CN2154862Y - 一种三层膜结构的镀膜玻璃 - Google Patents

一种三层膜结构的镀膜玻璃 Download PDF

Info

Publication number
CN2154862Y
CN2154862Y CN 93228092 CN93228092U CN2154862Y CN 2154862 Y CN2154862 Y CN 2154862Y CN 93228092 CN93228092 CN 93228092 CN 93228092 U CN93228092 U CN 93228092U CN 2154862 Y CN2154862 Y CN 2154862Y
Authority
CN
China
Prior art keywords
coated
metal
oxide
glass
oxide film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 93228092
Other languages
English (en)
Inventor
信觉俗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Northeastern University China
Original Assignee
Northeastern University China
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Northeastern University China filed Critical Northeastern University China
Priority to CN 93228092 priority Critical patent/CN2154862Y/zh
Application granted granted Critical
Publication of CN2154862Y publication Critical patent/CN2154862Y/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本实用新型提供的一种三层膜结构的镀膜玻璃， 该镀膜玻璃是在一片透明玻璃或着色玻璃基片(1)上 镀有第一层金属氧化物膜(2)，在该金属氧化物膜(2) 上镀有一层金属氮氧化物膜(3)，在该金属氮氧化物 膜(3)上镀有第二层金属氧化物膜(4)。该镀膜玻璃 有较高的红外反射率和较高的可见光透射率，这种玻 璃可按建筑设计要求产生不同反射色，可广泛用于建 筑门窗、墙幕、车船及民宅，可节省空调降温费和取暖 费。

Description

本实用新型涉及一种平板玻璃制品，特别是涉及一种经磁控溅射镀膜处理的平板玻璃制品，即镀膜玻璃。
现代社会，新型豪华建筑林立，能源消耗已成一大问题。在供给建筑物内部的能量当中，从没有经过处理的普通玻璃窗辐射损失的能量占总能量的1／3，因此，市场上急需一种具有隔热作用的玻璃制品。而现有技术中，镀膜玻璃制品主要是热反射彩色镀膜玻璃，只具有装饰作用和遮阳作用，但隔热作用很差。镀膜隔热玻璃制品要求：对可见光有高透过率，对红外辐射有高反射率。生产隔热玻璃的现有技术一般提供一种多层膜系的透明制品，如美国专利4.462.884、日本公开特许公报昭61－188446，德国专利DE3413587，欧洲专利Ep185314，一般这种多层膜系包括夹在两层金属氧化物膜之间的一个具有高红外反射率的金属膜。该金属可以是Au、Ag、Cu。Au、Ag都属稀有贵金属，成本高。Cu虽不是贵金属，但其附着性不好，降低了制品的耐久性。此外，三层膜系比以往少镀一层膜系，从经济方面大大降低了成本，而且保温性能及色饱和度又能优于以前。
本实用新型的目的，在于提供一种对可见光有高透过率，对红外辐射有高反射率却不消耗Au、Ag等贵金属，又具有保温隔热、遮阳及装饰作用的三层膜系的镀膜玻璃。
本实用新型的目的可以通过下述措施实现。利用某些金属的氮氧化物对红外辐射与Au对红外辐射的光谱反射率相似的特点，来代替贵金属，利用金属氧化物对光的吸收和干涉特性这就是：在一片透明玻璃或着色玻璃基片的一个表面上，镀有第一层金属氧化物膜，在该金属氧化物膜上，再镀有金属氮氧化的膜，在该金属氮氧化物膜上，又镀有第二层金属氧化物膜；金属氧化物膜（2）、（4）是下列金属氧化物（包括其混合物和合金氧化物）之一：氧化锡、氧化锌、氧化钛、氧化铝、氧化铬、不锈钢氧化物。金属氮氧化物（包括混合物和合金氮氧化物）之一：氮氧化钛、氮氧化铬、不锈钢氮氧化物。
下面结合附图1具体说明：
1、为透明玻璃或着色玻璃；2、金属氧化物；3、金属的氮氧化物；4、金属氧化物。
上述各层中金属元素可以相同、部分相同，也可以不同。
本实用新型的镀膜方法主要是以磁控溅射镀膜方法，也可以是蒸发镀膜法。
本实用新型提供的一种三层膜系结构的镀膜玻璃对红外反射率及色饱和度有很大提高，与多层膜系的镀膜玻璃相比，可大大降低成本。不消耗贵金属，而且附着性强，又具有保温隔热性能，降低了空调的成本，对加热成本更关注的地区，有很重要的意义。
下面结合实施例具体说明：
实施例1：
三层膜系结构为
玻璃／氧化钛／氮氧化钛／氧化钛
阴极靶尺寸480×180mm2。
阴极靶材为金属钛。
该镀膜玻璃性能：
550nm透射率：21.5％
6000nm反射率：81.8％
反射色为黄褐色。
实施例2：
三层膜系结构为
玻璃／氧化铬／氮氧化钛／氧化铬
阴极靶尺寸480×180mm2。
阴极靶材为金属钛。
另一阴极靶尺寸450×250mm2。
阴极靶材为金属铬。
该镀膜玻璃性能：
550nm透射率：68.10％
6000nm反射率：72％
反射色为橙色。
实施例3：
三层膜系结构为
玻璃／不锈钢氧化物／氮氧化钛／不锈钢氧化物
阴极靶尺寸480×180mm2。
阴极靶材：金属钛、不锈钢各一个。
该镀膜玻璃性能：
550nm透射率：49.5％
6000nm反射率：75％
反射色为浅兰色。
实施例4：
三层膜系结构为
玻璃／氧化铬／氮氧化铬／氧化铬
阴极靶尺寸450×250mm2。
阴极靶材为金属铬。
该镀膜玻璃性能：
550nm透射率：47.6％
6000nm反射率：72.5％
反射色为黄色。
实施例5：
三层膜系结构为
玻璃／氧化钛／氮氧化铬／氧化钛
阴极靶尺寸480×180mm2。
阴极靶材为金属钛。
阴极靶尺寸450×250mm2。
阴极靶材金属铬。
该镀膜玻璃性能：
550nm透射率：30.8％
6000nm反射率：78％
反射色为宝石兰色。

Claims (4)

1、一种三层膜结构的镀膜玻璃，其特征在于：是在一片透明玻璃或着色玻璃基片(1)的一个表面上，镀有第一层金属氧化物膜(2)，在该金属氧化物膜(2)上，再镀有金属氮氧化物膜(3)，在该金属氮氧化物膜(3)上，又镀有第二层金属氧化物膜(4)。
2、按照权利要求1所述的三层膜结构的镀膜玻璃，其特征在于：金属氧化物膜（2）、（4）是下列金属氧化物（包括其混合物和合金氧化物）之一：氧化锡、氧化锌、氧化钛、氧化铝、氧化铬、不锈钢氧化物。
3、按照权利要求1所述的三层膜结构的镀膜玻璃，其特征在于：金属氮氧化物（包括混合物和合金氮氧化物）之一：氮氧化钛、氮氧化铬、不锈钢氮氧化物。
4、按照权利要求1所述的三层膜结构的镀膜玻璃，其特征在于：所述各镀层（2）－（4）中的各金属元素可以相同、或部分相同，也可以不同。
CN 93228092 1993-05-06 1993-05-06 一种三层膜结构的镀膜玻璃 Expired - Fee Related CN2154862Y (zh)