CN213925238U - Jacquard silk fabric made of acetate yarn and modified polyester yarn combination - Google Patents
Jacquard silk fabric made of acetate yarn and modified polyester yarn combination Download PDFInfo
- Publication number
- CN213925238U CN213925238U CN202021298777.8U CN202021298777U CN213925238U CN 213925238 U CN213925238 U CN 213925238U CN 202021298777 U CN202021298777 U CN 202021298777U CN 213925238 U CN213925238 U CN 213925238U
- Authority
- CN
- China
- Prior art keywords
- yarns
- jacquard
- silk
- modified polyester
- acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a jacquard silk satin surface fabric by acetate silk and modified polyester silk combination preparation, jacquard silk satin surface fabric includes warp and woof, the warp adopts the acetate silk, the woof adopts diacetate silk and modified polyester silk combination, the total share content that the acetic acid of jacquard silk satin surface fabric accounted for in the fabric is more than 70%. The utility model discloses a acetate silk and polyester yarn are the raw materials, adopt the close satin ground jacquard weave of high warp, embody the distinctive soft gloss of acetate surface fabric well, and splendid feeling and drapability adopt its third dimension of the jacquard weave on the satin ground of the small exquisite jacquard weave messenger of full ground stronger, and the cloth cover decorative pattern more shows high fender, elegant, high-grade. The fabric has the advantages of elegant, bright and beautiful appearance, pearly luster, excellent drapability, coolness, air permeability, gorgeous color and soft hand feeling due to the unique process and pattern design, adds high-grade new patterns to high-grade fashion fabrics, and is popular in the market once being launched.
Description
Technical Field
The utility model relates to a textile fabric field and weaving technology field, especially a jacquard weave silk satin surface fabric of making by acetate silk and modified polyester silk combination.
Background
Among textile raw materials, acetate yarn is used as a green and environment-friendly filament yarn and is derived from sustainable forest wood. Converts the natural rich gift into a comfortable and easy-to-wear luxury fabric that gives people excellent qualities of comfort, skin-friendliness, brilliant luxury, soft drape, and ease of care. The modified polyester yarn has better dyeing property. The combination of the acetate yarn and the modified polyester yarn enables physical indexes of the fabric such as strength, dyeing property, elasticity and the like to be more excellent, and the taking effect is better. Because the appearance, hand feeling and luster of the acetic acid fabric and the silk fabric are extremely similar, the price of the silk raw material is several times higher, and the clothes made of the silk fabric are difficult to handle.
SUMMERY OF THE UTILITY MODEL
The utility model aims to provide a jacquard fashion fabric which adopts diacetate yarn and modified terylene as raw material combination to produce on jacquard weaving aiming at the defects that silk fabric is expensive and the fabric is difficult to be arranged.
In order to achieve the above purpose, the utility model adopts the following technical scheme:
the jacquard satin fabric made of the combination of the acetate yarns and the modified polyester yarns comprises warp yarns and weft yarns, wherein the warp yarns adopt diacetate yarns, the denier number of the warp yarns is between 75D and 150D, the twist number is between 400 plus materials and 600 per meter, the weft yarns adopt the combination of the diacetate yarns and the modified polyester yarns, the denier number after the combination is between 120D and 300D, the total content of acetic acid of the jacquard satin fabric in the fabric is more than 70 percent, the jacquard satin fabric is woven by a high warp density process, the density of the warp yarns is 100 plus materials and 115 plus materials per centimeter, the weave of the jacquard satin fabric is a small jacquard weave taking the weave as the ground weave, and the satin ground weave accounts for more than 50 percent of the surface of the fabric.
Furthermore, the denier of the diacetate yarns and the modified polyester yarns of the weft yarns is between 55D and 150D, and the twist of the diacetate yarns and the modified polyester yarns of the weft yarns is between 800 and 1200 yarns/m.
Furthermore, the weft yarn is formed by twisting diacetate yarn and modified polyester yarn respectively, then combining and twisting, and the total twist is between 2000 and 3000 yarns/m.
Further, the weft yarns are arranged in two groups of different twisting directions, the two groups of different twisting directions are an S twisting direction (A) and a Z twisting direction (B), and the S twisting direction and the Z twisting direction are arranged in an AABB combined circulation mode.
Furthermore, the gram weight of the finished product of the jacquard silk fabric per square meter is 150-230 g/m2In the meantime.
Further, the width of the finished product of the jacquard silk fabric is 135-155 CM.
Further, the weaving process of the jacquard silk fabric comprises the following steps:
a. warp yarn: spooling, twisting, warp lifting, warp sizing and shaft combining;
b. weft yarn: spooling, twisting, doubling and twisting;
c. the method comprises the steps of loading, probing, weaving, blank cloth inspection, after finishing, finished product inspection, packaging and warehousing.
Further, the spooling in the process is as follows: winding the raw silk into a silk winding drum on a silk winder, wherein the winding speed is 250-350min, and the tension is 5-7 CN.
Further, in the process, twisting: twisting the silk tube after silk winding in a twisting machine with the twist of 400T/m and the twisting direction: s direction, the twisting speed is 4700-.
Further, the warp lifting in the process is as follows: the twisted and poured bobbin is lifted on a piece-by-piece warp lifting machine at the speed of 150-; the coiling tension is 6-8 CN/piece, the pressure standard of the pressure roller is 1/2 × 0.1MPa, 1/4 × 0.1MPa, and the coiling hardness is 70-75.
Further, the process comprises the following steps: uniformly sizing the warp yarn after warp lifting by a sizing machine and winding the warp yarn into a sizing shaft, wherein the sizing speed is 90-100 m/min; the pressure of the slurry soaking roller is 1 plus or minus 0.1 and 0.1 Mpa; the pressure of the side pressure roller is 1.5 +/-0.1X 0.1 MPa; sending out 10-16g of tension; the coiling tension is 14-18 g; elongation of 0.25-0.9%; the slurry temperature is 35-45 ℃, and the slurry is a paste.
Further, the merging axis in the process is as follows: combining and winding the sized pulp shafts on a shaft combining machine to form a warp beam, wherein the shaft combining speed is 40-60m/min, and the winding tension is 240-250 kg; sending out tension of 11-14 CN/root; the coiling hardness is 70-80.
Further, the doubling in the process is as follows: the two different raw materials are combined into a doubling cylinder on a doubling machine, the speed of doubling is 250-350min, and the tension is 10-18 CN.
Further, the weaving in the process comprises: weaving the beam on a high-speed jacquard loom, wherein the weaving process has the following technological parameters: the speed of the vehicle is 380 r/min-480 r/min, the opening height is about 22, the height position of a back beam is about 0.5, the machine tension is about 20, the reed number is 26-28 teeth/cm, and 4 yarns/tooth are arranged; weave big jacquard weave, side weave drafting 1, 2, side weave reeding 4, side weave 2/2 warp rebinning.
The utility model has the advantages that: the utility model discloses a acetate silk and polyester yarn are the raw materials, and the assembly portion content that acetic acid accounted for in the fabric is more than 70%, adopts the satin ground jacquard weave of high warp density, and satin ground jacquard weave accounts for more than 50% on the fabric surface, embodies the peculiar soft gloss of acetate surface fabric well, and splendid feeling and drapability adopt its third dimension of the jacquard weave of full exquisite little jacquard weave messenger satin on the ground stronger, and the cloth cover decorative pattern more shows high fender, graceful, high-grade. The fabric has the advantages of elegant, bright and beautiful appearance, pearly luster, excellent drapability, coolness, air permeability, gorgeous color and soft hand feeling due to the unique process and pattern design, adds high-grade new patterns to high-grade fashion fabrics, and is popular in the market once being launched.
Drawings
Fig. 1 is a schematic structural diagram of the present invention.
Fig. 2 is a weave diagram of a ground weave of a jacquard silk fabric and satin fabric in an embodiment of the present invention.
Reference numerals: warp yarn 1, weft yarn 2.
Detailed Description
For further understanding and appreciation of the structure, features, and advantages of the invention, reference should now be made to a preferred embodiment thereof, in conjunction with which the invention will be further described:
as shown in figure 1, the jacquard satin fabric made of the combination of the acetate yarns and the modified polyester yarns comprises warp yarns 1 and weft yarns 2, wherein the warp yarns 1 adopt diacetate yarns, the denier of the warp yarns 1 is between 75D and 150D, the twist degree is between 400-, the density of the warp 1 is 100-115 pieces/cm, the weave of the jacquard silk fabric is a small jacquard weave taking a satin weave as a ground weave, and the satin weave accounts for more than 50% of the fabric surface.
The gram weight of the jacquard silk fabric per square meter is 145-150 g/m2Meanwhile, the width of the elastic double-sided forged strip fashion fabric is 153-155 CM.
The weft yarns 2 are arranged in two groups of different twisting directions, the two groups of different twisting directions are respectively an S twisting direction (A) and a Z twisting direction (B), and the S twisting direction and the Z twisting direction are arranged in an AABB combined circulation manner.
The implementation case of the process is as follows:
as shown in fig. 1 and fig. 2, the stretch double-faced welt fabric produced by weaving the combination of acetate yarn and novel high stretch yarn has the following specific specifications: the warp is 75D acetic acid 4T/CM; the weft yarn is (75D acetate 12T/CM +75D high stretch yarn 12T/CM) 10T/CM; density: 110 by 36/CM, the production process flow is as follows:
a. processing the vinegar raw material barrel into a silk winding barrel meeting certain requirements on a silk winding machine, wherein the winding speed is 250-350min, and the tension is 5-7 CN.
b. Twisting the twine silk tube on a twisting machine, wherein the twist number is 4T/cm, and the twisting direction is as follows: s direction, the twisting speed is 4700-.
c. Carrying out warp lifting on the twisted and poured bobbin on a piece-by-piece warp lifting machine, wherein 1300 warp lifting swing drums are used, the width of a lifting shaft is 170cm, and the speed is 150-; the coiling tension is 6-8 CN/piece, the pressure standard of the pressure roller is 1/2 × 0.1MPa, 1/4 × 0.1MPa, and the coiling hardness is 70-75.
d. Sizing the warp yarns by a lifting shaft through a sizing machine, wherein the speed of the sized warp yarns is 90-100 m/min; the pressure of the slurry soaking roller is 1 plus or minus 0.1 and 0.1 Mpa; the pressure of the side pressure roller is 1.5 +/-0.1X 0.1 MPa; sending out 10-16g of tension; the coiling tension is 14-18 g; elongation of 0.25-0.9%; the slurry temperature is 35-45 ℃, the slurry is a paste material, and the sizing rate is 5-8%;
e. combining and winding the sized pulp shafts on a shaft combining machine according to requirements to form a weaving shaft, wherein the shaft combining speed is 40-60m/min, and the shaft combining amplitude is 160-190 cm; the coiling tension is 240-250 kg; sending out tension of 11-14 CN/root; the coiling hardness is 70-80.
f. The loom beam after sizing is arranged on a machine, healed according to the process requirement and reeded
g. Weft yarn: respectively winding the raw materials of the 75D acetic acid and the 75D high stretch yarn on a winder at the winding speed of 250-350min and the tension of 5-7 CN. Twisting the winding bobbin on a twisting machine to form a twisting bobbin, wherein the twist number is 12T/cm, and the twisting direction is as follows: the S direction and the Z direction have the twisting speed of 4500-.
h. And combining the twisted cylinders of the 75D acetic acid and the 75D high-elastic yarns into a combined cylinder on a doubling machine, wherein the speed of the combined cylinder is 250-350min, and the tension is 10-18 CN.
i. The combined tube of 75D acetic acid and 75D high elastic yarn is twisted on a twisting machine. The twist is 10T/CM, the twist direction is S direction and Z direction, the ratio of S direction to Z direction is 1: 1, the twisting speed is 5000-.
j. The weaving beam is arranged on a machine, assembled according to the process and then passes through a warp, a reed and a loom, the variety can be woven on a high-speed rapier loom, and the weaving process has the following process parameters: the vehicle speed is 350 r/min-400 r/min; the height of the opening is about 20, the height position of the back beam is about 0.5, and the upper machine tension is about 20; weft yarn arrangement: 1 in S direction and Z direction: 1 weaving in; weft density is 36 pieces/CM; grey fabric width 165 CM.
k. The grey cloth weaved into coils is processed into finished products by adopting an after-finishing procedure after inspection, and the process flow is as follows: the dyeing pretreatment, dyeing, cleaning, reduction and cleaning, softening, padding, drying and shaping, and the specific process comprises the following steps: (1) dyeing pretreatment: pre-washing, desizing, refining and washing the grey cloth by equipment; (2) dyeing: placing the pre-treated clean fabric in a high-temperature high-pressure dye vat, dyeing by adopting a dispersion medium-temperature one-bath method, adjusting the pH value to 6-9, adding a dispersing agent, heating the solution to 70 ℃ with the concentration of 1-1.5 g/L, adding a dispersion dye, heating to 105-110 ℃ at the heating rate of 1 ℃/min for dyeing, keeping the temperature for 50 minutes, and discharging the liquor; (3) cleaning, reducing and cleaning: adding a reducing cleaning agent F into the aqueous solution, wherein the concentration is 1g/L, the pH value is 6.5-7.5, treating at 85 ℃ for 20 minutes, and taking out of the tank; (4) softening, padding, drying and shaping: the concentration of the nonionic softener PD is 20g/L, the pH value is 6.5-8, the setting speed is 30m/min, and the setting temperature is 190-210 ℃: the temperature is 100 ℃, and the vehicle speed is 10-20 m/s.
l, finished product inspection: and (5) inspecting the finished product according to the finished product inspection standard and inspection specification.
m, packaging and warehousing: and packaging and warehousing the finished products after the inspection.
The preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings, which are for purposes of illustration and description, and are not intended to limit the scope of the invention. Any modification, equivalent replacement, improvement and the like made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (6)
1. The jacquard satin fabric made of the combination of the acetate yarns and the modified polyester yarns comprises warp yarns (1) and weft yarns (2), and is characterized in that the warp yarns (1) adopt diacetate yarns, the denier of the warp yarns is between 75D and 150D, the twist is between 400 and 600 yarns/m, the weft yarns (2) adopt the combination of the diacetate yarns and the modified polyester yarns, the denier after the combination is between 120D and 300D, the jacquard satin fabric is woven by adopting a high warp density process, the density of the warp yarns (1) is 100 and 115 yarns/cm, the weave of the jacquard satin fabric is small with satin as ground weave, and the satin ground weave accounts for more than 50% of the surface of the fabric.
2. The jacquard silk fabric made of the acetate yarns and the modified polyester yarns in combination as claimed in claim 1, wherein the denier numbers of the diacetate yarns and the modified polyester yarns of the weft yarns (2) are within 55D-150D, and the twist numbers of the diacetate yarns and the modified polyester yarns of the weft yarns (2) are within 800-.
3. The jacquard silk fabric made of the combination of acetate yarns and modified polyester yarns as claimed in claim 1, wherein the weft yarns (2) are formed by twisting, combining and twisting diacetate yarns and modified polyester yarns respectively, and the total twist is between 2000 and 3000 yarns/m.
4. The jacquard silk fabric made of acetate silk and modified polyester silk in combination according to claim 1, wherein the weft yarns (2) are arranged in two groups of different twisting directions, the two groups of different twisting directions are respectively an S twisting direction and a Z twisting direction, and the S twisting direction and the Z twisting direction are circularly arranged in an AABB combination manner.
5. The jacquard silk fabric made of the combination of the acetate yarns and the modified polyester yarns according to claim 1, wherein the finished product of the jacquard silk fabric with the gram weight per square meter is 150-230 g/m2In the meantime.
6. The jacquard silk fabric made of the combination of the acetate yarns and the modified polyester yarns according to claim 1, wherein the finished product of the jacquard silk fabric has a width of 135CM to 155 CM.