CN1837412B - 用高含水料电解制备钇-镁中间合金的方法 - Google Patents
用高含水料电解制备钇-镁中间合金的方法 Download PDFInfo
- Publication number
- CN1837412B CN1837412B CN2005101191219A CN200510119121A CN1837412B CN 1837412 B CN1837412 B CN 1837412B CN 2005101191219 A CN2005101191219 A CN 2005101191219A CN 200510119121 A CN200510119121 A CN 200510119121A CN 1837412 B CN1837412 B CN 1837412B
- Authority
- CN
- China
- Prior art keywords
- electrolytic
- master alloy
- alloy
- high moisture
- yttrium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供了用高含水料电解制备钇-镁中间合金的方法。以市售纯度为99.5%的KCl、经脱水处理的纯度为99.5%的YCl3·xH2O·yNH4Cl为熔盐电解质的原料,其中x=2.2~5.4,y=0.7~1.2;CaF2为消渣剂;以含10%Y-90%Mg中间合金为初始阴极的原料;本发明解决了难以用高含水料电解制备稀土-镁中间合金的技术难题。同时解决了氯化稀土保存和使用中二次吸水问题带来的麻烦,使电解槽的辐射热和电解槽阳极产生的氯气获得综合利用。电解炉中捞出的电解渣或淤泥破碎后与风罩后面一级回收器中的回收物混合,与新鲜电解质炉料混合返回电解炉再次使用,大大降低了成本。
Description
技术领域
本发明涉及用高含水料电解制备钇-镁中间合金的方法。
背景技术
几十年来,在氯化物体系熔盐电解生产金属镁或稀土金属RE或二者的合金领域,一直追求用半脱水料或不脱水料直接投入到电解槽进行电解,以缩短生产流程、降低脱水成本和与镁业上游产品MgCl2·6H2O或稀土行业上游产品RECl3·6H2O进行完美对接。到目前为止,稀土行业生产富镧ML、富铈MC或镧镨铈MLPC混合轻稀土金属过程中,已经达到用含有3~5个H2O的半脱水料RECl3·3~5H2O或完全结晶料RECl3·6H2O直接投入到电解槽进行电解生产的理想境地。电解法生产金属镁行业也达到了用含有0.5~4个H2O的半脱水料MgCl2·0.5~4H2O直接投入到镁电解槽电解的先进水平。但是,与上述生产单一金属Mg和单一金属RE不同的是,生产二者的合金RE-Mg目前尚需要严格的脱水,氯化物体系共电沉积法生产Ce-Mg中间合金目前达到的最好水平为能够使用含有1个H20的原料CeCl3·H2O和不含水的MgCI2原料进行生产。这主要是RE和Mg的交互作用导致生产二者中间合金比生产对应的单一金属在工艺条件方面要求更加苛刻。中国专利99115002.3号公开了题为“镧镨铈新型混合稀土金属及其生产工艺”的专利,该专利在RECl3-KCl氯化物熔盐体系中,直接向电解槽中投入最大含水量的原料组成为77%RECl3-28%H2O-5%NH4Cl;该原料换算成摩尔组成为RECl3·5.3H2O·0.32NH4Cl,用这种含5.3H2O的高脱水料成功的电解出混合轻稀土金属。美国专利2,880,151号公开了题为“金属镁的生产”的专利,该专利在MgCl2-KCl-1%CaF2氯化物熔盐体系中,直接向电解槽中投入最大含水量的原料组成MgCl2·4H2O的半脱水料,用这种高含水的MgCl2·4H2O。原料成功的电解出金属镁。另一中国专利94113824.0号公开了题为“氯化物电解共析法制取铈镁合金”的专利,该专利在CeCl3-MgCl2-KCl的熔融氯化物熔盐体系中,直接向电解槽中投入原料组成为CeCl3·H2O+MgCI2的低含水料,电解出5~15%Ce-Mg中间合金;阴极电流效率达到77%。显然,生产稀土-镁中间合金与单一稀土金属或金属镁相比,在利用高含水料方面,既存在技术难度,也并存着较大的发展空间。
发明内容
本发明的目的在于提供一种在熔融氯化物体系中,用高含水料电解制备钇-镁中间合金的方法。
实现本发明所基于的主要原理是:通过综合控制电解质的环流速度、加料速度、物料粒度和物料中H2O和NH4Cl比例等条件,使高含水料在电解槽液面瞬间脱水和二次氯化的效率达到最大化。对于组成为RECl3·2.2~5.4H2O·0.7~1.2NH4Cl的高含水料,当其被投撒到700℃~900℃的熔盐液面上,水和氯化铵要汽化和分解,副发应所生成主要有害产物为REOCl和RE2O3;RECl3的脱水、脱铵盐反应与发生副反应相互竞争。电解质合适的环流速度,能有效利用阳极产生的Cl2作为优质的氯化剂和吸水剂,可以最大化的避免发生副反应发生;若该环流速度小,Cl2数量不够;反之,环流速度过快,REOCl等被迅速的卷入到电解质中而失去与Cl2的反应机会。另一方面,物料中NH4Cl的汽化和分解,对于脱掉物料内部的水和防止副反应发生也起到支撑作用。但物料中NH4Cl含量同样不能太多,过多导致猛烈的汽化和分解,同样减弱Cl2的二次氯化效果,同时增加回收和尾气处理的负担。
本发明是采取如下的技术方案实现的:
用高含水料电解制备钇-镁中间合金的方法的步骤和条件如下:以市售纯度为99.5%的KCl、经脱水处理的纯度为99.5%的YCl3·xH2O·yNH4Cl为融盐电解质的原料,其中x=2.2~5.4,y=0.7~1.2;以含10%Y-90%Mg中间合金为初始阴极的原料;以纯度为99.5%的CaF2为消渣剂;该中间合金原料的纯度为99.5%;
阴极电流导出所用的阴极导流体材料为金属W,该导流体采用上插式;阴极承受器材料为刚玉或镁砂-Y2O3-Ti-高铝复合材料;石墨为阳极材料;
向圆柱形电解槽中加入占总电解质的重量百分比为9%~26%的KCl;再用交流电弧使所述的KCl熔化,向已经熔化的该KCl表面匀速添加YCl3·xH2O·yNH4Cl,其中,x=2.2~5.4,y=0.7~1.2;再向阴极承受器内加入上述10%Y-90%Mg中间合金形成初始阴极,每炉投入量为8~22公斤;通1000A以上直流电进行自热式电解;不断添加YCl3·x·x H2O·y NH4Cl,其中,x=2.2~5.4,y=0.7~1.2和补加所述的KCl,维持电解质重量百分组成为p%YCl3-(100-p)%KCl的相对浓度,其中p=9~26;单槽电解电流控制在1000A~2000A,并用该电流作为自热源,维持电解温度在700℃~860℃;阴极电流密度控制在2A/cm2-4A/cm2电解,得到用高含水料电解制备钇-镁中间合金。
有益效果:结晶氯化稀土RECl3·6H2O,其目前由于直接使用数量的限制,往往大部分作为稀土分离厂的中间体;对其简单脱掉约1个水直接用于电解生产合金,显然,该中间体的合理利用使得稀土行业上、下游产物良好衔接。缩短生产总流程。RECl3·6H2O脱掉约1个水的能耗比继续脱掉其余水的能耗低得非常多;大大降低脱水能耗,避免无水氯化稀土保存和使用中二次吸水问题带来的麻烦,使电解槽的辐射热和电解槽阳极产生的氯气获得综合利用。而且,电解炉中捞出的电解渣或淤泥破碎后与风罩后面一级回收器中的回收物混合,积累到一定数量后将其与大量的新鲜电解质炉料混合,返回电解炉再次使用。
具体实施方式
实施例1在内径Φ500mm圆柱形石墨槽中,该石墨槽兼作阳极。用金属W棒作为上插式阴极导流体。用镁砂-Y2O3-Ti-高铝复合坩埚作为阴极承受器。氯化稀土原料用YCl3·x H2O·yNH4Cl,其中x=5.4,y=1.2,初始阴极合金用10%Y-90%Mg;
在交流电弧熔化一定量的KCl后继续熔化一定量的YCl3·x H2O·yNH4Cl,其中x=5.4,y=1.2;在向阴极承受器中加入重量百分比为10%Y-90%Mg的初始阴极合金Ws为13Kg,通直流电进行自热式电解,用不断添加YCl3·xH2O·y NH4Cl,其中x=5.4,y=1.2的原料的方法维持电解质组成为p%YCl3-(100-p)%KCl,其中的p=26,电解温度TE为860℃,阴极电流密度DK为DK=4A/cm2,出炉前捞渣勺捞出少量的电解渣,得到用高含水料电解制备的钇-镁中间合金。出炉合金中忆浓度为26.4%,η=67%。
实施例2
取x=2.2,y=0.7;p=9;Ws=8;TE=700℃;DK=2A/cm2,出炉合金中钇浓度为19%,η=65.5%;其余同实施例1。
实施例3刚玉坩埚作为阴极承受器。取x=4,,y=1;p=13;Ws=22;TE=800℃;DK=3.6A/cm2;另在电解质中加入CaF2,加入该CaF2占电解质重量百分比浓度为1.5%;出炉前捞渣,捞出很少电解渣,其余同实施例1;出炉合金中钇浓度为20.8%,η=63.7%。
实施例4取x=3.1,y=0.7;p=16;Ws=16;TE=750℃;DK=3A/cm2,出炉合金中铭浓度为24.8%,η=66.9%;其余同实施例1。
Claims (4)
1.用高含水料电解制备钇-镁中间合金的方法,其特征在于,在内径Φ500mm圆柱形石墨槽中,该石墨槽兼作阳极,用金属W棒作为上插式阴极导流体,用镁砂-Y2O3-Ti-高铝复合坩埚作为阴极承受器,氯化稀土原料用YCl3·x H2O·y NH4Cl,其中x=5.4,y=1.2,初始阴极合金用10%Y-90%Mg;
在交流电弧熔化KCl后继续熔化YCl3·x H2O·y NH4Cl,其中x=5.4,y=1.2;在向阴极承受器中加入重量百分比为10%Y-90%Mg的初始阴极合金Ws为13Kg,通直流电进行自热式电解,用不断添加YCl3·x H2O·y NH4Cl,其中x=5.4,y=1.2的原料的方法维持电解质组成为p%YCl3-(100-p)%KCl,其中的p=26,电解温度TE为860℃,阴极电流密度DK为4A/cm2,出炉前捞渣勺捞出电解渣,得到用高含水料电解制备的钇-镁中间合金。
2.如权利要求1所述的用高含水料电解制备钇-镁中间合金的方法,其特征在于,所述的x=2.2,y=0.7;p=9;Ws=8;TE=700℃;阴极电流密度DK为2A/cm2。
3.如权利要求1所述的用高含水料电解制备钇-镁中间合金的方法,其特征在于,刚玉坩埚作为阴极承受器,取x=4,y=1;p=13;WS=22;TE=800℃;DK=3.6A/cm2;另在电解质中加入CaF2,该CaF2占电解质重量百分比浓度为1.5%。
4.如权利要求1所述的用高含水料电解制备钇-镁中间合金的方法,其特征在于,所述的x=3.1,y=0.7;p=16;WS=16;TE=750℃;阴极电流密度DK为3A/cm2。