CN206189760U - Anti integrated layer structure of scribbling of decoration that keeps warm that splits of elasticity reflection thermal barrier coating material - Google Patents
Anti integrated layer structure of scribbling of decoration that keeps warm that splits of elasticity reflection thermal barrier coating material Download PDFInfo
- Publication number
- CN206189760U CN206189760U CN201621067797.8U CN201621067797U CN206189760U CN 206189760 U CN206189760 U CN 206189760U CN 201621067797 U CN201621067797 U CN 201621067797U CN 206189760 U CN206189760 U CN 206189760U
- Authority
- CN
- China
- Prior art keywords
- layer
- elastic
- insulation paint
- heat preservation
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to an anti integrated layer structure of scribbling of decoration that keeps warm that splits of elasticity reflection thermal barrier coating material, a mao floating coat, elasticity reflection thermal barrier coating material layer and organic inorganic hydridization light catalytic cover surface course are drawn to waterproof crack resistance mortar layer, heat preservation putty layer, alkali -resistant sealing primer layer, elasticity including from interior to exterior coats in proper order on the wall body. Should scribble the layer structure and can not only hide wall body fine crack in order to realize anti splitting, in addition can reflect sunlight in order to reduce wall body outer surface temperature to realize thermal -insulated heat preservation effect, can keep permanent beautiful if new and the lasting reflective insulation effect of wall body in addition, have simultaneously that thickness thinly, easy is under construction, advantage such as with low costs.
Description
Technical field
The utility model is related to a kind of coating structure, more particularly to a kind of elastic reflective heat-insulation paint cracking resistance insulation and decoration one
Body coating structure.
Background technology
As country is to the pay attention to day by day of energy-conserving and environment-protective, requirement to building energy conservation also more and more higher, then external wall
Energy-saving scheme also arises.By " greenhouse effects " influence, and the constantly propulsion of urbanization ground, China's summer is most of in recent years
There is continuous high temperature in area, and energy consumption of air conditioning in summer is ramped.Therefore exploitation heat insulating material, development Green energy-saving buildings are
The most important thing.
Conventional insulation mainly uses thickness high and thermal resistance high, and heat-insulated guarantor is reached by the way of intercepting, passive
The effect of temperature, Typical Representative is warming plate, but warming plate cost is high, construction cost of labor is higher, easy to fall off and after coming off
It is difficult to repair.
Elastomeric paint (including elasticity is flat apply and elastic napping) has and covers that wall blind crack, various colors are colorful, decoration
Property good advantage, but there is also the poor shortcoming of stain resistance, and traditional elastic paint does not have reflective insulation effect.
Utility model content
The purpose of this utility model is to overcome disadvantage mentioned above, there is provided a kind of elastic reflective heat-insulation paint cracking resistance insulation and decoration
Integrative Coating structure, the coating structure can not only cover wall blind crack to realize cracking resistance, and can reflected sunlight with
Reduce exterior surface of wall temperature, so as to realize thermal insulation function, be furthermore possible to keep wall it is permanent it is beautiful as it is new with it is lasting
Reflective insulation effect, while having both thickness of thin, easily construction, low cost and other advantages.
What the utility model was realized in:A kind of elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating knot
Structure, it is characterised in that:Including the waterproof anti-crack mortar layer, heat preservation putty layer, the alkali resistant envelope that are coated on successively from the inside to the outside on wall
Close prime coat, elastic napping floating coat, elastic reflective heat-insulation paint layer and organic inorganic hybridization photocatalysis finishing coat.
Preferably, the waterproof anti-crack mortar layer is uniformly applied by the waterproof anti-crack mortar with water resistance and cracking resistance
Cover and form.Building masonry wall is typically built into by clay brick or structural clay tile, surface irregularity, it is necessary first to is criticized and is scraped cement bonded sand
Slurry is levelling:On the one hand the gap between filling brick and brick makes that surface is more smooth, reduce putty consumes, and on the other hand ensures wall
Steadiness.Waterproof anti-crack mortar both has traditional polymer cement mortar advantage, also overcomes traditional polymer cement mortar easy
The defect of shrinkage cracking, wall crazing, cracking are efficiently solved the problems, such as with its unique pliability;Meanwhile, with water proofing property
Can be excellent the characteristics of, can prevent rainwater from penetrating into influence endothecium structure.
Preferably, heat preservation putty layer is uniformly coated by insulation putty for architectural exterior wall and formed and thickness is 5-15 millimeters.Exterior wall
Contain appropriate hollow structure powder (such as cenosphere, expanded perlite etc.) in heat preservation putty, it had both been had higher viscous
Knotting strength, and with lower thermal conductivity, heat insulation and preservation effect.
In order to adequate closure heat preservation putty layer, the accumulation of salt in the surface soil is prevented, the alkali-resistant sealing primer layer is closed by alkali resistant
Uniformly coating is formed priming paint and thickness is 20-60 microns.
Preferably, by applying coating in elastic napping, uniformly coating is formed the elastic napping floating coat.Applied in elastic napping
Coating has concavo-convex texture and texture, and finishing effect is protruded, and third dimension is strong, can effectively cover wall blind crack;And bullet
Property plucking in apply coating price it is much cheaper than elastic napping painting coating, unit price is substantially reduced, with significant competing
Strive advantage.Preferably, using coating in the elastic napping of higher elasticity, its technical indicator meets the elastic napping floating coat
JG/T 172-2014《Elastic building paint》Requirement, with reach effectively cover wall blind crack effect.
Preferably, the elastic reflective heat-insulation paint layer is uniformly coated by the elastic reflective heat-insulation paint of energy reflected sunlight
Form and thickness is 30-100 microns.The elastic reflective heat-insulation paint layer using high resiliency and with sun luminous reflectance high and
The elastic reflective heat-insulation paint of near-infrared reflection ratio, its elastic performance and physical property meet JG/T 172-2014《Elasticity building
Coating》Property indices, and heat-reflecting heat-insulating performance meets JG/T 235-2014《Architectural reflective heat-insulation paint》Will
Ask.The thickness can either ensure to be completely covered by ground, unit area material price it is moderate and ensure that effectively reflection is too
Sunlight (especially near infrared band), reduces sunshine actual absorption amount, so as to effectively reduce elastic reflective heat-insulation paint layer
Surface temperature;Simultaneously plus the lower thermal conductivity of heat preservation putty layer, heat can be effectively reduced to wall and indoor transmission, substantially reduce
Air conditioning energy consumption, reaches energy-conservation purpose.
Preferably, the organic inorganic hybridization photocatalysis finishing coat is uniformly applied by organic inorganic hybridization photocatalysis overlay coating
Cover and form.Because elastic reflective heat-insulation paint film is softer, stain resistance is poor, and after staiing its reflected sunlight ability
Also drastically decline, corresponding reflective insulation performance also drastically have dropped.In order to keep elastic reflective heat-insulation paint layer permanent beautiful
As newly, one layer of organic inorganic hybridization photocatalysis cover of very thin water white transparency being provided with elastic reflective heat-insulation paint layer surface
Layer.There is organic inorganic hybridization photocatalysis finishing coat, the coating photocatalysis (under sunlight, to be excited by sunshine
HO, HO of formation2And O2 -Contour active factors can decompose the oiliness pollution for being attached to elastic reflective heat-insulation paint layer surface
Thing and part inorganic matter;While NO, N0 in the air that can degrade2And SO2Deng toxic gas, purify air) and the self-cleaning characteristic of light
(make coating surface that hydrophily very high is presented, it is suppressed that the generation of exterior wall electrostatic, make the pollutants such as dust, dust and analyte
It is more easy to be fallen by rain drop erosion):On the premise of elastic reflective heat-insulation paint layer outward appearance is not influenceed, elastic reflective heat-insulation paint is improved
Weatherability, the automatically cleaning of layer, this ensure that elastic reflective heat-insulation paint layer is permanent beautiful such as new, and reach permanent reflection
Heat insulation and preservation effect.
For prior art, the utility model has advantages below:
(1) the elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure that the utility model is provided, can not only
Wall blind crack is covered to realize cracking resistance, and energy reflected sunlight is to reduce exterior surface of wall temperature, it is heat-insulated so as to realize
Insulation effect, is furthermore possible to keep the permanent beautiful such as new and lasting reflective insulation effect of wall, while having both thickness of thin, easily applying
Work, low cost and other advantages;
(2) the elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure that the utility model is provided, waterproof resists
Split mortar and wall crazing, cracking are efficiently solved the problems, such as with its unique pliability;Excellent water resistance can prevent rain
Water penetrates into influence endothecium structure;
(3) the elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure that the utility model is provided, exterior wall is protected
Contain appropriate hollow structure powder (such as cenosphere, expanded perlite etc.) in warm putty, with lower thermal conductivity, excellent
Heat insulation and preservation effect;
(4) the elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure that the utility model is provided, elasticity is drawn
Hair floating coat and elastic reflective heat-insulation paint layer have high resiliency, can effectively cover wall blind crack, reach cracking resistance and dress
Decorations effect;
(5) the elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure that the utility model is provided, elasticity is drawn
Hair floating coat (cheap) and elastic reflective heat-insulation paint layer (price) are used cooperatively, concavo-convex texture needed for can reaching with
Texture, can reduce unit price again;
(6) the elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure that the utility model is provided, elasticity is anti-
Penetrate insulating moulding coating layer can high-efficiency reflective sunshine (especially near infrared band), sunshine actual absorption amount is greatly decreased to drop
Parapet external surface temperature, so as to realize thermal insulation function, environmental protection and energy saving;
(7) the elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure that the utility model is provided, You Jiwu
Machine hydridization photocatalysis finishing coat has photocatalysis and the self-cleaning characteristic of light, is not influenceing elastic reflective heat-insulation paint layer outward appearance
Under the premise of, weatherability, the automatically cleaning of elastic reflective heat-insulation paint layer are improved, this ensure that the length of elastic reflective heat-insulation paint layer
It is beautiful long such as new, and reach permanent reflecting heat insulation effect;
(8) the elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure that the utility model is provided, You Jiwu
Machine hydridization photocatalysis finishing coat can degrade NO, N0 in air2And SO2Deng toxic gas, purify air, environmental protection.
Brief description of the drawings
The utility model is described in further detail in conjunction with the embodiments with reference to the accompanying drawings:
Fig. 1 is the structural representation of the utility model elasticity reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure
Figure.
Symbol description in figure:1st, wall;2nd, waterproof anti-crack mortar layer;3rd, heat preservation putty layer;4th, alkali-resistant sealing primer layer;5、
Elastic napping floating coat;6th, elastic reflective heat-insulation paint layer;7th, organic inorganic hybridization photocatalysis finishing coat.
Specific embodiment
The utility model content is described in detail with reference to Figure of description and specific embodiment:
As shown in figure 1, for a kind of elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative that the utility model is provided is applied
Rotating fields, it is characterised in that:Including be coated on successively from the inside to the outside on wall 1 waterproof anti-crack mortar layer 2, heat preservation putty layer 3,
Alkali-resistant sealing primer layer 4, elastic napping floating coat 5, elastic reflective heat-insulation paint layer 6 and organic inorganic hybridization photocatalysis finishing coat
7。
Preferably, the waterproof anti-crack mortar layer 2 is uniform by the waterproof anti-crack mortar with water resistance and cracking resistance
Coating is formed.Building masonry wall is typically built into by clay brick or structural clay tile, surface irregularity, it is necessary first to is criticized and is scraped cement
Mortar levelling:On the one hand filling brick and brick between gap make surface it is more smooth, reduce putty consume, on the other hand ensure wall
Steadiness.Waterproof anti-crack mortar both has traditional polymer cement mortar advantage, also overcomes traditional polymer cement mortar
The defect of easy shrinkage cracking, wall crazing, cracking are efficiently solved the problems, such as with its unique pliability;Meanwhile, with waterproof
The characteristics of excellent performance, can prevent rainwater from penetrating into influence endothecium structure.The waterproof anti-crack mortar layer 2 can use application number
Uniformly coating is formed waterproof anti-crack mortar described in 201410672336.2, it would however also be possible to employ other mortars.
Preferably, heat preservation putty layer 3 is uniformly coated by insulation putty for architectural exterior wall and formed and thickness is 5-15 millimeters.Exterior wall
Contain appropriate hollow structure powder (such as cenosphere, expanded perlite etc.) in heat preservation putty, it had both been had higher viscous
Knotting strength, and with lower thermal conductivity, heat insulation and preservation effect.Heat preservation putty layer 3 can use application number 201410621238.6
Described in construction wall heat preservation putty uniformly coating form, it would however also be possible to employ other heat preservation putties.
In order to adequate closure heat preservation putty layer 3, the accumulation of salt in the surface soil is prevented, the alkali-resistant sealing primer layer 4 is sealed by alkali resistant
Uniformly coating is formed and thickness is 20-60 microns to close priming paint.Alkali-resistant sealing primer layer 4 can use application number 201410808817.1
Described in external wall waterproof alkali-resistant sealing primer uniformly coating form, it would however also be possible to employ other alkali-resistant sealing primers.
By applying coating in elastic napping, uniformly coating is formed the elastic napping floating coat 5.Applying coating in elastic napping can
Application reference number is coating in a kind of elastic napping for being previously mentioned in 201510228588.0, the coating have absorption affinity it is good,
Surface flatness is high, intensity is high and the good advantage of anti-division performance.
Preferably, the elastic reflective heat-insulation paint layer 6 is uniformly applied by the elastic reflective heat-insulation paint of energy reflected sunlight
Cover form and thickness be 30-100 microns.The elastic reflective heat-insulation paint layer 6 is using high resiliency and with sunshine high reflection
Than the elastic reflective heat-insulation paint with near-infrared reflection ratio, its elastic performance and physical property meet JG/T 172-2014《Elasticity
Building coating》Requirement, and heat-reflecting heat-insulating performance meets JG/T235-2014《Architectural reflective heat-insulation paint》Requirement.Elasticity
Reflective heat-insulation paint layer 6 can be applied using the elastic stain resistant solar heat reflecting and heat insulating described in application number 201510943709.X
The uniform coating of material is formed, it would however also be possible to employ other elastic reflective heat-insulation paints.
Preferably, the organic inorganic hybridization photocatalysis finishing coat 7 is uniform by organic inorganic hybridization photocatalysis overlay coating
Coating is formed.Easily stain because 6 paint film of elastic reflective heat-insulation paint layer are softer, and after staiing its reflected sunlight ability
Also drastically decline, corresponding reflective insulation performance also drastically have dropped.In order to keep elastic reflective heat-insulation paint layer 6 permanent beautiful
As newly, one layer of organic inorganic hybridization photocatalysis cover of very thin water white transparency is provided with 6 surface of elastic reflective heat-insulation paint layer
Layer 7.There is organic inorganic hybridization photocatalysis finishing coat 7, the coating photocatalysis (under sunlight, to be swashed by sunshine
Send out HO, the HO for being formed2And O2 -Contour active factors can decompose the oiliness dirt for being attached to elastic 6 surface of reflective heat-insulation paint layer
Dye thing and part inorganic matter;While NO, N0 in the air that can degrade2And SO2Deng toxic gas, purify air) and the self-cleaning spy of light
Property (make coating surface that hydrophily very high is presented, it is suppressed that the generation of exterior wall electrostatic, make the pollutants such as dust, dust and decomposition
Thing is more easy to be fallen by rain drop erosion):On the premise of 6 outward appearance of elastic reflective heat-insulation paint layer are not influenceed, elastic reflective insulation is improved
The weatherability of dope layer 6, automatically cleaning, this ensure that elastic reflective heat-insulation paint layer 6 is permanent beautiful such as new, and reach length
Long reflecting heat insulation effect.The organic inorganic hybridization photocatalysis finishing coat 7 can use application number 201510298546.4
Described in organic inorganic hybridization photocatalysis overlay coating uniformly coating form, it would however also be possible to employ other organic inorganic hybridization light
Catalysis overlay coating.
Above-mentioned specific embodiment is that the technical solution of the utility model is explained in detail, and the utility model is not
Above-described embodiment is only limited only to, every any improvement or replacement according to the utility model principle all should be new in this practicality
Within the protection domain of type.
Claims (7)
1. a kind of elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure, it is characterised in that:Including from the inside to the outside
Waterproof anti-crack mortar layer (2), heat preservation putty layer (3), alkali-resistant sealing primer layer (4), elasticity drawing on wall (1) are coated on successively
Hair floating coat (5), elastic reflective heat-insulation paint layer (6) and organic inorganic hybridization photocatalysis finishing coat (7).
2. elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure according to claim 1, its feature exists
In:By the waterproof anti-crack mortar with water resistance and cracking resistance, uniformly coating is formed waterproof anti-crack mortar layer (2).
3. elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure according to claim 1, its feature exists
In:Heat preservation putty layer (3) is uniformly coated by insulation putty for architectural exterior wall and formed and thickness is 5-15 millimeters.
4. elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure according to claim 1, its feature exists
In:Alkali-resistant sealing primer layer (4) is uniformly coated by alkali-resistant sealing primer and formed and thickness is 20-60 microns.
5. elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure according to claim 1, its feature exists
In:By applying coating in elastic napping, uniformly coating is formed the elastic napping floating coat (5).
6. elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure according to claim 1, its feature exists
In:By the elastic reflective heat-insulation paint of energy reflected sunlight, uniformly coating is formed and thick elastic reflective heat-insulation paint layer (6)
Spend is 30-100 microns.
7. elastic reflective heat-insulation paint cracking resistance heat preservation decoration integrative coating structure according to claim 1, its feature exists
In:By organic inorganic hybridization photocatalysis overlay coating, uniformly coating is formed the organic inorganic hybridization photocatalysis finishing coat (7).