CN1821167A - 一种刚玉－莫来石复合材料及制备方法 - Google Patents

一种刚玉－莫来石复合材料及制备方法 Download PDF

Info

Publication number
CN1821167A
CN1821167A CN 200610057163 CN200610057163A CN1821167A CN 1821167 A CN1821167 A CN 1821167A CN 200610057163 CN200610057163 CN 200610057163 CN 200610057163 A CN200610057163 A CN 200610057163A CN 1821167 A CN1821167 A CN 1821167A
Authority
CN
China
Prior art keywords
corundum
mullite
coal gangue
composite material
bauxitic clay
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610057163
Other languages
English (en)
Other versions
CN1321937C (zh
Inventor
张梅
王习东
董鹏莉
王海娟
李华军
张歪牛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHONGYUAN WEIYE NEW MATERIAL Co Ltd
Original Assignee
University of Science and Technology Beijing USTB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Science and Technology Beijing USTB filed Critical University of Science and Technology Beijing USTB
Priority to CNB2006100571639A priority Critical patent/CN1321937C/zh
Publication of CN1821167A publication Critical patent/CN1821167A/zh
Application granted granted Critical
Publication of CN1321937C publication Critical patent/CN1321937C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种刚玉－莫来石复合材料及制备方法，属于耐火材料领域。特别涉及一种刚玉－莫来石复合材料。其特征在于合成刚玉－莫来石的主要原料是铝矾土和煤矸石，煤矸石的重量百分比含量为5～25％，铝矾土的重量百分比含量为75～95％，铝矾土中Al2O3含量要求大于75％。合成刚玉－莫来石的步骤为：原料用无水乙醇做介质，经过球磨6小时后在烘箱中保温12小时，取出后机压成型，在1350℃～1450℃保温3～6个小时，空气气氛下进行合成。试验结果表明：合成的刚玉－莫来石复合材料非常纯，能显著提高材料的各方面性能。因为合成刚玉－莫来石的主要原料是铝矾土和煤矸石，原料丰富价格低廉，合成的刚玉－莫来石复合材料具有很高的附加值，所以是制备高温耐火材料的又一个新途径。

Description

一种刚玉-莫来石复合材料及制备方法
技术领域
本发明属于耐火材料领域，特别涉及一种刚玉-莫来石复合材料。
背景技术
由于莫来石具有良好的高温力学、高温热学性能，使合成莫来石制品具有较高的密度和纯度，较低的热传导系数和热膨胀系数，高温结构强度高，高温蠕变率低，抗热震性和化学侵蚀性强，熔点高等有点；而刚玉弹性好，熔点高，在高温下具有良好的耐磨、抗化学侵蚀性和体积稳定性，硬度大，耐火度高；另外莫来石晶体一般为柱状或者棱柱状，刚玉体一般为粒状，所以制备刚玉-莫来石复合材料将汇集刚玉晶体和莫来石晶体的双重优点，从而使这种材料在各方面都优于单相莫来石材料或刚玉材料。但是如果用纯原料来合成则严重提高了材料的生产成本，尤其是作为耐火材料。因此，采用天然原料无疑可以大幅度降低材料的生产成本。
我国铝矾土储量极为丰富，产地从黄河以北的山西、河北和山东，穿过中部的河南和广西，直到西南的贵州和云南，目前出产铝矾土熟料的主要产地在山西、河南和贵州。铝矾土是由长石、云母等矿物风化而形成的，他的主要矿物类型是三水铝石、硬水铝石和勃姆石，此外由于形成的条件不同，还可能含有高岭石、石英、方解石等杂质。我国铝矾土中的水铝石-高岭石型(DK)和勃姆石-高岭石型(BK)应用最为广泛，DK型铝矾土熟料按Al2O3含量氛围特等、I等、IIA等、IIB等、III等，其主要化学成分见表1和表2
                    表1各类BK型高铝矾土煅烧后化学成分(wt％)
  Al2O3   SiO2   Fe2O3   TiO2   Na2O   K2O   I.L
  贵州河南   59.8062.44   23.5220.68   0.510.64   1.081.82   0.070.03   0.020.11   14.6614.12
                 表2各类DK型高铝矾土煅烧后化学成分(wt％)
  级别   Al2O3   SiO2   Fe2O3   TiO2   CaO   MgO   K2O   Na2O
  SIIIIAIIAIIAIIBIIBIII   86.2082.4079.8076.0372.2069.8067.5060.5054.10   7.6011.5514.5019.4022.0025.7027.4033.7040.50   1.761.521.641.461.781.711.541.921.72   4.023.643.172.872.642.442.822.943.00   ---------   0.250.280.300.150.180.170.110.180.17   0.140.130.100.100.150.120.160.160.14   0.060.060.050.100.050.060.200.100.05
煤矸石是在煤炭开采和洗选过程中产生的副产品，是我国排放量最大的工业废渣之一。煤矸石产量按原煤产量的15％计算，每年煤矸石至少增加1～2亿吨以上，历年堆存的煤矸石约20亿吨，占地近10万亩，且仍在不断增加，2000年就上升到了3.1亿吨，不仅占用大量的农田和土地，而且严重污染环境，如何治理和综合利用煤矸石也正在得到人们的重视。山西是产煤大省，所以同时也有大量的煤矸石堆积，其主要化学成分为SiO2含量在50％左右，Al2O3含量在20％左右，同时还含有少量的CaO、MgO、TiO2、Na2O、K2O和不同含量的C，其开发利用前景非常乐观。
发明内容：
本发明目的目的在于结合我国现有资源的充分利用及促进固体废弃物资源化再生利用，选择了一种天然原料和固体废弃物来合成耐火材料制作刚玉-莫来石复合材料，不仅充分利用了现有资源，同时也减少了固体废弃物带来的污染，大大降低生产成本。
一种刚玉-莫来石复合材料，其特征在于合成刚玉-莫来石的主要原料是铝矾土和煤矸石，煤矸石的重量百分比含量为5～25％，铝矾土的重量百分比含量为75～95％，铝矾土中Al2O3含量要求大于75％。最佳原料配比：煤矸石的重量百分比含量为10～20％，铝矾土的重量百分比含量为80～90％。
其制作方法为：原料用无水乙醇做介质，经过球磨6小时后在烘箱中保温12小时，取出后机压成型，在1350℃～1450℃保温3～6个小时，空气气氛下进行合成。经试验，并利用XRD分析了复合材料的组成，试验结果表明：合成的刚玉-莫来石复合材料非常纯，从SEM断口形貌分析可看出晶体形貌为典型的长柱状晶，相互交错状的密集生长，其长径比大约在8∶1甚至更大，晶粒横断面尺寸已接近纳米级，断裂方式为穿晶断裂，这能显著提高材料的各方面性能。
因为合成刚玉-莫来石的主要原料是铝矾土和煤矸石，原料丰富价格低廉，合成的刚玉-莫来石复合材料具有很高的附加值，所以是制备高温耐火材料的又一个新途径。
附图说明：
图1：刚玉-莫来石复合材料合成工艺图
图2：刚玉-莫来石复合材料XRD图(10wt％煤矸石)
图3：刚玉-莫来石复合材料XRD图(20wt％煤矸石)
图4：刚玉-莫来石复合材料SEM图(10wt％煤矸石)
图5：刚玉-莫来石复合材料SEM图(20wt％煤矸石)
具体实施方式：
1.原料选取
①铝矾土的化学分析结果
Figure A20061005716300051
②煤矸石的化学分析结果
2.原料合成
原料配比分别为：5、10、20wt.％煤矸石和95、90、80wt.％的铝矾土
3.合成步骤：见图1
从XRD图中标注中很清晰的看到在此试验条件下合成了非常纯的刚玉-莫来石复合材料。
从SEM断口形貌分析可看出晶体形貌为典型的长柱状晶，相互交错状的密集生长，其长径比大约在8∶1甚至更大，晶粒横断面尺寸已接近纳米级，断裂方式为穿晶断裂，这能显著提高材料的各方面性能。

Claims (3)

1、一种刚玉-莫来石复合材料，其特征在于合成刚玉-莫来石的主要原料是铝矾土和煤矸石，煤矸石的重量百分比含量为5～25％，铝矾土的重量百分比含量为75～95％，铝矾土中Al2O3含量要求大于75％。
2、如权利要求1所述的一种刚玉-莫来石复合材料，其特征在于合成刚玉-莫来石的原料配比：煤矸石的重量百分比含量为10～20％，铝矾土的重量百分比含量为80～90％。
3、如权利要求1或2所述的一种刚玉-莫来石复合材料，其特征在于合成刚玉-莫来石的步骤为：原料用无水乙醇做介质，经过球磨6小时后在烘箱中保温12小时，取出后机压成型，在1350℃～1450℃保温3～6个小时，空气气氛下进行合成。
CNB2006100571639A 2006-03-13 2006-03-13 一种刚玉－莫来石复合材料及制备方法 Expired - Fee Related CN1321937C (zh)