CN204059839U - Three-dimensional vitrified brick - Google Patents
Three-dimensional vitrified brick Download PDFInfo
- Publication number
- CN204059839U CN204059839U CN201420412064.8U CN201420412064U CN204059839U CN 204059839 U CN204059839 U CN 204059839U CN 201420412064 U CN201420412064 U CN 201420412064U CN 204059839 U CN204059839 U CN 204059839U
- Authority
- CN
- China
- Prior art keywords
- patterned layer
- dimensional
- lines
- base material
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of three-dimensional vitrified brick, the front and back of sheet glass base material scribbles the first patterned layer and the second patterned layer respectively, the lines that first patterned layer and the second patterned layer are parallel to each other by many respectively form, lines are straight line or dotted line, be parallel to a wherein limit of described sheet glass base material, and lines are on the front and back oppositely arranged, the second patterned layer scribbles covering layer, the material of the first patterned layer, the second patterned layer and covering layer is high temperature ceramic pigment.The utility model, utilize thickness and the light refraction principle of glass, allow people can observe the different patterns enhanced each other's beauty at diverse location, produce the artistic dynamic three-dimensional effect of tool, and high temperature ceramic pigment is after high-temperature baking, difficult drop-off and fading, color keeps lasting, manufacture craft is simple, reduces cost of production.
Description
Technical field
The utility model relates to architectural decoration material field, is specifically related to three-dimensional vitrified brick.
Background technology
In interior decoration and decoration, in room, the decorative effect of floor tile and walltile should not be underestimated, because of the quality of floor tile and pattern kind various, people can decorate out according to the general layout in room the style liked.Sufficient light is mostly needed in general room, even corridor and entry place more need the decoration that can produce magical effect of shadow, so select vitrified brick just can meet this demand very well, vitrified brick has good light transmission, and easily build dynamic and three-dimensional effect, larger visual impact can be brought also to the aesthetic feeling that people is a feast for the eyes.Vitrified brick can be applicable to exterior wall or partition, provides good daylighting effect, and has the effect in continuity space, no matter be that monolithic inlays use, or full wafer metope uses, and all can have the effect of crucial touch.And vitrified brick has waterproof, fireproof advantage, heat insulation also splendid with soundproof effect.
Vitrified brick is in the market of a great variety, and manufacture craft has larger difference, main following five kinds of modes:
(1) wherein at sheet glass base material simultaneously spray or stamp low temperature solid paint or stereo paint, dry through less than 200 degree temperature, but coating only limitting low-temperature bake, easily can come off and fade, and do not present three-dimensional stereo effect after oven dry;
(2) between two panels sheet glass base material, place the material (as: cloth with space pattern, film etc. containing plastic components), shaping through vacuum high-pressure, but technological process is complicated, cost is high, and product does not really present three-dimensional stereo effect;
(3) carry out computer numerical controlled engraving at surface of plate glass, make glass surface produce three-dimensional concave-convex effect, equipment investment is huge, and efficiency is low, and cost is high, three-dimensional male and fomale(M&F) shortcoming smoothness and natural beauty;
(4) glass is warmed to fusing point and forms glass solution, and be fed into irregular grinding tool, after the demoulding, glass surface presents three-dimensional concave-convex effect.Technique falls behind, and grinding tool has high input, and efficiency is low, and weaken the distinctive sparkling and crystal-clear penetrating characteristic of glass, contaminating air bubbles is more, shortcoming surface gloss and natural beauty;
(5) wherein simultaneously stamp high temp glass ink at sheet glass base material or stick the high temp glass applique of printed pattern, the high temperature sintering more than 600 degree, after sintering, glass is still plane.Then rough surface is suppressed at the other one side mould high temperature of sheet glass base material.Three-dimensional effect can be seen in non-coat side.Mould has high input, and efficiency is low, and cost is large, and glass surface is uneven, is unfavorable for the dirty of cleaning glass surface.
Summary is learnt, current vitrified brick exist pattern three-dimensional not attractive in appearance, coating easily comes off and easily fades, the high in cost of production problem that causes of technological process complexity.
Utility model content
Technical problem to be solved in the utility model is that vitrified brick exists three-dimensional not attractive in appearance, coating easily comes off and easily fades, technological process complexity causes the problem of high in cost of production of pattern.
In order to solve the problems of the technologies described above, the technical scheme that the utility model adopts there is provided a kind of three-dimensional vitrified brick, comprise sheet glass base material, the front and back of described sheet glass base material scribbles the first patterned layer and the second patterned layer respectively, the lines that described first patterned layer and described second patterned layer are parallel to each other by many respectively form, described lines are straight line or dotted line, and be parallel to a wherein limit of described sheet glass base material, described lines are on the front and back oppositely arranged, described second patterned layer scribbles covering layer, described first patterned layer, the material of the second patterned layer and covering layer is high temperature ceramic pigment.
In above-mentioned three-dimensional vitrified brick, described lines are on the front and back straight line or dotted line.
In above-mentioned three-dimensional vitrified brick, described lines one is on the front and back straight line, and another kind is dotted line.
In above-mentioned three-dimensional vitrified brick, described lines protrude from the surface 0.2 ~ 0.4mm of described sheet glass base material.
In above-mentioned three-dimensional vitrified brick, the live width of described lines is 0.3mm-0.6mm, and spacing is 0.4mm-0.8mm.
In above-mentioned three-dimensional vitrified brick, the thickness of described first patterned layer, the second patterned layer and described covering layer is different, and the thickness of described covering layer is more than or equal to the thickness of described second patterned layer.
The utility model, the front and back of sheet glass base material scribbles the first patterned layer and the second patterned layer respectively, second patterned layer scribbles covering layer, the lines that first patterned layer and described second patterned layer are parallel to each other by many respectively form, lines are straight line or dotted line, and described lines are on the front and back oppositely arranged.Utilize thickness and the light refraction principle of glass, allow people can observe the different patterns enhanced each other's beauty at diverse location, the design of line image is coordinated to produce the artistic dynamic three-dimensional effect of tool, and high temperature ceramic pigment is after high-temperature baking, difficult drop-off and fading, color keeps lasting, and manufacture craft is simple, reduces cost of production.
Accompanying drawing explanation
Fig. 1 is the front view of embodiment one of the present utility model;
Fig. 2 is the right view of embodiment one of the present utility model;
Fig. 3 is the front view of embodiment two of the present utility model;
Fig. 4 is the structural representation of embodiment three of the present utility model;
Fig. 5 is the front view of embodiment four of the present utility model.
Detailed description of the invention
The technical scheme that the utility model adopts there is provided a kind of three-dimensional vitrified brick, front and back scribbles the first and second patterned layer respectively, the back side also covers and scribbles covering layer, utilizes thickness and the light refraction principle of glass, allows people can observe the different patterns enhanced each other's beauty at diverse location, produce the artistic dynamic three-dimensional effect of tool, and high temperature ceramic pigment is after high-temperature baking, should not come off and fade, color keeps lasting, and manufacture craft is simple, reduces cost of production.Below in conjunction with specific embodiment and Figure of description, the utility model is described in detail.
As shown in Figure 2, the three-dimensional vitrified brick that the utility model provides comprises sheet glass base material 1, first patterned layer 2, second patterned layer 3 and covering layer 4.
First patterned layer 2, second patterned layer 3 is coated in the front and back of sheet glass base material 1 respectively, the outside of the second patterned layer 3 also covers and scribbles covering layer 4, first patterned layer 2, second patterned layer 3 and covering layer 4 all use the printing of paste high temperature ceramic pigment to form, the lines that first patterned layer 2 and the second patterned layer 3 are parallel to each other by many respectively form, and the color of covering layer 4 and the first patterned layer 2, the color of the second patterned layer 3 is different, covering layer 4 is equivalent to for three-dimensional vitrified brick is provided with background color, thus set off the first patterned layer 2, the pattern of the second patterned layer 3 produces more clear bright and beautiful and in picturesque disorder visual effect.
The lines of the first patterned layer 2, second patterned layer 3 protrude from the surface 0.2 ~ 0.4mm of sheet glass base material 1, and make the front of three-dimensional vitrified brick have antiskid function, and pattern can be made more three-dimensional, visual effect is stronger.The thickness of the first patterned layer 2, second patterned layer 3 can adjust as required.
The live width of lines is 0.3mm-0.6mm, and spacing is the combination of 0.4mm-0.8mm, various live width and spacing, can produce different visual effects, can adjust as required.
In addition, the line color of the first patterned layer 2, second patterned layer 3 can be different, and the line color of the second patterned layer 3 can change, and every bar line segment can be interrupted incoherent line segment by many and form, thus can the various pattern form of design forming, as animal flowers and plants etc.
The utility model can obtain with following manufacture method manufacture, and concrete steps are as follows:
Step one, is cut into the sheet glass base material of preset shape, and grinds seamed edge and corner angle by glass raw material;
Further, the thickness of the former material of glass is between 4mm ~ 12mm.
Step 2, the high temperature ceramic pigment of paste is adopted to form the first patterned layer and the second patterned layer at the front and back silk-screen of sheet glass base material respectively, the lines that first patterned layer and the second patterned layer are parallel to each other by many respectively form, lines are straight line or dotted line, and lines are on the front and back oppositely arranged;
Further, brush one times pattern in the high temperature ceramic pigment print of glass baseplate back side paste and form the second patterned layer, and then the high temperature ceramic pigment printing the paste playing covering effect for twice forms covering layer, brush one times pattern in the high temperature ceramic pigment print of sheet glass base material front paste and form the first patterned layer.
Further, for second patterned layer at the glass baseplate back side, its coating weight is at 120g/m
2~ 280g/m
2between.
Step 3, to the sheet glass base material baking after step 2 process 20 ~ 30 minutes at the temperature of 100 DEG C to 150 DEG C, makes high temperature ceramic pigment fix;
Step 4, sheet glass base material after step 3 process is put into high temperature furnace, sinter at the high temperature sintering temperature of the 3rd default value to the 4th default value, high temperature ceramic pigment is firmly attached to the front and back of sheet glass base material, and three-dimensional vitrified brick is shaped;
Further, the 3rd default value preferably 600 DEG C, the 4th default value preferably 800 DEG C.
Step 5, adopts cold wind to be cooled to room temperature the three-dimensional vitrified brick sent out in high temperature furnace;
Step 6, carries out surfacing.
Embodiment 1 (straight line is to straight line)
Select thickness to be the former material of glass of 8mm, and be cut into the sheet glass base material of preset shape, and seamed edge and corner angle are ground;
Brush one times straight-line pattern in the high temperature ceramic pigment print of glass baseplate back side paste and form the second patterned layer, and then the high temperature ceramic pigment printing the paste playing covering effect for twice forms covering layer, brush one times straight-line pattern in the high temperature ceramic pigment print of sheet glass base material front paste and form the first patterned layer, the live width of lines is 0.4mm, spacing is 0.8mm, the thickness of the first patterned layer and the second layer is 0.3mm, and coating weight is 200g/m
2, the thickness of covering layer is 0.6mm;
At the temperature of 120 DEG C, 30 minutes are toasted to the sheet glass base material after above-mentioned process, high temperature ceramic pigment is fixed;
Then sheet glass base material is put into high temperature furnace, sinter at the high temperature sintering temperature of 700 DEG C, high temperature ceramic pigment is firmly attached to the front and back of sheet glass base material, and three-dimensional vitrified brick is shaped;
By progressive to room temperature from the three-dimensional vitrified brick sent out in high temperature furnace;
Carry out surfacing, remove burr and make any surface finish.
As shown in Figure 1, the first patterned layer 2 and the second patterned layer 3 are many straight lines parallel to each other, and the linear position of front and back is relative, and the second patterned layer 3 is identical or different with the first patterned layer 2 color, can present simple air and be rich in the luxurious visual effect felt.
Embodiment 2 (dotted line is to dotted line)
First patterned layer 2 and the second patterned layer 3 are dashed line shape, and other steps are identical with embodiment 1.
As shown in Figure 3, the first patterned layer 2 and the second patterned layer 3 are many dotted lines parallel to each other, and the linear position of front and back is relative, and the second patterned layer 3 is identical or different with the first patterned layer 2 color, can present the visual effect of simple warm romance again.
Embodiment 3 (dotted line is to straight line)
First patterned layer 2 and the second patterned layer 3 are respectively straight line and dashed line shape, and other steps are identical with embodiment 1.
As shown in Figure 4, the first patterned layer 2 is arranged and point-like parallel to each other for interval, and patterned layer 3 is for interval setting and straight line parallel to each other, identical or different with patterned layer 2 color, can present the neatly lucid and lively visual effect not losing again charm.
Embodiment 4 (fish shape pattern)
First patterned layer 2 and the second patterned layer 3 are rectilinear form, wherein live width is 0.3mm, spacing is 0.6mm, first patterned layer 2 is many straight lines parallel to each other, but the rectilinear form of the second patterned layer 3 has unique features, every bar straight line by many conllinear but incoherent line segment form, and can different colours be established at the line segment of zones of different, as the red line segment be parallel to each other with many being combined into the shape of fish in the present embodiment, the end points of many line segments forms red fish shape profile, the wave of seawater is combined to form again by the line segment of blueness, formed between the end points of many line segments of wave and the line segment end points of fish shape and there is spacing, other steps are identical with embodiment 1.So just can form the situation that lively fish plays in the water.The visual effect that gracefulness has classical beauty can be presented.
Learn thus, the utility model can produce the artistic dynamic three-dimensional effect of tool, and high temperature ceramic pigment is after high-temperature baking, difficult drop-off and fading, color keeps lasting, and manufacture craft is simple, reduce cost of production, efficiently solve current three-dimensional vitrified brick field Problems existing.
The utility model is not limited to above-mentioned preferred forms, and anyone should learn the structure change made under enlightenment of the present utility model, and every have identical or close technical scheme with the utility model, all falls within protection domain of the present utility model.
Claims (6)
1. three-dimensional vitrified brick, it is characterized in that, comprise sheet glass base material, the front and back of described sheet glass base material scribbles the first patterned layer and the second patterned layer respectively, the lines that described first patterned layer and described second patterned layer are parallel to each other by many respectively form, described lines are straight line or dotted line, and be parallel to a wherein limit of described sheet glass base material, described lines are on the front and back oppositely arranged, described second patterned layer scribbles covering layer, and the material of described first patterned layer, the second patterned layer and covering layer is high temperature ceramic pigment.
2. three-dimensional vitrified brick as claimed in claim 1, is characterized in that, described lines are on the front and back straight line or dotted line.
3. three-dimensional vitrified brick as claimed in claim 1, is characterized in that, described lines one is on the front and back straight line, and another kind is dotted line.
4. three-dimensional vitrified brick as claimed in claim 1, is characterized in that, described lines protrude from the surface 0.2 ~ 0.4mm of described sheet glass base material.
5. three-dimensional vitrified brick as claimed in claim 1, is characterized in that, the live width of described lines is 0.3mm-0.6mm, and spacing is 0.4mm-0.8mm.
6. three-dimensional vitrified brick as claimed in claim 1, is characterized in that, the thickness of described first patterned layer, the second patterned layer and described covering layer is different, and the thickness of described covering layer is more than or equal to the thickness of described second patterned layer.