CN204531156U - A kind of composite plate - Google Patents
A kind of composite plate Download PDFInfo
- Publication number
- CN204531156U CN204531156U CN201520240427.9U CN201520240427U CN204531156U CN 204531156 U CN204531156 U CN 204531156U CN 201520240427 U CN201520240427 U CN 201520240427U CN 204531156 U CN204531156 U CN 204531156U
- Authority
- CN
- China
- Prior art keywords
- foamed ceramic
- plate
- steel
- wire
- stainless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of composite plate, it comprises foamed ceramic plate, adhesive linkage and stone plate from below to up successively; Described foamed ceramic plate surface is bonding with described stone plate surface by described adhesive linkage; Described foamed ceramic plate surface and bottom surface are respectively arranged with stainless (steel) wire.The utility model, by being respectively arranged with stainless (steel) wire on foamed ceramic plate surface and bottom surface, increases cracking resistance and the rupture strength of foamed ceramic plate; Stainless (steel) wire intensity is large, makes the stress that whole composite board tool is stronger, more firmly; And stainless (steel) wire is corrosion-resistant, can also increase the service life.
Description
Technical field
The utility model relates to building material technical field, particularly relates to a kind of composite plate.
Background technology
Foamed ceramic sheet material is a kind of novel environment friendly building materials, is with potter's clay mine tailing, potsherd, riverway sludge, admixture etc. for primary raw material, adopts foaming technique, through the closed pore ceramic materials of the high porosity of high-temperature roasting.There is superior fire retardant performance, and have lightweight, sound insulation good, coefficient of deformation is little, anti-aging, stable performance, eco-environmental prote are good, with plinth course with float coat compatibility is good, safety and firmness is good, can with the advantage of building with the life-span.
Inside and outside the modern projects such as a lot of hotel, megastore, office premises, lithotome, with its irreplaceable texture, tone and property durable in use, is widely used, and lithotome also has the trend of carrying out on a large scale entering family and frock simultaneously.But due to the restriction of lithotome self performance, be applied to the batch stone material thickness overwhelming majority in construction work more than more than 20mm, and stone material density is at about 3000 kilograms/cubic metre, so application of pure stone material is blocked up overweight, cause engineering cost too high, transport constructional difficulties.
At present, foamed ceramic plate and stone plate combine and form new composite plate by a lot of ceramic producer, this composite plate has wide market sight and promotional value, but the fastness of this composite plate and stress exist certain defect, therefore have impact on its application life further.
Summary of the invention
The purpose of this utility model is to solve and improves and strengthen composite plate fastness and stress, increases the service life further and proposes a kind of composite plate.
For reaching this object, the utility model by the following technical solutions:
A kind of composite plate, it comprises foamed ceramic plate, adhesive linkage and stone plate from below to up successively; Described foamed ceramic plate surface is bonding with described stone plate surface by described adhesive linkage; Described foamed ceramic plate surface and bottom surface are respectively arranged with stainless (steel) wire.
Described foamed ceramic plate surface and bottom surface are respectively arranged with stainless (steel) wire, increase cracking resistance and rupture strength; Stainless (steel) wire intensity is large, makes the stress that whole composite board tool is stronger, more firmly; And stainless (steel) wire is corrosion-resistant, therefore can also increase the service life.
Preferably, the surface of described foamed ceramic plate and bottom surface and described stainless (steel) wire directly bond fixing by cementing agent.
Adopt cementing agent directly to bond convenient fixing fast, save time, enhance productivity; And cost is low.
Preferably, the thickness of described stainless (steel) wire is 0.5-5mm.
Stainless (steel) wire is too thin, and its anti-cracking function is too low, and whole composite plate stress is inadequate, and fastness neither be fine; Stainless (steel) wire is too thick, and make the thickness of described composite plate blocked up, the scope of application reduces.
Preferably, the grid of described stainless (steel) wire is long and wide is 1mm-2mm.
The grid of described stainless (steel) wire is long and wide is 1mm-2mm, make described stainless (steel) wire and described foamed ceramic plate connection more closely, the fastness of increase foamed ceramic plate, thus increase the fastness of whole composite plate.
Preferably, the thickness of described foamed ceramic plate is 30-150mm.
Described foamed ceramic plate is too thin, affects its intensity; Too thick, cause that engineering cost is too high, transport constructional difficulties, its thickness is good in the intensity of 30-150mm, and it is moderate that itself and stone plate combine the composite plate thickness formed, and expands the scope of application of composite plate.
Preferably, the thickness of described stone plate is 2.5-8mm.
Described stone plate is too thin, affects its intensity; Too thick, cause that engineering cost is too high, transport constructional difficulties, its thickness is good in the intensity of 2.5-8mm, and itself and foamed ceramic harden, and to close the composite plate thickness formed moderate, expands the scope of application of composite plate.
Preferably, described adhesive linkage is epoxy resin glue.
Epoxy resin glue, also known as AB glue, is solid after smearing mummification, can fills up, meet the production requirement of described foamed ceramic plate to the gap pit at the place of smearing.
The utility model, by being respectively arranged with stainless (steel) wire on foamed ceramic plate surface and bottom surface, increases cracking resistance and the rupture strength of foamed ceramic plate; Stainless (steel) wire intensity is large, makes the stress that whole composite board tool is stronger, more firmly; And stainless (steel) wire is corrosion-resistant, can also increase the service life.
Accompanying drawing explanation
Fig. 1 is the structural representation that the utility model one is specifically implemented.
Wherein: 1 is foamed ceramic plate, 2 is adhesive linkage, and 3 is material slabstone, and 5 is stainless (steel) wire.
Detailed description of the invention
The technical solution of the utility model is further illustrated by detailed description of the invention below in conjunction with accompanying drawing.
As shown in Figure 1, a kind of composite plate, it comprises foamed ceramic plate 1, adhesive linkage 2 and stone plate 3 from below to up successively; Described foamed ceramic plate 1 surface is bonding with described stone plate 3 surface by described adhesive linkage 2; Described foamed ceramic plate 1 surface and bottom surface are respectively arranged with stainless (steel) wire 5.
Illustrate at this, described stone plate 3 can be lithotome plate or artificial stone plate.
Embodiment 1, a kind of composite plate, it comprises foamed ceramic plate 1, adhesive linkage 2 and stone plate 3 from below to up successively; Described foamed ceramic plate 1 surface is bonding with described stone plate 3 surface by described adhesive linkage 2; Described foamed ceramic plate 1 surface and bottom surface are respectively arranged with stainless (steel) wire 5;
The thickness of described foamed ceramic plate 1 is 30mm, and the thickness of described stainless (steel) wire 5 is 0.8mm, grid length and width are 2mm, and described stone plate 3 thickness is 2.8mm, and described adhesive linkage 2 is epoxy resin glue, and described adhesive linkage can also be butadiene-styrene rubber or high-grade resin.
Embodiment 2
A kind of composite plate, it comprises foamed ceramic plate 1, adhesive linkage 2 and stone plate 3 from below to up successively; Described foamed ceramic plate 1 surface is bonding with described stone plate 3 surface by described adhesive linkage 2; Described foamed ceramic plate 1 surface and bottom surface are respectively arranged with stainless (steel) wire 5;
The thickness of described foamed ceramic plate 1 is 90mm, and the thickness of described stainless (steel) wire 5 is 1.3mm, grid length and width are 1.0mm, and described stone plate 3 is marble slab, thickness is 4.5mm, and described adhesive linkage 2 is unsaturated polyester resin.
Embodiment 3
A kind of composite plate, it comprises foamed ceramic plate 1, adhesive linkage 2 and stone plate 3 from below to up successively; Described foamed ceramic plate 1 surface is bonding with described stone plate 3 surface by described adhesive linkage 2; Described foamed ceramic plate 1 surface and bottom surface are respectively arranged with stainless (steel) wire 5;
The thickness of described foamed ceramic plate 1 is 150mm, and the thickness of described stainless (steel) wire 5 is 2mm, grid length and width are 0.5mm, and described stone plate 3 is artificial stone plate, thickness is 7.2mm, and described adhesive linkage 2 is butadiene-styrene rubber.
Embodiment 4
A kind of composite plate, it comprises foamed ceramic plate 1, adhesive linkage 2 and stone plate 3 from below to up successively; Described foamed ceramic plate 1 surface is bonding with described stone plate 3 surface by described adhesive linkage 2; Described foamed ceramic plate 1 surface and bottom surface are respectively arranged with stainless (steel) wire 5;
The thickness of described foamed ceramic plate 1 is 75mm, and the thickness of described stainless (steel) wire 5 is 1.1mm, grid length and width are 1.5mm, and described stone plate 3 is lithotome plate, and thickness is 6.0mm, and described adhesive linkage 2 is epoxy resin glue.
Embodiment 5
A kind of composite plate, it comprises foamed ceramic plate 1, adhesive linkage 2 and stone plate 3 from below to up successively; Described foamed ceramic plate 1 surface is bonding with described stone plate 3 surface by described adhesive linkage 2; Described foamed ceramic plate 1 surface and bottom surface are respectively arranged with stainless (steel) wire 5;
The thickness of described foamed ceramic plate 1 is 120mm, and the thickness of described stainless (steel) wire 5 is 1.8mm, grid length and width are 0.8mm, and described stone plate 3 thickness is 5.5mm, and described adhesive linkage 2 is unsaturated polyester resin.
Embodiment 6
A kind of composite plate, it comprises foamed ceramic plate 1, adhesive linkage 2 and stone plate 3 from below to up successively; Described foamed ceramic plate 1 surface is bonding with described stone plate 3 surface by described adhesive linkage 2; Described foamed ceramic plate 1 surface and bottom surface are respectively arranged with stainless (steel) wire 5;
The thickness of described foamed ceramic plate 1 is 60mm, and the thickness of described stainless (steel) wire 5 is 0.7mm, grid length and width are 1.5mm, and described stone plate 3 is marble slab, thickness is 3.8mm, and described adhesive linkage 2 is butadiene-styrene rubber.
Below know-why of the present utility model is described in conjunction with specific embodiments.These describe just in order to explain principle of the present utility model, and can not be interpreted as the restriction to the utility model protection domain by any way.Based on explanation herein, those skilled in the art does not need to pay performing creative labour can associate other detailed description of the invention of the present utility model, and these modes all will fall within protection domain of the present utility model.
Claims (7)
1. a composite plate, is characterized in that: it comprises foamed ceramic plate, adhesive linkage and stone plate from below to up successively; Described foamed ceramic plate surface is bonding with described stone plate surface by described adhesive linkage; Described foamed ceramic plate surface and bottom surface are respectively arranged with stainless (steel) wire.
2. composite plate according to claim 1, is characterized in that: the surface of described foamed ceramic plate and bottom surface and described stainless (steel) wire directly bond fixing by cementing agent.
3. composite plate according to claim 1, is characterized in that: the thickness of described stainless (steel) wire is 0.5-5mm.
4. composite plate according to claim 3, is characterized in that: the grid of described stainless (steel) wire is long and wide is 1mm-2mm.
5. composite plate according to claim 1, is characterized in that: the thickness of described foamed ceramic plate is 30-150mm.
6. composite plate according to claim 1, is characterized in that: the thickness of described stone plate is 2.5-8mm.
7. composite plate according to claim 1, is characterized in that: described adhesive linkage is epoxy resin glue.