CN1868709A - Manufacturing method of incombustibe material - Google Patents
Manufacturing method of incombustibe material Download PDFInfo
- Publication number
- CN1868709A CN1868709A CN 200510073797 CN200510073797A CN1868709A CN 1868709 A CN1868709 A CN 1868709A CN 200510073797 CN200510073797 CN 200510073797 CN 200510073797 A CN200510073797 A CN 200510073797A CN 1868709 A CN1868709 A CN 1868709A
- Authority
- CN
- China
- Prior art keywords
- mixing
- glue
- jelly
- fire resistant
- string
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A process for preparing the material difficult to burn includes such steps as providing vegetative fibers, immersing them in an incombustible liquid, mixing them with the incombustible adhesive liquid chosen from sodium silicate polyvinyl acetate (PVA) and potassium silicate, and hot die pressing at 120-180 deg.C under 160-180 kg/sq.m.
Description
Technical field
The present invention is applied to building material technical field, refers to a kind of manufacture method that can conveniently produce the incombustibe material of lightweight and convenient construction incombustibe material especially.
Background technology
Progress along with the modern life, the modern is also exquisite day by day with respect to environment requirement, and beautifying the environment need be about compartment, decoration ... Deng, but general compartment, decorate if do not install setting such as incombustibe material additional, in case breaking out of fire, then form a threat greatly, and significantly shorten the very first time of so-called " escape ", cause the deficiency on the safety for life and property.
For improving above-mentioned general decoration, clamping plate that compartment uses, combustibles such as log, and in having incombustibe material on the market, but general incombustibe material manufacturing is difficult for and Heavy Weight, for example: with the gypsum of high burning-point manufacturing, again before gypsum, the back side affixes ornamental paper wood, but because the Heavy Weight of gypsum, be unfavorable for construction, for the workmen is a puzzlement greatly, and because the material character of gypsum, under the higher environment of temperature, for example: under the situation that burning is back or weather is xeothermic, the easy embrittlement of this gypsum, even cause bending, peel off, be full of cracks ... etc. problem, especially under the modern Global Greenhouse Effect, temperature rises year by year, therefore be nonflammable material with the gypsum, do not met modern requirement, form the field that the another kind of utmost point need improve.
Summary of the invention
Main purpose of the present invention is to overcome the deficiencies in the prior art and defective, and a kind of manufacture method of incombustibe material is provided, and it can effectively have anti-flaming effect, and significantly reduces weight, and reaches the good and easy construction of result of use.
For reaching above-mentioned purpose, the manufacture method of a kind of incombustibe material of the present invention, it comprises: steps A is prepared material: prepare in advance and be provided with string; Step B soaks fire resistant liquid: is 25%～45% to be that 75%～55% ratio is mixed mutually with the fire resistant liquid weight ratio with string with weight ratio, make this string be soaked in the fire resistant liquid fully, and fully absorb fire resistant liquid, form the string that contains fire resistant liquid; Step C mixes difficult combustion and sticks together glue: the string that will contain fire resistant liquid is 20%～40% with weight ratio, and in addition mixed weight sticks together glue than the difficulty combustion that is 80%～60%, with the increase denseness, forms a jelly; Step D puts into mould: the mixing jelly that will be added with incombustible agent is put into a mould, and adds in the end face of this mixing jelly and to be provided with a flame proof ethlyene dichloride skin, and the recycled writing paper of fitting in the bottom surface of this mixing jelly; Step F heating pressurization: with the mixing jelly in the mould by temperature Celsius 120 ℃～180 ℃, and with 160kg/m
2～180kg/m
2Pressure under, hot-forming; Step G finishes incombustibe material: hot-forming incombustibe material by taking out in this mould, is promptly finished the manufacturing of incombustibe material.
The present invention utilizes above-mentioned technological means, after implementing, because this string can fully absorb fire resistant liquid, the string that will be absorbed with fire resistant liquid again mixes difficult combustion and sticks together glue, increase whole denseness, and the formation jelly, so that put into mould, hot-forming, reach and to produce incombustibe material quickly and easily, can not only have effective difficult combustion effect, and the incombustibe material that produces can effectively have lightweight, and can convenient construction and reduce the problem of being out of shape, peeling off, chapping.
Description of drawings
Fig. 1 is a manufacturing process calcspar of the present invention.
The specific embodiment
As shown in Figure 1, be the manufacture method of incombustibe material of the present invention, its step comprises in regular turn:
Steps A is prepared material: prepare in advance and be provided with string;
Step B soaks fire resistant liquid: is 25%～45% to be that 75%～55% ratio is mixed mutually with the fire resistant liquid weight ratio with string with weight ratio, for example string is 35%, and fire resistant liquid is 65% ratio mixing, make this string be soaked in the fire resistant liquid fully, and fully absorb fire resistant liquid, form the string that contains fire resistant liquid;
Step C mixes difficult combustion and sticks together glue: the string that will contain fire resistant liquid is 20%～40% with weight ratio, in addition mixed weight sticks together glue than the difficulty combustion that is 80%～60%, for example: string is 30%, it is that 70% ratio is mixed that glue is sticked together in the combustion of this difficulty, wherein should difficulty combustion stick together glue and can be sodium metasilicate, polyvinyl acetate (Polyvinyl acetate is called for short PVA) or potassium silicate, to increase denseness, form a jelly;
Step D adds incombustible agent: stick together in the jelly of glue and add incombustible agent mixing difficult combustion, and the weight ratio of this jelly and this incombustible agent is 99.7%～75% to 0.3%～25%, increase difficult effect of firing with effective;
Step e is put into mould: the mixing jelly that will be added with incombustible agent is put into a mould, and the end face adding in this mixing jelly is provided with a flame proof ethlyene dichloride skin (Polyvinylchloride is called for short PVC), and is fitted with a recycled writing paper in the bottom surface of this mixing jelly;
Step F heating pressurization: with the temperature of the mixing jelly in the mould by 120 degree～180 degree Celsius, and with 160kg/m
2～180kg/m
2Pressure under, hot-forming;
Step G finishes incombustibe material: hot-forming incombustibe material by taking out in this mould, is promptly finished the manufacturing of incombustibe material; By above steps, finish the manufacture method of incombustibe material of the present invention.
Claims (5)
1. the manufacture method of an incombustibe material is characterized in that, comprising:
Steps A is prepared material: prepare in advance and be provided with string;
Step B soaks fire resistant liquid: is 25%～45% to be that 75%～55% ratio is mixed mutually with the fire resistant liquid weight ratio with string with weight ratio, make this string be soaked in the fire resistant liquid fully, and fully absorb fire resistant liquid, form the string that contains fire resistant liquid;
Step C mixes difficult combustion and sticks together glue: the string that will contain fire resistant liquid is 20%～40% with weight ratio, and in addition mixed weight sticks together glue than the difficulty combustion that is 80%～60%, with the increase denseness, forms a jelly;
Step D puts into mould: the mixing jelly that will be added with incombustible agent is put into a mould, and adds in the end face of this mixing jelly and to be provided with a flame proof ethlyene dichloride skin, and the recycled writing paper of fitting in the bottom surface of this mixing jelly;
Step F heating pressurization: with the mixing jelly in the mould by temperature Celsius 120 ℃～180 ℃, and with 160kg/m
2～180kg/m
2Pressure under, hot-forming;
Step G finishes incombustibe material: hot-forming incombustibe material by taking out in this mould, is promptly finished the manufacturing of incombustibe material.
2. the manufacture method of incombustibe material as claimed in claim 1, wherein, jelly after the glue step is sticked together in the difficult combustion of this mixing was added with incombustible agent before putting into mould, and this jelly and this incombustible agent with weight ratio be 99.7%～75% to 0.3%～25%.
3. the manufacture method of incombustibe material as claimed in claim 1, wherein, difficulty combustion in the glue step is sticked together in the difficult combustion of this mixing, and to stick together glue be potassium silicate.
4. the manufacture method of incombustibe material as claimed in claim 1, wherein, difficulty combustion in the glue step is sticked together in the difficult combustion of this mixing, and to stick together glue be polyvinyl acetate.
5. the manufacture method of incombustibe material as claimed in claim 1, wherein, difficulty combustion in the glue step is sticked together in the difficult combustion of this mixing, and to stick together glue be sodium metasilicate.