CN1944324A - 城市通沟污泥的处理方法 - Google Patents
城市通沟污泥的处理方法 Download PDFInfo
- Publication number
- CN1944324A CN1944324A CNA200610117322XA CN200610117322A CN1944324A CN 1944324 A CN1944324 A CN 1944324A CN A200610117322X A CNA200610117322X A CN A200610117322XA CN 200610117322 A CN200610117322 A CN 200610117322A CN 1944324 A CN1944324 A CN 1944324A
- Authority
- CN
- China
- Prior art keywords
- solidifying agent
- cement
- mud
- ditch mud
- sludge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种城市通沟污泥的处理方法,先将通沟污泥进行风干及降解,使污泥含水率降低至20%以下;然后采用由水泥、复合活性掺合料按一定比例组成的固化剂,对通沟污泥进行固化。固化剂的组成及重量百分比为:水泥30~50,粉煤灰10~30,矿渣10~30,钢渣5~20,沸石3~10;经配料混合均匀后制得污泥固化剂。然后制备污泥固化体,固化体的组成及重量百分比为:通沟污泥20~40,上述的固化剂15~30,砂子30~50;将各材料按规定称重后,加入少量水,经一定时间的搅拌混合均匀后,按国家标准GB/T17671-1999《水泥砂浆强度检验方法》进行成型、养护,最终得到通沟污泥的砂浆固化体。该固化体主要可用作路用材料或建筑材料。
Description
技术领域
本发明涉及一种城市通沟污泥的处理方法,属固体废弃物综合利用技术领域。
背景技术
城市污泥传统的处理方法有填埋、焚烧、排海、农用等,但这些方法都存在一定弊端,且污泥也没有达到有效的资源化。从可持续发展的角度看,污泥的处置必须遵循资源化的原则,在考虑环境效益和社会效益的前提下,尽可能提高其经济价值。现阶段城市污泥资源化的主要途径是土地利用和建材利用为主,其中污泥作为建材或筑路材料则具有很大经济的价值,其他处于试验阶段的污泥资源化方法也有一些,但是我国污泥的资源化利用技术离大规模的推广应用还有很大的距离。
发明内容
本发明的目的是提供一种城市通沟污泥的处理方法。本发明的另一目的是将通沟污泥通过固化作用制成固化体,用作路用材料或建筑材料,以达到资源化利用。
本发明一种城市通沟污泥的处理方法,其特征在于该处理方法包括有以下几个步骤:
a.首先制备好污泥固化剂
固化剂由水泥和复合活性掺合料组成,其具体组成成分和重量百分比为:
水泥 30~50,为42.5标号普通硅酸盐水泥;
粉煤灰 10~30 为II级粉煤灰;
矿渣 10~30 比表面积为400m2/kg的磨细微粉;
钢渣 5~20 比表面积为500m2/kg的磨细微粉;
沸石 3~10 其细度为300目;
把上述各材料按规定比例称重后,放入搅拌釜中,经一定时间的搅拌混和均匀后,即得到污泥固化剂;备用;
b.取一定量的通沟污泥,使其自然风干及降解,并使污泥的含水率降低至20%以下;
c.在上述的通沟污泥中,加入由上述的水泥及复合活性掺合料组成的固化剂,再加入一定量的砂子,以制得使通沟污泥固化的固化体材料;该固化体材料的组成及重量百分比如下:
通沟污泥 20~40%;
固化剂 15~30%;
砂子 30~50%,其细度模数为2.6~2.8的中砂;
将上述各材料按规定比例称重后,再加入少量水,经一定时间的搅拌混合均匀后,按照规定标准GB/T17671-1999《水泥砂浆强度检验方法》进行成型、养护,最终得到通沟污的砂浆固化体;该固化体主要用作路用材料或建筑材料。
本发明的特点如下:
1、采用以水泥和粉煤灰、矿渣、钢渣等工业废渣制成的固化剂来固化城市通沟污泥,达到了以废治废的目的,具有一定的环境效益、社会经济效益和经济效益。
2、实现了城市通沟污泥无害化处理,并达到固体废弃物的资源化利用的要求。
3、本发明制得的固化体可大量用于路用材料或建筑材料。
4、本发明的污泥处理方法,其工艺简单、易实施、可操作性强、易实现产业化生产。
具体实施方式
现将本发明的具体实施例叙述于后。
实施例1
(1)首先制备好污泥固化剂
本实施例中,以制备10千克污泥固化剂为例:分别称取水泥4千克、粉煤灰2千克、矿渣2千克、钢渣1.5千克、沸石0.5千克,将这些材料放入搅拌釜中,经15分钟搅拌混合均匀后,即得污泥固化剂,备用。
(2)取一定量的通沟污泥,使其自然风干及降解,使污泥中的含水率降低至20%以下。
(3)制备污泥固化体
称取上述通沟污泥5.4千克、砂子8.1千克、固化剂4.5千克,另外加入水2.25千克,共同搅拌混合均匀;按照规定标准GB/T17671-1999《水泥砂浆强度检验方法》进行成型、养护,即得到通沟污泥的砂浆固化体。
经测试,养护28天后,该固化体的材料力学性能为:抗压强度为28.8MPa,抗折强度为5.4MPa。固化体浸出毒性测试满足国家标准《污水综合排放标准》(GB8978-1996)的要求,无二次污染。
Claims (1)
1.一种城市通沟污泥的处理方法,其特征在于该处理方法包括有以下几个步骤:
a.首先制备好污泥固化剂
固化剂由水泥和复合活性掺合料组成,其具体组成成分和重量百分比为:
水泥 30~50, 为42.5标号普通硅酸盐水泥;
粉煤灰 10~30 为II级粉煤灰;
矿渣 10~30 比表面积为400m2/kg的磨细微粉;
钢渣 5~20 比表面积为500m2/kg的磨细微粉;
沸石 3~10 其细度为300目;
把上述各材料按规定比例称重后,放入搅拌釜中,经一定时间的搅拌混和均匀后,即得到污泥固化剂,备用;
b.取一定量的通沟污泥,使其自然风干及降解,并使污泥的含水率降低至20%以下;
c.在上述的通沟污泥中,加入由上述的水泥及复合活性掺合料组成的固化剂,再加入一定量的砂子,以制得使通沟污泥固化的固化体材料;该固化体材料的组成及重量百分比如下:
通沟污泥 20~40%;
固化剂 15~30%;
砂子 30~50%,其细度模数为2.6~2.8的中砂;
将上述各材料按规定比例称重后,再加入少量水,经一定时间的搅拌混合均匀后,按照规定标准GB/T17671-1999《水泥砂浆强度检验方法》进行成型、养护,最终得到通沟污的砂浆固化体;该固化体主要用作路用材料或建筑材料。