CS257686B1

CS257686B1 - A method of making artificial lures made of plastic for fishing on udio

Info

Publication number: CS257686B1
Application number: CS866437A
Authority: CS
Inventors: Budimir Veruovic
Original assignee: Budimir Veruovic
Priority date: 1986-05-14
Filing date: 1986-05-14
Publication date: 1988-05-16
Also published as: CS643786A1

Abstract

Způsob výroby umělých nástrah z plastů pro lov ryb na udici probíhá tak, že se 16 až 50 hmot. dílů paetotvornáho polyvinylchloridu o K hodnotě 60 až 73 smíohá s 49,5 až 72 díly dioktylftalátu, 2 až 5 dílů stabilizátoru polyvinylchloridu, 0,1 až 5 dílů barvlva, 0,2 az 2 díly hydroohinonu až vznikne homogenní směs, která se želatinuj4 při teplotě 160 až 190 °C po dobu 60 až 15 minut a vzniklý gel se taví při teplotě 160 až 180 °C po dobu 25 až 60 minut a tavenina se vpraví pod tlakem do formy.The method of producing artificial plastic baits for fishing on an angling line is carried out by mixing 16 to 50 parts by weight of a paste-forming polyvinyl chloride with a K value of 60 to 73 with 49.5 to 72 parts of dioctyl phthalate, 2 to 5 parts of a polyvinyl chloride stabilizer, 0.1 to 5 parts of a dye, and 0.2 to 2 parts of hydroquinone until a homogeneous mixture is formed, which is gelatinized at a temperature of 160 to 190 °C for 60 to 15 minutes and the resulting gel is melted at a temperature of 160 to 180 °C for 25 to 60 minutes and the melt is introduced into a mold under pressure.

Description

Vynález se týká způsobu výroby umělých nástrah z plaétů pro lov ryb na udici.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of making artificial baits from fishing rods.

Při lovu ryb na udici používají rybáři různé druhy návnad, nejčastěji živočišného, rostlinného nebo syntetického původu. Jako živočišné návnady se nejčastěji používají žížaly, červi, různé druhy hmyzu, které se navlékají na háček udice. Uvedené návnady živočišného původu jsou nejvhodnější zejména pro lov říčních ryb. Návnady rostlinného původu se připravují zejména z těsta, ovoce, chleba a jiných moučných a ovocných výrobků. Návnady syntetického původu bývají většinou vyrobeny z kovů, syntetických vláken, z různých polymerních materiálů a nebo kombinací uvedených materiálů. U syntetických nástrah háčky udice představují obvykle součást nástrahy. Tvary umělých nástrah představují většinou živočichy, které ryby rády loví a nebo i jiné tvary, které upoutávají pozornost ryb. Ryby vybírají jednotlivé druhy návnad i podle jejich barvy. Je známo, že ryby některé barvy nemají v oblibě. Z těchto důvodů se věnuje výběru barvy a barevných odstínů návnad velká pozornost. Návnady světlé barvy, například žlutá, oranžová, červená, přilákají ryby spíše než návnady tmavých barev, například modré či hnědé.When fishing with a line, fishermen use different types of baits, most often of animal, vegetable or synthetic origin. The most commonly used animal baits are earthworms, worms, various insects, which are strung on hook hooks. These baits of animal origin are particularly suitable for catching river fish. Baits of vegetable origin are prepared mainly from dough, fruit, bread and other flour and fruit products. The baits of synthetic origin are usually made of metals, synthetic fibers, various polymeric materials or combinations of these materials. In synthetic lures, hook hooks are usually part of the lure. The shapes of artificial lures are mostly animals that fish like to catch or other shapes that attract the attention of fish. Fish choose different types of baits according to their color. It is known that fish of some colors do not like. For these reasons, great attention is paid to the color selection and color shades. Lures of light color, such as yellow, orange, red, attract fish rather than lures of dark color, such as blue or brown.

Nevýhodou dosavadních nástrah, které rybáři používají, spočívají především v tom, že živočišné nástrahy nejsou k dispozici v potřebném množství a v požadovaném čase. Na návnady rostlinného původu se chytají jen určité druhy ryb, avšak ne v průběhu celé sezóny. Návnady z kovů a syntetických materiálů nejsou návnady univerzálního charakteru, nebot se na ně chytá jen určitý druh ryb a v určitou dobu v sezóně. Stejný druh ryb v rozdílných lokalitách se Čgrsto chytá na stejný druh návnad.The disadvantage of the current lures used by fishermen is mainly that animal lures are not available in the required amount and in the required time. Only certain fish are caught on bait of plant origin, but not during the whole season. Baits made of metals and synthetic materials are not universal lures, because they are caught only by a certain type of fish and at a certain time in the season. The same kind of fish in different locations catches the same kind of bait.

Ze zkušeností rybářů je však známo, že na stejnou návnadu není možno chytat stejný druh ryb v rozdílných lokalitách.However, it is known from the experience of fishermen that it is not possible to catch the same species in different locations on the same bait.

'257686 ifaedfené st&va.iící nedostatky V oblasti výroby umělých ná* ** ' · vnad pro lov ryb na udici od2*tra«ftje způsob výroby umělých nástrah z plastů pro lov ryb na udici, podle vynálezu. Jeho podstata spočívá v tom, že se vyrobí z pastotvorného polyvinylchloridu, změkčovadla, například dioktylftalátu, dibutylftalátu, trikresylfosfátu, stabilizátoru polyvinylchloridu, například stearátu vápenatého, zinečnatého nebo jejich směsí, dále hydrochinonu a barviva tak, že tato směs se homogenizuje mícháním v hnětači a potom se želatinuje zahříváním při teplotě 160 až 190 °Č. Gelová hmota se dále taví při teplotě 160 až 180 °C po dobu 25 až 60 minut a tavenina se vpravuje do předehřáté formy pod tlakem za použití například zubového Čerpadla nebo injekční stříkačky. Po ochlazení hmoty ve formě na' teplotu 60 až 100 °C je možno hotový produkt, tedy návnadu, vyjmout z formy. V případě výroby několikabarevné návnady postupuje se tak, že se návnada vyrobí v jedné barvě a druhá, respektive třetí barva se nanáší na příslušnou část návnady štětečkem nebo vstřikováním. Háček se zavádí do návnady po její celkové úpravě. Háček může být i jako součást návnady, napodobující živočicha, například hlavičky a podobně. Vlastní konzistence hmoty návnady se upravuje poměrem pťivodních složek, zejména, poměrem polyvinylchloridu a změkčovadla, podle toho, zda návnada má být měkčí, elastická nebo tužší, se sníženou elasticitou. 'The present invention relates to a method for the production of plastic bait bait baits according to the invention. It consists of a paste-forming polyvinyl chloride, a plasticizer, for example dioctyl phthalate, dibutyl phthalate, tricresyl phosphate, a polyvinyl chloride stabilizer, for example calcium stearate, zinc stearate or mixtures thereof, hydroquinone and a colorant, such that the mixture is homogenized and then blended in brown is gelatinized by heating at 160-190 ° C. The gel mass is further melted at a temperature of 160 to 180 ° C for 25 to 60 minutes and the melt is introduced into a preheated mold under pressure using, for example, a gear pump or syringe. After the mold mass is cooled to 60 to 100 ° C, the finished product, i.e. the bait, can be removed from the mold. In the case of producing a multicolored bait, the bait is produced in one color and the second and third colors, respectively, are applied to the respective part of the bait by brush or injection. The hook is introduced into the bait after it has been completely modified. The hook may also be part of an animal-like bait, such as a head or the like. The intrinsic consistency of the bait mass is adjusted by the ratio of the water components, in particular the ratio of polyvinyl chloride and plasticizer, depending on whether the bait is to be softer, elastic or stiffer, with reduced elasticity. '

Nástrahy vyrobené způsobem podle vynálezu dokonale napodobují tvar a pohyby některých živočichů, které ryby rády loví a z’ hlediska barevné přitažlivosti tyto nástrahy předčí řadu živočichů, jako jsou žížaly, různé druhy červů, chobotničky, rybky a jiné. Další výhodou nástrah podle vynálezu je, že se mohou zhotovovat v libovolných tvarech, obsahujících vibrující nebo kmitající části, jako jsou ocásky, křidélka, ploutvičky a podobně. Kombinací tvarů, barev a hmotové konzistence poskytuje způsob podle vynálezu výrobu různých návnad, které je možno mít v zásobě a použít ten druh, o který ryby v příslušné lokalitě a době projevují největší zájem. Způsob podle vynálezu lze využít i pro výrobu'elastických, respektive plastických hraček s rychlou vratnou deformací nebo k'výrobě modelů zvířat, plazů, ryb a podobně. Výrobky podle vynálezu jsou trvanlivé, dobře se barví a z hlediska hygienického jsou nezávadné.The baits made by the method of the invention perfectly mimic the shape and movements of some of the animals the fish love to fish, and in terms of color attraction these baits outperform a number of animals such as earthworms, various types of worms, squid, fish and others. A further advantage of the baits of the invention is that they can be made in any shape including vibrating or oscillating parts such as tails, wings, fins and the like. By combining shapes, colors and mass consistency, the method of the invention provides the production of various baits that can be kept in stock and use the species of interest to the fish at the location and time in question. The method according to the invention can also be used for the production of elastic or plastic toys with rapid reversible deformation or for the production of animal models, reptiles, fish and the like. The products according to the invention are durable, well-colored and hygienic.

Vynález a jeho účinky jsou vysvětleny v popise třech příkladů provádění způsobu výroby umělých nástrah z plastů pro lov ryb na udici podlé vynálezu.The invention and its effects are explained in the description of three exemplary embodiments of a method of making synthetic bait baits according to the invention.

Příklad 1Example 1

13,1 g polyvinylchbridu vyrobeného emulzní technikou o K hodnotě 72 bylo zamícháno v porcelánové misce se 49,7 g dioktylftalátu, 1,04 g směsi stearátu vápenatého a stearátu zinečnatého v poměru 1 : 1, 0,1 g hydroohinonu a 0,01 g barviva fluorescenčního výrobního označení Hostagelb 86. Směs byla homogenizována mícháním-po dobu 2 hodin a ponechána přes noc k nabotnání. Druhý den hmota byla promíchána a vpravena do baňky, ve které byla zahřívána při 180 °C za občasného míchání. Během 20 minut tekutý obsah v baňce utvořil gel, který byl dále zahříván po dobu 25 minut, kdy se postupně roztavil na celkem velmi dobře tekoucí taveninu. Tavenina byla přelita do celoskleněné injekční stříkačky a vstřiknuta do formy ze silikonového kaučuku. Po ochlazení hmoty ve formě na teplotu asi 60 °C byl produkt po otevření formy vyjmut. Hmota přesně kopírovala formu a produkt je elastický, homogenního vybarvení.13.1 g of polyvinyl chloride produced by emulsion technique of K value 72 were mixed in a porcelain dish with 49.7 g of dioctyl phthalate, 1.04 g of a 1: 1 mixture of calcium stearate and zinc stearate, 0.1 g hydroquinone and 0.01 g Hostagelb 86 fluorescent product dyes. The mixture was homogenized by stirring for 2 hours and left to swell overnight. The next day, the mass was mixed and placed in a flask in which it was heated at 180 ° C with occasional stirring. Within 20 minutes, the liquid content of the flask formed a gel, which was further heated for 25 minutes when it gradually melted to a fairly well flowing melt. The melt was poured into an all-glass syringe and injected into a silicone rubber mold. After the mold mass was cooled to about 60 ° C, the product was removed after opening the mold. The mass accurately copied the mold and the product is elastic, homogeneous coloring.

Příklad 2Example 2

235 g emulzního pastotvořného polyvínylchloridu o K hodnotě 71 bylo smícháno s 892 g dibutylftalátu, 18,64 g stabilizátoru uvedeného v příkladě 1, 5 g hydroohinonu a 0,2 g barviva obchodního označení Pluorogrůngold a směs dále zpracována jako u příkladu 1. Výsledný produkt je příjemný na omak, homogenní struktury a homogenního vybarvení.235 g of an emulsion paste-forming polyvinyl chloride having a K value of 71 were mixed with 892 g of dibutyl phthalate, 18.64 g of the stabilizer mentioned in Example 1, 5 g of hydroquinone and 0.2 g of dye Pluorogrüngold and further processed as in Example 1. pleasant to the touch, homogeneous texture and homogeneous coloring.

Příklad 3Example 3

235 g emulzního pastotvořného polyvínylchloridu o K hodnotě 69 bylo smícháno s 892 g dioktylftalátu, 18,64 g stabilizátoru polyvínylchloridu na bázi stearátu vápenatého a zinečnatého, 5 g hydroohinonu a 0,4 g červeného barviva a směs déle zpracována jako u příkladu 1. Výsledný produkt se vyznačoval vysokou elasticitou, homogenním vybarvením a homogenní konzistencí hmoty.235 g of an emulsion paste-forming polyvinyl chloride having a K value of 69 were mixed with 892 g of dioctyl phthalate, 18.64 g of a polyvinyl chloride stabilizer based on calcium and zinc stearate, 5 g of hydroquinone and 0.4 g of a red dye. characterized by high elasticity, homogeneous coloring and homogeneous consistency of the mass.

Claims

SUBJECT OF THE INVENTION

Process for the production of plastic bait baits, characterized in that 16 to 50 wt. % of paste-forming polyvinyl chloride having a K value of 60 to 75 is mixed with 49.5 to 72 wt. parts by weight of dioctyl phthalate, 2 to 5 wt. 0.1 parts by weight of a polyvinyl chloride stabilizer; 5 wt. 0.2 parts to 2 wt. parts of hydroquinone to form a homogeneous mixture, which is gelatinized at 160-190 ° C for 60-15 minutes and the gel formed melts at 160-180 ° C for 25-60 minutes, and the melt is pressed into a mold under pressure.