CN1861712A - Multifunctional water-proof paint - Google Patents
Multifunctional water-proof paint Download PDFInfo
- Publication number
- CN1861712A CN1861712A CN 200610086950 CN200610086950A CN1861712A CN 1861712 A CN1861712 A CN 1861712A CN 200610086950 CN200610086950 CN 200610086950 CN 200610086950 A CN200610086950 A CN 200610086950A CN 1861712 A CN1861712 A CN 1861712A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- fly ash
- softening agent
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a multifunction waterproof coating of organic-inorganic compound roofing. It is made up of the elastic acrylate synthetic latex, water, silica sol, the titanium white powder, the heavy CaCO3, the wollastonite in powder, the flyash, the hollow micro ball, the reflecting agent, the film forming assistant, the dispersant, the wetting agent, the antiseptic sunstance, the antifoam agent, the levelling agent, the thickener, the plasticizing agent, the soft agent and the pH adjustment. The character is it compounds the organic and inorganic material. The invention is easy to do and cost little. The film has the good elasticity and is resistance to the acid, the alkali and the aging.
Description
Technical field
The present invention relates to building water-proof paint, more particularly is a kind of organic and inorganic composite roof multifunctional water-proof paint.
Background technology
At present, domestic heat insulation house surface waterproof adopts three traditional oily four felts, heat construction, contaminate environment mostly; High temperature resistance, low temperature properties are poor, and be easily aging.Though aqueous polyurethane, polymer cement waterproof paint water-repellancy are good, heat insulation property is poor.
Summary of the invention
The purpose of this invention is to provide a kind ofly promptly has good waterproof effect, possesses a kind of multifunctional water-proof paint of good insulation, thermal insulation, resistance to deterioration, long service life again.
The object of the present invention is achieved like this, and it is made up of elastic acrylate synthetic emulsion, water, silicon sol, titanium dioxide, water-ground limestone, wollastonite powder, fly ash float, cenosphere, reflective dose, film coalescence aid, dispersion agent, wetting agent, anticorrosion and bactericidal agent, defoamer, flow agent, thickening material, softening agent, softening agent, pH value conditioning agent etc.
The present invention compared with prior art has the following advantages:
1. its adopts organic and inorganic to combine, and is coated with simultaneously to have added softening agent and softening agent in prescription, makes that to be coated with film elasticity big, good waterproof performance, hard again anti-aging, acidproof, alkaline-resisting, good weatherability simultaneously, long service life.
2. it is solvent with water, and easy construction is nonpoisonous and tasteless, environmental protection.
3. heat insulation property is good.Owing in filler, selected for use to have extremely low fly ash float of thermal conductivity and nano level cenosphere, added efficient reflective dose again simultaneously with reflected sunlight.Coating is neither absorbed heat, do not conduct heat again, make its heat insulation property be better than other roof waterpoof material, have one and be coated with the effect of using more.
Embodiment
Its weight percentages of components is as follows: elastic acrylate emulsion: 30-50; Water: 10-28; Silicon sol: 3-8; Titanium dioxide: 5-15; Coarse whiting: 6-10; Wollastonite powder: 5-8; Fly ash float: 5-15; Cenosphere: 1-8; Reflective dose: 1-3; Film coalescence aid: 0.5-2.5; Dispersion agent 0.3-1; Wetting agent: 0.2-0.5; Anticorrosion and bactericidal agent: 0.01-0.5; Defoamer: 0.3-0.8; Flow agent: 0.2-0.6; Thickening material: 0.5-0.8; Softening agent: 0.2-0.5; Softening agent: 0.1-0.3; PH value conditioning agent 0.1-0.5.
Dispensing information: the elastic acrylate emulsion in the prescription is self-crosslinking elastic styrene acrylic emulsion or pure acrylate elastic emulsion, silicon acrylate elastic emulsion; Water in the prescription is deionized water; Silicon sol in the prescription is that particle diameter 5-80nm and dioxide-containing silica are 20%-40%; Titanium dioxide in the prescription is the titanium dioxide of good weatherability; Coarse whiting in the prescription, wollastonite powder are the 400-800 order; Fly ash float in the prescription is through flotation, and the surface pretreated order number of parcel is between the 200-400 order; Cenosphere in the prescription is that Shanghai just U.S. inferior nanometer super-fine material company limited produces, and it is a kind of hollow sphere structure that has, and hard shell is arranged, and main component is SiO
2And Al
2O
3, diameter is between 0.01-400um; Reflective dose in the prescription is reflective dose of ccw-1 type, but its usable reflection sunlight; Film coalescence aid is propylene glycol, alcohol ester-12 in the prescription; Dispersion agent in the prescription is an organic and inorganic mating type dispersion agent; Softening agent in the prescription is a dibutyl phthalate; The NK-2000 that softening agent in the prescription selects for use Beijing Nuo Gen company to produce.
Preparation method of the present invention is: it is standby 1, the deionized water of getting umber ready, dispersion agent, wetting agent, defoamer, anticorrosion and bactericidal agent, titanium dioxide, coarse whiting, wollastonite powder, fly ash float, cenosphere etc. to be added stirrer for mixing high speed dispersion (1500 rev/mins) 20-30 minute successively.2, be 8-9 with the pH value of pH value conditioning agent elasticity adjusting emulsion after, add silicon sol lentamente and stir, add film coalescence aid, reflective dose, softening agent, softening agent, flow agent more successively and mix.3, add thickening material after (100-300 rev/min) mixes under stirring at low speed 1 and 2, the part defoamer filters, and barrelling is finished product.
The present invention is further illustrated below in conjunction with example:
Embodiment 1 (weight percent):
Deionized water: 20; Primal
2438 elastic emulsions: 35.5; Silicon sol: 6; Titanium dioxide R-960:5; Coarse whiting: 7; Wollastonite powder: 4; Fly ash float: 15; Cenosphere: 2; Reflective dose of CCW-1: 1.5; Propylene glycol: 1.5; Sodium hexametaphosphate 99: 0.4; Flow agent RM-2020:0.3; ASE-60:8; Dibutyl phthalate: 0.2; NK-2000 softening agent: 0.2; Anticorrosion and bactericidal agent: 0.1; Amp-95:0.1; Defoamer: 0.4.
Production technique:
1. in deionized water, added sodium hexametaphosphate dispersant, defoamer, anticorrosion and bactericidal agent, R-960 type titanium dioxide, coarse whiting, wollastonite powder, fly ash float, cenosphere high speed dispersion successively 20-30 minute.
2. be that 8-9 slowly adds silicon sol, propylene glycol, reflective dose of CCW-1, NK-2000 softening agent, plasticizer phthalic acid dibutylester again and mixes with the pH value of Amp-95 elasticity adjusting emulsion 2438.
3. adding defoamer, flow agent, thickening material to 1 and 2 after slowly mixing under the stirring at low speed transfers to required denseness and filters barrelling and be finished product.
Embodiment 2 (weight percent):
Elastic emulsion Primal
2438:50; Deionized water: 12; Silicon sol: 3; Titanium dioxide RCL-575:13; Coarse whiting: 2; Fly ash float: 10; Cenosphere: 3; Reflective dose of CCW-1: 2.2; Propylene glycol: 1.5; Alcohol ester-12:0.5; Orotan
731A:0.4; RM-8W:0.3; ASE-60:0.5; X-405:0.2; Dibutyl phthalate: 0.5; Softening agent NK-2000:0.2; Defoamer: 0.5, anticorrosion and bactericidal agent: 0.1; Amp-95:0.1-0.5.
Production technique:
1. in deionized water, added 731A dispersion agent, anticorrosion and bactericidal agent, defoamer, X-405 wetting agent, RCL-575 titanium dioxide, coarse whiting, fly ash float, cenosphere high speed dispersion successively 20-30 minute.
2. transferring the pH value of 2438 elastic emulsions with Amp-95 is slowly to add silicon sol, propylene glycol, alcohol ester-12, reflective dose of CCW-1, NK-2000, dibutyl phthalate etc. behind the 8-9 to mix.
3. adding defoamer, RM-8W flow agent, ASE-60 thickening material to 1 and 2 after slowly mixing under the low speed transfers to the barrelling of required denseness after-filtration and is finished product.
Claims (2)
1. multifunctional water-proof paint, it is made up of elastic acrylate synthetic emulsion, water, silicon sol, titanium dioxide, water-ground limestone, wollastonite powder, fly ash float, cenosphere, reflective dose, film coalescence aid, dispersion agent, wetting agent, anticorrosion and bactericidal agent, defoamer, flow agent, thickening material, softening agent, softening agent, pH value conditioning agent etc., it is characterized in that, its adopts organic and inorganic to combine, and has added fly ash float, nano-hollow microballon, reflective dose, softening agent etc. simultaneously and has carried out scientific matching.
2. multifunctional water-proof paint according to claim 1 is characterized in that weight percentages of components is as follows: elastic acrylate emulsion: 30-50; Water: 10-28; Silicon sol: 3-8; Titanium dioxide: 5-15; Coarse whiting: 6-10; Wollastonite powder: 5-8; Fly ash float: 5-15; Cenosphere: 1-8; Reflective dose: 1-3; Film coalescence aid: 0.5-2.5; Dispersion agent 0.3-1; Wetting agent: 0.2-0.5; Anticorrosion and bactericidal agent: 0.01-0.5; Defoamer: 0.3-0.8; Flow agent: 0.2-0.6; Thickening material: 0.5-0.8; Softening agent: 0.2-0.5; Softening agent: 0.1-0.3; PH value conditioning agent 0.1-0.5.