CS236678B2 - Cooling and lubricating paste for metal working and theier cold pressing - Google Patents
Cooling and lubricating paste for metal working and theier cold pressing Download PDFInfo
- Publication number
- CS236678B2 CS236678B2 CS825935A CS593582A CS236678B2 CS 236678 B2 CS236678 B2 CS 236678B2 CS 825935 A CS825935 A CS 825935A CS 593582 A CS593582 A CS 593582A CS 236678 B2 CS236678 B2 CS 236678B2
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- weight
- lubricating
- bentonite
- coolant
- cooling
- Prior art date
Description
Vynález se týká nových chladicích a mazacích přípravků, které je možné používat - při třískovém a beztřískovém obrábění kovů a jiných materiálů, jakož i způsobu zlepšení známých chladicích a mazacích kapalin.
Při provádění zmíněných obráběcích technologií se používá větší počet chladicích a mazacích prostředků, které mají takový chladicí a mazací účinek, že zabraňují poškození materiálu ohřevem a mohou zaručit potřebnou hladkost povrchu materiálu. Tyto prostředky nesmí být škodlivé pro -lidi a okolí, dále musí být smývatelné a jejich použití musí být ekonomické.
Jako chladicí a mazací prostředky se používá obecně vhodná kapalina, například olejové emulze, avšak u profilových nástrojů, při velkých pracovních rychlostech a velkém plošném tlaku nelze chlazení pomocí kapalíny zaručit.
V odborrné literatuře je popsáno- více řešení shora uvedeného problému a některé zde uvedené přípravky lze již v obchodě dostat.
V rakouském patentovém spisu č. 313 452 je popsána chladicí kapalina, která obsahuje soli těžkých kovů a potřebný chladicí účinek se dosahuje chemickým ’ procesem. Nedostatek tohoto přípravku spočívá v jeho obsahu síranu a dusitanu železa, niklu a kobaltu, což s ohledem na nebezpečí intoxikace vyžaduje při používání velkou opatrnost.
Ve švýcarském patentovém spisu 481 208 je popsána chladicí kapalina, která obsahuje jako emulzi alkanolaminy a glykoly. Zmíněné složky mohou ale vyvolávat onemocnění kůže.
V DE-PS č. 239 895 je popsáno mazivo, které sestává v podstatě z oleje, hliníkového prášku a grafitového prášku. Při použití směsi je důležitým předpokladem, že teplota látky, která se bude obrábět, bude vyšší, než je teplota tání hliníku, a proto je možné tuto směs používat jen ve válcovnách.
V DE-PS č. -1 594 532 je popsán přípravek s -omezeným- vývinem kouře, který je ale rovněž upotřebitelný jen ve válcovnách.
Je známé, že možnost -zatížení teplem lze zvyšovat pomocí syntetických -olejů nebo syntetických tuků, tyto látky jsou ale značně drahé a škodlivé pro okolí.
K těmto- přípravkům patří například pasta pro závitovou frézu firmy Ci-ncinatti, Holandsko, a kapalina „Dundy“ firmy Daniel a Jáger, Stuttgart. Tyto přípravky mohou ale snadno- při velkých řezných výkonech snadno zplynovat a vznikající plyny jsou škodlivé -pro- zdraví.
U některých chladicích kapalin vystupují vedle problémů použitelnosti také velké problémy -s osídlením bakteriemi. Švýcarský patentový spis č. 508 035 nabízí řešení tohoto· problému například použitím formaldehydu. S ^ohledem na jeho rychlé odpařování je ale třeba jej dávkovat ve velkých množstvích, tato množství mohou vyvolávat onemocnění kůže a znečišťovat vzduch. Stejné nedostatky mají i ostatní dezinfekční prostředky.
Zlepšení vlastností známých chladicích a mazacích kapalin zabraňuje ale i ta skutečnost, že v těchto kapalinách nejsou rozpustné vhodné přísady, jako jsou například látky, které zvyšují mazací účinek, například mýdla, grafit, síra a jiné -přísady, a výroba homogenních a stabilních přípravků naráží na velké potíže.
Úkolem vynálezu je proto- vytvoření takových chladicích a mazacích prostředků, které by při obrábění kovů a jiných materiálů za velkých řezných výkonů mohly poskytnout odpovídající chladicí účinek, které by tedy připouštěly možnost velikého zatížení a měly dobrou přilnavost.
Pokusy prokázaly, že bentonit -může s ohledem na botnavost tvořit s kapalinami, například -s různými bodno-bazickými chladicími a mazacími kapalinami, pastu, - která r^ů:že být s dobrými výsledky používána jako- chladicí a mazací pasta i při velkých rychlostech obrábění.
Pokusy také ukázaly, že kvalita a homogenita pasty je- ovlivňována rozdělením velikosti zrn bentonitu. Jestliže bentonitová drť má částice větší než 70 μία, nelze zaručit při použití pasty obsahující bentonit s ohledem na špatnou botnavost příliš velkých částic například při lisování - desky potřebnou hladkost povrchu.
Vynález se proto týká chladicí a mazací pasty k obrábění kovů a jiných materiálů, která sestává z vody, 5,0 až 30,0 °/o hmot, bentonitu s velikostí zrna pod 70 μΐη a popřípadě z obvyklého oleje běžného druhu a obvyklého- množství, který je použitelný pro vodně-bazické chladicí a mazací kapaliny, popřípadě z přísad sloužících pro zlepšení mazacích schopností.
Chladicí a mazací pasta podle vynálezu sestává s výhodou ze 40,0 až 60,0 % hmot, vody, 5,0 až 30,0 % hmot, bentonitu a 10,0 až 50,0 % hmot, obvyklého oleje.
Chladicí a mazací pasta podle vynálezu obsahuje vedle vody, -bentonitu a obvyklého oieje s výhodou také 1,0 až 10,0 % hmot, přísad pro zlepšení mazacího účinku, zejména mýdlo, grafit a/nebo síru, s tou výhradou, že celkové množství bentonitu a přísad nesmí být větší než 30,0 % hmot., dále 5,0 až 20,0 °/o dezinfekčního -činidla a 0,1 až 1,0 % hmot, aromatické látky.
K pastě podle vynálezu se jako přísada mohou používat s výhodou mýdla jako například stearát vápenatý, horečnatý, hlinitý nebo- zlneěnatý, grafit, síra, dále všechny obvyklé dezinfekční látky, například formaldehyd a aromatické -látky.
Vynález se týká dále způsobu zlepšení obvyklých chladicích a mazacích kapalin, který spočívá v tem, že se 0,1 až 20 % hmot, přísad, nerozpustných v chladicí a mazací
236S78 б
kapalině, s výhodou látek zvyšujících mazací účinek, dezinfekčních prostředků a/nebo aromatických látek promísí se směsí, sestávající ze 30,0 až 80,0 % hmot, vody, 5,0 až 30,0 % hmot, bentonitu a popřípadě 30,0 až 50,0 % hmot, obvyklého oleje a přidají se к chladicí a mazací kapalině.
Způsobem podle vynálezu lze značně rozšířit okruh použití obvyklých chladicích a mazacích kapalin, neboť je možné použít takové přísady, jako jsou například mýdla, grafit, síru a/nebo aromatické látky a/nebo dezinfekční prostředky pro zlepšení obvyklých chladicích a mazacích kapalin, které s ohledem na nerozpustnost ve vodě a rychlé vylučování se к tomu nehodily.
Chladicí a mazací pasta podle vynálezu má následující přednosti:
a) Obsah vázané vody v bentonitu se uvolňuje při teplotě 500 až 700 °C, a proto má pasta podle vynálezu chladicí účinek během obrábění i při tak vysokých teplotách, při kterých se olej spaluje,
b) s ohledem na bod a) se zabraňuje vzniku par a plynů,
c) odvodněný bentonit má i sám o sobě dobrý mazací účinek a mazací účinek pasty je tedy větší než mazací účinek oleje,
d) zapracováním přísad jako například mýdel, grafitu, síry, aromatických látek a dezinfekčních prostředků, které s ohledem na rychlé vylučování nebyly až dosud použitelné, lze dále zvýšit mazací účinek pasty,
e) bentonit je vhodný také jako prostředek stabilizující emulzi, a tak je možné použitím siměsi sestávající z bentonitu a přísad zabránit nebo při nejmenším oddálit vylučování u chladicích a mazacích kapalin,
f) smíšením dezinfekčního prostředku a bentonitu a přidáním této směsi к obvyklé chladicí a mazací kapalině je možné dosáhnout koncentrace dezinfekčního prostředku pod obvyklou citlivostí kůže a současně zajistit biologickou čistotu a zabránit špičkové koncentrace dezinfekčního prostředku,
g) pasty podle vynálezu se mohou v protikladu ke známým syntetickým pastám a tukům snadno smývat.
Chladicí a mazací pasty podle vynálezu a způsob podle vynálezu jsou objasněny následujícími příklady, aniž by se omezovaly pouze na ně.
Příklad 1
Pro zjištění hlubokotažnosti byla z ocelové desky o tloušťce 2 mm vytažena nádobka o průměru 70 mm a výšce 40 mm. Podle obvyklých způsobů se deska má fosfátovat, jinak se povrch nádobky poruší, zbrázdí a síla stěny bude nerovnoměrná. Rychlost lisování činí 0,1 m/s.
Jako; chladicí a mazací pasta byla vyrobena emulze, obsahující vodu, chladicí a mazací olej v poměru 1 :1. Chladicí a mazací olej sestává z 84,0 % hmot, lehkého· minerálního. oleje, 10,0 °/o hmot, směsi řepkového oleje, parafínového oleje a palmového oleje, 5,0 % hmot, emulgátoru, 0Ό5 °/o hmot, baktericidního prostředku a 0,5 % hmot, sulfonátu vyššího alifatického alkoholu. 95 dílů hmotnostních emulze bylo· smícháno s 5,0 díly· hmotnostními bentonitu.
Touto pastou byla deska zpracována bez fosfátování a potom byla hlubokotažena, jak je uvedeno shora. Získala so nádobka s rovnoměrnou tloušťkou stěny a hladkým povrchem.
Příklad 2
Vířivou frézou byl vysoustružen kulový závit následujících technických parametrů:
Závit:
stoupání 20 mm délka 190 mm vnější průměr 0 28 h 11 hloubka 2,6 mm kužel 0 7 mm.
Soustružení:
řezná rychlost 300 m/min soustružení 5 min.
nástroj: soustružnický nůž s břitem ze slinutého karbidu základní surovina: ocel normalizovaná na 660 až 800 N/mm2 (Ra = 2,5 μ).
Požadovaná kvalita povrchu je Ra = 2,5 μ. Pro tento proces byla jako chladicí a mazací prostředek použita koncentrovaná kapalina pro frézování závitů na bázi silikonu. Životnost nástroje byla 2 hodiny a bylo možno konstatovat velmi silný vývoj plynů. S ohledem na koncentrovaný prostředek vznikala na kůži ekzematická onemocnění. Zdraví škodlivý účinek bylo možno zmírnit například zředěním kapaliny, ale tím se současně zkrátila i životnost nástroje.
Vyrobila se pasta smísením 30,0 dílů hmotnostních bentonitu, 56,0 dílů hmotnostních vody a 14,0 dílů hmotnostních silikonového· oleje. Proces byl opakován za použití této pasty, a bylo tak dosaženo zvýšení životnosti o 50 % a současné zabránění vývoje plynů a onemocnění kůže.
Příklad 3
Pro stejné soustružení jako v příkladu 2 byla použita pasta z chladicího a mazacího oleje, popsaného v příkladu 1, sestávající ze 13,0 dílů hmotnostních bentonitu, 45,0 dílů hmotnostních vody a 42,0 dílů hmotnostních shora zmíněného oleje. S touto pastou byly dosaženy stejné výsledky jako; v příkladu 2.
Potom byla zjišťována závislost účinku množství vody, bentonitu a oleje a bylo kom236 * statováno, že zvýšení obsahu oleje vede ke zlepšení kvality povrchu, toto zlepšení není ale značné a při obsahu oleje nad 50,0 % * hmot, nijak významné. Zvýšení obsahu vody vede k několikaprocentnímu zvýšení životnosti, avšak při obsahu nad 60 °/o hmot, poškozuje kvalitu povrchu. Snížení obsahu bentonitu pod 5,0 % hmot, se ukázalo být neúčinné. Při soustružení závitů, analogicky jako v příkladu 2, se základními surovinami s velkou pevností, bylo nalezeno nejpříznivější prodloužení životnosti při obsahu bentonitu maximálně 30 % hmot.
Příklad 4
Do pasty pro hluboké tažení jako v příkladu 1 byl jako- přísada vmíchán stearát vápenatý. Pastou, která obsahovala 44,5 % hmot, vody, 44,5 % hmot, oleje uvedeného v příkladu 1 a 5,0 % hmot, bentonitu a 6,0 procent hmot, stearátu vápenatého. Byla zpracována bez fosfátování deska a po- hlubokém tažení byl získán hrnec s dokonale hladkým povrchem. Kvalita povrchu byla dokonce vyšší než v příkladu 1. Stejný účinek byl dosažen i s grafitem a se sírou.
Příklad 5
Účinek stearátů byl zjišťován i při obrábění za odběru třísek. Bylo- provedeno soustružení závitů analogicky jako v příkladu 2, přičemž základní surovinou byla ocel s pevností vyšší o 100 až 150 N/mm2. Zde se životnost může při obsahu 1 % hmot, stearátu prodloužit o 5 až 8 %, přičemž prodloužení životnosti se může dále zvýšit až na 10 %. Při obsahu -stearátu nad 10 % hmot, se již účinnost dále -nezvyšuje.
Tyto- výsledky lze dosáhnout s různými stearáty nebo jejich směsmi.
Příklad 6
Jak bylo dříve popsáno, spočívá -velký pro-
Claims (5)
- PŘEDMĚT1. Chladicí a mazací pasta k obrábění ko;vů a jejich lisování za studená, vyznačující se tím, že obsahuje 40 až 60 % hmot, vody, 5,0 až 30,0 % hmot, bentonitu s velikostí zrna pod 70 μη a 10,0 až 50,0 % hmot, oleje libovolného- druhu, použitelného- pro- vodné bazické a chladicí mazací kapaliny -a popřípadě přísady pro zlepšení -mazacích vlastností, přičemž celkové množství bentonitu a přísad činí maximálně 30- % hmot.
- 2. Chladicí a mazací pasta podle bodu 1, vyznačující se tím, že jako přísadu obsahuje grafit a/nebo síru.7 3 blém. při použití chladicích a mazacích kapalin v udržení jejich biologické čistoty. Podle odborné literatury se pro zabránění bakteriologickému procesu má k emulzi v nezabezpečeném stavu přidat jako šok minimálně 0,5 % hmot, dezinfekčního prostředku. Aby se zajistila čistota čisté emulze, má se koncentrace dezinfekčního prostředku udržovat minimálně v rozmezí 0,1 až 0,15 % hmot. Obě uvedené hodnoty jsou velmi vysoké - a mohou vyvolat onemocnění kůže. Tak vysoká koncentrace se má udržeti proto, že dezinfekční prostředek z emulze v krátké době vypadne a potom se rychle rozloží.Aby se zabránilo vylučování dezinfekčního prostředku, vyrobila se směs sestávající ze 60,0 dílů hmot, obvyklé chladicí a mazací kapaliny, 20,0 dílů hmot, bentonitu a 20,0 dílů hmot, formaldehydu. Do- 100 1 nádoby -obráběcího· -stroje odebírajícího třísky bylo přidáno- po 8 hodinách provozu 30 gramů shora uvedené směsi. Tak byla dosažena v chladicí a mazací kapalině stroje koncentrace formaldehdu 0,006 % hmot, a pomocí tohoto množství byla kapalina během 16hodinového pracovního- klidu dokonale vyčištěna.Stejných výsledků bylo dosaženo, když byla ve směsi místo obvyklé chladicí a mazací kapaliny použita voda. Tato- druhá směs má ještě tu přednost, že je použitelná pro všechny chladicí a -mazací kapaliny.Použitím bentonitu by -se tedy koncentrace formaldehydu mohla snížit -na 1/20 až 1/30 dílu.Jak je zřejmé ze shora uvedených příkladů, -může se použitím bentonitu u - past podle vynálezu značně prodloužit životnost nástrojů a zabránit zdraví škodlivým účinkům chladicích a mazacích prostředků.VYNÁLEZU
- 3. Chladicí a mazací pasta podle bodu 1, vyznačující se tím., že jako přísadu obsahuje 3 až 10 % hmot, stearátu vápenatého, stearátu hořečnatého, stearátu hlinitého a/ /nebo- stearátu -zinečnatého.
- 4. Chladicí a mazací pasta podle bodu 1, vyznačující se tím, že dále obsahuje -5 až 20 procent hmot, dezinfekčního prostředku.
- 5. Chladicí a mazací pasta- podle jednoho z bodů 1 až 4, vyznačující se tím, že dále obsahuje 0,1 až 1 % hmot, aromatického prostředku.