CN85102472B - 高温耐热铁基合金 - Google Patents
高温耐热铁基合金 Download PDFInfo
- Publication number
- CN85102472B CN85102472B CN 85102472 CN85102472A CN85102472B CN 85102472 B CN85102472 B CN 85102472B CN 85102472 CN85102472 CN 85102472 CN 85102472 A CN85102472 A CN 85102472A CN 85102472 B CN85102472 B CN 85102472B
- Authority
- CN
- China
- Prior art keywords
- resistance
- high temperature
- alloy
- heat resisting
- deformation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
高温耐热铁基合金是利用高铬、高碳、低镍含氮的配方，获得铸态下为奥氏体基体并含有部分碳化物的金相组织。本发明能在1000-1100℃高温下抗氧化、抗变形、抗混燃煤磨损，在铸态下具有良好的机加工性，可焊性，而且其熔铸工艺方便。本发明适用于要求高温下抗氧化、抗变形、抗混燃煤粉磨损的发电厂锅炉喷燃器火嘴，要求较高的热处理式加热炉炉底板和要求高温抗氧化、抗变形、抗碳的井式加热炉茂福罐等。
Description
本发明是关于一种高温耐热铁基合金，特别是关于一种铬系高温耐热铁基合金。
一般火力发电厂锅炉喷燃器火嘴，在锅炉运行时，工作温度一般在850-1100℃范围内，并且承受高速混燃煤粉的冲刷。因此，要求火嘴材料能够抗高温氧化、抗变形、抗混燃煤粉磨损，迄今锅炉厂生产的火力发电厂锅炉，均配备着RQTSi5.5材质的喷燃器火嘴和1Cr18Ni9Ti材质的喷燃器火嘴。苏联塔于洛戈“红色锅炉者”工厂制造的T II E-211/c系列锅炉，配备着Cr20Ni14Si2材质火嘴。然而RQTSi5.5材质火嘴一般寿命仅达2000-3000小时，达不到一个小修期，1Cr18Ni9Ti与Cr20Ni14Si2材质火嘴在有的锅炉上寿命可达8000小时，而装在某些锅炉上的某些部位其寿命仅达4000小时，就因严重变形、氧化、磨损而坏掉。在已有的ACl/ASTM规格，(及JIS规格中)：HC(SCH-2)、HD(SCH-11)、HF(SCH-17)、HF(SCH-12)、HH(SCH-13)、HI(SCH-18)、HK-30(SCH-21)、HK-40(SCH-22)、HI、HN、(SCH-19)、HP、HT-(SCH-15)、HT-30(SCH-16)、HU、HW、HX(HW与HX为镍基合金)等，虽然有良好的高温抗氧化性，但高温下抗混燃煤磨损性却不理想，含镍量低的高温强度不高，而高温强度高的则其含镍量均高，成本太高，部分马氏体耐热钢虽高温下抗氧化、抗磨损、但铸态难以加工，不具备可焊性。
本发明的任务是提供一种高温耐热铁基合金，能在1000-1100℃高温下抗氧化、抗变形、抗混燃煤磨损，在铸态下具有良好的机加工性，可焊性，而且其熔铸工艺简便。
本发明是利用高铬、高碳、低镍含氮的配方获得铸态下为奥氏体基体并含有部分碳化物的金相组织，其组成重量的百分比是：
Cr：24-30％；C：0.4-1.1％；Ni：3.5-7.5％；
Mn：2.5-4.5％；N：0.2-0.3、％；Si：0.3-1.5％。
P≤0.035％ S：≤0.03％
Cr/C＝23～50，出炉时外加0.3-0.5％包头1#稀土硅铁合金处理，其余为铁及杂质。
本发明最佳配比的重量百分比是：
Cr：25～27％；C：0.8～1.0％；Ni：3.5～4％；
Mn：2.5～3.5％；N：0.2～0.3％；
Si：0.8～1.5％
Cr/C：24～35，外加0.3～0.5％包头1#稀土硅铁合金处理。
本发明适用于要求高温下抗氧化、抗变形、抗混燃煤磨损的发电厂锅炉喷燃器火嘴、要求较高的热处理箱式加热炉炉底板和要求高温抗氧化、抗变形、抗渗碳的井式加热炉马费罐等。
实施例：1、用表1编号2成分试制。2只火力发电厂锅炉喷燃器火嘴。委托河南姚孟电厂进行实际运行实验，从1983年9月安装试用至今还仍在运行中，在一次小修检查时，其它所有火嘴全部烧坏，唯有2只实验火嘴完好元损。
2、用表1中编号3成分试制4只喷燃器火嘴，委托河北马头发电厂做运行实验，在同一安装部位原苏制Cr20Ni14Si2材质火嘴，仅运行约4000小时左右就因严重变形而坏掉，而新装4只试验火嘴现已运行20000小时，提高寿命5倍以上。
3、用表1中编号4成分试制RJX45-9箱式加热炉改造成的节能炉的异形炉底板，自1983年11月至今其试用寿命(在相同条件下)已达铬锰氮钢普通炉底板寿命的3倍，现仍完好无损(改造炉现已节约电8万度以上)。
表1
Claims (1)
1.一种高温耐热铁基合金，其特征在于它的组成为(重量％)：Cr：25～27％；C：0.8～1.0％；Ni：3.5～4％；Mn：2.5～3.5％；N：0.2～0.3％；Si：0.8～1.5％；
Cr/C＝24～50；出炉加包头1#稀上硅铁合金
0.3～0.5％，余为铁及杂质。