CN212201114U - Wood floor with magnetic surface layer - Google Patents
Wood floor with magnetic surface layer Download PDFInfo
- Publication number
- CN212201114U CN212201114U CN201922205986.7U CN201922205986U CN212201114U CN 212201114 U CN212201114 U CN 212201114U CN 201922205986 U CN201922205986 U CN 201922205986U CN 212201114 U CN212201114 U CN 212201114U
- Authority
- CN
- China
- Prior art keywords
- layer
- magnetic
- magnetic adsorption
- coated
- adsorption layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a wood floor with magnetic surface layer, which comprises a base material layer, a magnetic adsorption layer and a finish paint layer; the surface of the base material layer is coated with a magnetic adsorption layer, and the surface of the magnetic adsorption layer is coated with a finish paint layer; make timber apron have magnetism through coating magnetic adsorption layer, when making decoration parts such as wall, can adsorb any light-duty magnetic object, perhaps paste the magnetic paste on some string decorations, can hang the decorations on the wallboard, the change of parts such as the decorations of being convenient for hanging need not to adopt technologies such as double faced adhesive tape and nailing simultaneously, avoids leaving nail hole or glue mark on the timber apron surface, guarantees the pleasing to the eye and the intact line of timber apron.
Description
Technical Field
The utility model relates to a floor technical field especially relates to a top layer has magnetic timber apron.
Background
In recent years, wood floors are more and more common as background walls, the unique wood texture of the wood floors is simple and real without losing the style, and the wood floors can bring more visual impact to people compared with tiles, wallpaper, paint and the like.
Most homes and businesses now often place some photos, pictures, or notes on the background wall of the house for decoration. The display modes are as follows: wall nailing, frame hook or sticky tape or glue let the wall fixed with drawing (looks) frame bonding, and this kind of mode can destroy the wall, leaves nail hole or glue trace on the wall and remains, and shift position need nailing or viscose again when again, changes the picture difficult or unable change.
SUMMERY OF THE UTILITY MODEL
An object of the utility model is to provide a top layer has magnetism, is convenient for adsorb light-duty magnetic object's timber apron.
In order to achieve the above purpose, the utility model provides a wood floor with magnetic surface layer, which comprises a base material layer, a magnetic adsorption layer and a finish paint layer; the magnetic adsorption layer is coated on the surface of the base material layer, and the finish paint layer is coated on the surface of the magnetic adsorption layer.
Preferably, the substrate layer is a solid wood floor blank or a solid wood composite floor blank.
Preferably, at least 4 magnetic adsorption layers are coated on the surface of the base material layer, and the coating amount of each magnetic adsorption layer is 15-30g/m2。
Preferably, the magnetic adsorption layer comprises a primer layer and magnetic iron powder, and the magnetic iron powder is mixed in the primer layer.
Preferably, the magnetic iron powder is nano ferroferric oxide particles; the particle size of the nano ferroferric oxide particles is less than or equal to 50 nm.
Preferably, the weight of the magnetic iron powder accounts for 40-60% of the total weight of the magnetic adsorption layer.
Preferably, the primer layer is a UV primer layer.
Compared with the prior art, the utility model has the advantages that: the utility model provides a top layer has magnetic timber apron, make the timber apron have magnetism through coating magnetic adsorption layer, when making decoration parts such as wall, can adsorb any light-duty magnetic object, perhaps paste the magnetic paste on some string decorations, can hang the decorations on the wallboard, be convenient for hang the change of parts such as decorations, need not to adopt technologies such as double faced adhesive tape and nailing simultaneously, avoid leaving the nail hole or glue the trace on the timber apron surface, guarantee pleasing to the eye and the intact line of timber apron.
The utility model discloses used UV priming paint layer hardness is big, and the wearability is good, and the transparency is high to UV lacquer can not volatilize any material, green.
The magnetic adsorption layer of the utility model adopts nano-scale ferroferric oxide particles as magnetic iron powder, has high hardness, and effectively improves the hardness of the floor paint film after being mixed with the UV primer layer; and the ferroferric oxide is used as a black crystal, and the magnetic adsorption layer can show excellent decorative effect after being coated on the surface of the finish coat layer, so that a separate device using paint such as color concentrate or color paste is not needed, and the method is economical and environment-friendly.
Drawings
Fig. 1 is a schematic structural view of a wood floor with magnetic surface layer in an embodiment of the present invention.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention clearer, the technical solutions of the present invention will be further described below.
As shown in fig. 1, the present invention provides a wood floor with magnetic surface layer, which comprises a substrate layer 1, a magnetic adsorption layer 2 and a finish paint layer 3; the surface of the substrate layer 1 is coated with a magnetic adsorption layer 2, and the surface of the magnetic adsorption layer 2 is coated with a finish paint layer 3.
In the present embodiment, the substrate layer 1 is a solid wood floor blank or a solid wood composite floor blank.
In this embodiment, at least 4 magnetic absorption layers 2 are coated on the surface of the substrate layer 1, and the coating amount of each magnetic absorption layer 2 is 15-30g/m2The purpose is to ensure the magnetic effect of the magnetic adsorption layer 2.
In the present embodiment, the magnetic adsorption layer 2 includes a primer layer and magnetic iron powder, and the magnetic iron powder is mixed in the primer layer.
In the present embodiment, in order to ensure the environmental protection effect, the top paint layer 3 is a UV top paint layer.
In the embodiment, the magnetic iron powder is nano ferroferric oxide particles; the grain size of the nano ferroferric oxide particles is less than or equal to 50 nm; the nano ferroferric oxide particles are used as magnetic iron powder, so that the hardness is high, and after the nano ferroferric oxide particles are mixed with the UV primer layer for use, the hardness of a floor paint film is effectively improved; and the ferroferric oxide is used as a black crystal, the magnetic adsorption layer 2 can show an excellent decorative effect after being coated on the surface of the finish paint layer 3, and a device using paint such as color concentrate or color paste is not needed, so that the paint is economic and environment-friendly.
In this embodiment, the weight of the magnetic iron powder is 40-60% of the total weight of the magnetic adsorption layer 2, so as to ensure the magnetic effect and the hardness of the paint film of the soleplate.
In the embodiment, the primer layer is the UV primer layer, the UV primer layer has high hardness, good wear resistance and high transparency, and the UV paint does not volatilize any substance and is green and environment-friendly.
The wood flooring of the present invention will be further explained by the method for manufacturing the wood flooring having magnetic surface layer:
step 1: preparing a substrate layer 1; the substrate layer 1 is a solid wood floor blank or a solid wood composite floor blank, and after the blank is subjected to fixed-thickness sanding by using a sanding machine, a mortise is milled at the periphery of the floor blank by using slotting equipment; according to the decoration design demand, the optional archaize processing of carrying out blank surface.
Step 1.1: the oak bark with the thickness of 1.2mm is pressed and pasted on 7 layers of structural plywood with the thickness of 14mm by using the environment-friendly adhesive, and wood fibers between adjacent layers of 7 layers of wood veneers of the plywood are criss-cross and have symmetrical structures.
Step 1.2: and (3) after curing for 3 days, cutting the plate blank into small pieces with the same width, sanding the small pieces of the blank in a fixed thickness by using a Holland sand sander to enable the thickness of the blank to be within the range of 15 +/-0.1 mm, and slotting the periphery of the blank by using Jintian Haemai slotting equipment to finally obtain the specification of 1200 x 150 x 15 mm.
Step 2: preparing a magnetic adsorption layer 2;
ferroferric oxide (Fe) with the diameter less than or equal to 50nm3O4) Magnetic particles are added to the UV primer layer in a weight ratio of 1:1Stirring uniformly to obtain the magnetic primer layer.
And step 3: coating the magnetic adsorption layer 2 on the surface of the base material layer 1;
roller coating equipment is used for roller coating four magnetic adsorption layers 2 on the surface of the floor substrate layer 1: after each roller is coated with one magnetic adsorption layer 2, the roller is dried by a UV lamp (the drying degree is semi-dry) and then coated with the next magnetic adsorption layer 2, and the coating weight of each magnetic adsorption layer 2 is 25g/m2。
And 4, step 4: coating a finish paint layer 3 on the surface of the magnetic adsorption layer 2;
after roller coating with 1-2 UV finishes, drying with UV lamp with energy more than 400mj/cm2The coating weight of the finish paint is 10 g/square meter.
And 5: and (5) inspecting a finished product.
Wherein, in the utility model discloses in, UV lacquer: the english abbreviation of ultravioletcurringpaint, namely ultraviolet light curing paint, is also called photo-initiation coating and photo-curing coating. The paint is automatically coated on the surface of a furniture board by roller coating and curtain coating through machine equipment, an initiator is promoted to decompose under the irradiation of ultraviolet light to generate free radicals, resin reaction is initiated, and the paint is instantly cured to form a film.
The above description is only for the preferred embodiment of the present invention, and does not limit the present invention. Any technical personnel who belongs to the technical field, in the scope that does not deviate from the technical scheme of the utility model, to the technical scheme and the technical content that the utility model discloses expose do the change such as the equivalent replacement of any form or modification, all belong to the content that does not break away from the technical scheme of the utility model, still belong to within the scope of protection of the utility model.
Claims (6)
1. A wood floor with magnetic surface layer is characterized by comprising a base material layer, a magnetic adsorption layer and a finish paint layer; the magnetic adsorption layer is coated on the surface of the base material layer, and the finish paint layer is coated on the surface of the magnetic adsorption layer.
2. The magnetic surface layer wood flooring according to claim 1, wherein the substrate layer is a solid wood flooring material or a solid wood composite flooring material.
3. The wood flooring having a magnetic surface layer according to claim 1, wherein the surface of the base material layer is coated with at least 4 magnetic adsorption layers, each of the magnetic adsorption layers being coated in an amount of 15 to 30g/m2。
4. The wood flooring having a magnetic surface layer according to claim 1, wherein the magnetic adsorption layer includes a primer layer and a magnetic iron powder embedded in the primer layer.
5. The wood flooring with a magnetic surface layer according to claim 4, wherein the magnetic iron powder is nano-sized ferroferric oxide particles; the particle size of the nano ferroferric oxide particles is less than or equal to 50 nm.
6. The wood flooring with magnetic surface layer according to claim 4, wherein the primer layer is a UV primer layer.