DE102005001101B4 - Dry mix and its use in or for putty, screed or ground leveling compound - Google Patents

Dry mix and its use in or for putty, screed or ground leveling compound Download PDF

Info

Publication number
DE102005001101B4
DE102005001101B4 DE200510001101 DE102005001101A DE102005001101B4 DE 102005001101 B4 DE102005001101 B4 DE 102005001101B4 DE 200510001101 DE200510001101 DE 200510001101 DE 102005001101 A DE102005001101 A DE 102005001101A DE 102005001101 B4 DE102005001101 B4 DE 102005001101B4
Authority
DE
Germany
Prior art keywords
dry mixture
dry
weight
mixture according
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE200510001101
Other languages
German (de)
Other versions
DE102005001101A1 (en
Inventor
Jens Gudrian
Wilhelm FÜTTERER
Udo Dr. Windhövel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henkel AG and Co KGaA
Original Assignee
Henkel AG and Co KGaA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henkel AG and Co KGaA filed Critical Henkel AG and Co KGaA
Priority to DE200510001101 priority Critical patent/DE102005001101B4/en
Priority to DE202005020698U priority patent/DE202005020698U1/en
Priority to PCT/EP2005/011999 priority patent/WO2006072273A1/en
Priority to EP05806761A priority patent/EP1833770A1/en
Publication of DE102005001101A1 publication Critical patent/DE102005001101A1/en
Application granted granted Critical
Publication of DE102005001101B4 publication Critical patent/DE102005001101B4/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Trockenmischung, enthaltend
– 0,5 bis 20 Gew.-% Portlandkalksteinzement,
– 5 bis 30 Gew.-% Aluminatzement und
– 3 bis 20 Gew.-% Calciumsulfat
in Kombination mit 0,001 bis 2 Gew.-% Eisensulfat und 0,001 bis 2 Gew.-% Aluminiumsulfat,
wobei alle vorgenannten Gewichtsprozentangaben auf die Trockenmischung bezogen sind.Dry mix containing
0.5 to 20% by weight Portland limestone cement,
5 to 30% by weight of aluminate cement and
- 3 to 20 wt .-% calcium sulfate
in combination with 0.001 to 2% by weight of iron sulphate and 0.001 to 2% by weight of aluminum sulphate,
wherein all the aforementioned weight percentages are based on the dry mixture.

Figure 00000001
Figure 00000001

Description

Die vorliegende Erfindung betrifft eine Trockenmischung, welche sich insbesondere für eine Spachtel-, Estrich- oder Bodenausgleichsmasse eignet.The The present invention relates to a dry mix which comprises especially for a leveling screed, screed or ground leveling compound is suitable.

Weiterhin betrifft die vorliegende Erfindung die Verwendung der erfindungsgemäßen Trockenmischung in oder als Spachtel-, Estrich- oder Bodenausgleichsmasse.Farther The present invention relates to the use of the dry mix according to the invention in or as a leveling, screed or ground leveling compound.

Böden, die mit einem Oberboden oder mit einem Oberbelag (z. B. einem PVC-Oberbelag) belegt werden, müssen für die Verlegung des Oberbodens bzw. Oberbelags vorbereitet werden. Hierzu werden sogenannte Spachtel-, Estrich- oder Bodenausgleichsmassen auf den mit dem Oberboden oder dem Oberbelag zu versehenden Untergrund aufgetragen, um etwaige Unebenheiten auszugleichen und den Boden für eine Verklebung des Oberbelags vorzubereiten.Floors that with a topsoil or with a topping (eg a PVC topping) be occupied for the Laying the topsoil or topping be prepared. For this become so-called filler, screed or ground leveling compounds on the surface to be provided with the topsoil or topsoil applied to compensate for any bumps and the ground for one Prepare gluing of the top coat.

Die Spachtel-, Estrich- oder Bodenausgleichsmassen des Standes der Technik liefern nach ihrer Applikation und Aushärtung im allgemeinen nur relativ rauhe und stumpfe Oberflächen. Dies hat den Nachteil, daß der Auftragswiderstand von Klebstoffen für die Oberbeläge hierdurch signifikant erhöht wird, was einen stärkeren Werkzeugverschleiß einerseits und eine schnellere Ermüdung des Verarbeiters andererseits zur Folge hat. Bedingt durch die Rauhigkeit der ausgehärteten Masse, ist der Klebstoffverbrauch zudem erhöht. Für bestimmte Oberbeläge (z. B. PVC-Oberbeläge) ist zudem ein Vorschleifen der gespachtelten Fläche unerläßlich.The Putty, screed or ground leveling compounds of the prior art provide relatively little after their application and curing in general rough and dull surfaces. This has the disadvantage that the Coating resistance of adhesives for the top linings thereby significantly increased becomes, what a stronger Tool wear on the one hand and a faster fatigue the processor on the other hand result. Due to the roughness the cured one Mass, the adhesive consumption is also increased. For certain surface coverings (eg PVC floor coverings) In addition, a pre-grinding of the filled area is essential.

Die DE 33 39 197 A1 beschreibt eine Trockenmischung für eine selbstverfließende, glättende Estrichmasse auf der Basis eines komplexen Gemisches von 36 bis 45 Masse-% Zement, 45 bis 58 Masse-% Sand und/oder Kalksteinmehl, 2 bis 5 Masse-% Gips, Kieselerde, Bentonit oder deren Gemische, 1 bis 3 Masse-% Kasein und 0,05 bis 0,18 Masse-% NaF, gegebenenfalls zusammen mit Silikonöl, Soda, Kalkhydrat, Zeolith, Methylcellulose, Flugasche und/oder gemahlener Hochofenschlacke. Die dort beschriebene Trockenmischung wird durch Vermischen ihrer einzelnen Komponenten hergestellt und durch Anmachen mit 20 bis 30 % Wasser zu einer Estrichmasse angerührt, die dann in einer Schichtdicke von 2 bis 20 mm aufgetragen werden soll. Auf diese Weise soll sich schnell eine glatte Oberfläche bilden. Als Zement kommt ein in Spachtel-, Estrich- oder Bodenausgleichsmassen üblicherweise verwendeter Portlandzement zum Einsatz. Portlandkalksteinzement dagegen wird nirgends erwähnt, zumal nicht in Kombination mit Aluminatzement.The DE 33 39 197 A1 describes a dry mix for a self-flowing, smoothing screed mass based on a complex mixture of 36 to 45 mass% cement, 45 to 58 mass% sand and / or limestone, 2 to 5 mass% gypsum, silica, bentonite or mixtures thereof , 1 to 3 mass% casein and 0.05 to 0.18 mass% NaF, optionally together with silicone oil, soda, hydrated lime, zeolite, methyl cellulose, fly ash and / or ground blast furnace slag. The dry mixture described therein is prepared by mixing their individual components and mixed by mixing with 20 to 30% water to a screed mass, which is then to be applied in a layer thickness of 2 to 20 mm. In this way, should quickly form a smooth surface. The cement used is a Portland cement commonly used in leveling, screed or leveling compounds. By contrast, Portland limestone cement is nowhere mentioned, especially not in combination with aluminate cement.

S. Puntke, W. Wassing, "Technische Zusammenhänge bei der Herstellung und Analyse chromatarmer Zemente", in: Zement-Kalk-Gips (ZKG) International, Heft 3/2002, Seiten 82 bis 93, beschreiben die Herstellung chromatarmer Sackzemente zu Zwecken der Einhaltung eines Chromatgrenzwertes von 2 ppm durch Zusatz geeigneter Reduktionsmittel, wobei als ein Beispiel für ein geeignetes Reduktionsmittel Eisen(II)-sulfat Fe(II)SO4 genannt wird.S. Puntke, W. Wassing, "Technical Connections in the Production and Analysis of Low-Chromium Cements", in: Cement Lime Gypsum (ZKG) International, Issue 3/2002, pages 82 to 93, describe the production of low-chromium sack cements for the purposes of Compliance with a chromium limit of 2 ppm by addition of suitable reducing agents, wherein as an example of a suitable reducing agent iron (II) sulfate Fe (II) SO 4 is called.

Die Aufgabe der vorliegenden Erfindung besteht nun darin, eine Spachtel-, Estrich- oder Bodenausgleichsmasse bereitzustellen, welche die zuvor geschilderten Nachteile und Probleme des Standes der Technik weitgehend vermeidet oder zumindest verringert.The The object of the present invention is therefore to provide a spatula, Screed or ground leveling compound to provide the previously described disadvantages and problems of the prior art largely avoids or at least reduces.

Zur Lösung der zuvor geschilderten Aufgabe schlägt die vorliegende Erfindung eine Trockenmischung gemäß Anspruch 1 und deren erfindungsgemäße Verwendung gemäß Anspruch 20 vor. Weitere, vorteilhafte Ausgestaltungen sind Gegenstand der abhängigen Ansprüche.to solution The object described above proposes the present invention a dry mix according to claim 1 and its use according to the invention according to claim 20 ago. Further, advantageous embodiments are the subject of dependent Claims.

Denn die Anmelderin hat nun herausgefunden, daß eine Trockenmischung, welche Portlandkalksteinzement, Aluminatzement und Calciumsulfat in Kombination mit Eisensulfat und Aluminiumsulfat enthält, sich ausgezeichnet als oder zur Verwendung in einer Spachtel-, Estrich- oder Bodenausgleichsmasse eignet.Because the Applicant has now found that a dry mix, which Portland limestone cement, aluminate cement and calcium sulfate in combination Contains with iron sulfate and aluminum sulfate, excellent as or for use in a leveling, screed or leveling compound suitable.

Gegenstand der vorliegenden Erfindung – gemäß einem ersten Aspekt der vorliegenden Erfindung – ist somit eine Trockenmischung, welche sich insbesondere für eine Spachtel-, Estrich- oder Bodenausgleichsmasse eignet und welche

  • – 0,5 bis 20 Gew.-% Portlandkalksteinzement,
  • – 5 bis 30 Gew.-% Aluminatzement und
  • – 3 bis 20 Gew.-% Calciumsulfat
in Kombination mit 0,001 bis 2 Gew.-% Eisensulfat und 0,001 bis 2 Gew.-% Aluminiumsulfat enthält, wobei alle vorgenannten Gewichtsprozentangaben auf die Trockenmischung bezogen sind.The present invention - according to a first aspect of the present invention - is thus a dry mix, which is particularly suitable for a leveling, screed or ground leveling compound and which
  • 0.5 to 20% by weight Portland limestone cement,
  • 5 to 30% by weight of aluminate cement and
  • - 3 to 20 wt .-% calcium sulfate
in combination with 0.001 to 2 wt .-% iron sulfate and 0.001 to 2 wt .-% aluminum sulfate, all of the aforementioned weight percentages are based on the dry blend.

Der Begriff "Trockenmischung" wurde erfindungsgemäß gewählt, um die Mischung als solche gegenüber der eigentlichen Spachtel-, Estrich- oder Bodenausgleichsmasse, welche erst durch Zusetzen von Wasser zu der Trockenmischung resultiert, abzugrenzen. Der Begriff "Trockenmischung" bezeichnet also die Basis- oder Ausgangsmischung, aus der sich durch Anmachen mit Wasser dann die eigentliche Spachtel-, Estrich- oder Bodenausgleichsmasse herstellen läßt.Of the The term "dry mixture" was chosen according to the invention in order to the mixture as such the actual leveling, screed or ground leveling compound, which results only by adding water to the dry mixture, delineate. The term "dry mix" thus refers to the basic or starting mixture, from which by mixing with Water then the actual filler, screed or ground leveling compound can be produced.

Die erfindungsgemäße Rezeptur bzw. Zusammensetzung mit Portlandkalksteinzement, Aluminatzement (Tonerdezement) und Calciumsulfat in Kombination mit Eisensulfat und Aluminiumsulfat und gegebenenfalls weiteren Inhaltsstoffen, insbesondere Additiven, wie z. B. Verflüssigern, Verzögerern, Stabilisierern, Erhärtungsbeschleunigern etc., ermöglicht überraschenderweise die Ausbildung einer insgesamt sehr glatten Oberfläche mit einer deutlich reduzierten Rauhigkeit im Vergleich zum Stand der Technik, wenn die vorgenannte Trockenmischung mit Wasser angemacht und als Spachtel-, Estrich- oder Bodenausgleichsmasse auf einen Untergrund aufgetragen wird und abbindet bzw. abtrocknet, um dann nachfolgend hierauf einen Oberboden oder einen Oberbelag aufzubringen zu können. Aufgrund der Ausbildung einer insgesamt sehr glatten Oberfläche mit einer deutlich reduzierten Rauhigkeit ist dann das Auftragen von Oberbelagsklebstoffen signifikant erleichtert. Ein Vorschleifen der gespachtelten bzw. aufgetragenen Fläche ist im allgemeinen nicht mehr erforderlich. Der Klebstoffverbrauch für die Verklebung des Oberbelags ist signifikant reduziert, verglichen mit dem Stand der Technik um etwa 20 Prozent und mehr. Zudem weist die auf diese Weise erhältliche Oberfläche ein ausgezeichnetes optisches Erscheinungsbild, insbesondere ein gleichmäßige Färbung über die gesamte Fläche, vorzugsweise ohne Fehlstellen, auf.The inventive formula or composition with Portland limestone cement, aluminate cement (Alumina cement) and calcium sulfate in combination with iron sulfate and aluminum sulfate and optionally other ingredients, in particular additives, such. As condensers, retarders, Stabilizers, hardening accelerators etc., surprisingly allows the formation of an overall very smooth surface with a significantly reduced roughness compared to the state of Technique when the aforementioned dry mix is mixed with water and as a filler, screed or Floor leveling compound is applied to a substrate and sets or dries, then then on top of this or to be able to raise an upper surface. Because of the training an overall very smooth surface with a significantly reduced Roughness is then significantly facilitated by the application of top coat adhesives. A pre-grinding of the filled or applied surface is generally no longer necessary. The adhesive consumption for the bonding of the topping is significantly reduced compared to the stand technology by about 20 percent and more. It also points to this Way available surface an excellent visual appearance, especially one uniform coloring over the the whole area, preferably without any defects.

Die glattere Oberfläche mit der deutlich reduzierten Rauhigkeit ist insbesondere auf die im Vergleich zum Stand der Technik relativ kurzstengelige, gedrungene bis tonnenförmige Ausbildung der Ettringitkristalle zurückzuführen, welche in der abgebundenen bzw. ausgehärteten Spachtel-, Estrich- bzw. Bodenausgleichsmasse, insbesondere an deren Oberfläche, vorhanden sind. Die gezielte, insbesondere kurzstengelige Ettringitbildung wird erfindungsgemäß durch den Einsatz von Portlandkalksteinzement, Aluminatzement (Tonerdezement) und Calciumsulfat in Kombination mit Eisensulfat und Aluminiumsulfat erreicht. In rasterelektronenmikroskopischen (REM) Studien konnte die Anmelderin an der Oberfläche der aufgetragenen und ausgehärteten Spachtel-, Estrich- oder Bodenausgleichsmasse die ungewöhnlich kurzstengeligen und gedrungenen Ettringitstrukturen nachweisen.The smoother surface with the significantly reduced roughness is particular to the Relatively short-stemmed, stocky compared to the prior art to barrel-shaped Formation of Ettringitkristalle attributed to the hardened or cured Putty, screed or ground leveling compound, in particular at the Surface, available. The targeted, especially kurzstengelige Ettringitbildung is inventively the use of Portland limestone cement, aluminate cement (alumina cement) and calcium sulfate in combination with iron sulfate and aluminum sulfate reached. In scanning electron microscopy (SEM) studies could the applicant on the surface the applied and cured Spachtel, screed or ground leveling compound the unusually short-stemmed and stubborn ettringite structures.

Unter Ettringit versteht man im allgemeinen ein hexagonales Mineral der chemischen Zusammensetzung Ca6Al2[(OH)4/SO4]3·24 H2O oder 26 H2O, welches glasglänzende bis seidenglänzende Kristalle oder Nadeln ausbildet. Bei der Abbindung von hydraulischen Bindemitteln entsteht Ettringit in tricalciumaluminathaltigem Portlandkalksteinzement durch Bindung von CaSO4 aus umgebendem Wasser. Für weitere diesbezügliche Einzelheiten kann verwiesen werden auf Römpp Chemielexikon, 10. Auflage, Band 2, 1997, Georg Thieme Verlag Stuttgart/New York, Seite 1245, Stichwort: "Ettringit".Ettringite is generally understood to mean a hexagonal mineral of the chemical composition Ca 6 Al 2 [(OH) 4 / SO 4 ] 3 .24H 2 O or 26H 2 O, which forms glazed or semi-glossy crystals or needles. When binding hydraulic binders, ettringite is formed in tricalcium aluminate-containing Portland limestone cement by binding CaSO 4 from surrounding water. For further details in this regard may be made to Römpp Chemielexikon, 10th edition, Volume 2, 1997, Georg Thieme Verlag Stuttgart / New York, page 1245, keyword: "ettringite".

Eine Besonderheit der erfindungsgemäßen Trockenmischung bzw. Rezeptur muß darin gesehen werden, daß anstelle von ansonsten in Spachtel-, Estrich- oder Bodenausgleichsmassen üblicherweise verwendetem Portlandzement Portlandkalksteinzement eingesetzt wird.A Particularity of the dry mix according to the invention or recipe must be in it be seen that instead otherwise in leveling, screed or ground leveling compounds usually used Portland cement Portland limestone cement is used.

Der Anteil an Portlandkalksteinzement kann in weiten Bereichen variieren. Er liegt bezogen auf die erfindungsgemäße Trockenmischung im Bereich von 0,5 bis 20 Gew.-%, insbesondere 1,5 bis 12 Gew.-%, bevorzugt 2 bis 8 Gew.-%.Of the Portland limestone cement content can vary widely. It is based on the dry blend according to the invention in the field from 0.5 to 20 wt .-%, in particular 1.5 to 12 wt .-%, preferably 2 to 8 wt .-%.

Besonders gute Ergebnisse werden erhalten, wenn Portlandkalksteinzement mit einer spezifischen Oberfläche nach Blaine von 3.000 bis 6.000 cm2/g, insbesondere 3.500 bis 5.500 cm2/g, bevorzugt 4.500 bis 5.000 cm2/g, verwendet wird.Particularly good results are obtained when Portland limestone cement having a Blaine surface area of from 3,000 to 6,000 cm 2 / g, in particular 3,500 to 5,500 cm 2 / g, preferably 4,500 to 5,000 cm 2 / g, is used.

Ein erfindungsgemäß besonders bevorzugter Portlandkalksteinzement enthält, jeweils bezogen auf den Portlandkalksteinzement, 60 bis 70 Gew.-% CaO, 20 bis 30 Gew.-% SiO2, 2 bis 6 Gew.-% Al2O3 und 1 bis 5 Gew.-% Fe2O3, jeweils bestimmt nach DIN EN 196-2:1994.An inventively particularly preferred Portland limestone cement contains, based on the Portland limestone cement, 60 to 70 wt .-% CaO, 20 to 30 wt .-% SiO 2 , 2 to 6 wt .-% Al 2 O 3 and 1 to 5 wt. % Fe 2 O 3 , each determined according to DIN EN 196-2: 1994.

Was die Aluminatzementkomponente anbelangt, so kann die Menge an Aluminatzement – synonym auch als Tonerdezement bezeichnet – in der erfindungsgemäßen Trockenmischung bzw. Rezeptur gleichermaßen in weiten Bereichen variieren. Die Menge an Aluminatzement liegt im Bereich von 5 bis 30 Gew.-%, insbesondere 5 bis 25 Gew.-%, bevorzugt 15 bis 20 Gew.-%, bezogen auf die erfindungsgemäße Trockenmischung.What As far as the aluminate cement component is concerned, the amount of aluminate cement may be synonymous called alumina cement - in the dry mix according to the invention or recipe alike vary widely. The amount of aluminate cement is in the range of 5 to 30 wt .-%, in particular 5 to 25 wt .-%, preferably 15 to 20 wt .-%, based on the dry blend according to the invention.

Besonders gute Ergebnisse werden erhalten, wenn ein Aluminatzement mit einer spezifischen Oberfläche nach Blaine von 2.000 bis 4.000 cm2/g, insbesondere 2.500 bis 3.750 cm2/g, bevorzugt 2.750 bis 3.500 cm2/g, eingesetzt wird.Particularly good results are obtained when an aluminate cement having a Blaine surface area of from 2,000 to 4,000 cm 2 / g, in particular 2,500 to 3,750 cm 2 / g, preferably 2,750 to 3,500 cm 2 / g, is used.

Der eingesetzte Aluminatzement ist ein hydraulisches Bindemittel auf der Grundlage von Calciumaluminaten – im Gegensatz zur Portlandzementen, die aus Calciumsilikaten bestehen. Die Calciumaluminate geben dem Aluminatzement Eigenschaften, die im Rahmen der erfindungsgemäßen Rezeptur besonders bei der Formulierung von bauchemischen Anwendungen erforderlich sind, insbesondere für selbstverlaufende bzw. selbstfließende Spachtel-, Estrich- oder Bodenausgleichsmassen. Im Gegensatz zu Portlandzementen setzt der Aluminatzement bei der Hydratation keinen Kalk frei; diese Eigenschaften sowie seine geringe Porosität gibt bauchemischen Formulierungen der zuvor genannten Art eine gute chemische Widerstandfähigkeit und vermeidet Ausblühungen. Insbesondere wirkt der erfindungsgemäß eingesetzte Aluminatzement im Rahmen der erfindungsgemäßen Trockenmischung unter anderem als ein Abbinde- und Erhärtungsbeschleuniger, so daß eine Trockenmischung resultiert, die sich nach Anmachen mit Wasser durch eine hohe Leistungsfähigkeit und eine hohe Schnelligkeit bei der Hydratation auszeichnet.Of the used Aluminatzement is a hydraulic binder on the basis of calcium aluminates - in contrast to Portland cements, which consist of calcium silicates. The calcium aluminates give the Aluminate cement properties that are within the formulation of the invention especially required in the formulation of construction chemical applications are, in particular for Self-leveling or self-flowing filler, screed or screed Floor leveling compounds. In contrast to Portland cements, the Aluminate cement does not lime on hydration; these properties and its low porosity chemical mixtures of the type mentioned above have a good chemical resistance and avoids efflorescence. In particular, the aluminate cement used according to the invention acts in the context of the dry mix according to the invention other than a setting and hardening accelerator, so that one Dry mixture results, which after mixing with water through a high performance and a high speed of hydration is characterized.

Ein erfindungsgemäß bevorzugt eingesetzter Aluminatzement weist, jeweils bezogen auf den Aluminatzement und jeweils bestimmt nach DIN EN 196-2:1994, 35 bis 41 Gew.-% CaO, 1 bis 6 Gew.-% SO2, 35 bis 45 Gew.-% Al2O3 und 12 bis 19 Gew.-% Fe2O3 auf.An inventive preferred aluminate cement, in each case based on the aluminate cement and in each case determined according to DIN EN 196-2: 1994, 35 to 41 wt .-% CaO, 1 to 6 wt .-% SO 2 , 35 to 45 wt .-% Al 2 O 3 and 12 to 19 wt .-% Fe 2 O 3 on.

Was die Calciumsulfat-Komponente der erfindungsgemäßen Trockenmischung anbelangt, so wird diese vorzugsweise in hydratisierter Form, insbesondere in Form des Hemihydrats, eingesetzt.What As regards the calcium sulfate component of the dry blend according to the invention, so this is preferably in hydrated form, in particular in the form of hemihydrate.

Auch die Menge an eingesetztem Calciumsulfat in der erfindungsgemäßen Trockenmischung kann in weiteren Bereichen variieren. Die Menge an Calciumsulfat liegt im Bereich von 3 bis 20 Gew.-%, insbesondere 5 bis 15 Gew.-%, bevorzugt 5 bis 10 Gew.-%, bezogen auf die Trockenmischung.Also the amount of calcium sulfate used in the dry mix according to the invention can vary in other areas. The amount of calcium sulfate is in the range from 3 to 20% by weight, in particular from 5 to 15% by weight, preferably 5 to 10 wt .-%, based on the dry mixture.

Besonders gute Ergebnisse werden erhalten, wenn ein Calciumsulfat mit einer spezifischen Oberfläche nach Blaine von 2.500 bis 3.500 cm2/g, bevorzugt 2.750 bis 3.250 cm2/g, besonders bevorzugt von etwa 3.000 cm2/g, eingesetzt wird. Das eingesetzte Calciumsulfat sollte einen Calciumsulfatgehalt von mindestens 90 Gew.-% aufweisen, bezogen auf das Calciumsulfat.Particularly good results are obtained when a calcium sulfate having a Blaine surface area of from 2,500 to 3,500 cm 2 / g, preferably 2,750 to 3,250 cm 2 / g, more preferably from about 3,000 cm 2 / g, is used. The calcium sulfate used should have a calcium sulfate content of at least 90% by weight, based on the calcium sulfate.

Ein erfindungsgemäß bevorzugtes Calciumsulfat besitzt eine Reindichte von 2,5 bis 3,0 g/cm3, insbesondere 2,7 bis 2,9 g/cm3, und eine Schüttdichte von 800 bis 1.200 g/l, insbesondere 850 bis 1.150 g/l, vorzugsweise 900 bis 1.100 g/l.A preferred calcium sulfate according to the invention has a true density of 2.5 to 3.0 g / cm 3 , in particular 2.7 to 2.9 g / cm 3 , and a bulk density of 800 to 1200 g / l, in particular 850 to 1150 g / 1, preferably 900 to 1100 g / l.

Wie zuvor geschildert, läßt sich das erfindungsgemäß geforderte Ergebnis – die Herstellung einer selbstverlaufenden bzw. selbstausgleichenden Spachtel-, Estrich- oder Bodenausgleichsmasse mit exzellenten Oberflächeneigenschaften, insbesondere hoher Eben- bzw. Glattheit und gutem optischem Erscheinungsbild – dann erreichen, wenn man die zuvor genannten Komponenten – nämlich Portlandkalksteinzement, Aluminatzement und Calciumsulfat – mit Eisensulfat und Aluminiumsulfat kombiniert.As previously described, can be the invention required Result - the Production of a self-leveling or self-leveling spatula, Screed or floor leveling compound with excellent surface properties, especially high level smoothness and good visual appearance - then achieve if you include the aforementioned components - namely Portland limestone cement, Aluminate cement and calcium sulfate - with iron sulfate and aluminum sulfate combined.

Denn die Anmelderin hat herausgefunden, daß gerade die vorgenannte Kombination von Komponenten zu exzellenten Oberflächen führt, wenn die erfindungsgemäße Trockenmischung zu Spachtel-, Estrich- oder Bodenausgleichsmassen durch Anmachen mit Wasser verarbeitet und auf einen Untergrund aufgetragen und dort nachfolgend ausgehärtet bzw. abgebunden wird. Die erzielten Oberflächen der Spachtel-, Estrich- oder Bodenausgleichsmasse zeichnen sich nicht nur durch eine exzellente Oberflächenglattheit aus, sondern auch durch ein exzellentes und einheitliches optisches Erscheinungsbild mit durchgehend kontinuierlicher, gleichmäßiger Färbung der Oberfläche.Because the Applicant has found that it is the aforementioned combination from components to excellent surfaces, when the dry mix according to the invention to putty, screed or ground leveling compounds by dressing processed with water and applied to a substrate and cured there below or is tied off. The achieved surfaces of putty, screed or Soil balancing mass are not only characterized by an excellent Surface smoothness but also through an excellent and consistent visual Appearance with continuous continuous, even coloring of the Surface.

Was das erfindungsgemäß eingesetzte Eisensulfat anbelangt, so wird dieses bevorzugt in Form von Eisen(II)sulfat eingesetzt, vorzugsweise in hydratisierter Form, besonders bevorzugt in Form des Hexa- bis Heptahydrats. Die Menge an erfindungsgemäß eingesetzten Eisensulfat kann in weiten Bereichen variieren; sie liegt im Bereich von 0,001 bis 2 Gew.-%, insbesondere 0,01 bis 0,25 Gew.-%, bevorzugt 0,025 bis 0,2 Gew.-%, bezogen auf die Trockenmischung.What the invention used As regards iron sulfate, this is preferably in the form of iron (II) sulfate used, preferably in hydrated form, more preferably in the form of hexa- to heptahydrate. The amount of inventively used Iron sulfate can vary widely; she lies in the area from 0.001 to 2 wt .-%, in particular 0.01 to 0.25 wt .-%, preferably 0.025 to 0.2 wt .-%, based on the dry mixture.

Ein erfindungsgemäß bevorzugtes Eisensulfat weist ein Schüttgewicht von 0,6 bis 1,0 t/m3, insbesondere 0,7 bis 0,9 t/m3, vorzugsweise von etwa 0,8 t/m3 auf.An inventively preferred iron sulfate has a bulk density of 0.6 to 1.0 t / m 3 , in particular 0.7 to 0.9 t / m 3 , preferably from about 0.8 t / m 3 .

Was das erfindungsgemäß eingesetzte Aluminiumsulfat anbelangt, so kann dieses gleichermaßen in weiten Mengenbereichen eingesetzt werden. Es werden Mengen an Aluminiumsulfat von 0,001 bis 2 Gew.-%, insbesondere 0,01 bis 0,25 Gew.-%, bevorzugt 0,025 bis 0,2 Gew.-%, bezogen auf die Trockenmischung eingesetzt.As far as the aluminum sulphate used according to the invention is concerned, this can be applied equally in wide ranges of quantities are used. Amounts of aluminum sulfate of from 0.001 to 2% by weight, in particular from 0.01 to 0.25% by weight, preferably from 0.025 to 0.2% by weight, based on the dry mixture, are used.

Die Leistungsfähigkeit der erfindungsgemäßen Trockenmischung läßt sich noch dadurch steigern, daß ihr außerdem noch Calciumhydroxid, insbesondere in hydratisierter Form, vorzugsweise in Form von Weißkalkhydrat, zugesetzt wird. Die Menge an Calciumhydroxid kann gleichermaßen in weiten Bereichen variieren. Im allgemeinen wird das Calciumhydroxid in Mengen von 0,001 bis 3 Gew.-%, insbesondere 0,01 bis 0,25 Gew.-%, bezogen auf die Trockenmischung, eingesetzt; dennoch kann es gegebenenfalls erforderlich sein von den vorgenannten Werten abzuweichen.The capacity the dry mix according to the invention let yourself even more by increasing your Furthermore nor calcium hydroxide, especially in hydrated form, preferably in the form of hydrated lime, is added. The amount of calcium hydroxide can be equally wide Ranges vary. In general, the calcium hydroxide is in Amounts of 0.001 to 3 wt .-%, in particular 0.01 to 0.25 wt .-%, based on the dry mixture used; nevertheless, it may possibly be required to deviate from the abovementioned values.

Weiterhin kann die erfindungsgemäße Trockenmischung außerdem Kalksteinmehl enthalten, insbesondere in Mengen von 5 bis 40 Gew.-%, vorzugsweise 20 bis 35 Gew.-%, besonders bevorzugt 25 bis 35 Gew.-%, bezogen auf die Trockenmischung. Erfindungsgemäß bevorzugtes Kalksteinmehl enthält mindestens 90 Gew.-%, vorzugsweise mindestens 95 Gew.-%, Calciumcarbonat, bezogen auf das Kalksteinmehl. Besonders gute Ergebnisse werden mit einem Kalksteinmehl mit einer Schüttdichte von 800 bis 1.000 g/l, insbesondere 900 bis 950 g/l, erhalten. Im Rahmen der vorliegenden Erfindung bevorzugtes Kalksteinmehl besitzt eine spezifische Oberfläche nach Blaine von 3.500 bis 4.500 cm2/g, vorzugsweise 3.750 bis 4.250 cm2/g, besonders bevorzugt von etwa 4.000 cm2/g.Furthermore, the dry mixture according to the invention may also contain limestone powder, in particular in amounts of 5 to 40 wt .-%, preferably 20 to 35 wt .-%, particularly preferably 25 to 35 wt .-%, based on the dry mixture. Limestone flour preferred according to the invention contains at least 90% by weight, preferably at least 95% by weight, of calcium carbonate, based on the limestone flour. Particularly good results are obtained with a limestone powder having a bulk density of 800 to 1,000 g / l, in particular 900 to 950 g / l. Limestone flour preferred in the context of the present invention has a Blaine specific surface area of 3,500 to 4,500 cm 2 / g, preferably 3,750 to 4,250 cm 2 / g, particularly preferably about 4,000 cm 2 / g.

Weiterhin kann es vorteilhaft sein, wenn die erfindungsgemäße Trockenmischung bzw. Rezeptur außerdem Quarzsand enthält, insbesondere in Mengen von 15 bis 80 Gew.-%, vorzugsweise 25 bis 50 Gew.-%, besonders bevorzugt 30 bis 35 Gew.-%, bezogen auf die Trockenmischung.Farther It may be advantageous if the dry mixture or formulation according to the invention Furthermore Contains quartz sand, especially in amounts of 15 to 80 wt .-%, preferably 25 to 50 wt .-%, particularly preferably 30 to 35 wt .-%, based on the Dry mixture.

Gemäß einer besonderen Ausführungsform der vorliegenden Erfindung wird ein Gemisch von Quarzsanden unterschiedlicher Korngrößen und/oder unterschiedlicher spezifischer Oberflächen nach Blaine eingesetzt. Insbesondere wird ein etwas feinkörnigerer Quarzsand mit einem etwas grobkörnigerem Quarzsand kombiniert. Erfindungsgemäß bevorzugter Quarzsand weist einen SiO2-Gehalt von mehr als 95 Gew.-%, vorzugsweise von mehr als 98 Gew.-%, bezogen auf den Quarzsand auf. Erfindungsgemäß bevorzugter Quarzsand weist eine theoretische spezifische Oberfläche (Blaine) von mindestens 65 cm2/g, vorzugsweise mindestens 75 cm2/g, besonders bevorzugt mindestens 85 cm2/g, auf.According to a particular embodiment of the present invention, a mixture of quartz sands of different grain sizes and / or Blaine specific surface areas is used. In particular, a somewhat finer-grained quartz sand is combined with a somewhat coarser-grained quartz sand. Quartz sand preferred according to the invention has an SiO 2 content of more than 95% by weight, preferably more than 98% by weight, based on the quartz sand. Quartz sand preferred according to the invention has a theoretical specific surface area (Blaine) of at least 65 cm 2 / g, preferably at least 75 cm 2 / g, particularly preferably at least 85 cm 2 / g.

Weiterhin kann es vorgesehen sein, daß die erfindungsgemäße Trockenmischung außerdem weitere Inhaltsstoffe und/oder Additive enthält, um die Anwendungseigenschaften erfindungsgemäßen Trockenmischung zu optimieren. Solche Inhaltsstoffe bzw. Additive können beispielsweise ausgewählt aus der Gruppe von Verflüssigern, Verzögerern, Stabilisierungsmitteln, Entschäumern, Beschleunigern, Füllstoffen und dergleichen.Farther can it be provided that the Dry mixture according to the invention Furthermore contains other ingredients and / or additives to the application properties Dry mixture according to the invention to optimize. Such ingredients or additives may, for example selected from the group of condensers, retarders, Stabilizers, defoamers, Accelerators, fillers and the same.

Beispielsweise kann die erfindungsgemäße Trockenmischung mindestens einen Verflüssiger enthalten, insbesondere in Mengen von 0,01 bis 5 Gew.-%, vorzugsweise 0,05 bis 2 Gew.-%, besonders bevorzugt 0,1 bis 0,5 Gew.-%, bezogen auf die Trockenmischung. Beispiele für erfindungsgemäß bevorzugte Verflüssiger sind Verflüssiger auf der Basis modifizierter Polycarboxylatether. Insbesondere werden die Verflüssiger derart ausgewählt, daß sie den Wasserbedarf beim Anmachen reduzieren und zudem vorteilhafterweise auch zu einer besonders guten Frühfestigkeitsentwicklung führen bzw. diese fördern.For example can the dry mix according to the invention at least one condenser contain, in particular in amounts of 0.01 to 5 wt .-%, preferably 0.05 to 2 wt .-%, particularly preferably 0.1 to 0.5 wt .-%, based on the dry mix. Examples of preferred according to the invention Condenser are condenser based on modified polycarboxylate ethers. In particular, be the liquefiers so selected that she to reduce the need for water when Anmachen and also advantageously also to a particularly good early strength development to lead or promote them.

Weiterhin kann die erfindungsgemäße Trockenmischung zur Optimierung der Anwendungseigenschaften ein die rheologischen und/oder physikalischen Eigenschaften verbesserndes bzw. beeinflussenden Additiv enthalten. Dieses kann beispielsweise auf Basis eines in Wasser redispergierbaren Polymerbindemittels, vorzugsweise auf Basis von Vinylacetat und Ethylen ausgebildet sein (Ethylen/Vinylacetat-Copolymer). Ein derartiges Additiv kann insbesondere in Mengen von 1 bis 15 Gew.-%, vorzugsweise 2 bis 10 Gew.-%, bezogen auf die Trockenmischung, eingesetzt werden.Farther can the dry mix according to the invention to optimize the application properties a the rheological and / or physical properties improving or influencing additive contain. This can for example be based on a in water redispersible polymer binder, preferably based on Be formed vinyl acetate and ethylene (ethylene / vinyl acetate copolymer). One Such additive may in particular be used in amounts of from 1 to 15% by weight, preferably 2 to 10 wt .-%, based on the dry mixture used become.

Weiterhin kann es für die Optimierung der Anwendungseigenschaften förderlich sein, wenn die erfindungsgemäße Trockenmischung außerdem mindestens einen Beschleuniger, insbesondere einen Erhärtungsbeschleuniger, enthält, beispielsweise auf Basis von Alkali- oder Erdalkalicarbonaten, besonders bevorzugt Lithiumcarbonat. Der Beschleuniger kann in Mengen von 0,001 bis 1 Gew.-%, insbesondere 0,05 bis 0,25 Gew.-%, bezogen auf die Trockenmischung, eingesetzt werden.Farther can it for the optimization of the application properties to be beneficial if the dry mix according to the invention Furthermore at least one accelerator, in particular a hardening accelerator, contains for example, based on alkali or alkaline earth carbonates, especially preferably lithium carbonate. The accelerator can be used in quantities of 0.001 to 1 wt .-%, in particular 0.05 to 0.25 wt .-%, based on the dry mix, are used.

Weiterhin kann die erfindungsgemäße Trockenmischung auch mindestens einen Entschäumer enthalten, beispielsweise eine feste Kombination von flüssigen Kohlenwasserstoffen, Polyglykolen und amorpher Kieselsäure. Ein solcher Entschäumer kann insbesondere in Mengen von 0,001 bis 1 Gew.-%, vorzugsweise 0,05 bis 3 Gew.-%, bezogen auf die Trockenmischung, eingesetzt werden.Furthermore, the dry mixture according to the invention may also contain at least one defoamer, for example a solid combination of liquid hydrocarbons, polyglycols and amorphous Silica. Such an antifoaming agent can be used in particular in amounts of from 0.001 to 1% by weight, preferably from 0.05 to 3% by weight, based on the dry mixture.

Des weiteren kann die erfindungsgemäße Trockenmischung außerdem mindestens ein Stabilisierungsmittel enthalten. Solche Stabilisierungsmittel können beispielsweise ausgewählt sein aus Gummen (z. B. Diutan Gum) oder aber auf Basis von Cellulose oder Cellulosederivaten (z. B. Hydroxyethylcellulose ausgebildet sein). Gleichermaßen können verschiedene Stabilisierungsmittel miteinander kombiniert werden, z. B. Gummen einerseits und Cellulose oder Cellulosederivate andererseits. Wenn als Stabilisierungsmittel Gummen eingesetzt werden, können diese in Mengen von 0,001 bis 0,2 Gew.-%, vorzugsweise 0,03 bis 0,08 Gew.-%, bezogen auf die Trockenmischung eingesetzt werden. Wenn als Stabilisierungsmittel Cellulose bzw. Cellulosederivate (z. B. Hydroxyethylcellulose) eingesetzt werden, können diese in Mengen von 0,001 bis 0,5 Gew.-%, vorzugsweise 0,05 bis 0,15 Gew.-%, bezogen auf die Trockenmischung, eingesetzt werden.Of another can dry mix according to the invention Furthermore contain at least one stabilizing agent. Such stabilizers can for example, selected be made of gums (eg Diutan Gum) or based on cellulose or cellulose derivatives (eg hydroxyethyl cellulose) be). equally can different stabilizers are combined with each other, z. B. gums on the one hand and cellulose or cellulose derivatives on the other. If gums are used as stabilizers, they can in amounts of 0.001 to 0.2% by weight, preferably 0.03 to 0.08% by weight, be used based on the dry mix. When as a stabilizer Cellulose or cellulose derivatives (eg., Hydroxyethylcellulose) used can, can these in amounts of 0.001 to 0.5 wt .-%, preferably 0.05 to 0.15 wt .-%, based on the dry mixture used.

Für alle vorgenannten Mengenangaben gilt, daß es einzelfallbedingt oder anwendungstechnisch gegebenenfalls erforderlich sein kann, von diesen Mengenangaben abzuweichen. Dies zu entscheiden, liegt im Ermessen des Fachmanns.For all the above Quantity information applies that it depending on the individual case or application technology possibly required may be different from these quantities. To decide this is at the discretion of the skilled person.

Außerdem kann die erfindungsgemäße Trockenmischung mindestens einen Zusatz zur Einstellung des Wasserrückhaltevermögens enthalten.In addition, can the dry mix according to the invention contain at least one additive for adjusting the water retention capacity.

Im allgemeinen wird die erfindungsgemäße Trockenmischung derart formuliert, daß mehr als 99 % der Teilchen der Trockenmischung Teilchengrößen bzw. Teilchendurchmesser unterhalb von 400 μm, vorzugsweise unterhalb von 355 μm, gemäß Siebanalyse (DIN 66 165, April 1987, insbesondere Teil 2, Trockensiebung) und/oder mehr als 35 % der Teilchen Teilchengrößen bzw. Durchmesser im Bereich von bis zu 63 μm gemäß Siebanalyse aufweisen.in the In general, the dry mix according to the invention is formulated in such a way that that more 99% of the particles of the dry mixture have particle sizes or Particle diameter below 400 microns, preferably below 355 μm, according to sieve analysis (DIN 66 165, April 1987, especially Part 2, dry screening) and / or more than 35% of the particles have particle sizes or diameters in the range of up to 63 μm according to sieve analysis exhibit.

Insbesondere ist die Trockenmischung nach der vorliegenden Erfindung durch die folgenden Teilchengrößenverteilung gemäß Siebanalyse gekennzeichnet:

Figure 00110001
In particular, the dry mix according to the present invention is characterized by the following particle size distribution according to sieve analysis:
Figure 00110001

Die erfindungsgemäße Trockenmischung bzw. Rezeptur eignet sich insbesondere zur Verwendung in Spachtel-, Estrich- oder Bodenausgleichsmassen bzw. zu deren Herstellung.The Dry mixture according to the invention or formulation is particularly suitable for use in spatula, Screed or floor leveling compounds or for their production.

Gegenstand der vorliegenden Erfindung – gemäß einem weiteren Aspekt der vorliegenden Erfindung – ist somit die Verwendung der Trockenmischung nach der vorliegenden Erfindung in Spachtel-, Estrich- oder Bodenausgleichsmassen oder zur Herstellung von Spachtel-, Estrich- oder Bodenausgleichsmassen.object of the present invention - according to a Another aspect of the present invention - is thus the use the dry mix of the present invention in putty, Screed or leveling compounds or for the production of filler, Screed or ground leveling compounds.

Ausgehend von der erfindungsgemäßen Trockenmischung können die Spachtel-, Estrich- oder Bodenausgleichsmassen durch Anmachen der erfindungsgemäßen Trockenmischung mit Wasser bzw. durch Zusetzen von Wasser zu der erfindungsgemäßen Trockenmischung hergestellt werden. Im allgemeinen wird die erfindungsgemäßen Trockenmischungen unter Zugabe von 10 bis 30 Gew.-%, vorzugsweise 20 bis 30 Gew.-%, Wasser angemacht.outgoing from the dry blend according to the invention can the putty, screed or ground leveling compounds by dressing the dry mix according to the invention with water or by adding water to the dry mixture according to the invention getting produced. In general, the dry mixtures according to the invention with the addition of 10 to 30% by weight, preferably 20 to 30% by weight, Water turned on.

Die unter Verwendung der erfindungsgemäßen Trockenmischung durch Anmachen mit Wasser erhältlichen und nachfolgend auf einen Untergrund aufgetragenen und schließlich abgebundenen bzw. abgetrockneten Spachtel-, Estrich- oder Bodenausgleichsmassen, welche Ettringitkristalle enthalten, sind dadurch gekennzeichnet, daß die hierin enthaltenen, beim Abbinden entstan denen Ettringitkristalle – im Vergleich zu Spachtel-, Estrich- oder Bodenausgleichsmassen des Standes der Technik – besonders kurzstengelig bzw. gedrungen, sozusagen tonnenförmig ausgebildet ist.The available using the dry mixture according to the invention by mixing with water and subsequently applied to a substrate and finally set or tucked off Neten putty, screed or ground leveling compounds containing Ettringitkristalle are characterized in that the herein contained when setting entstan which Ettringitkristalle - compared to putty, screed or Bodenausgleichsmassen of the prior art - particularly kurzstengelig or squat, so to speak is barrel-shaped.

Das Länge/Durchmesser- bzw. Länge/Breite-Verhältnis der Ettringitkristalle in den ausgehend von der erfindungsgemäßen Trockenmischung hergestellten Spachtel-, Estrich- oder Bodenausgleichsmassen nach Abbinden bzw. Abtrocknen/Aushärten, wie es durch Analyse von REM-Aufnahmen bestimmt worden ist, liegt im allgemeinen unterhalb von 5,0, insbesondere unterhalb von 4,5, vorzugsweise unterhalb von 4,0. Insbesondere liegt das Länge/Durchmesser- bzw. Länge/Breite-Verhältnis der Ettringitkristalle in diesen Spachtel-, Estrich- oder Bodenausgleichsmassen nach Abbinden bzw. Abtrocknen und Aushärten im Bereich von 1,0 bis 4,0, insbesondere 1,3 bis 3,0, vorzugsweise 1,4 bis 2,0, ganz besonders bevorzugt 1,4 bis 1,9.The Length / diameter or length / width ratio of Ettringite crystals in the starting from the dry mixture according to the invention prepared putty, screed or ground leveling compounds after setting or drying / curing, as determined by analysis of SEM images lies in the general below 5.0, especially below 4.5, preferably below 4.0. In particular, the length / diameter or length / width ratio of Ettringite crystals in these leveling, screed or leveling compounds after setting or drying and curing in the range of 1.0 to 4.0, especially 1.3 to 3.0, preferably 1.4 to 2.0, especially preferably 1.4 to 1.9.

Im Vergleich hierzu ist das Länge/Durchmesser- bzw. Länge/Breite-Verhältnis in Ettringitkristallen in Spachtel-, Estrich- oder Bodenausgleichsmassen des Standes der Technik deutlich größer und liegt oberhalb von 5,0, da diese Ettringitkristalle nadelförmig ausgebildet sind und für die rauhe, unebene Oberfläche verantwortlich sind.in the In comparison, the length / diameter or length / width ratio in Ettringite crystals in putty, screed or ground leveling compounds of the prior art significantly larger and is above 5.0, since these ettringite crystals are needle-shaped and for the rough, uneven surface are responsible.

Die Begriffe "Länge" einerseits und "Durchmesser" bzw. "Breite" andererseits beziehen sich auf das Erscheinungsbild der Kristalle in REM-Aufnahmen, wobei der Begriff "Länge" die maximale Längsausdehnung der Kristalle und der Begriff "Durchmesser" (oder synonym "Breite") die maximale Querausdehnung der Kristalle bezeichnet.The Relate terms "length" on the one hand and "diameter" or "width" on the other referring to the appearance of crystals in SEM images, taking the term "length" is the maximum longitudinal extent of the Crystals and the term "diameter" (or synonymously "width") the maximum transverse extent called the crystals.

Dies wird anhand der 1 und 2 deutlich. Während die Ettringitkristalle gemäß 1, wie sie in Spachtel-, Estrich- oder Bodenausgleichsmassen des Standes der Technik auftreten, nadelförmig ausgebildet sind und im konkreten Fall der 1 ein Länge/Durchmesser- bzw. Länge/Breite-Verhältnis von etwa 5,5 bis 5,8 aufweisen, liegt dieses Länge/Durchmesser- bzw. Länge/Breite-Verhältnis bei Ettringitkristallen in ausgehend von der erfindungsgemäßen Trockenmischung hergestellten Spachtel-, Estrich- oder Bodenausgleichsmassen, wie 2 zeigt, unterhalb von 5,0 und im konkreten Fall von 2 bei etwa 1,8, wobei die Ettringitkristalle in der Struktur gemäß 2 kurz stengeliger, gedrungener und etwa tonnenförmig im Vergleich zu den nadelförmigen Ettringitkristallen der 1 erscheinen.This is based on the 1 and 2 clear. While the ettringite crystals according to 1 , as they occur in spatula, screed or ground leveling compounds of the prior art, are needle-shaped and in the specific case of 1 have a length / diameter or length / width ratio of about 5.5 to 5.8, this length / diameter or length / width ratio for ettringite crystals is based on the putty, screed or ground leveling compounds, such as 2 shows below 5.0 and in the specific case of 2 at about 1.8, with the ettringite crystals in the structure according to 2 short stemmed, stocky and approximately barrel shaped compared to the acicular ettringite crystals of 1 appear.

Weitere Ausführungsformen, Ausgestaltungen, Abwandlungen und Variationen der vorliegenden Erfindung sind für den Fachmann beim Lesen der vorliegenden Anmeldung ohne weiteres erkennbar und realisierbar, ohne daß er dabei den Rahmen der vorliegenden Erfindung verläßt.Further Embodiments, Embodiments, modifications and variations of the present invention are for those skilled in the reading of the present application readily recognizable and realizable, without being the scope of the present Invention leaves.

Die vorliegende Erfindung wird anhand des folgenden Ausführungsbeispiels veranschaulicht. The The present invention will become apparent from the following embodiment illustrated.

Ausführungsbeispiel:Embodiment:

Eine erfindungsgemäß bevorzugte Rezeptur für eine Trockenmischung nach der vorliegenden Erfindung lautet insbesondere wie folgt:

Figure 00140001
A formulation according to the invention for a dry mix according to the present invention is in particular as follows:
Figure 00140001

Die vorgenannte Trockenmischung eignet sich insbesondere zur Herstellung von oder Einarbeiten in Spachtel-, Estrich- oder Bodenausgleichsmassen. Derartige Spachtel-, Estrich- oder Bodenausgleichsmassen zeichnen sich durch eine extrem geringe Oberflächenrauhigkeit bei exzellentem optischem Erscheinungsbild (= gleichmäßige weiß-gräuliche Färbung) aufgrund des Gehalts an kurzstengeligen Ettringitkristallen aus.The The aforementioned dry mix is particularly suitable for the production of or incorporation into putty, screed or ground leveling compounds. Draw such leveling, screed or ground leveling compounds characterized by an extremely low surface roughness with excellent optical appearance (= uniform white-grayish color) due to the content on short-stemmed ettringite crystals.

Claims (20)

Trockenmischung, enthaltend – 0,5 bis 20 Gew.-% Portlandkalksteinzement, – 5 bis 30 Gew.-% Aluminatzement und – 3 bis 20 Gew.-% Calciumsulfat in Kombination mit 0,001 bis 2 Gew.-% Eisensulfat und 0,001 bis 2 Gew.-% Aluminiumsulfat, wobei alle vorgenannten Gewichtsprozentangaben auf die Trockenmischung bezogen sind.Dry mix containing - 0.5 to 20% by weight Portland limestone cement, 5 to 30% by weight of aluminate cement and - 3 to 20 wt .-% calcium sulfate in combination with 0.001 to 2 Wt .-% iron sulfate and 0.001 to 2 wt .-% aluminum sulfate, in which All the above weight percentages on the dry mix are related. Trockenmischung nach Anspruch 1, enthaltend Portlandkalksteinzement in Mengen von 1,5 bis 12 Gew.-%, bevorzugt 2 bis 8 Gew.-%, bezogen auf die Trockenmischung.A dry mix according to claim 1 containing Portland limestone cement in amounts of 1.5 to 12 wt .-%, preferably 2 to 8 wt .-%, based on the dry mix. Trockenmischung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß der Portlandkalksteinzement eine spezifische Oberfläche nach Blaine von 3.000 bis 6.000 cm2/g, insbesondere 3.500 bis 5.500 cm2/g, bevorzugt 4.500 bis 5.000 cm2/g, aufweist.Dry mixture according to Claim 1 or 2, characterized in that the Portland limestone cement has a Blaine specific surface area of 3,000 to 6,000 cm 2 / g, in particular 3,500 to 5,500 cm 2 / g, preferably 4,500 to 5,000 cm 2 / g. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, daß der Portlandkalksteinzement, jeweils bezogen auf den Portlandkalksteinzement, 60 bis 70 Gew.-% CaO und/oder 20 bis 30 Gew.-% SiO2 und/oder 2 bis 6 Gew.-% Al2O3 und/oder 1 bis 5 Gew.-% Fe2O3 enthält, jeweils bestimmt nach DIN EN 196-2:1994.Dry mixture according to one or more of the preceding claims, characterized in that the Portland limestone cement, in each case based on the Portland limestone cement, 60 to 70 wt .-% CaO and / or 20 to 30 wt .-% SiO 2 and / or 2 to 6 wt. Contains -% Al 2 O 3 and / or 1 to 5 wt .-% Fe 2 O 3 , each determined according to DIN EN 196-2: 1994. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, enthaltend Aluminatzement in Mengen von 15 bis 25 Gew.-%, bevorzugt 15 bis 20 Gew.-%, bezogen auf die Trockenmischung.Dry mixture according to one or more of the preceding Claims, containing aluminate cement in amounts of 15 to 25 wt .-%, preferably 15 to 20 wt .-%, based on the dry mixture. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, daß der Aluminatzement eine spezifische Oberfläche nach Blaine von 2.000 bis 4.000 cm2/g, insbesondere 2.500 bis 3.750 cm2/g, bevorzugt 2.750 bis 3.500 cm2/g, aufweist.Dry mixture according to one or more of the preceding claims, characterized in that the aluminate cement has a Blaine surface area of from 2,000 to 4,000 cm 2 / g, in particular 2,500 to 3,750 cm 2 / g, preferably 2,750 to 3,500 cm 2 / g. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, daß der Aluminatzement, jeweils bezogen auf den Aluminatzement, 35 bis 41 Gew.-% CaO und/oder 1 bis 6 Gew.-% SiO2 und/oder 35 bis 45 Gew.-% Al2O3 und/oder 12 bis 19 Gew.-% Fe2O3 enthält, jeweils bestimmt nach DIN EN 196-2:1994.Dry mixture according to one or more of the preceding claims, characterized in that the aluminate cement, based in each case on the aluminate cement, contains 35 to 41% by weight of CaO and / or 1 to 6% by weight of SiO 2 and / or 35 to 45% by weight. Contains -% Al 2 O 3 and / or 12 to 19 wt .-% Fe 2 O 3 , each determined according to DIN EN 196-2: 1994. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, enthaltend Calciumsulfat, vorzugsweise in hydratisierter Form, insbesondere Form des Hemihydrats, in Mengen von 5 bis 15 Gew.-%, bevorzugt 5 bis 10 Gew.-%, bezogen auf die Trockenmischung.Dry mixture according to one or more of the preceding Claims, containing calcium sulfate, preferably in hydrated form, in particular Form of hemihydrate, in amounts of 5 to 15 wt .-%, preferably 5 to 10 wt .-%, based on the dry mixture. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, daß das Calciumsulfat eine spezifische Oberfläche nach Blaine von 2.500 bis 3.500 cm2/g, bevorzugt 2.750 bis 3.250 cm2/g, besonders bevorzugt von etwa 3.000 cm2/g, aufweist und/oder daß das Calciumsulfat einen Calciumsulfatgehalt von mindestens 90 Gew.-%, bezogen auf das Calciumsulfat, aufweist.Dry mixture according to one or more of the preceding claims, characterized in that the calcium sulphate has a Blaine surface area of from 2,500 to 3,500 cm 2 / g, preferably 2,750 to 3,250 cm 2 / g, more preferably about 3,000 cm 2 / g, and or that the calcium sulfate has a calcium sulfate content of at least 90 wt .-%, based on the calcium sulfate having. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, daß das Calciumsulfat eine Reindichte von 2,5 bis 3,0 g/cm3, insbesondere 2,7 bis 2,9 g/cm3, aufweist und/oder daß Calciumsulfat eine Schüttdichte von 800 bis 1.200 g/l, insbesondere 850 bis 1.150 g/l, vorzugsweise 900 bis 1.100 g/l, aufweist.Dry mixture according to one or more of the preceding claims, characterized in that the calcium sulphate has a true density of 2.5 to 3.0 g / cm 3 , in particular 2.7 to 2.9 g / cm 3 , and / or that calcium sulphate has a Bulk density of 800 to 1200 g / l, in particular 850 to 1150 g / l, preferably 900 to 1100 g / l, having. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, enthaltend Eisensulfat, insbesondere Eisen(II)sulfat, vorzugsweise in hydratisierter Form, insbesondere in Form des Hexa- bis Heptahydrats, in Mengen von 0,01 bis 0,25 Gew.-%, bevorzugt 0,025 bis 0,2 Gew.-%, bezogen auf die Trockenmi schung, insbesondere wobei das Eisensulfat ein Schüttgewicht von 0,6 bis 1,0 t/m3, insbesondere 0,7 bis 0,9 t/m3, vorzugsweise von etwa 0,8 t/m3, aufweist.Dry mixture according to one or more of the preceding claims, containing iron sulfate, in particular iron (II) sulfate, preferably in hydrated form, in particular in the form of hexa to heptahydrate, in amounts of 0.01 to 0.25 wt .-%, preferably 0.025 to 0.2 wt .-%, based on the dry mix, in particular wherein the iron sulfate has a bulk density of 0.6 to 1.0 t / m 3 , in particular 0.7 to 0.9 t / m 3 , preferably from about 0.8 t / m 3 . Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, enthaltend Aluminiumsulfat in Mengen von 0,01 bis 0,25 Gew.-%, bevorzugt 0,025 bis 0,2 Gew.-%, bezogen auf die Trockenmischung.Dry mixture according to one or more of the preceding Claims, containing aluminum sulfate in amounts of 0.01 to 0.25 wt .-%, preferably 0.025 to 0.2 wt .-%, based on the dry mixture. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, enthaltend außerdem Kalksteinmehl, insbesondere in Mengen von 5 bis 40 Gew.-%, vorzugsweise 20 bis 35 Gew.-%, besonders bevorzugt 25 bis 35 Gew.-%, bezogen auf die Trockenmischung.Dry mixture according to one or more of the preceding Claims, containing also limestone flour, especially in amounts of from 5 to 40% by weight, preferably from 20 to 35% by weight, especially preferably 25 to 35 wt .-%, based on the dry mixture. Trockenmischung nach Anspruch 13, dadurch gekennzeichnet, daß das Kalksteinmehl mindestens 90 Gew.-%, insbesondere mindestens 95 Gew.-%, Calciumcarbonat enthält, bezogen auf das Kalksteinmehl, und/oder daß das Kalksteinmehl eine Schüttdichte von 800 bis 1.000 g/l, insbesondere 900 bis 950 g/l, aufweist und/oder daß das Kalksteinmehl eine spezifische Oberfläche nach Blaine von 3.500 bis 4.500 cm2/g, vorzugsweise 3.750 bis 4.250 cm2/g, besonders bevorzugt von etwa 4.000 cm2/g, aufweist.A dry mix according to claim 13, characterized in that the limestone flour contains at least 90% by weight, in particular at least 95% by weight, of calcium carbonate, based on the limestone flour, and / or that the limestone flour has a bulk density of 800 to 1000 g / l, in particular 900 to 950 g / l, and / or that the limestone flour has a Blaine surface area of from 3,500 to 4,500 cm 2 / g, preferably 3,750 to 4,250 cm 2 / g, particularly preferably about 4,000 cm 2 / g. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, enthaltend außerdem Quarzsand, insbesondere in Mengen von 15 bis 80 Gew.-%, vorzugsweise 25 bis 50 Gew.-%, besonders bevorzugt 30 bis 35 Gew.-%, bezogen auf die Trockenmischung.Dry mixture according to one or more of the preceding Claims, containing quartz sand, especially in amounts of 15 to 80 wt .-%, preferably 25 to 50 wt .-%, especially preferably 30 to 35 wt .-%, based on the dry mixture. Trockenmischung nach Anspruch 15, dadurch gekennzeichnet, daß ein Gemisch von Quarzsanden unterschiedlicher Korngrößen und/oder unterschiedlicher spezifischer Oberflächen nach Blaine eingesetzt wird und/oder daß der Quarzsand einen SiO2-Gehalt von mehr als 95 Gew.-%, vorzugsweise von mehr als 98 Gew.-%, bezogen auf den Quarzsand aufweist und/oder daß der Quarzsand eine theoretische spezifische Oberfläche nach Blaine von mindestens 65 cm2/g, vorzugsweise mindestens 75 cm2/g, besonders bevorzugt mindestens 85 cm2/g, aufweist.Dry mixture according to claim 15, characterized in that a mixture of quartz sands of different grain sizes and / or different Blaine specific surface areas is used and / or that the quartz sand has an SiO 2 content of more than 95% by weight, preferably more than 98% Wt .-%, based on the quartz sand and / or that the quartz sand has a theoretical specific surface area of Blaine of at least 65 cm 2 / g, preferably at least 75 cm 2 / g, particularly preferably at least 85 cm 2 / g. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, enthaltend außerdem Calciumhydroxid, insbesondere in hydratisierter Form, vorzugsweise in Form von Weißkalkhydrat, vorzugsweise in Mengen von 0,001 bis 3 Gew.-%, insbesondere 0,01 bis 0,25 Gew.-%, bezogen auf die Trockenmischung.Dry mixture according to one or more of the preceding Claims, also containing calcium hydroxide, especially in hydrated form, preferably in the form of hydrated lime, preferably in amounts of 0.001 to 3 wt .-%, in particular 0.01 to 0.25 wt .-%, based on the dry mixture. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, enthaltend außerdem weitere Inhaltsstoffe und/oder Additive, insbesondere ausgewählt aus der Gruppe von Verflüssigern, Verzögerern, Stabilisierungsmitteln, Entschäumern, Beschleunigern und Füllstoffen.Dry mixture according to one or more of the preceding Claims, containing further Ingredients and / or additives, in particular selected from the group of condensers, retarders, Stabilizers, defoamers, Accelerators and fillers. Trockenmischung nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, daß mehr als 99 % der Teilchen der Trockenmischung Teilchengrößen oder Teilchendurchmesser unterhalb von 400 μm, vorzugsweise unterhalb von 355 μm, gemäß Siebanalyse aufweisen und/oder daß mehr als 35 % der Teilchen Teilchengrößen oder Durchmesser im Bereich von bis zu 63 μm gemäß Siebanalyse aufweisen, insbesondere wobei die Trockenmischung durch die folgende Teilchengrößenverteilung gemäß Siebanalyse gekennzeichnet ist:
Figure 00180001
Dry mixture according to one or more of the preceding claims, characterized in that more than 99% of the particles of the dry mixture have particle sizes or particle diameters below 400 μm, preferably below 355 μm, according to sieve analysis and / or that more than 35% of the particles have particle sizes or Have diameters in the range of up to 63 microns according to sieve analysis, in particular wherein the dry mixture is characterized by the following particle size distribution according to sieve analysis:
Figure 00180001
 Verwendung einer Trockenmischung nach einem der Ansprüche 1 bis 19 in Spachtel-, Estrich- oder Bodenausgleichsmassen oder zur Herstellung von Spachtel-, Estrich- oder Bodenausgleichsmassen.Use of a dry mix according to one of claims 1 to 19 in putty, screed or ground leveling compounds or for the production of fillers, floor screed or floor leveling compounds.
DE200510001101 2005-01-08 2005-01-08 Dry mix and its use in or for putty, screed or ground leveling compound Expired - Fee Related DE102005001101B4 (en)