CN206189759U - Sun thermoreflectance feel coating scribble layer structure - Google Patents
Sun thermoreflectance feel coating scribble layer structure Download PDFInfo
- Publication number
- CN206189759U CN206189759U CN201621067792.5U CN201621067792U CN206189759U CN 206189759 U CN206189759 U CN 206189759U CN 201621067792 U CN201621067792 U CN 201621067792U CN 206189759 U CN206189759 U CN 206189759U
- Authority
- CN
- China
- Prior art keywords
- coating
- layer
- heat reflection
- solar heat
- reflection texture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a sun thermoreflectance feel coating scribble layer structure, including from interior to exterior coat in proper order waterproof crack resistance mortar layer, heat preservation putty layer, alkali -resistant sealing primer layer, thermoreflectance feel dope layer and organic inorganic hydridization light catalytic cover surface course on the wall body. Should scribble the layer structure and not only have a three -dimensional fashion effect of ordinary feel coating, in addition can reflect sunlight in order to reduce wall body outer surface temperature to realize thermal -insulated heat preservation effect, can keep permanent beautiful if new and the lasting reflective insulation effect of wall body in addition, have simultaneously that thickness thinly, easy is under construction, advantage such as with low costs.
Description
Technical field
The utility model is related to a kind of coating structure, more particularly to a kind of coating structure of solar heat reflection texture coating.
Background technology
As country is to the pay attention to day by day of energy-conserving and environment-protective, requirement to building energy conservation also more and more higher, then external wall
Energy-saving scheme also arises.By " greenhouse effects " influence, and the constantly propulsion of urbanization ground, China's summer is most of in recent years
There is continuous high temperature in area, and energy consumption of air conditioning in summer is ramped.Therefore exploitation heat insulating material, development Green energy-saving buildings are
The most important thing.
Conventional insulation mainly uses thickness high and thermal resistance high, and heat-insulated guarantor is reached by the way of intercepting, passive
The effect of temperature, Typical Representative is warming plate, but warming plate cost is high, construction cost of labor is higher, easy to fall off and after coming off
It is difficult to repair.
Texture (art) coating is a kind of personalized, painting design of fashion-orientation of modern exterior wall application, with abundant many
Color artistic expression, the artistic effect of various three-dimensional fashion can be createed with different construction tool and technique；
There is certain pliability simultaneously, being capable of cracking resistance.But, just because of texture coating uniqueness third dimension and rough surface, uneven,
It is easily piled up dust and cause to stain；Meanwhile, existing texture coating layer can not effectively reflected sunlight with reach reflect every
Hot insulation effect.
Utility model content
The purpose of this utility model is to overcome disadvantage mentioned above, there is provided a kind of coating knot of solar heat reflection texture coating
Not only there is structure, the coating structure the three-dimensional fashion statement of common texture coating, and energy reflected sunlight to reduce outside wall
Surface temperature, so as to realize thermal insulation function, is furthermore possible to keep wall permanent beautiful as new and lasting reflective insulation is imitated
Really, while having both thickness of thin, easily construction, low cost and other advantages.
What the utility model was realized in：A kind of coating structure of solar heat reflection texture coating, it is characterised in that：Bag
Include waterproof anti-crack mortar layer, heat preservation putty layer, alkali-resistant sealing primer layer, the heat reflection matter being coated on successively from the inside to the outside on wall
Sense dope layer and organic inorganic hybridization photocatalysis finishing coat.
Preferably, the waterproof anti-crack mortar layer is uniformly applied by the waterproof anti-crack mortar with water resistance and cracking resistance
Cover and form.Building masonry wall is typically built into by clay brick or structural clay tile, surface irregularity, it is necessary first to is criticized and is scraped cement bonded sand
Slurry is levelling：On the one hand the gap between filling brick and brick makes that surface is more smooth, reduce putty consumes, and on the other hand ensures wall
Steadiness.Waterproof anti-crack mortar both has traditional polymer cement mortar advantage, also overcomes traditional polymer cement mortar easy
The defect of shrinkage cracking, wall crazing, cracking are efficiently solved the problems, such as with its unique pliability；Meanwhile, with water proofing property
Can be excellent the characteristics of, can prevent rainwater from penetrating into influence endothecium structure.
Preferably, heat preservation putty layer is uniformly coated by insulation putty for architectural exterior wall and formed and thickness is 5-15 millimeters.Exterior wall
Contain appropriate hollow structure powder (such as cenosphere, expanded perlite etc.) in heat preservation putty, it had both been had higher viscous
Knotting strength, and with lower thermal conductivity, heat insulation and preservation effect.
In order to adequate closure heat preservation putty layer, the accumulation of salt in the surface soil is prevented, the alkali-resistant sealing primer layer is closed by alkali resistant
Uniformly coating is formed priming paint and thickness is 20-60 microns.
Preferably, the heat reflection texture coating layer is by the uniform coating of reflective insulation texture paint of energy reflected sunlight
Into and thickness be 1-3 millimeters.Reflective insulation texture paint can reflect most sunshine (especially near infrared band), greatly
The big actual absorption amount for reducing sunshine, so as to effectively reduce the surface temperature of heat reflection texture coating layer；Simultaneously plus insulation
The lower thermal conductivity of putty layer, can effectively reduce heat to wall and indoor transmission, substantially reduce air conditioning energy consumption, reach energy-conservation mesh
's.
Preferably, the organic inorganic hybridization photocatalysis finishing coat is uniformly applied by organic inorganic hybridization photocatalysis overlay coating
Cover and form.Because texture coating unique solid and surface roughness, make its easily dust stratification and contamination, and dust stratification and contamination
The ability of its reflected sunlight also drastically declines afterwards, and corresponding reflective insulation performance also drastically have dropped.In order to keep heat reflection
Texture coating layer is permanent beautiful as newly, one layer of organic-inorganic of very thin water white transparency being provided with heat reflection texture coating layer surface
Hydridization photocatalysis finishing coat.Organic inorganic hybridization photocatalysis finishing coat, the coating has photocatalysis (in sunlight
Under, HO, the HO to be formed are excited by sunshine2And O2 -Contour active factors can be decomposed and be attached to heat reflection texture coating layer table
The oiliness pollutant and part inorganic matter in face；While NO, N0 in the air that can degrade2And SO2Deng toxic gas, purify air)
(make coating surface that hydrophily very high is presented, it is suppressed that the generation of exterior wall electrostatic, make the dirts such as dust, dust with the self-cleaning characteristic of light
Dye thing and analyte are more easy to be fallen by rain drop erosion)：On the premise of heat reflection texture coating layer outward appearance is not influenceed, heat reflection is improved
Weatherability, the automatically cleaning of texture coating layer, this ensure that heat reflection texture coating layer is permanent beautiful such as new, and reach length
Long reflecting heat insulation effect.
For prior art, the utility model has advantages below：
(1) coating structure of the solar heat reflection texture coating that the utility model is provided, not only with common texture coating
Three-dimensional fashion statement, and can reflected sunlight to reduce exterior surface of wall temperature, so as to realize thermal insulation function, in addition
The permanent beautiful such as new and lasting reflective insulation effect of wall can be kept, while it is low excellent to have both thickness of thin, easily construction, cost
Point；
(2) coating structure of the solar heat reflection texture coating that the utility model is provided, waterproof anti-crack mortar is unique with it
Pliability efficiently solve the problems, such as wall crazing, cracking；Excellent water resistance can prevent rainwater from penetrating into influence internal layer
Structure；
(3) coating structure of the solar heat reflection texture coating that the utility model is provided, containing suitable in insulation putty for architectural exterior wall
The hollow structure powder (such as cenosphere, expanded perlite etc.) of amount, with lower thermal conductivity, excellent heat insulation and preservation effect；
(4) coating structure of the solar heat reflection texture coating that the utility model is provided, heat reflection texture coating layer has
Certain toughness, can cover wall blind crack；Various, three-dimensional fashion can be createed according to customer demand simultaneously
Artistic effect；
(5) coating structure of the solar heat reflection texture coating that the utility model is provided, heat reflection texture coating layer can
High-efficiency reflective sunshine (especially near infrared band), sunshine actual absorption amount is greatly decreased to reduce exterior surface of wall temperature
Degree, so as to realize thermal insulation function, environmental protection and energy saving；
(6) coating structure of the solar heat reflection texture coating that the utility model is provided, organic inorganic hybridization photocatalysis cover
Surface layer has photocatalysis and the self-cleaning characteristic of light, on the premise of heat reflection texture coating layer outward appearance is not influenceed, improves heat anti-
Weatherability, the automatically cleaning of texture coating layer are penetrated, this ensure that heat reflection texture coating layer is permanent beautiful such as new, and is reached
Permanent reflecting heat insulation effect；
(7) coating structure of the solar heat reflection texture coating that the utility model is provided, organic inorganic hybridization photocatalysis cover
Surface layer can degrade NO, N0 in air2And SO2Deng toxic gas, purify air, environmental protection.
Brief description of the drawings
The utility model is described in further detail in conjunction with the embodiments with reference to the accompanying drawings：
Fig. 1 is the structural representation of the coating structure of the utility model solar heat reflection texture coating.
Symbol description in figure：1st, wall；2nd, waterproof anti-crack mortar layer；3rd, heat preservation putty layer；4th, alkali-resistant sealing primer layer；5、
Heat reflection texture coating layer；6th, organic inorganic hybridization photocatalysis finishing coat.
Specific embodiment
The utility model content is described in detail with reference to Figure of description and specific embodiment：
As shown in figure 1, a kind of coating structure of the solar heat reflection texture coating provided for the utility model, its feature exists
In：Including waterproof anti-crack mortar layer 2, heat preservation putty layer 3, the alkali-resistant sealing primer layer being coated on successively from the inside to the outside on wall 1
4th, heat reflection texture coating layer 5 and organic inorganic hybridization photocatalysis finishing coat 6.
Preferably, the waterproof anti-crack mortar layer 2 is uniform by the waterproof anti-crack mortar with water resistance and cracking resistance
Coating is formed.Building masonry wall is typically built into by clay brick or structural clay tile, surface irregularity, it is necessary first to is criticized and is scraped cement
Mortar levelling：On the one hand filling brick and brick between gap make surface it is more smooth, reduce putty consume, on the other hand ensure wall
Steadiness.Waterproof anti-crack mortar both has traditional polymer cement mortar advantage, also overcomes traditional polymer cement mortar
The defect of easy shrinkage cracking, wall crazing, cracking are efficiently solved the problems, such as with its unique pliability；Meanwhile, with waterproof
The characteristics of excellent performance, can prevent rainwater from penetrating into influence endothecium structure.The waterproof anti-crack mortar layer 2 can use application number
Uniformly coating is formed waterproof anti-crack mortar described in 201410672336.2, it would however also be possible to employ other mortars.
Preferably, heat preservation putty layer 3 is uniformly coated by insulation putty for architectural exterior wall and formed and thickness is 5-15 millimeters.Exterior wall
Contain appropriate hollow structure powder (such as cenosphere, expanded perlite etc.) in heat preservation putty, it had both been had higher viscous
Knotting strength, and with lower thermal conductivity, heat insulation and preservation effect.Heat preservation putty layer 3 can use application number 201410621238.6
Described in construction wall heat preservation putty uniformly coating form, it would however also be possible to employ other heat preservation putties.
In order to adequate closure heat preservation putty layer 3, the accumulation of salt in the surface soil is prevented, the alkali-resistant sealing primer layer 4 is sealed by alkali resistant
Uniformly coating is formed and thickness is 20-60 microns to close priming paint.Alkali-resistant sealing primer layer 4 can use application number 201410808817.1
Described in external wall waterproof alkali-resistant sealing primer uniformly coating form, it would however also be possible to employ other alkali-resistant sealing primers.
Preferably, the heat reflection texture coating layer 5 is uniformly coated by the reflective insulation texture paint of energy reflected sunlight
Form and thickness is 1-3 millimeters.Reflective insulation texture paint can reflect most sunshine (especially near infrared band),
Greatly reduce the actual absorption amount of sunshine, so as to effectively reduce the surface temperature of heat reflection texture coating layer 5；Simultaneously plus guarantor
The lower thermal conductivity of warm putty layer 3, can effectively reduce heat to wall 1 and indoor transmission, substantially reduce air conditioning energy consumption, reach energy-conservation
Purpose.Heat reflection texture coating layer 5 can be equal using the reflective insulation texture paint described in application number 201510515042.3
Even coating is formed, it would however also be possible to employ other reflective insulation texture paints.
Preferably, the organic inorganic hybridization photocatalysis finishing coat 6 is uniform by organic inorganic hybridization photocatalysis overlay coating
Coating is formed.Because texture coating unique solid and surface roughness, make its easily dust stratification and contamination, and dust stratification and contamination
The ability of its reflected sunlight also drastically declines afterwards, and corresponding reflective insulation performance also drastically have dropped.In order to keep hot anti-
Penetrate that texture coating layer 5 is permanent beautiful as new, the organic of one layer of very thin water white transparency is provided with 5 surface of heat reflection texture coating layer
Inorganic hybridization photocatalysis finishing coat 6.Organic inorganic hybridization photocatalysis finishing coat 6, the coating has photocatalysis (in sunshine
Under irradiation, HO, the HO to be formed are excited by sunshine2And O2 -Contour active factors can be decomposed and be attached to heat reflection texture coating
The oiliness pollutant and part inorganic matter on 5 surface of layer；While NO, N0 in the air that can degrade2And SO2Deng toxic gas, purification
Air) and the self-cleaning characteristic of light (make coating surface that hydrophily very high is presented, it is suppressed that the generation of exterior wall electrostatic, make dust, dust
It is more easy to be fallen by rain drop erosion Deng pollutant and analyte)：On the premise of heat reflection texture coating 5 outward appearance of layer are not influenceed, improve
Weatherability, the automatically cleaning of heat reflection texture coating layer 5, this ensure that heat reflection texture coating layer 5 is permanent beautiful such as new, and
And reach permanent reflecting heat insulation effect.The organic inorganic hybridization photocatalysis finishing coat 6 can use application number
Uniformly coating is formed organic inorganic hybridization photocatalysis overlay coating described in 201510298546.4, it would however also be possible to employ other
Organic inorganic hybridization photocatalysis overlay coating.
Above-mentioned specific embodiment is that the technical solution of the utility model is explained in detail, and the utility model is not
Above-described embodiment is only limited only to, every any improvement or replacement according to the utility model principle all should be new in this practicality
Within the protection domain of type.
Claims (6)
1. a kind of coating structure of solar heat reflection texture coating, it is characterised in that：Including being coated on wall successively from the inside to the outside
(1) waterproof anti-crack mortar layer (2), heat preservation putty layer (3) on, alkali-resistant sealing primer layer (4), heat reflection texture coating layer (5)
With organic inorganic hybridization photocatalysis finishing coat (6).
2. the coating structure of solar heat reflection texture coating according to claim 1, it is characterised in that：The water-proofing anticracking
By the waterproof anti-crack mortar with water resistance and cracking resistance, uniformly coating is formed screed (2).
3. the coating structure of solar heat reflection texture coating according to claim 1, it is characterised in that：The heat preservation putty
Layer (3) uniformly coated by insulation putty for architectural exterior wall form and thickness be 5-15 millimeters.
4. the coating structure of solar heat reflection texture coating according to claim 1, it is characterised in that：The alkali resistant closing
Prime coat (4) uniformly coated by alkali-resistant sealing primer form and thickness be 20-60 microns.
5. the coating structure of solar heat reflection texture coating according to claim 1, it is characterised in that：The heat reflection matter
By the reflective insulation texture paint of energy reflected sunlight, uniformly coating is formed and thickness is 1-3 millimeters for sense dope layer (5).
6. the coating structure of solar heat reflection texture coating according to claim 1, it is characterised in that：The organic-inorganic
By organic inorganic hybridization photocatalysis overlay coating, uniformly coating is formed for hydridization photocatalysis finishing coat (6).