CN1872777A - Inorganic, elastic, heatproof dope for terrace - Google Patents

Inorganic, elastic, heatproof dope for terrace Download PDF

Info

Publication number
CN1872777A
CN1872777A CNA2006100447307A CN200610044730A CN1872777A CN 1872777 A CN1872777 A CN 1872777A CN A2006100447307 A CNA2006100447307 A CN A2006100447307A CN 200610044730 A CN200610044730 A CN 200610044730A CN 1872777 A CN1872777 A CN 1872777A
Authority
CN
China
Prior art keywords
elastic
heatproof
dope
terrace
inorganic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2006100447307A
Other languages
Chinese (zh)
Other versions
CN100436363C (en
Inventor
李广志
夏文强
钟涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Zerui New Material Technology Co., Ltd.
Original Assignee
SITAIPULI HI-NEW BUILDING MATERIALS Co Ltd SHANDONG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SITAIPULI HI-NEW BUILDING MATERIALS Co Ltd SHANDONG filed Critical SITAIPULI HI-NEW BUILDING MATERIALS Co Ltd SHANDONG
Priority to CNB2006100447307A priority Critical patent/CN100436363C/en
Publication of CN1872777A publication Critical patent/CN1872777A/en
Application granted granted Critical
Publication of CN100436363C publication Critical patent/CN100436363C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

This invention relates to an elastic inorganic floor material. The material is composed of cement 50-100 wt. parts, sand 200-400 wt. parts, and glass microbeads 200-400 wt. parts. The material is also composed of foaming agent 1 wt.%, polymer emulsion 10-30 wt.%, water reducer 0.7 wt.%, and cellulose 0.1-0.4 wt.%. The material has such advantages as good wear resistance, high self-leveling ability and high thermal insulating ability, and is environmentally friendly.

Description

Inorganic, elastic, heatproof dope for terrace
Technical field
The present invention relates to a kind of floor material, specifically is a kind of inorganic, elastic, heatproof dope for terrace.
Background technology
The floor material that uses is that material cement, sand and small amounts of additives stir, mix composition at present, and its defective is easy cracking, plays dirt, dusting, is difficult to satisfy terrace service requirementss such as factory building, laboratory, office, room.
Summary of the invention
Purpose of the present invention is exactly the defective that exists at prior art, provides a kind of and does not ftracture, the inorganic, elastic, heatproof dope for terrace of environmental protection, insulation.
Its technical scheme is: the raw material that comprises following weight part: cement 50-100, sand 200-400, glass microballon 200-400 and account for all material raw materials by weight percent: whipping agent 1%, polymer emulsion 10-30%, water reducer 0.7%, Mierocrystalline cellulose 0.1-0.4% form.
Described cement is silicate cement, the particle diameter 2-6 millimeter of sand, glass microballon particle diameter 80-200 order, whipping agent is that the hydrolysis of solid content 20% is from domestic animal blood foaming agent liquid, polymer emulsion is the ACRYLIC EMULSION of solid content 40%, water reducer is a how sodium sulfonate pressed powder of polymethine, and Mierocrystalline cellulose is the Natvosol pressed powder.
Products characteristics of the present invention: include the insulation material, wear-resisting except having terrace paint, suffer from one's own actions outside the equality performance, also have heat insulation function, can be used as the floor heating material and use, energy-saving heat preserving replaces leveling mortar, one-object-many-purposes, environmental protection and energy saving.Terraces such as the factory building of having relatively high expectations in suitable various ground, laboratory, office, room use.
The key technical indexes:
Project Index
Degree of mobilization Initial mm ≥200
15min mm ≥190
Ultimate compression strength 3d MPa ≥14
7d MPa ≥21
28d MPa ≥35
Wear resistance g ≤0.5
Shrinking percentage % ≤0.1
Working conditions ℃ ≥5
Specific embodiment (composition of raw materials)
Title material Specification Ratio range (example 1) Ratio range (example 2) Ratio range (example 3) Material function and effect
Cement 425R silicate 50 75 100 Bonding
Sand The 2-6 millimeter 200 300 400 Filler
Glass microballon The 80-200 order 200 300 400 The insulation filler
Whipping agent Liquid, solid content 20% 1％ 1％ 1％ The bleed bubbling
ACRYLIC EMULSION Solid content 40%, oyster white 10％ 20％ 30％ Tackify
Polymethine is sodium sulfonate how Pressed powder 0.7％ 0.7％ 0.7％ Strengthen
Natvosol Pressed powder 0.14％ 0.24％ 0.4％ Regulate setting time
Powder in the prescription uses the duplex cone-type mixer, earlier cement and fine sand is added mixing machine, machines, mixed 5-10 minute, and added other stopping composition then, continue to mix 5-10 minute, observe color and interface and whether mix, if it is think the inhomogeneous mixing time that continues to prolong, last, with addings such as Mierocrystalline celluloses, continue to mix 5-10 minute, finally be discharged in the woven bag of the waterproof and dampproof plastic film of liner, and the sealing sack, the into water that prevents to make moist, stand-by.
The liquid polymers emulsion is put into the plastics or the metal bucket of designated volume, sealing, the on-the-spot unlatching, pour agitation vat into,, use electric blender, fully stir according to formula rate, to evenly,, can add entry in right amount the denseness of adhesive mortar is regulated according to temperature and construction requirement.

Claims (2)

1, a kind of inorganic, elastic, heatproof dope for terrace, it is characterized in that comprising the raw material of following weight part: cement 50-100, sand 200-400, glass microballon 200-400 and account for all material raw materials by weight percent: whipping agent 1%, polymer emulsion 10-30%, water reducer 0.7%, Mierocrystalline cellulose 0.1-0.4% form.
2, inorganic, elastic, heatproof dope for terrace according to claim 1, it is characterized in that: described cement is silicate cement, the particle diameter 2-6 millimeter of sand, glass microballon particle diameter 80-200 order, whipping agent is that the hydrolysis of solid content 20% is from domestic animal blood foaming agent liquid, polymer emulsion is the ACRYLIC EMULSION of solid content 40%, and water reducer is a how sodium sulfonate pressed powder of polymethine, and Mierocrystalline cellulose is the Natvosol pressed powder.
CNB2006100447307A 2006-06-10 2006-06-10 Inorganic, elastic, heatproof dope for terrace Expired - Fee Related CN100436363C (en)