich- oder Bodenausgleichsmassen nach Abbinden bzw. Abtrocknen/Aushärten, wie es durch Analyse von REM-Aufnahmen bestimmt worden ist, liegt im allgemeinen unterhalb von 5,0, insbesondere unterhalb von 4,5, vorzugsweise unterhalb von 4,0. Insbesondere liegt das Länge/Durchmesser- bzw. Länge/Breite-Verhältnis der Ettringitkristalle in den erfindungsgemäßen Spachtel-, Estrich- oder Bodenausgleichsmassen nach Abbinden bzw. Abtrocknen und Aushärten im Bereich von 1,0 bis 4,0, insbesondere 1,3 bis 3,0, vorzugsweise 1,4 bis 2,0, ganz besonders bevorzugt 1,4 bis 1,9.The length / diameter or length / width ratio of the ettringite crystals in the putty, screed or ground leveling compositions according to the invention after setting or drying / curing, as determined by analysis of SEM images, is generally below 5 , 0, in particular below 4.5, preferably below 4.0. In particular, the length / diameter or length / width ratio of the ettringite crystals is in the leveling, screed or floor leveling according to the invention After setting or drying and curing in the range of 1.0 to 4.0, in particular 1.3 to 3.0, preferably 1.4 to 2.0, most preferably 1.4 to 1.9.
Im Vergleich hierzu ist das Länge/Durchmesser- bzw. Länge/Breite-Verhältnis in Ettringitkristallen in Spachtel-, Estrich- oder Bodenausgleichsmassen des Standes der Technik deutlich größer und liegt oberhalb von 5,0, da diese Ettringitkristalle nadelförmig ausgebildet sind und für die rauhe, unebene Oberfläche verantwortlich sind.in the In comparison, the length / diameter or length / width ratio in Ettringite crystals in putty, screed or ground leveling compounds of the prior art significantly larger and is above 5.0, since these ettringite crystals are needle-shaped and for the rough, uneven surface are responsible.
Die Begriffe "Länge" einerseits und "Durchmesser" bzw. "Breite" andererseits beziehen sich auf das Erscheinungsbild der Kristalle in REM-Aufnahmen, wobei der Begriff "Länge" die maximale Längsausdehnung der Kristalle und der Begriff "Durchmesser" (oder synonym "Breite") die maximale Querausdehnung der Kristalle bezeichnet.The Relate terms "length" on the one hand and "diameter" or "width" on the other referring to the appearance of crystals in SEM images, taking the term "length" is the maximum longitudinal extent of the Crystals and the term "diameter" (or synonymously "width") the maximum transverse extent called the crystals.
Dies
wird anhand der
Weitere Ausführungsformen, Ausgestaltungen, Abwandlungen und Variationen der vorliegenden Erfindung sind für den Fachmann beim Lesen der vorliegenden Anmeldung ohne weiteres erkennbar und realisierbar, ohne daß er dabei den Rahmen der vorliegenden Erfindung verläßt.Further Embodiments, Embodiments, modifications and variations of the present invention are for those skilled in the reading of the present application readily recognizable and realizable, without being the scope of the present Invention leaves.
Die vorliegende Erfindung wird anhand des folgenden Ausführungsbeispiels veranschaulicht, welches die vorliegende Erfindung jedoch keinesfalls beschränken soll.The The present invention will become apparent from the following embodiment However, which illustrates the present invention in no way restrict should.
Ausführungsbeispiel:Embodiment:
Eine
erfindungsgemäß bevorzugte
Rezeptur für
eine Trockenmischung nach der vorliegenden Erfindung lautet insbesondere
wie folgt: 
Die vorgenannte Trockenmischung eignet sich insbesondere zur Herstellung von oder Einarbeiten in Spachtel-, Estrich- oder Bodenausgleichsmassen. Derartige Spachtel-, Estrich- oder Bodenausgleichsmassen zeichnen sich durch eine extrem geringe Oberflächenrauhigkeit bei exzellentem optischem Erscheinungsbild (= gleichmäßige weiß-gräuliche Färbung) aufgrund des Gehalts an kurzstengeligen Ettringitkristallen aus.The The aforementioned dry mix is particularly suitable for the production of or incorporation into putty, screed or ground leveling compounds. Draw such leveling, screed or ground leveling compounds characterized by an extremely low surface roughness with excellent optical appearance (= uniform white-grayish color) due to the content on short-stemmed ettringite crystals.
Claims (24)