CO6210695A2 - Abrasivos unidos a alta temperatura de alfa alumina de tamaño submicrometrico - Google Patents
Abrasivos unidos a alta temperatura de alfa alumina de tamaño submicrometricoInfo
- Publication number
- CO6210695A2 CO6210695A2 CO09064246A CO09064246A CO6210695A2 CO 6210695 A2 CO6210695 A2 CO 6210695A2 CO 09064246 A CO09064246 A CO 09064246A CO 09064246 A CO09064246 A CO 09064246A CO 6210695 A2 CO6210695 A2 CO 6210695A2
- Authority
- CO
- Colombia
- Prior art keywords
- alumina
- high temperature
- fixing agent
- abrasive
- granules
- Prior art date
Abstract
1.- Abrasivo unido a alta temperatura, que comprende: gránulos abrasivos de alúmina; y una matriz de unión vítrea en la que se distribuyen los gránulos abrasivos de alúmina, teniendo la matriz de unión vítrea una temperatura de curado no inferior a 1000°C, en el que los gránulos abrasivos de alúmina comprenden alfaalúmina policristalina que tiene una microestructura cristalina fina caracterizada por un tamaño de dominio promedio de alfa-alúmina no superior a 500 nm, y en el que los gránulos abrasivos de alúmina comprenden además un agente de fijación, comprendiendo el agente de fijación una fase dispersa en la alfa-alúmina policristalina. 2.- Abrasivo unido a alta temperatura según la reivindicación 1, en el que el agente de fijación es un óxido de al menos un elemento del grupo que consiste en silicio, boro, titanio, circonio, tierra rara, productos de reacción de los mismos con la alfa-alúmina policristalina y combinaciones de los mismos. 3.- Abrasivo unido a alta temperatura según la reivindicación 2, en el que el agente de fijación comprende óxido de circonio. 4.- Abrasivo unido a alta temperatura según la reivindicación 1, en el que el agente de fijación está presente en los gránulos abrasivos de alúmina en una cantidad no inferior a aproximadamente el 0,1% en peso. 5.- Abrasivo unido a alta temperatura según la reivindicación 4, en el que el agente de fijación está presente en los gránulos abrasivos de alúmina dentro de un intervalo de aproximadamente el 0,1 a aproximadamente el 20% en peso. 6.- Abrasivo unido a alta temperatura según la reivindicación 1, en el que el agente de fijación tiene un tamaño de material particulado promedio no superior a aproximadamente 1 micra. 7.- Abrasivo unido a alta temperatura según la reivindicación 1, en el que los gránulos abrasivos de alúmina tienen un tamaño de dominio cristalino promedio no superior a 400 nm. 8.- Abrasivo unido a alta temperatura según la reivindicación 7, en el que los dominios de la alfa-alúmina policristalina son monocristalinos y tienen un tamaño de dominio cristalino promedio no superior a 200 nm.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US87074006P | 2006-12-19 | 2006-12-19 |
Publications (1)
Publication Number | Publication Date |
---|---|
CO6210695A2 true CO6210695A2 (es) | 2010-10-20 |
Family
ID=39284199
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CO09064246A CO6210695A2 (es) | 2006-12-19 | 2009-06-19 | Abrasivos unidos a alta temperatura de alfa alumina de tamaño submicrometrico |
Country Status (22)
Country | Link |
---|---|
US (3) | US8932378B2 (es) |
EP (1) | EP2094443B1 (es) |
JP (1) | JP5231446B2 (es) |
KR (1) | KR101132159B1 (es) |
CN (1) | CN101594966B (es) |
AU (1) | AU2007337145B2 (es) |
BR (1) | BRPI0720401B1 (es) |
CA (1) | CA2672139C (es) |
CO (1) | CO6210695A2 (es) |
ES (1) | ES2452324T3 (es) |
HK (1) | HK1139102A1 (es) |
IL (2) | IL199408A (es) |
MX (1) | MX2009006591A (es) |
NZ (1) | NZ577441A (es) |
PL (1) | PL2094443T3 (es) |
PT (1) | PT2094443E (es) |
RU (1) | RU2415006C1 (es) |
SI (1) | SI2094443T1 (es) |
TW (1) | TWI351334B (es) |
UA (1) | UA92690C2 (es) |
WO (1) | WO2008079680A1 (es) |
ZA (1) | ZA200904293B (es) |
Families Citing this family (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8617273B2 (en) | 2009-10-08 | 2013-12-31 | Saint-Gobain Abrasives, Inc. | Bonded abrasive article and method of forming |
CA2781144C (en) | 2009-12-02 | 2014-11-25 | Saint-Gobain Abrasives, Inc. | Bonded abrasive article and method of forming |
KR20120101077A (ko) | 2009-12-02 | 2012-09-12 | 생-고벵 아브라시프 | 결합된 연마 물품 및 생성 방법 |
EP2616219A4 (en) * | 2010-09-15 | 2015-05-27 | Saint Gobain Abrasives Inc | IMPRESENTED FRICTION BRUSH |
EP2636655B1 (en) * | 2010-11-01 | 2016-07-20 | Showa Denko K.K. | Alumina sintered body, abrasive grains, and grindstone |
TWI470069B (zh) * | 2011-03-31 | 2015-01-21 | Saint Gobain Abrasives Inc | 用於高速磨削操作之磨料物品 |
TWI471196B (zh) | 2011-03-31 | 2015-02-01 | Saint Gobain Abrasives Inc | 用於高速磨削操作之磨料物品 |
WO2013049239A1 (en) | 2011-09-26 | 2013-04-04 | Saint-Gobain Ceramics & Plastics, Inc. | Abrasive articles including abrasive particulate materials, coated abrasives using the abrasive particulate materials and methods of forming |
CN106062122B (zh) | 2014-02-27 | 2018-12-07 | 3M创新有限公司 | 磨料颗粒、磨料制品及其制备和使用方法 |
TW201821580A (zh) | 2014-12-30 | 2018-06-16 | 美商聖高拜磨料有限公司 | 磨料製品及其成形方法 |
KR101953091B1 (ko) | 2014-12-30 | 2019-03-04 | 생-고뱅 어브레이시브즈, 인코포레이티드 | 연마 물품 및 이의 형성 방법 |
WO2016141575A1 (en) * | 2015-03-11 | 2016-09-15 | Shengguo Wang | Manufacturing method for nano sized alpha alumina |
KR20180088753A (ko) * | 2015-12-30 | 2018-08-06 | 생-고뱅 세라믹스 앤드 플라스틱스, 인코포레이티드 | 연마 입자 및 이의 형성 방법 |
CN106007685A (zh) * | 2016-05-12 | 2016-10-12 | 青岛四砂泰益超硬研磨股份有限公司 | 一种含锆的具有亚微米晶粒结构的α-氧化铝基磨料及制备方法 |
CN107160296B (zh) * | 2017-06-16 | 2018-12-04 | 江西冠亿研磨股份有限公司 | 一种高强度低温烧结微晶玻璃结合剂及其制备方法 |
JP6725752B2 (ja) * | 2017-08-18 | 2020-07-22 | ユニプレス株式会社 | クラッチ板保持用筒状部品及びそのプレス成形方法 |
WO2019133866A1 (en) | 2017-12-28 | 2019-07-04 | Saint-Gobain Abrasives, Inc. | Bonded abrasive articles |
WO2019166920A1 (en) * | 2018-02-28 | 2019-09-06 | 3M Innovative Properties Company | Kit of parts and process for fast firing a porous zirconia article in combination with a surface treating agent containing a glass powder |
CN108942703A (zh) * | 2018-05-30 | 2018-12-07 | 安徽佑开科技有限公司 | 一种超薄金刚石砂轮生产方法 |
CN108857932A (zh) * | 2018-05-30 | 2018-11-23 | 安徽佑开科技有限公司 | 一种金刚石砂轮配方 |
WO2022140275A1 (en) * | 2020-12-21 | 2022-06-30 | Oerlikon Metco (Us) Inc. | Lightweight corrosion-resistant wear-resistant brake disc, and method of manufacturing |
Family Cites Families (16)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4623364A (en) * | 1984-03-23 | 1986-11-18 | Norton Company | Abrasive material and method for preparing the same |
CA1254238A (en) | 1985-04-30 | 1989-05-16 | Alvin P. Gerk | Process for durable sol-gel produced alumina-based ceramics, abrasive grain and abrasive products |
US5259147A (en) | 1986-02-15 | 1993-11-09 | Vereinigte Schmirgel-Und Maschinenfabriken Aktiengesellschaft | Granular abrasive material |
US4881951A (en) | 1987-05-27 | 1989-11-21 | Minnesota Mining And Manufacturing Co. | Abrasive grits formed of ceramic containing oxides of aluminum and rare earth metal, method of making and products made therewith |
US5009676A (en) | 1989-04-28 | 1991-04-23 | Norton Company | Sintered sol gel alumina abrasive filaments |
US5219806A (en) | 1990-07-16 | 1993-06-15 | Minnesota Mining And Manufacturing Company | Alpha phase seeding of transition alumina using chromium oxide-based nucleating agents |
US5139978A (en) | 1990-07-16 | 1992-08-18 | Minnesota Mining And Manufacturing Company | Impregnation method for transformation of transition alumina to a alpha alumina |
US5282875A (en) | 1992-03-18 | 1994-02-01 | Cincinnati Milacron Inc. | High density sol-gel alumina-based abrasive vitreous bonded grinding wheel |
KR960702420A (ko) * | 1992-09-25 | 1996-04-27 | 워렌 리처드 보비 | 알루미나 및 지르코니아를 함유하는 연마 입자(abrasive grain containing alumina and zirconia) |
BR9408462A (pt) * | 1993-12-28 | 1997-08-26 | Minnesota Mining & Mfg | Tipo nominal especificado de grão abrasivo e artigo abrasivo |
US5989301A (en) * | 1998-02-18 | 1999-11-23 | Saint-Gobain Industrial Ceramics, Inc. | Optical polishing formulation |
DE19945335A1 (de) | 1999-09-22 | 2001-04-05 | Treibacher Schleifmittel Gmbh | Al¶2¶O¶3¶/SiC-Nanokomposit-Schleifkörner, Verfahren zu ihrer Herstellung sowie ihre Verwendung |
US20040148868A1 (en) * | 2003-02-05 | 2004-08-05 | 3M Innovative Properties Company | Methods of making ceramics |
US20040148869A1 (en) * | 2003-02-05 | 2004-08-05 | 3M Innovative Properties Company | Ceramics and methods of making the same |
US6802878B1 (en) * | 2003-04-17 | 2004-10-12 | 3M Innovative Properties Company | Abrasive particles, abrasive articles, and methods of making and using the same |
CN1194932C (zh) * | 2003-07-25 | 2005-03-30 | 湖南泰鑫瓷业有限公司 | 高性能耐磨陶瓷材料 |
-
2007
- 2007-12-12 PT PT78655370T patent/PT2094443E/pt unknown
- 2007-12-12 KR KR1020097012931A patent/KR101132159B1/ko active IP Right Grant
- 2007-12-12 ES ES07865537.0T patent/ES2452324T3/es active Active
- 2007-12-12 WO PCT/US2007/087155 patent/WO2008079680A1/en active Application Filing
- 2007-12-12 UA UAA200906857A patent/UA92690C2/ru unknown
- 2007-12-12 US US11/954,735 patent/US8932378B2/en active Active
- 2007-12-12 MX MX2009006591A patent/MX2009006591A/es active IP Right Grant
- 2007-12-12 NZ NZ577441A patent/NZ577441A/en not_active IP Right Cessation
- 2007-12-12 CN CN2007800465401A patent/CN101594966B/zh active Active
- 2007-12-12 EP EP07865537.0A patent/EP2094443B1/en active Active
- 2007-12-12 CA CA2672139A patent/CA2672139C/en active Active
- 2007-12-12 RU RU2009125451/02A patent/RU2415006C1/ru active
- 2007-12-12 BR BRPI0720401-9A patent/BRPI0720401B1/pt active IP Right Grant
- 2007-12-12 SI SI200731434T patent/SI2094443T1/sl unknown
- 2007-12-12 PL PL07865537T patent/PL2094443T3/pl unknown
- 2007-12-12 AU AU2007337145A patent/AU2007337145B2/en active Active
- 2007-12-12 JP JP2009543073A patent/JP5231446B2/ja active Active
- 2007-12-19 TW TW096148770A patent/TWI351334B/zh active
-
2009
- 2009-06-17 IL IL199408A patent/IL199408A/en active IP Right Grant
- 2009-06-18 ZA ZA200904293A patent/ZA200904293B/xx unknown
- 2009-06-19 CO CO09064246A patent/CO6210695A2/es not_active Application Discontinuation
-
2010
- 2010-05-26 HK HK10105167.4A patent/HK1139102A1/xx unknown
-
2014
- 2014-01-31 US US14/170,081 patent/US9144887B2/en active Active
-
2015
- 2015-08-25 US US14/835,216 patent/US9669517B2/en active Active
- 2015-09-21 IL IL241777A patent/IL241777B/en active IP Right Grant
Also Published As
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CO6210695A2 (es) | Abrasivos unidos a alta temperatura de alfa alumina de tamaño submicrometrico | |
Schmücker et al. | Microstructure of sodium polysialate siloxo geopolymer | |
RU2014117287A (ru) | Композиции для покрытия неорганических литейных форм и стерженей, а также их применение и способ обмазки | |
Okada et al. | Water-retention properties of porous ceramics prepared from mixtures of allophane and vermiculite for materials to counteract heat island effects | |
JP2010503232A5 (es) | ||
NZ588716A (en) | Fixed abrasive articles utilizing coated abrasive particles | |
Du et al. | Thermal decomposition of grinding activated bayerite | |
JP2015038165A5 (es) | ||
CN103351716A (zh) | 一种环保型珠光油墨 | |
Kong et al. | Effect of transition metal oxides on mullite whisker formation from mechanochemically activated powders | |
WO2011012510A3 (fr) | Procédé d'oxydo-réduction en boucle utilisant comme masse oxydo-réductrice une composition à base d'oxyde supporté de cérium ou de cérium, de zirconium et/ou de terre rare | |
Liu | Properties and manufacturing method of silicon carbide ceramic new materials | |
TH74419B (th) | สารขัดถูที่ได้รับการยึดเหนี่ยวที่อุณหภูมิสูงของแอลฟาอะลูมินาระดับสับไมครอน | |
JP2010275453A (ja) | 中空粒子およびそれを含む接着剤組成物 | |
ES2909065T3 (es) | Método para recubrir una superficie de cerámica, vidrio o plástico con un revestimiento de diamante | |
CN106554196A (zh) | 一种高温陶瓷涂层 | |
RU2010107874A (ru) | Термостойкий полимерный нанокомпозит, обладающий яркой фотолюминисценцией | |
Wu et al. | In-situ modification-dispersion technique for nano-fillers in rubber matrix | |
CHEN et al. | «Í 200K¤¶© ½Ï¤ Ô¥ ÐÞÆ¥ 200K¤ Ф Ô | |
Masuda et al. | Effects of strain rate and mode ratio on mixed mode interlaminar fracture behavior of carbon fiber/epoxy composite laminates | |
Bingfeng | Properties and Manufacturing Method of Silicon Carbide Ceramic New Materials | |
Tsuchiya et al. | Rock Failure by Decompression Boiling of Geofluids | |
CZ23355U1 (cs) | Superfínišovací nástroj | |
BR0301848A (pt) | Sìntese do pigmento de óxido de ferro encapsulado em matriz de sìlica amorfa | |
ES2421622T3 (es) | Material sinterizado que comprende circonia estabilizada, alúmina y plaquetas de aluminato de tierras raras, método de fabricación y usos |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
FC | Application refused |