CZ40293A3 - Alkaline silicate glass - Google Patents
Alkaline silicate glass Download PDFInfo
- Publication number
- CZ40293A3 CZ40293A3 CZ93402A CZ40293A CZ40293A3 CZ 40293 A3 CZ40293 A3 CZ 40293A3 CZ 93402 A CZ93402 A CZ 93402A CZ 40293 A CZ40293 A CZ 40293A CZ 40293 A3 CZ40293 A3 CZ 40293A3
- Authority
- CZ
- Czechia
- Prior art keywords
- glass
- composition according
- tio
- weight
- glass composition
- Prior art date
Description
Vynález se týká složeni skla a výrobků, vyrobených ze skla tohoto složeni.
Dosavadní stav techniky
Vynález se zejména, ale ne výlučně, týká zboží z křišťálového skla. Zatímco olověné křišťálové sklo bylo široce využíváno po mnoho let pro takový artikl, jako jsou karafy, poháry a jiné výrobky určené pro nápoje a, v případě dekantérů jako baleni pro dlouhodobé skladováni, potenciální toxicita olova a jeho sloučenin vyvolala snahy snižovat obsah olova. Zároveň musely být udrženy optické vlastnosti, které udávají estetické kvality tradičního složení olověného skla a vlastnosti a ekonomika potřebná pro výrobu skla a jeho produktů. Pro tradiční průmysl olověného křišťálového skla, je rovněž požadováno, aby sklo bylo schopno dalšího zpracováni, to je formováni do výrobků ručně i strojově.
Po dobu více než tři sta let se používaly olověné sloučeniny jako přísady pro své schopnosti udávat nutné tepelné, optické, mechanické a chemické vlastnosti sklům s ekonomicky dosažitelnými tavícími teplotami. Olověné sloučeniny také způsobují postupné zvyšováni viskozity, jak se teplota snižuje, pro umožnění ručního zpracování skla do konečných výrobků, to jest, ve sklářské terminologii řečeno, udávají delší rozmezí zpracováni. Skla musí být rovněž schopna podstoupit řezání, broušeni a leštěni.
Je známo, že určité prvky a sloučeniny poskytnou alkalickému křemičitému sklu některé z žádoucích vlastnosti. Optická skla v oblasti lanthanové koruny mají vysoké indexy lomu, ale nízký rozptyl. Sloučeniny baria jsou používány některými výrobci jako náhrada za olovo při výrobě křišťálového skla, ale indexy lomu a rozptyl jsou mnohem nižší než u olovnatého křišťálového skla. Barium a sloučeniny baria, s výjimkou sulfátu, jsou rovněž toxické. Sloučeniny zinku byly používány při výrobě zinkového křišťálového skla, ale nezvyšují výrazně index lomu nebo disperzi nad hodnoty základního skla. Titan zvyšuje index lomu a rozptyl všech skel, ale je obtížné ho začlenit bez zavedení krystalizace a barvy a skla nejsou poddajná pro ruční tvarování.
Podstata vynálezu
Předmětem vynálezu je takové složeni skla, které odstraňuje všechny tyto nevýhody tím, že používá nejedovaté přísady pro umožnění výroby skla a skleněných výrobků, které by měly výhodné výrobní ceny a podobný nebo lepši estetický vzhled než mají olověné křišťálové výrobky a zejména křišťálové sklénice, založené na konvenčním alkalicko- křemičitém složení skla s vysokými indexy lomu v přebytku 1,55, vysoké disperzi, jak je naměřena Abbovým číslem - méně než 46, a které má následující vlastnosti:
- je barvy prosté, tavící teploty umožňující použiti konvenčních peci pro tavbu křišťálových skel, elektrické vlastnosti, které dovoluji elektrické taveni, pracovní rozsah umožňující ruční i strojové zpracování, vysokou trvanlivost, odolnost proti solarizaci a extremně nízkou tendenci ke krystalizaci .
Podle vynálezu je složeni skla následující:
SiCr
45-65% hmotnostních
M;0 12-23% hmotnostních a
B12O3 a/nebo TiO? až do 30% hmotnostních kde M=Na, K nebo Li
Jestliže chybí TiO?, pak Bi;O3 samotné může být < 30% hmotnostních. Jestliže B12O3 chybí, pak TiO: samotné může být <20% hmotnostních. Menšinové přísady až do 12% hmot. v celkovém množství, mohou být zahrnuty do složeni, aby se získaly specifické charakteristiky pro taviči a formovací proces a pro vzhled skla a výrobků z něj.
Je-li to požadováno, může křišťálové sklo navíc obsahovat jako čisticí činidla jeden nebo více antimon trioxyd, arsen trioxyd nebo oxyd ceričitý v celkovém množství do 1% hmot. Navíc mohou být rovněž do složeni zahrnuty odbarvovaci sloučeniny, jako jedna nebo více z následujících sloučenin N1O2, Nd2O3 nebo MnO.
Zjistili jsme, že přidáním sloučenin bismutu do alkalického křemičitého skla, může být index lomu a rozptyl zvýšen více, než může být dosaženo podobnými přísadami olova na obou bázích, hmotnostních %, i molových %. Zjistili jsme také, že přidáni bismuthu udělí dlouhý rozsah zpracování, vhodný pro ruční zpracováni. Navíc se skla taví při hladině teploty podobné, nebo mírně nižší, než je teplota tavení skel, obsahujících olovo s podobným množstvím přísad.
Sloučeniny bismutu jsou sice mnohem dražší než sloučeniny olova a proto ceny surového materiálu bismutových skel jsou vyšši, než ceny surového materiálu olověných skel. Zjistili jsme, že je možné nahradit trochu nebo všechen bismut titanem, s následným zlepšením obou ukazatelů - indexů lomu a rozptylů a sníženi cen suroviny. Titan je přidáván nejběžněji použitím titaničitanů, ale mohou být použity i ostatní sloučeniny. Rozsah zpracováni skel obsahujících titan je kratší, než bismutového skla, ale je stale ještě vhodný pro ruční zpracováni při nižší hladině titanu a pro strojové tvarováni při vyšší hladině titanu.
Menšinové přísady mohou být použity například pro upraveni elektrických vlastnosti skla pro jeho výrobu v elektricky vytápěných pecích, slabé barvy, kterým může být dána přednost ve výrobku a zvučnost. Malé přísady mohou zahrnovat jednu nebo více z následujících sloučenin AS2O3, SbzCb, MnO, NiO, Nd2O3, CaO, ZrO2, SrO2 La2O3 a ZnO, aby dodaly specifické vlastnosti, které mohou být podle vynálezu požadovány pro zvláštní sklo.
Příklady provedeni vynálezu
Následující tabulka udává indexy lomu a Abbova čísla složeni skla podle vynálezu.
Tabulka 1 - Příklady složení podle vynálezu
« | Č . | SiO2 | m2o | BÍ 203 | TiO 2 | — ZnO | ZrO2 | La 2 0 3 | — Other |
1 | 59.9 | 20.0 | 20.0 | - | - | - | 0.1 | ||
2 | 59.8 | 15.0 | 20.0 | - | 5.0 | - | - | 0.2 | |
3 | 59.8 | 20.0 | 15.0 | 5.0 | - | 0.2 | |||
4 | 57.8 | 20.0 | 10.0 | 8.0 | 5.0 | - | - | 0.2 | |
5 | 59.8 | 20.0 | 10.0 | 10.0 | - | - | 0.2 | ||
6 | 59.8 | 20.0. | 5.0 | 15.0 | - | 0.2 | |||
1 ; 7 | 59. Θ | 20.0 | 20.0 | - | - | 0.2 | |||
i 8 | 59.4 | 20.1 | 15.1 | 5.0 | - | 0.4 | |||
! 9 | 58.3 | 17.5 | 11.0 | 8.0 | 5.0 | 0.2 | |||
1 : 0 | 58.8 | 18.0 | 12.0 | 7.0 | - | - | 4.0 | 0.2 |
Tabulka 2 - Indexy lomu a Abbova čísla skla podle příkladu
— č . | Index lomu Nd | Abbovo číslo Vd |
1 | 1.551 | 45.2 |
2 | 1.557 | 44.5 |
3 | 1.560 | 43.5 |
4 | 1.570 | 42.5 |
5 | 1.566 | 42.0 |
6 | 1.575 | 39.5 |
7 | 1.582 | 36.8 |
8 | 1.558 | 44.3 |
9 | 1.572 | 43.0 |
10 1_ | 1.568 | 44.1 |
Bylo zjištěno, že jednotlivá složení skla podle vynálezu jsou vyhovující pro tavbu v běžných průmyslových pecích, mají pracovní rozsah umožňující tvarování křišťálových skleněných výrobků pomoci stávajících postupů, jsou odolná proti solarizaci, proti působeni okolí a odolná proti vylohováni komponent skla do obsahu nádob z nich vyrobených.
Oxydy, hydroxydy, uhličitany a dalši kyslikaté sloučeniny mohou být použity jako suroviny k přípravě složeni skla podle vynálezu.
Vynález také zahrnuje výrobky, především křišťálové sklenice, vyrobené ze skla, jehož složeni je podle vynalezu.
Claims (7)
1. Složeni alkalického křemičitého skla s indexem lomu 1,55
hmot. a Bi2O3 a/nebo TiO2 0 až 30 % hmot. (kde M=Na, K nebo Li) a Bi2O3 až do 30 % hmot.
3. Složení skla podle nároku 1, vyznačující se tím, že sestává z SiO2 45-65 % , M20 12-23 % a Bi2O3 a/nebo TiO2 0 až 30 % hmot. (kde M=Na, K nebo Li) a TiO3 až do 20 % hmot.
4. Složeni skla podle kteréhokoliv předchozího nároku vyznačující se tím, že dále obsahuje jednu nebo více z následujících sloučenin Al2O3, MnO, NiO, Nd2O3, CaO, ZrO2, SrO2 La2O3 a ZnO v celkovém obsahu do
12% hmot.
5. Složeni skla podle kteréhokoliv předchozího nároku vyznačující se tím, že dále obsahuje jako čisticí činidla jednu nebo více z následujících sloučenin trioxyd antimon, trioxyd arsenik nebo kysličník ceričitý, v celkovém množství do 1% hmot.
6. Složeni skla podle kteréhokoliv předchozího nároku vyznačující se tím, že dále obsahuje jako odbarvovaci sloučeniny jednu nebo více z následujících sločenin: N1O2 , NdjOs nebo MnO až do 0,1% hmot.
7. Složení skla podle kteréhokoliv předchozího nároku , vyznačující se tim, že dále obsahuje • jako menšinové přísady jednu nebo více z následujících sloučenin: AS2O3, Sb2O3, MnO, NiO, Nd2O3, AI2O3J CaO,
ZrO2, Sr02, La2O3 a ZnO.
8. Zboží, zejména křišťálové sklenice, vyrobené ze skla o složeni podle předcházejících nároků.