CN1888176A - Bamboo carbon dacron fiber and viscose rayon blended yarn and producing method thereof - Google Patents
Bamboo carbon dacron fiber and viscose rayon blended yarn and producing method thereof Download PDFInfo
- Publication number
- CN1888176A CN1888176A CN 200610103794 CN200610103794A CN1888176A CN 1888176 A CN1888176 A CN 1888176A CN 200610103794 CN200610103794 CN 200610103794 CN 200610103794 A CN200610103794 A CN 200610103794A CN 1888176 A CN1888176 A CN 1888176A
- Authority
- CN
- China
- Prior art keywords
- bamboo carbon
- blended yarn
- carbon dacron
- viscose
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a bamboo carbon polyester fibre and viscose fibre blended yarn and its preparation method. Said blended yarn is made up by using 20-40% of bamboo carbon polyester fibre and 60-80% of viscose fibre through a certain preparation method. The performance indexes of said blended yarn are as follows: single yarn breaking strength is 9.0-18.0 cN/tex, the coefficient of variation CV value of single yarn breaking strength is 8.0-22.0% and the coefficient of variation CV value of yarn evenness is 12.5-24.0%.
Description
One, technical field:
The present invention relates to a kind of yarn that contains bamboo charcoal particle and preparation method thereof, more particularly relate to a kind of bamboo carbon dacron fiber and viscose fiber blended yarn and preparation method thereof.
Two, background technology
Bamboo carbon dacron fiber has absorption and eliminates the peculiar smell function, has far infrared, anion, uvioresistant, antimicrobial health care function.But the fabric that utilizes pure bamboo carbon terylene to make, hygroscopicity is poor, and feel is not soft, and comfortable function is not good.
Pure viscose fiber fabric good hygroscopicity, soft, comfortable function is good, but wet strength is low, and shrinking deformation is big.
Three, summary of the invention
One of purpose of the present invention provides a kind of have absorption elimination peculiar smell, far infrared, anion, uvioresistant and antimicrobial health care function, and yarn or fabric moisture are strong, the feel particularly soft, warming, bamboo carbon dacron fiber that comfortable function is good and viscose fiber blended yarn.
Two of purpose of the present invention provides the preparation method of a kind of bamboo carbon dacron fiber and viscose fiber blended yarn.
These and other purpose of the present invention will further embody and set forth by following detailed description and explanation.
The objective of the invention is to realize by following technical proposals:
Bamboo carbon dacron fiber of the present invention and viscose fiber blended yarn, form by bamboo carbon dacron fiber and viscose, wherein, bamboo carbon dacron fiber and viscose fiber blending percentage by weight are 20-40: 60-80, the blended yarn performance indications are: single thread fracture strength 9.0-18.0cN/tex, single thread fracture strength coefficient of variation CV value 8.0-22.0%, strip dry uniformity variant coefficient CV value 12.5-24.0%.
Further, bamboo carbon dacron fiber of the present invention and viscose fiber blended yarn, wherein the blended yarn performance indications are: single thread fracture strength 9.0-16.0cN/tex, single thread fracture strength coefficient of variation CV value 8.0-15.0%, strip dry uniformity variant coefficient CV value 12.5-18.0%.
In the preparation method of bamboo carbon dacron fiber of the present invention and viscose fiber blended yarn, in the mixed cotton step, do not use automatic plucker; Opener adopts kirschner beater in the opener step, and this kirschner beater speed is 500-600 rev/min, and single beater scutcher adopts kirschner beater, and this kirschner beater speed is 700-900 rev/min; In the comb and parallel cotton fibers prior to spinning step cylinder speed 270-350 of carding machine rev/min, licker-in speed 700-800 rev/min, 5 space and are respectively 0.30mm, 0.28mm, 0.28mm, 0.28mm and 0.30mm from import to outlet between cylinder-cover plate; Drawing frame adopts three road drawing frames in the drafting step, and each road drawing frame all adopts the feeding of 8 one threads and 8 times of drawing-offs.
Compared with prior art, blended yarn that employing bamboo carbon dacron fiber of the present invention and viscose are spun into and the fabric that makes, not only having absorption eliminates outside peculiar smell, far infrared, anion, uvioresistant and the antimicrobial health care function, and fabric moisture is good, the feel particularly soft, warming, comfortable function is good, is applicable to underwear and the socks product made.
In the present invention, the bamboo carbon dacron fiber of use has absorption and eliminates the peculiar smell function, and has far infrared, anion, uvioresistant and antimicrobial health care function.
The physical index of bamboo carbon dacron fiber: filament line density 1.7D, length 38mm, fracture strength 3.75cN/dtex, elongation at break are 25.0%, than resistance 5.56 * 10
6Ω cm, regain 0.9%, crispation number are 6.8/25mm, crimp percent is that 6.1%, 180 ℃ of dry-hot shrinkage is 8.5%; Bamboo carbon dacron fiber can and be weaved Co., Ltd and buy by jiangsu wuxi hundred.
In the present invention, the viscose of use has good hygroscopicity, soft and characteristics that comfortable function is good.The physical index of viscose is: length 38mm, fineness 1.5-2.0D; Dry strength 1.8-2.5g/D, dried elongation at break 15-20%; Viscose can be by buying on the market.
The manufacture method of bamboo carbon dacron fiber and viscose fiber blended yarn is further described below:
Spinning technological process:
The opening picking associating unit that opener → A092A hopper feeder → A076C single beater scutcher is formed is made volume → A186F → carding machine and is made bamboo carbon dacron fiber and viscose blended sliver → A272F (mix and one) drawing frame → A272F (mix and two) drawing frame → A272F (mix also three) drawing frame → A454 simplex flyer frame → FA506 fine spining machine → 1332MD bobbin winder
Technological requirement:
(1), bamboo carbon dacron fiber and viscose fiber blending percentage by weight are 20-40: 60-80;
(2), except that the technological requirement of routine, the present invention is because bamboo carbon dacron fiber contains assorted few, and in order to prevent fibre damage, so the improvement process conditions in opening picking associating unit are that (1) omits automatic plucker, (2) opener adopts kirschner beater promptly to adopt A036C card wire cylinder opener, this machine kirschner beater speed is 500-600 rev/min, and single beater scutcher also must adopt kirschner beater promptly to adopt the A076C single beater scutcher, and this machine kirschner beater speed is 700-900 rev/min; The present invention is in order to prevent that the bigger generation static of bamboo carbon dacron fiber and viscose and pin tooth coefficient of friction is easily around cylinder with in order to prevent fibre damage, so the improvement process conditions of carding machine are to reduce cylinder and licker-in speed, 270-350 rev/min of its cylinder speed, licker-in speed 700-800 rev/min, 5 easily amplifications of spacing are respectively 0.30mm, 0.28mm, 0.28mm, 0.28mm, 0.30mm from import to outlet between cylinder-cover plate; The present invention does not produce aberration in order to guarantee finished product, must improve the even immixture of mixing in doubling step, and the improvement process conditions of drawing frame are to adopt three road drawing frames for this reason, and each road drawing frame all adopts the feeding of 8 one threads and 8 times of drawing-offs.
The performance indications of bamboo carbon dacron fiber and viscose fiber blended yarn are as follows:
Single thread fracture strength: 9.0-18.0cN/tex;
Single thread fracture strength coefficient of variation CV value: 8.0-22.0%;
Strip dry uniformity variant coefficient CV value: 12.5-24.0%;
Cotton junction grain number: no more than 10-85 grain/gram;
Cotton junction impurity sum: no more than 10-95 grain/gram;
Blended yarn twist with the fingers to: adopt Z to twist with the fingers;
Number number twist factor: 280-380.
The performance indications of bamboo carbon dacron fiber and viscose fiber blended yarn fabric are as follows:
Dry fabric weight: 128-180g/m
2
Bursting strength: 33-56kg;
Color fastness to washing: 3-4 level;
Washing shrinkage: ± 2-± 3.
All raw material of Shi Yonging and the Processes and apparatus do not described etc. all are conventional uses in the present invention, maybe can buy from market.In the present invention, refer in particular to as non-, all amount, percentages are unit of weight.
Below in conjunction with embodiment the present invention is carried out concrete description.As known by the technical knowledge, the present invention can realize by other the embodiment that does not break away from its spiritual essence or essential feature.Therefore, following embodiment with regard to each side, all just illustrates, and is not only.All within the scope of the present invention or the change that is equal in the scope of the present invention all be included in the invention.
Four, the specific embodiment
Embodiment 1:
Propping up with 32 English is example, and bamboo carbon dacron fiber and viscose fiber blending percentage by weight are 40: 60.Opener adopts kirschner beater promptly to adopt A036C card wire cylinder opener, and this machine kirschner beater speed is 500-600 rev/min, and single beater scutcher adopts kirschner beater promptly to adopt the A076C single beater scutcher, and this machine kirschner beater speed is 700-900 rev/min.The cylinder speed 270-350 of carding machine rev/min, licker-in speed 700-800 rev/min, 5 easily amplifications of spacing are respectively 0.30mm, 0.28mm, 0.28mm, 0.28mm, 0.30mm from import to outlet between cylinder-cover plate; Drawing frame adopts three road drawing frames, and each road drawing frame all adopts the feeding of 8 one threads and 8 times of drawing-offs.Through spinning technological process provided by the invention with process 32 English that spinned and prop up blended yarn, its single thread fracture strength is 15.0cN/tex after tested, single thread fracture strength coefficient of variation CV value is 12.4%, strip dry uniformity variant coefficient CV value is 14.4%, cotton junction grain number is 11 a/gram, and cotton junction impurity adds up to 11/gram; The knitted fabric that makes carries out the far infrared test, and normal emittance reaches 80%, 3500/cubic centimetre of anion emission amounts, and rate of ultraviolet shield 90%, ammonia adsorption rate 20% has the peculiar smell function of elimination and antimicrobial health care function; The knitted fabric hygroscopicity is strong, and is soft, and comfortable function is good, the intensity height, and dimensionally stable is applicable to underwear and socks product.
Embodiment 2:
Propping up with 32 English is example, and bamboo carbon dacron fiber and viscose fiber blending percentage by weight are 30: 70.Opener adopts kirschner beater promptly to adopt A036C card wire cylinder opener, and this machine kirschner beater speed is 500-600 rev/min, and single beater scutcher adopts kirschner beater promptly to adopt the A076C single beater scutcher, and this machine kirschner beater speed is 700-900 rev/min.The cylinder speed 270-350 of carding machine rev/min, licker-in speed 700-800 rev/min, 5 easily amplifications of spacing are respectively 0.30mm, 0.28mm, 0.28mm, 0.28mm, 0.30mm from import to outlet between cylinder-cover plate; Drawing frame adopts three road drawing frames, and each road drawing frame all adopts the feeding of 8 one threads and 8 times of drawing-offs.Through spinning technological process provided by the invention with process 32 English that spinned and prop up blended yarn, its single thread fracture strength is 14.3cN/tex after tested, single thread fracture strength coefficient of variation CV value is 12.7%, strip dry uniformity variant coefficient CV value is 15.8%, cotton junction grain number is 10 a/gram, and cotton junction impurity adds up to 10/gram; The knitted fabric that makes carries out the far infrared test, and normal emittance reaches 85%, 4000/cubic centimetre of anion emission amounts, and rate of ultraviolet shield 95%, ammonia adsorption rate 22% has the peculiar smell function of elimination and antimicrobial health care function; The knitted fabric hygroscopicity is strong, and is soft, and comfortable function is good, the intensity height, and dimensionally stable is applicable to underwear and socks product.
Embodiment 3:
Propping up with 32 English is example, and charcoal carbon polyester fiber and viscose fiber blending percentage by weight are 20: 80.Opener adopts kirschner beater promptly to adopt A036C card wire cylinder opener, and this machine kirschner beater speed is 500-600 rev/min, and single beater scutcher adopts kirschner beater promptly to adopt the A076C single beater scutcher, and this machine kirschner beater speed is 700-900 rev/min.The cylinder speed 270-350 of carding machine rev/min, licker-in speed 700-800 rev/min, 5 easily amplifications of spacing are respectively 0.30mm, 0.28mm, 0.28mm, 0.28mm, 0.30mm from import to outlet between cylinder-cover plate; Drawing frame adopts three road drawing frames, and each road drawing frame all adopts the feeding of 8 one threads and 8 times of drawing-offs.Through spinning technological process provided by the invention with process 32 English that spinned and prop up blended yarn, its single thread fracture strength is 14.0cN/tex after tested, single thread fracture strength coefficient of variation CV value is 13.1%, strip dry uniformity variant coefficient CV value is 16.3%, cotton junction grain number is 8 a/gram, and cotton junction impurity adds up to 8/gram; The knitted fabric that makes carries out the far infrared test, and normal emittance reaches 87%, 4500/cubic centimetre of anion emission amounts, and rate of ultraviolet shield 98%, ammonia adsorption rate 25% has the peculiar smell function of elimination and antimicrobial health care function; The knitted fabric hygroscopicity is strong, and is soft, and comfortable function is good, the intensity height, and dimensionally stable is applicable to underwear and socks product.
Claims (6)
1, a kind of bamboo carbon dacron fiber and viscose fiber blended yarn, it is characterized in that forming by bamboo carbon dacron fiber and viscose, wherein, bamboo carbon dacron fiber and viscose fiber blending percentage by weight are 20-40: 60-80, the blended yarn performance indications are: single thread fracture strength 9.0-18.0cN/tex, single thread fracture strength coefficient of variation CV value 8.0-22.0%, strip dry uniformity variant coefficient CV value 12.5-24.0%.
2, bamboo carbon dacron fiber according to claim 1 and viscose fiber blended yarn, it is characterized in that the blended yarn performance indications are: single thread fracture strength 9.0-16.0cN/tex, single thread fracture strength coefficient of variation CV value 8.0-15.0%, strip dry uniformity variant coefficient CV value 12.5-18.0%.
3, the preparation method of bamboo carbon dacron fiber according to claim 1 and 2 and viscose fiber blended yarn is characterized in that not using automatic plucker in the mixed cotton step.
4, the preparation method of bamboo carbon dacron fiber according to claim 1 and 2 and viscose fiber blended yarn, it is characterized in that opener adopts kirschner beater in the opener step, this kirschner beater speed is 500-600 rev/min, single beater scutcher adopts kirschner beater, and this kirschner beater speed is 700-900 rev/min.
5, the preparation method of bamboo carbon dacron fiber according to claim 1 and 2 and viscose fiber blended yarn, it is characterized in that cylinder speed 270-350 rev/min of carding machine in the comb and parallel cotton fibers prior to spinning step, licker-in speed 700-800 rev/min, 5 space and are respectively 0.30mm, 0.28mm, 0.28mm, 0.28mm and 0.30mm from import to outlet between cylinder-cover plate.
6, the preparation method of bamboo carbon dacron fiber according to claim 1 and 2 and viscose fiber blended yarn is characterized in that drawing frame adopts three road drawing frames in the drafting step, and each road drawing frame all adopts the feeding of 8 one threads and 8 times of drawing-offs.