CN206553811U - A kind of noctilucent coating cloth - Google Patents
A kind of noctilucent coating cloth Download PDFInfo
- Publication number
- CN206553811U CN206553811U CN201720008761.0U CN201720008761U CN206553811U CN 206553811 U CN206553811 U CN 206553811U CN 201720008761 U CN201720008761 U CN 201720008761U CN 206553811 U CN206553811 U CN 206553811U
- Authority
- CN
- China
- Prior art keywords
- coating
- noctilucent
- cloth
- noctilucent coating
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model is related to a kind of noctilucent coating cloth, noctilucent coating including base material and with luminous effect, wherein base material is fabric, and substrate upper surface is coated with interface by air brushing mode and connects coating, and noctilucent coating is coated on interface by air brushing mode and connects coating surface.This noctilucent coating cloth simple production process of the utility model, fluorescent lifetime is long, and luminescent powder firmly can be attached on painting canvas, without dropping easily.In addition, such a material can also waterproof, sun-proof, be particularly suitable for the printing of outdoor advertising.
Description
Technical field
The utility model is related to a kind of coating cloth, particularly a kind of noctilucent coating cloth.
Background technology
Coating cloth, such as canvas using extremely wide, are usually used in printed decoration picture or advertisement etc. in daily life.Prior art
In, what picture, advertisement, other printing supplies were typically only capable to could to see under bright and clear environment arrives, in the ground root of dark
This appreciation not, can only turn on light, and so both waste electric power energy, and can only can appreciate single image.Therefore one kind is needed
Medium, as long as we are in medium printed thereon or air brushing or transfer etc., other production methods adhere to a kind of image, and this image exists
The effect of another different pictures displaying can be enjoyed any time.And the instruction of some light can be given people in the dark,
Process when light is dimmed suddenly to one adaptation of eyes, reduces the generation of contingency, had not only saved the energy but also can increase
Aesthetic feeling and security.Therefore, the picture with noctilucent function, printed matter just arise at the historic moment.Generally, it is this with noctilucent function
Draw, printed matter is that producer is bought after common painting canvas, will draw, pattern is first printed, then one layer of luminescent powder of air brushing reaches noctilucence
Effect.Luminous picture is typically used to the occasions such as outdoor advertising or bar.This air brushing can only spray after the completion of picture, pattern printing
On, the stability of noctilucence is not strong, and processing technology is complex, wasting manpower and material resources' financial resources.
There is the Chinese patent of Application No. 200710024318.3 in addition, disclose a kind of backing-adhesive luminous picture paper, wrap
The coating of base material and coating in its surface is included, base material has RC paper substrates and PET book films to be composited, be blotting on base material front
It is photosensitive layer above coating, ink-absorbed coated layer, ink absorbing layer and photosensitive layer are solid comprising polyvinyl alcohol, polyvinylpyrrolidone, cation
Toner, luminescent powder etc., by the combination of ink absorbing layer and noctilucent coating to reach imaging luminous effect.This coating is in RC printing paper
On the basis of be coated with light sensitive layer, the conjugation of light sensitive layer and ink absorbing layer is difficult to grasp, and the function of ink absorbing layer is quick inhales
Ink can also reduce ratio defective product with influence imaging effect that can be serious after high-resolution imaging, but photosensitive coated layer,
Improve cost.
In addition, the Chinese patent of Application No. 201220472638.1, discloses a kind of two-sided digital ink-jet cloth, it is wrapped
Base fabric is included, base fabric upper surface is combined successively sets surface layer PVC film and noctilucence surface layer, and base fabric lower surface is combined successively sets PVC to hide
Light film, bottom PVC film and noctilucence bottom.Its process composite PVC photomask PVC underlying membranes and noctilucence face successively in base fabric
Layer is to reach luminous effect.This technique is the compound of pure layer upon layer, and base material is that have coating to be formed, finished product be by
Layer upon layer it is compound, waste too many time and the heating energy, the iron of current high production and low cost do not met so
Rule, and noctilucence layer can reduce the aesthetic effect of imaging each side.
Utility model content
The purpose of this utility model is to provide a kind of noctilucent coating cloth, including base material and the noctilucence with luminous effect are applied
Layer, the base material is fabric, and substrate upper surface is coated with interface by coating method and connects coating, and noctilucent coating passes through coating side
Formula is coated on interface connection coating surface.
Further, the base material material is cotton or burlap or woven dacron or non-woven fabrics or polyester-cotton blend fiber crops mixing cloth.
Further, the noctilucent coating upper surface is also coated with protective layer.
Further, luminescent powder particle diameter is 200 ~ 800 mesh in the noctilucent coating.
Further, the luminescent powder particle diameter is 300 mesh.
Further, the coating weight of the interface connection coating is 120 ~ 800 grams/m.
Further, the coating weight of the noctilucent coating is 100 ~ 180 grams/m.
The preparation method of this noctilucent coating cloth, comprises the following steps：
（1）Base material pre-treatment step, preliminary treatment is carried out to base material, is flattened；
（2）Interface connects coating blend step：By deionized water, dispersant, defoamer, titanium dioxide, PVA emulsions, propylene
Yogurt liquid, thickener are mixed evenly, filtering；
（3）Noctilucent coating blend step：Acrylic emulsion, luminescent powder, dispersant, defoamer are mixed, disperse 10 ~ 30 points
Clock, is mixed evenly；
（4）Application step：First will（2）In interface connection coating be coated in substrate surface, treat interface connection coating do
, will after dry（3）In noctilucent coating be coated on interface connect coating surface, dry, finally by protective layer be coated on noctilucence apply
The surface of layer.
The beneficial effect of this noctilucent coating cloth of the utility model and preparation method thereof is：
1st, interface is connected into coating and luminescent coating is applied directly on common fabric, as long as advertiser or printing factory
Such a luminous cloth of direct bulk purchase, in spray printed pattern-making above, technique is simply, conveniently.Without as present city
On face, these businessmans buy common painting canvas, carry out pattern production process, then individually carry out noctilucence coating.
2nd, the technical solution adopted in the utility model, can solve the problem that colour vividness not enough, luminosity also not strong defect
Problem, its extinction-storage light-luminescence process Infinite Cyclic, is forever used, the image of making is life-like, gorgeous true to nature, product
Use value is also greatly improved；And the simple production process of this coating cloth, the common coating machine of tradition can just be produced excellent
Good product.
3rd, it is luminous more steady using in this noctilucent coating cloth, can not only cause made pattern more exquisite but also can cause
Fixed, effect more preferably, is difficult affected by environment.
4th, matcoveredn is coated using on noctilucent coating surface, further protects noctilucent coating so that be luminous more stable, effect
Fruit more preferably, is less susceptible to ambient influnence.
5th, through many experiments, using optimal noctilucent coating component proportion, the degree of containing of luminescent powder, compatible performance are enhanced,
It is attached to so that luminescent powder is stronger on painting canvas, without dropping easily.In addition, such a material can also waterproof, sun-proof, spy
It is not suitable for photo making, heat transfer image, the making of indoor and outdoor advertisement description air brushing.
6th, using the luminescent powder particle diameter of 300 mesh, dispersive property and illumination effect are optimal.Too thick point of the fineness of luminescent powder
Dissipate property poor, too thin savings light is few, through lot of experiments, draws the optimized particle size, taken into account dispersive property, illumination effect, lighted
Time.The painting canvas is after the savings luminous energy by 30 minutes or so, and light source can be any light source such as natural light or illumination light,
Just can in noctilucence 8-10 more than hour, noctilucent coating can Reusability up to more than 15 years.
7th, through many experiments, optimal interface connection coating proportioning is selected, compatibility of the painting canvas to ink is improved, and have
There is high glaze.
Brief description of the drawings
Fig. 1 is a kind of noctilucent coating cloth structural representation of the utility model；
Fig. 2 is a kind of preparation method flow chart of noctilucent coating cloth of the utility model；
Drawing reference numeral explanation：1st, base material；2nd, interface connection coating；3rd, noctilucent coating；4th, protective layer.
Embodiment
The utility model is described in further detail below in conjunction with the accompanying drawings.
Embodiment one
Referring to the drawings 1 ~ 2, the noctilucent coating cloth of the present embodiment, it include base material 1, interface connect coating 2, noctilucent coating 3
With protective layer 4, interface connection coating 2 is coated on the upper surface of base material 1 by coating method, and noctilucent coating 3 is applied by coating method
Interface connection coating 2 upper surface is overlying on, protective layer 4 is coated on the upper surface of noctilucent coating 3.
Actually the material of base material can be various for cotton or burlap or woven dacron or non-woven fabrics or polyester-cotton blend fiber crops mixing cloth etc.
Need to do the cloth of noctilucent coating, the base material 1 that the present embodiment is used is the numb material of polyester-cotton blend.
Interface connection coating material is prepared, deionized water 30kg, the kg of dispersant 0.3, the kg of defoamer 0.3, titanium white is weighed
Powder 25 kg, PVA emulsion 20 kg, the kg of acrylic emulsion 20, the kg of thickener 5, put it into mixing inside stainless steel groove tank, press
Sequence mixed at high speed stirs, stand-by.
Noctilucent coating material is prepared, deionized water 30kg, acrylic emulsion 80kg, the kg of luminescent powder 20, dispersant 1 is weighed
Kg, the kg of defoamer 1, luminescent powder selection particle diameter is 300 mesh, puts it into mixing inside stainless steel groove tank, disperses 20 minutes, mistake
Filter, it is stand-by.
Configuration protection layer material, weighs acrylic emulsion 50kg, defoamer 0.5kg, thickener 0.5kg, is mixed, treats
With.
The coating weight of control interface connection coating is 180 grams/m, and the coating weight of noctilucent coating is 150 grams/square
Rice, the coating weight of protective layer is 150 grams/m.The assay method of coating weight is to take 1 square metre of uncoated fabric first
Weight is weighed, then takes the cloth after 1 square metre of coating to weigh weight, the latter's data are subtracted into former data, is exactly the painting of gained
Cloth amount.
The preparation method of this noctilucent coating cloth, referring to the drawings 2, comprises the following steps：
（1）Base material pre-treatment step S1, preliminary treatment is carried out to base material, and base material, then perching, fabric surface are selected first
It must not have a stain, the end of a thread is controlled at 5/every square metre, then enter drying box drying.
（2）Interface connection coating blend step S2：By deionized water, dispersant, defoamer, titanium dioxide, PVA emulsions, third
Olefin(e) acid emulsion, thickener are mixed evenly, filtering.
（3）Noctilucent coating blend step S3：Deionized water, acrylic emulsion, luminescent powder, dispersant, defoamer are mixed,
It is scattered 10 ~ 30 minutes, it is mixed evenly.
（4）Application step S4：First will（2）In interface connection coating be coated in substrate surface, enter 120 DEG C of drying box and do
Dry 3 minutes；, will after interface connection coating is dried（3）In noctilucent coating be coated on interface connect coating surface, enter drying box
120 DEG C of dryings 5 minutes, take out observation.Protective layer is finally coated on to the surface of noctilucent coating, then is dried.
The 5 groups of samples of this coating cloth for choosing gained after above-mentioned steps carry out measuring, and label sample 1 ~ 5 determines knot
Fruit is as follows：
It is demonstrated experimentally that the coating cloth fluorescent lifetime, air brushing effect, glossiness, whiteness are higher standard, meet demand.
Embodiment two
The noctilucent coating cloth of the present embodiment, it includes base material 1, interface connection coating 2, noctilucent coating 3 and protective layer 4, boundary
Face connects coating 2 and is coated on the upper surface of base material 1 by coating method, and noctilucent coating 3 is coated on interface by coating method and connected
The upper surface of coating 2, protective layer 4 is coated on the upper surface of noctilucent coating 3.
Actually the material of base material can be various for cotton or burlap or woven dacron or non-woven fabrics or polyester-cotton blend fiber crops mixing cloth etc.
Need to do the cloth of noctilucent coating, the base material 1 that the present embodiment is used is the numb material of polyester-cotton blend.
Interface connection coating material is prepared, deionized water 40kg, the kg of dispersant 0.4, the kg of defoamer 0.4, titanium white is weighed
Powder 30 kg, PVA emulsion 25 kg, the kg of acrylic emulsion 25, the kg of thickener 6, put it into mixing inside stainless steel groove tank, press
Sequence mixed at high speed stirs, stand-by.
Noctilucent coating material is prepared, deionized water 40kg, acrylic emulsion 80kg, the kg of luminescent powder 60, dispersant is weighed
2kg, defoamer 2.5kg, luminescent powder selection particle diameter is 800 mesh, puts it into mixing inside stainless steel groove tank, disperses 20 minutes,
Filtering, it is stand-by.
Configuration protection layer material, weighs acrylic emulsion 50kg, defoamer 0.5kg, thickener 0.5kg, is mixed, treats
With.
The coating weight of control interface connection coating is 180 grams/m, and the coating weight of noctilucent coating is 180 grams/square
Rice, the coating weight of protective layer is 180 grams/m.The assay method of coating weight is to take 1 square metre of uncoated fabric first
Weight is weighed, then takes the cloth after 1 square metre of coating to weigh weight, the latter's data are subtracted into former data, is exactly the painting of gained
Cloth amount.
The preparation method of the noctilucent coating cloth is identical with embodiment one.
The 5 groups of samples of this coating cloth for choosing gained after above-mentioned steps carry out measuring, and label sample 6 ~ 10 determines knot
Fruit is as follows：
It is demonstrated experimentally that the coating cloth fluorescent lifetime, air brushing effect, glossiness, whiteness are higher standard, meet demand.
Embodiment three
The noctilucent coating cloth of the present embodiment, it includes base material 1, interface connection coating 2, noctilucent coating 3 and protective layer 4, boundary
Face connects coating 2 and is coated on the upper surface of base material 1 by coating method, and noctilucent coating 3 is coated on interface by coating method and connected
The upper surface of coating 2, protective layer 4 is coated on the upper surface of noctilucent coating 3.
Actually the material of base material can be that cotton or burlap or fabric or polyester fiber or non-woven fabrics or polyester-cotton blend fiber crops etc. are each
Planting needs to make the cloth of noctilucent coating, and the base material 1 that the present embodiment is used is the numb material of polyester-cotton blend.
Interface connection coating material is prepared, deionized water 20kg, dispersant 0.2kg, the kg of defoamer 0.2, titanium dioxide is weighed
20 kg, PVA emulsion 15 kg, the kg of acrylic emulsion 15, the kg of thickener 4, put it into mixing inside stainless steel groove tank, sequentially
Mixed at high speed stirs, stand-by.
Noctilucent coating material is prepared, deionized water 20kg, acrylic emulsion 60kg, the kg of luminescent powder 10, dispersant is weighed
0.5 kg, the kg of defoamer 0. 5, luminescent powder selection particle diameter is 200 mesh, puts it into mixing inside stainless steel groove tank, disperses 20
Minute, filtering is stand-by.
Configuration protection layer material, weighs acrylic emulsion 50kg, defoamer 0.5kg, thickener 0.5kg, is mixed, treats
With.
The coating weight of control interface connection coating is 200 grams/m, and the coating weight of noctilucent coating is 100 grams/square
Rice, the coating weight of protective layer is 120 grams/m.The preparation method of the noctilucent coating cloth is identical with embodiment one.Choose above-mentioned
The 5 groups of samples progress measurings of this coating cloth of gained, label sample 11 ~ 15 after step, measurement result is as follows：
It is demonstrated experimentally that the coating cloth fluorescent lifetime, air brushing effect, glossiness, whiteness are higher standard, meet demand.
In summary, preferred embodiment of the present utility model is these are only, is not intended to limit of the present utility model
Protection domain.All any modification, equivalent substitution and improvements made within spirit of the present utility model and principle etc., all should be wrapped
It is contained within protection domain of the present utility model.
Claims (5)
1. a kind of noctilucent coating cloth, it is characterised in that the noctilucent coating including base material and with luminous effect, the base material is base
Cloth, substrate upper surface is coated with interface by coating method and connects coating, and noctilucent coating is coated on interface by coating method and connected
Connect coating surface；Luminescent powder particle diameter is 200 ~ 800 mesh in the noctilucent coating；The coating weight of the noctilucent coating is 100 ~ 180
Gram/m.
2. a kind of noctilucent coating cloth according to claim 1, it is characterised in that the base material material be cotton or burlap or
Woven dacron or non-woven fabrics or polyester-cotton blend fiber crops mixing cloth.
3. a kind of noctilucent coating cloth according to claim 1, it is characterised in that the noctilucent coating upper surface is also coated with
Protective layer.
4. a kind of noctilucent coating cloth according to claim 1, it is characterised in that the luminescent powder particle diameter is 300 mesh.
5. a kind of noctilucent coating cloth according to claim 1, it is characterised in that the coating weight of the interface connection coating is
120 ~ 800 grams/m.